Abstract

The present invention relates to a method of manufacturing wood grain porcelain, to produce a circular frame by carving a good wood grain, such as pine, larch, and to the circular frame by using a torch lamp to burn the circular frame To produce a step, using a gypsum on the wood frame formed in the step using a gypsum manufacturing method and then to make a gypsum mold using the mold, injecting the extruded soil into the molding mold, extrusion Molding and shaping wood grain porcelain, shaping the molded wood grain porcelain and roasting it at a temperature of about 700 ° C. to 1000 ° C., applying glaze to the bee porcelain and roasting it at a temperature of 1230 ° C. to 1300 ° C. It is a manufacturing method of wood grain ceramics, characterized in that the step consists of.

Description

Manufacturing method of wood grain ceramics {AAAAA}

The present invention relates to a method for producing wood grain porcelain, and more particularly, to a method for producing porcelain, which can reproduce the appearance of solid wood with good wood grain, such as pine and larch.

In general, the first time humankind used earthenware was about 10,000 to 6 thousand years ago. In Korea, earthenware started making and using earthenware from 7-8 thousand years ago. In the early world, pottery and stoneware were made and used in Hwado within 1,100 degrees. However, only Korea, China, and Vietnam could produce porcelain. Especially, Korea and China have unique and high-quality porcelain. Could produce.

In the first half of the ninth century, Korea adopted the celadon manufacturing technology through active trade with China in the Silla era, and then entered the culture of self-culture out of the earthenware culture. Since then, the celadon, which began to be created in the Unification Silla period, developed into the 12th century Goryeo Dynasty, and produced the world's most beautiful self, which is the most beautiful in the world. Influenced by the Goryeo Dynasty, a Buddhist country centered on the aristocracy, the celadon was left behind by the late Goryeo Dynasty, leaving many masterpieces with its splendor and refinement.

In addition, the development of world ceramics has developed from earthenware to pottery / stoneware, pottery / stoneware to celadon, and celadon to white porcelain. In the process of changing from celadon to white porcelain, Korea has a process of making a very distinctive and excellent ceramic called 'Buncheongsagi' in the early 15th century.

This unique bonsai scavenger spread to Japan through the war of the Imjin War in the 16th century, which became the point of Japanese self-development. At the time, Japan was using pottery that could not produce porcelain, but it was not until the Japanese brought enough Korean potters to Japan to make pottery, which allowed them to produce porcelain. The one, Lee Sam-pyeong, is still Japanese.

At that time, the war between Korea and Japan was destroyed, and many potters were attracted to Japan.

Later, against the background of the Confucian culture of the 17th century Joseon Dynasty, Joseon, a white-ethnic people, developed pure white porcelain symbolizing purity, purity and humility. Later on, thanks to the high preferences of the scholars of the Joseon Dynasty, white porcelain evolved from beautiful pure white porcelain to various patterns and bold transformations, making it a painting art with a vivid sophistication of humor and wit.

Korean pottery is clear and unique based on its excellent qualities, and its shape is healthy and youthful. Korean potters always live in harmony with nature in the mountains they have paid for and spend more time and effort than expressing complicated techniques and various colors focusing on the functions necessary for life. Invented ingenious great porcelain art.

However, until now, Korean ceramics manufacturing methods have not been newly attempted in addition to traditional methods.

Therefore, it is a technical subject to provide the manufacturing method of the ceramics by a new manufacturing method instead of the conventional ceramics manufacturing method.

In addition, the present invention is to provide a method for producing a ceramic ware that can be produced in a large amount by the mold rather than the conventional handmade molding step as a technical problem.

1 is a photograph of porcelain produced by the method of manufacturing a grain of wood pattern ceramics according to the present invention.

Hereinafter, the present invention will be described in detail.

The present invention is to produce a circular frame by carving a solid wood, such as pine, larch, good wood grain, and to produce a circular frame of wood grain pattern by drawing a circular pattern by using the torch lamp Manufacturing a use-type case using plaster on a circular frame having wood grains, and then forming a gypsum use-molding mold with the case; injecting and extruding soaked soil into the molding mold, and molding wood grain porcelain; Shaping the molded wood grain porcelain and baking the first at a temperature of about 700 ℃ ~ 1000 ℃, applying a glaze to the first porcelain, the wood grain pattern ceramics, characterized in that consisting of the step of baking at a temperature of 1230 ℃ ~ 1300 ℃ It is a manufacturing method of.

Hereinafter, the present invention will be described in detail step by step based on the accompanying drawings.

First stage

The first step is a step of producing a circular frame by carving a solid wood, such as pine, larch, good wood grain, and by drawing a circular pattern using the torch lamp to produce a circular frame of wood grain pattern. Brush off the burned wood with a brush. The first step is to sculpt the product you are going to produce, including all kinds of household appliances, kitchen utensils, frying pens, kettles, plates, tableware, tea tables, vases, flower pots, headboards, small cabinets, lighting, and interior accessories. Can be mentioned.

2nd step

The second step is to prepare a use case using gypsum on the wood frame formed in the first step, and then to make a gypsum mold using the case.

3rd step

The third step is a step of molding wood grain ceramics by injecting and extruding the soil received in the molding mold. This stage is the molding stage to make pores of porcelain, and there are extrusion molding.

At this time, the soil used in the molding mold is a crushed soil, and finely crushed the raw material, the impurities are filtered out and removed in the water, and precipitated in water to collect only fine sediments and dried in a shade for a certain period of time. At this time, the molding method to be used is to mold ceramics by pressure injection, grueling, plate making type, and soil water injection method.

4th step

The fourth step is to mold the wood grain ceramics formed in the third step and to roast first at a temperature of about 700 ℃ ~ 100 ℃. In this stage, the dried foods are dried thoroughly and then cooked. The fire is generally burned at the temperature for 15 to 25 hours.

5th step

The fifth step is the step of applying the glaze to the porcelain first staged in the step to roast the chaebol at a temperature of 1230 ℃ ~ 1300 ℃. At this time, glaze is applied to the grilled objects (器物), the method of the immersion method, the spray method, the painting method. The chaebol roasts 20-30 hours at this temperature.

The wood grain pattern porcelain made of the above steps include all of the porcelain, kitchen utensils, frying pens, kettles, plates, tableware, tea tables, vases, flower pots, headboards, small items, lighting, interior accessories, etc. Is shown in FIG. 1.

As described above, the method of manufacturing wood grain ceramics according to the present invention can be applied to various types of products such as household ceramics, ornaments, and interior accessories in addition to traditional ceramics, and the natural texture of wood grain can be displayed on the inside or outside of the ceramics. It can be displayed on both sides, and it shows the effect of creating new ceramics out of the pattern or frame of existing ceramics.

In addition, the natural wood grain texture of the glaze can be represented according to the yin-embossed volume of wood grain, and the inlay technique is applied to partially improve the texture of raw wood.

Claims (2)

The present invention is to produce a circular frame by carving a solid wood, such as pine, larch, good wood grain, and to produce a circular frame of wood grain pattern by drawing a circular pattern by using the torch lamp Manufacturing a use-type case using plaster on a circular frame having wood grains, and then forming a gypsum use-molding mold with the case; injecting and extruding soaked soil into the molding mold, and molding wood grain porcelain; Shaping the molded wood grain porcelain and baking the first at a temperature of about 700 ℃ ~ 1000 ℃, applying a glaze to the first porcelain, the wood grain pattern ceramics, characterized in that consisting of the step of baking at a temperature of 1230 ℃ ~ 1300 ℃ Manufacturing method. The wood grain ceramics as claimed in claim 1, wherein the kind of wood grain ceramics is one of a standing porcelain, a kitchen utensil, a frying pan, a kettle, a plate, a tableware, a tea table, a vase, a flower pot, a headboard, a small cabinet, lighting, an interior accessory, etc. Method of making patterned ceramics.