KR0178603B1 - 연알루미늄 재료로 일체형 경금속 휠을 제조하는 방법 - Google Patents
연알루미늄 재료로 일체형 경금속 휠을 제조하는 방법 Download PDFInfo
- Publication number
- KR0178603B1 KR0178603B1 KR1019950703462A KR19950703462A KR0178603B1 KR 0178603 B1 KR0178603 B1 KR 0178603B1 KR 1019950703462 A KR1019950703462 A KR 1019950703462A KR 19950703462 A KR19950703462 A KR 19950703462A KR 0178603 B1 KR0178603 B1 KR 0178603B1
- Authority
- KR
- South Korea
- Prior art keywords
- blank
- temperature
- rolling
- light metal
- metal wheel
- Prior art date
Abstract
본 발명은 따뜻한 블랭크를 플로우 턴 또는 압연함으로써, 가공된 알루미늄 재료, 바람직하게는 AIMgSi 타입의 합금으로 일체형 경금속 휠을 제조하는 방법에 관한 것이다. 블랭크를 약 530℃의 온도에서 용액 열처리한 다음 약 150℃ 내지 200℃에서 시효처리한다. 용액 열처리된 블랭크를 약 200℃에서 조절가능하게 캔칭하고, 이 온도에서 부가의 온도상승를 피하면서 플로우 턴 또는 압연한 다음 시효처리한다.
Description
본 발명은 플루우 터닝(flow turning) 또는 압연을 고온상태에서 수행하는 단계와, 합금의 형태에 따라 약 530℃의 온도에서 용체화 처리하는 단계와, 후속하는 캔칭 및 150℃ 내지 200℃에서 시효처리하는 단계를 거쳐서 경화가능한 연알루미늄 합금으로 된 블랭크로부터 일체형 경금속 휠을 제조하는 방법 및 상술한 방법을 사용해서 AIMgSi 타입의 합금으로 일체형 경금속 휠의 제조하는 방법에 관한 것이다.
상술한 방식의 공지 방법에서는, 횡단면이 대략 직사각형인 플랜지를 방사방향으로 분할하고, 그 다음에 림의 벽을 압연한 소위 플랜지 블랭크, 또는 가장자리영역으로부터 지지부를 가진 림의 벽을 압연한 소위 포트 블랭크가 사용된다.
통상적으로 알려진 공지 방법에서는 플랜지 블랭크의 분할 및 마무리 압연 전에, 또는 하나의 작업 공정인 포트 블랭크의 최종 압연에서, 블랭크가 150℃ 내지 250℃의 온도범위로 가열된다. 이렇게 한 후에 합금의 타입에 따라 약 530℃의 온도에서 용체화 처리되고 150℃ 내지 200℃에서 시효처리가 이루어진다.
이 때에, 압연된 블랭크의 용체화 처리 및 시효처리시, 특히 림의 벽이 심하게 찌그러질 위험이 있다. 게다가, 나중에 압연처리를 하기 위해서는 다시 가열을 해야하며, 이러한 가열은 많은 부가의 에너지 소비를 필요로 한다.
본 발명의 목적은 상술한 방식의 방법을 개량하여 마무리 압연된 부품의 찌그러짐을 가급적 피하고 에너지 소비를 줄이는 것이다.
상기 목적은 블랭크를 용체화 처리 단계 후에 합금의 타입에 따라서 약 200℃로 조절가능한 방식으로 캔칭하는 단계와, 이 온도에서, 보다 높은 가열을 피하면서 마무리 제품을 만들도록 플로우 터닝 또는 압연하는 단계와, 그 후에 시효경화하는 단계로 이루어진 본 발명에 의해 달성된다.
캔칭 및 후속하는 터닝으로 인해 유발되는, 마무리 압연된 부품의 찌그러짐을 피할 수 있을 정도로, 용체화 처리단계로부터 나온 압연되지 않은 블랭크를 합금의 타입에 따라 약 200℃까지 조절가능한 방식으로 캔칭한 다음에 마무리 압연한다. 합금의 타입에 따라 약 200℃의 온도로 블랭크를 조정가능한 방식으로 캔칭함으로써, 주변온도로부터 재가열을 해야하는 공지방법에 비해 현저한 에너지 절감이 이루어진다. 합금의 타입에 따라 약 200℃의 온도에서 블랭크를 분할하고 계속해서 포트 블랭크를 플로우 터닝 또는 압연을 실시하여 최종 제품을 만든다. 블랭크의 용체화 처리 온도로부터 조절가능한 방식으로 캔칭한 후 압연함으로써 재료의 조직형성이 개선되고, 그에 따라 사용 특성도 개선된다. 그 다음에, 시효처리가 공지된 방식으로 이루어진다.
용체화 처리후 캔칭을 일정한 물의 량 및 온도를 가진 물 샤워기로 높은 캔칭속도로 실시하는 것도 본 발명에 속한다. 이로 인해 양호한 기계적 특성이 얻어진다. 물론, 적합한 프레임내에 다수의 블랭크를 설치하여 여기에 물을 뿌려서 다수의 블랭크를 캔칭하는 것도 가능하다.
상술한 방법을 AIMgSi 타입의 합금으로 일체형 경금속 휠을 제조하는데 양호하게 사용할 수 있다.
또한, 압연 공정 또는 프레스 공정 동안 유지되어야 하는 합금의 타입에 따른 약 200℃의 압연온도가 후속하는 시효처리에 사용되는 것이 바람직하다.
마무리 압연된 블랭크의 적은 찌그러짐으로 인해, 림의 벽에 대한 비틀림이 현저히 줄어들 수 있다. 동심성 편차 및 불평형도 줄어든다.
Claims (4)
- 플루우 터닝(flow turning) 또는 압연을 고온상태에서 수행하는 단계와, 합금의 형태에 따라 530℃의 온도에서 용체화 처리하는 단계와, 후속하는 캔칭 및 150℃ 내지 200℃에서 시효처리하는 단계를 거쳐서 경화 가능한 연알루미늄 합금으로 된 블랭크로부터 일체형 경금속 휠을 제조하는 방법에 있어서, 먼저 상기 블랭크를 용체화 처리하는 단계화, 다음으로 합금의 타입에 따라서 상기 블랭크를 200℃까지 조절가능한 방식으로 캔칭시키는 단계와, 상기 캔칭 온도에서, 보다 높은 가열을 피하면서 마무리 제품을 만들도록 상기 블랭크를 플로우 터닝 또는 압연시키는 단계와, 마지막으로 상기 블랭크를 시효경화처리 하는 단계를 포함하는 것을 특징으로 하는 방법.
- 제1항에 있어서, 상기 조절가능한 방식으로 캔칭하는 단계동안 먼저 압연온도 미만으로 만든다음 다시 압연온도로 가열하는 것을 특징으로 하는 방법.
- 제1항에 있어서, 상기 블랭크 각각을 일정한 물의 량 및 온도를 가진 물 샤워기로 높은 캔칭속도로 캔칭하는 것을 특징으로 하는 방법.
- AIMgSi 타입의 합금으로부터 일체형 경금속 휠을 제조하는 방법에 있어서, 제1항 내지 제3항중 어느 한 항에 따른 방법을 사용하는 것을 특징으로 하는 방법.