JPWO2020171196A1 - 塗料組成物及び塗装物品 - Google Patents
塗料組成物及び塗装物品 Download PDFInfo
- Publication number
- JPWO2020171196A1 JPWO2020171196A1 JP2021502171A JP2021502171A JPWO2020171196A1 JP WO2020171196 A1 JPWO2020171196 A1 JP WO2020171196A1 JP 2021502171 A JP2021502171 A JP 2021502171A JP 2021502171 A JP2021502171 A JP 2021502171A JP WO2020171196 A1 JPWO2020171196 A1 JP WO2020171196A1
- Authority
- JP
- Japan
- Prior art keywords
- solid lubricant
- coating composition
- fluororubber
- coating
- vdf
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
上記固体潤滑剤は、固体潤滑剤(A)と、上記固体潤滑剤(A)とは異なる固体潤滑剤(B)とを含むことを特徴とする塗料組成物に関する。
上記金属板の片面又は両面に設けられたエラストマー層と、
上記エラストマー層の上に設けられた、本開示の塗料組成物から形成された塗膜と
を有することを特徴とする塗装物品にも関する。
本開示は、フッ素ゴム、加硫剤、固体潤滑剤及び有機溶剤を含み、上記固体潤滑剤は、固体潤滑剤(A)と、上記固体潤滑剤(A)とは異なる固体潤滑剤(B)とを含むことを特徴とする塗料組成物に関する。
本開示の塗料組成物は、上記成分を含むので、非粘着性及び耐引掻き傷性に優れる塗膜を与えることができる。
上記非粘着性としては、例えば、本開示の塗料組成物から形成される塗膜の製造又は保管時における、当該塗膜同士の非粘着性や、本開示の塗料組成物から形成される塗膜の製造又は使用時における、当該塗膜の表面と接触する他の材料(プレス金型等)に対する非粘着性が挙げられる。
本開示の塗料組成物は、また、塗料安定性にも優れる。
上記フッ素ゴムは、1種又は2種以上を用いることができる。
式(1):
CH2=CFRf (1)
(式中、Rfは炭素数1〜12の直鎖状又は分岐状のフルオロアルキル基)
上記ポリオール加硫剤としては、上記以外にも、フッ素ゴム用ポリオール系加硫剤として市販されているものはいずれも使用することができる。
上記ポリオール加硫剤は、1種又は2種以上を用いることができる。
本明細書において、平均粒径は、堀場製作所製CAPA700(遠心沈降式粒度分布測定装置)にて測定した値である。
上記充填材としては、カーボンブラック、ホワイトカーボン、炭酸カルシウム、硫酸バリウム、タルク、珪酸カルシウム等が例示できる。なかでもカーボンブラックが好ましい。
上記着色剤としては、無機顔料、複合酸化物顔料等が例示できる。
上記消泡剤としてはシリコン系消泡剤、ポリマー系消泡剤等が例示できる。
上記表面調整剤としてはシロキサン化合物、アクリル系共重合物、メタクリル系共重合物等が例示できる。
乾燥及び硬化の条件は、本開示の塗料組成物及び塗布対象物の種類等に応じて適宜設定することができる。
上記フッ素ゴムは、1種又は2種以上を用いることができる。
式(1):
CH2=CFRf (1)
(式中、Rfは炭素数1〜12の直鎖状又は分岐状のフルオロアルキル基)
本開示の塗装物品は、本開示の塗料組成物から形成された塗膜を有するので、非粘着性及び耐引掻き傷性に優れる。
各層を形成する塗料組成物を塗布・乾燥した後、必要に応じて硬化を行ってもよい。上記硬化は、一層ごとに行ってもよく、複数の層についてまとめて行ってもよい。また、上記硬化を、上記乾燥と同時に行ってもよい。
乾燥及び硬化の条件は、本開示の塗料組成物及びエラストマー層の種類等に応じて適宜設定することができる。
実施例1
フッ素ゴムとしてビニリデンフルオライド/テトラフルオロエチレン/ヘキサフルオロプロピレン共重合体(フッ素濃度:68質量%)からなるエラストマーの固形分100質量部に対し、グラファイト37.5質量部、フッ素樹脂(ポリテトラフルオロエチレン〔PTFE〕)112.5質量部及び受酸剤5質量部をオープンロールにて混練しコンパウンドとした。このコンパウンドを有機溶剤としてのメチルエチルケトン700質量部と混合し、コンパウンド溶液を得た。
一方、ポリオール系加硫剤2質量部と加硫助剤0.5質量部を、有機溶剤としてのメチルエチルケトン200質量部及びエタノール5質量部から構成される混合溶媒に溶解し、その中に安定剤として、オルト酢酸エステル系化合物2質量部及び有機酸2質量部を加えた。この溶液を、先に調製したコンパウンド溶液とディスパーで混合して非粘着処理用塗料組成物を得た。
フッ素ゴム、フッ素樹脂及びグラファイトの配合量を表1に示すように変更し、かつカーボンブラックを配合したこと以外は実施例1と同様にして、非粘着処理用塗料組成物を得た。
フッ素ゴム、フッ素樹脂及びグラファイトの配合量を表1に示すように変更したこと以外は実施例1と同様にして、非粘着処理用塗料組成物を得た。
グラファイトを表1に示すように変更したこと以外は実施例1と同様にして、非粘着処理用塗料組成物を得た。
フッ素ゴム、フッ素樹脂及びグラファイトの配合量を表1に示すように変更したこと以外は実施例1と同様にして、非粘着処理用塗料組成物を得た。
フッ素ゴム(ビニリデンフルオライド/テトラフルオロエチレン/ヘキサフルオロプロピレン共重合体)の水性ディスパージョン(フッ素ゴム含有量60質量%)100質量部、フッ素樹脂(ポリテトラフルオロエチレン〔PTFE〕)の水性ディスパージョン(フッ素樹脂含有量60質量%)100質量部、アミノ基含有シランカップリング剤6質量部、水3800質量部を混合し非粘着処理用塗料組成物を得た。
予めアセトン洗浄しておいたアルミ板に、フッ素ゴム塗料(VdF/HFP共重合体のジイソブチルケトン溶液)をフローコーターにて塗装し、100℃で30分乾燥した後に、200℃で30分焼成して、ゴム層厚み25μmの塗装板を得た。
上記で得られた塗装板を実施例及び比較例で得られた非粘着処理用塗料組成物に、常温で浸漬塗装し、次いで80〜100℃で5分間乾燥を行った後、200℃で5分間焼成し、厚み1μmの非粘着処理層をもつ試験片(塗装物品)を得た。
<非粘着性試験(塗膜同士の非粘着性)>
上記試験片を2cm幅で切り出して2cm×3cmの塗膜面同士を重ね、荷重1kg、200℃の条件下で1時間保持した。上記条件で重ね合わせた状態の試験片について、室温下でJIS K6850の引張せん断接着強さ試験法に従い、万能試験機(島津製作所社製)を用いて引張強さを測定し、下記の基準で表面の粘着力を評価した。
○:引張強さ0MPa
△:引張強さ1.0×10−2MPa未満
×:引張強さ1.0×10−2MPa以上
上記試験片を2cm幅で切り出し、別途用意したアルミ板(2cm幅)を2cm×3cmの塗膜面に重ね、荷重1kg、200℃の条件下で、1時間保持した。重ね合わせた試験片を剥がした後のアルミ板の汚染度を以下の基準で目視評価した。
○:汚染無し
△:わずかに汚染
×:全面に汚染
HEIDON試験機を用いて、上記試験片の塗膜の傷発生荷重を測定し、以下の基準で評価した。
○:80g以上
△:60〜70g
×:40〜50g
実施例及び比較例で得られた非粘着処理用塗料組成物を25℃で24時間保管後に再分散し、100メッシュ金網でろ過し、ろ過残渣の濃度を測定し、以下の基準で評価した。
○:1質量%未満
△:2〜4質量%
×:5質量%以上
Claims (10)
- フッ素ゴム、加硫剤、固体潤滑剤及び有機溶剤を含み、
前記固体潤滑剤は、固体潤滑剤(A)と、前記固体潤滑剤(A)とは異なる固体潤滑剤(B)とを含むことを特徴とする塗料組成物。 - 前記固体潤滑剤(A)はフッ素樹脂である請求項1記載の塗料組成物。
- 前記固体潤滑剤(B)はグラファイト、二硫化モリブデン、二硫化タングステン、フッ化黒鉛及び窒化ホウ素からなる群より選択される少なくとも1種である請求項1又は2記載の塗料組成物。
- 前記フッ素ゴムと前記固体潤滑剤との質量比(フッ素ゴム/固体潤滑剤)が20/80〜80/20である請求項1〜3のいずれかに記載の塗料組成物。
- 前記固体潤滑剤(A)と前記固体潤滑剤(B)との質量比(固体潤滑剤(A)/固体潤滑剤(B))が50/50〜90/10である請求項1〜4のいずれかに記載の塗料組成物。
- 非粘着処理用塗料組成物である請求項1〜5のいずれかに記載の塗料組成物。
- エラストマー層の非粘着処理用塗料組成物である請求項1〜6のいずれかに記載の塗料組成物。
- 金属板と、
前記金属板の片面又は両面に設けられたエラストマー層と、
前記エラストマー層の上に設けられた、請求項1〜7のいずれかに記載の塗料組成物から形成された塗膜と
を有することを特徴とする塗装物品。 - 前記エラストマー層は、フッ素ゴム層である請求項8記載の塗装物品。
- フッ素ゴムコートガスケット材料である請求項8又は9記載の塗装物品。