JPWO2020090280A5 - - Google Patents
Download PDFInfo
- Publication number
- JPWO2020090280A5 JPWO2020090280A5 JP2020512898A JP2020512898A JPWO2020090280A5 JP WO2020090280 A5 JPWO2020090280 A5 JP WO2020090280A5 JP 2020512898 A JP2020512898 A JP 2020512898A JP 2020512898 A JP2020512898 A JP 2020512898A JP WO2020090280 A5 JPWO2020090280 A5 JP WO2020090280A5
- Authority
- JP
- Japan
- Prior art keywords
- cemented carbide
- powder
- total content
- ratio
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000000843 powder Substances 0.000 claims 11
- 229910052759 nickel Inorganic materials 0.000 claims 8
- 239000000956 alloy Substances 0.000 claims 5
- 229910045601 alloy Inorganic materials 0.000 claims 5
- 239000002994 raw material Substances 0.000 claims 5
- 239000002245 particle Substances 0.000 claims 4
- 150000001875 compounds Chemical class 0.000 claims 3
- 239000000463 material Substances 0.000 claims 2
- 239000011812 mixed powder Substances 0.000 claims 2
- 239000011248 coating agent Substances 0.000 claims 1
- 238000000576 coating method Methods 0.000 claims 1
- 239000000470 constituent Substances 0.000 claims 1
- 229910021480 group 4 element Inorganic materials 0.000 claims 1
- 229910021478 group 5 element Inorganic materials 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 238000013507 mapping Methods 0.000 claims 1
- 150000001247 metal acetylides Chemical class 0.000 claims 1
- 238000000465 moulding Methods 0.000 claims 1
- 230000000737 periodic effect Effects 0.000 claims 1
- 238000005245 sintering Methods 0.000 claims 1
Claims (8)
- 第1硬質相および結合相を含む超硬合金であって、
前記第1硬質相はWCからなり、
前記結合相は、Co、NiおよびCrの3種の元素、またはCo、Ni、CrおよびMoの4種の元素から構成され、
前記超硬合金中のCoの含有量をM1、前記超硬合金中のCrおよびMoの合計含有量をM2、前記超硬合金中のNi、CrおよびMoの合計含有量をM3、および前記超硬合金中のCo、Ni、CrおよびMoの合計含有量をM4と表したとき、
M4に対するM1の割合が15%以上50%以下であり、
M3に対するM2の割合が15%以上40%以下であり、
前記超硬合金中におけるCr/Moリッチ粒子の占める面積の割合が1%未満であり、
前記Cr/Moリッチ粒子は、前記超硬合金の断面の元素マッピングにおいて、CrおよびMoの少なくとも1つの濃度がM4に対するM2の割合よりも高い領域の構成粒子である、超硬合金。 - 周期表の第4族元素および第5族元素からなる群より選ばれる少なくとも1種の第1元素と、C、N、OおよびBからなる群より選ばれる少なくとも1種の第2元素と、の化合物からなる第2硬質相をさらに含む、請求項1に記載の超硬合金。
- 前記化合物は、炭化物である、請求項2に記載の超硬合金。
- 前記炭化物は、TiC、NbC、TaC、TaNbCおよびTiNbCから選択される少なくとも1種である、請求項3に記載の超硬合金。
- 前記第2硬質相を構成する前記化合物の平均粒子径は、0.1μm以上5μm以下である、請求項2から4のいずれか1項に記載の超硬合金。
- 請求項1から5のいずれか1項に記載の超硬合金からなる基材を備える切削工具。
- 前記基材の表面の少なくとも一部に被膜を備える、請求項6に記載の切削工具。
- 第1硬質相の原料粉末および結合相の原料粉末を混合して、混合粉末を調製する工程と、
前記混合粉末を加圧成形して成形体を調製する工程と、
前記成形体を焼結して超硬合金を作製する工程と、を備え、
前記第1硬質相の原料粉末はWC粉末であり、
前記結合相の原料粉末はCo粉末と合金粉末とを含み、
前記合金粉末は、NiとCrとからなる合金粉末およびNiとCrとMoとからなる合金粉末の少なくとも一方であり、
前記結合相の原料粉末において、Coの含有量をW1、CrおよびMoの合計含有量をW2、Ni、CrおよびMoの合計含有量をW3、Co、Ni、CrおよびMoの合計含有量をW4と表したとき、
W4に対するW1の割合が15%以上50%以下であり、
W3に対するW2の割合が15%以上40%以下である、超硬合金の製造方法。