JPS635993A - 感熱転写記録用色素及び感熱転写シート - Google Patents
感熱転写記録用色素及び感熱転写シートInfo
- Publication number
- JPS635993A JPS635993A JP61149740A JP14974086A JPS635993A JP S635993 A JPS635993 A JP S635993A JP 61149740 A JP61149740 A JP 61149740A JP 14974086 A JP14974086 A JP 14974086A JP S635993 A JPS635993 A JP S635993A
- Authority
- JP
- Japan
- Prior art keywords
- base film
- transfer sheet
- group
- material layer
- thermal transfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
[産業上の利用分野]
本発明は、昇華型感熱転写記録に使用される感熱転写シ
ートに関する。
ートに関する。
[従来の技術]
従来、ファクシミリプリンター、複写機あるいは、テレ
ビ画像等をカラー記録する技術が要望され、電子写真、
インクジェット、感熱転写等によるカラー記録技術が検
討されている。
ビ画像等をカラー記録する技術が要望され、電子写真、
インクジェット、感熱転写等によるカラー記録技術が検
討されている。
感熱転写記録方式は、装置の保守や操作が容易で、装置
や消耗品が安価であるため、他の方法に比べ有利と考え
られている。
や消耗品が安価であるため、他の方法に比べ有利と考え
られている。
感熱転写方式には、ベースフィルム上に熱溶融性インク
層を形成させた転写シートを、感熱ヘッドにより加熱し
て、該インクを溶融し、被記録体上に転写記録する溶融
方式と、ベースフィルム上に昇華性色素を含有するイン
ク層を形成させた転写シートを、感熱ヘツドにより加熱
して色素を昇華させ、被記録体上に転写記録する昇華方
式とがあるが、昇華方式は感熱ヘッドに与えるエネルギ
ーを変えることにより色素の昇華転写量を制御すること
ができるので、階調記録か容易となり、フルカラー記録
には特に有利と考えられている。
層を形成させた転写シートを、感熱ヘッドにより加熱し
て、該インクを溶融し、被記録体上に転写記録する溶融
方式と、ベースフィルム上に昇華性色素を含有するイン
ク層を形成させた転写シートを、感熱ヘツドにより加熱
して色素を昇華させ、被記録体上に転写記録する昇華方
式とがあるが、昇華方式は感熱ヘッドに与えるエネルギ
ーを変えることにより色素の昇華転写量を制御すること
ができるので、階調記録か容易となり、フルカラー記録
には特に有利と考えられている。
昇華方式の感熱転写記録においては、転写シー1〜に用
いられる昇華性色素は転写記録のスピード、記録物の画
質、保存安定性などに大ぎな影響を与え非常に重要でお
り、下記のような条件を満足する必要がある。
いられる昇華性色素は転写記録のスピード、記録物の画
質、保存安定性などに大ぎな影響を与え非常に重要でお
り、下記のような条件を満足する必要がある。
■ 感熱記録ヘッドの作動条件で容易に昇華すること。
■ 感熱記録ヘッドの作動条件で熱分解しないこと。
■ 色再現上、好ましい色相を有すること。
■ 分子吸光係数が大きいこと。
■ 熱、光、湿気、薬品などに対して安定なこと。
■ 合成が容易なこと。
■ インク化適・lか優れていること。
従来上記の条件を仝て満足りる色素は児い出されておら
ず特にシアン色素においては昇華し易く、色相□及び耐
光性の良好な色素は見い出されていない。
ず特にシアン色素においては昇華し易く、色相□及び耐
光性の良好な色素は見い出されていない。
[発明が解決しようとする問題点]
本発明は上記の条件を全て満足するシアン色素を用いた
感熱転写シートを提供することを目的としている。
感熱転写シートを提供することを目的としている。
[問題点を解決するための手段]
本発明は下記一般式[I]
(ただし上記式中、Rはアルキル基、置換アルキル基、
アラルキル基、アルケニル基、シクロアルキル基を表わ
す。)で示されるアントラキノン系色素を含む色材層を
ベースフィルム上に有することを特徴とする感熱転写シ
ートをその要旨とするものである。
アラルキル基、アルケニル基、シクロアルキル基を表わ
す。)で示されるアントラキノン系色素を含む色材層を
ベースフィルム上に有することを特徴とする感熱転写シ
ートをその要旨とするものである。
本発明の感熱転写シートに用いられる上記の色素の製造
方法としては、たとえば下記構造式[II] (式中、Rは前記定義に同じ) で示されるアントラキノン系化合物に、水媒中あるいは
有機溶媒中シアン化ナトリウムあるいはシアン化カリウ
ムなどのシアン化剤を反応させることにより得られる。
方法としては、たとえば下記構造式[II] (式中、Rは前記定義に同じ) で示されるアントラキノン系化合物に、水媒中あるいは
有機溶媒中シアン化ナトリウムあるいはシアン化カリウ
ムなどのシアン化剤を反応させることにより得られる。
本発明の感熱転写シートに用いられる前記一般式[I]
の色素の具体例としては、実施例に示したものなどが挙
げられるが、それらに限定されるものではない。
の色素の具体例としては、実施例に示したものなどが挙
げられるが、それらに限定されるものではない。
特に好ましいものとしては、前記一般式「I]において
、Rがアリル基、C1〜C8のアルキル基、C7〜C8
のアラルキル基、C3・−〇Bのアルコキシアルキル基
、シクロヘキシル基で示される色素が挙げられる。
、Rがアリル基、C1〜C8のアルキル基、C7〜C8
のアラルキル基、C3・−〇Bのアルコキシアルキル基
、シクロヘキシル基で示される色素が挙げられる。
本発明の感熱転写シートに上記の色素を適用する場合、
色素を結着剤とともに媒体中に溶解あるいは微粒子状に
分散させることによりインクを調製し、該インクをベー
スフィルム上に塗布、乾燥することによりベースフィル
ム上に色材層を形成する。
色素を結着剤とともに媒体中に溶解あるいは微粒子状に
分散させることによりインクを調製し、該インクをベー
スフィルム上に塗布、乾燥することによりベースフィル
ム上に色材層を形成する。
インク調製のための結着剤としては、セルロース系、ア
クリル酸系、デンプン系などの水溶性樹脂、アクリル樹
脂、メタクリル樹脂、ポリスチレン、ポリカーボネート
、ポリスルホン、ポリエーテルスルホン、エチルセルロ
ース、アセチルセルロースなどの有機溶剤あるいは水に
可溶性の樹脂などを挙げることができる。
クリル酸系、デンプン系などの水溶性樹脂、アクリル樹
脂、メタクリル樹脂、ポリスチレン、ポリカーボネート
、ポリスルホン、ポリエーテルスルホン、エチルセルロ
ース、アセチルセルロースなどの有機溶剤あるいは水に
可溶性の樹脂などを挙げることができる。
インク調製のための媒体としては水の他に、メチルアル
コール、イソプロピルアルコール、イソブチルアルコー
ルなどのアルコール類、メチルセロソルブ、エチルセロ
ソルブなどのセロソルブ類、トルエン、キシレン、クロ
ロベンゼンなどの芳香族類、酢酸エチル、酢酸プ゛チー
ル4丁どの二[ステル類、アセトン、メチルエチルケ[
−ン、メチルイソブチルケトン、シフ[1ヘニ1−ザノ
ンなどのケトン類、塩化メチレン、り]二10ボルム、
1〜リクロロエヂレンなどの塩素系溶剤、テトラヒドロ
フラン、ジオキリーンなとのエーテル類、N、N−ジメ
チルホルムアミド、N−メチルピロリドンなどの有)幾
溶剤を埜げることかできる。
コール、イソプロピルアルコール、イソブチルアルコー
ルなどのアルコール類、メチルセロソルブ、エチルセロ
ソルブなどのセロソルブ類、トルエン、キシレン、クロ
ロベンゼンなどの芳香族類、酢酸エチル、酢酸プ゛チー
ル4丁どの二[ステル類、アセトン、メチルエチルケ[
−ン、メチルイソブチルケトン、シフ[1ヘニ1−ザノ
ンなどのケトン類、塩化メチレン、り]二10ボルム、
1〜リクロロエヂレンなどの塩素系溶剤、テトラヒドロ
フラン、ジオキリーンなとのエーテル類、N、N−ジメ
チルホルムアミド、N−メチルピロリドンなどの有)幾
溶剤を埜げることかできる。
上記のインキ中には上記の成分の他に必要に応じて41
機、無機の非昇華性微粒子、分散剤、帯電防上剤、ブロ
ッキング防止剤、消泡剤、酸化防止剤、粘度調整剤など
を添加することもてきる。
機、無機の非昇華性微粒子、分散剤、帯電防上剤、ブロ
ッキング防止剤、消泡剤、酸化防止剤、粘度調整剤など
を添加することもてきる。
転写シー1ル作製のためのインクを塗布するベースフィ
ルムとしては、コンデンサー紙、グラシン紙のような薄
葉紙、ポリエステル、ポリアミド、ポリイミドのような
耐熱性の良好なプラスチックのフィルムが適しているが
、それらの厚さとしては3〜50μmの範囲を挙げるこ
とができる。
ルムとしては、コンデンサー紙、グラシン紙のような薄
葉紙、ポリエステル、ポリアミド、ポリイミドのような
耐熱性の良好なプラスチックのフィルムが適しているが
、それらの厚さとしては3〜50μmの範囲を挙げるこ
とができる。
インクをベースフィルムに塗布する方法としては、リバ
ースロールコータ−、グラビアコーター、ロッドコータ
ー、エアドクタコーターなどを使用して実施することが
でき、インキの塗布層の厚さは乾燥後0.1〜5μmの
範囲となるよう塗布すれば良い(原崎勇次著、槓書店1
979年発行「コーティング方式」)。
ースロールコータ−、グラビアコーター、ロッドコータ
ー、エアドクタコーターなどを使用して実施することが
でき、インキの塗布層の厚さは乾燥後0.1〜5μmの
範囲となるよう塗布すれば良い(原崎勇次著、槓書店1
979年発行「コーティング方式」)。
[作 用]
本発明の感熱転写シー1へに用いられる前記[工]で示
されるアントラキノン系色素は鮮明なシアン色を有する
ため、適当なイエロー色及びマゼンタ色と組み合せるこ
とにより色再現性の良好なフルカラー記録を得るのに適
しており、又、昇華し易く、分子吸光係数が大きいため
感熱ヘッドに大きな負担をかけることなく、高速で色濃
度の高い記録を得ることができる。更に熱、光、湿気、
薬品などに対して安定であるため、転写記録中に熱分解
することなく、得られた記録の保存性も優れている。特
(こ耐光性が優れているため、他のシアン色素を使用し
た場合には得られない優れた保存性の記録を得ることが
できる。
されるアントラキノン系色素は鮮明なシアン色を有する
ため、適当なイエロー色及びマゼンタ色と組み合せるこ
とにより色再現性の良好なフルカラー記録を得るのに適
しており、又、昇華し易く、分子吸光係数が大きいため
感熱ヘッドに大きな負担をかけることなく、高速で色濃
度の高い記録を得ることができる。更に熱、光、湿気、
薬品などに対して安定であるため、転写記録中に熱分解
することなく、得られた記録の保存性も優れている。特
(こ耐光性が優れているため、他のシアン色素を使用し
た場合には得られない優れた保存性の記録を得ることが
できる。
本発明の感熱転写シートは加熱手段としてリーーマルヘ
ットのみならず赤外線、レーザー尤なとも利用すること
かできる。
ットのみならず赤外線、レーザー尤なとも利用すること
かできる。
[実施例]
以下実施例によりこの発明を具体的に説明するか、かか
る実施例は本発明を限定するものではない。
る実施例は本発明を限定するものではない。
実施例1
a)インクの調製
(り[旧]小ルム中での吸収極大値644nm)上記本
発明のアントラキノン系色素 10(] 酢酸セルロース(ダイセル化学社製、 1.30) 1og メヂルエチルグトン 80g上記組成の混
合物をペイントコンディショナーで10分間処理し、イ
ンクの調製を行なった。
発明のアントラキノン系色素 10(] 酢酸セルロース(ダイセル化学社製、 1.30) 1og メヂルエチルグトン 80g上記組成の混
合物をペイントコンディショナーで10分間処理し、イ
ンクの調製を行なった。
b)転写シートの作製
上記(7) イ”、/ クヲハー 1−ター(RK P
r1ntCoat InStrumentS社製N0.
1)を用いてコンデンサー紙(10μm厚)上に塗布、
乾燥しく乾燥膜厚的1μm)、転写シートを得た。
r1ntCoat InStrumentS社製N0.
1)を用いてコンデンサー紙(10μm厚)上に塗布、
乾燥しく乾燥膜厚的1μm)、転写シートを得た。
C)転写記録
上記転写シートのインク塗布面を被記録体と重ね感熱ヘ
ッドを用い下記条件で記録し、鮮明なシアン色で1,2
0の均一な色S度の記録を得ることができた。
ッドを用い下記条件で記録し、鮮明なシアン色で1,2
0の均一な色S度の記録を得ることができた。
記録条件
主走査、副走査の線密度二 8ドツト/mm記録電カニ
0.25W/ドツト ヘッドの加熱時間: 10m5ec なお、被記録体は、飽和ポリエステル34重量%の水分
散液(東洋紡績株式会社製造、パイロナールM D−1
200、商品名)10(]とシリ力(日本シリカニ業株
式会社製造、N:ps:IE 220A、商品名)l+
を混合し調製した液をポリプロピレン合成紙(200μ
m厚〉にバーコーター(RK Pr1nt Coat
Instruments社製造、NO,3>を用いて塗
布後、乾燥して製造したものである。
0.25W/ドツト ヘッドの加熱時間: 10m5ec なお、被記録体は、飽和ポリエステル34重量%の水分
散液(東洋紡績株式会社製造、パイロナールM D−1
200、商品名)10(]とシリ力(日本シリカニ業株
式会社製造、N:ps:IE 220A、商品名)l+
を混合し調製した液をポリプロピレン合成紙(200μ
m厚〉にバーコーター(RK Pr1nt Coat
Instruments社製造、NO,3>を用いて塗
布後、乾燥して製造したものである。
色濃度は、米国マクベス社製造、デンシトメーターRD
−514型(フィルタm:うッテンN 0.25 )を
用いて測定した。
−514型(フィルタm:うッテンN 0.25 )を
用いて測定した。
得られた記録の耐光性試験をカーボンアークフェードメ
ーター(スガ試験機株式会社製造〉を用いて実施(ブラ
ックパネル温度63±2°C)したが、40時間の照射
後はとんど変退邑しなかった。また、転写シートおよび
記録は熱・湿気に耐して安定であり、暗所保存性にすぐ
れていた。
ーター(スガ試験機株式会社製造〉を用いて実施(ブラ
ックパネル温度63±2°C)したが、40時間の照射
後はとんど変退邑しなかった。また、転写シートおよび
記録は熱・湿気に耐して安定であり、暗所保存性にすぐ
れていた。
実施例2
実施例1で用いた色素のかわりに第1表に示す色素を用
い実施例1と同様の方法、でインクの調製、転写シート
の作製、転写記録を実施した結果、各々第1表に示す色
濃度の鮮明なシアン色の記録を得ることができた。
い実施例1と同様の方法、でインクの調製、転写シート
の作製、転写記録を実施した結果、各々第1表に示す色
濃度の鮮明なシアン色の記録を得ることができた。
得られた記録の耐光性は全て良好でおった。
Xクロロホルム中での測定値
[発明の効果]
以上説明したように、本発明の感熱転写シートを用いる
ことによって、濃度が高いシアン色の鮮明な画像で、し
かも熱、湿気に対しで安定、かつ、耐光性の大きい転写
画像を形成づ−ることができる。
ことによって、濃度が高いシアン色の鮮明な画像で、し
かも熱、湿気に対しで安定、かつ、耐光性の大きい転写
画像を形成づ−ることができる。
Claims (2)
- (1)ベースフィルム上に下記一般式[ I ]▲数式、
化学式、表等があります▼・・・・・・[ I ] ただし上記式中、 Rはアルキル基、置換アルキル基、アラルキル基、アル
ケニル基、シクロアルキル基を表わす。) で示されるアントラキノン系色素を含む色材層を有する
ことを特徴とする感熱転写シート。 - (2)特許請求の範囲第(1)項記載の一般式[ I ]
で示されるアントラキノン系色素において、Rがアリル
基、C_1〜C_8のアルキル基、C_7〜C_8のア
ラルキル基、C_3〜C_8のアルコキシアルキル基、
シクロヘキシル基を表わすアントラキノン系色素を含む
色材層を基体上に有する感熱転写シート。