JPS63264649A - 難燃性電気絶縁組成物 - Google Patents
難燃性電気絶縁組成物Info
- Publication number
- JPS63264649A JPS63264649A JP9899687A JP9899687A JPS63264649A JP S63264649 A JPS63264649 A JP S63264649A JP 9899687 A JP9899687 A JP 9899687A JP 9899687 A JP9899687 A JP 9899687A JP S63264649 A JPS63264649 A JP S63264649A
- Authority
- JP
- Japan
- Prior art keywords
- flame
- lubricant
- polyolefin
- insulating composition
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は、難燃性電気絶縁組成物に係り、特に燃焼時に
ハロゲンガスの発生がなく、シかも水に浸漬しても白色
の析出物を生じない難燃性電気絶縁組成物に関するもの
である。
ハロゲンガスの発生がなく、シかも水に浸漬しても白色
の析出物を生じない難燃性電気絶縁組成物に関するもの
である。
［従来の技術］
電線・ケーブルの絶縁材料やシース材料としては、電気
絶縁性にすぐれたポリオレフィンが多用されてきている
。最近の趨勢として、原子力発電所用電線・ケーブル、
車輛用電線および盤内・機内配線用電線等に難燃性を付
与することが強く要望されるようになってきたつ ポリオレフィンを難燃化する方法としては、ハロゲン含
有化合物、二酸化アンチモン、リン含有化合物などを混
和する方法が採用されてきたが、これらは燃焼時に多量
の煙を発生し、機器への腐食性、人体への有害性等が問
題になっている。特に、最近は安全面からハロゲン系ガ
スを発生しないことが強く要望されている。
絶縁性にすぐれたポリオレフィンが多用されてきている
。最近の趨勢として、原子力発電所用電線・ケーブル、
車輛用電線および盤内・機内配線用電線等に難燃性を付
与することが強く要望されるようになってきたつ ポリオレフィンを難燃化する方法としては、ハロゲン含
有化合物、二酸化アンチモン、リン含有化合物などを混
和する方法が採用されてきたが、これらは燃焼時に多量
の煙を発生し、機器への腐食性、人体への有害性等が問
題になっている。特に、最近は安全面からハロゲン系ガ
スを発生しないことが強く要望されている。
このような情勢を踏まえ、発煙性が非常に少なく、有害
なガスも発生しない水酸化アルミニウム、水酸化マグネ
シウムのような無機含水化合物を難燃剤として使用する
ことが注目されるようになってきた。
なガスも発生しない水酸化アルミニウム、水酸化マグネ
シウムのような無機含水化合物を難燃剤として使用する
ことが注目されるようになってきた。
［発明が解決しようとする問題点］
含水無機化合物を配合した樹脂組成物のロール加工性お
よび押出加工性を向上する目的から滑剤としてステアリ
ン酸あるいはその金属塩を添加しているが、成形品を水
道水などに浸漬すると表面に白色物が析出し、外観を損
ねるという問題がある。
よび押出加工性を向上する目的から滑剤としてステアリ
ン酸あるいはその金属塩を添加しているが、成形品を水
道水などに浸漬すると表面に白色物が析出し、外観を損
ねるという問題がある。
本発明は上記に基づいてなされたもので、燃焼時の有毒
ガスの発生を抑止でき、しかも水に浸漬した場合でも白
色の析出物が生じない難燃性電気絶縁組成物の提供を目
的とするものである。
ガスの発生を抑止でき、しかも水に浸漬した場合でも白
色の析出物が生じない難燃性電気絶縁組成物の提供を目
的とするものである。
［問題点を解決するための手段］
本発明の難燃性電気絶縁組成物は、ポリオレフィンおよ
び無機含水化合物を含む組成物に滑剤として分子中に水
酸基を有する脂肪酸またはその金属塩を配合してなるこ
とを特徴とするものである。
び無機含水化合物を含む組成物に滑剤として分子中に水
酸基を有する脂肪酸またはその金属塩を配合してなるこ
とを特徴とするものである。
本発明において、ポリオレフィンとしては、ポリエチレ
ン、ポリプロピレン、ポリブテン、ポリメチルペンテン
−１等のα−オレフィン、エチレンプロピレンコポリマ
、エチレンプロピレンジェンターポリマ、ポリエチレン
、エチレン酢酸ビニルコポリマ、エチレンエチルアクリ
レートコポリマ、エチレンブテンコポリマ、エチレンブ
テンジェンターポリマ等のエチレン系共重合体などがあ
げられ、これらは単独使用あるいは２種類以上の併用が
可能ある。
ン、ポリプロピレン、ポリブテン、ポリメチルペンテン
−１等のα−オレフィン、エチレンプロピレンコポリマ
、エチレンプロピレンジェンターポリマ、ポリエチレン
、エチレン酢酸ビニルコポリマ、エチレンエチルアクリ
レートコポリマ、エチレンブテンコポリマ、エチレンブ
テンジェンターポリマ等のエチレン系共重合体などがあ
げられ、これらは単独使用あるいは２種類以上の併用が
可能ある。
無機含水化合物としては、水酸化アルミニウム、水酸化
マグネシウム、塩基性炭酸マグネシウム、ハイドロタル
サイ！・類等があげられる。これらの無機含水化合物は
必要に応じ、吸水吸湿の防止のため脂肪酸、脂肪酸金属
塩、シランカップリング剤、チタネー）・カップリング
剤等で表面処理したものを使用してもよい。無機含水化
合物はポリオレフィン１００重量部に対して５０〜３０
０重量部程度配合することが好ましく、５０重量部未満
では難燃性が不十分となり、３００重世部を越えると押
出加工性や機械的強度が低下する傾向にある。
マグネシウム、塩基性炭酸マグネシウム、ハイドロタル
サイ！・類等があげられる。これらの無機含水化合物は
必要に応じ、吸水吸湿の防止のため脂肪酸、脂肪酸金属
塩、シランカップリング剤、チタネー）・カップリング
剤等で表面処理したものを使用してもよい。無機含水化
合物はポリオレフィン１００重量部に対して５０〜３０
０重量部程度配合することが好ましく、５０重量部未満
では難燃性が不十分となり、３００重世部を越えると押
出加工性や機械的強度が低下する傾向にある。
分子中に水酸基を有する脂肪酸またはその金属塩として
は、ヒドロキシカプリン酸、ヒドロキシウンデジノン酸
、ヒドロキシパルミチン酸、ヒドロキシステアリン酸、
リシノール酸あるいはこれらの金属塩があげられ、金属
としてはＣａ、 Ｌｉ、 Ｚｎ。
は、ヒドロキシカプリン酸、ヒドロキシウンデジノン酸
、ヒドロキシパルミチン酸、ヒドロキシステアリン酸、
リシノール酸あるいはこれらの金属塩があげられ、金属
としてはＣａ、 Ｌｉ、 Ｚｎ。
Ｂａ、 Ｐｂ等がある。これらは、ポリオレフィン１０
０重量部に対して０．２〜５重量部程度添加することが
好ましい。
０重量部に対して０．２〜５重量部程度添加することが
好ましい。
本発明においては、上記成分に加えて充填剤、酸化防止
剤、軟化剤、分散剤等を適宜添加してもよい。
剤、軟化剤、分散剤等を適宜添加してもよい。
以下、本発明の実施例を比較例と対比しながら説明する
。
。
第１表に示すような配合に従い各種成分を６インチオー
プンロール（スチーム加熱）を用いて約１０００Ｃ混練
する。混練物を１．２ｍｍ程度にシート出し後、１５０
°Ｃに設定したプレスにて５分間加熱し、約１ｍｍ厚の
シートを作製した。
プンロール（スチーム加熱）を用いて約１０００Ｃ混練
する。混練物を１．２ｍｍ程度にシート出し後、１５０
°Ｃに設定したプレスにて５分間加熱し、約１ｍｍ厚の
シートを作製した。
ロール加工性およびシートの白色析出物の有無について
評価した結果を第１表の下欄に示した。なお、析出物の
有無の評価は約１ｍｍ厚のシートを２０Ｘ５０ｍｍの大
きさにし、直径２５ ｍ ｍの試験管に入れてこれに水
道水８０ｃｃ満たし、９０℃の恒温槽に２日間放置後、
目視により白色析出物の有無を観察した。
評価した結果を第１表の下欄に示した。なお、析出物の
有無の評価は約１ｍｍ厚のシートを２０Ｘ５０ｍｍの大
きさにし、直径２５ ｍ ｍの試験管に入れてこれに水
道水８０ｃｃ満たし、９０℃の恒温槽に２日間放置後、
目視により白色析出物の有無を観察した。
■第１表から明らかな通り、本発明に係る実施例〜６で
は、いずれもロール加工性に優れ、しかも浸水による白
色析出物の発生がない。これに対し、ステアリン酸、ス
テアリン酸金属塩を用いた比較例１〜４ではロール加工
性は良いものの白色析出物が発生した。比較例５は滑剤
としてパラフィンワックスを用いたもので、白色析出物
の発生はないが、ロール加工性が悪い。
は、いずれもロール加工性に優れ、しかも浸水による白
色析出物の発生がない。これに対し、ステアリン酸、ス
テアリン酸金属塩を用いた比較例１〜４ではロール加工
性は良いものの白色析出物が発生した。比較例５は滑剤
としてパラフィンワックスを用いたもので、白色析出物
の発生はないが、ロール加工性が悪い。
［発明の効果］
以上説明してきた通り、本発明によれば燃焼時の有毒カ
スの発生を抑止でき、しかも水に浸漬した場合でも白色
の析出物が生じない難燃性電気絶縁組成物が得られるよ
うになる。
スの発生を抑止でき、しかも水に浸漬した場合でも白色
の析出物が生じない難燃性電気絶縁組成物が得られるよ
うになる。
Claims (1)
- （１）ポリオレフィンに無機含水化合物および滑剤を配
合してなり、該滑剤として分子中に水酸基を有する脂肪
酸またはその金属塩を用いてなることを特徴とする難燃
性電気絶縁組成物。