JPS6241104B2 - - Google Patents
Info
- Publication number
- JPS6241104B2 JPS6241104B2 JP54069721A JP6972179A JPS6241104B2 JP S6241104 B2 JPS6241104 B2 JP S6241104B2 JP 54069721 A JP54069721 A JP 54069721A JP 6972179 A JP6972179 A JP 6972179A JP S6241104 B2 JPS6241104 B2 JP S6241104B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- film
- plastic molded
- component
- cured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は、優れた表面硬度と金属の薄層皮膜に
よる金属性外観とを有し、しかも耐熱性において
も優れた性質を具備するプラスチツク成形品とそ
の製造方法とに関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a plastic molded product that has excellent surface hardness and a metallic appearance due to a thin metal coating, and also has excellent heat resistance properties, and a method for producing the same. It is something.
プラスチツク成形品に金属性外観を付与するた
めに、プラスチツク成形品の外表面に、真空蒸
着、スパツタリング、イオンプレーテイング等の
方向で金属の薄層皮膜を形成させることは公知で
あるが、この金属の薄層皮膜は、その表面に成形
品同士の擦れ合い等による擦り傷が生じ易く、成
形品の商品価値の低下の要因となつている。 In order to give a plastic molded product a metallic appearance, it is known to form a thin layer of metal on the outer surface of the plastic molded product by vacuum evaporation, sputtering, ion plating, etc. The thin layer film is prone to scratches on its surface due to molded products rubbing against each other, which is a factor in reducing the commercial value of molded products.
本第１の発明は、耐熱性樹脂を材料とするプラ
スチツク成形品と、該成形品の外表面に直接形成
されている高度の架橋結合を有する硬化樹脂皮膜
からなるアンダーコーテイング層と、該アンダー
コーテイング層面に形成されている金属の薄層皮
膜と、前記金属の薄層皮膜面に直接形成されてい
るところの二液型アクリル系樹脂、二液型ウレタ
ン系樹脂、及び二液型エポキシ系樹脂の中から選
択される二液型の樹脂による硬化皮膜からなるプ
ライマー層と、該プライマー層面に形成されてい
る高度の架橋結合を有する透明な硬化樹脂皮膜と
からなる硬質表面を有する金属化プラスチツク成
形品とすることにより、金属の薄層皮膜による金
属性外観を呈し、かつ優れた表面硬度を有し、し
かも耐熱性においても優れた性質を具備するプラ
スチツク成形品を提供し得たものである。 The first invention provides a plastic molded article made of a heat-resistant resin, an undercoating layer consisting of a cured resin film with a high degree of crosslinking formed directly on the outer surface of the molded article, and a plastic molded article made of a heat-resistant resin. A thin metal film formed on the surface of the layer, and a two-part acrylic resin, a two-part urethane resin, and a two-part epoxy resin formed directly on the surface of the thin metal film. A metallized plastic molded product having a hard surface consisting of a primer layer made of a cured film made of a two-component resin selected from among the above, and a transparent cured resin film with a high degree of crosslinking formed on the surface of the primer layer. By doing so, it was possible to provide a plastic molded article that exhibits a metallic appearance due to a thin metal film, has excellent surface hardness, and also has excellent heat resistance properties.
また、本第２の発明は、予め成形されている耐
熱性樹脂を材料とするプラスチツク成形品の外表
面に、ジフエニルジサルフアイド、ベンゾイン、
ベンジル、あるいはベンゾインメチルエーテル等
の光増感剤を含有している硬質皮膜形成能を有す
る樹脂塗料を塗布し、次いでこの塗布面に紫外線
照射処理を行なつて硬化樹脂皮膜からなるアンダ
ーコーテイング層を形成し、しかる後に、該アン
ダーコーテイング層の表面に真空蒸着、スパツタ
リング、イオンブレーテイング等の方法で金属を
薄層皮膜を形成し、さらに、該金属の薄層皮膜面
に、二液型アクリル系樹脂、二液型ウレタン系樹
脂、及び二液型エポキシ系樹脂の中から選択され
る二液型の樹脂による塗料を塗布して該樹脂によ
る硬化皮膜からなるプライマー層を形成し、次い
でこのプライマー層の表面に、ジフエニルジサル
フアイド、ベンゾイン、ベンジル、あるいはベン
ゾインメチルエーテル等の光増感剤を含有してい
る透明な硬化皮膜形成能を有する樹脂塗料を塗布
し、引き続いてこの塗装面に、紫外線照射処理を
行なうことからなる金属化プラスチツク成形品の
製造方法とすることにより、前記第１の発明の硬
質表面を有する金属化プラスチツク成形品を、確
実に、かつ量産し得る方法を提供し得たものであ
る。 Further, the second invention provides diphenyl disulfide, benzoin,
A resin paint containing a photosensitizer such as benzyl or benzoin methyl ether and capable of forming a hard film is applied, and then the coated surface is subjected to ultraviolet irradiation treatment to form an undercoating layer consisting of a hardened resin film. After that, a thin metal film is formed on the surface of the undercoating layer by a method such as vacuum evaporation, sputtering, or ion brating, and then a two-component acrylic film is applied to the surface of the thin metal film. A paint made of a two-component resin selected from resin, two-component urethane resin, and two-component epoxy resin is applied to form a primer layer consisting of a cured film of the resin, and then this primer layer A resin coating containing a photosensitizer such as diphenyl disulfide, benzoin, benzyl, or benzoin methyl ether and having the ability to form a transparent cured film is applied to the surface of the coating, and subsequently, on this coated surface, By providing a method for producing a metallized plastic molded article that includes ultraviolet irradiation treatment, it is possible to provide a method that can reliably and mass-produce the metallized plastic molded article having a hard surface according to the first invention. It is something that
以下図示実施例に基づいて本各発明の金属化プ
ラスチツク成形品とその製造方法との構成を説明
する。 The constructions of the metallized plastic molded products of the present invention and their manufacturing methods will be explained below based on the illustrated embodiments.
図は耐熱性樹脂を材料とする容器形状のプラス
チツク成形品における本第１の発明の実施例品を
示すものであり、第１図は硬質表面を有する金属
化プラスチツク成形品の正面図、第２図は第１図
に示される金属化プラスチツク成形品たる容器形
状のプラスチツク成形品の容器胴部の一部拡大断
面図である。 The figures show an embodiment of the first invention, which is a container-shaped plastic molded article made of heat-resistant resin. This figure is a partially enlarged sectional view of the container body of the container-shaped plastic molded product shown in FIG. 1, which is a metallized plastic molded product.
硬質表面を有する金属化プラスチツク成形品１
は、容器口部２と容器胴部３と底部４とからなる
容器形状をなすものであり、容器胴部３と底部４
が第２図に示される通りの層構成によつて形成さ
れている。 Metalized plastic molded product with hard surface 1
has a container shape consisting of a container opening 2, a container body 3, and a bottom 4.
is formed by the layer structure shown in FIG.
すなわち、容器胴部３と底部４との層構成は、
素材たる耐熱性樹脂を材料とする容器形状のプラ
スチツク成形品の容器壁５の外表面に、高度の架
橋結合が導入された硬化樹脂皮膜からなるアンダ
ーコーテイング層６を介して金属の薄層皮膜７が
一体に形成されており、この金属の薄層皮膜７の
外表面に、二液型アクリル系樹脂、二液型ウレタ
ン系樹脂、及び二液型エポキシ系樹脂の中から選
択される二液型の樹脂による硬化皮膜からなるプ
ライマー層８を介して高度の架橋結合が導入され
た透明な硬化樹脂皮膜９が一体に形成された構成
とされているものである。 That is, the layer structure of the container body 3 and bottom 4 is as follows:
A thin metal film 7 is applied to the outer surface of the container wall 5 of a container-shaped plastic molded product made of heat-resistant resin as a raw material, via an undercoating layer 6 consisting of a cured resin film with a high degree of cross-linking. is integrally formed, and on the outer surface of this thin metal film 7, a two-part type acrylic resin, a two-part urethane resin, and a two-part epoxy resin are applied. The transparent cured resin film 9 is integrally formed with a high degree of crosslinking through a primer layer 8 made of a cured resin film.
このため、容器形状をなすプラスチツク成形品
１の容器胴部３と底部４との外表面に、金属の薄
層皮膜７と該薄層皮膜７を被覆している透明な硬
化樹脂皮膜９が一体に積層された構成とされてお
り、金属の薄層皮膜７が透明な硬化樹脂皮膜９を
通して視認できるので、プラスチツク成形品１は
金属外観を呈し、その表面が優れた表面硬度を有
するものとなつており、しかも耐熱性においても
優れた性質を奏するというプラスチツク成形品１
の素材たる耐熱性樹脂を材料とするプラスチツク
成形品本来の性質をもそのまま具備するものであ
る。 For this reason, a thin metal film 7 and a transparent cured resin film 9 covering the thin film 7 are integrally formed on the outer surfaces of the container body 3 and bottom 4 of the container-shaped plastic molded product 1. The thin metal film 7 is visible through the transparent cured resin film 9, so the plastic molded product 1 has a metallic appearance and its surface has excellent surface hardness. A plastic molded product that has excellent properties in terms of heat resistance and heat resistance.
It also has the original properties of plastic molded products made from the heat-resistant resin that is the raw material.
以上の実施例においては、素材たる耐熱性樹脂
を材料とする容器形状のプラスチツク成形品の容
器胴部と底部との全外表面に金属の薄層皮膜と透
明な硬化樹脂皮膜との積層構成を適用した例を示
したが、素材たるプラスチツク成形品の所望の外
表面のみに、部分的に、例えば模様状に、金属の
薄層皮膜と透明な硬化樹脂皮膜との積層構成を適
用することも可能である。 In the above embodiment, a laminated structure of a thin metal film and a transparent cured resin film is applied to the entire outer surface of the container body and bottom of a container-shaped plastic molded product made of heat-resistant resin. Although an application example is shown, it is also possible to apply a laminated structure of a thin metal film and a transparent cured resin film partially, for example, in a pattern, only to the desired outer surface of the plastic molded product. It is possible.
上述の実施例における構成を有する容器形状を
なす硬質表面を有する金属化プラスチツク成形品
は次に説明する製造方法によつて製造される。 A container-shaped metallized plastic molded article having a hard surface having the structure in the above-described embodiment is manufactured by the manufacturing method described below.
すなわち、第１工程として、耐熱性樹脂を材料
とする素材たる容器形状のプラスチツク成形品を
公知の方法で製作する。 That is, as a first step, a container-shaped plastic molded article made of heat-resistant resin is manufactured by a known method.
第２工程として、前記得られた容器形状のプラ
スチツク成形品の容器胴部と底部との外表面に、
ジフエニルジサルフアイド、ベンゾイン、ベンジ
ル、あるいはベンゾインメチルエーテル等の光増
感剤が添加されている硬化皮膜形成能を有する合
成樹脂による塗料を塗布した後、この塗布面に紫
外線照射処理を行なうことにより、高度の架橋結
合を有する硬化樹脂皮膜からなるアンダーコーテ
イング層を形成する。 As a second step, on the outer surfaces of the container body and bottom of the obtained container-shaped plastic molded product,
After applying a paint made from a synthetic resin that has the ability to form a cured film and containing a photosensitizer such as diphenyl disulfide, benzoin, benzyl, or benzoin methyl ether, the coated surface is subjected to ultraviolet irradiation treatment. As a result, an undercoating layer consisting of a cured resin film having a high degree of crosslinking is formed.
第３工程として、前記第２工程で形成したアン
ダーコーテイング層たる硬化樹脂皮膜の表面に、
アルミニウム、スズ、クロム合金、ステンレスス
チール等の金属の薄層皮膜を、真空蒸着、スパツ
タリング、イオンプレーテイング等の方法で形成
し、引き続いて、第４工程として、前記第３工程
で形成した金属の薄層皮膜の表面に、硬化剤を含
有する所謂二液型アクリル系樹脂、二液型ウレタ
ン系樹脂、及び二液型エポキシ系樹脂の中から選
択される二液型の樹脂を成分とする塗料を塗布
し、これを熱風乾燥等によつて乾燥し、前記樹脂
による硬化皮膜からなるプライマー層を形成す
る。 As a third step, on the surface of the cured resin film that is the undercoating layer formed in the second step,
A thin film of metal such as aluminum, tin, chromium alloy, stainless steel, etc. is formed by a method such as vacuum evaporation, sputtering, or ion plating, and then, as a fourth step, the metal formed in the third step is A paint containing a two-component resin selected from two-component acrylic resins, two-component urethane resins, and two-component epoxy resins containing a hardening agent on the surface of the thin film. is applied and dried by hot air drying or the like to form a primer layer consisting of a cured film of the resin.
第５工程として、前記第４工程で形成した樹脂
の硬化皮膜によるプライマー層の表面に、ジフエ
ニルジサルフアイド、ベンゾイン、ベンジル、あ
るいはベンゾインメチルエーテル等の光増感剤が
添加されているところの、透明な硬質皮膜形成能
を有する樹脂による塗料を塗布した後、この塗布
面に紫外線照射処理を行なうことによつて高度の
架橋結合が導入されている透明な硬化樹脂皮膜を
形成するものである。 As a fifth step, a photosensitizer such as diphenyl disulfide, benzoin, benzyl, or benzoin methyl ether is added to the surface of the primer layer formed by the cured resin film formed in the fourth step. After applying a resin paint that has the ability to form a transparent hard film, the coated surface is irradiated with ultraviolet rays to form a transparent cured resin film with a high degree of crosslinking. .
図示実施例に基づく本各発明の硬質表面を有す
る金属化プラスチツク成形品及びその製造方法の
構成は叙上の通りの構成から成るものであり、素
材として使用される耐熱性樹脂を材料とするプラ
スチツク成形品は、例えば耐熱性ABS樹脂、耐
熱性アクリル樹脂、ユリヤ樹脂、フエノール樹
脂、メラミン樹脂等を材料とするプラスチツク成
形品であり、素材たるプラスチツク成形品は、そ
れ自体が耐熱性に優れた性質を有するものであ
る。 The structure of the metallized plastic molded product having a hard surface and the method for manufacturing the same according to the present invention based on the illustrated embodiments is as described above, and the metallized plastic molded product having a hard surface and the manufacturing method thereof are as described above. The molded product is a plastic molded product made of heat-resistant ABS resin, heat-resistant acrylic resin, urea resin, phenolic resin, melamine resin, etc. The plastic molded product itself has excellent heat resistance. It has the following.
第２工程で、素材たるプラスチツク成形品の外
表面にアンダーコーテイング層を形成する際に使
用される硬化皮膜形成能を有する合成樹脂は、第
５工程で使用される硬質皮膜形成能を有する樹脂
と同様のものが利用されるが、この第２工程で使
用されるものは、特に形成される皮膜における透
明性を不可欠な要件として具備するものではな
い。なお、このアンダーコーテイング層を欠除す
る場合には、金属皮膜はクロステープカツト試験
で剥離してしまうような結合強度の小さい金属の
積層皮膜しか形成することができず、耐熱性樹脂
を材料とするプラスチツク成形品からなる素材の
表面の薄層皮膜を強固、一体に形成させることは
不可能となる。 The synthetic resin with hard film-forming ability used in the second step to form an undercoating layer on the outer surface of the plastic molded product is the same as the resin with hard film-forming ability used in the fifth step. Although similar materials can be used, those used in this second step do not particularly have transparency in the formed film as an essential requirement. In addition, if this undercoating layer is omitted, the metal film can only be formed as a laminated film of metal with low bonding strength that peels off in the cross tape cut test, and heat-resistant resin is used as the material. It becomes impossible to form a thin film on the surface of a material made of plastic molded products in a strong and integral manner.
第４工程で、金属の薄層皮膜の表面にプライマ
ー層として形成される二液型アクリル系樹脂、二
液型ウレタン系樹脂、及び二液型エポキシ系樹脂
の中から選択される二液型の樹脂による硬化皮膜
は、第３工程で形成された金属の薄層皮膜の表面
に、高度の架橋結合を有する透明な硬化樹脂皮膜
を一体に形成されるために必要な中間層であつ
て、このプライマー層を欠除する場合には、金属
の薄層皮膜の表面に直接高度の架橋結合が導入さ
れた硬化樹脂皮膜を強固、一体に形成することは
不可能である。 In the fourth step, a two-component acrylic resin, a two-component urethane resin, and a two-component epoxy resin are formed as a primer layer on the surface of the thin metal film. The cured resin film is a necessary intermediate layer in order to integrally form a transparent cured resin film with a high degree of crosslinking on the surface of the thin metal film formed in the third step. When the primer layer is omitted, it is impossible to form a strong and integral cured resin film with a high degree of crosslinking directly on the surface of the thin metal film.
また、第５工程で使用される硬質皮膜形成能と
透明皮膜形成能とを兼備する樹脂としては、不飽
和ポリエステル樹脂、アクリル系樹脂、アルキツ
ド系樹脂、エポキシ系樹脂、ウレタン系樹脂、お
よびそれぞれの変性樹脂あるいはこれらの共重合
樹脂等が使用される。 In addition, the resins that have both hard film-forming ability and transparent film-forming ability used in the fifth step include unsaturated polyester resins, acrylic resins, alkyd resins, epoxy resins, urethane resins, and their respective Modified resins or copolymer resins thereof are used.
更に、第２工程および第５工程における紫外線
照射処理は、200〜600nm程度の波長を有する高
圧水銀ランプやメタルハライドランプ等を使用し
たものが利用される。 Further, the ultraviolet irradiation treatment in the second step and the fifth step uses a high-pressure mercury lamp, metal halide lamp, or the like having a wavelength of about 200 to 600 nm.
以上、本発明に係る硬質表面を有する金属化プ
ラスチツク成形品およびその製造方法を、容器形
状をなすプラスチツク成形品の例に基づいて説明
したが、本発明はかかる容器形状のプラスチツク
成形品に限定されるものではなく、例えば容体に
施蓋されるキヤツプ形状のプラスチツク成形品を
はじめ、一般の形状のプラスチツク成形品全般に
ついて適用できるものである。 Above, the metallized plastic molded article with a hard surface and the manufacturing method thereof according to the present invention have been explained based on the example of a container-shaped plastic molded article, but the present invention is limited to such a container-shaped plastic molded article. The present invention is applicable to general plastic molded products in general shapes, including, for example, cap-shaped plastic molded products that are placed on containers.
本第１の発明の硬質表面を有する金属化プラス
チツク成形品は、アンダーコーテイング層とプラ
イマー層との存在により、耐熱性樹脂を材料とす
るプラスチツク成形品からなる素材の外表面に、
金属の薄層皮膜と高度の架橋結合を有する硬化樹
脂皮膜とを強固、一体に積層せしめた、積層強度
の大きな成形品たらしめることができるし、また
成形品自体は金属様の装飾を有する外観を呈し、
その表面はステンレスウールで擦つても、あるい
は硬度3H〜4H程度のシヤープな鉛筆芯で擦過し
ても傷跡が付かない程の優れた硬度を有し、しか
も、素材たるプラスチツク成形品が具備する優れ
た耐熱性をそのまま具備するという効果を有する
ものである。また、本第２の発明の方法は、アン
ダーコーテイング層の存在により、耐熱性樹脂を
材料とするプラスチツク成形品の外表面に金属の
薄層皮膜を強固、一体に形成させることができ、
またプライマー層の存在により、プラスチツク成
形品の外表面に一体に強固に積層されている金属
の薄層皮膜面に、優れた硬質表面を有する透明な
樹脂皮膜を強固、一体に形成させることができ、
本第１の発明の金属化プラスチツク成形品を確実
に製造することができるし、またアンダーコーテ
イング層の形成および最外層たる透明な硬質表面
を有する樹脂皮膜の形成に際しては、紫外線照射
処理による硬化作用を利用しているので、短時間
内の硬化時間で所望の硬化樹脂皮膜を形成させる
ことができ、量産を行なうことができる等の効果
を有する。 The metallized plastic molded article with a hard surface of the first invention has an undercoating layer and a primer layer, so that on the outer surface of the plastic molded article made of heat-resistant resin,
A thin metal film and a cured resin film with a high degree of cross-linking are laminated together to form a molded product with high lamination strength, and the molded product itself has a metal-like decorative appearance. exhibits,
Its surface has such excellent hardness that it will not leave any scratches even when rubbed with stainless steel wool or sharp pencil lead with a hardness of 3H to 4H. This has the effect of providing heat resistance as is. Further, the method of the second invention allows a thin metal film to be formed firmly and integrally on the outer surface of a plastic molded product made of heat-resistant resin due to the presence of the undercoating layer.
Additionally, due to the presence of the primer layer, a transparent resin film with an excellent hard surface can be firmly and integrally formed on the surface of the thin metal film that is firmly and integrally laminated on the outer surface of the plastic molded product. ,
The metallized plastic molded article of the first invention can be reliably produced, and when forming the undercoating layer and the resin film having a transparent hard surface as the outermost layer, the curing effect is achieved by ultraviolet irradiation treatment. Since a desired cured resin film can be formed in a short curing time, mass production can be carried out.
第１図は本第１の発明の硬質表面を有する金属
化プラスチツク成形品の一例たる容器形状のプラ
スチツク成形品の正面図、第２図は第１図に示さ
れる容器形状の容器胴部の一部拡大断面図であ
る。
１：硬質表面を有する金属化プラスチツク成形
品、２：容器口部、３：容器胴部、４：底部、
５：素材たるプラスチツク成形品の容器壁、６：
アンダーコーテイング層、７：金属の薄層皮膜、
８：プライマー層、９：透明な硬化樹脂皮膜。
FIG. 1 is a front view of a container-shaped plastic molded product, which is an example of a metallized plastic molded product with a hard surface according to the first invention, and FIG. 2 is a front view of a container-shaped container body shown in FIG. 1. FIG. 1: metallized plastic molded product with a hard surface, 2: container mouth, 3: container body, 4: bottom,
5: Container wall made of plastic molded material, 6:
Undercoating layer, 7: thin metal film,
8: Primer layer, 9: Transparent cured resin film.
Claims (1)
の外表面に、高度の架橋結合を有する硬化樹脂皮
膜からなるアンダーコーテイング層を介して金属
の薄層皮膜が一体に形成されており、この金属の
薄層皮膜の外表面に、高度の架橋結合を有する透
明な硬化樹脂皮膜が、二液型アクリル系樹脂、二
液型ウレタン系樹脂、及び二液型エポキシ系樹脂
の中から選択された二液型の樹脂による硬化皮膜
からなるプライマー層を介して一体に形成されて
いることを特徴とする硬質表面を有する金属化プ
ラスチツク成形品。 ２ 予め成形されている耐熱性樹脂を材料とする
プラスチツク成形品の外表面に、ジフエニルジサ
ルフアイド、ベンゾイン、ベンジル、あるいはベ
ンゾインメチルエーテル等の光増感剤を含有して
いる硬質皮膜形成能を有する樹脂塗料を塗布し、
次いでこの塗布面に紫外線照射処理を行なつて硬
化樹脂皮膜からなるアンダーコーテイング層を形
成し、しかる後に、該アンダーコーテイング層の
表面に真空蒸着、スパツタリング、イオンプレー
テイング等の方法で金属の薄層皮膜を形成し、さ
らに、該金属の薄層皮膜面に、二液型アクリル系
樹脂、二液型ウレタン系樹脂、及び二液型エポキ
シ系樹脂の中から選択される二液型の樹脂による
塗料を塗布して該樹脂による硬化皮膜からなるプ
ライマー層を形成し、次いでこのプライマー層の
表面に、ジフエニルジサルフアイド、ベンゾイ
ン、ベンジル、あるいはベンゾインメチルエーテ
ル等の光増感剤を含有している透明な硬質皮膜形
成能を有する樹脂塗料を塗布し、引き続いてこの
塗装面に、紫外線照射処理を行なうことを特徴と
する硬質表面を有する金属化プラスチツク成形品
の製造方法。[Scope of Claims] 1. A thin metal film is integrally formed on the outer surface of a plastic molded product made of heat-resistant resin with an undercoating layer made of a cured resin film having a high degree of crosslinking. On the outer surface of this thin metal film, a transparent cured resin film with a high degree of cross-linking is applied to a resin selected from two-part acrylic resin, two-part urethane resin, and two-part epoxy resin. A metallized plastic molded article having a hard surface, characterized in that it is integrally formed with a primer layer consisting of a cured film made of a selected two-component resin. 2. Ability to form a hard film containing a photosensitizer such as diphenyl disulfide, benzoin, benzyl, or benzoin methyl ether on the outer surface of a pre-formed plastic molded product made of heat-resistant resin. Apply a resin paint with
This coated surface is then subjected to ultraviolet irradiation treatment to form an undercoating layer made of a cured resin film, and then a thin metal layer is formed on the surface of the undercoating layer by a method such as vacuum evaporation, sputtering, or ion plating. A coating is formed on the thin film surface of the metal using a two-component resin selected from two-component acrylic resins, two-component urethane resins, and two-component epoxy resins. is applied to form a primer layer consisting of a cured film of the resin, and then a photosensitizer such as diphenyl disulfide, benzoin, benzyl, or benzoin methyl ether is contained on the surface of this primer layer. A method for producing a metallized plastic molded article having a hard surface, which comprises applying a resin paint having the ability to form a transparent hard film, and subsequently subjecting the coated surface to ultraviolet irradiation treatment.