JPS62233287A - 光学的情報記録媒体 - Google Patents
光学的情報記録媒体Info
- Publication number
- JPS62233287A JPS62233287A JP61075980A JP7598086A JPS62233287A JP S62233287 A JPS62233287 A JP S62233287A JP 61075980 A JP61075980 A JP 61075980A JP 7598086 A JP7598086 A JP 7598086A JP S62233287 A JPS62233287 A JP S62233287A
- Authority
- JP
- Japan
- Prior art keywords
- group
- information recording
- different
- recording medium
- recording layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、レーザー光線によって情報を記録、再生する
ことのできる光学的情報記録媒体に関するものであり、
更に詳しくは、特定のナフタロシアニン化合物を含有す
る情報記録層をもつ光学的情報記録媒体に関するもので
ある。
ことのできる光学的情報記録媒体に関するものであり、
更に詳しくは、特定のナフタロシアニン化合物を含有す
る情報記録層をもつ光学的情報記録媒体に関するもので
ある。
従来、レーザー光線により情報を記録、再生する光学的
情報記録媒体の材料として、Te合金、Te酸化物等の
無機物及び種々の有機色素類が多数提案されている。有
機色素類は無機物に比べ、無公害で高感度の媒体をより
安価に作製できる可能性を有している。例えば、フタロ
シアニン系、シアニン系、メロシアニン系、スクワリリ
ウム塩基、ビリリウム塩基、アントラキノン系、トリフ
ェニルメタン系等が挙げられるが、光学的情報記録媒体
として用いるための必要特性、即ち、吸収波長・感度・
安定性・薄膜加工性等をすべて満足するものはまだ見出
されていないのが現状である。
情報記録媒体の材料として、Te合金、Te酸化物等の
無機物及び種々の有機色素類が多数提案されている。有
機色素類は無機物に比べ、無公害で高感度の媒体をより
安価に作製できる可能性を有している。例えば、フタロ
シアニン系、シアニン系、メロシアニン系、スクワリリ
ウム塩基、ビリリウム塩基、アントラキノン系、トリフ
ェニルメタン系等が挙げられるが、光学的情報記録媒体
として用いるための必要特性、即ち、吸収波長・感度・
安定性・薄膜加工性等をすべて満足するものはまだ見出
されていないのが現状である。
上記の有機色素類の中で、フタロシアニン系色素は、古
くから青色〜緑色の顔料として知られ、安定性の優れた
色素として広く用いられている。例えば銅フタロシアニ
ン、鉛フタロシアニン、チタニウムフタロシアニン、バ
ナジルフクロシアニン、錫フタロシアニン等を光学的情
報記録媒体の材料として用いる提案が数多く発表されて
いるが(特開昭55−97033号公報、特開昭56−
130742号公報、特開昭58−36490号公報、
特開昭59−11292号公報等)、これらの吸収波長
は700 nm付近に極大があり、現在、記録用レーザ
ーとして汎用される半導体レーザーの波長領域(780
〜830 nm)では若干吸光度が低下する。そこでベ
ンゾフェノンのようなシフト化剤となるものを用いる(
特開昭59−16153号公報)とか、溶剤処理あるい
は加熱処理を行うとかの手段により吸収位置を長波長ヘ
シフトさせる方法が提案されているが、工程が煩雑とな
り好ましくない。また、これら金属フタロシアニン系色
素は、有機溶媒等への溶解性に乏しく、溶液塗工による
薄膜形成が行えないため真空蒸着法に頼らざるを得す、
大型設備が必要となって加工コストが高くなる欠点を有
する。
くから青色〜緑色の顔料として知られ、安定性の優れた
色素として広く用いられている。例えば銅フタロシアニ
ン、鉛フタロシアニン、チタニウムフタロシアニン、バ
ナジルフクロシアニン、錫フタロシアニン等を光学的情
報記録媒体の材料として用いる提案が数多く発表されて
いるが(特開昭55−97033号公報、特開昭56−
130742号公報、特開昭58−36490号公報、
特開昭59−11292号公報等)、これらの吸収波長
は700 nm付近に極大があり、現在、記録用レーザ
ーとして汎用される半導体レーザーの波長領域(780
〜830 nm)では若干吸光度が低下する。そこでベ
ンゾフェノンのようなシフト化剤となるものを用いる(
特開昭59−16153号公報)とか、溶剤処理あるい
は加熱処理を行うとかの手段により吸収位置を長波長ヘ
シフトさせる方法が提案されているが、工程が煩雑とな
り好ましくない。また、これら金属フタロシアニン系色
素は、有機溶媒等への溶解性に乏しく、溶液塗工による
薄膜形成が行えないため真空蒸着法に頼らざるを得す、
大型設備が必要となって加工コストが高くなる欠点を有
する。
本発明者らは上記の従来技術の問題点を解決するため鋭
意検討を行った結果、特定のナフタロシアニン化合物を
用いた光学的情報記録媒体が吸光特性、加工性、安定性
に優れていることを見出し、本発明に至った。
意検討を行った結果、特定のナフタロシアニン化合物を
用いた光学的情報記録媒体が吸光特性、加工性、安定性
に優れていることを見出し、本発明に至った。
即ち、本発明は、基板上に情報記録層を設けてなる光学
的情報記録媒体において、該情報記録層が次式(I)で
表されるシリコンナフタロシアニン化合物を含有するも
のであることを特徴とする光学的情報記録媒体を提供す
るものである。
的情報記録媒体において、該情報記録層が次式(I)で
表されるシリコンナフタロシアニン化合物を含有するも
のであることを特徴とする光学的情報記録媒体を提供す
るものである。
〔式中、Rは炭素数1〜20のアルキル基、アルケニル
基、芳香族炭化水素基、アシル基又はトリ置換シリル基
のいずれかを表し、5i−0結合の一方は紙面の上方に
、もう一方は紙面の下方に存在するものとする。紙面上
方のRと、紙面下方のRとは異なるものであってもよい
。また、I?1.R2,I?3.R4は、水素原子、ハ
ロゲン原子、炭素数1〜20の置換もしくは装置IAの
アルキル基またはアルケニル基のいずれかを表し、これ
らは同一であっても相異なるものであってもよい。また
、a、 b、 c、 dは1〜4の整数を表し、これら
は同一であっても相異なるものであってもよい。〕 前記(I)式で表されるシリコンナフタロシアニン化合
物としては、例えば、ビス(トリー〇−へキシルシロキ
シ)(2,3−ナフタロシアナ1−)シリコン、ビスー
〇−オクチルオキシ−(2,3−ナフタロシアナト)シ
リコン、ビス−ステアリルオキシ−(2,3−ナフタロ
シアナト)シリコン、ビス−フェニルオキシ−(2,3
−ナフタロシアナト)シリコン、ビス−アセトオキシ−
(2,3−ナフタロシアナト)シリコン、テトラ−(−
プチル−ビスー〇−オクチルオキシ−(2,3−ナフタ
ロシアナト)シリコン等を挙げることができる。
基、芳香族炭化水素基、アシル基又はトリ置換シリル基
のいずれかを表し、5i−0結合の一方は紙面の上方に
、もう一方は紙面の下方に存在するものとする。紙面上
方のRと、紙面下方のRとは異なるものであってもよい
。また、I?1.R2,I?3.R4は、水素原子、ハ
ロゲン原子、炭素数1〜20の置換もしくは装置IAの
アルキル基またはアルケニル基のいずれかを表し、これ
らは同一であっても相異なるものであってもよい。また
、a、 b、 c、 dは1〜4の整数を表し、これら
は同一であっても相異なるものであってもよい。〕 前記(I)式で表されるシリコンナフタロシアニン化合
物としては、例えば、ビス(トリー〇−へキシルシロキ
シ)(2,3−ナフタロシアナ1−)シリコン、ビスー
〇−オクチルオキシ−(2,3−ナフタロシアナト)シ
リコン、ビス−ステアリルオキシ−(2,3−ナフタロ
シアナト)シリコン、ビス−フェニルオキシ−(2,3
−ナフタロシアナト)シリコン、ビス−アセトオキシ−
(2,3−ナフタロシアナト)シリコン、テトラ−(−
プチル−ビスー〇−オクチルオキシ−(2,3−ナフタ
ロシアナト)シリコン等を挙げることができる。
上記のシリコンナフタロシアニン化合物は、フタロシア
ニン系色素に比べて、π電子の非局在領域が拡大してい
ることから、フタロシアニン系よりも長波長領域である
800 nn+前後の近赤外領域で吸収を示す。更にこ
れらの化合物は、塩化メチレン、クロロホルム、四塩化
炭素等のハロゲン化炭化水素、トルエン、ベンゼン等の
芳香族炭化水素、アセトン、メチルエチルケトン、シク
ロヘキサノン等のケトン系化合物等、汎用の有機溶媒に
可溶性を示し、これらのうち適当な溶媒に溶解すること
により、スプレー、ローラーコーティング、ディッピン
グ、スピンコーティング等の方法で基板上に薄膜塗工す
ることができる。この際、シリコンナフタロシアニン化
合物単体で薄膜塗工するごともできるが、適当な高分子
バインダーを併用してもよい。ここで言う高分子バイン
ダーとしては、ニトロセルロース、ポリスチレン、ポリ
エチレン、ポリ酢酸ビニル、ポリビニルアルコール、ポ
リウレタン、ポリアミド、ポリエステル等の熱可塑性樹
脂を例示することができる。また、前記(I)式で表さ
れるシリコンナフタロシアニン化合物と合わせて、同一
の有機溶媒に可溶な他の有機色素類を併用することも可
能である。
ニン系色素に比べて、π電子の非局在領域が拡大してい
ることから、フタロシアニン系よりも長波長領域である
800 nn+前後の近赤外領域で吸収を示す。更にこ
れらの化合物は、塩化メチレン、クロロホルム、四塩化
炭素等のハロゲン化炭化水素、トルエン、ベンゼン等の
芳香族炭化水素、アセトン、メチルエチルケトン、シク
ロヘキサノン等のケトン系化合物等、汎用の有機溶媒に
可溶性を示し、これらのうち適当な溶媒に溶解すること
により、スプレー、ローラーコーティング、ディッピン
グ、スピンコーティング等の方法で基板上に薄膜塗工す
ることができる。この際、シリコンナフタロシアニン化
合物単体で薄膜塗工するごともできるが、適当な高分子
バインダーを併用してもよい。ここで言う高分子バイン
ダーとしては、ニトロセルロース、ポリスチレン、ポリ
エチレン、ポリ酢酸ビニル、ポリビニルアルコール、ポ
リウレタン、ポリアミド、ポリエステル等の熱可塑性樹
脂を例示することができる。また、前記(I)式で表さ
れるシリコンナフタロシアニン化合物と合わせて、同一
の有機溶媒に可溶な他の有機色素類を併用することも可
能である。
本発明におけるシリコンナフタロシアニン化合物を含有
する記録層を担持する基板材料としては塩化ビニル樹脂
、アクリル樹脂、ポリオレフィン樹脂、ポリカーボネー
ト樹脂、ポリビニルアセクール樹脂等の熱可塑性樹脂、
又はエポキシ樹脂、不飽和ポリエステル樹脂、ビニルエ
ステル樹脂等の熱硬化性樹脂、あるいはガラス、金属類
を用いることができる。これらの材料により、成型され
た基板の鏡面上あるいは案内溝パターン(プリグループ
)の刻まれた面上に、上記のような方法で薄膜塗工する
ことができる。
する記録層を担持する基板材料としては塩化ビニル樹脂
、アクリル樹脂、ポリオレフィン樹脂、ポリカーボネー
ト樹脂、ポリビニルアセクール樹脂等の熱可塑性樹脂、
又はエポキシ樹脂、不飽和ポリエステル樹脂、ビニルエ
ステル樹脂等の熱硬化性樹脂、あるいはガラス、金属類
を用いることができる。これらの材料により、成型され
た基板の鏡面上あるいは案内溝パターン(プリグループ
)の刻まれた面上に、上記のような方法で薄膜塗工する
ことができる。
また、基板が上記材料で成型された平板の上に光硬化性
樹脂を積層し、案内溝パターンが該光硬化性樹脂層の表
面に転写された構造であってもよい。
樹脂を積層し、案内溝パターンが該光硬化性樹脂層の表
面に転写された構造であってもよい。
これら基板上に形成する記録層の膜厚は0.O1〜5μ
の範囲であればよく、好ましくは0.05〜1−の範囲
である。更に、反射層、保護層等を設けてディスク状あ
るいはシート状の光学的情報記録媒体を構成するが、本
発明はそれら構成の如何は問わない。
の範囲であればよく、好ましくは0.05〜1−の範囲
である。更に、反射層、保護層等を設けてディスク状あ
るいはシート状の光学的情報記録媒体を構成するが、本
発明はそれら構成の如何は問わない。
こうして作製した、本発明の光学的情報記録媒体に、レ
ーザー光線を照射することにより、該照射部分にピット
が形成され情報の記録及び再生を行うことができるが、
用いるレーザー光は、記録層の吸収波長に応じてNZ+
l1e−Ne、Δr。
ーザー光線を照射することにより、該照射部分にピット
が形成され情報の記録及び再生を行うことができるが、
用いるレーザー光は、記録層の吸収波長に応じてNZ+
l1e−Ne、Δr。
ルビー、色素、半導体等の各レーザー光を選ぶことがで
きる。中でもGa−Al−As半恵体レーザー(発振波
長780 nm)などの近赤外領域に発振波長を有する
レーザーを用いるシステムが好適である。
きる。中でもGa−Al−As半恵体レーザー(発振波
長780 nm)などの近赤外領域に発振波長を有する
レーザーを用いるシステムが好適である。
以下に、実施例を示して本発明を具体的に説明するが、
本発明はこれらの実施例に限定されるものではない。
本発明はこれらの実施例に限定されるものではない。
実施例1
J、八m、 Chem、 Soc、、 106 、74
04 (I984)の記述に準じて、ビス(トリー〇−
へキシルシロキシ) (2,3−ナフタロシアナト)シ
リコンを合成した。得られた緑色固体は276〜279
℃に融点をもち、塩化メチレン、クロロホルム、四塩化
炭素、トルエン、シクロヘキサノン等の溶媒に可溶であ
った。塩化メチレン溶液について吸光度分析を行った結
果、772 nmに極めて強い吸収(ε= 2.5 X
10’ l /mol −cm)を示した。このシリ
コンナフタロシアニン化合物とポリスチレン樹脂とを、
重量比l:1でクロロホルムに溶解し、ガラス板上にス
ピンコード法で、厚さ0.1−の均一な膜を作成した。
04 (I984)の記述に準じて、ビス(トリー〇−
へキシルシロキシ) (2,3−ナフタロシアナト)シ
リコンを合成した。得られた緑色固体は276〜279
℃に融点をもち、塩化メチレン、クロロホルム、四塩化
炭素、トルエン、シクロヘキサノン等の溶媒に可溶であ
った。塩化メチレン溶液について吸光度分析を行った結
果、772 nmに極めて強い吸収(ε= 2.5 X
10’ l /mol −cm)を示した。このシリ
コンナフタロシアニン化合物とポリスチレン樹脂とを、
重量比l:1でクロロホルムに溶解し、ガラス板上にス
ピンコード法で、厚さ0.1−の均一な膜を作成した。
このaDAは、778 nmに極大のある強い吸収を示
し、波長780 nm、ビーム径1.0 ttmのレー
ザー光を照射したところ、鮮明なピントが形成された。
し、波長780 nm、ビーム径1.0 ttmのレー
ザー光を照射したところ、鮮明なピントが形成された。
上記積層物を60°C190%R11の環境下に放置し
、吸光特性を経口追跡したが、2000時間の後におい
ても、はとんど変化は見られなかった。
、吸光特性を経口追跡したが、2000時間の後におい
ても、はとんど変化は見られなかった。
実施例2
実施例1における反応中間体であるジヒドロキシ(2,
3−ナフタロシアナト)シリコンとn−オクタツールと
を還流下2時間反応させ、得られた緑色結晶をベンゼン
中で再結晶により精製し、ビス−n−オクチルオキシ−
(2,3−ナフタロシアナト)シリコンを得た。これは
塩化メチレン、クロロホルム、四塩化炭素、シクロヘキ
サノン等の溶媒に可溶であった。
3−ナフタロシアナト)シリコンとn−オクタツールと
を還流下2時間反応させ、得られた緑色結晶をベンゼン
中で再結晶により精製し、ビス−n−オクチルオキシ−
(2,3−ナフタロシアナト)シリコンを得た。これは
塩化メチレン、クロロホルム、四塩化炭素、シクロヘキ
サノン等の溶媒に可溶であった。
塩化メチレン溶液について吸光度分析を行ったところ、
776 no+に吸収極大(t =2.3 XIO’j
!/mol・cm)を示した。このシリコンナフタロシ
アニン化合物とニトロセルロースとを、重量比1:1で
シクロヘキサノンに溶解し、エポキシ樹脂よりなる厚さ
1.2mmの透明板上にスピンコード法により塗工し、
厚さ0.121Mの均一な膜を作成した。
776 no+に吸収極大(t =2.3 XIO’j
!/mol・cm)を示した。このシリコンナフタロシ
アニン化合物とニトロセルロースとを、重量比1:1で
シクロヘキサノンに溶解し、エポキシ樹脂よりなる厚さ
1.2mmの透明板上にスピンコード法により塗工し、
厚さ0.121Mの均一な膜を作成した。
この薄膜は、780 nmに極大のある強い吸収を示し
、実施例1と同様のレーザー光照射により、鮮明なピッ
トを形成した。
、実施例1と同様のレーザー光照射により、鮮明なピッ
トを形成した。
また実施例1と同じ高温高温条件下での保存テストにお
いても、2000時間後に何ら特性の変化は見られなか
った。
いても、2000時間後に何ら特性の変化は見られなか
った。
本発明の光学的情報記録媒体は、前記のように、特定の
シリコンナフタロシアニン化合物を記録層に用いるが、
このものは、種々の有機溶媒に溶解することができ、溶
液塗工法により、適当な基板上に容易に薄膜を形成する
。
シリコンナフタロシアニン化合物を記録層に用いるが、
このものは、種々の有機溶媒に溶解することができ、溶
液塗工法により、適当な基板上に容易に薄膜を形成する
。
得られた薄膜は近赤外領域の光に対して好適な吸収スペ
クトル及び高い感度を有しており、光学的情報記録媒体
として好適に用いることができる。
クトル及び高い感度を有しており、光学的情報記録媒体
として好適に用いることができる。
Claims (1)
- 【特許請求の範囲】 1、基板上に情報記録層を設けてなる光学的情報記録媒
体において、該情報記録層が次式( I )で表されるシ
リコンナフタロシアニン化合物を含有するものであるこ
とを特徴とする光学的情報記録媒体。 ▲数式、化学式、表等があります▼( I ) 〔式中、Rは炭素数1〜20のアルキル基、アルケニル
基、芳香族炭化水素基、アシル基又はトリ置換シリル基
のいずれかを表し、Si−O結合の一方は紙面の上方に
、もう一方は紙面の下方に存在するものとする。紙面上
方のRと、紙面下方のRとは異なるものであってもよい
。また、R_1、R_2、R_3、R_4は、水素原子
、ハロゲン原子、炭素数1〜20の置換もしくは非置換
のアルキル基またはアルケニル基のいずれかを表し、こ
れらは同一であっても相異なるものであってもよい。ま
た、a、b、c、dは1〜4の整数を表し、これらは同
一であっても相異なるものであってもよい。〕