JPS6159338B2 - - Google Patents

Info

Publication number
JPS6159338B2
JPS6159338B2 JP57170931A JP17093182A JPS6159338B2 JP S6159338 B2 JPS6159338 B2 JP S6159338B2 JP 57170931 A JP57170931 A JP 57170931A JP 17093182 A JP17093182 A JP 17093182A JP S6159338 B2 JPS6159338 B2 JP S6159338B2
Authority
JP
Japan
Prior art keywords
corrosion
polyolefin
weight
sheet
glass mat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP57170931A
Other languages
English (en)
Other versions
JPS5962636A (ja
Inventor
Yoshiharu Takeyama
Naoaki Myamoto
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Idemitsu Petrochemical Co Ltd
Yokohama Rubber Co Ltd
Original Assignee
Idemitsu Petrochemical Co Ltd
Yokohama Rubber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Idemitsu Petrochemical Co Ltd, Yokohama Rubber Co Ltd filed Critical Idemitsu Petrochemical Co Ltd
Priority to JP57170931A priority Critical patent/JPS5962636A/ja
Publication of JPS5962636A publication Critical patent/JPS5962636A/ja
Publication of JPS6159338B2 publication Critical patent/JPS6159338B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】 本発明は鋼管防蝕カバーの製法に関する。 鋼管杭はバースを支えるために海中で使用され
るものであり、その防蝕対策が極めて重要であ
る。同様に、化学工場などにおけるパイプライン
についてもその防蝕対策は重要な課題とされてい
る。以下、主に鋼管杭を代表例として説明する。 従来、鋼管杭の防蝕カバーとしてFRPやFRV
（繊維強化塩化ビニル樹脂）が使用されている。
しかしながら、FRPは主に熱硬化性樹脂を素材
としているため、柔軟性に劣り施工時に締付けが
出来ず内側の防蝕材との機密性に劣るほか短繊維
のガラス繊維が用いられているため、耐衝撃性が
劣るという欠点があつた。また、FRVは柔軟性
はあるけれども短繊維のガラス繊維を使用してい
るため、耐衝撃性が十分でなく、しかも塩化ビニ
ル樹脂は鋭角に曲げたときに割れ破損が生じ易
く、耐候性や耐衝撃性に劣るものであつた。 本発明の目的は、このような欠点のない鋼管防
蝕カバーの製造方法を提供することである。 本発明は、ポリオレフイン90〜50重量％に長繊
維ガラスマツト10〜50重量％を配合した強化ポリ
オレフインシートと該シートより作製した樹脂ア
ングルとを金属線もしくは金網を介して２〜20
Kg／cm2の圧力下で高周波溶着することを特徴とす
る鋼管防蝕カバーの製法である。 本発明に用いるポリオレフインとしてはポリエ
チレン、ポリプロピレン、エチレンやプロピレン
と他のモノマーとのコポリマーなどがあり、特に
ポリプロピレンが好ましい。ポリオレフインはメ
ルトインデツクス（MI）１〜５ｇ／10分、密度
0.90〜0.97ｇ／cm2程度のものを使用することが好
ましい。その理由は、高分子量域の樹脂を用いる
ことにより引張強度、弾性率の高いポリオレフイ
ンシートを得ることができるからである。 また、長繊維ガラスマツトとしては繊維長50mm
以上のものを用い、できる限り連続のものを用い
ることが好ましい。繊維長が50mm以下のものは耐
衝撃性および耐久性に劣り好ましくない。 上記ポリオレフインと長繊維ガラスマツトの配
合割合は、ポリオレフイン90〜50重量％に対して
長繊維ガラスマツト10〜50重量％とすべきであ
る。ポリオレフインの配合量が90重量％を超える
と、補強効果を充分に得ることができずまた、50
重量％未満であると、柔軟性に劣り、長期使用に
よりガラス繊維の表面への浮き上がりが激しくな
り、外観上好ましくないばかりか耐久性の点でも
逆効果となり好ましくない。 強化ポリオレフインシートを製造するには種々
の方法を適用することができ、原則的にはポリオ
レフインを加熱加圧して長繊維ガラスマツトに含
浸せしめてシート化するものであり、一般的には
長繊維ガラスマツト層の両面にポリオレフイン層
を重ね、プレス機あるいは連続ロール、ラミネー
ター等で加熱圧着した後、冷却することによつて
得ることができる。 パイプライン等の鋼管の保護には上記シートを
そのまま使用することができる。また、鋼管杭防
蝕カバーとして用いるときは、上記ポリオレフイ
ンと長繊維ガラスマツトを配合した強化ポリオレ
フインシートを素材とし、好ましくは第１図に示
した如く、平板状シートとアングル状に加工した
樹脂アングルより構成されている。樹脂アングル
は平板状シートを赤外線ヒーター等を用いて局部
的に加熱したのち鋼材アングル等を金型として使
用し、５Kg／cm2程度の低圧により簡易的にプレス
することによつて製作することができる。 平板状シートと樹脂アングルとの接合は、素材
として強化ポリオレフインを用いているため、接
着剤等を使用して行なうことができない。また、
リベツト、ボルト・ナツト等による接合は腐蝕が
生じ易く、長期間に亘る使用が期待できない。そ
れ故、本発明では両者の間に金属線もしくは金網
を介在させて高周波溶着を行なうのである。高周
波溶着は通常、次の手法により行なう。まず、平
板状シートと樹脂アングルとの間に金属線もしく
は金網を挿入し、両者の一方の側に加熱管を設
け、高周波を発振せしめる。高周波磁界中に金属
が存在するため、該金属に誘導電流が流れて極め
て短時間に発熱し、素材である合成樹脂を溶か
す。他方の側より加圧して金属を介在させたまま
合成樹脂素材を溶着させる。次いで、適当な時間
冷却することによつて操作を終了する。このよう
にして、第１図に例示したような鋼管杭防蝕カバ
ーが得られる。なお、平板状シートや樹脂アング
ルの寸法は使用目的を考慮して適当に決定すれば
よい。また、金属としては鉄、ステンレススチー
ル、アルミニウム等があり、特に制限されない。
金網は10〜30メツシユのものが好ましい。溶着は
２〜20Kg／cm2の圧力下で５〜15秒間加熱すること
により行なう。ここで20Kg／cm2を越える加圧では
樹脂がはみ出して外観が悪いものとなる。 鋼管杭防蝕カバーは第２図に示した態様で使用
され、平板状シートによつて鋼管杭を被覆し、樹
脂アングルはフランジ部を形成する。フランジ部
はボルト・ナツト等により締付ければよい。締付
けに用いたボルト・ナツト等は腐蝕した場合には
容易に交換することができる。 鋼管杭の防蝕効果をあげるためには、鋼管杭の
周囲にペトロラタム系の水中ペースト、エポキシ
樹脂系等の防蝕材を塗布し、その上に防蝕テープ
を巻いた後、本発明の防蝕カバーを保護カバーと
して装着することが望ましい。本発明の防蝕カバ
ーは平板状シートと樹脂アングルとの間が高強度
に接合しており、しかも接合部分は腐蝕の心配が
なく、長期間に亘る使用が可能である。その上、
金属材料が介在しているため、該材料による補強
効果が奏されることも本発明の特色の１つであ
る。 次に、本発明の実施例を示す。 実施例 プロピレンホモポリマー（MI：2.0ｇ／10分、
密度：0.90ｇ／cm2）75重量％と長繊維ガラスマツ
ト（繊維長：50mm以上）25重量％よりなる構成の
ものを加熱ゾーン250℃、冷却ゾーン80℃の温
度、ロール圧３Kg／cm2の条件でプレスして厚さ
2.0mmの強化ポリオレフインシートを得た。この
シートの物性の測定値を以下に示す。 引張強度（Kg／cm2） 750 引張弾性率（Kg／cm2） 45000 曲げ強度（Kg／cm2） 1400 曲げ弾性率（Kg／cm2） 48000 アイゾツド衝撃強度（ノツチ付）（Kg．cm／
cm） 60 線膨張係数（cm／cm，℃） 2.69×10-5 次に、プロピレンホモポリマーと長繊維ガラス
マツトの配合量をそれぞれプロピレンホモポリマ
ー60重量％、長繊維ガラスマツト40重量％とした
こと以外は上記と同様にして厚さ3.5mmの強化ポ
リオレフインシートを得、このシートの中央部の
両面より赤外線ヒーターで数分間加熱して表面温
度を130℃以上とした。このようにして該シート
を部分的に加熱したのち鋼材アングルを金型と
し、約５Kg／cm2のエアー圧にてプレスして樹脂ア
ングルを作成した。 前記強化ポリオレフインの平板状シートと樹脂
アングルの間に金網（鉄）を介在させ所定圧力に
て所定時間加熱することによつて溶着せしめ、第
１図に示した鋼管杭防蝕カバーを得た。溶着条件
と該カバーの引張強度（ASTM−Ｄ−638，単位
Kg／cm2）との関係を第１表に示す。 【表】
【図面の簡単な説明】
第１図は本発明の鋼管杭防蝕カバーを例示した
正面図、第２図はその使用状態の説明図である。 １……平板状シート、２……樹脂アングル。

Claims (1)

  1. 【特許請求の範囲】 １ ポリオレフイン90〜50重量％に長繊維ガラス
    マツト10〜50重量％を配合した強化ポリオレフイ
    ンシートと該シートより作製した樹脂アングルと
    を金属線もしくは金鋼を介して２〜20Kg／cm2の圧
    力下で高周波溶着することを特徴とする鋼管防蝕
    カバーの製法。 ２ ポリオレフインがポリプロピレンである特許
    請求の範囲第１項記載の鋼管防蝕カバーの製法。 ３ 長繊維ガラスマツトが繊維長50mm以上のもの
    である特許請求の範囲第１項記載の鋼管防蝕カバ
    ーの製法。
JP57170931A 1982-10-01 1982-10-01 鋼管防蝕カバ−およびその製法 Granted JPS5962636A (ja)