JPS61242640A - 酸化触媒 - Google Patents
酸化触媒Info
- Publication number
- JPS61242640A JPS61242640A JP60085737A JP8573785A JPS61242640A JP S61242640 A JPS61242640 A JP S61242640A JP 60085737 A JP60085737 A JP 60085737A JP 8573785 A JP8573785 A JP 8573785A JP S61242640 A JPS61242640 A JP S61242640A
- Authority
- JP
- Japan
- Prior art keywords
- carrier
- rare earth
- oxidation catalyst
- composite oxide
- activity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
産業−にの利用分野
木発用は排ガス浄化、脱臭あるいはプロパンガス、都市
ガスあるいは灯油、軽油等を触媒燃焼させる酸化触媒に
関するものである。
ガスあるいは灯油、軽油等を触媒燃焼させる酸化触媒に
関するものである。
従来の技術
Ｎ−
一般に未燃の炭化水素を空気の存在下、炭酸ガスと水蒸
気に完全酸化させる酸化触媒について附、白金、パラジ
ウム、ロジウム等の白金族が最も活性が高い。このだめ
アルミナ、シリカ等の各種担持に担持させた白金族系触
媒が酸化触媒として使用されている。一方コパルｌ−、
ニッケル、鉄等のいわゆる卑金属については単独の金属
酸化物としてよりも、最近では各種複合酸化物か検討さ
れており、（例えば中相、御園生ら、日化、１９８０．
１６７９） 特にベロア゛スカイト型構造をもったも
のか活性か高いとされている。
気に完全酸化させる酸化触媒について附、白金、パラジ
ウム、ロジウム等の白金族が最も活性が高い。このだめ
アルミナ、シリカ等の各種担持に担持させた白金族系触
媒が酸化触媒として使用されている。一方コパルｌ−、
ニッケル、鉄等のいわゆる卑金属については単独の金属
酸化物としてよりも、最近では各種複合酸化物か検討さ
れており、（例えば中相、御園生ら、日化、１９８０．
１６７９） 特にベロア゛スカイト型構造をもったも
のか活性か高いとされている。
発明か解決しようとする問題点
白金、ロジウム、パラジウム等の白金族はそれ自体、酸
化活性は高いか耐熱性に問題かあり、コスト的にも高い
という問題点かある。一方、ニッケル、コバル１−１鉄
等の遷移金属の各種組合せによる複合炭酸物について幻
−最近ペロブスカイト構造をもったものが活性が高いと
いうことで各種研究されているか、これらげいづれも各
種塩を量論比で混合したものを蒸発、し、・焼成すると
いう方・法で作製していた。このだめ得られた状態ばい
づれも粉末の状態で、これを各種担体に塗布するという
方法で作製していた。この為、触媒とした場合、常に剥
離の問題があると共に、触媒活性の点からも、粉末では
比表面積が小さいものしか得られ捷いという問題かあっ
た。この為各種担体に直接担持する方法について種々検
刺されてい為かう甘くいっていない。即ちペロプスカイ
ト構造を作るには少くとも７００ ’Ｃ以」―の温度で
焼成することが必要であるか、このような温度条件では
、むしろ担体と担持金属の成分が反応するという問題か
ある。例えば遷移金属としてコバルト、ニッケル等を用
い、担体としてアルミナを用いた場合には、アルミン酸
コバルト（ＣｏＡ Ｉ ２０４ ）、アルミン酸ニッケ
ル（ＮｉＡＩ２０４）を生成し、目的とするペロプスカ
イトが生成１〜ないという問題かあった。本発明にこの
」：う（Ｃ直接担持法に捷つわる問題を解決しようとす
るものである。
化活性は高いか耐熱性に問題かあり、コスト的にも高い
という問題点かある。一方、ニッケル、コバル１−１鉄
等の遷移金属の各種組合せによる複合炭酸物について幻
−最近ペロブスカイト構造をもったものが活性が高いと
いうことで各種研究されているか、これらげいづれも各
種塩を量論比で混合したものを蒸発、し、・焼成すると
いう方・法で作製していた。このだめ得られた状態ばい
づれも粉末の状態で、これを各種担体に塗布するという
方法で作製していた。この為、触媒とした場合、常に剥
離の問題があると共に、触媒活性の点からも、粉末では
比表面積が小さいものしか得られ捷いという問題かあっ
た。この為各種担体に直接担持する方法について種々検
刺されてい為かう甘くいっていない。即ちペロプスカイ
ト構造を作るには少くとも７００ ’Ｃ以」―の温度で
焼成することが必要であるか、このような温度条件では
、むしろ担体と担持金属の成分が反応するという問題か
ある。例えば遷移金属としてコバルト、ニッケル等を用
い、担体としてアルミナを用いた場合には、アルミン酸
コバルト（ＣｏＡ Ｉ ２０４ ）、アルミン酸ニッケ
ル（ＮｉＡＩ２０４）を生成し、目的とするペロプスカ
イトが生成１〜ないという問題かあった。本発明にこの
」：う（Ｃ直接担持法に捷つわる問題を解決しようとす
るものである。
間頴点を解決するだめの手段
この問題を解決するために、アルミナ、シリカ、コージ
ライト等の無機耐熱材料に予め、アルカリ金属、アルカ
リ土類金属、希土類等の塩基性の強い物質を所定用担持
し、担体自体の表面をおお５）だ後、ペロジスカイ１〜
構造を構成する複合酸化物を担持するという手段を採用
した。
ライト等の無機耐熱材料に予め、アルカリ金属、アルカ
リ土類金属、希土類等の塩基性の強い物質を所定用担持
し、担体自体の表面をおお５）だ後、ペロジスカイ１〜
構造を構成する複合酸化物を担持するという手段を採用
した。
作 用
アルミナ、シリカ等の無機面」熱４Ａ料か予め塩基性の
強い材料でコーティングされているため、ペロシスカイ
ト構造を構成するランタン、ネオジウム等の希土類とコ
ノ（ル）・、ニッケル、鉄等の遷移金族を量論比に溶か
した各挿填の溶液に浸漬後、蒸発、焼成しても、ペロプ
スカイト構造を構成する元素の一部が母材と反応すると
いうことがなく々った。この結果、均一なペロプスカイ
ト構造を担持体の」二で形成することか出来た。
強い材料でコーティングされているため、ペロシスカイ
ト構造を構成するランタン、ネオジウム等の希土類とコ
ノ（ル）・、ニッケル、鉄等の遷移金族を量論比に溶か
した各挿填の溶液に浸漬後、蒸発、焼成しても、ペロプ
スカイト構造を構成する元素の一部が母材と反応すると
いうことがなく々った。この結果、均一なペロプスカイ
ト構造を担持体の」二で形成することか出来た。
実施例
以下本発明による酸化触媒を利用した天然ガスの触媒燃
焼器について図面に基つき説明する。図は直接担持法に
よって製造したＬａＣｏＯ３のぺ叢プスカイト構造から
なる複合酸化物を有する酸化５・・− 触媒体を塔載した触媒燃焼器である。図に示すととく本
実施例の働媒燃焼器本体ケース１の前面には金網２及び
背面パネル３に保持さね、た酸化触媒体４かある。酸化
触媒体４けアルミナファイバを最初に硝酸ストロンチク
ムの溶液に浸漬し、乾燥後、８００°Ｃて１ｈ焼成し、
酸化ストロンチクムと１．て７重量パーセント担持した
のち、硝酸ランタン、硝酸コパル１へを量論比に々るよ
うに混合した溶液に浸漬し、乾燥後、８００ ’Ｃで１
ｈ焼成したものであり、ＬａＣｏＣ５として１０重量パ
ーセント担持したものである。Ｘ線回折の結果は均一な
ペロプスカイト描造が得られていた。次にガス量のコン
トロールを行うガスコック５が本体ケ・−ス１前面下部
にある。
焼器について図面に基つき説明する。図は直接担持法に
よって製造したＬａＣｏＯ３のぺ叢プスカイト構造から
なる複合酸化物を有する酸化５・・− 触媒体を塔載した触媒燃焼器である。図に示すととく本
実施例の働媒燃焼器本体ケース１の前面には金網２及び
背面パネル３に保持さね、た酸化触媒体４かある。酸化
触媒体４けアルミナファイバを最初に硝酸ストロンチク
ムの溶液に浸漬し、乾燥後、８００°Ｃて１ｈ焼成し、
酸化ストロンチクムと１．て７重量パーセント担持した
のち、硝酸ランタン、硝酸コパル１へを量論比に々るよ
うに混合した溶液に浸漬し、乾燥後、８００ ’Ｃで１
ｈ焼成したものであり、ＬａＣｏＣ５として１０重量パ
ーセント担持したものである。Ｘ線回折の結果は均一な
ペロプスカイト描造が得られていた。次にガス量のコン
トロールを行うガスコック５が本体ケ・−ス１前面下部
にある。
次にその作用について述べる。
ガスコック５を開くことにより流れてきだガスは酸化触
媒体４下部の点火プラグ（図示せず）により酸化触媒体
４」二で灼−に火炎を形成する。この火炎により酸化触
媒体４は予熱された後、触媒燃焼に移行し、ガスは水蒸
気と炭酸ガスに完全に酸６ベー 化される。この時に発生する熱を暖房用と１〜で利用す
る。
媒体４下部の点火プラグ（図示せず）により酸化触媒体
４」二で灼−に火炎を形成する。この火炎により酸化触
媒体４は予熱された後、触媒燃焼に移行し、ガスは水蒸
気と炭酸ガスに完全に酸６ベー 化される。この時に発生する熱を暖房用と１〜で利用す
る。
発明の効果
以」−のように本発明により溶液からの直接担持法によ
り、アルミナ、シリカ、コージライト等の無機側熱相開
の上にペロプスカイト構造造をもつ複合酸化物を担持さ
せることが出来た結果次のような効果が得られた。
り、アルミナ、シリカ、コージライト等の無機側熱相開
の上にペロプスカイト構造造をもつ複合酸化物を担持さ
せることが出来た結果次のような効果が得られた。
（１）従来の粉末法と異なり担体からの剥離という問題
が全く々くなっだ。この結果、自動車のような振動の激
しい所でも使用か可能となった。
が全く々くなっだ。この結果、自動車のような振動の激
しい所でも使用か可能となった。
（２）担体自体の表面積を利用することが出来るように
なった結果、粉末法にくらべ、粒子径が非常に小さくな
り、その結果活性か向」ニした。
なった結果、粉末法にくらべ、粒子径が非常に小さくな
り、その結果活性か向」ニした。
図は本発明の一実施例の酸化触媒体を塔載した触媒燃焼
器の一部切欠斜視図である。 ４・・・・・・酸化触媒体。
器の一部切欠斜視図である。 ４・・・・・・酸化触媒体。
Claims (1)
- アルミナ、シリカ、コージライト等の無機耐熱材料をハ
ニカム状に成形したもの、あるいは発泡セラミック又は
ファイバー状に織ったものに予めストロンチウム、カル
シウム、マグネシウム、セリウム等のアルカリ金属又は
アルカリ土類金属、希土類を５〜３０重量パーセント担
持した後、ランタン、ネオジウム、プラセオジウム等の
希土類及びコバルト、鉄、ニッケル等の遷移金属の混合
物からなるペロブスカイト型構造をもつ複合酸化物を５
〜５０重量パーセント担持した酸化触媒。