JPS60264341A - 指標付き光フアイバの製造方法 - Google Patents

指標付き光フアイバの製造方法

Info

Publication number
JPS60264341A
JPS60264341A JP59123093A JP12309384A JPS60264341A JP S60264341 A JPS60264341 A JP S60264341A JP 59123093 A JP59123093 A JP 59123093A JP 12309384 A JP12309384 A JP 12309384A JP S60264341 A JPS60264341 A JP S60264341A
Authority
JP
Japan
Prior art keywords
groove
optical fiber
index
soot
quartz tube
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP59123093A
Other languages
English (en)
Inventor
Masao Suzuki
雅夫 鈴木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujikura Ltd
Original Assignee
Fujikura Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujikura Ltd filed Critical Fujikura Ltd
Priority to JP59123093A priority Critical patent/JPS60264341A/ja
Publication of JPS60264341A publication Critical patent/JPS60264341A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 （イ）産業上の利用分野 この発明は、指標付き光ファイバの製造方法に関する。
（ロ）従来技術 小編波光ファイバ等と呼ばれている、光伝搬モードの偏
波面を保存する光ファイバでは、光フアイバ同士を接続
する際その偏波面を両者で合致させる必要がある。そこ
で偏波面を表わす指標を光ファイバに設けることが考え
られるが、従来では簡単にこの指標を設けることができ
なかった。
（ハ）目的 この発明は、上記に鑑み、偏波面を表わす指標が設けら
れた光ファイバを容易に製造できる指標付き光ファイバ
の製造方法を提供することを目的とする。
（ニ）構成 この発明によれば、まず、石英管の内壁に、周方向には
特定の箇所に位置している軸方向に長い溝部を形成し、
つぎに、この溝部を埋めるよう内付けＣＶＤ法により、
屈折率の異なる細長い部分を設ける。そして、この石英
管の中空部にコアおよびクラッドとなる部材を挿入して
紡糸し、光ファイバを製造する。こうして出来」；った
光ファイバでは開方向の特定位置に位置する細長い屈折
率の異なる部分が長さ方向に伸びているので、外部から
この部分を容易に識別でき、偏波面を表わす指標として
役立てることができる。この製造方法によれば、簡単に
指標を設けることができるとともに、指標を設けるにつ
いて光フアイバ自体の特性に何らかの悪影響が生じるこ
とを避けることができる。
（ホ）実施例 以下、この発明の一実施例について図面を参照しながら
説明する。まず第１図に示すように、中空パイプ状の石
英管ｌの中空部にＣＦ４やＳ　Ｆ　４などのガスを導入
し、加熱源２で石英管ｌの外部より加熱する。すると、
つぎの反応式で示される通り、 ＣＦ　４　＋　Ｓ　ｉ　Ｏ、→Ｓ　ｉ　Ｆ　４　＋　Ｃ
Ｏ２加熱された部分において石英管ｌの内壁が削られ、
溝３が形成される。そこで石英管ｌを回転させないよう
にして加熱源２を軸方向に移動させ、周方向には一定の
位置で軸方向に細長い溝３を形（、・　成す６・′″０
実施例−ｔ’ｊｉＱぎａ＞ｘ″′を条件１００工程を行
ない、周方向には１８０’方向に異なっている深さ０．
３ｍｍ程の溝３．３を形成した。
石英管；内径２６ｍｍ、厚さ２．５ｍｍ。
屈折率１．４５８ 使用ガス；　ＣＦ　４１流量１００ｃｃ／ｍｉｎ加熱源
；酸水素バーナ、加熱温度１７００°Ｃ移動速度１００
ｍｍ／ｍｉｎ つぎに、こうして溝３の形成された石英管１の中空部に
、第２図に示すように、ガラス原料ガス（ＳｉＣ１４）
と屈折率制御用ドーパントガス（ＧｅＣ１４など）と酸
素ガスとを導入し、加熱源２により石英管ｌの外部から
加熱して内部で酸化反応を起こさせ、溝３内にガラス微
粉末を堆積させてこの溝３を埋め、ついで加熱源２によ
り加熱することによってこのガラス微粉末堆積層を透明
ガラス化する。この工程を、加熱源２を溝３に沿って軸
方向に移動させながら行なって、溝３内に、石英管ｌと
は屈折率の異なる部分４を形成する。実施例ではつぎの
ような条件でこの工程が行なわれ、屈折率の異なる部分
４の屈折率は１．４６３程となった。
導入ガス；　Ｓ　ｒ　Ｃｌ　４１流量　１０ｃｃ／ｗｉ
ｎＧｅＣ１４，流量２．５ｃｃ／ＩｗｉｎＯ□、　流量
１０００ｃｃ／＋ａｉｎ 加熱源；酸水素バーナ、加熱温度１８００℃移動速度１
５０ｍｍ／ｍ　ｉ　ｎ つぎに、これらの工程を経て作成された、一部に屈折率
の異なる部分４を有する石英管ｌを用い、この石英管ｌ
の中空部に、第３図に示すように、コアおよびクラッド
となる部材を挿入し、ロッドインチューブ法により光フ
ァイバを作る。
すなわち、この実施例では、ＶＡＤ法によって作った、
コア５を有する単一モード母材６を中心部に置き、その
周囲に４木の石英棒７と２本の応力付与母材８とを配置
し、さらにこれらに石英管９を被せ、そのまわりに多数
の石英棒７を配置したものを石英管ｌの中に入れる。応
力付与母材８は、石英とは線膨張率が著しく異なるＦ、
Ｇｅ。
Ｂ、Ｐ、Ｔｉなどが豊富にドープされたＳ　ｉ　Ｏ２の
ロッドよりなり、石英管１の屈折率の異なる部分４と位
置合せされて配置される。これらを図示しない線引き装
置により加熱して溶融した後線引しファイバ径が１２５
ｐｍとなるように細径化し紡糸する。こうして第４図に
示すような、コア５の両脇に応力付与部８が位置する単
個波光ファイバｉｏが出来上る。
このようにして作られた単個波光ファイバｌＯでは、外
部から見ると屈折率の異なる部分４が線状になって見え
、外部から容易に識別できるので、この部分４を指標と
して偏波面を知ることが容易である。また、この指標と
なる部分４は最外周部を覆う石英管ｌに設けられ、コア
５から遠く離れているので、単個波光ファイバとしての
特性に何ら悪影響を与えることがない。
なお、上記では指標となる屈折率の異なる部分４の位置
を応力付与部８の位置と合わせているが、上記の位置か
ら９０°異なる位置としてもよい。また、上記では指標
となる屈折率の異なる部分４は２個であるが１個でもよ
い。さらに、楕円クラッド型中偏波光ファイバなど他の
タイプの単個波光ファイバにも同様にして適用し、偏波
面を表わす指標として役立てることができる。
（へ）効果 以上実施例について説明したように、この発明によれば
、指標伺き光ファイバを容易に製造でき、しかも指標を
設ける工程をイ」加したことによって光ファイバとして
の特性に悪影響を与えない。
【図面の簡単な説明】
図面はこの発明の一実施例に係る指標付き光ファイバの
製造方法の各工程をそれぞれ示すもので、第１図および
第２図は模式的な斜視図、第３図および第４図は断面図
である。 ■、９・・・石英管　２・・・加熱源 ３・・・溝　４・・・屈折率の異なる部分５・・・コア
　６・・・単一モード母材７・・・石英棒　８・・・応
カイ４与部１０・・・中傷波光ファイバ ー、１［ 出願人　藤倉電線株式会社

Claims (1)

    【特許請求の範囲】
  1. （１）中空パイプ状石英管の内壁に周方向の特定箇所に
    位置する溝部を軸方向に形成する工程と、この溝部に内
    付けＣＶＤ法により上記石英管とは屈折率の異なるガラ
    ス微粉末を堆積させてこの溝部を埋めた後この堆積層を
    透明ガラス化する工程と、上記各工程を経た石英管の中
    空部にコアおよびクラッドとなる部材を挿入した後紡糸
    する工程とからなる指標付き光ファイバの製造方法。
JP59123093A 1984-06-14 1984-06-14 指標付き光フアイバの製造方法 Pending JPS60264341A (ja)