JPS60153946A - 酸化触媒 - Google Patents
酸化触媒Info
- Publication number
- JPS60153946A JPS60153946A JP59009490A JP949084A JPS60153946A JP S60153946 A JPS60153946 A JP S60153946A JP 59009490 A JP59009490 A JP 59009490A JP 949084 A JP949084 A JP 949084A JP S60153946 A JPS60153946 A JP S60153946A
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- carrier
- mullite
- catalysts
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は、−酸化炭素（（１！Ｏ）、水素（Ｈ２）、炭
化水素（Ｈｅ ）ガスなど可燃性ガスの酸化触媒、即ち
これらのガスを燃焼させる触媒に関するものである。
化水素（Ｈｅ ）ガスなど可燃性ガスの酸化触媒、即ち
これらのガスを燃焼させる触媒に関するものである。
一酸化炭素、水素および炭化水素ガスなどの可燃性ガス
を酸化触媒の存在下で燃焼させる接触燃焼法は、主とし
て自動車排ガス浄化を目的に研究され、多くの酸化触媒
が開発されている。
を酸化触媒の存在下で燃焼させる接触燃焼法は、主とし
て自動車排ガス浄化を目的に研究され、多くの酸化触媒
が開発されている。
その主なものは、白金のような貴金属、銅や鉄のような
卑金属の酸化物、ＬＩＬＯＯＯ３や０ｕＣｒ０４などの
複合酸化物を触媒成分とし、該触媒成分そのものを粒状
やハニカム状等に成形したもの、あるいはそれらの触媒
成分をアルミナやチタニアなどの担体に直接担持させた
ものである。
卑金属の酸化物、ＬＩＬＯＯＯ３や０ｕＣｒ０４などの
複合酸化物を触媒成分とし、該触媒成分そのものを粒状
やハニカム状等に成形したもの、あるいはそれらの触媒
成分をアルミナやチタニアなどの担体に直接担持させた
ものである。
一方、最近では、低ＮＯＸ燃焼法開発の一環として、プ
ロパン、低ＢＴＵガスおよびオイルなどを燃焼させる酸
化触媒が研究されている。この触媒は、ハニカム型のコ
ージュライトヤムライトなどのセラミックを基材とし、
この基材ｔｔｃｒ−ｈｔ４ｏ３、ジルコニア、マグネシ
ア、α−ＡＩ４０ｓ ｆｉどの担体をウォッシュコート
し、触媒成分としてｐｔ 、 ｐｔ ４− ：ｐａ 、
ｐａ 、ｐｔ ４− Ｒｈ 、などの貴金属あるいはコ
バルト、ニッケル、マンガンなどの酸化物を担持させた
ものである。
ロパン、低ＢＴＵガスおよびオイルなどを燃焼させる酸
化触媒が研究されている。この触媒は、ハニカム型のコ
ージュライトヤムライトなどのセラミックを基材とし、
この基材ｔｔｃｒ−ｈｔ４ｏ３、ジルコニア、マグネシ
ア、α−ＡＩ４０ｓ ｆｉどの担体をウォッシュコート
し、触媒成分としてｐｔ 、 ｐｔ ４− ：ｐａ 、
ｐａ 、ｐｔ ４− Ｒｈ 、などの貴金属あるいはコ
バルト、ニッケル、マンガンなどの酸化物を担持させた
ものである。
本発明者は可燃性ガスのうちで最も酸化（燃焼）させる
ことが難しいメタン（Ｃ３Ｈａ ）の酸化について検討
した結果、メタンの着火（酸化開始）温度が、ハニカム
状触媒を通過するガス流速が大きくなる程、低温側に移
行すること、メタンの酸化率がガス流速が大きくなる程
低下することを見出し、本発明を提案するに至った。
ことが難しいメタン（Ｃ３Ｈａ ）の酸化について検討
した結果、メタンの着火（酸化開始）温度が、ハニカム
状触媒を通過するガス流速が大きくなる程、低温側に移
行すること、メタンの酸化率がガス流速が大きくなる程
低下することを見出し、本発明を提案するに至った。
即ち、本発明の触媒は、例えば第１図、第２図に示すよ
うに、ガスＧの入口側から出口側にかけて触媒Ｃの断面
積を順次大きく（すなわち第１．２図の場合でいえば触
媒Ｃの直径を順次大きく）シたことを特徴とし、これに
よって入口側ガス流速を増し、よシ低温で着火させ、出
口に向う程、ガス流速を低下させて、酸化率を向上させ
ることができるものである。
うに、ガスＧの入口側から出口側にかけて触媒Ｃの断面
積を順次大きく（すなわち第１．２図の場合でいえば触
媒Ｃの直径を順次大きく）シたことを特徴とし、これに
よって入口側ガス流速を増し、よシ低温で着火させ、出
口に向う程、ガス流速を低下させて、酸化率を向上させ
ることができるものである。
以下、実施例により本発明触媒を具体的に説明する。
実施例１
■ コーレとムライト １２．７ＩＩＩＩＩφ １９６
子Ｖ１ｎ２７−Ａｌ２Ｏ２ｐａ １．５重ｆｔ％■ コ
ージェライト １＆５ｔｎφ １９６子Ｖｉｒｉ’ ｙ
−Ａｌ２Ｏ２ＰＣｌ １．５重量％■ ムライト ２α
３叫φ ４００子１７’１ｎ２Ｚｒ０２ ｐｔ ２．１
重量％■ ムライト ２５．４ｍｎφ ４００Ｊｌ／’
ｉｎ” Ｚｒ０１ Ｎｉｏ ６ ｇｆＪ＠％触媒■（長
さ１４．７■）を先頭に、触媒■（長さ１４．７簡）、
触媒■（長さ７．７■）、触媒■（長さ５．０ ｍ ）
の順で各々２０簡の間隔をおいて反応管に充填し、第１
表の条件にてメタンの酸化を実施した（触媒入口ガス流
速＝６，６ｍＮ／ｅθＣ）。結果を第２表に示す。
子Ｖ１ｎ２７−Ａｌ２Ｏ２ｐａ １．５重ｆｔ％■ コ
ージェライト １＆５ｔｎφ １９６子Ｖｉｒｉ’ ｙ
−Ａｌ２Ｏ２ＰＣｌ １．５重量％■ ムライト ２α
３叫φ ４００子１７’１ｎ２Ｚｒ０２ ｐｔ ２．１
重量％■ ムライト ２５．４ｍｎφ ４００Ｊｌ／’
ｉｎ” Ｚｒ０１ Ｎｉｏ ６ ｇｆＪ＠％触媒■（長
さ１４．７■）を先頭に、触媒■（長さ１４．７簡）、
触媒■（長さ７．７■）、触媒■（長さ５．０ ｍ ）
の順で各々２０簡の間隔をおいて反応管に充填し、第１
表の条件にてメタンの酸化を実施した（触媒入口ガス流
速＝６，６ｍＮ／ｅθＣ）。結果を第２表に示す。
第１表
触媒体積（空塔部を除く）：約１０−（前段１．８６ｓ
ｄ＋五１４ｄ＋Ｚ４９ｄ＋２．５３ ｄ） ガス量 ：３ｍ’Ｎ／ｈ ＳＶ値 ： ３０００００ ｈ−” 昇温速度 ニア℃／ｍ１ｎ（保持温度まで）入口ガス保
持温度 ：３３０℃ 燃料／空気比 ： ｏ、 ０２ ｋｙ／ｋｙ （メタン
五５容積％） 第２表 着火温度 メタン酸化率 ２６０℃ ８．７．３％ 比較例 ■ ムライト １６．５ ｍφ ４００孔／ｉｎ２ Ｚ
ｒＯ２Ｐｔ、２．１重量％■ ムライト １６．５ ｗ
ｎφ ４００孔４ｎ２ ＺｒＯ２Ｎ１０６ 重量％実施
例で用いた触媒■（長さ２３■）を先頭に、触媒■（長
さ１１．５■）、触媒■（長さ１１．５ｍ＋）の順で各
々２０ｍ５＋の間隔をおいて反応管に充填し、第１表の
条件でメタンの酸化を実施した（触媒入ロガス流速＝五
９ ｍＮ／ｓｅｃ、）。
ｄ＋五１４ｄ＋Ｚ４９ｄ＋２．５３ ｄ） ガス量 ：３ｍ’Ｎ／ｈ ＳＶ値 ： ３０００００ ｈ−” 昇温速度 ニア℃／ｍ１ｎ（保持温度まで）入口ガス保
持温度 ：３３０℃ 燃料／空気比 ： ｏ、 ０２ ｋｙ／ｋｙ （メタン
五５容積％） 第２表 着火温度 メタン酸化率 ２６０℃ ８．７．３％ 比較例 ■ ムライト １６．５ ｍφ ４００孔／ｉｎ２ Ｚ
ｒＯ２Ｐｔ、２．１重量％■ ムライト １６．５ ｗ
ｎφ ４００孔４ｎ２ ＺｒＯ２Ｎ１０６ 重量％実施
例で用いた触媒■（長さ２３■）を先頭に、触媒■（長
さ１１．５■）、触媒■（長さ１１．５ｍ＋）の順で各
々２０ｍ５＋の間隔をおいて反応管に充填し、第１表の
条件でメタンの酸化を実施した（触媒入ロガス流速＝五
９ ｍＮ／ｓｅｃ、）。
結果を第３表に示す。
第３表
着火温度 メタン酸化率
２９７℃ ７６．１チ
第２表および第３表から明らかなように、本発明触媒は
、比較例に比べ、着火温度が低く、メタンの酸化率が高
いことが判る。
、比較例に比べ、着火温度が低く、メタンの酸化率が高
いことが判る。
第１図及び第２′図は本発明触媒の一例を示す図である
。 復代理人 内 １） 明 復代理人 萩 原 亮 −
。 復代理人 内 １） 明 復代理人 萩 原 亮 −
Claims (1)
- コージエライト、ムライトなどのセラミック耐熱性ハニ
カム基材表面を、アルミナ、ジルコニア、マグネシアな
どの担体で被覆し、該担体にＰ（１，Ｐｔ、 Ｒｈ な
どの貴金属、ニッケル、コバルト、マンガンなど卑金属
の酸化物、Ｌａ０ｏ０３や０ｕＯｒ０４ などの複合酸
化物などの活性体を担持した可燃性ガスの酸化触媒にお
いて、触媒の前段から後段に向って触媒断面積を順次広
げたことを特徴とする酸化触媒。