JPS5943231B2 - ポリエ−テル精製濾過ケ−キの圧縮成形固化方法 - Google Patents
ポリエ−テル精製濾過ケ−キの圧縮成形固化方法Info
- Publication number
- JPS5943231B2 JPS5943231B2 JP52010019A JP1001977A JPS5943231B2 JP S5943231 B2 JPS5943231 B2 JP S5943231B2 JP 52010019 A JP52010019 A JP 52010019A JP 1001977 A JP1001977 A JP 1001977A JP S5943231 B2 JPS5943231 B2 JP S5943231B2
- Authority
- JP
- Japan
- Prior art keywords
- polyether
- filter cake
- compression molding
- purification filter
- solidification method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明はポリエーテルの吸着剤処理による精製の際に排
出される濾過ケーキの固化方法に関するものである。
出される濾過ケーキの固化方法に関するものである。
活性水素を有する化合物にアルキレンオキシドを付加し
て得られるポリエーテルの用途は広くポリウレタン原料
、界面活性剤、潤滑油、化粧品等に使用されている。
て得られるポリエーテルの用途は広くポリウレタン原料
、界面活性剤、潤滑油、化粧品等に使用されている。
これらの用途拡大に伴いポリエーテルの生産量は年々増
加の一途をたどっているが、その一般的な生産工程で排
出される濾過ケーキの処分方法が問題視されてきた。
加の一途をたどっているが、その一般的な生産工程で排
出される濾過ケーキの処分方法が問題視されてきた。
すなわち、活性水素を有する化合物とアルキレンオキシ
ド付加の触媒として使用する水酸化カリウム、水酸化ナ
トリウムは反応終了後、吸着剤処理等により除去し、製
品となる。
ド付加の触媒として使用する水酸化カリウム、水酸化ナ
トリウムは反応終了後、吸着剤処理等により除去し、製
品となる。
この工程で排出される濾過ケーキは高濃度アルカリ、有
機成分（ポリエーテル）を含み、その廃棄に際しては、
中和、焼却等の処理を行なわなくてはならなかった。
機成分（ポリエーテル）を含み、その廃棄に際しては、
中和、焼却等の処理を行なわなくてはならなかった。
本発明は、この沢過ケーキの有効利用に関するもので、
本発明の方法の必須の構成要件は、活性水素を有する化
合物に水酸化ナトリウムあるいは水酸化カリウム触媒の
存在下アルキレンオキサイドを付加して得られる粗製の
ポリエーテルに水を０．５〜２，０重量％含有させ、触
媒吸着処理剤として合成けい酸アルミニウムを加えた後
、濾過により精製ポリエーテルを戸別して得られる水酸
化ナトリウムあるいは水酸化カリウムと合成けい酸ナト
リウムを主成分とする濾過ケーキを５０〜２００℃、ｏ
、５ｋｇ／ｃｒＡ以上の圧力で加熱圧縮成形する事にあ
る。
本発明の方法の必須の構成要件は、活性水素を有する化
合物に水酸化ナトリウムあるいは水酸化カリウム触媒の
存在下アルキレンオキサイドを付加して得られる粗製の
ポリエーテルに水を０．５〜２，０重量％含有させ、触
媒吸着処理剤として合成けい酸アルミニウムを加えた後
、濾過により精製ポリエーテルを戸別して得られる水酸
化ナトリウムあるいは水酸化カリウムと合成けい酸ナト
リウムを主成分とする濾過ケーキを５０〜２００℃、ｏ
、５ｋｇ／ｃｒＡ以上の圧力で加熱圧縮成形する事にあ
る。
活性水素含有化合物としてはアミン類（エチレンジアミ
ン、アルキルエチレンジアミン、イソプロパツールアミ
ン、エタノールアミン等）、アルコール類（メタノール
、エタノール、ブタノール、高級アルコール、エチレン
グリコール、フロピレンゲリコール、クリセリン、ソル
ビトール、ペンタエリスリトール、メチルグリコシド、
蔗糖、等）、フェノール類（フェノール、アルキルフェ
ノール、ビスフェノールＡ等）が挙げられる。
ン、アルキルエチレンジアミン、イソプロパツールアミ
ン、エタノールアミン等）、アルコール類（メタノール
、エタノール、ブタノール、高級アルコール、エチレン
グリコール、フロピレンゲリコール、クリセリン、ソル
ビトール、ペンタエリスリトール、メチルグリコシド、
蔗糖、等）、フェノール類（フェノール、アルキルフェ
ノール、ビスフェノールＡ等）が挙げられる。
また、アルキレンオキシドとしてはエチレンオキシド、
プロピレンオキシド等が挙げられる。
プロピレンオキシド等が挙げられる。
合成けい酸アルミニウムとしてはたとえば表１に示され
るものが挙げられる。
るものが挙げられる。
また、通常の概念内での濾過助剤も支障なく併用出来、
たとえばけいそう±（ラジオライト；昭和化学工業製）
が挙げられる。
たとえばけいそう±（ラジオライト；昭和化学工業製）
が挙げられる。
尚、本発明の目的の範囲内で他の物質たとえば固化を助
けるための硬化性物質（イソシアネートなど）、強化材
等を加えることも許される。
けるための硬化性物質（イソシアネートなど）、強化材
等を加えることも許される。
本発明の方法により得られる固化物は極めて固く、種々
の建築基材、家具芯材等に利用出来る。
の建築基材、家具芯材等に利用出来る。
また本発明の方法はポリエーテル精製時の吸着剤の量を
従来法より減することが出来、又、濾過性も良く作業性
が良い精製法でもある。
従来法より減することが出来、又、濾過性も良く作業性
が良い精製法でもある。
以下に製造例、実施例、比較例、参考例を示し本発明を
更に詳述する。
更に詳述する。
尚、例中１部」は「重量部」である。
製造例 １
グリセリン９２部、水酸化カリウム９．６部をオートク
レーブに仕込み、窒素置換を行なった後、１００〜１２
０℃でプロピレンオキシド３０５０部、次いでエチレン
オキシド５０部を送入し、反応させた。
レーブに仕込み、窒素置換を行なった後、１００〜１２
０℃でプロピレンオキシド３０５０部、次いでエチレン
オキシド５０部を送入し、反応させた。
得られた生成物は粘ちょうな液体でその水酸基価は５４
．３■ＫＯＨｌ＆であった。
．３■ＫＯＨｌ＆であった。
この生成物をポリエーテルＡとする。
製造例 ２
ブタノール７４部、水酸化カリウム１４部をオートクレ
ーブに仕込み、窒素置換を行なった後、プロピレンオキ
シド６２００部を送入し、反応させた。
ーブに仕込み、窒素置換を行なった後、プロピレンオキ
シド６２００部を送入し、反応させた。
反応温度は１１０〜１２５℃、送入時間は約１０時間で
あった。
あった。
得られた生成物は淡黄色の液体であった。
この生成物をポリエーテルＢとする。
実施例−１〜２、比較例−１
温度計、かきまぜ装置の付いたフラスコに、粗製のポリ
エーテル、所定量の水、吸着剤をとり、窒素下、９０〜
１１０℃で１時間かきまぜた。
エーテル、所定量の水、吸着剤をとり、窒素下、９０〜
１１０℃で１時間かきまぜた。
次いで、ガラスフィルター（２６Ｇ−３：シバタ化学製
）を用い、窒素下、１００℃恒温槽中で濾過を行なった
。
）を用い、窒素下、１００℃恒温槽中で濾過を行なった
。
上記で得られた濾過ケーキ１１を加熱装置、加える荷重
の測定装置の付いた鉄製ピストン型シリンダー（直径２
ＣｒｒＬ、長さ５（Ｘ）にとり、所定の温度、圧力で加
熱圧縮を行なった。
の測定装置の付いた鉄製ピストン型シリンダー（直径２
ＣｒｒＬ、長さ５（Ｘ）にとり、所定の温度、圧力で加
熱圧縮を行なった。
固化したケーキを放冷後、圧縮強さ試験に供した。
圧縮強さ試験はＪ ｌ５−Ｒ５２０１（セメントの物理
試験方法）な準じて行なった。
試験方法）な準じて行なった。
精製時、固化時の諸データー、圧縮強さ等を表２に記載
した。
した。
参考例
実施例−２で得た、精製ポリエーテル１００部、Ｎ−メ
チルモルホリン０．４部、トリエチレンジアミンｏ、
ｉ 部、トリクロロモノフルオロメタン６部、水４部、
シリコン系整泡剤２．０部を混合しておき、。
チルモルホリン０．４部、トリエチレンジアミンｏ、
ｉ 部、トリクロロモノフルオロメタン６部、水４部、
シリコン系整泡剤２．０部を混合しておき、。
次いでトルエンジイソシアネート５０部を加え、急速に
混合し、モールドに注ぎ込み、泡化、重合させた。
混合し、モールドに注ぎ込み、泡化、重合させた。
得られたウレタンフオームは良好なものであった。
比較例−１で得たポリエーテルについても上記と同様に
してウレタンフオームを得たが、・内部焼けを起こし収
縮した。
してウレタンフオームを得たが、・内部焼けを起こし収
縮した。
このことから、実施例−２で得たポリエーテルの精製は
充分性なわれているが、比較例−１のポリエーテルは精
製が不充分であることがわかる。
充分性なわれているが、比較例−１のポリエーテルは精
製が不充分であることがわかる。
Claims (1)
- １ 活性水素を有する化合物に水酸化ナトリウムあるい
は水酸化カリウム触媒の存在下アルキレンオキサイドを
付加して得られる粗製のポリエーテルに水を０．５〜２
．０重量％含有させ、触媒吸着処理剤として合成けい酸
アルミニウムを加えた後、濾過により精製ポリエーテル
を戸別して得られる水酸化ナトリウムあるいは水酸化カ
リウムと合成けい酸ナトリウムを主成分とする濾過ケー
キを５０〜２００℃、０．５ｋｇ／ｄ以上の圧力で加熱
圧縮成形する事を特徴とするポリエーテル精製濾過ケー
キの圧縮成形固化方法。