JPS5826405B2 - 鉄損特性の優れた電機機器用電磁鋼板の製造方法 - Google Patents
鉄損特性の優れた電機機器用電磁鋼板の製造方法Info
- Publication number
- JPS5826405B2 JPS5826405B2 JP54127662A JP12766279A JPS5826405B2 JP S5826405 B2 JPS5826405 B2 JP S5826405B2 JP 54127662 A JP54127662 A JP 54127662A JP 12766279 A JP12766279 A JP 12766279A JP S5826405 B2 JPS5826405 B2 JP S5826405B2
- Authority
- JP
- Japan
- Prior art keywords
- iron loss
- electrical steel
- steel sheets
- steel sheet
- loss characteristics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は方向性電磁鋼板、特に一方向性電磁鋼板の鉄損
値を改良する方法に関するものである。
値を改良する方法に関するものである。
周知の通り変圧器その他の電気機器の鉄心用材料として
使用されるものは、通常結晶学的には（１１０）〔００
１〕組織として表示される方向性電磁鋼板であるが、一
面高級な大型回転機あるいは変圧器のＥＩココアして用
いられる電磁鋼板としでは方向性電磁鋼板でも例えば０
． ３ ｍｔｔｔ ｔの一方向性電磁鋼板の圧延方向（
以下Ｌ方向という）の鉄損値はＷｌ ７ ／５ ０ 、
１．０ 〜１． ２ ５Ｗａｔｔ ／心で良好になる
に反し、Ｃ方向のそれはＷ５Ｓｉ３ ０ 、 ２．８
〜３．ＯＷａｔｔ ／ｋｇであってＬ方向に比較シて不
良である。
使用されるものは、通常結晶学的には（１１０）〔００
１〕組織として表示される方向性電磁鋼板であるが、一
面高級な大型回転機あるいは変圧器のＥＩココアして用
いられる電磁鋼板としでは方向性電磁鋼板でも例えば０
． ３ ｍｔｔｔ ｔの一方向性電磁鋼板の圧延方向（
以下Ｌ方向という）の鉄損値はＷｌ ７ ／５ ０ 、
１．０ 〜１． ２ ５Ｗａｔｔ ／心で良好になる
に反し、Ｃ方向のそれはＷ５Ｓｉ３ ０ 、 ２．８
〜３．ＯＷａｔｔ ／ｋｇであってＬ方向に比較シて不
良である。
従ってカットコアあるいは巻鉄心としては有用であるに
も拘らず大型回転機用材あるいは変圧器のＥＩココア材
としては、Ｃ方向の鉄損値を改善する要求が強い。
も拘らず大型回転機用材あるいは変圧器のＥＩココア材
としては、Ｃ方向の鉄損値を改善する要求が強い。
勿論二方向性電磁鋼板は上述の要求を磁気特性としては
満足し得ても、現状では工業的多量生産はコスト的に不
向きである。
満足し得ても、現状では工業的多量生産はコスト的に不
向きである。
これ筐で電磁鋼板の鉄損値を改良する幾多の手段、方法
が提起されてきたが、例えば特公昭５０−３ ５ ６
７ ９号公報に記載されるように機械的な加工を鋼板表
面に与えることは鋼板を積層して構成される鉄心用とし
ては好ましい方法ではなく実際には使用できない。
が提起されてきたが、例えば特公昭５０−３ ５ ６
７ ９号公報に記載されるように機械的な加工を鋼板表
面に与えることは鋼板を積層して構成される鉄心用とし
ては好ましい方法ではなく実際には使用できない。
本発明は上述の課題を解決するもので、方向性電磁鋼板
に非接触で鋼板４面に形状変化を与えることなく微少塑
性歪を加えて鉄損値を改善することを提案するものであ
る。
に非接触で鋼板４面に形状変化を与えることなく微少塑
性歪を加えて鉄損値を改善することを提案するものであ
る。
即ち本発明は、一方向性電磁鋼板のＬ方向に沿ってレー
ザー光を線状照射することを要旨とする。
ザー光を線状照射することを要旨とする。
レーザー光を鋼板に照射して磁性を改善しようとする試
みはこれ１で全く発表されているものはなかった。
みはこれ１で全く発表されているものはなかった。
本発明者らは、特定の照射エネルギーをもつレーザー光
が磁気的性質、特に鉄損値改善に極めて有効であること
を認識してこれを究明した結果、本発明を完成したもの
であって、レーザー光を電磁鋼板のＬ方向に並列に線状
照射するに際し、 照 射 巾（ｄ）０．０１−１＊ｉ 照射間隔（ｌ） ２．５−２０１ｍ 照射エネルギー（Ｐ） ０．５−５Ｊ／ｃｒＡ照 射
方 向 圧延方向とのなす角４５度以下の諸元による
ときが極めて有効であることを知つた。
が磁気的性質、特に鉄損値改善に極めて有効であること
を認識してこれを究明した結果、本発明を完成したもの
であって、レーザー光を電磁鋼板のＬ方向に並列に線状
照射するに際し、 照 射 巾（ｄ）０．０１−１＊ｉ 照射間隔（ｌ） ２．５−２０１ｍ 照射エネルギー（Ｐ） ０．５−５Ｊ／ｃｒＡ照 射
方 向 圧延方向とのなす角４５度以下の諸元による
ときが極めて有効であることを知つた。
すなわち上記諸元によってレーザー照射された鋼板部分
には衝撃波効果によって鋼板に変形を与えることなく転
位が導入され、これによって照射部分には第１図すに示
すように微細な新しい磁区がＣ方向に伸びた形で生じて
いる。
には衝撃波効果によって鋼板に変形を与えることなく転
位が導入され、これによって照射部分には第１図すに示
すように微細な新しい磁区がＣ方向に伸びた形で生じて
いる。
第１図すは電子顕微鏡写真（ＸＩＯ）でΔ印はレーザー
照射部分を示す。
照射部分を示す。
第１図ａはレーザー照射前の電磁鋼板の電子顕微鏡写真
（×１０）であるが、これと比較してこの新しい磁区が
Ｃ方向の磁気特性向上に効果があるものと考えられる。
（×１０）であるが、これと比較してこの新しい磁区が
Ｃ方向の磁気特性向上に効果があるものと考えられる。
本発明に用いるレーザー装置としては現在一般に市販さ
れているルビーレーザー、ＹＡＧＬ／−ｆ−または窒素
レーザー等を用いることができる。
れているルビーレーザー、ＹＡＧＬ／−ｆ−または窒素
レーザー等を用いることができる。
照射エネルギーは０．５−５Ｊｌｃａｔが適当であるが
、パルス発振時間巾が１０ｍ５以下であることが好まし
い。
、パルス発振時間巾が１０ｍ５以下であることが好まし
い。
パルス時間巾が１０ｍ５を超えると照射時に鋼板に生ず
る転位密度の増大効果よりむしろ熱的溶融現象が支配的
になり結晶構造の変化等を引き起すために実質的に鉄損
改善効果は望めない。
る転位密度の増大効果よりむしろ熱的溶融現象が支配的
になり結晶構造の変化等を引き起すために実質的に鉄損
改善効果は望めない。
なお本発明にかいては、レーザー光は鋼板面の垂直方向
から鋼板のＬ方向に沿って線状照射するが、照射部は０
．０１−１ ｍｗをうるように光源を集束して線光源を
うるとよいが、必ずしもこれに限定されるものではない
。
から鋼板のＬ方向に沿って線状照射するが、照射部は０
．０１−１ ｍｗをうるように光源を集束して線光源を
うるとよいが、必ずしもこれに限定されるものではない
。
又電磁鋼板のＬ方向に照射するレーザー光の照射間隔は
２．５ｍｍ−２０ｍｒｎをおいて該鋼板の巾全域に複数
条の線状照射をうるものとする。
２．５ｍｍ−２０ｍｒｎをおいて該鋼板の巾全域に複数
条の線状照射をうるものとする。
照射方向と圧延方向のなす角度が４５度以内、望１しく
は３０度以内であればＬ方向の鉄損値はほとんど変化せ
ずＣ方向鉄損値のみが改善される効果を示すが、該角度
が４５度をこすとＬ方向鉄損値は次第に改善されるが肝
心のＣ方向鉄損値の改善効果は急激に消失してし１う。
は３０度以内であればＬ方向の鉄損値はほとんど変化せ
ずＣ方向鉄損値のみが改善される効果を示すが、該角度
が４５度をこすとＬ方向鉄損値は次第に改善されるが肝
心のＣ方向鉄損値の改善効果は急激に消失してし１う。
以下に本発明の実施例を示す。
厚板０．３ ｍｍの３％Ｓｉ含有一方向性電磁鋼板のＬ
方向に の諸元によりＹＡＧレーザーを開いて、パルス発振時間
巾１５０ｎ−ｓｅｃのパルスレーザーヲ照射した。
方向に の諸元によりＹＡＧレーザーを開いて、パルス発振時間
巾１５０ｎ−ｓｅｃのパルスレーザーヲ照射した。
得られた製品の鉄損値は次の通りであった。以上に示す
通り本発明によるときは、Ｌ方向の磁気性を害うことな
くＣ方向の磁気特性、特に鉄損値は照射前に比較して照
射後は０．９１（Ｗ１５０）向上した。
通り本発明によるときは、Ｌ方向の磁気性を害うことな
くＣ方向の磁気特性、特に鉄損値は照射前に比較して照
射後は０．９１（Ｗ１５０）向上した。
第１図ａは本発明方法実施前の電磁鋼板の磁区構造を示
す電子顕微鏡写真、第１図すは本発明方法実施後の電磁
鋼板の磁区構造を示す電子顕微鏡写真である。
す電子顕微鏡写真、第１図すは本発明方法実施後の電磁
鋼板の磁区構造を示す電子顕微鏡写真である。
Claims (1)
- １ 一方向性電磁鋼板の圧延方向に沿って、あるいは圧
延方向との角度が′４５°以内の方向にレーザー光を線
状照射することを特徴とする特許の優れた電機機器用電
磁鋼板の製造方法。