JPS58190835A - 耐腐食性導電性ガラス - Google Patents
耐腐食性導電性ガラスInfo
- Publication number
- JPS58190835A JPS58190835A JP1902483A JP1902483A JPS58190835A JP S58190835 A JPS58190835 A JP S58190835A JP 1902483 A JP1902483 A JP 1902483A JP 1902483 A JP1902483 A JP 1902483A JP S58190835 A JPS58190835 A JP S58190835A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- oxide
- anticorrosive
- dioxide
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明シま２酸化ルテニウム及び酸化ジルコニウム・ガ
ラス？使用した耐アルカリ腐食性乞有し、導電性？示す
ガラス組成に関する。
ラス？使用した耐アルカリ腐食性乞有し、導電性？示す
ガラス組成に関する。
印計１１ヘッドの如き小型で正確な細工物のための耐腐
食性電極のための要求゛はガラス技法における貴金属の
便用に等き、セラミックに埋もれた導線を営む種々の印
判回路技法の使用に導いた。印刷ヘッド及び他の正確な
電極装置はアルカリ性の環境で動作する時に腐食の問題
？生ずる。
食性電極のための要求゛はガラス技法における貴金属の
便用に等き、セラミックに埋もれた導線を営む種々の印
判回路技法の使用に導いた。印刷ヘッド及び他の正確な
電極装置はアルカリ性の環境で動作する時に腐食の問題
？生ずる。
薄膜ケなす低融点ガラスの結合剤中に焼結された２酸化
ルテニウム？便用する方法１１１９８１年２月干ＩＩＩ
ＢＭ Ｔｅｃｈｎｉｃａｌ Ｄｉｓｃｌｏｓｕｒ
ｅＢｕｌｌｅｔ、ｉｎ 、 Ｖａｔ、２３、扁９中の
Ｃ，Ｊ。
ルテニウム？便用する方法１１１９８１年２月干ＩＩＩ
ＢＭ Ｔｅｃｈｎｉｃａｌ Ｄｉｓｃｌｏｓｕｒ
ｅＢｕｌｌｅｔ、ｉｎ 、 Ｖａｔ、２３、扁９中の
Ｃ，Ｊ。
Ｓａｍｂｕｃｅｔｔｉ ａｎｄ Ｈ，Ｋ、 ５ｅｉｔｚ
著＋１Ｓｉｎｔｅｒｉｎｇ ｏｆ Ｐｏｗｅｒｅｄ
ＲｕＯ２ｔ。
著＋１Ｓｉｎｔｅｒｉｎｇ ｏｆ Ｐｏｗｅｒｅｄ
ＲｕＯ２ｔ。
Ｆａｂｒｉｃａｔｅ Ｅｌｅｃｔｒｏｄｅ ５ｔｒ
ｕｃｔｕｒｅｓ”に説明されている。
ｕｃｔｕｒｅｓ”に説明されている。
米国特許第４０００３４６号をまガラスの如き光学透明
基板の表面上にルテニウムの如き貴金属の酸化物の薄ｊ
値ケ寸着する技法ケ開示している。同様にこの特許は熱
分解摩耗及び腐食性の化学的環境に対する耐性を増大す
るためにバルブ金属（チタン、ジルコニウム、ハフニウ
ム、バナジウム、ニオブ、タンタル・クロム、モリブデ
ン及びウルツラム）の酸化物と貴金属酸化物？混合する
事？開示している。この被覆；ｌま２酸比ケイ素、酸化
アルミニウム、酸化ナトリウム、酸化カリウム及び酸化
リチウム？含んでいない。薄膜をまガラスでなく被覆で
ある。米国特許第３００６７７５号はガラスを含む２酸
化ジルコニウムを含むが２酸化ルテニウムを含寸ないガ
ラスを説明している。
基板の表面上にルテニウムの如き貴金属の酸化物の薄ｊ
値ケ寸着する技法ケ開示している。同様にこの特許は熱
分解摩耗及び腐食性の化学的環境に対する耐性を増大す
るためにバルブ金属（チタン、ジルコニウム、ハフニウ
ム、バナジウム、ニオブ、タンタル・クロム、モリブデ
ン及びウルツラム）の酸化物と貴金属酸化物？混合する
事？開示している。この被覆；ｌま２酸比ケイ素、酸化
アルミニウム、酸化ナトリウム、酸化カリウム及び酸化
リチウム？含んでいない。薄膜をまガラスでなく被覆で
ある。米国特許第３００６７７５号はガラスを含む２酸
化ジルコニウムを含むが２酸化ルテニウムを含寸ないガ
ラスを説明している。
米国特許第４１０００５０号は消耗率を、減少するため
の被覆金属陽極を説明している。この特許はチタン電極
上の被覆として２酸化ルテニウムを使用することを開示
しているがこれは被覆としてであって、ガラスとしてで
はない。ＲｕＯ２１製、プラスティク中のＲｕＯ２粉を
使用する他の技法及び他り）付着技１去は次の米国特許
に開示されている。
の被覆金属陽極を説明している。この特許はチタン電極
上の被覆として２酸化ルテニウムを使用することを開示
しているがこれは被覆としてであって、ガラスとしてで
はない。ＲｕＯ２１製、プラスティク中のＲｕＯ２粉を
使用する他の技法及び他り）付着技１去は次の米国特許
に開示されている。
第３１６８．！１６７号、第３３３４３５２号、第３７
６１９５４号、第３８９１５１３号、第３９５１７５７
号、第４００７１０７号、第４０１７３６６号、第４０
４２９６６号、再発行特許第２９４１９号、第４１３１
４６３号、第４１１２１４Ｄ号、第４１５４６６５号 ガラス中に電極を封止する方法は十分に満足すべき方法
ではない。なんとなれ１ば、封止ガラスは酬アルカリ腐
食性において叱較的貧弱であるから（ろ） である。
６１９５４号、第３８９１５１３号、第３９５１７５７
号、第４００７１０７号、第４０１７３６６号、第４０
４２９６６号、再発行特許第２９４１９号、第４１３１
４６３号、第４１１２１４Ｄ号、第４１５４６６５号 ガラス中に電極を封止する方法は十分に満足すべき方法
ではない。なんとなれ１ば、封止ガラスは酬アルカリ腐
食性において叱較的貧弱であるから（ろ） である。
本発明の目的は必要とされる導電性と耐摩耗性及びアル
カリに対する耐腐食性をあわ伊もち、しかも十分な熱膨
張及び高い融点を有する導電性ガラス複合体を与えるこ
とにある。
カリに対する耐腐食性をあわ伊もち、しかも十分な熱膨
張及び高い融点を有する導電性ガラス複合体を与えるこ
とにある。
本発明に従えば約１，６乃至２：１の比率で２酸化ルテ
ニウムの微細粉及び高融点、高アルカリ抵抗性の酸化ジ
ルコニウム・ガラスを含む導電性ガラス複合体が形成さ
れる。
ニウムの微細粉及び高融点、高アルカリ抵抗性の酸化ジ
ルコニウム・ガラスを含む導電性ガラス複合体が形成さ
れる。
本発明に従うガラス複合体は微細分ＲｕＯ２対２酸化ジ
ルコニウムを含むガラス・フリツｉ・の比が１６乃至２
：１である複合体をＲ２０の導電性を破壊する事なくつ
−や出しする十分な８００乃至１０００℃の温度で焼成
する事によって調整てれる。
ルコニウムを含むガラス・フリツｉ・の比が１６乃至２
：１である複合体をＲ２０の導電性を破壊する事なくつ
−や出しする十分な８００乃至１０００℃の温度で焼成
する事によって調整てれる。
（４）
〔詳細な説明〕
図面は本発明の耐アルカリ性の導電性複合体を示してい
る。ガラス２中の２酸化ルテニウム１はガラスを通る導
電路を与える。導電機構は個々の２酸化ルテニウム間の
接触を含む７ｊＸ、＠る場合には、２酸化ルテニウムは
ガラスによって完全に四重れでもその厚σが薄いために
この誘電体は導電性を阻害するには十分ではない。金属
及びイオンによる導電性は極めて小さく、無視可能であ
る。接点３．４がガラス中を流ね、る電流の比較的低い
抵抗接続を与えている。
る。ガラス２中の２酸化ルテニウム１はガラスを通る導
電路を与える。導電機構は個々の２酸化ルテニウム間の
接触を含む７ｊＸ、＠る場合には、２酸化ルテニウムは
ガラスによって完全に四重れでもその厚σが薄いために
この誘電体は導電性を阻害するには十分ではない。金属
及びイオンによる導電性は極めて小さく、無視可能であ
る。接点３．４がガラス中を流ね、る電流の比較的低い
抵抗接続を与えている。
細かく砕かれたＲＩＩ０２及びガラス・フリット材料は
次の割合で互いに混合された。
次の割合で互いに混合された。
（５）
組成
１乃至２部 ： ガラス・フリット１乃至６部：
５ｉＯｚ ６７−７８％ ： ＺｒＯ２１５−２０％ Ｒｕ ０２１００％ ： Ｎａ２Ｏ４−１１％：
Ａｚ、、ｏ３ １％ ： Ｋ２Ｏ０，５−４係 ： Ｌｉ２Ｏ０，７−１チ （焼成温度８００°乃至１０００℃） （重量％） Ｓ ｉＯｚ Ｚ ｒｏ２Ｎａ２０ ＡｔｚＯ３に２０
Ｌｉ２Ｏ計６．７，２ １５．６ １０．５ １
．０．３．９．０．７ ９Ｂ、５７１ １５
１１ １．０ ０．５ １．’０ ９９．５７１
２０ ０６ １．０ ０．５ １，０ ９
９．５７８ １５ ０４ １．０ ０．５
１．０ ９９．８（６） ガラス及びＲ２゛０は混合する之めボール・ミル中中で
別個に粉砕され混合されるか、−緒に粉砕され、所望の
形状へ圧縮され、焼結される迄るつぼ中で８００乃至ｉ
ｏｏｏ℃に加熱さね、た。この様にして製潰芒れた導
電２性複合材料は製造された時点の形状のｉｔ使用する
事が出来、もしくは細い粉末に粉砕して所望の形状に再
形成し、再び焼成して使用する事が出来る。
５ｉＯｚ ６７−７８％ ： ＺｒＯ２１５−２０％ Ｒｕ ０２１００％ ： Ｎａ２Ｏ４−１１％：
Ａｚ、、ｏ３ １％ ： Ｋ２Ｏ０，５−４係 ： Ｌｉ２Ｏ０，７−１チ （焼成温度８００°乃至１０００℃） （重量％） Ｓ ｉＯｚ Ｚ ｒｏ２Ｎａ２０ ＡｔｚＯ３に２０
Ｌｉ２Ｏ計６．７，２ １５．６ １０．５ １
．０．３．９．０．７ ９Ｂ、５７１ １５
１１ １．０ ０．５ １．’０ ９９．５７１
２０ ０６ １．０ ０．５ １，０ ９
９．５７８ １５ ０４ １．０ ０．５
１．０ ９９．８（６） ガラス及びＲ２゛０は混合する之めボール・ミル中中で
別個に粉砕され混合されるか、−緒に粉砕され、所望の
形状へ圧縮され、焼結される迄るつぼ中で８００乃至ｉ
ｏｏｏ℃に加熱さね、た。この様にして製潰芒れた導
電２性複合材料は製造された時点の形状のｉｔ使用する
事が出来、もしくは細い粉末に粉砕して所望の形状に再
形成し、再び焼成して使用する事が出来る。
もしくは、ペーストがガラス・フリットより形成され、
シルク・スクリーン技法の如き周知の技法によってセラ
ミック基板上に、もしくはセラミック基板中の貫通孔中
に所望の形に置かれ、基板へ複合体を結合するに十分な
８０１］ −１０００℃の温変に加熱される。この方法
は印刷ヘッドの如き複雑な電子装置に要求される導電性
パターンを形成する１、結果の装置はアルカリ性腐食の
みならず、機械損耗に対する抵抗性を与える。結果の導
電性ガラス複合体は同様（Ｃ水及び酸の如き通常の化学
薬品に対して抵抗を示す。
シルク・スクリーン技法の如き周知の技法によってセラ
ミック基板上に、もしくはセラミック基板中の貫通孔中
に所望の形に置かれ、基板へ複合体を結合するに十分な
８０１］ −１０００℃の温変に加熱される。この方法
は印刷ヘッドの如き複雑な電子装置に要求される導電性
パターンを形成する１、結果の装置はアルカリ性腐食の
みならず、機械損耗に対する抵抗性を与える。結果の導
電性ガラス複合体は同様（Ｃ水及び酸の如き通常の化学
薬品に対して抵抗を示す。
本発明は従来の処決では得られなかった最適の（７）
耐摩耗性、而・１アルカリ性及び導′ば性を与え、電気
化学印刷の使用に対する電極としては１．１乃至２：１
のＲｕＯ２／ガラス・フリットが特に有用である。
化学印刷の使用に対する電極としては１．１乃至２：１
のＲｕＯ２／ガラス・フリットが特に有用である。
図面は本発明の耐アルカリ導電性ガラス複合体を示した
図である。 １ ・・２酸化ルテニウム、２・・・ガラス、３・・・
・電気的接点。 出願人インタブｂ佃ナノいビジ木ス・７フーンズ・コゴ
艮トウ田ン（８）
図である。 １ ・・２酸化ルテニウム、２・・・ガラス、３・・・
・電気的接点。 出願人インタブｂ佃ナノいビジ木ス・７フーンズ・コゴ
艮トウ田ン（８）
Claims (1)
- ２酸化ケイ累、２酸化ルテニウム、２酸化ジルコニウム
及び酸化ナトリウム並びに少量の酸化アルミニウム、酸
化カリウム及び酸化リチウムより成り８００乃至１００
０℃で焼成さね、た副アルカリ性導電性ガラス。