JPS57145965A - High strength hot rolled steel plate and its manufacture - Google Patents
High strength hot rolled steel plate and its manufactureInfo
- Publication number
- JPS57145965A JPS57145965A JP3178981A JP3178981A JPS57145965A JP S57145965 A JPS57145965 A JP S57145965A JP 3178981 A JP3178981 A JP 3178981A JP 3178981 A JP3178981 A JP 3178981A JP S57145965 A JPS57145965 A JP S57145965A
- Authority
- JP
- Japan
- Prior art keywords
- steel plate
- hot rolled
- bainite
- strength
- excess
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
PURPOSE: To obtain a high strength hot rolled steel plate with superior formability, eapecially stretch flanging property, resistance weldability and fatigue characteristics by spedifying the C, Si and Mn contents of a hot rolled steel plate and the areal percentage of bainite in the structure composed of polygonal ferrite and bainite.
CONSTITUTION: This steel plate contains 0.01W0.12% c, 0.1W1.6%Si and 0.7W 2.5%Mn and has a composite structure composed of polygonal ferrite and 5W 60% by area of bainite. steel having said composition is hot rolled, cooled to 700W500°C at 5W35°C/sec average cooling rate, further cooled at 25W80°C/sec average cooling rate, and coiled at 575W250°C. Thus, this steel can be manufactured. C is added to enhance the strength and hardenability, yet excess C increases the didderence in hardness between the flash butt weld line and its vicinity. Mn is added to compensate for a reduction in strength due to the lower C content and to obtain bainite, yet excess Mn makes the refining difficult and deteriorates the ductility. Si is added to facilitate the formation of polygonal ferrite and to enhance the strength and ductility, yet excess Si causes embrittlement to the weld zone.
COPYRIGHT: (C)1982,JPO&Japio
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP3178981A JPS57145965A (en) | 1981-03-04 | 1981-03-04 | High strength hot rolled steel plate and its manufacture |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP3178981A JPS57145965A (en) | 1981-03-04 | 1981-03-04 | High strength hot rolled steel plate and its manufacture |
Related Child Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| JP11953585A Division JPS6196057A (en) | 1985-06-01 | 1985-06-01 | Hot-rolled steel plate having maximum strength |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| JPS57145965A true JPS57145965A (en) | 1982-09-09 |
| JPH0146583B2 JPH0146583B2 (en) | 1989-10-09 |
Family
ID=12340824
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| JP3178981A Granted JPS57145965A (en) | 1981-03-04 | 1981-03-04 | High strength hot rolled steel plate and its manufacture |
Country Status (1)
| Country | Link |
|---|---|
| JP (1) | JPS57145965A (en) |
Cited By (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPS60184628A (en) * | 1984-02-29 | 1985-09-20 | Nippon Steel Corp | Manufacture of hot-rolled high-tension steel sheet having superior workability |
| JPS6173829A (en) * | 1984-09-17 | 1986-04-16 | Nippon Steel Corp | Manufacture of high tensile steel composed of ultrafine structure |
| KR100954201B1 (en) * | 2007-12-24 | 2010-04-21 | 주식회사 포스코 | Hot-rolled steel sheet superior in tensile strength and elongation and manufacturing method thereof |
| JP2010189738A (en) * | 2009-02-20 | 2010-09-02 | Jfe Steel Corp | High strength hot rolled steel sheet having excellent workability, and method for producing the same |
| CN104962807A (en) * | 2015-07-10 | 2015-10-07 | 攀钢集团攀枝花钢铁研究院有限公司 | High-strength hot rolled steel as well as manufacturing method and application thereof |
-
1981
- 1981-03-04 JP JP3178981A patent/JPS57145965A/en active Granted
Cited By (6)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPS60184628A (en) * | 1984-02-29 | 1985-09-20 | Nippon Steel Corp | Manufacture of hot-rolled high-tension steel sheet having superior workability |
| JPS6173829A (en) * | 1984-09-17 | 1986-04-16 | Nippon Steel Corp | Manufacture of high tensile steel composed of ultrafine structure |
| KR100954201B1 (en) * | 2007-12-24 | 2010-04-21 | 주식회사 포스코 | Hot-rolled steel sheet superior in tensile strength and elongation and manufacturing method thereof |
| JP2010189738A (en) * | 2009-02-20 | 2010-09-02 | Jfe Steel Corp | High strength hot rolled steel sheet having excellent workability, and method for producing the same |
| CN104962807A (en) * | 2015-07-10 | 2015-10-07 | 攀钢集团攀枝花钢铁研究院有限公司 | High-strength hot rolled steel as well as manufacturing method and application thereof |
| CN104962807B (en) * | 2015-07-10 | 2017-06-23 | 攀钢集团攀枝花钢铁研究院有限公司 | A kind of high strength rolled steel and its preparation method and application |
Also Published As
| Publication number | Publication date |
|---|---|
| JPH0146583B2 (en) | 1989-10-09 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| JPS54148124A (en) | Manufacture of high strength rall of excellent weldability | |
| JP4071906B2 (en) | Manufacturing method of steel pipe for high tension line pipe with excellent low temperature toughness | |
| CN111057945B (en) | 500 MPa-level high-toughness weather-resistant bridge steel and preparation method thereof | |
| JPS58171526A (en) | Manufacture of steel for extra-low temperature use | |
| CN103451570A (en) | Spiral submerged-arc welded pipe for oil and gas transmission suitable for low temperatures and manufacturing method thereof | |
| JPS57145965A (en) | High strength hot rolled steel plate and its manufacture | |
| CN101082105A (en) | High tensile steel excellent in high temperature strength and method for production thereof | |
| JPS595649B2 (en) | Method for manufacturing high-strength hot-dip galvanized steel sheet with excellent workability | |
| CN103388111A (en) | Longitudinal submerged arc welded pipe with excellent low-temperature toughness for oil-gas transmission and preparation method thereof | |
| US3778316A (en) | Method for producing stainless steel | |
| JPS5573848A (en) | High strength steel for welded structure with superior sulfide stress corrosion cracking resistance | |
| US3787250A (en) | Corrosion-resistant high-strength low-alloy steels | |
| JP2000178697A (en) | Martensitic stainless steel excellent in corrosion resistance and weldability | |
| JP3895002B2 (en) | Non-tempered high-tensile steel with excellent resistance to hot-dip galvanizing cracking | |
| JP3355957B2 (en) | Non-tempered high-strength steel with excellent hot-dip galvanizing crack resistance | |
| JPS63160799A (en) | Coated electrode for rail | |
| JP3568710B2 (en) | 590 N / mm2 grade steel sheet for welded structure having excellent HAZ toughness during large heat input welding and yield ratio of 80% or less and method for producing the same | |
| JPS57120651A (en) | Steel plate for nof system galvanizing | |
| JPH07150240A (en) | Production of steel plate | |
| JPH05331596A (en) | Galvannealed steel plate, using high strength hot rolled starting plate, excellent in fatigue characteristic in weld zone and its production | |
| JPS565949A (en) | High tensile steel with superior sulfide corrosion crack resistance and superior corrosion resistance | |
| JPS57143465A (en) | Steel for railroad wheel with superior wear resistance and cracking loss resistance | |
| JP3322139B2 (en) | Non-tempered high-strength steel with excellent hot-dip galvanizing crack resistance | |
| JPH1096062A (en) | High strength and high tensile strength steel excellent in hot dip galvanizing plating resistance | |
| JPH0196329A (en) | Manufacture of steel for welding construction excellent in sulfide stress corrosion cracking resistance and having >=56kgf/mm2 tensile strength |