JPS5662924A - Production of chilled material for rolling roll - Google Patents
Production of chilled material for rolling rollInfo
- Publication number
- JPS5662924A JPS5662924A JP13846079A JP13846079A JPS5662924A JP S5662924 A JPS5662924 A JP S5662924A JP 13846079 A JP13846079 A JP 13846079A JP 13846079 A JP13846079 A JP 13846079A JP S5662924 A JPS5662924 A JP S5662924A
- Authority
- JP
- Japan
- Prior art keywords
- chilled material
- roll
- matrix
- produced
- abrasion resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
PURPOSE:To produce a chilled material of superior abrasion resistance for rolling rolls by die-casting the molten cast iron contg. Ni, Cr and Mo to a roll by means of centrifugal casting then subjecting the same to heat treatment under specific conditions. CONSTITUTION:Molten metal of the low alloy cast iron contg. 2.8-3.5% C, 0.3- 0.9% Si, 0.3-1.2% Mn, 1.5-3.5% Ni, 2.0-5.0% Cr and 0.2-1.0% Mo is cast in dies by centrifugal casting, whereby a roll-like chilled material is produced. This is heated to the temp. to 950-up to 50 deg.C below solidus temp. to be made into two phase structure of cementite +gamma, after which it is quickly cooled down to 450- 550 deg.C by spray water cooling. Next, it is further reheated to 780-860 deg.C, to grain the matrix of the structure, whereby chilled material of superior abrasion resistance having the matrix of high surface hardness and superior toughness for rolling rolls may be produced.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP13846079A JPS5835576B2 (en) | 1979-10-26 | 1979-10-26 | Manufacturing method of chilled material for rolling rolls |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP13846079A JPS5835576B2 (en) | 1979-10-26 | 1979-10-26 | Manufacturing method of chilled material for rolling rolls |
Publications (2)
Publication Number | Publication Date |
---|---|
JPS5662924A true JPS5662924A (en) | 1981-05-29 |
JPS5835576B2 JPS5835576B2 (en) | 1983-08-03 |
Family
ID=15222534
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
JP13846079A Expired JPS5835576B2 (en) | 1979-10-26 | 1979-10-26 | Manufacturing method of chilled material for rolling rolls |
Country Status (1)
Country | Link |
---|---|
JP (1) | JPS5835576B2 (en) |
-
1979
- 1979-10-26 JP JP13846079A patent/JPS5835576B2/en not_active Expired
Also Published As
Publication number | Publication date |
---|---|
JPS5835576B2 (en) | 1983-08-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN100485075C (en) | High-carbon high-vanadium high-speed steel composite roller and heat treatment method thereof | |
CN102766824B (en) | Abrasion-resistant high-speed-steel roller ring and preparation method thereof | |
CN101805869B (en) | Boron-contained high-chromium high-speed steel roller material and heat treatment method thereof | |
GB820099A (en) | Improvements in or relating to crushing and the like rolls | |
GB1381170A (en) | Heatresistant steel | |
KR900001424A (en) | Manufacturing method of hot rolled steel or weight plate | |
CN100352952C (en) | Process for prodn. of grain oriented electrical steel strips | |
GB1534095A (en) | Chill cast roll for hot rolling | |
JPS6421037A (en) | Free-cutting high-temperature low-thermal expansion casting alloy and its production | |
JPS55131125A (en) | Production of unmodified high-strength high-toughness steel | |
GB1400872A (en) | Production of low alloy steel wire | |
JP3002392B2 (en) | Method for manufacturing centrifugally cast composite roll | |
GB1228179A (en) | ||
GB1339647A (en) | Iron alloy | |
JPS5662924A (en) | Production of chilled material for rolling roll | |
JPS55131126A (en) | Production of modified by low alloy containing boron high tensile steel plate | |
JPS58207354A (en) | Manufacture of crane parts made of spheroidal graphite cast iron | |
JPS6462415A (en) | Production of high-tensile unequal-sided unequal thickness steel shape | |
JPS5457418A (en) | Manufacture of high toughness, refined steel | |
JPS5726125A (en) | Production of hot rolled steel plate of superior longitudinal crack resistance having low yield ratio and high tensile strength | |
CN110656281A (en) | High-hardness die steel and preparation method thereof | |
US3251215A (en) | Process for making rails | |
JP2672598B2 (en) | Graphite-crystallized high chromium cast iron roll material and composite roll for rolling with excellent wear resistance and surface roughness | |
JPS6462414A (en) | Production of high-tensile unequal-sided unequal thickness steel shape | |
JPS55152128A (en) | Preparation of low yield ratio and high strength cold rolled steel plate with excellent processability by continuous annealing |