JPS5614439A - Manufacture of optical fiber base material - Google Patents

Manufacture of optical fiber base material

Info

Publication number
JPS5614439A
JPS5614439A JP9056679A JP9056679A JPS5614439A JP S5614439 A JPS5614439 A JP S5614439A JP 9056679 A JP9056679 A JP 9056679A JP 9056679 A JP9056679 A JP 9056679A JP S5614439 A JPS5614439 A JP S5614439A
Authority
JP
Japan
Prior art keywords
clad layer
temp
sicl4
vitrification
deposited
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP9056679A
Other languages
Japanese (ja)
Other versions
JPS5723654B2 (en
Inventor
Yukio Terunuma
Tetsuo Miya
Toshito Hosaka
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Telegraph and Telephone Corp
Original Assignee
Nippon Telegraph and Telephone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Telegraph and Telephone Corp filed Critical Nippon Telegraph and Telephone Corp
Priority to JP9056679A priority Critical patent/JPS5614439A/en
Publication of JPS5614439A publication Critical patent/JPS5614439A/en
Publication of JPS5723654B2 publication Critical patent/JPS5723654B2/ja
Granted legal-status Critical Current

Abstract

PURPOSE:To control a transmission loss and an absorption loss due to OH group by carrying out vitrification at a lower temp. at first when a clad layer is deposited and vitrifying a layer part close to a core at a higher temp. to change the vitrifying temp. in the through thickness direction of the deposited clad layer. CONSTITUTION:When a clad layer is formed, vitrification is carried out at 1,500- 1,550 deg.C in the first half and at 1,600-1,650 deg.C in the latter half. For example, oxygen gas is fed from starting material feed section 1 to preburn quartz pipe 3 with oxyhydrogen burner 5. SiCl4 of a fixed temp. is bubbled with carrier gas oxygen, introduced into rotating pipe 3 together with oxygen gas, heated and scanned with moving burner 5, and vitrified after vapor phase reaction of SiCl4 to deposite a clad layer. The vitrification is carried out at 1,500-1,550 deg.C in the first half and at 1,600-1,650 deg.C in the latter half. SiCl4 and GeCl4 are then introduced into pipe 5 after adjusting carrier gas so as to attain a desired refractive index, and a core is deposited on the inside of the clad layer. Finally, they are made solid to obtain an optical fiber base material.
JP9056679A 1979-07-17 1979-07-17 Manufacture of optical fiber base material Granted JPS5614439A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP9056679A JPS5614439A (en) 1979-07-17 1979-07-17 Manufacture of optical fiber base material

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP9056679A JPS5614439A (en) 1979-07-17 1979-07-17 Manufacture of optical fiber base material

Publications (2)

Publication Number Publication Date
JPS5614439A true JPS5614439A (en) 1981-02-12
JPS5723654B2 JPS5723654B2 (en) 1982-05-19

Family

ID=14001973

Family Applications (1)

Application Number Title Priority Date Filing Date
JP9056679A Granted JPS5614439A (en) 1979-07-17 1979-07-17 Manufacture of optical fiber base material

Country Status (1)

Country Link
JP (1) JPS5614439A (en)

Also Published As

Publication number Publication date
JPS5723654B2 (en) 1982-05-19

Similar Documents

Publication Publication Date Title
US4224046A (en) Method for manufacturing an optical fiber preform
US4406684A (en) Core torch for fabricating single-mode optical fiber preforms
GB2128982A (en) Fabrication method of optical fiber preforms
SE9604358L (en) Process for producing optical fiber glass preform
EP0146659A1 (en) A method for the preparation of synthetic quartz glass suitable as a material of optical fibers
JP3053320B2 (en) Method for producing porous glass preform for optical fiber
US4915716A (en) Fabrication of lightguide soot preforms
DE3160533D1 (en) Process for making a glass coating on the internal surface of a hollow object
JPS5619008A (en) Optical fiber and its manufacture
JPS5614439A (en) Manufacture of optical fiber base material
JPS54134128A (en) Manufacture of basic material for light transmitting fiber
JP2965235B2 (en) Method for producing porous glass preform for optical fiber
JPS5711838A (en) Preparation of cylindrical base material for optical fiber
JPS61158836A (en) Production of parent material for optical glass
EP0135175B1 (en) Methods for producing optical fiber preform and optical fiber
JPS6424041A (en) Production of base material for dispersed shift fiber
JPS569236A (en) Manufacture of optical fiber
JPS5614433A (en) Manufacture of optical fiber base material
JPS55158144A (en) Manufacture of optical fiber base material
JPS5747735A (en) Manufacture of base material for optical fiber
JPS5614434A (en) Manufacture of optical fiber base material
JPS54142318A (en) Production of anhydrous basic material for optical communication fibers
JPS5614431A (en) Manufacture of optical fiber
JPS577832A (en) Manufacture of base material for optical fiber
JPS6243934B2 (en)