JPH10261664A - Semiconductor element, method of forming projecting electrode and wire-bonding method - Google Patents

Semiconductor element, method of forming projecting electrode and wire-bonding method

Info

Publication number
JPH10261664A
JPH10261664A JP9349449A JP34944997A JPH10261664A JP H10261664 A JPH10261664 A JP H10261664A JP 9349449 A JP9349449 A JP 9349449A JP 34944997 A JP34944997 A JP 34944997A JP H10261664 A JPH10261664 A JP H10261664A
Authority
JP
Japan
Prior art keywords
electrode
metal foil
wire
metal
ball
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP9349449A
Other languages
Japanese (ja)
Inventor
Satoru Zama
悟 座間
Yasuhisa Kaga
靖久 加賀
Junya Hirano
潤也 平野
Hitoshi Yuzawa
均 湯沢
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Furukawa Electric Co Ltd
Original Assignee
Furukawa Electric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Furukawa Electric Co Ltd filed Critical Furukawa Electric Co Ltd
Priority to JP9349449A priority Critical patent/JPH10261664A/en
Publication of JPH10261664A publication Critical patent/JPH10261664A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a method for providing a semiconductor element, having the projecting electrode of high junction strength on an electrode pad, for forming the projecting electrode of high junction strength on the electrode of the semiconductor element, without damaging the semiconductor element and executing the wire-bonding of high junction strength. SOLUTION: An electrode pad 2 and a metallic stud jointed to the electrode pad are provided and the metal stud 6 is the semiconductor element jointed to the electrode 7 through a metallic foil 3. The forming method of the projecting electrode, which has a process for melting the tip part of wire 4 and forming a ball 6, a process for arranging the ball 6 on the electrode 2 of the semiconductor element 1 through metallic foil 3 and a process for depressing the ball 6 on the electrode and jointing the electrode 2, metallic foil 3 and the ball 6, and a wire-bonding method are provided.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、半導体素子、突起
電極の形成方法およびワイヤボンディング方法、並びに
それらの方法を実施するための超音波接合装置に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a semiconductor device, a method for forming a bump electrode, a wire bonding method, and an ultrasonic bonding apparatus for performing the method.

【０００２】[0002]

【従来の技術】従来、半導体素子を配線基板に実装する
方法として、半導体チップの電極と外部リードとを金か
らなるボンディングワイヤにより接続するワイヤボンデ
ィング法、および半導体チップの電極パッド上に突起電
極、いわゆるバンプを形成し、このバンプを半田や導電
性ペースト等を介して配線基板に直接実装する表面実装
法が知られている。2. Description of the Related Art Conventionally, as a method of mounting a semiconductor element on a wiring board, a wire bonding method of connecting an electrode of a semiconductor chip and an external lead by a bonding wire made of gold, a projecting electrode on an electrode pad of the semiconductor chip, There is known a surface mounting method in which a so-called bump is formed and the bump is directly mounted on a wiring board via solder, conductive paste, or the like.

【０００３】表面実装法におけるバンプとしては、メッ
キや蒸着により形成されたもの以外に、金属スタッドを
電極パッド上に接合形成したスタッドバンプが知られて
いる。スタッドバンプは、例えば金属ワイヤを加熱溶融
してボール状としたものを金属スタッドとして用いて、
超音波ボンディング法により金属スタッドを電極パッド
上に接合した後、ボール付近でワイヤを切断することに
より形成される。また、形成されたスタッドバンプ上に
半田層を形成したバンプ構造も知られている。As a bump in the surface mounting method, a stud bump formed by bonding a metal stud to an electrode pad is known in addition to a bump formed by plating or vapor deposition. Stud bumps are used, for example, by heating and melting a metal wire into a ball shape as a metal stud,
It is formed by bonding a metal stud on an electrode pad by an ultrasonic bonding method, and then cutting a wire near a ball. A bump structure in which a solder layer is formed on the formed stud bump is also known.

【０００４】[0004]

【発明が解決しようとする課題】上述のワイヤボンディ
ング法やスタッドバンプの形成においては、ボンディン
グワイヤあるいは金属スタッド材として通常は金が用い
られている。これは、銅やパラジウム等の硬度の高い金
属を用いると、ボンディングワイヤや金属スタッドを電
極上に接合する際の押圧力や超音波エネルギーの影響
で、半導体素子にストレスが加わって素子内部に亀裂や
割れを生じたり、半導体素子の信頼性が低下するなどの
問題が生じるためである。In the wire bonding method and the formation of the stud bump, gold is usually used as a bonding wire or a metal stud material. This is because when a metal with high hardness, such as copper or palladium, is used, stress is applied to the semiconductor element due to the pressing force and ultrasonic energy at the time of bonding the bonding wire or metal stud to the electrode, and cracks occur inside the element. This causes problems such as cracks and cracks and a decrease in the reliability of the semiconductor element.

【０００５】しかし、硬度の低い金を用いても、接合時
にある程度のダメージを半導体素子に与えてしまうの
で、よりダメージの少ないワイヤボンディング法やスタ
ッドバンプの形成法が望まれていた。[0005] However, even if gold having a low hardness is used, a certain amount of damage is given to the semiconductor element at the time of bonding. Therefore, a wire bonding method or a stud bump forming method with less damage has been desired.

【０００６】また、金は高価であり、より安価な金属を
使用することによりコストダウンを図ることが必要とさ
れていた。更に、特にスタッドバンプの場合は、実装時
に素子上に形成したバンプと実装基板を半田により接合
するために、金属スタッド材として金を用いると、半田
食われを生じて、接合信頼性が低下するおそれがあると
いう問題もあった。[0006] Gold is expensive, and it has been necessary to reduce costs by using cheaper metals. Furthermore, particularly in the case of stud bumps, when gold is used as a metal stud material to bond the bump formed on the element and the mounting board by soldering during mounting, solder erosion occurs and the bonding reliability decreases. There was also a problem that there was a risk.

【０００７】一方、スタッドバンプをメッキや蒸着によ
り形成する方法を用いれば、半導体素子内部の亀裂等や
防げるが、実装性を高めるためにはバンプ高さを高くす
る必要があり、メッキや蒸着で十分な高さのバンプを得
ることは技術的に困難であり、またコストアップともな
ってしまう。On the other hand, if a method of forming stud bumps by plating or vapor deposition is used, it is possible to prevent cracks or the like inside the semiconductor element, but it is necessary to increase the height of the bumps in order to improve the mountability. It is technically difficult to obtain a bump having a sufficient height, and the cost increases.

【０００８】なお、電極上に予め金属スタッドを接合し
ておいて、この金属スタッド上に更に半田層を形成する
ことで、スタッドバンプの高さを高くして実装性を高め
る方法も知られているが、金属スタッドの接合時に半導
体チップにダメージを与えてしまう点は通常のスタッド
バンプの場合と同様であり、更に、金属スタッド上に設
けた半田層が高さ方向よりも幅方向に形成される傾向が
あって、十分な高さのスタッドバンプを形成することが
難しいという問題があった。A method is also known in which a metal stud is previously bonded on an electrode, and a solder layer is further formed on the metal stud, thereby increasing the height of the stud bump and improving the mountability. However, the point that damages the semiconductor chip when joining metal studs is the same as in the case of normal stud bumps, and the solder layer provided on the metal studs is formed in the width direction rather than the height direction. Therefore, there is a problem that it is difficult to form a stud bump having a sufficient height.

【０００９】本発明は、このような事情の下になされ、
電極パッド上に高い接合強度の突起電極を具備する半導
体素子を提供することを目的とする。本発明の他の目的
は、半導体チップを損傷することなく、高い接合強度の
突起電極を、半導体チップの電極上に形成することを可
能とする、突起電極の形成方法を提供することを目的と
する。The present invention has been made under such circumstances,
It is an object of the present invention to provide a semiconductor device having a protruding electrode having a high bonding strength on an electrode pad. Another object of the present invention is to provide a method for forming a bump electrode, which allows a bump electrode having high bonding strength to be formed on an electrode of a semiconductor chip without damaging the semiconductor chip. I do.

【００１０】本発明の更に他の目的は、半導体チップを
損傷することなく、高い接合強度のワイヤボンディング
を行うことを可能とするワイヤボンディング方法を提供
することにある。It is still another object of the present invention to provide a wire bonding method capable of performing high bonding strength wire bonding without damaging a semiconductor chip.

【００１１】本発明の更に他の目的は、半導体チップを
損傷することなく、高い接合強度の突起電極を、効率よ
く半導体チップの電極上に形成することを可能とする超
音波接合装置を提供することにあるStill another object of the present invention is to provide an ultrasonic bonding apparatus which can efficiently form a projection electrode having a high bonding strength on an electrode of a semiconductor chip without damaging the semiconductor chip. Is in

【００１２】[0012]

【課題を解決するための手段】上記課題を解決するた
め、本発明（請求項１）は、電極パッドと、この電極パ
ッドに接合された金属スタッドとを有する半導体素子で
あって、前記金属スタッドは、金属箔を間に介して前記
電極パッドに接合されていることを特徴とする半導体素
子を提供する。According to a first aspect of the present invention, there is provided a semiconductor device having an electrode pad and a metal stud joined to the electrode pad. Provides a semiconductor device, wherein the semiconductor device is bonded to the electrode pad via a metal foil.

【００１３】即ち、本発明では、電極上に金属箔を介し
て金属スタッドが接合されて突起電極（スタッドバン
プ）が形成されており、接合部分に金属箔が介在してい
るがために、接合時に素子に加わるストレスが緩和さ
れ、これにより素子中のダメージが非常に低減された突
起電極を有する半導体素子が得られる。That is, according to the present invention, the metal stud is bonded to the electrode via the metal foil to form the protruding electrode (stud bump), and the metal foil is interposed at the bonding portion. In some cases, stress applied to the element is reduced, whereby a semiconductor element having a protruding electrode with significantly reduced damage in the element can be obtained.

【００１４】このとき金属箔は、金属スタッドを構成す
る材料よりも硬度の低い材料、例えばアルミニウム、
銀、金、半田、これらの積層箔、またはこれらを被覆し
た箔などを用いると、接合時に素子に加わるストレスを
小さくでき、好適である。また、このとき使用する金属
箔はその純度が高い方がより硬度が低くなって好適であ
り、例えばアルミニウムの場合には純度９９％以上のも
のを用いることが好ましいことが確認されている。At this time, the metal foil is made of a material having a lower hardness than the material constituting the metal stud, for example, aluminum,
It is preferable to use silver, gold, solder, a laminated foil of these, or a foil covering these, since the stress applied to the element at the time of bonding can be reduced. In addition, it is confirmed that the higher the purity of the metal foil used at this time is, the lower the hardness is. Therefore, for example, in the case of aluminum, it is preferable to use a metal foil having a purity of 99% or more.

【００１５】また、金属箔は５〜１００μｍの厚さのも
のを用いるのが好ましく、１０〜５０μｍの厚さのもの
が特に好ましい。金属箔の厚さが５μｍ未満では、十分
な緩衝効果を得ることが出来ないため、半導体チップの
損傷が生じやすく、一方、１００μｍを越えると金属ス
タッドと電極の接合強度を十分とすることが難しくなる
からである。なお、ここでいう金属箔の厚みは接合前の
金属箔の厚みであり、接合後の厚みではない。It is preferable to use a metal foil having a thickness of 5 to 100 μm, particularly preferably 10 to 50 μm. If the thickness of the metal foil is less than 5 μm, a sufficient buffer effect cannot be obtained, and the semiconductor chip is likely to be damaged. On the other hand, if the thickness exceeds 100 μm, it is difficult to make the bonding strength between the metal stud and the electrode sufficient. Because it becomes. The thickness of the metal foil referred to here is the thickness of the metal foil before joining, not the thickness after joining.

【００１６】本発明では、接合の際のストレスが緩和さ
れているために、金属スタッドの材料として、金の他に
銅やアルミニウム、パラジウムを使用することも可能で
あり、銅やパラジウムを使用した場合には、金食われの
ような現象を生じないスタッドバンプを構成することが
でき、中でも９９．９９％以上の銅を用いることが最良
である。In the present invention, since the stress at the time of joining is reduced, copper, aluminum, or palladium can be used as the material of the metal stud, in addition to gold, and copper or palladium is used. In such a case, a stud bump which does not cause a phenomenon such as gold erosion can be formed, and among them, it is best to use 99.99% or more of copper.

【００１７】電極上に金属スタッドを接合する方法とし
ては、超音波ボンディング装置を用いて、金属ワイヤを
溶融して金属ボールを形成し、これを電極上に超音波接
合する方法が知られているが、本発明における金属スタ
ッドはこれに限るものではなく、他の方法で形成しても
良く、また、形状もボール形状に限るものではなく、例
えば金属スタッドの電極との接合予定部を偏平形状とし
ておくことで、より素子内部のストレスが軽減された半
導体素子を得ることができる。As a method of joining a metal stud on an electrode, there is known a method in which a metal wire is melted to form a metal ball using an ultrasonic bonding apparatus, and the metal ball is ultrasonically joined on the electrode. However, the metal stud in the present invention is not limited to this, and may be formed by another method.The shape is not limited to a ball shape. By doing so, it is possible to obtain a semiconductor device in which stress inside the device is further reduced.

【００１８】なお、本発明においても、電極上に金属箔
を介して接合した金属スタッド上に半田層を形成して、
より実装性を高めることができる。金属箔としてアルミ
箔のように半田に濡れない金属を使用し、金属スタッド
と金属箔の接合部から外方に金属箔を展出するように構
成すれば、展出した金属箔部分が半田をはじく作用をし
て、スタッド上に形成した半田層が上方に盛り上がるた
め、極めて実装性の高いスタッドバンプを得ることがで
きる。In the present invention, a solder layer is formed on a metal stud joined to a metal via a metal foil.
The mountability can be further improved. If a metal that does not get wet with solder, such as aluminum foil, is used as the metal foil and the metal foil is extended outward from the joint between the metal stud and the metal foil, the exposed metal foil part The repelling action causes the solder layer formed on the stud to rise upward, so that a stud bump having extremely high mountability can be obtained.

【００１９】また、第２の発明（請求項２）は、電極上
に金属箔を介してボンディングワイヤが接合されている
ことを特徴とする半導体素子を提供する。上述の発明
（請求項１）と同様、金属箔による応力緩和作用によっ
て、素子中のダメージが非常に低減された接合部を有す
る半導体素子を得ることが出来る。Further, a second invention (claim 2) provides a semiconductor device, wherein a bonding wire is bonded to the electrode via a metal foil. As in the case of the above invention (claim 1), a semiconductor element having a joint portion in which damage in the element is greatly reduced can be obtained by the stress relaxation effect of the metal foil.

【００２０】本発明では、接合の際のストレスが緩和さ
れているために、ボンディングワイヤの材料として、金
の他に銅やアルミニウム、パラジウムを使用することも
可能であり、銅やアルミニウム、パラジウムを使用すれ
ば、安価でかつ金食われのような現象を生じないワイヤ
ボンディングを構成することが可能となる。In the present invention, since the stress at the time of joining is reduced, it is possible to use copper, aluminum, or palladium in addition to gold as the material of the bonding wire. If it is used, it is possible to configure wire bonding which is inexpensive and does not cause a phenomenon such as gold erosion.

【００２１】第３の発明（請求項７）は、金属材料から
なるワイヤの先端部を溶融してボールを形成する工程
と、半導体チップの電極上に金属箔を間に介して前記ボ
ールを配置する工程と、前記電極、金属箔およびボール
を相互に接合する工程と、前記ボールからワイヤを切断
して、前記電極上にスタッドバンプを形成する工程とを
具備することを特徴とする突起電極の形成方法を提供す
る。According to a third aspect of the present invention (claim 7), a step of melting a tip portion of a wire made of a metal material to form a ball, and disposing the ball on a semiconductor chip electrode with a metal foil interposed therebetween. And bonding the electrode, metal foil and ball to each other, and cutting a wire from the ball to form a stud bump on the electrode. A method of forming is provided.

【００２２】第３の発明における請求項８の発明は、上
述の突起電極の形成方法（請求項７）において、前記金
属箔が、前記ボールを接合する前にあらかじめ前記電極
上に押圧され、前記電極に接合されることを特徴とす
る。According to a third aspect of the present invention, in the above-described method for forming a protruding electrode (claim 7), the metal foil is pressed on the electrode in advance before joining the ball. It is characterized by being joined to an electrode.

【００２３】第３の発明における請求項９の発明は、上
述の突起電極の形成方法（請求項７，８）において、前
記金属箔が、前記ワイヤを構成する金属材料よりも軟質
の金属材料からなることを特徴とする。According to a ninth aspect of the present invention, in the above-mentioned method for forming a bump electrode (claims 7 and 8), the metal foil is made of a metal material softer than a metal material constituting the wire. It is characterized by becoming.

【００２４】第３の発明における請求項１０の発明は、
上述の突起電極の形成方法（請求項７〜９）において、
前記金属箔が、アルミニウム、銀、金、半田、これらの
積層箔、およびこれらを被覆した箔からなる群から選ば
れた１種であることを特徴とする。According to a tenth aspect of the present invention,
In the above-described method for forming a protruding electrode (claims 7 to 9),
The metal foil is one kind selected from the group consisting of aluminum, silver, gold, solder, a laminated foil of these, and a foil covering these.

【００２５】第３の発明における請求項１１の発明は、
上述の突起電極の形成方法（請求項７〜１０）におい
て、前記金属箔の厚さが、５〜１００μｍであることを
特徴とする。[0025] The invention of claim 11 in the third invention is as follows.
In the above-described method for forming a bump electrode (claims 7 to 10), the thickness of the metal foil is 5 to 100 μm.

【００２６】第３の発明における請求項１２の発明は、
上述の突起電極の形成方法（請求項７〜１０）におい
て、前記ワイヤを構成する金属材料は、パラジウム、銅
および金からなる群から選ばれた１種であることを特徴
とする。According to a twelfth aspect of the third invention,
In the above-described method for forming a bump electrode (claims 7 to 10), the metal material forming the wire is one selected from the group consisting of palladium, copper, and gold.

【００２７】第４の発明（請求項１３）は、第１の金属
材料からなる第１のワイヤの先端部または先端部を溶融
して得た第１のボールを半導体チップの電極に押圧する
工程と、前記第１のワイヤの先端部または第１のボール
から第１のワイヤを切断して、金属緩衝層を形成する工
程と、前記第１の金属材料および金よりも硬質の第２の
金属材料からなる第２のワイヤの先端部を溶融して得た
第２のボールを前記金属緩衝層に押圧する工程と、前記
第２のボールから第２のワイヤを切断して、前記電極上
にスタッドバンプを形成する工程とを具備することを特
徴とする突起電極の形成方法を提供する。According to a fourth invention (claim 13), a step of pressing a tip of a first wire made of a first metal material or a first ball obtained by melting a tip of the first wire against an electrode of a semiconductor chip. Cutting the first wire from the tip of the first wire or the first ball to form a metal buffer layer; and a second metal harder than the first metal material and gold. Pressing a second ball obtained by melting a tip of a second wire made of a material against the metal buffer layer, cutting the second wire from the second ball, and placing the second wire on the electrode; And a step of forming a stud bump.

【００２８】第４の発明における請求項１４の発明は、
上述の突起電極の形成方法（請求項１３）において、前
記第１の金属材料が、アルミニウムまたは金であること
を特徴とする。According to a fourth aspect of the present invention,
In the above-described method of forming a bump electrode (claim 13), the first metal material is aluminum or gold.

【００２９】第４の発明における請求項１５の発明は、
上述の突起電極の形成方法（請求項１３，１４）におい
て、前記第２の金属材料が、パラジウム、銅および金か
らなる群から選ばれた１種であることを特徴とする。[0029] The invention of claim 15 in the fourth invention is as follows.
In the above method of forming a bump electrode (claims 13 and 14), the second metal material is one selected from the group consisting of palladium, copper and gold.

【００３０】第５の発明（請求項１６）は、金属材料か
らなるワイヤの先端部を溶融してボールを形成する工程
と、半導体チップの電極上に金属箔を間に介して前記ボ
ールを配置する工程と、前記電極、金属箔およびボール
を接合する工程と、前記ワイヤをループ状に導いて、外
部リードに接続する工程とを具備することを特徴とする
ワイヤボンディング方法を提供する。According to a fifth aspect of the present invention (claim 16), a step of melting a tip portion of a wire made of a metal material to form a ball, and disposing the ball on a semiconductor chip electrode with a metal foil interposed therebetween. And bonding the electrode, the metal foil and the ball, and guiding the wire in a loop and connecting the wire to an external lead.

【００３１】第５の発明における請求項１７の発明は、
上述のワイヤボンディング方法（請求項１６）におい
て、前記金属箔が、前記ボールを接合する前にあらかじ
め前記電極上に押圧され、前記電極に接合されることを
特徴とする。According to a fifth aspect of the present invention,
In the above-described wire bonding method (claim 16), the metal foil is pressed on the electrode in advance before bonding the ball, and is bonded to the electrode.

【００３２】第５の発明における請求項１８の発明は、
上述のワイヤボンディング方法（請求項１６，１７）に
おいて、前記金属箔が、前記ワイヤを構成する金属材料
よりも軟質の金属材料からなることを特徴とする。[0032] The invention of claim 18 in the fifth invention is as follows.
In the above wire bonding method (claims 16 and 17), the metal foil is made of a metal material softer than the metal material forming the wire.

【００３３】第５の発明における請求項１９の発明は、
上述のワイヤボンディング方法（請求項１６〜１８）に
おいて、前記金属箔が、アルミニウム、銀、金、半田、
これらの積層箔、およびこれらを被覆した箔からなる群
から選ばれた１種であることを特徴とする。According to a fifth aspect of the present invention,
In the above wire bonding method (claims 16 to 18), the metal foil is made of aluminum, silver, gold, solder,
It is characterized by being one kind selected from the group consisting of these laminated foils and foils covering them.

【００３４】第５の発明における請求項２０の発明は、
上述のワイヤボンディング方法（請求項１６〜１９）に
おいて、前記金属箔の厚さが、５〜１００μｍであるこ
とを特徴とする。[0034] According to a twentieth aspect of the fifth aspect,
In the above wire bonding method (claims 16 to 19), the thickness of the metal foil is 5 to 100 μm.

【００３５】第５の発明における請求項２１の発明は、
上述のワイヤボンディング方法（請求項１６〜２０）に
おいて、前記ワイヤを構成する金属材料が、パラジウ
ム、銅および金からなる群から選ばれた１種であること
を特徴とする。According to a fifth aspect of the present invention,
In the above wire bonding method (claims 16 to 20), the metal material forming the wire is one selected from the group consisting of palladium, copper, and gold.

【００３６】第６の発明（請求項２２）は、第１の金属
材料からなる第１のワイヤの先端部または先端部を溶融
して得た第１のボールを半導体チップの電極に押圧する
工程と、前記第１のワイヤの先端部または第１のボール
から第１のワイヤを切断して、金属緩衝層を形成する工
程と、前記第１の金属材料および金よりも硬質の第２の
金属材料からなる第２のワイヤの先端部を溶融して得た
第２のボールを前記金属緩衝層に押圧する工程と、前記
ワイヤをループ状に導いて、外部リードに接続する工程
とを具備することを特徴とするワイヤボンディング方法
を提供する。According to a sixth aspect of the present invention (claim 22), a step of pressing a tip of a first wire made of a first metal material or a first ball obtained by melting a tip of the first wire against an electrode of a semiconductor chip. Cutting the first wire from the tip of the first wire or the first ball to form a metal buffer layer; and a second metal harder than the first metal material and gold. A step of pressing a second ball obtained by melting a tip portion of a second wire made of a material against the metal buffer layer; and a step of guiding the wire in a loop and connecting to an external lead. A wire bonding method is provided.

【００３７】第６の発明における請求項２３の発明は、
上述のワイヤボンディング方法（請求項２２）におい
て、前記第１の金属材料は、アルミニウムまたは金であ
ることを特徴とする。The twenty-third invention of the sixth invention is characterized in that:
In the above wire bonding method (Claim 22), the first metal material is aluminum or gold.

【００３８】第６の発明における請求項２４の発明は、
上述のワイヤボンディング方法（請求項２２，２３）に
おいて、前記第２の金属材料が、パラジウム、銅および
金からなる群から選ばれた１種であることを特徴とす
る。According to a twenty-fourth aspect of the sixth aspect,
In the wire bonding method described above (claims 22 and 23), the second metal material is one selected from the group consisting of palladium, copper, and gold.

【００３９】第７の発明（請求項２５）は、金属箔テー
プを半導体チップの電極上に供給する工程と、金属材料
からなるワイヤの先端部を溶融してボールを形成する工
程と、半導体チップの電極上に前記金属箔テープを間に
介して前記ボールを配置する工程と、前記電極、金属箔
テープおよびボールを接合する工程と、前記ボールから
ワイヤを切断して、前記電極上にスタッドバンプを形成
する工程と、前記金属箔テープと前記半導体チップとを
相対移動させて、前記金属箔テープを前記電極との接合
部の周辺において切断する工程とを具備することを特徴
とする突起電極の形成方法を提供する。According to a seventh aspect of the present invention, there is provided a semiconductor chip comprising: a step of supplying a metal foil tape onto an electrode of a semiconductor chip; a step of forming a ball by melting a tip of a wire made of a metal material; Arranging the ball on the electrode with the metal foil tape interposed therebetween, joining the electrode, the metal foil tape and the ball, and cutting a wire from the ball to form a stud bump on the electrode. Forming the metal foil tape and the semiconductor chip relative to each other, and cutting the metal foil tape around a joint with the electrode. A method of forming is provided.

【００４０】第８の発明（請求項３１）は、金属箔テー
プを半導体チップの電極上に供給する工程と、金属材料
からなるワイヤの先端部を溶融してボールを形成する工
程と、半導体チップの電極上に前記金属箔テープを間に
介して前記ボールを配置する工程と、前記電極、金属箔
テープおよびボールを接合する工程と、前記金属箔テー
プと前記半導体チップとを相対移動させて、前記金属箔
テープを前記電極との接合部の周辺において切断する工
程と、前記ワイヤをループ状に導いて、外部リードに接
続する工程とを具備することを特徴とするワイヤボンデ
ィング方法を提供する。According to an eighth aspect of the present invention, there is provided a semiconductor chip comprising: a step of supplying a metal foil tape onto an electrode of a semiconductor chip; a step of melting a tip of a wire made of a metal material to form a ball; Arranging the ball on the electrode with the metal foil tape therebetween, and bonding the electrode, the metal foil tape and the ball, and relatively moving the metal foil tape and the semiconductor chip, A wire bonding method comprising: a step of cutting the metal foil tape around a joint with the electrode; and a step of guiding the wire in a loop shape and connecting the loop to an external lead.

【００４１】第９の発明（請求項３７）は、半導体チッ
プを載置するステージと、金属材料からなるワイヤを供
給および保持し、水平および垂直方向に移動可能なボン
ディングヘッドとを備えた超音波接合装置において、枠
体の開口部に金属箔を取付けてなる金属箔テープを前記
ステージ上に供給するユニットを備えたことを特徴とす
る超音波接合装置を提供する。A ninth invention (claim 37) provides an ultrasonic wave provided with a stage on which a semiconductor chip is mounted, and a bonding head which supplies and holds a wire made of a metal material and is movable in horizontal and vertical directions. An ultrasonic bonding apparatus, comprising: a unit for supplying a metal foil tape, in which a metal foil is attached to an opening of a frame, to the stage, in the bonding apparatus.

【００４２】以上のように、本発明の突起電極の形成方
法は、ワイヤの先端部に形成されたボールを、金属箔ま
たは金属緩衝層を間に介して、半導体チップの電極に押
圧して接合した後、ボールからワイヤを切断して、スタ
ッドバンプを形成することを特徴とする。As described above, according to the method of forming a projecting electrode of the present invention, the ball formed at the tip of the wire is bonded to the electrode of the semiconductor chip by pressing the ball through the metal foil or the metal buffer layer. After that, the wire is cut from the ball to form a stud bump.

【００４３】また、本発明のワイヤボンディング方法
は、ワイヤの先端部に形成されたボールを、金属箔また
は金属緩衝層を間に介して、半導体チップの電極に押圧
して接合した後、ワイヤをループ状に導いて、外部リー
ドに接続することを特徴とする。Further, in the wire bonding method of the present invention, after the ball formed at the tip of the wire is pressed and bonded to the electrode of the semiconductor chip via a metal foil or a metal buffer layer, the wire is bonded. It is characterized in that it is guided in a loop and connected to an external lead.

【００４４】本発明の方法において使用される金属箔
は、ワイヤよりも軟質の材料、即ちアルミニウム、銀、
金、半田からなることが好ましい。また、これらの積層
箔、およびこれらを被覆した箔であってもよい。これら
の材料が好ましい理由は、軟質であるため、素子へのダ
メージが小さく、ボール接合時の衝撃を吸収する役目を
するからである。The metal foil used in the method of the present invention is made of a material softer than the wire, ie, aluminum, silver,
It is preferably made of gold or solder. Further, these laminated foils and foils covering them may be used. The reason why these materials are preferable is that since they are soft, damage to the element is small, and they play a role of absorbing the impact at the time of ball bonding.

【００４５】金属箔の厚さは、５〜１００μｍであるこ
とが好ましく、１０〜５０μｍが特に好ましい。金属箔
の厚さが５μｍ未満では、十分な緩衝効果を得ることが
出来ないため、半導体チップの損傷が生じ易く、一方、
１００μｍを越えると、ボールの電極への接合が十分行
われないためである。The thickness of the metal foil is preferably from 5 to 100 μm, particularly preferably from 10 to 50 μm. If the thickness of the metal foil is less than 5 μm, a sufficient buffer effect cannot be obtained, so that the semiconductor chip is likely to be damaged.
If the thickness exceeds 100 μm, the ball is not sufficiently bonded to the electrode.

【００４６】金属箔テープと半導体チップの相対移動の
形としては、金属箔テープを、水平方向に張力をかけた
状態で垂直方向に移動させること、金属箔テープと電極
との接合部を中心に、金属箔テープと半導体チップとを
相対的に回転または振動させることが挙げられる。The form of relative movement between the metal foil tape and the semiconductor chip is to move the metal foil tape in the vertical direction while applying tension in the horizontal direction, and to focus on the joint between the metal foil tape and the electrode. And rotating or vibrating the metal foil tape and the semiconductor chip relatively.

【００４７】なお、金属箔テープと半導体チップの相対
移動に際しては、金属箔テープの接合部の周辺にあらか
じめ切り欠きを形成しておくことにより、切断の容易に
かつ確実に行うことができる。When the metal foil tape and the semiconductor chip are moved relative to each other, the cut can be easily and reliably made by forming a notch in advance around the joint of the metal foil tape.

【００４８】また、金属箔に均一に張力をかける他の方
法として、金属箔に張力をかけた状態で、フレームで保
持する方法がある。なお、スタッドバンプの形成におい
ては、上述した金属箔を介してのボール接合および金属
箔の切断の工程は、必ずしも各スタッドバンプ毎に繰り
返して行う必要はない。As another method of uniformly applying tension to the metal foil, there is a method of holding the metal foil with a frame while applying tension to the metal foil. In the formation of stud bumps, the above-described steps of ball bonding via metal foil and cutting of metal foil need not necessarily be repeated for each stud bump.

【００４９】一般的な半導体装置においては、複数個
（一般的には十〜数十個）のバンプ形成場所が直線的に
配列されたパターンを有している場合が多く、このよう
な場合は、金属箔を介してのボール接合を当該複数個の
バンプ形成場所に対して連続的に行い、しかる後に金属
箔の切断をまとめて行うことが能率的であり、好まし
い。In a general semiconductor device, there are many cases where a plurality of (generally, ten to several tens) bump formation locations have a pattern in which the bump formation locations are linearly arranged. It is efficient and preferable that the ball bonding via the metal foil is continuously performed on the plurality of bump forming locations and then the metal foil is cut at a time.

【００５０】この場合は、当該複数個のバンプ形成場所
に対するボール接合を行った後、直線状に配列した接合
部分の両サイドから金属箔にテンションを加えた状態
で、バンプの配列方向と平行、あるいは垂直方向に振動
を加える、ないしは、金属箔の、直線状に配列した接合
部分の両サイドを持ち上げるようにした状態で、バンプ
の配列方向と平行、あるいは垂直方向に振動を加えるこ
とにより、金属箔の切断を行うと、良好な切断結果を得
ることができる。In this case, after the ball is bonded to the plurality of bump formation locations, tension is applied to the metal foil from both sides of the linearly arranged bonding portion, and the metal foil is parallel to the bump arranging direction. Alternatively, by applying vibration in the vertical direction, or by applying vibration in the direction parallel to or perpendicular to the arrangement direction of the bumps in a state where both sides of the linearly arranged joint portion of the metal foil are lifted, When the foil is cut, a good cutting result can be obtained.

【００５１】金属緩衝層は、アルミニウム、金からなる
ことが好ましい。これらの材料が好ましい理由は、軟質
であり、変形し易いこと、大気中での接合が可能である
こと、特にアルミニウムは常温にて接合できるからであ
る。The metal buffer layer is preferably made of aluminum or gold. The reason why these materials are preferable is that they are soft, easily deformed, can be bonded in the air, and particularly, aluminum can be bonded at room temperature.

【００５２】金属緩衝層の厚さは、０．１〜１０μｍで
あることが好ましい。金属緩衝層の厚さが０．１μｍ未
満では、十分な緩衝効果を得ることが出来ないため、半
導体チップの損傷が生じ易く、一方、１０μｍを越える
と、十分な接合状態を得ることができない。The thickness of the metal buffer layer is preferably 0.1 to 10 μm. If the thickness of the metal buffer layer is less than 0.1 μm, a sufficient buffer effect cannot be obtained, so that the semiconductor chip is likely to be damaged. On the other hand, if the thickness exceeds 10 μm, a sufficient bonding state cannot be obtained.

【００５３】本発明の突起電極の形成方法およびワイヤ
ボンディング方法において、金属緩衝層として、金属粉
末層を用いることもできる。金属粉末は、例えば、金属
粉末と液体の混合物の形で半導体チップ上に供給され、
次いで液体を蒸発させることにより、金属粉末層を形成
することができる。使用可能な液体としては、金属粉末
を均一に分散させることができるとともに、蒸発が容易
なように、沸点が低いものであることが好ましい。その
ような液体としては、エタノール、アセトン、ヘキサン
等を挙げることができる。なお、余分な金属粉末層は、
金属スタッドもしくはボンディングワイヤを接合した後
に、容易に除去することが出来る。In the method for forming a bump electrode and the wire bonding method of the present invention, a metal powder layer may be used as the metal buffer layer. The metal powder is supplied on the semiconductor chip, for example, in the form of a mixture of the metal powder and a liquid,
Next, the metal powder layer can be formed by evaporating the liquid. It is preferable that the liquid that can be used has a low boiling point so that the metal powder can be uniformly dispersed and is easily evaporated. Examples of such a liquid include ethanol, acetone, and hexane. The extra metal powder layer is
After joining the metal stud or bonding wire, it can be easily removed.

【００５４】ワイヤを構成する材料としては、安価な銅
やパラジウムを用いることが好ましいが、金を用いるこ
とも可能である。以上のように、本発明の方法による
と、半導体チップの電極とボールとの間に金属箔または
金属緩衝層を介在させているため、これら金属箔または
金属緩衝層がボールを電極に押圧する際の衝撃を吸収
し、それによって、半導体チップの損傷が防止されるの
で、高い接合強度のバンプを容易に形成することが可能
である。また、それによって、スタッドバンプの形成お
よびワイヤーボンディングの信頼性の向上を図ることが
できる。As a material forming the wire, it is preferable to use inexpensive copper or palladium, but it is also possible to use gold. As described above, according to the method of the present invention, since the metal foil or the metal buffer layer is interposed between the electrode of the semiconductor chip and the ball, the metal foil or the metal buffer layer presses the ball against the electrode. Is absorbed, thereby preventing damage to the semiconductor chip, so that bumps having high bonding strength can be easily formed. In addition, it is possible to improve the reliability of the formation of the stud bump and the wire bonding.

【００５５】また、金属箔または金属緩衝層の存在のた
め、ボールのつぶれが小さくて済み、高いバンプ高を得
ることがが可能である。このことは、半導体素子と基板
との接合に非常に有利である。Further, the presence of the metal foil or the metal buffer layer can reduce the crushing of the ball, and can obtain a high bump height. This is very advantageous for joining the semiconductor element and the substrate.

【００５６】更に、特に、スタッドバンプおよびボンデ
ィングワイヤとして銅やパラジウムを用いた場合には、
コストを下げることが出来るとともに、半田との間で金
属間化合物を形成して接合が脆化する現象を防止するこ
とが可能である。Further, particularly when copper or palladium is used for the stud bump and the bonding wire,
It is possible to reduce the cost and to prevent the phenomenon that the intermetallic compound is formed with the solder and the joining is embrittled.

【００５７】[0057]

【発明の実施の形態】以下、図面を参照して、本発明の
種々の実施例について説明する。最初に、以下の実施例
で使用されたワイヤボンディング装置（超音波接合装
置）について説明する。図２０は、本発明に使用される
ワイヤボンディング装置の概要を示す図である。図２０
に示すワイヤボンディング装置では、ステージ２０１上
に半導体チップ２０２が載置され、ボンディングヘッド
２０３には、キャピラリ２０４、トランスジューサ２０
５、ワイヤクランパ２０６が取り付けられている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Various embodiments of the present invention will be described below with reference to the drawings. First, a wire bonding apparatus (ultrasonic bonding apparatus) used in the following embodiments will be described. FIG. 20 is a diagram showing an outline of a wire bonding apparatus used in the present invention. FIG.
In the wire bonding apparatus shown in FIG. 1, a semiconductor chip 202 is mounted on a stage 201, and a capillary 204 and a transducer 20 are mounted on a bonding head 203.
5. The wire clamper 206 is attached.

【００５８】ボンディングヘッド２０３は、ＸＹテーブ
ル２０７上に取付けられ、ＸＹテーブル２０７がＸ方向
およびＹ方向に移動することにより、ボンディングの位
置合せが行われる。キャピラリ２０４は、Ｚ駆動モータ
２０８により上下動し、位置合せはカメラ２０９により
行われる。The bonding head 203 is mounted on an XY table 207, and the XY table 207 moves in the X direction and the Y direction, thereby performing bonding alignment. The capillary 204 is moved up and down by a Z drive motor 208, and alignment is performed by a camera 209.

【００５９】ワイヤ２１０は、スプール２１１からワイ
ヤクランパ２０６によりキャピラリ２０４へ供給され、
その先端部には、電気トーチによる放電によりボールが
形成される。バンプの形成に際しては、ステージ２０１
上に載置された半導体チップ２０２の上方に金属箔を配
置し、このボールを金属箔を間に介して半導体チップ２
０２の電極パッドに押しつけることにより接合する。こ
のとき、トランスジューサ２０５により、超音波と荷重
を加えることによりバンプを形成する。なお、図２０に
示すワイヤボンディング装置では、後述する、図６に示
すような、フレームの開口部に金属箔を接着したユニッ
ト７０を用いて、連続的に金属箔を供給出来るようにし
ている。The wire 210 is supplied from the spool 211 to the capillary 204 by the wire clamper 206,
A ball is formed at the tip of the ball by electric discharge from the electric torch. When forming the bump, the stage 201
A metal foil is arranged above the semiconductor chip 202 mounted thereon, and the ball is placed between the semiconductor chip 2 and the metal foil with the metal foil interposed therebetween.
Bonding is performed by pressing against the electrode pad No. 02. At this time, a bump is formed by applying ultrasonic waves and a load by the transducer 205. In the wire bonding apparatus shown in FIG. 20, a metal foil can be continuously supplied by using a unit 70 in which a metal foil is adhered to an opening of a frame as described later with reference to FIG.

【００６０】実施例１ 図１に示す手順に従って、突起電極を形成した。即ち、
まず、図１（ａ）に示すように、シリコンチップ１に形
成された、１００μｍ角、厚さ１μｍのアルミニウム電
極２の上に、厚さ１５μｍのアルミ箔３を配置した。次
いで、４０μｍの線径のパラジウム線４をキャピラリ５
に通し、放電によって８０μｍ径の金属スタッド（パラ
ジウムボール）６を形成した。なお、図ではシリコンチ
ップ１上にアルミニウム電極２が突出しているように描
かれているが、実際には、アルミニウム電極２の周囲に
は絶縁膜が形成されていて、アルミニウム電極２は絶縁
膜に埋め込まれた形となっている。Example 1 A protruding electrode was formed according to the procedure shown in FIG. That is,
First, as shown in FIG. 1A, a 15 μm-thick aluminum foil 3 was disposed on a 100 μm-square, 1 μm-thick aluminum electrode 2 formed on a silicon chip 1. Next, a palladium wire 4 having a wire diameter of 40 μm was inserted into the capillary 5.
And a metal stud (palladium ball) 6 having a diameter of 80 μm was formed by discharging. In the figure, the aluminum electrode 2 is drawn so as to protrude on the silicon chip 1, but in actuality, an insulating film is formed around the aluminum electrode 2, and the aluminum electrode 2 is formed on the insulating film. It has an embedded shape.

【００６１】次に、シリコンチップ１を３００℃に加熱
し、図１（ｂ）に示すように、キャピラリ５を下降させ
ることにより、パラジウムボール６をアルミニウム電極
２の上に１５０ｇｆの加重で押圧し、パラジウムボール
６に、１．５Ｗの出力の超音波振動を１５０ｍ秒間与え
た。その結果、パラジウムボール６は、アルミ箔３を圧
延しながら変形し、アルミ箔３を間に介在した状態でア
ルミニウム電極２と接合された。即ち、パラジウムボー
ル６とアルミ箔３、アルミ箔３とアルミニウム電極２が
それぞれ同時に接合された。Next, the silicon chip 1 is heated to 300 ° C., and the palladium ball 6 is pressed onto the aluminum electrode 2 with a load of 150 gf by lowering the capillary 5 as shown in FIG. The ultrasonic vibration of 1.5 W output was applied to the palladium ball 6 for 150 msec. As a result, the palladium ball 6 was deformed while rolling the aluminum foil 3 and joined to the aluminum electrode 2 with the aluminum foil 3 interposed therebetween. That is, the palladium ball 6 and the aluminum foil 3, and the aluminum foil 3 and the aluminum electrode 2 were simultaneously bonded.

【００６２】その後、パラジウム線４を上方に引っ張っ
て、パラジウムボール６の近傍で切断し、更に、アルミ
箔３を斜め上方に持ち上げるように力を加えることによ
り剥離し、図１（ｃ）に示すように、スタッドバンプ８
を形成した。この場合、アルミ箔３は、押圧部との境界
付近において切断され易くなっているため、押圧部以外
の部分は容易に除去可能である。なお、振動を与えるこ
とにより、バンプ８の周辺でアルミ箔３をより剥離しや
すくすることも可能である。Thereafter, the palladium wire 4 is pulled upward, cut in the vicinity of the palladium ball 6, and further separated by applying a force so as to lift the aluminum foil 3 obliquely upward, as shown in FIG. 1 (c). Like stud bump 8
Was formed. In this case, since the aluminum foil 3 is easily cut in the vicinity of the boundary with the pressing portion, portions other than the pressing portion can be easily removed. By applying vibration, the aluminum foil 3 can be more easily peeled around the bump 8.

【００６３】以上のように形成された突起電極について
接合強度を試験し、かつシリコンチップの割れの有無を
観察した。接合強度の試験は、ボールに対し剪断力（シ
ェア）を加え、引き剥がすのに必要な力を測定すること
により行った。その結果を下記表に示す。また、シリコ
ンチップの割れは、シェア試験後の破断面を観察し、破
断面がシリコンチップの内部ならば割れの可能性ありと
判断したが、本実施例では、割れ、陥没ともに観察され
なかった。The bonding strength of the protruding electrodes formed as described above was tested, and the presence or absence of cracks in the silicon chip was observed. The bonding strength test was performed by applying a shearing force (shear) to the ball and measuring the force required to peel the ball. The results are shown in the table below. In addition, the crack of the silicon chip was observed by observing the fracture surface after the shear test, and if the fracture surface was inside the silicon chip, it was determined that there was a possibility of the fracture. However, in this example, neither the fracture nor the depression was observed. .

【００６４】なお、研磨により接合部の断面を露出し、
接合界面を観察することによっても、シリコンチップの
割れの有無を判断することができる。 実施例２ 実施例１において、金属スタッド（パラジウムボール）
６を、アルミ箔３を間に介してアルミニウム電極２と接
合した後、パラジウム線４を切断することなく、ループ
状に外部に導き、外部リード（図示せず）と接続した。
形成されたワイヤボンディングについて接合強度を試験
し、かつシリコンチップの割れの有無を観察したとこ
ろ、実施例１と同様の結果が得られた。The cross section of the joint is exposed by polishing.
By observing the bonding interface, it is possible to determine whether or not the silicon chip is cracked. Example 2 In Example 1, a metal stud (palladium ball) was used.
6 was joined to the aluminum electrode 2 with the aluminum foil 3 interposed therebetween, then led to the outside in a loop without cutting the palladium wire 4, and connected to an external lead (not shown).
When the bonding strength of the formed wire bonding was tested and the presence or absence of cracks in the silicon chip was observed, the same results as in Example 1 were obtained.

【００６５】実施例３ 図２に示す手順に従って、突起電極を形成した。即ち、
まず、図２（ａ）に示すように、シリコンチップ１に形
成された、１００μｍ角、厚さ１μｍのアルミニウム電
極２の上に、厚さ３５μｍのアルミ箔１１を載置した。
次いで、シリコンチップ１を３００℃に加熱し、中空の
キャピラリ１２を下降させて、アルミ箔１１をアルミニ
ウム電極２に、１５０ｇｆの加重で押圧して、１．５Ｗ
の出力の超音波振動を１５０ｍ秒間与え、アルミ箔１１
をアルミニウム電極２に接合した。Example 3 A protruding electrode was formed according to the procedure shown in FIG. That is,
First, as shown in FIG. 2A, a 35 μm thick aluminum foil 11 was placed on a 100 μm square, 1 μm thick aluminum electrode 2 formed on a silicon chip 1.
Next, the silicon chip 1 is heated to 300 ° C., the hollow capillary 12 is lowered, and the aluminum foil 11 is pressed against the aluminum electrode 2 with a load of 150 gf to obtain 1.5 W
Of ultrasonic vibration for 150 msec.
Was bonded to the aluminum electrode 2.

【００６６】その後、アルミ箔１１を斜め上方に持ち上
げるように力を加えることにより剥離し、図２（ｂ）に
示すように、圧延層１３を形成した。次に、実施例１と
同様にして、金属スタッド（パラジウムボール）６（図
示せず）をアルミニウム電極２の上に、５５ｇｆの加重
で押圧し、パラジウムボール６に０．５５Ｗの出力の超
音波振動を５５ｍ秒間与えた。その結果、パラジウムボ
ール６は変形して、圧延層１３を間に介在した状態でア
ルミニウム電極２と接合された。その後、パラジウム線
（図示せず）を上方に引っ張って、パラジウムボール６
の近傍で切断し、図１（ｃ）に示すようなバンプ８を形
成し、突起電極とした。Thereafter, the aluminum foil 11 was peeled off by applying a force so as to lift it obliquely upward, and a rolled layer 13 was formed as shown in FIG. 2 (b). Next, in the same manner as in Example 1, a metal stud (palladium ball) 6 (not shown) is pressed onto the aluminum electrode 2 with a load of 55 gf, and an ultrasonic wave having an output of 0.55 W is applied to the palladium ball 6. Vibration was applied for 55 msec. As a result, the palladium ball 6 was deformed and joined to the aluminum electrode 2 with the rolling layer 13 interposed therebetween. Thereafter, a palladium wire (not shown) is pulled upward, and a palladium ball 6 is drawn.
And bumps 8 were formed as shown in FIG. 1 (c) to form bump electrodes.

【００６７】なお、アルミ箔１１を押圧するキャピラリ
１２は、中空のものに限らず、棒状のものを用い、図２
（ｃ）に示すような平坦な圧延層１４を形成することも
可能である。The capillary 12 for pressing the aluminum foil 11 is not limited to a hollow one, but may be a rod-shaped one.
It is also possible to form a flat rolled layer 14 as shown in FIG.

【００６８】以上のように形成された突起電極につい
て、実施例１と同様にして、接合強度を試験し、かつシ
リコンチップの割れの有無を観察した。接合強度の測定
結果を下記表に示す。また、シリコンチップの割れ、陥
没ともに観察されなかった。For the protruding electrodes formed as described above, the bonding strength was tested in the same manner as in Example 1, and the presence or absence of cracks in the silicon chip was observed. The measurement results of the bonding strength are shown in the following table. Neither cracking nor sinking of the silicon chip was observed.

【００６９】実施例４ 実施例３において、金属スタッド（パラジウムボール）
６を、圧延層１３を間に介してアルミニウム電極２と接
合した後、パラジウム線４を切断することなく、ループ
状に外部に導き、外部リード（図示せず）と接続した。
形成されたワイヤボンディングについて接合強度を試験
し、かつシリコンチップの割れの有無を観察したとこ
ろ、実施例３と同様の結果が得られた。Example 4 In Example 3, a metal stud (palladium ball) was used.
6 was joined to the aluminum electrode 2 with the rolled layer 13 interposed therebetween, then led to the outside in a loop without cutting the palladium wire 4, and connected to an external lead (not shown).
When the bonding strength of the formed wire bonding was tested and the presence or absence of cracks in the silicon chip was observed, the same results as in Example 3 were obtained.

【００７０】実施例５ 図３に示す手順に従って、突起電極を形成した。即ち、
まず、シリコンチップ１を３００℃に加熱し、図３
（ａ）に示すように、シリコンチップ１に形成された、
１００μｍ角、厚さ１μｍのアルミニウム電極２に、７
０μｍ径のアルミニウム線２１の先端部をキャピラリ２
２によって超音波をかけて押圧した。加重は１５０ｇ
ｆ、超音波の出力は１．５Ｗ、時間は１５０ｍ秒間であ
った。その結果、アルミニウム線２１の先端部は、アル
ミニウム電極２に接合された。Example 5 A protruding electrode was formed according to the procedure shown in FIG. That is,
First, the silicon chip 1 was heated to 300 ° C.
(A) As shown in FIG.
100 μm square, 1 μm thick aluminum electrode 2
The tip of the aluminum wire 21 having a diameter of 0 μm is
Ultrasonic waves were applied by means of No. 2. Weight is 150g
f, the output of the ultrasonic wave was 1.5 W and the time was 150 msec. As a result, the tip of the aluminum wire 21 was joined to the aluminum electrode 2.

【００７１】次いで、接合部の近傍においてアルミニウ
ム線２１を切断し、図３（ｂ）に示すように、台座状の
突起からなる緩衝層２３を形成した。以下、実施例２と
同様の条件で、パラジウムボールを緩衝層２３に接合
し、その上に図１（ｃ）に示すようなバンプ８を形成し
た。Next, the aluminum wire 21 was cut in the vicinity of the joint to form a buffer layer 23 composed of a pedestal-shaped projection as shown in FIG. 3B. Thereafter, a palladium ball was bonded to the buffer layer 23 under the same conditions as in Example 2, and a bump 8 as shown in FIG. 1C was formed thereon.

【００７２】以上のように形成されたバンプについて、
実施例１と同様にして、接合強度を試験し、かつシリコ
ンチップの割れの有無を観察した。接合強度の測定結果
を下記表に示す。また、シリコンチップの割れ、陥没と
もに観察されなかった。With respect to the bumps formed as described above,
In the same manner as in Example 1, the bonding strength was tested, and the presence or absence of cracks in the silicon chip was observed. The measurement results of the bonding strength are shown in the following table. Neither cracking nor sinking of the silicon chip was observed.

【００７３】なお、緩衝層２３を形成するワイヤとして
は、アルミニウムに限らず、金を用いることも可能であ
る。金ワイヤを用いる場合には、放電によって金ワイヤ
の先端にボールを形成し、これをアルミニウム電極に押
圧して緩衝層２３を形成してもよい。The wire forming the buffer layer 23 is not limited to aluminum, but may be gold. When a gold wire is used, a ball may be formed at the tip of the gold wire by electric discharge, and this may be pressed against an aluminum electrode to form the buffer layer 23.

【００７４】実施例６ 実施例５において、パラジウムボールを、緩衝層２３を
間に介してアルミニウム電極２と接合した後、パラジウ
ム線を切断することなく、ループ状に外部に導き、外部
リード（図示せず）と接続した。形成されたワイヤボン
ディングについて接合強度を試験し、かつシリコンチッ
プの割れの有無を観察したところ、実施例５と同様の結
果が得られた。Example 6 In Example 5, after the palladium ball was joined to the aluminum electrode 2 with the buffer layer 23 interposed therebetween, the palladium wire was led outside in a loop without cutting, and the external lead (FIG. (Not shown). When the bonding strength of the formed wire bonding was tested and the presence or absence of cracks in the silicon chip was observed, the same results as in Example 5 were obtained.

【００７５】比較例 図４に示す手順に従って、突起電極を形成した。即ち、
まず、図４（ａ）に示すように、４０μｍの線径のパラ
ジウム線３１をキャピラリ３２に通し、放電によって８
０μｍ径のパラジウムボール３３を形成した。次いで、
図４（ｂ）に示すように、シリコンチップ１を３００℃
に加熱し、キャピラリ３２を下降させることにより、パ
ラジウムボール３３をアルミニウム電極２の上に５５ｇ
ｆの加重で押圧し、パラジウムボール３３に、０．５５
Ｗの出力の超音波振動を５５ｍ秒間与えた。その結果、
パラジウムボール６は変形し、アルミニウム電極２と接
合された。Comparative Example A protruding electrode was formed according to the procedure shown in FIG. That is,
First, as shown in FIG. 4A, a palladium wire 31 having a wire diameter of 40 μm is passed through a capillary 32 and discharged by discharging.
A palladium ball 33 having a diameter of 0 μm was formed. Then
As shown in FIG. 4B, the silicon chip 1 is heated at 300 ° C.
The palladium ball 33 is placed on the aluminum electrode 2 by 55 g by lowering the capillary 32.
f, and press the palladium ball 33 with 0.55
Ultrasonic vibration of W output was applied for 55 msec. as a result,
The palladium ball 6 was deformed and joined to the aluminum electrode 2.

【００７６】その後、パラジウム線３１を上方に引っ張
って、パラジウムボール３３の近傍で切断し、図４
（ｃ）に示すように、バンプ３４を形成した。以上のよ
うに形成されたバンプについて接合強度を試験し、かつ
シリコンチップの割れの有無を観察した。接合強度の試
験結果を下記表に示す。また、シリコンチップの割れに
ついては、本比較例では、図４（ｃ）に示すように、割
れ３５が観察された。Thereafter, the palladium wire 31 is pulled upward and cut in the vicinity of the palladium ball 33.
As shown in (c), the bump 34 was formed. The bonding strength of the bumps formed as described above was tested, and the presence or absence of cracks in the silicon chip was observed. The test results of the bonding strength are shown in the table below. Regarding the crack of the silicon chip, in this comparative example, as shown in FIG. 4C, a crack 35 was observed.

【００７７】[0077]

【表１】 [Table 1]

【００７８】上記表から明らかなように、従来のボール
ボンディング法による比較例では、平均３５．２ｇｆの
剪断力によりバンプが剥がれたが、実施例１、３、５で
は、それぞれ平均１２１．３ｇｆ、７６．８ｇｆ、７
３．９ｇｆの剪断力によりバンプが剥がれ、本発明の方
法により得たバンプは、高い接合強度を有することがわ
かる。As is clear from the above table, in the comparative example using the conventional ball bonding method, the bump was peeled off by an average shear force of 35.2 gf, but in Examples 1, 3 and 5, the average was 121.3 gf, respectively. 76.8 gf, 7
The bump was peeled off by the shear force of 3.9 gf, and it was found that the bump obtained by the method of the present invention had high bonding strength.

【００７９】なお、一般に、バンプは５０ｇｆ以上のシ
ェア強度を有することが望ましいとされており、従来の
方法では安定して５０ｇｆ以上のシェア強度を得ること
が困難であるが、本発明の方法では、安定して５０ｇｆ
を越えるシェア強度を得ることが可能である。また、比
較例では、実施例１よりも低い加重および超音波出力の
条件を用いたが、この条件よりも高い条件を採用する
と、シリコンチップの割れがひどくなってしまう。Generally, it is desirable that the bump has a shear strength of 50 gf or more, and it is difficult to stably obtain a shear strength of 50 gf or more by the conventional method. , Stable 50gf
It is possible to obtain a shear strength exceeding. Further, in the comparative example, the conditions of the weight and the ultrasonic output lower than those in the first embodiment were used. However, if the conditions higher than these conditions were adopted, the silicon chip would be severely cracked.

【００８０】実施例７ 実施例１にて作製した突起電極に、図５（ａ）に示すよ
うに、半田５５を接合したところ、金属箔を用いないと
きに比べ、半田高さが高くなった。これは、金属箔を用
いた突起電極では、図５（ａ）のＡ部を拡大して示す図
５（ｂ）に示すように、バンプ４８とＡｌ電極２との間
に金属箔４１が噛み込んだ形となり、その結果、半田は
Ａｌ電極には到達せず、金属箔４１により下で支えられ
た形となり、半田層が高くなったものである。Example 7 As shown in FIG. 5A, when the solder 55 was joined to the protruding electrode manufactured in Example 1, the solder height was higher than when no metal foil was used. . This is because, in the protruding electrode using a metal foil, as shown in FIG. 5 (b), which enlarges part A of FIG. 5 (a), the metal foil 41 is caught between the bump 48 and the Al electrode 2. As a result, the solder did not reach the Al electrode, but was supported below by the metal foil 41, and the solder layer was raised.

【００８１】実施例８ 図６に示すように、ユニット７０により、Ａｌ箔テープ
６２を、ワイヤボンディング装置のステージ６３上に載
置された半導体チップ６１上に固定した。Ａｌ箔テープ
６２は、図７に示すように、厚さ０．２ｍｍの、開口部
６５を有する銅製フレーム６４の一方の面に、厚さ１５
μｍのＡｌ箔６６を張力を加えた状態で接着したものを
用いた。また、Ａｌ箔テープ６２の幅は２０ｍｍ、開口
部６５の径は１０ｍｍであった。なお、フレーム６４
は、銅製に限らず、鉄、樹脂等でもよい。Example 8 As shown in FIG. 6, an Al foil tape 62 was fixed on a semiconductor chip 61 mounted on a stage 63 of a wire bonding apparatus by a unit 70. As shown in FIG. 7, the Al foil tape 62 has a thickness of 15 mm on one surface of a copper frame 64 having an opening 65 and a thickness of 0.2 mm.
The one in which the Al foil 66 of μm was adhered under tension was used. The width of the Al foil tape 62 was 20 mm, and the diameter of the opening 65 was 10 mm. The frame 64
Is not limited to copper, but may be iron, resin, or the like.

【００８２】次いで、図８に示すように、半導体チップ
６１のＡｌ電極パッド６７上に、Ａｌ箔テープ６２の開
口部６５がくるように、Ａｌ箔テープ６２を配置した。
そして、ワイヤボンディング法により、キャピラリ７１
の先端に形成した１００μｍ径の銅ボール７２を、Ａｌ
箔６６を間に介してＡｌ電極パッド６７に押しつけ、ス
テージ温度２５０℃、超音波出力１．５Ｗ、荷重１５０
ｇｆで接合した。なお、金属ボール７２は、銅に限ら
ず、金、パラジウム等でもよい。Next, as shown in FIG. 8, the Al foil tape 62 was placed on the Al electrode pad 67 of the semiconductor chip 61 such that the opening 65 of the Al foil tape 62 came.
Then, the capillary 71 is formed by a wire bonding method.
100 μm diameter copper ball 72 formed at the tip of
The foil 66 is pressed against the Al electrode pad 67 with a stage temperature of 250 ° C., an ultrasonic output of 1.5 W, and a load of 150.
gf. The metal ball 72 is not limited to copper, but may be gold, palladium, or the like.

【００８３】その後、図９に示すように、ワイヤを引上
げ、ボール接続部７３においてワイヤを切断し、バンプ
６８を形成した。なお、キャピラリ７１の先端の周囲を
ボール７２に衝突させることにより、ワイヤを切断して
もよい。次に、Ａｌ箔テープ６２をユニット７０ととも
に真上に５ｍｍ引上げ、図１０に示すように、バンプ６
８の周囲において、Ａｌ箔テープ６２を切断した。Thereafter, as shown in FIG. 9, the wire was pulled up, and the wire was cut at the ball connection portion 73 to form a bump 68. The wire may be cut by colliding the periphery of the tip of the capillary 71 with the ball 72. Next, the Al foil tape 62 was pulled up 5 mm directly above the unit 70 together with the unit 70, and as shown in FIG.
Around 8, the Al foil tape 62 was cut.

【００８４】これらの工程、即ち、フレーム６４の開口
部６５の位置合わせのためのＡｌ箔テープ６２の供給、
バンプ６８の形成、Ａｌ箔テープ６２の引上げは連続し
て行われる。そして、これらの工程の繰り返しにより、
複数のバンプの形成が可能であった。These steps, namely, supply of the Al foil tape 62 for positioning the opening 65 of the frame 64,
The formation of the bump 68 and the pulling up of the Al foil tape 62 are performed continuously. And by repeating these steps,
A plurality of bumps could be formed.

【００８５】その後、図１１に示すように、半田６９を
上記のようにして形成したバンプ６８に供給して、バン
プ６８を有する半導体チップ６１を、基板８１にフェー
スダウンで一括して接続した。Thereafter, as shown in FIG. 11, solder 69 was supplied to the bumps 68 formed as described above, and the semiconductor chips 61 having the bumps 68 were connected to the substrate 81 face-to-face.

【００８６】なお、製品によっては、上述のように、ワ
イヤボンディングにより銅ボール７２をＡｌ箔６６を間
に介してＡｌ電極パッド６７に接合したのち、ワイヤを
切断することなく、Ａｌ箔テープ６２を切断し、ワイヤ
を外部リードに接続してもよい。As described above, depending on the product, after bonding the copper ball 72 to the Al electrode pad 67 via the Al foil 66 by wire bonding as described above, the Al foil tape 62 is cut without cutting the wire. It may be cut and the wires connected to external leads.

【００８７】実施例９ 図１２に示すように、２０μｍの厚さのＡｌ箔９１の片
面に、１μｍの厚さの銅メッキ層９２を形成し、テープ
９３を作製した。このテープ９３を、図１３に示すよう
に、棒状のキャピラリ９４を用いて、ステージ温度１５
０℃、超音波１Ｗ、荷重１２０ｇｆで、テープ９３を半
導体チップ９５のＡｌパッド９６に押し当て、テープ９
３をＡｌ電極パッド９６に接合した。EXAMPLE 9 As shown in FIG. 12, a copper plating layer 92 having a thickness of 1 μm was formed on one surface of an Al foil 91 having a thickness of 20 μm, and a tape 93 was manufactured. As shown in FIG. 13, the tape 93 is moved to a stage temperature 15 using a rod-shaped capillary 94.
The tape 93 is pressed against the Al pad 96 of the semiconductor chip 95 at 0 ° C., 1 W of ultrasonic wave, and a load of 120 gf, and the tape 9 is pressed.
3 was joined to an Al electrode pad 96.

【００８８】なお、テープ９３は、Ａｌ箔に限らず、
銅、半田、金等の箔を用いても、またこれらの箔の多層
膜を用いて作製してもよい。また、テープ９３は、図１
４に示すように、Ａｌ箔９１の片面に、ニッケル層９７
および銅層９８を順次メッキにより形成したものでもよ
い。即ち、半田との濡れ性の良好な金属である銅とＡｌ
箔との間に、半田の拡散を防止する高融点金属であるニ
ッケルを介在させてもよい。The tape 93 is not limited to the Al foil.
A foil such as copper, solder, or gold may be used, or a multilayer film of these foils may be used. The tape 93 is shown in FIG.
As shown in FIG. 4, a nickel layer 97 is formed on one side of the Al foil 91.
And the copper layer 98 may be formed by successive plating. That is, copper and Al which are metals having good wettability with solder
Nickel, which is a high melting point metal for preventing diffusion of solder, may be interposed between the foil.

【００８９】次いで、図１５に示すように、支持ロール
９９によりテープ９３に張力を加え、この状態で、テー
プ９３の接合部１００を中心に時計方向に、支持ロール
９９を９０°回転させた後、逆方向に９０°回転させ、
接合部１００の周辺部でテープ９３を切断した。Next, as shown in FIG. 15, a tension is applied to the tape 93 by the support roll 99, and in this state, the support roll 99 is rotated 90 ° clockwise around the joint 100 of the tape 93. , Rotate 90 degrees in the opposite direction,
The tape 93 was cut around the joint 100.

【００９０】この一連の動作を繰り返して、複数の突起
電極を形成した。なお、本実施例では、支持ロール９９
を接合部１００を中心に回転させることによりテープ９
３を切断したが、支持ロール９９に水平方向または垂直
方向に振動を与えて、テープ９３を半導体チップと相対
的に移動させることにより、テープ９３を切断してもよ
い。By repeating this series of operations, a plurality of protruding electrodes were formed. In this embodiment, the support roll 99
The tape 9 is rotated by rotating the
Although the tape 3 is cut, the tape 93 may be cut by applying a vibration to the support roll 99 in the horizontal direction or the vertical direction to move the tape 93 relative to the semiconductor chip.

【００９１】実施例１０ 図１６に示すように、１０μｍの厚さのＡｌ箔テープ１
０１をエッチングし、１００μｍ径の一対の半環状切り
欠き部１０２を複数対形成した。なお、切り欠き部１０
２は、エッチングに限らず、スタンピング等により形成
してもよい。Example 10 As shown in FIG. 16, an Al foil tape 1 having a thickness of 10 μm
01 was etched to form a plurality of pairs of semi-circular cutouts 102 having a diameter of 100 μm. The notch 10
2 is not limited to etching, and may be formed by stamping or the like.

【００９２】次いで、図１７（ａ）に示すように、この
テープ１０１を半導体チップ１０３上に設置し、半導体
チップ１０３のＡｌパッド１０４上に切り欠き部１０２
の中心を合わせた。そして、図１７（ｂ）に示すよう
に、キャピラリ１１１の先端に形成した１００μｍ径の
銅ボール１１２を、テープ１０１を間に介してＡｌ電極
パッド１０４に押しつけ、接合した。Next, as shown in FIG. 17A, this tape 101 is set on a semiconductor chip 103, and a notch 102 is formed on an Al pad 104 of the semiconductor chip 103.
Centered. Then, as shown in FIG. 17B, a copper ball 112 having a diameter of 100 μm formed at the tip of the capillary 111 was pressed against the Al electrode pad 104 via the tape 101 and joined.

【００９３】その後、ワイヤを引上げ、ボール接続部に
おいてワイヤを切断し、バンプを形成した。次に、テー
プ１０１を軽く上方に移動させることにより、テープ１
０１を切り欠き部１０２において切断した。Thereafter, the wire was pulled up, and the wire was cut at the ball connection portion to form a bump. Next, the tape 101 is slightly moved upward to
01 was cut at the notch 102.

【００９４】なお、切り欠き部は、図１８に示すように
一対の半環状切り欠き部に限らず、一対の直線状切り欠
き部１２１であってもよい。また、切り欠き部は、貫通
しているものに限らず、溝状のものであってもよい。更
に、切り欠き部は、半導体チップ上に設置する前に、あ
らかじめ形成しておき、半導体チップのＡｌ電極パッド
上に切り欠き部の中心を合わせて、接合してもよいが、
図２３に示すように、切り欠き部が形成されていないテ
ープ１０１を半導体チップ１０３上に設置した後、爪１
０５により、切り欠き部を形成し、次いで、接合を行っ
てもよい。The notch is not limited to a pair of semicircular notches as shown in FIG. 18, but may be a pair of linear notches 121. Further, the notch is not limited to the penetrating one and may be a groove. Further, the notch may be formed in advance before being placed on the semiconductor chip, and the center of the notch may be aligned on the Al electrode pad of the semiconductor chip and joined.
As shown in FIG. 23, after the tape 101 having no notch formed thereon is placed on the semiconductor chip 103,
According to 05, a notch may be formed, and then joining may be performed.

【００９５】[0095]

【発明の効果】以上詳述したように、本発明の方法によ
ると、半導体素子の電極とボールとの間に金属箔、また
は金属緩衝層を介在させているため、これらがボールを
電極に押圧する際の衝撃を吸収し、それによって、半導
体素子が損傷することなく、高い接合強度の突起電極お
よびワイヤボンディングを容易に形成することが可能で
ある。As described above in detail, according to the method of the present invention, since the metal foil or the metal buffer layer is interposed between the electrode of the semiconductor element and the ball, these press the ball against the electrode. In this case, a bump at the time of bonding can be absorbed, and thereby, a bump electrode and wire bonding having high bonding strength can be easily formed without damaging the semiconductor element.

【００９６】また、金属箔、または金属緩衝層の存在の
ため、ボールのつぶれが小さくて済み、高い突起電極高
を得ることがが可能であるため、半導体素子と基板との
接合に非常に有利である。更に、特にスタッドバンプお
よびボンディングワイヤーとして銅やパラジウムを用い
た場合には、コストを下げることが出来るとともに、半
田との間で金属間化合物を形成して接合が脆化する現象
を防止することが可能である。Further, the presence of the metal foil or the metal buffer layer allows the ball to be crushed little and a high protruding electrode height can be obtained, which is very advantageous for bonding the semiconductor element to the substrate. It is. Further, in particular, when copper or palladium is used as the stud bump and the bonding wire, the cost can be reduced, and the phenomenon that the intermetallic compound is formed between the solder and the solder to prevent the bonding from becoming brittle can be prevented. It is possible.

【００９７】また、金属箔を用いる場合には、金属箔に
均一に張力をかけて切断することにより、または金属箔
テープの接合部の周辺にあらかじめ切り欠きを形成して
おくことにより、切断の容易にかつ確実に行うことが可
能である。When a metal foil is used, the metal foil is cut by applying a uniform tension, or a notch is formed in the vicinity of the joint of the metal foil tape in advance, so that the metal foil is cut. It can be done easily and reliably.

【図面の簡単な説明】[Brief description of the drawings]

【図１】実施例１に係る突起電極の形成工程を示す断面
図。FIG. 1 is a sectional view showing a step of forming a bump electrode according to a first embodiment.

【図２】実施例３に係る突起電極の形成工程を示す断面
図。FIG. 2 is a cross-sectional view illustrating a step of forming a bump electrode according to a third embodiment.

【図３】実施例５に係る突起電極の形成工程を示す断面
図。FIG. 3 is a cross-sectional view illustrating a step of forming a bump electrode according to a fifth embodiment.

【図４】比較例に係る突起電極の形成工程を示す断面
図。FIG. 4 is a sectional view showing a step of forming a bump electrode according to a comparative example.

【図５】実施例１により得た突起電極を従来例と比較し
て示す断面図。FIG. 5 is a cross-sectional view showing a projection electrode obtained in Example 1 in comparison with a conventional example.

【図６】実施例８で用いたＡｌ箔テープ供給ユニットを
備えたワイヤボンディング装置を示す図。FIG. 6 is a diagram showing a wire bonding apparatus provided with an Al foil tape supply unit used in Example 8.

【図７】実施例８で用いたＡｌ箔テープを示す図。FIG. 7 is a view showing an Al foil tape used in Example 8.

【図８】実施例８に係る突起電極の形成工程を示す断面
図。FIG. 8 is a sectional view showing a step of forming a bump electrode according to an eighth embodiment.

【図９】実施例８に係る突起電極の形成工程を示す断面
図。FIG. 9 is a cross-sectional view illustrating a step of forming a bump electrode according to an eighth embodiment.

【図１０】実施例８に係る突起電極の形成工程を示す断
面図。FIG. 10 is a sectional view showing a step of forming a bump electrode according to an eighth embodiment.

【図１１】実施例８により得た半導体チップを基板にフ
ェースダウンで一括して接続した状態を示す断面図。FIG. 11 is a sectional view showing a state in which the semiconductor chips obtained in Example 8 are collectively connected face-down to a substrate.

【図１２】実施例９で用いたＡｌ箔テープを示す図。FIG. 12 is a view showing an Al foil tape used in Example 9.

【図１３】実施例９に係る突起電極の形成工程を示す断
面図。FIG. 13 is a cross-sectional view illustrating a step of forming a bump electrode according to a ninth embodiment.

【図１４】Ａｌ箔テープの他の例を示す図。FIG. 14 is a view showing another example of the Al foil tape.

【図１５】実施例９に係る突起電極の形成工程を示す
図。FIG. 15 is a view showing a step of forming a bump electrode according to a ninth embodiment.

【図１６】実施例１０で用いたＡｌ箔テープを示す図。FIG. 16 is a view showing an Al foil tape used in Example 10.

【図１７】実施例１０に係る突起電極の形成工程を示す
断面図。FIG. 17 is a cross-sectional view illustrating a step of forming the bump electrode according to the tenth embodiment.

【図１８】Ａｌ箔テープの他の例を示す図。FIG. 18 is a view showing another example of the Al foil tape.

【図１９】実施例１０に係る突起電極の形成工程の他の
例を示す断面図。FIG. 19 is a sectional view showing another example of the process of forming the bump electrode according to the tenth embodiment.

【図２０】本発明に使用されるワイヤボンディング装置
（超音波接合装置）の概要を示す図。FIG. 20 is a diagram showing an outline of a wire bonding apparatus (ultrasonic bonding apparatus) used in the present invention.

【符号の説明】[Explanation of symbols]

１，６１，９５，１０３…シリコンチップ ２，９６，６７，１０４…電極パッド ３，１１，４１…金属箔 ４，２１，３１，４４，２１０…ワイヤ ５，１２，２２，３２，７１，２０４…キャピラリ ６，３３，４６，７２…ボール ８，３４，４８，６８…スタッドバンプ ５１…型 ５３…ホットプレート ５５…半田層 ６１，９５，１０３，２０２…半導体チップ ６２，９３…Ａｌ箔テープ ６４…銅製フレーム ７０…ユニット ７３…ボール接続部 ８１…基板 ９９…支持ロール １０２，１２１…切り欠き部 １０５…爪 ２０１…ステージ ２０３…ボンディングヘッド ２０５…トランスジューサ ２０６…ワイヤクランパ ２０７…ＸＹテーブル ２０８…Ｚ駆動モータ ２０９…カメラ ２１０…ワイヤ ２１１…スプール 1, 61, 95, 103 ... silicon chip 2, 96, 67, 104 ... electrode pad 3, 11, 41 ... metal foil 4, 21, 31, 44, 210 ... wire 5, 12, 22, 32, 71, 204 ... Capillary 6,33,46,72 ... Ball 8,34,48,68 ... Stud bump 51 ... Type 53 ... Hot plate 55 ... Solder layer 61,95,103,202 ... Semiconductor chip 62,93 ... Al foil tape 64 ... Copper frame 70 ... Unit 73 ... Ball connection part 81 ... Substrate 99 ... Support rolls 102 and 121 ... Notch part 105 ... Claw 201 ... Stage 203 ... Bonding head 205 ... Transducer 206 ... Wire clamper 207 ... XY table 208 ... Z drive Motor 209: Camera 210: Wire 211: Spool

───────────────────────────────────────────────────── フロントページの続き (72)発明者 湯沢 均 東京都千代田区丸の内２丁目６番１号 古 河電気工業株式会社内 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Hitoshi Yuzawa 2-6-1 Marunouchi, Chiyoda-ku, Tokyo Furukawa Electric Co., Ltd.

Claims (38)

【特許請求の範囲】[Claims] 【請求項１】 電極パッドと、この電極パッドに接合さ
れた金属スタッドとを有する半導体素子であって、前記
金属スタッドは、金属箔を間に介して前記電極パッドに
接合されていることを特徴とする半導体素子。1. A semiconductor device having an electrode pad and a metal stud joined to the electrode pad, wherein the metal stud is joined to the electrode pad via a metal foil. Semiconductor element. 【請求項２】 電極パッドと、この電極パッドに接合さ
れたボンディングワイヤとを有する半導体素子であっ
て、前記ボンディングワイヤは、金属箔を間に介して前
記電極パッドに接合されていることを特徴とする半導体
素子。2. A semiconductor device having an electrode pad and a bonding wire bonded to the electrode pad, wherein the bonding wire is bonded to the electrode pad via a metal foil. Semiconductor element. 【請求項３】 前記金属箔は、前記金属スタッドまたは
ボンディングワイヤを構成する金属材料よりも軟質の金
属材料からなることを特徴とする請求項１または２に記
載の半導体素子。3. The semiconductor device according to claim 1, wherein the metal foil is made of a metal material softer than a metal material forming the metal stud or the bonding wire. 【請求項４】 前記金属箔が、アルミニウム、銀、金、
半田、これらの積層箔、またはこれらを被覆した箔から
なることを特徴とする請求項１または２に記載の半導体
素子。4. The method according to claim 1, wherein the metal foil is made of aluminum, silver, gold,
The semiconductor device according to claim 1, comprising a solder, a laminated foil thereof, or a foil covering the same. 【請求項５】 前記金属箔の厚さは、５〜１００μｍで
あることを特徴とする請求項１〜４のいずれか１項に記
載の半導体素子。5. The semiconductor device according to claim 1, wherein said metal foil has a thickness of 5 to 100 μm. 【請求項６】 前記金属スタッドまたは前記ボンディン
グワイヤを構成する金属材料は、パラジウムまたは銅で
あることを特徴とする請求項１〜５のいずれか１項に記
載の半導体素子。6. The semiconductor device according to claim 1, wherein the metal material forming the metal stud or the bonding wire is palladium or copper. 【請求項７】 金属材料からなるワイヤの先端部を溶融
してボールを形成する工程と、半導体チップの電極上に
金属箔を間に介して前記ボールを配置する工程と、前記
電極、金属箔およびボールを相互に接合する工程と、前
記ボールからワイヤを切断して、前記電極上にスタッド
バンプを形成する工程とを具備することを特徴とする突
起電極の形成方法。7. A step of melting a tip end of a wire made of a metal material to form a ball, a step of arranging the ball on a semiconductor chip electrode with a metal foil interposed therebetween, And bonding the ball to each other, and cutting a wire from the ball to form a stud bump on the electrode. 【請求項８】 前記金属箔は、前記ボールを接合する前
にあらかじめ前記電極上に押圧され、前記電極に接合さ
れることを特徴とする請求項７に記載の突起電極の形成
方法。8. The method according to claim 7, wherein the metal foil is pressed onto the electrode before bonding the ball and is bonded to the electrode. 【請求項９】 前記金属箔は、前記ワイヤを構成する金
属材料よりも軟質の金属材料からなることを特徴とする
請求項７または８に記載の突起電極の形成方法。9. The method according to claim 7, wherein the metal foil is made of a metal material softer than a metal material forming the wire. 【請求項１０】 前記金属箔は、アルミニウム、銀、
金、半田、これらの積層箔、またはこれらを被覆した箔
であることを特徴とする請求項７〜９のいずれか１項に
記載の突起電極の形成方法。10. The metal foil is made of aluminum, silver,
The method for forming a bump electrode according to claim 7, wherein the bump electrode is gold, solder, a laminated foil of these, or a foil covering these. 【請求項１１】 前記金属箔の厚さは、５〜１００μｍ
であることを特徴とする請求項７〜１０のいずれか１項
に記載の突起電極の形成方法。11. The metal foil has a thickness of 5 to 100 μm.
The method for forming a bump electrode according to any one of claims 7 to 10, wherein 【請求項１２】 前記ワイヤを構成する金属材料は、パ
ラジウム、銅または金であることを特徴とする請求項７
〜１１のいずれか１項に記載の突起電極の形成方法。12. The metal material forming the wire is palladium, copper or gold.
12. The method for forming a bump electrode according to any one of items 11 to 11. 【請求項１３】 第１の金属材料からなる第１のワイヤ
の先端部または先端部を溶融して得た第１のボールを半
導体チップの電極パッドに押圧する工程と、前記第１の
ワイヤの先端部または第１のボールから第１のワイヤを
切断して、金属緩衝層を形成する工程と、前記第１の金
属材料および金よりも硬質の第２の金属材料からなる第
２のワイヤの先端部を溶融して得た第２のボールを前記
金属緩衝層に押圧する工程と、前記第２のボールから第
２のワイヤを切断して、前記電極上にスタッドバンプを
形成する工程とを具備することを特徴とする突起電極の
形成方法。13. A step of pressing a tip of a first wire made of a first metal material or a first ball obtained by melting a tip of the first wire against an electrode pad of a semiconductor chip; Cutting a first wire from a tip or a first ball to form a metal buffer layer; and forming a second wire made of a second metal material harder than the first metal material and gold. Pressing a second ball obtained by melting the tip against the metal buffer layer, and cutting a second wire from the second ball to form a stud bump on the electrode. A method for forming a bump electrode, comprising: 【請求項１４】 前記第１の金属材料は、アルミニウム
または金であることを特徴とする請求項１３に記載の突
起電極の形成方法。14. The method according to claim 13, wherein the first metal material is aluminum or gold. 【請求項１５】 前記第２の金属材料は、パラジウム、
銅または金であることを特徴とする請求項１３または１
４に記載の突起電極の形成方法。15. The method according to claim 15, wherein the second metal material is palladium,
13. The method according to claim 13, wherein the material is copper or gold.
5. The method for forming a bump electrode according to 4. 【請求項１６】 金属材料からなるワイヤの先端部を溶
融してボールを形成する工程と、半導体チップの電極上
に金属箔を間に介して前記ボールを配置する工程と、前
記電極、金属箔およびボールを接合する工程と、前記ワ
イヤをループ状に導いて、外部リードに接続する工程と
を具備することを特徴とするワイヤボンディング方法。16. A step of melting a tip portion of a wire made of a metal material to form a ball, a step of disposing the ball on a semiconductor chip electrode with a metal foil interposed therebetween, And a step of joining the balls, and a step of guiding the wires in a loop and connecting them to external leads. 【請求項１７】 前記金属箔は、前記ボールを接合する
前にあらかじめ前記電極上に押圧され、前記電極に接合
されることを特徴とする請求項１６に記載のワイヤボン
ディング方法。17. The wire bonding method according to claim 16, wherein the metal foil is pressed on the electrode before bonding the ball and bonded to the electrode. 【請求項１８】 前記金属箔は、前記ワイヤを構成する
金属材料よりも軟質の金属材料からなることを特徴とす
る請求項１６または１７に記載のワイヤボンディング方
法。18. The wire bonding method according to claim 16, wherein the metal foil is made of a metal material softer than a metal material forming the wire. 【請求項１９】 前記金属箔は、アルミニウム、銀、
金、半田、これらの積層箔、またはこれらを被覆した箔
であることを特徴とする請求項１６〜１８のいずれか１
項に記載のワイヤボンディング方法。19. The metal foil is made of aluminum, silver,
19. A method according to claim 16, wherein the foil is gold, solder, a laminated foil thereof, or a foil covering these.
Item 14. The wire bonding method according to Item 1. 【請求項２０】 前記金属箔の厚さは、５〜１００μｍ
であることを特徴とする請求項１６〜１９のいずれか１
項に記載のワイヤボンディング方法。20. The metal foil has a thickness of 5 to 100 μm.
20. The method according to claim 16, wherein
Item 14. The wire bonding method according to Item 1. 【請求項２１】 前記ワイヤを構成する金属材料は、パ
ラジウム、銅または金からなる群から選ばれた１種であ
ることを特徴とする請求項１６〜２０のいずれか１項に
記載のワイヤボンディング方法。21. The wire bonding according to claim 16, wherein the metal material forming the wire is one selected from the group consisting of palladium, copper, and gold. Method. 【請求項２２】 第１の金属材料からなる第１のワイヤ
の先端部または先端部を溶融して得た第１のボールを半
導体チップの電極に押圧する工程と、前記第１のワイヤ
の先端部または第１のボールから第１のワイヤを切断し
て、金属緩衝層を形成する工程と、前記第１の金属材料
および金よりも硬質の第２の金属材料からなる第２のワ
イヤの先端部を溶融して得た第２のボールを前記金属緩
衝層に押圧する工程と、前記ワイヤをループ状に導い
て、外部リードに接続する工程とを具備することを特徴
とするワイヤボンディング方法。22. A step of pressing a tip portion of a first wire made of a first metal material or a first ball obtained by melting the tip portion against an electrode of a semiconductor chip, and a tip of the first wire. Cutting a first wire from a portion or a first ball to form a metal buffer layer; and a tip of a second wire made of the first metal material and a second metal material harder than gold. A wire bonding method comprising: a step of pressing a second ball obtained by melting a portion on the metal buffer layer; and a step of guiding the wire in a loop shape and connecting the wire to an external lead. 【請求項２３】 前記第１の金属材料は、アルミニウム
または金であることを特徴とする請求項２２に記載のワ
イヤボンディング方法。23. The wire bonding method according to claim 22, wherein the first metal material is aluminum or gold. 【請求項２４】 前記第２の金属材料は、パラジウム、
銅または金であることを特徴とする請求項２２または２
３に記載のワイヤボンディング方法。24. The second metal material is palladium,
23. The method according to claim 22, wherein the material is copper or gold.
4. The wire bonding method according to 3. 【請求項２５】 金属箔テープを半導体チップの電極上
に供給する工程と、金属材料からなるワイヤの先端部を
溶融してボールを形成する工程と、半導体チップの電極
上に前記金属箔テープを間に介して前記ボールを配置す
る工程と、前記電極、金属箔テープおよびボールを接合
する工程と、前記ボールからワイヤを切断して、前記電
極上にスタッドバンプを形成する工程と、前記金属箔テ
ープと前記半導体チップとを相対移動させて、前記金属
箔テープを前記電極との接合部の周辺において切断する
工程とを具備することを特徴とする突起電極の形成方
法。25. A step of supplying a metal foil tape on an electrode of a semiconductor chip, a step of melting a tip end of a wire made of a metal material to form a ball, and a step of applying the metal foil tape on an electrode of the semiconductor chip. Arranging the ball with an intervening step, joining the electrode, a metal foil tape and a ball, cutting a wire from the ball to form a stud bump on the electrode, Cutting the metal foil tape around the joint with the electrode by relatively moving the tape and the semiconductor chip. 【請求項２６】 前記金属箔テープを前記電極との接合
部の周辺において切断する工程は、前記金属箔テープ
を、水平方向に張力をかけた状態で垂直方向に移動させ
ることにより行われることを特徴とする請求項２５に記
載の突起電極の形成方法。26. A step of cutting the metal foil tape around a junction with the electrode, wherein the step of moving the metal foil tape in the vertical direction while applying tension in the horizontal direction is performed. The method for forming a bump electrode according to claim 25, wherein: 【請求項２７】 前記金属箔テープを前記電極との接合
部の周辺において切断する工程は、前記金属箔テープと
前記電極との接合部を中心に、前記金属箔テープと前記
半導体チップとを相対的に回転または振動させることに
より行われることを特徴とする請求項２５に記載の突起
電極の形成方法。27. The step of cutting the metal foil tape around a junction with the electrode, wherein the step of cutting the metal foil tape and the semiconductor chip relative to each other is centered on the junction between the metal foil tape and the electrode. 26. The method of claim 25, wherein the method is performed by rotating or vibrating the electrode. 【請求項２８】 前記金属箔テープを前記電極との接合
部の周辺において切断する工程は、前記接合部の周辺に
切り欠きが形成された前記金属箔テープと前記半導体チ
ップとを相対的に移動させることにより行われることを
特徴とする請求項２５に記載の突起電極の形成方法。28. The step of cutting the metal foil tape around a joint with the electrode, wherein the metal foil tape having a notch formed around the joint and the semiconductor chip are relatively moved. The method for forming a bump electrode according to claim 25, wherein the method is performed. 【請求項２９】 前記金属箔テープは、多数の開口部を
有するテープ状フレームと、これら開口部に張られた金
属箔とからなり、前記金属箔テープは、前記開口部に張
られた金属箔が前記半導体チップの電極上に位置するよ
うに供給されることを特徴とする請求項２５に記載の突
起電極の形成方法。29. The metal foil tape comprises a tape-shaped frame having a large number of openings, and a metal foil stretched over these openings, wherein the metal foil tape is a metal foil stretched over the openings. 26. The method according to claim 25, wherein is supplied so as to be located on an electrode of the semiconductor chip. 【請求項３０】 前記金属箔テープは、テープの幅に対
応する大きさの開口部を有し、この開口部が前記半導体
チップの電極上に位置するように配置されたユニットを
介して供給され、このユニットとともに上方に引き上げ
られることにより、前記電極との接合部の周辺において
切断されることを特徴とする請求項２５に記載の突起電
極の形成方法。30. The metal foil tape has an opening having a size corresponding to the width of the tape, and the opening is supplied through a unit arranged such that the opening is located on an electrode of the semiconductor chip. 26. The method according to claim 25, wherein the projection electrode is cut up around the joint with the electrode by being pulled up together with the unit. 【請求項３１】 金属箔テープを半導体チップの電極上
に供給する工程と、金属材料からなるワイヤの先端部を
溶融してボールを形成する工程と、半導体チップの電極
上に前記金属箔テープを間に介して前記ボールを配置す
る工程と、前記電極、金属箔テープおよびボールを接合
する工程と、前記金属箔テープと前記半導体チップとを
相対移動させて、前記金属箔テープを前記電極との接合
部の周辺において切断する工程と、前記ワイヤをループ
状に導いて、外部リードに接続する工程とを具備するこ
とを特徴とするワイヤボンディング方法。31. A step of supplying a metal foil tape onto an electrode of a semiconductor chip, a step of melting a tip portion of a wire made of a metal material to form a ball, and a step of applying the metal foil tape on an electrode of the semiconductor chip. Arranging the ball with the electrode, a step of bonding the electrode, the metal foil tape and the ball, and moving the metal foil tape and the semiconductor chip relative to each other so that the metal foil tape is A wire bonding method comprising: a step of cutting around a bonding portion; and a step of guiding the wire in a loop shape and connecting the wire to an external lead. 【請求項３２】 前記金属箔テープを前記電極との接合
部の周辺において切断する工程は、前記金属箔テープ
を、水平方向に張力をかけた状態で垂直方向に移動させ
ることにより行われることを特徴とする請求項３１に記
載のワイヤボンディング方法。32. The step of cutting the metal foil tape around the joint with the electrode is performed by moving the metal foil tape in a vertical direction while applying a tension in a horizontal direction. 32. The wire bonding method according to claim 31, wherein: 【請求項３３】 前記金属箔テープを前記電極との接合
部の周辺において切断する工程は、前記金属箔テープと
前記電極との接合部を中心に、前記金属箔テープと前記
半導体チップとを相対的に回転または振動させることに
より行われることを特徴とする請求項３１に記載のワイ
ヤボンディング方法。33. A step of cutting the metal foil tape around a joint with the electrode, wherein the metal foil tape and the semiconductor chip are relatively positioned around a joint between the metal foil tape and the electrode. 32. The wire bonding method according to claim 31, wherein the method is performed by rotating or vibrating. 【請求項３４】 前記金属箔テープを前記電極との接合
部の周辺において切断する工程は、前記接合部の周辺に
切り欠きが形成された前記金属箔テープと前記半導体チ
ップとを相対的に移動させることにより行われることを
特徴とする請求項３１に記載のワイヤボンディング方
法。34. The step of cutting the metal foil tape around a joint with the electrode, wherein the metal foil tape having a notch formed around the joint and the semiconductor chip are relatively moved. 32. The wire bonding method according to claim 31, wherein the method is performed by performing the following. 【請求項３５】 前記金属箔テープは、多数の開口部を
有するテープ状フレームと、これら開口部に張られた金
属箔とからなり、前記金属箔テープは、前記開口部に張
られた金属箔が前記半導体チップの電極上に位置するよ
うに供給されることを特徴とする請求項３１に記載のワ
イヤボンディング方法。35. The metal foil tape comprises a tape-shaped frame having a large number of openings, and a metal foil stretched over these openings, wherein the metal foil tape comprises a metal foil stretched over the openings. 32. The wire bonding method according to claim 31, wherein is supplied so as to be located on an electrode of the semiconductor chip. 【請求項３６】 前記金属箔テープは、テープの幅に対
応する大きさの開口部を有し、この開口部が前記半導体
チップの電極上に位置するように配置されたユニットを
介して供給され、このユニットとともに上方に引き上げ
られることにより、前記電極との接合部の周辺において
切断されることを特徴とする請求項３１に記載のワイヤ
ボンディング方法。36. The metal foil tape has an opening having a size corresponding to the width of the tape, and the opening is supplied through a unit arranged so that the opening is located on an electrode of the semiconductor chip. 33. The wire bonding method according to claim 31, wherein the wire bonding method is cut off around the joint with the electrode by being pulled upward together with the unit. 【請求項３７】 半導体チップを載置するステージと、
金属材料からなるワイヤを供給および保持し、水平およ
び垂直方向に移動可能なボンディングヘッドとを備えた
超音波接合装置において、枠体の開口部に金属箔を取付
けてなる金属箔テープを前記ステージ上に供給するユニ
ットを備えたことを特徴とする超音波接合装置。37. A stage on which a semiconductor chip is mounted,
In an ultrasonic bonding apparatus having a bonding head that supplies and holds a wire made of a metal material and that can move in a horizontal and vertical direction, a metal foil tape obtained by attaching a metal foil to an opening of a frame is placed on the stage. An ultrasonic bonding apparatus, comprising: a unit for supplying the ultrasonic wave to a substrate. 【請求項３８】 前記金属箔テープを供給するユニット
が、金属箔テープを上方に引き上げる機構を有すること
を特徴とする請求項３７に記載の超音波接合装置。38. The ultrasonic bonding apparatus according to claim 37, wherein the unit for supplying the metal foil tape has a mechanism for lifting the metal foil tape upward.
JP9349449A 1997-01-17 1997-12-18 Semiconductor element, method of forming projecting electrode and wire-bonding method Pending JPH10261664A (en)