JPH0797540A - Ink for ink-jet printer - Google Patents

Abstract

PURPOSE:To provide an ink-jet printing ink consisting of an aqueous dispersion containing a specific compound and colored polyester particles having ionic group, free from blotting of ink on a recording paper, giving extremely excellent image density and exhibiting excellent light resistance. CONSTITUTION:This ink for an ink-jet printer is an aqueous dispersion containing a compound of the formula (R1 is H or halogen; R2 and R3 are H or 1-20C substituent) and a dispersoid consisting of colored polyester particles produced by coloring polyester particles having 20-100eq/ton of ionic group with a dye or pigment. The ink can be produced e.g. by introducing a monomer containing ionic group into a polyester resin to obtain a copolymerized polyester resin containing ionic group, mixing the resin with a water-soluble organic solvent (e.g. methyl ethyl ketone), a dye and a compound of the formula [e.g. 2-(5-methyl-2-hydroxyphenyl)benzotriazole], heating and dissolving the mixture and adding water to the solution. The monomer containing ionic group is preferably 5-Na sulfoisophthalic acid, etc.

Description

Detailed Description of the Invention

[0001]

FIELD OF THE INVENTION This invention relates to inks, and more particularly to inks for ink jet printers.

[0002]

2. Description of the Related Art As an output device of information equipment such as a computer, a dot matrix printer, a thermal transfer printer,
There are various methods such as laser printers, among them, recently,
Inkjet systems are attracting attention as a system with low running cost, high definition, and easy colorization. As an ink for an inkjet printer, a dye aqueous solution has been used so far, but when the ink ejected from the nozzle adheres to the recording paper, the ink bleeds on the recording paper and is more likely than the ink particles formed when the ink is ejected. There were problems such as large dots and water resistance of the recorded image.

Conventionally, in such ink jet inks, many ideas have been proposed in order to solve these problems. a) A water-soluble dye is dissolved in a mixed solvent of water and an organic solvent so that the concentration of the dye is 5 wt% or less, and the organic solvent additive is 3 to 30%.
% Range (JP-A-62-124166) b) ink containing a specific diether compound (JP-A-62-32159) c) water-soluble direct dye in which surface-active substances are removed by an adsorption resin Or using an acid dye (JP-A-60-4907)
0) d) Ink to which a dye and an emulsion for forming a film are added (JP-A-4-18462) e) Using emulsion-polymerized or dispersion-polymerized particles dyed with a dye (JP-A-3-250069), etc. Is proposed.

[0004]

The above-mentioned inks a) to d).
Although the ink bleeding on the recording paper was reduced to some extent, it was impossible to completely prevent the ink bleeding due to the capillary phenomenon on the fibers of the recording paper. On the other hand, in the above method e), bleeding does not occur because the dyed polymer particles are used, but the particles obtained by this method have poor stability of the particles and the dye precipitates when left for a long time. It will settle or float on the particle surface. Further, since it is difficult to dye with high density, sufficient image density cannot be obtained. Furthermore, in the case of using a water-soluble dye that is generally widely used, the dye itself is directly applied to the paper, and the light resistance is very poor.

[0005]

SUMMARY OF THE INVENTION The present invention provides an ink for an ink jet printer which is capable of eliminating ink bleeding on recording paper, obtaining an extremely good image density, and having good light resistance. It is a thing. That is, the present invention is an aqueous dispersion containing polyester compounds colored by a dye or a pigment, containing the compound represented by Chemical formula 1, and having an ionic group in the range of 20 to 1000 eq / ton as a dispersoid. An ink for an inkjet printer characterized by the following.

The present invention has solved the problem of obtaining a high image density by using polyester, which is easy to dye, as colored particles. Further, since the polyester is an emulsion, it has an effect of reducing bleeding when it adheres to the recording paper. The polyester colored particles used in the present invention are preferably in an emulsion state, but more preferably have a particle size of 1 micron or less. Further, the polyester resin used for the polyester colored particles of the present invention comprises polyvalent carboxylic acids and polyvalent alcohols. Examples of the polyvalent carboxylic acids used for the polyester resin include terephthalic acid, isophthalic acid, orthophthalic acid, 1,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, diphenic acid, sulfoterephthalic acid, 5- Sulfoisophthalic acid, 4
-Sulfophthalic acid, 4-sulfonaphthalene-2,7 dicarboxylic acid, 5 [4-sulfophenoxy] isophthalic acid,
Aromatic dicarboxylic acids such as sulfoterephthalic acid and / or their metal salts and ammonium salts, aromatic oxycarboxylic acids such as p-oxybenzoic acid and p- (hydroxyethoxy) benzoic acid, succinic acid, adipic acid, azelaic acid , Sebacic acid, aliphatic dicarboxylic acids such as dodecanedicarboxylic acid, fumaric acid, maleic acid, itaconic acid,
Hexahydrophthalic acid, tetrahydrophthalic acid, and other unsaturated aliphatic and alicyclic dicarboxylic acids, and other polyvalent carboxylic acids such as trimellitic acid, trimesic acid, and pyromellitic acid. The polyvalent carboxylic acid and the like can be exemplified.

Examples of the polyvalent alcohols used in the polyester resin include aliphatic polyvalent alcohols, alicyclic polyvalent alcohols, aromatic polyvalent alcohols and the like.
Examples of the aliphatic polyhydric alcohols include ethylene glycol
, Propylene glycol, 1,3-propanedioe
2,3-butanediol, 1,4-butanediol
1,5-pentanediol, 1,6-hexanediol, neopentyl glycol, diethylene glycol
, Dipropylene glycol, 2,2,4-trimethyl-1,3-pentanediol, polyethylene glycol
Examples include aliphatic diols such as propylene, polypropylene glycol and polytetramethylene glycol, triols such as trimethylolethane, trimethylolpropane, glycerin, pentaerythritol and tetraols. it can.

The alicyclic polyvalent alcohols are 1,4-
Cyclohexanediol, 1,4-cyclohexanedimethanol, spiroglycol, hydrogenated bisphenol A, ethylene oxide adduct and propylene oxide adduct of hydrogenated bisphenol A, tricyclodecanediol, Examples thereof include tricyclodecane dimethanol. As aromatic polyhydric alcohols, paraxylene glycol, metaxylene glycol, orthoxylene glycol, 1,4-phenylene glycol, and ethylene oxide adduct of 1,4-phenylene glycol. , Bisphenol A, ethylene oxide adduct of bisphenol A, propylene oxide adduct and the like.

Further, as a polyester polyol, ε
Examples thereof include lactone-based polyester polyols obtained by ring-opening polymerization of lactones such as caprolactone. In addition to these, a monofunctional monomer may be introduced into the polyester for the purpose of blocking polar groups at the ends of the polyester polymer. Examples of monofunctional monomers include benzoic acid, chlorobenzoic acid, bromobenzoic acid, parahydroxybenzoic acid, sulfobenzoic acid monoammonium salt, sulfobenzoic acid monosodium salt, cyclohexylaminocarbonylbenzoic acid, n-dodecylaminocarbonylbenzoic acid. Acid, tert-butylbenzoic acid, naphthalenecarboxylic acid, 4-methylbenzoic acid, 3-methylbenzoic acid, salicylic acid, thiosalicylic acid, phenylacetic acid, acetic acid, propionic acid, butyric acid, isobutyric acid, octanecarboxylic acid, lauric acid, stearyl acid , And monocarboxylic acids such as lower alkyl esters thereof, or aliphatic alcohols
Mono alcohols such as alcohol, aromatic alcohol and alicyclic alcohol can be used.

In the present invention, an unsaturated monomer among these is an essential component, and the other components are appropriately selected depending on the glass transition temperature of the polyester resin, the compatibility with the monomer, and the like.

As the ionic group to be introduced into the polyester, a mono- or dicarboxylic acid having an alkali metal sulfonate or ammonium sulfonate can be preferably used. For example, an alkali metal carboxylate or an ammonium carboxylate can be used. Having a monomer, a sulfuric acid group, a phosphoric acid group, a phosphonic acid group, a phosphinic acid group or an anionic group such as an ammonium salt or a metal salt thereof, or a cationic group such as a primary to tertiary amine group. You can use a quantity etc.

When an alkali metal carboxylate or ammonium carboxylate is introduced, a polyvalent carboxylic acid such as trimellitic acid is introduced into the system at the final stage of polymerization of polyester to add a carboxyl group to the polymer terminal. Then, a method of exchanging it with a carboxylate group by neutralizing it with ammonia, sodium hydroxide or the like can be used. Further, by containing a mono- or dicarboxylic acid having an alkali metal sulfonate or ammonium sulfonate, these ionic groups can be introduced into the polyester resin. As salts, ammonium-based ions, Li, Na,
Examples thereof include salts of K, Mg, Ca, Cu, Fe and the like, and particularly preferred are K salt or Na salt. In the present invention, 5-
It is preferable to use sodium sulfoisophthalic acid or metasodium sulfobenzoic acid. Alternatively, a carboxylate group and a sulfonate group may be used.

More specific examples of the main component of the polyester resin in the present invention are shown below. a) a polyvalent carboxylic acid containing 80 mol% or more of an aromatic monomer, and b) a polyester resin obtained from 0 to 90 mol% of ethylene glycol and 100 to 10 mol% of propylene glycol, or a) A polyester resin obtained from polyvalent carboxylic acids containing 80 mol% or more of an aromatic monomer, and b) 2,3-butanediol 5-80 mol% and ethylene glycol 20-95 mol%, or a ) Polyvalent carboxylic acids containing 80 mol% or more of aromatic monomers, b) 70 to 95 mol% of C2 to C4 aliphatic glycols, and c) mono- or polyvalent compounds having a tricyclodecane skeleton. A polyester resin obtained from 5 to 30 mol% of alcohols, or a) a polyvalent carboxylic acid containing 80 mol% or more of an aromatic monomer, and b) a C2 to C4 aliphatic glycol 70-95 mol%, c) hydroxymethyl Polyester resins obtained from cyclodecane 5 to 30 mol%, or,

A) polyvalent carboxylic acids containing 80 mol% or more of an aromatic monomer, b) 70 to 95 mol% of C2 to C4 aliphatic glycols, and c) tricyclodecane dimethanoe. Polyester resin obtained from 5 to 30 mol%, or a) polyvalent carboxylic acid containing 80 mol% or more of an aromatic monomer, and b) 70 to 95 mol of C2 to C4 aliphatic glycols. %, C) a polyester resin obtained from 5 to 30 mol% of mono- or polyvalent alcohols having a cyclohexane skeleton,
Or a) polyvalent carboxylic acids containing 80 mol% or more of an aromatic monomer, b) 70 to 95 mol% of C2 to C4 aliphatic glycols, and c) 5 to 30 mol% of cyclohexanediol. Or a) a) polyvalent carboxylic acid containing 80 mol% or more of an aromatic monomer, b) C2 to C4 aliphatic glycols 70 to 95 mol%, c) water Polyester resin obtained from 5 to 30 mol% of added biphenol, or

A) polycarboxylic acids containing 80 mol% or more of an aromatic monomer, b) 70 to 95 mol% of C2 to C4 aliphatic glycols, and c) hydrogenated bisphenol A5 From 30 to 30 mol%, or a) a polycarboxylic acid containing 80 mol% or more of an aromatic monomer containing 1 to 20 mol% of a mono- or divalent carboxylic acid having a naphthalene skeleton, b) C2 to C4 aliphatic glycols 70 to 100 mol
%, C) Polyvalent alcohol containing 0 to 30 mol% of alicyclic monomer
Examples thereof include polyester resins obtained from and the like. Further, the "a) aromatic monomer" shown here is preferably terephthalic acid or isophthalic acid.
The ratio of terephthalic acid and isophthalic acid is terephthalic acid content / isophthalic acid content = 90 to 40/10 to 60
[Mol%] is preferable, and terephthalic acid content / isophthalic acid content = 80 to 50/20 to 50 [mol%],
Furthermore, terephthalic acid content rate / isophthalic acid content rate =
85-60 / 15-40 [mol%] is preferable.

When an ionic group-containing monomer is introduced into a polyester resin to give an ionic group to the polyester resin, the polyester resin exhibits water dispersibility. As the ionic group-containing monomer, a mono- or dicarboxylic acid having the above-mentioned alkali metal sulfonate or ammonium sulfonate can be preferably used. For example, a monomer having an alkali metal carboxylate or ammonium carboxylate can be used. Anionic group such as a monomer, a sulfate group, a phosphoric acid group, a phosphonic acid group, a phosphinic acid group or an ammonium salt or a metal salt thereof, or a first
A cationic group monomer such as a primary to tertiary amine group can be used. When an alkali metal carboxylate or ammonium carboxylate is introduced, a polyvalent carboxylic acid such as trimellitic acid is introduced into the system at the final stage of polymerization of polyester to add a carboxyl group to the polymer terminal, It is possible to use a method of neutralizing this with ammonia, sodium hydroxide or the like to exchange it for a carboxylate group.

The content of these ionic groups is 10 to 1000 meq / 1000 g, preferably 20 to 500 meq / 1000 g, and more preferably 50, based on the polyester resin, including the groups of sulfonic acid groups and / or salts thereof. ~ 200 meq / 1000 g. When the content of the ionic group is less than the predetermined amount, sufficient water dispersibility cannot be obtained.

In the present invention, in the compound of Chemical formula 1 used for the purpose of improving the light resistance, R1 has a hydrogen atom or a halogen atom such as chlorine or bromine, and R2 and R3 each have a substituent having 1 to 20 carbon atoms. It is a thing. Specific examples of the compound are shown below, but the compound used in the present invention is not limited to these compounds. Further, two or more kinds of the compounds represented by Chemical Formula 1 may be mixed and used. 2- (5-methyl-
2-hydroxyphenyl) benzotriazole, 2-
(2-Hydroxy-3,5-bis (α, α-dimethylbenzyl) phenyl) -2H-benzotriazole, 2-
(3,5-di-t-butyl-2-hydroxyphenyl)
Benzdriazole, 2- (3-t-butyl-5-methyl-2-hydroxyphenyl) -5-chlorobenzotriazole, 2- (3,5-di-t-butyl-2-hydroxyphenyl) -5- Chlorobenzotriazole, 2-
(3,5-di-t-amyl-2-hydroxyphenyl)
Benzotriazole, 2- (2'-hydroxy-5'-
t-octylphenyl) benzotriazole and the like.
The addition amount of the compound used in the present invention is preferably in the range of 0.5 to 5% by weight based on the polyester resin.

As the dye, "a dye insoluble in water at room temperature"
Is preferably used. These are generally classified as disperse dyes or oil-soluble dyes. More specifically, C.I. I. Disperse Yellow 198 C.I. I. Disperse Yellow 42 C.I. I. Disperse Yellow 162. C.I. I. Disperse Red 92 C.I. I. Disperse Red 60 C.I. I. Disperse Violet 26 C.I. I. Disperse Violet 35 C.I. I. Disperse Blue 60 C.I. I. Disperse Blue 87 C.I. I. Solvent Blue 25 C.I. I. Solvent Blue 35 C.I. I. Solvent Blue 38 C.I. I. Solvent Blue 64 C.I. I. Solvent Blue 70 C.I. I. At least one dye selected from Solvent Black 3 is preferably used. These are particularly excellent in light fastness, sublimation fastness, hue and saturation, and are preferable as three primary colors for process color. In addition, known dyes and pigments may be used in combination for fine adjustment of hue.

It is essential that the average particle size of the fine particle dispersion in the present invention is 1.0 μm or less, preferably 0.5 μm or less, more preferably 0.2 μm or less, and still more preferably 0.1 μm or less. is there. If the particle system of the fine particle dispersion exceeds this range, the dispersion stability may deteriorate.

A fine particle dispersion of the polyester resin can be obtained by the method described below. That is, when it contains an ionic group, the polyester resin of the present invention exhibits water dispersibility. Water dispersibility means a state generally called emulsion or colloidal dispersion. The ionic group dissociates in the aqueous medium and forms an electric double layer at the interface between the polyester resin and water. When the polyester resin is present as fine microparticles in the water system, an electrostatic repulsive force is generated between the microparticles due to the action of the electric double layer, and the microparticles are stably dispersed in the water system.

The aqueous dispersion of the ionic group-containing polyester resin is prepared by previously mixing the ionic group-containing polyester resin and the water-soluble organic compound, and then adding water, and the ionic group-containing polyester resin, the water-soluble organic compound and water. Can be obtained by a method of mixing and heating all at once. At that time, a surfactant or the like can be used together. As the water-soluble organic compound, ethanol, isopropanol,
Butanol, ethylene glycol, propylene glycol
, Methyl cellosolve, ethyl cellosolve, butyl cellosolve, acetone, methyl ethyl ketone, tetrahydrofuran, dioxane and the like can be used. The water-soluble organic compound is preferably one that can be removed by azeotropic distillation after the ionic group-containing polyester resin is dispersed in water.

The polyester resin of the present invention has good light fastness even when colored with a dye. As the dye, a disperse dye, an oil-soluble dye, a building bath dye, a vat dye, a slene dye, a basic dye or the like can be used. As a method for incorporating the dye into the polyester resin, a high temperature dispersion dyeing method can be used. The method of directly kneading the dye base material into the resin is not preferable in consideration of the damage of the dye due to heating. Since the polyester resin of the present invention exhibits good stable dispersibility in water due to the action of ionic groups, it is possible to perform high-density dyeing while maintaining the particulate state. Further, a dye may be added when the polyester resin is dissolved in a solvent during emulsification. The ink for an ink jet printer of the present invention contains the colored polyester particles dispersed in water in an amount of 1 to 50 wt%.
In addition to the colored polyester particles, the ink for an inkjet printer of the present invention may optionally contain a dispersant and a dispersion stabilizing aid such as a surfactant or a polymer dispersion stabilizer. Further, ethylene glycol, glycerin, and various polyhydric alcohols may be added to improve the wettability of the particles. Further, various chelating agents may be added to block the metal ions mixed in the ink. Further, in order to improve the storage stability of the ink, various germicides, fungicides, ultraviolet absorbers, antioxidants and the like may be added.

[0024]

Example 1 (Synthesis of polyester resin) 130 parts by weight of dimethyl terephthalate, 56 parts by weight of dimethyl isophthalate, and 5 sodium sulfoisophthalic acid were placed in an autoclave equipped with a thermometer and a stirrer. Dimethyl ester 6
Parts by weight, ethylene glycol 159 parts by weight, tricyclodecane dimethanol 30 parts by weight, tetrabutoxy titanate 0.1 parts by weight were charged and the transesterification reaction was carried out by heating at 180 to 230 ° C. for 120 minutes. . Then, the reaction system was heated to 240 ° C., and the reaction was continued for 60 minutes at a system pressure of 1 to 10 mmHg, and as a result, a copolyester resin was obtained. Next, 340 parts by weight of the obtained polyester resin, 150 parts by weight of methyl ethyl ketone, 140 parts by weight of tetrahydrofuran, dye C.I. I. 30 parts by weight of Disperse Blue 87 conc., 4 parts by weight of 2- (5-methyl-2-hydroxydiphenyl) benzotriazole at 80 ° C.
After being dissolved in, 680 parts of water at 80 ° C. was added to obtain an aqueous microdispersion of a copolyester resin having a particle diameter of about 0.15 μm. Further, the obtained water-based microdispersion was placed in a distillation flask and distilled until the distillate temperature reached 100 ° C. After cooling, water was added to make the solid content concentration 30%. Hereinafter, the dyes: C.I. I. Disperse Yellow 198 C.I. I. Instead of Disperse Red 92, dyeing was performed in the same manner to obtain an aqueous microdispersion.

The aqueous microdispersion thus obtained was used as an ink for an ink jet printer (EPSON HG-4000). The paper used was unprocessed for inkjet. As a result, no ink bleeding was observed when the ink according to the present invention was used. The density of the obtained image was extremely high and the image was clear. In addition, the produced water-based micro dispersion is
Even when left at room temperature for 3 months or longer, no precipitation or dye precipitation was observed, and the stability was extremely good. On the other hand, the dispersion obtained by emulsion-polymerizing a styrene polymer and then dyed has a low coloring density, and further, the stability of the dispersion is poor and precipitation of the dye is observed when left at room temperature for 3 months or more. It was Further, as a comparative example, ink bleeding was observed using a water-soluble dye that is commonly used in inkjet inks. The water-soluble dye used was C.I. I. Acid Yell
ow 7, C.I. I. Acid Red 94, C.I. I.
Acid Blue 1 was dissolved in water to prepare an ink.
As a result, when the special paper was used, the result was good, but when the plain paper was used, the present invention was different from the present invention, and was greatly blurred. Also, the light resistance was compared. The color difference of each printed ink was measured before and after irradiation with an ultraviolet fade meter (carbon arc) at 63 ° C. for 20 hours. As a result, the ink according to the present invention had ΔE of 1 to 3, whereas the ink based on the water-soluble dye had ΔE of 8
The color faded greatly to -40.

[0026]

INDUSTRIAL APPLICABILITY The ink jet printer ink of the present invention is excellent in light resistance and has excellent practicality as an ink without bleeding.

Claims (1)

[Claims] 1. A dye or a pigment, which contains a compound represented by the following general formula 1, 20 to 10
An ink for an inkjet printer, which is an aqueous dispersion containing polyester particles containing an ionic group in the range of 00 eq / ton as a dispersoid. [Chemical 1] In the formula, R1 represents a hydrogen atom or a halogen atom, and R2
And R3 each independently have hydrogen or a substituent having 1 to 20 carbon atoms.