JPH0712455U - Waste solidified combination concrete block - Google Patents
Waste solidified combination concrete blockInfo
- Publication number
- JPH0712455U JPH0712455U JP4234293U JP4234293U JPH0712455U JP H0712455 U JPH0712455 U JP H0712455U JP 4234293 U JP4234293 U JP 4234293U JP 4234293 U JP4234293 U JP 4234293U JP H0712455 U JPH0712455 U JP H0712455U
- Authority
- JP
- Japan
- Prior art keywords
- glass
- block
- cement
- sand
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】 焼却灰、ガラス及び／又は陶磁器を再利用し
た、砂をなるべく使用せず、表面に錆が出ず、必要に応
じて表面をきれいに着色したブロックを提供する。
【構成】 焼却灰、ガラス及び／又は陶磁器の砂状粉砕
物、セメント並びに水を混合して硬化させた基層の上に
ガラス及び／又は陶磁器の砂状粉砕物、セメント並びに
水を混合して硬化させた表層を接合してなるブロック。
(57) [Summary] [Objective] To provide a block in which incinerated ash, glass and / or ceramics are reused, sand is not used as much as possible, rust does not appear on the surface, and the surface is properly colored if necessary. [Composition] Incinerated ash, sandy ground material of glass and / or ceramics, cement and water mixed and hardened on a base layer mixed with sandy ground material of glass and / or ceramics, cement and water and hardened A block formed by joining the surface layers.
Description
【０００１】[0001]
本考案は焼却灰を利用したブロックに関する。 The present invention relates to a block using incineration ash.
【０００２】[0002]
従来、焼却灰は埋め立てて処理していた。しかし焼却灰は大量に生じるため埋 め立てる場所に困る状況である。そこで焼却灰を少しでも何らかの形で再利用す ることが出来ればまことに好都合である。焼却灰を砂、セメント及び水に混ぜて 硬化させてブロックとすることが考えられるが、しかしこの場合砂を用いるため 砂の費用がかかり過ぎ、又、焼却灰には鉄粉が入っているため錆が出るという欠 点がある。更に、焼却灰の色が黒いため、このブロックを着色しにくいという問 題点もある。それ以上に、焼却灰を混入させて強度のあるものが出来るかどうか という不安もある。 Traditionally, incinerated ash was disposed of in landfills. However, a large amount of incinerated ash is generated, which makes it difficult to bury it. Therefore, it would be very convenient if the incinerated ash could be reused in some way or another. It is considered that the incineration ash is mixed with sand, cement and water and hardened to form blocks, but in this case, the cost of sand is too high to use sand, and the incineration ash contains iron powder. It has the drawback of rusting. Another problem is that it is difficult to color this block because the color of the incineration ash is black. Furthermore, there is concern about whether strong ash will be produced by mixing incinerated ash.
【０００３】[0003]
本考案の目的は、焼却灰、ガラス及び／又は陶磁器を再利用した、砂をなるべ く使用せず、表面に錆が出ず、必要に応じて表面をきれいに着色した強度のある ブロックを提供することにある。 The object of the present invention is to provide a strong block that reuses incineration ash, glass and / or ceramics, does not use sand as much as possible, does not rust on the surface, and cleanly colors the surface as necessary. To do.
【０００４】[0004]
本考案は、焼却灰、ガラス及び／又は陶磁器の砂状粉砕物、セメント並びに水 を混合して硬化させた基層の上にガラス及び／又は陶磁器の砂状粉砕物、セメン ト並びに水を混合して硬化させた表層を接合してなるブロックを要旨とする。 The present invention mixes sand and ground ash, glass and / or ceramic sand, cement and water on a base layer which is hardened by mixing glass and / or sand and ceramic ground, cement and water. The gist is a block formed by joining surface layers cured by curing.
【０００５】 本考案のブロックを製造するためには、先ずガラスや陶磁器を砂状に粉砕し、 これをセメント及び水と混合してスラリーとし、型枠に流し込み第１の層とする （これが後に表層となる）。次いで、焼却灰に、上記と同じくガラスや陶磁器を 砂状に粉砕もの、セメント及び水を混合してスラリーとし、更に上記型枠に流し 込み第２の層とする。これを硬化させた後型枠からブロックを取り出してできあ がる。上記第１の層に着色剤を予め混合しておけば、上記表層はきれいに着色さ れたものとなる。このようにして作ったブロックの１例の斜視図を図１に示す。 図１において、１は表層、２は基層、３はブロックである。In order to manufacture the block of the present invention, first, glass or porcelain is crushed into a sand shape, which is mixed with cement and water to form a slurry, which is poured into a mold to form a first layer (which will be described later). Will be the surface). Next, the incinerated ash is crushed into glass like glass or ceramics in the same manner as above, cement and water are mixed to form a slurry, which is further poured into the above mold to form a second layer. After hardening this, the block is taken out from the formwork and it is completed. If the colorant is mixed in advance with the first layer, the surface layer becomes finely colored. A perspective view of an example of the block thus manufactured is shown in FIG. In FIG. 1, 1 is a surface layer, 2 is a base layer, and 3 is a block.
【０００６】 前記砂状にしたガラスや陶磁器は白色又は透明の状態になり、前記第１の層か ら形成される表層は、焼却灰を含まないから錆が出ず、着色がよい。第１層と第 ２層は強固に接合しており、そしてこのブロックは強度もあり、敷石や壁材の正 面に利用することができる。又、建築材のブロックとして積み上げ固定すること ができる。The sand-like glass and the ceramics are in a white or transparent state, and the surface layer formed from the first layer does not contain incineration ash and thus does not rust and is colored well. The first and second layers are firmly bonded, and the block is also strong and can be used to face paving stones and wall materials. It can also be stacked and fixed as a block of building material.
【０００７】[0007]
ガラスを砂状に粉砕したもの３７０ｇ、セメント１２５ｇ、顔料として赤の色 粉を５ｇ及び水１３ｇを混合してスラリーとし縦２０cm、横１０cm、深さ８cmの 型枠に流し込み、第１の層を形成した。その上にガラスを砂状に粉砕したもの３ ００ｇ、セメント５００ｇ、焼却灰１，２００ｇ及び水２４０ｇを混合してスラ リーとし、上記型枠の第１の層の上に流し込んだ。これらを１日放置して硬化さ せ、硬化物を型枠から取り出してブロックを得た。このブロックは表層がきれい な赤色をしており、でき上がったブロックを２８日間気乾養生し、圧縮強度を測 定したところ１２０ kgf／cm2 であった。Sand glass 370g, cement 125g, 5g red pigment as pigment and 13g water are mixed to make a slurry and poured into a mold of length 20cm, width 10cm, depth 8cm and the first layer Formed. 300 g of sand crushed glass, 500 g of cement, 1,200 g of incinerated ash, and 240 g of water were mixed to form a slurry, which was poured onto the first layer of the mold. These were left to cure for 1 day, and the cured product was taken out of the mold to obtain a block. The surface of this block had a beautiful red color, and the resulting block was air-dried for 28 days and the compressive strength was measured to be 120 kgf / cm 2 .
【０００８】[0008]
本考案によれば、焼却灰を再利用した、きれいで、強度のあるブロックを提供 できる。 According to the present invention, it is possible to provide a clean and strong block that reuses incinerated ash.
【図１】本考案にかかるブロックの斜視図。FIG. 1 is a perspective view of a block according to the present invention.
１…表層 ２…基層 ３…ブロック 1 ... Surface layer 2 ... Base layer 3 ... Block
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｅ０１Ｃ 5/22 7322−2Ｄ //(Ｃ０４Ｂ 28/02 18:10 Ｚ 18:16 14:22） ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Office reference number FI technical display location E01C 5/22 7322-2D // (C04B 28/02 18:10 Z 18:16 14:22)
Claims (1)
粉砕物、セメント並びに水を混合して硬化させた基層の
上にガラス及び／又は陶磁器の砂状粉砕物、セメント並
びに水を混合して硬化させた表層を接合してなるブロッ
ク。1. A mixture of incineration ash, glass and / or sand crushed ceramics, cement and water mixed and cured on a base layer to which glass and / or ceramic crushed sand, cement and water are mixed. A block formed by joining surface layers that have been cured.