JPH05169575A - 不織−メルトブロウン−フィルム組成物積層体 - Google Patents

不織−メルトブロウン−フィルム組成物積層体

Info

Publication number
JPH05169575A
JPH05169575A JP3213774A JP21377491A JPH05169575A JP H05169575 A JPH05169575 A JP H05169575A JP 3213774 A JP3213774 A JP 3213774A JP 21377491 A JP21377491 A JP 21377491A JP H05169575 A JPH05169575 A JP H05169575A
Authority
JP
Japan
Prior art keywords
web
layer
mat
meltblown
bonding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP3213774A
Other languages
English (en)
Inventor
Michael Peter Mathis
ピーター マーティス マイケル
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kimberly Clark Corp
Original Assignee
Kimberly Clark Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kimberly Clark Corp filed Critical Kimberly Clark Corp
Publication of JPH05169575A publication Critical patent/JPH05169575A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 （修正有） 【目的】 良好な耐摩耗性、同一材料内における吸収特
性及び液体遮蔽特性を有し、さらに、良好な強度と薄片
に裂ける性質とを有する、不織布を基質とする材料を提
供する。 【構成】 不織マット１２はメルトブロウンウェブ１６
に超音波結合される。不織マットとは反対側のメルトブ
ロウンウェブの面はポリマー材料の連続層２６で押し出
し被覆されており、この連続層はメルトブロウンウェブ
１６の繊維と接着し、液体非透過性の裏打ち層を形成し
ている。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は不織−メルトブロウン−
フィルム組成物積層体に関する。より詳細には、本発明
は超音波を用いてメルトブロウンウェブに結合してい
る、予め結合した不織マットに関する。不織マットとは
反対側のメルトブロウンウェブの面はポリマー材料の連
続層で被覆した押し出し材であり、この連続層はメルト
ブロウンウェブの繊維に接着しており、流体非透過性の
裏打ち層を形成しているものである。完成品としての積
層体は広範囲の用途に適しており、例えば手術用ドレー
プ、ガウン、作業着などの手術用品及びクリーン・ルー
ム用品の他に、オムツ、生理用ナプキン、トレーニング
パンツ、失禁用用品などの看護用品にも適している。
【０００２】
【従来の技術】不織布が用いられる用途は増大し続けて
いる。製品に用いられる頻度が増すにつれて、不織布が
発揮しなければならない機能も同様に増している。ある
最終製品の特定の要求を満たすのに必要な全ての機能を
有する材料がないということはしばしばあることであ
る。
【０００３】この問題に対する一つの解決策は積層体を
用いることである。このことは健康産業、特に手術用ド
レープやガウンなどの医療用品供給産業に関しては、特
に当てはまる。今日では外科において用いられる用品の
多くは、使用後に洗濯して殺菌された再使用可能な織布
材料からなるものである。不織布の市場が拡大するにつ
れて、これらの再使用可能な織布用品の多くは一回のみ
使用する使い捨ての不織布に取って代わられた。不織布
製品の多くが織布材料に対して大きな改良がなされてい
ることが証明されている。おそらく、織布材料の唯一の
利点は、それは通気性が良いため、比較的着やすいとい
う点である。これに対して、織布材料の最大の欠点は、
血液などの体液を容易に吸収してしまうことであった。
このため、伝染病で汚染された血液に対する関心が高ま
るにつれて、手術室などで使用する物質の遮蔽特性や液
体処理特性などが物理的な結合性とともに重要な問題に
なってきた。
【０００４】
【発明が解決しようとする課題】したがって、本発明の
目的は、良好な耐摩耗性、同一材料内における吸収特性
及び液体遮蔽特性を有し、さらに、良好な強度と薄片に
裂ける性質とを有する、不織布を基質とする材料を提供
することである。
【０００５】本発明の他の目的は、材料及びその製造方
法とによって、これらの利点を単一の組成物構造におい
て発揮するような不織材料を提供することである。
【０００６】本発明のこれらの、及び他の目的は以下の
説明を参照することによって一層明らかになる。
【０００７】
【課題を解決するための手段】本発明は不織−メルトブ
ロウン−フィルム組成物積層体、及びその製造方法に関
する。より詳細には、本発明は超音波を用いてメルトブ
ロウンウェブに結合している、予め結合した不織マット
に関する。不織マットとは反対側のメルトブロウンウェ
ブの面はポリマー材料の連続層で被覆した押し出し材で
あり、この連続層はメルトブロウンウェブの繊維に接着
しており、流体非透過性の裏打ち層を形成しているもの
である。完成品としての積層体は広範囲の用途に適して
おり、例えば手術用ドレープ、ガウン、作業着などの医
療用品及びクリーン・ルーム用品の他に、オムツ、生理
用ナプキン、トレーニングパンツ、失禁用用品などの看
護用品にも適している。
【０００８】押し出し材で被覆した不織積層体の製造方
法は、連続的に、かつランダムに堆積した熱可塑性繊維
のマットを熱可塑性微小繊維のウェブに隣接させて配置
する工程を有している。ウェブは表面と裏面とを有し、
マットは該ウェブの表面に隣接して配置されるものとし
て形成される。次いで、ウェブ及びマットは超音波を用
いて複数の結合箇所で相互に結合され、全結合面積はウ
ェブまたはマットのいずれかの表面積の１５％以下とさ
れる。この超音波結合に続いて、ウェブの裏面上に被覆
材料を押し出し、液体非透過性フィルムの連続層を裏面
に形成する。必要であれば、マットをウェブに隣接させ
る前にマットを一点で結合させることもできる。マット
を予め結合させておく面積はマットの全表面積の２０％
以上とする。
【０００９】
【実施例】本発明は不織材料の層を有する組成物不織積
層体に関する。不織材料の層は液体非透過性層のフィル
ムを有するメルトブロウン層に超音波で結合しており、
液体非透過性層のフィルムは押し出されて、不織層とは
反対側のメルトブロウン層の面上に被覆されたものであ
る。以下、説明を単純化するため、本発明を手術用ドレ
ープに用いる場合に関して説明するが、これは本発明の
用途を限定することを意図するものではない。それとは
逆に、本発明に係る積層体は広範囲の用途を有するもの
である。
【００１０】図１に示すように、本発明に係る組成物積
層体１０の最上層１２はランダムに堆積した熱可塑性の
連続繊維からなる層である。このような積層体及びそれ
を構成する層は公知のものであり、一般に不織布と呼ば
れているものである。例えば、米国特許第４，４０５，
２９７号にはこのような不織材料が示されている。不織
最上層１２を設けたのは、摩耗層と良好な作業表面とを
確保するためである。外科手術においては、この層が、
手術用器具及び用品とともに、最も一般的に手術室の人
員と接触するものである。このため、この表面は、乾燥
時及び湿潤時の双方において良好な強度を有し、リンテ
ィングに対して抵抗を示す繊維からつくる必要がある。
不織材料はこのような要求に対して適切なものである。
さらに、不織層は液体伝達機能を有し、体液及び排液を
不織層１２の外周層１４から積層体１０を通って下方に
伝えメルトブロウン中間層１６に伝えるものでなければ
ならない。体液及び排液はこの中間層１６において吸収
され、保持される。
【００１１】組成物積層体１０の不織層１２を形成する
繊維の材料としては多くの押し出し可能な材料を用いる
ことができる。熱可塑性材料がそのような繊維の形成に
特に適している。そのような熱可塑性樹脂としては、例
えば、ポリエステル、ポリエチレンやポリプロピレンな
どのポリオレフィンなどがあり、この他にランダム・コ
ポリマーやポリマー混合体がある。ただし、これらに限
定されるものではない。
【００１２】各繊維の繊維直径は約１０〜２５ミクロン
の範囲であり、好ましい範囲は１７〜２０ミクロンであ
る。疎水性の樹脂を用いる場合には、不織層の親水性を
高めるために、繊維内部に湿潤体を含ませるか、あるい
は表面処理剤として湿潤体を含ませることが一般的に好
ましい。これによって、液体を受け入れ運搬する性質が
一層増す。健康用品または看護用品に用いる材料の基本
重量は一般に約０．５〜１．５オンス／平方ヤード（ｏ
ｓｙ）であるが、容易に理解し得るように、この範囲
は、その材料を適用すべき特定の用途に応じて修正する
ことが可能である。
【００１３】不織層１２の結合性を高めるために、ま
た、処理を促進させるために、不織層１２は一点結合パ
ターンを用いて予め結合されている。適切な耐摩耗特性
を確保するため、結合面積はその材料の全表面積の少な
くとも２０％にする必要がある。このような結合を行う
には多くの既知の方法を用いることができる。例えば、
加熱されたパターン付き結合ロールや超音波結合法など
があるが、これらに限定されるものではない。例えば、
米国特許第４，３７４，８８８号を参照されたい。さら
に、不織層１２の機能的特性を高めるため、他の添加剤
や処理剤を加えることもできる。
【００１４】組成物積層体１０の中間層１６はランダム
に堆積された不連続の複数の微小繊維からなり、この微
小繊維は約１．０〜約５ミクロンの平均繊維直径を有
し、好ましい範囲は１．５〜３．０ミクロンである。こ
の繊維は不連続のものであることが多いが、その長さと
幅との比は無限大に近い。このような材料は通常「メル
トブロウン不織布」と呼ばれているもので、その形成方
法は良く知られているものである。例えば、米国特許第
３，６７６，２４２号（１９７２年７月１１日発行）を
参照されたい。あるいは、Ｎａｖａｌ Ｒｅｓｅａｒｃ
ｈ Ｌａｂｏｒａｔｏｒｉｅｓ が出している「Ｉｎｄ
ｕｓｔｒｉａｌ ＥｎｇｉｎｅｅｒｉｎｇＣｈｅｍｉｓ
ｔｒｙ」Ｖｏｌ．４８，Ｎｏ．８，１３４２〜１３４６
頁にある「極細熱可塑性繊維」という題の論文を参照さ
れたい。あるいは、１９５４年４月１５日付けの Ｎａ
ｖａｌ Ｒｅｓｅａｒｃｈ Ｌａｂｏｒａｔｏｒｙ Ｒ
ｅｐｏｒｔ １１４３７ を参照されたい。不織層１２
に関して言うと、メルトブロウン繊維を生成するために
用いられるポリマーまたは樹脂は広範囲の材料から選択
することができる。選択する材料が不織繊維の生成のた
めに用いられる材料と超音波で結合することができるも
のであれば良い。用いることのできる樹脂の例として
は、ナイロン、ポリエステル、ポリエチレンやポリプロ
ピレンなどのポリオレフィン、ランダム・コポリマー、
エラストマー、及び混合体などがあるが、これらに限定
されるものではない。看護用品または健康用品への応用
に関して再び言うと、メルトブロウン層１６の基本重量
は約１〜約４オンス／平方ヤードであり、好ましい範囲
は２．５〜３．０オンス／平方ヤードである。この範囲
から外れる基本重量も、組成物積層体１０が用いられる
特定の用途によっては、許容される。
【００１５】メルトブロウン中間層１６は、不織最上層
１２から該中間層１６に通過してくる液体を吸収する吸
収体として作用する。このため、好適な実施例において
は、メルトブロウン中間層１６は、それを超音波で不織
層１２に結合させる前に予め内部結合させておくことは
行わない。さらに、メルトブロウン中間層１６の極細繊
維の交絡の程度によっては、結合は必要でなくなること
もある。不織層１２に対しては、湿潤剤その他の薬剤お
よび処理剤を繊維に付加してもよい。
【００１６】本発明に係る組成物積層体を生成する方法
において重要な工程は、不織層１２をメルトブロウン中
間層１６に結合させる工程である。本発明に係る二つの
層は超音波結合法を用いて相互に点結合されている。メ
ルトブロウン層１６は一般に不織層１２よりもロフティ
ーであるので、二つの層を点結合させる場合には、通
常、メルトブロウン層１６の表面１８にパターン付き結
合ローラーを作用させて、結合点における繊維を相互に
押圧し、それらの繊維が、メルトブロウン中間層１６の
表面２０に隣接する不織層１２の繊維に結合できるよう
にしている。本件出願人は、熱を用いた従来の点結合法
では、加熱ローラーのパターンポイントによって繊維に
伝達された熱によって、メルトブロウン層内における結
合には繊維の部分的な溶融及び結合が生じている傾斜壁
が生じていることを発見した。すなわち、メルトブロウ
ン層１６の不織層１２への結合の度合いを何ら高めるこ
とのない過度な結合が生じている。これとは逆に、超音
波結合法を用いると、不織層１２とメルトブロウン層１
６とをよりきれいに結合させることができる。その理由
は、結合の大部分が実際の結合箇所２２においてのみ生
じ、パターン付きけつ結合ローラーにより形成される刻
み目の周囲の回りには生じないからである。さらに、結
合箇所２２に囲まれているメルトブロウン層１６の中の
側壁２４は垂直に立っており、これによって、この領域
において低い度合いの結合力で結合されたときには、メ
ルトブロウン層１６における液体保持のための吸収容量
が増加している。超音波結合法を用いることによって、
メルトブロウン層と不織層とを熱結合させることはでき
ないが超音波結合させることはできるような材料をも用
いることができるようになる。さらに、超音波結合法
は、熱結合法を用いて行った結合の度合いと比較して、
メルトブロウン層と不織層との間における剥離強度を向
上させることがわかった。超音波結合法の例としては米
国特許第４，６０５，４５４号がある。超音波結合の一
例として、超音波結合による断面を図３の顕微鏡写真に
示す。
【００１７】一般的には、不織層１２とメルトブロウン
層１６との間の結合の度合いが大きくなると、結合箇所
２２の領域におけるメルトブロウン層１６の不織層１２
への圧縮及び溶融のために、吸収性の度合いは減少す
る。健康用品及び看護用品に用いる際には、結合の度合
いは二つの層の結合に用いられている全表面積の約１５
％よりも少ない。ただし、この数字は用途に応じて大き
くすることが可能である。
【００１８】再び図１を参照すると、メルトブロウン層
１６の裏面１８は液体非透過層２６に接着している。こ
の液体非透過層２６は中間層１６の裏面１８に押し出し
被覆されたものである。押し出し被覆層２６は好適な適
用方法である。というのは、予め形成されたフィルムの
結合と異なり、押し出しによってコーティング材を部分
的に被覆し、従って、裏面１８に隣接している中間層１
６の繊維に結合させ、かつそれらの繊維をとり囲むよう
にすることができるからである。図３を参照されたい。
この結果として、フィルムを中間層１６のメルトブロウ
ン繊維と熱結合させる場合には、押し出し被覆層２６は
中間層１６と適合しないような材料からでも形成するこ
とが可能になる。
【００１９】押し出し被覆層２６を形成するために選択
される材料は、メルトブロウン層１６の裏面１８に一定
のコーティングを容易に形成でき、液体非透過層を形成
できる材料でなければならない。押し出し被覆材として
適当な材料としては、ポリエチレンやポリプロピレンな
どのポリオレフィン、ポリエチレンブレンド（ＥＶＡお
よびＥＭＡ）、熱可塑性エラストマー、ポリウレタン、
及びポリエステルなどがある。ただし、これらに限定さ
れるものではない。押し出し被覆層の形成は押し出した
フィルムを基質上にキャスティングすることにより行
う。代表的な被覆材重量は約０．７５〜約２．０ミルの
範囲である。例えば、押し出し材料として低密度のポリ
エチレンを用いる場合には、１．０〜１．５ミルの被覆
材重量が液体非透過性層を形成するには適している。さ
らに、押し出し被覆法が加熱点結合法よりも優れている
点はピンホールの発生のおそれを減らすことができる点
である。ピンホールは押し出し被覆層２６に達し、この
ため該被覆層２６に液体を浸透させてしまう好ましくな
いものである。
【００２０】前述したように、メルトブロウン層１６の
裏面１８に形成する押し出し被覆層２６によって、押し
出し被覆層２６はメルトブロウン層１６の裏面１８に隣
接する繊維を包み込むことができる。このことが図３の
顕微鏡写真に示されている。図３は、２．６５オンス／
平方ヤード、２〜３ミクロンの繊維直径のメルトブロウ
ン層に押し出し被覆したポリエチレンの０．１ミルのコ
ーティング材の顕微鏡写真であり、前記のメルトブロウ
ン層は１．０オンス／平方ヤード、繊維直径が２０ミク
ロンの不織層に超音波結合されており、メルトブロウン
層と不織層とは１２％の結合面積で結合している。
【００２１】再び図１を参照すると、形成された組成物
積層体１０においては、液体透過性最上層１２と液体非
透過性底部層２６とが液体吸収層１６により隔てられて
いる。液体吸収層１６は結合箇所２２の間にある複数の
ロフト領域２１を有している。結合箇所２２は複数の気
孔２５によって隔てられている。この気孔２５はメルト
ブロウン１６の不織層１２への圧縮および結合によって
生成したものである。さらに重要なことは、図３に示す
ように、押し出し被覆層２６はロフト領域２１の繊維を
被覆し、かつとり囲んでおり、また、気孔２５に架橋し
ている。これらの気孔２５は結合箇所２２の真下に位置
しており、ロフト領域２１とあいまって不織層１２の液
体透過性層を通って伝わってきた液体を吸収する領域を
形成している。超音波結合法を用いると、結合箇所２２
をとり囲む繊維の溶融はほとんど、あるいは全くない状
態で垂直な側壁２４が生成されるので、液体がロフト領
域２１から出て、気孔２５を満たすことが可能である。
熱結合法を用いると、繊維は、これらの気孔への液体の
流入が繊維の溶融のために少なくとも部分的に妨げられ
る程度に溶融する。
【００２２】以上、本発明に係る組成層の各要素、およ
び各層を結合させる適当な手段を説明してきたが、以下
では、本積層体の形成の方法を説明する。
【００２３】図２を参照すると、不織材料の第一供給源
３０が矢印３４の方向に回転しているエンドレス・ルー
プ状コンベアベルト３２に巻きほどかれている。次い
で、第二供給源３６、この場合にはメルトブロウン材料
のロールが巻きほどかれ、不織層３１の上に重ねて配置
される。不織層３１及びメルトブロウン層３５は超音波
結合手段３８を通過し、これら二つの層は相互に超音波
結合される。このときの結合面積比率は少なくとも１２
％である。超音波結合工程に続いて、押し出し被覆器４
０がメルトブロウン層３５の裏側に液体非透過材料の連
続層を形成し、これによって、本発明に係る組成物積層
体３９が形成される。その後、組成物積層体３９は貯蔵
ロール４２に巻き取られ、他の場所に運搬し、他の処理
を行い得るようにされる。あるいは、そのような他の処
理はこの組成物積層体生成ライン内において直接に行う
ようにしてもよい。
【００２４】以上、組成物積層体およびその製造方法を
説明してきたが、以下に改良された特性を示すサンプル
を説明する。
【００２５】（サンプル）まず最初に、平均直径が約２
０ミクロンのフィラメントを有する１．０オンス／平方
ヤードの不織ポリプロピレンマットを生成することによ
って、本発明に係る不織／メルトブロウン／フィルム組
成物積層体（ＳＭＦ）を生成した。不織ポリプロピレン
マットは、マットの表面積の約２６％を占めるダイアモ
ンド結合パターンを用いて、加熱及び加圧によって予め
結合されていた。次いで、ウェブを陰イオン界面活性剤
で処理して、ウェブを湿潤性にした。次いで、２〜３ミ
クロンの平均直径を有するフィラメントを備えるように
メルトブロウン微小繊維ウェブを形成した。このように
形成されたウェブは約２．６５オンス／平方ヤードの基
本重量を有しており、ウェブ形成の最中に非イオン性界
面活性剤をメルトブロウン繊維流れの中に噴射すること
により湿潤性にした。この後、不織マット及びメルトブ
ロウンウェブのロールをほどき、一方が他方の上になる
ように重ね合わせ、その後、超音波結合器に送り込む。
この際、不織マットが超音波ホーンに、メルトブロウン
ウェブがパターン付きアンビルに対するようにする。こ
れはエネルギを効果的に与えて、二つの材料の「接合」
を効果的に行うためである。この超音波結合法において
用いられるパターン付きアンビルロールは約１５％の結
合面積を有する長方形ピンロールである。このように生
成された不織／メルトブロウン組成物はロールに巻き取
られ、押し出し被覆ラインに運ばれ、ここでロールをほ
どかれ、被覆が行われる。コーティング材は、柔らかさ
を出すための９％のエチレンビニルアセテートと、所望
の色を出すための１０％濃度の色素とを含む１．０ミル
のポリエチレンフィルムである。
【００２６】表１には、本発明に係る不織布／メルトブ
ロウン／フィルム組成物積層体の特性が他の三つの布の
同じ特性と比較されている。用いた三つの布は「ＣＯＮ
ＴＲＯＬ（登録商標）」と「ＨＩ−ＬＯＦＴ（登録商
標）」と「ＤＲＩ−ＳＩＴＥ（登録商標）」である。
「ＣＯＮＴＲＯＬ」はキンバリー・クラーク（Ｋｉｍｂ
ｅｒｌｙ−Ｃｌａｒｋ）社が販売しているものである。
「ＨＩ−ＬＯＦＴ」はコンバーターズ（Ｃｏｎｖｅｒｔ
ｏｒｓ）が、「ＤＲＩ−ＳＩＴＥ」はジョンソン・アン
ド・ジョンソン（Ｊｏｈｎｓｏｎ ａｎｄ Ｊｏｈｎｓ
ｏｎ）が各々販売している。「ＣＯＮＴＲＯＬ」は手術
用ドレープ補強布として用いられる材料であり、米国特
許第３，６６８，０５０号に詳述されている。すなわ
ち、「ＣＯＮＴＲＯＬ」は４０ミルの連続気泡ポリウレ
タンフォームに接着して積層されている１．５ミルのポ
リエチレンフィルムからなる。「ＨＩ−ＬＯＦＴ」およ
び「ＤＲＩ−ＳＩＴＥ」の双方は市販されており、手術
用ドレープ用のセルロースをベースとした開窓補強材料
である。これらの材料を手術用ドレープ用の開窓補強材
料として用いる場合には、吸収効率、強度、及び耐摩耗
性が重要な性質である。このため、これらの性質は四つ
の材料全てについて測定した。これらの性質を調べた方
法は以下の通りであり、その結果は表１に示す通りであ
る。
【００２７】（吸収効率）この試験は連邦政府仕様（Ｆ
ｅｄｅｒａｌ Ｇｏｖｅｒｍｅｎｔ Ｓｐｅｃｉｆｉｃ
ａｔｉｏｎ）ＵＵ−Ｔ−５９５ｂに基づいて行った。こ
の試験は、まず４インチ×４インチのサンプルを裁断
し、計量し、水に３分間浸けて水で飽和させ、水から取
り出し、一つの角において３０秒吊るして過剰の水を抜
き、最後に再計量する。湿潤時の重量から乾燥時の重量
を減算し、その差を乾燥時の重量で割ると、その商が吸
収効率を表す。単位は〔水のグラム数／サンプルのグラ
ム数〕である。数値が大きいほど、吸収効率が高いこと
を示す。
【００２８】（ＣＤ台形引き裂き強度）各材料の横方向
（ＣＤ）の台形引き裂き強度は連邦標準１９１、方法５
１３６を用いて測定した。表１に示す値の単位はポンド
である。
【００２９】（グラブ引張強度）各材料における縦方向
（ＭＤ）および横方向（ＣＤ）のグラブ引張強度は連邦
標準１９１、方法５１０２を用いて求めた。表１に示す
値の単位はポンドである。
【００３０】（耐摩耗性）耐摩耗性の測定は、１２５グ
ラムの重り（総負荷は１２５グラム）と右側の摩耗ヘッ
ドにラバーＳ−３２ホィールを有するテーバー標準摩耗
器（１４０ＰＴ型）を用いて行った。試験結果は摩耗の
サイクル数で示した。測定失敗は、試験中において、け
ば立った、柱状の外見を呈した摩耗を示した表面の部分
において生じたものと考えられる。
【００３１】 表 １ SMF CONTROL HI-LOFT DRI-SITE 吸収効率 5.10 8.65 2.52 4.53 ＣＤ引き裂き強度 5.2 4.4 2.4 0.9 ＭＤグラブ引張強度 32.8 9.1 10.5 10.6 ＣＤグラブ引張強度 25.9 9.1 7.2 11.6 耐摩耗性 100+ 28 100+ 22
【００３２】表１に示した試験結果を見ると、本発明に
係る「ＳＭＦ」と市販されている他の開窓補強材料にと
の吸収効率の比較から、本発明の「ＳＭＦ」は手術用ド
レープ材料または手術ドレープ開窓補強材料としての用
途に適していることがわかる。
【００３３】台形引き裂き強度とグラブ引張強度の双方
で示した強度に関しては、本発明の「ＳＭＦ」は試験を
行った他の市販材料のどれよりもはるかに優れており、
これはまさに超音波結合法の直接的な効果である。この
結合強度は、タオルクリップを用いて手術用管を切開箇
所の回りのドレープにとめることが多い手術用の最終用
途においては特に重要である。タオルクリップが開窓補
強材料から引き裂かれてしまい、その結果、タオルクリ
ップで手術用管を所定の場所に確実にとめられなくなる
と、患者に危害が及ぶこととなってしまう。
【００３４】本発明の「ＳＭＦ」の耐摩耗性は現在市販
されている開窓補強材料と比較しても優れており、手術
用に極めて適したものとなっている。
【００３５】以上、本発明を説明してきたが、多くの修
正や変更が本発明の範囲内において可能である。
【図面の簡単な説明】
【図１】本発明に係る不織−メルトブロウン−フィルム
組成物積層体の側面断面図である。
【図２】本発明に係る積層体を形成する方法を示す概略
図である。
【図３】本発明に係る不織−メルトブロウン−フィルム
組成物積層体の側面断面を示す顕微鏡写真である。
【符号の説明】
１０ 組成物積層体 １２ 最上層 １４ 外周層 １６ 中間層 １８ 裏面 ２０ 表面 ２１ ロフト領域 ２２ 結合箇所 ２４ 側壁 ２５ 気孔 ２６ 押し出し被覆層 ３０ 第一供給源 ３１ 不織層 ３２ コンベアベルト ３５ メルトブロウン層 ３６ 第二供給源 ３７ 液体非透過材料 ３８ 超音波結合手段 ３９ 組成物積層体 ４０ 押し出し被覆層 ４２ 貯蔵ロール
─────────────────────────────────────────────────────
【手続補正書】
【提出日】平成４年１１月２０日
【手続補正１】
【補正対象書類名】明細書
【補正対象項目名】図面の簡単な説明
【補正方法】変更
【補正内容】
【図面の簡単な説明】
【図１】本発明に係る不織−メルトブロウン−フィルム
組成物積層体の側面断面図である。
【図２】本発明に係る積層体を形成する方法を示す概略
図である。
【図３】本発明に係る不織−メルトブロウン−フィルム
組成物積層体の繊維の形状の側面断面を示す顕微鏡写真
である。
【符号の説明】 １０ 組成物積層体 １２ 最上層 １４ 外周層 １６ 中間層 １８ 裏面 ２０ 表面 ２１ ロフト領域 ２２ 結合箇所 ２４ 側壁 ２５ 気孔 ２６ 押し出し被覆層 ３０ 第一供給源 ３１ 不織層 ３２ コンベアベルト ３５ メルトブロウン層 ３６ 第二供給源 ３７ 液体非透過材料 ３８ 超音波結合手段 ３９ 組成物積層体 ４０ 押し出し被覆層 ４２ 貯蔵ロール
【手続補正２】
【補正対象書類名】図面
【補正対象項目名】全図
【補正方法】変更
【補正内容】
【図１】
【図２】
【図３】
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 31/30 7141−4Ｆ // Ａ６１Ｂ 19/08 Ｄ０４Ｈ 3/03 Ａ 7199−3Ｂ Ｂ２９Ｌ 9:00 4Ｆ

Claims (4)

    【特許請求の範囲】
  1. 【請求項１】 押し出し被覆された不織布積層体を形成
    する方法であって、 連続的に、かつランダムに堆積された熱可塑性繊維を熱
    可塑性微小繊維のウェブに隣接させて配置する工程を備
    え、前記ウェブは表面と裏面とを有し、前記マットは前
    記ウェブの前記表面に隣接して配置され、 複数の結合箇所を介して前記マットを前記ウェブに超音
    波結合させ、全結合面積が前記ウェブまたは前記マット
    の何れかの表面積の１５％以下になるようにする工程を
    備え、 被覆材を前記ウェブの前記裏面上に押し出し、液体非透
    過性フィルムの連続層を形成する工程を備えた方法。
  2. 【請求項２】 前記マットを前記ウェブに隣接させて配
    置する前に前記マットを点結合させる工程をさらに備え
    ることを特徴とする請求項１記載の方法。
  3. 【請求項３】 前記マットの全表面積に対する全結合面
    積は前記点結合によって前記マットの全表面積の２０％
    以上となることを特徴とする請求項２記載の方法。
  4. 【請求項４】 連続的、かつランダムに堆積された熱可
    塑性繊維のマットを備え、 表面と裏面とを有する熱可塑性メルトブロウン微小繊維
    のウェブを備え、前記マットは前記ウェブの前記表面に
    超音波結合されており、その際の全表面積に対する結合
    面積の比率は１５％以下であり、 前記ウェブの前記裏面に押し出し被覆されたポリマー材
    料の連続フィルムを備えた押し出し被覆された不織布の
    積層体。
JP3213774A 1990-09-06 1991-08-26 不織−メルトブロウン−フィルム組成物積層体 Pending JPH05169575A (ja)