JPH0515165B2 - - Google Patents

Info

Publication number
JPH0515165B2
JPH0515165B2 JP60070755A JP7075585A JPH0515165B2 JP H0515165 B2 JPH0515165 B2 JP H0515165B2 JP 60070755 A JP60070755 A JP 60070755A JP 7075585 A JP7075585 A JP 7075585A JP H0515165 B2 JPH0515165 B2 JP H0515165B2
Authority
JP
Japan
Prior art keywords
article
substrate
composition
heat
polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP60070755A
Other languages
English (en)
Other versions
JPS60232932A (ja
Inventor
Roozenueigu Neichan
Soni Purabin
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Raychem Corp
Original Assignee
Raychem Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Raychem Corp filed Critical Raychem Corp
Publication of JPS60232932A publication Critical patent/JPS60232932A/ja
Publication of JPH0515165B2 publication Critical patent/JPH0515165B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】
［産業上の利用分野］ 本発明は、導電性ポリマー組成物を含んでなる
物品（特に熱回復性物品）、および基材（特に有
機ポリマーからなるパイプ）に接合、修復、補強
または他の改良を行う用途に関する。 ［従来技術］ パイプおよび他の基材に接合、修復、補強およ
び他の改良を行う多くの方法が知られている。こ
れらは、電力供給された場合に物品回復に必要な
熱を供給する導電性ポリマーを含んでなる熱回復
性物品を使用する方法を包含する。米国特許第
4085286、4177446および4421581号ならびに英国
特許第1265164号を参照されたい。しかし、全て
の既知の方法は、特に、有機ポリマーからなるパ
イプ（「プラスチツクパイプ」と呼ばれることが
頻繁である。）の接合において、１つまたはそれ
以上の不都合を有する。本発明は、プラスチツク
パイプ、およびポリマー組成物からなる外表面を
少なくとも有する他の基材を接合する新規で有益
な方法に関する。本発明の方法において、導電性
ポリマーからなつており、導電性ポリマーに電流
を流すことによつてその収縮温度に加熱される熱
収縮性カツプラーを使用することが好ましい。い
くつかの導電性ポリマー組成物は本発明のカツプ
ラーに適している。１つの好ましいカツプラーは
焼結導電性ポリマー組成物からなり、そのような
焼結組成物は、新規であり本発明の一部を形成す
る他の物品および方法においても非常に有用であ
る。 ［発明の構成］ 第１の要旨によれば、本発明は、有機ポリマー
を含んでなる熱軟化性の第１組成物からなる外表
面を少なくとも有する基材に接合、修復、補強ま
たは他の改良を行う方法であつて、 (1) (a)第１組成物と相溶し、(b)有機ポリマー、お
よびポリマーに分散する粒状導電性充填剤を含
んでなることを特徴とする第２組成物からなる
熱回復性要素を有してなる物品、ならびに接
合、修復、補強もしくは他の改良を行うべき基
材の一部分を相互に隣接して配置し、 (2) 要素内に熱を発生し、接合、修復、補強また
は他の改良を行うべき基材の一部分を接触する
ように要素を回復させ、要素と外表面の間を融
合させる ことを含んでなる方法を提供する。要素に電流を
流すことによつて熱を発生することが好ましい。 「融合」なる語句は、熱回復性要素と基材の外
表面の間に生じると表示され、本明細書におい
て、充分な分子的相溶性が要素と基材外表面の間
に存在し、基材の機械的性能に等しいかそれ以上
の機械的性能を供給する結合が形成することを意
味する。これは、ジエイ・エヌ・アナンドによる
接着（Adhesion）１（1969年）16頁、および接着
（Adhesion）２（1970年）16〜22頁に規定されて
いるように粘弾性接触を介してよく、あるいは界
面領域内に１つのポリマーの他での連続濃度勾配
があるように、ポリマー／ポリマー界面の横方向
に分子拡散を介してよい。 １つの好ましい態様において、物品は、粒子が
その識別性を失うことなく癒着するように一体に
焼結している有機ポリマー粒子から本質的になる
マトリツクスを含んでなる焼結導電性ポリマー組
成物からなる。焼結導電性ポリマー組成物は、分
子量少なくとも300万の超高分子量ポリエチレン
を含んでなることが好ましい。他の好ましい態様
において、物品は、好ましくは150000〜600000、
更に好ましくは300000〜400000の分子量の高分子
量ポリマーからなる。高分子量ポリマーは、焼結
されるより溶融形成されることが多い。高分子量
ポリエチレンが特に好ましい。 第２の要旨によれば、本発明は、 (a) 粒子がその識別性を失うことなく癒着するよ
うに一体に焼結している有機ポリマー粒子から
本質的になるマトリツクス、および (b) マトリツクスに分散しているが、癒着粒子の
境界付近でまたは境界でのみ実質的に存在する
粒状導電性充填剤 を含んでなる導電性ポリマー組成物からなる熱回
復性要素を有してなる物品を提供する。 第３の要旨によれば、本発明は、基材に接合、
修復、補強または他の改良を行う方法であつて、
上記のように焼結した導電性ポリマー組成物から
なる要素を有してなる物品（好ましくは熱回復性
物品）を基材に隣接して配置し、導電性ポリマー
要素内に熱を（好ましくは電流を流すことによつ
て）発生させ、物品を直接または間接に基材に密
着させることを含んでなる方法を提供する。 第４の要旨によれば、本発明は、その間に空〓
があるように相互に隣接して配置された少なくと
も２つの基材を接合する方法であつて、 (1) 少なくとも１つの基材が熱軟化性組成物から
なる外表面を少なくとも有するように基材を選
択し、および／または熱軟化性組成物からなる
インサート部材を供給し、 (2) 有機ポリマー、およびポリマーに分散してい
る粒状導電性充填剤を含んでなる熱回復性要素
を有してなる物品を基材に隣接して配置し、 (3) 要素内に熱を発生させ、(i)接合すべき基材の
一部分に接触するように要素を回復させ、(ii)熱
軟化性組成物を軟化させ、(iii)軟化した組成物に
よつて基材間の空隙を充填する ことを含んでなる方法を提供する。 第５の要旨によれば、本発明は、中空基材に接
合、修復、補強または他の改良を行う方法であつ
て、 (1) 有機ポリマー、およびポリマーに分散してい
る粒状導電性充填剤を含んでなる熱回復性要素
を有してなる物品を基材に隣接して配置し、 (2) 外表面に突起を有する支持部材を中空基材内
に配置し、 (3) 要素内に熱を発生させ、要素が支持部材の突
起間の空隙に基材を変形するように基材に向か
つて要素を回復させる ことを含んでなる方法を提供する。 本発明は、第１および第３の要旨の方法により
形成した改良された基材、ならびに第４の要旨の
方法により供給された少なくとも２つの基材の間
の接合をも提供する。 本発明の方法は、パイプおよびケーブル（例え
ば、電力ケーブル、通信ケーブルおよび光フアイ
バーを包含するケーブル）を包含するあらゆる基
材に接合、修復、補強または他の改良を行うため
に用いることができる。導電性ポリマー物品が熱
回復性物品であり、基材（２つまたはそれ以上の
基材を一体に接合する場合に少なくとも１つの基
材）が有機ポリマーを含んでなる熱軟化性組成物
（本明細書において「第１組成物」と呼ぶ。）から
なる（または該組成物からなる外表面を少なくと
も有する）場合、特に良好な結果が得られる。本
明細書において「有機ポリマー」なる語句は、主
鎖および／または側鎖に炭素を有するあらゆるポ
リマーを表し、例えば、オレフインモノマーのポ
リマー、ポリアミド、ポリエステル、ポリアクリ
レート、ポリイミド、ポリカーボネートおよびポ
リシロキサンを包含する。そのような物品および
基材を用いる場合、物品が回復して基材に接触し
た後に、基材の表面が加熱され軟化するように、
回復性物品を加熱し続けることが好ましい。これ
は、少なくとも一方の熱軟化性ポリマーが他方を
湿潤し、よつて界面で組成物を（上記のように）
融合するように、基材表面および回復性物品が相
互に直接に接触し、相互に相溶する組成物からな
る場合に特に有益である。例えば、好ましい焼結
導電性ポリマー組成物、または高分子量組成物を
用いる場合に、粘ちよう性の少ない基材組成物
は、焼結した物品またはカツプラーのまわりにお
よびおそらくそれの中に湿潤および流動する。そ
のような融合を行うため、組成物の少なくとも一
方および好ましくは両方はその軟化点（結晶性ポ
リマーの場合に結晶融点）より高い温度になる。
異なつたポリマー組成物の相溶性は、組成物のポ
リマーおよび他の成分（例えば、充填剤）の両方
の化学的性質を包含する種々の因子に依存する。
しかし、当業者は、その知識および本明細書の開
示から、２つの特定組成物のいずれが相溶するか
を決めるについて困難を要しない。多くの場合
（全ての場合でない。）、相溶性は、２つの組成物
のポリマーの共通繰り返し単位の実質量の結果で
ある。例えば、第１組成物のポリマー成分の繰り
返し単位の少なくとも10％、好ましくは少なくと
も30％が第２組成物のポリマー成分の少なくとも
10％、好ましくは少なくとも30％と同じである場
合がある。これら％は繰り返し単位の数に基づ
く。 界面を通過して結合するように２つの組成物が
相互に相溶しないおよび／または加熱されない場
合、および／または基材（２つもしくはそれ以上
の基材を用いる場合に少なくとも１つの基材）が
熱軟化性ポリマー組成物からならない場合（例え
ば、金属、コンクリートまたは熱硬化性ポリマー
からなる場合）、満足な結果を得るため、最終製
品の機能的要求に応じて、他の工程が好ましい。
そのような工程は、例えば、基材と物品の間のイ
ンサートの使用を包含する。本明細書において
「インサート」なる語句は、広い意味において、
自己支持または一表面に支持された層の形態であ
ろうと、基材への物品の取り付けを促進するまた
は界面での他の望ましい結果（例えば、電気絶
縁）を与えるあらゆる物品を包含する。インサー
トは、界面での物理的および／または化学的効果
の結果として効果的であり得て、例えば、ホツト
メルト接着剤、熱硬化性接着剤または熱硬化性樹
脂（例えば、エポキシ樹脂）を包含する接着剤、
一方もしくは両方の表面に対しての架橋剤または
他の化学的活性剤、熱回復性物品の溝に嵌合する
Ｏ−リングもしくは他の封止部材を包含する金
属、弾性もしくは繊維状部材であつてもよい。イ
ンサートの性質に応じて、インサート、基材およ
び物品の１つまたはそれ以上が望ましく変化する
ように、回復性物品が回復した後に回復性物品を
加熱し続けることが好ましい。 インサートは、回復性要素の内表面のライニン
グとして供給されてよく、あるいは（例えば、基
材に巻き付けるテープの形状で）別に供給かつ装
着されてよい。 本発明の第４の要旨によれば、基材からもしく
は別のインサート部材からもしくは両方からの熱
軟化性材料が基材間の空隙を充填するため、回復
性要素内に熱を発生させる。軟化した材料が基材
間の空隙を充填するよりも空隙を通過して流動す
るのを防止するため、基材に隣接して支持部材を
も含むことが好ましい。支持部材には、基材間に
空隙を与えるため基材を離す止めをも供給してよ
い。用いてよいライナーの例には、(i)基材間に良
好な結合を形成するため加熱に硬化するように好
ましくは選択された樹脂、特に熱硬化性樹脂（例
えば、エポキシ樹脂）、および(ii)熱活性接着剤
（例えば、ホツトメルト接着剤）がある。樹脂ま
たは接着剤は繊維またはホイスカーによつて補強
することが好ましい。 本発明の第４の要旨の方法は、熱回復性要素を
有してなる物品と相溶しない基材間にジヨイント
を形成することを可能にするので、特に有益であ
る。物品が、接合または修復すべき基材と相溶し
ない場合、軟化した材料は、空隙を充填し、形成
したジヨイントを補強するように機能する。補強
が必要でない場合、物品は、形成したジヨイント
から除去してもよい。本方法は、ライナー材料を
適切に選択することによつて、接合領域の性質
（例えば、ジヨイントの電気的連続性）が制御さ
れるので有益でもある。例えば、絶縁電気ケーブ
ルの一部の末端での絶縁を剥がし、ケーブルを電
気接続する場合、本方法は剥離絶縁を接合するた
めに用いてよい。ジヨイントの電気的連続性また
は不連続性は、導電性または非導電性インサート
を適切に選択することによつて行える。いくつか
の用途において、インサートは２つの要素からな
り、例えば、１つの導電性要素および１つの非導
電性要素は接合領域において望ましい性質を得る
ように選択してよい。 ライナーを本発明の方法（好ましくは第４の方
法）において用いる場合、熱回復性要素に(a)(i)そ
の識別性を失うことなく癒着するように焼結した
有機ポリマー粒子から本質的になるマトリツク
ス、および(ii)マトリツクスに分散しているが、癒
着した粒子の境界付近でまたは境界でのみ実質的
に存在する粒状導電性充填剤を含んでなる組成
物、あるいは(b)架橋していてもしていなくてもよ
い150000〜600000、更に好ましくは200000〜
400000の分子量の高分子量ポリマーを用いること
が好ましい。超高分子量ポリエチレンまたは高分
子量ポリエチレンを用いることは特に好ましい。
そのような材料で得られる利点は、そのような材
料が数時間までの長い時間にわたつてその融点よ
り100℃またはそれ以上高い温度の加熱に耐える
ことである。焼結材料または架橋高分子量材料を
用いる他の利点は、数百psi半径圧力程度の高回
復力を及ぼすことである。高回復力は、本発明の
第４の方法において、基材間の空隙を充填するた
め良好な駆動力を確実に与えるので特に有益であ
る。 パイプの表面、ライナーまたはこれら両方が流
動して基材間の空隙を充填する場合、物品は、物
品の末端に隣接したライナーまたはパイプのそれ
ら部分が軟化せず、よつて物品末端からの軟化し
た材料の流出を実質的に防止するダムとして働く
ように設計されていることが好ましい。これは、
例えば、その両末端に内環状溝を有するように物
品を形成することによつて行える。 本発明の第４の要旨による方法は、例えば、ガ
ラス補強プラスチツクパイプを接続するのに用い
ることができる。 物品は、基材の性質に応じてあらゆる適切な形
状であつてよい。１つの態様において物品は一般
にチユーブ状、好ましくは円筒状である。物品の
壁厚は、形状に関係なく、少なくとも0.07インチ
であることが好ましい。チユーブ状物品は、種々
の方法、例えば、直接にその形状に成形、押出、
または焼結することによつて、または所望厚さに
になるまで多層テープをマンドレルに螺旋状に巻
き付け、次いでマンドレルを除去することによつ
て形成してもよい。巻き付けたテープは、テープ
層を融合するために、マンドレルを除去する前に
加熱してよい。テープは押出によつて形成するこ
とが好ましい。 １つまたはそれ以上の基材が、過剰な加熱によ
り悪影響を受ける機能的性質を有する熱軟化性ポ
リマー組成物または他の材料を含んでなる場合、
悪影響を与えない量に導電性ポリマー内での発熱
を限定するように注意する必要がある。従つて熱
軟化性ポリマー材料からなるパイプにおいて、パ
イプが（カツプラーからの圧力の結果としてまた
は配向パイプの結果として）ゆがむ前に、加熱は
悪影響を実質的に与えない程度で中断しなければ
ならない。パイプの内表面は実質的に変化しない
ことが好ましい。 本発明の非常に有用な１つの態様において、２
つまたはそれ以上の基材を接合するためカツプラ
ー、好ましくは熱回復性カツプラーを用いること
が好ましい。パイプは、寸法が同じでも異なつて
もよく、組成が同じでも異なつてもよい。パイプ
末端は接合でき、１本またはそれ以上のパイプは
他のパイプ（通常、大きな直径のパイプ）に分岐
として接続できる。本発明の好ましい方法におい
て熱軟化性有機ポリマー組成物からそれぞれなる
２本のパイプ（好ましくは２本の同一のパイプ）
は、半径方向収縮性の中空カツプラーを用いて一
直線に接合する。 本発明のカツプラーは、異なつた寸法および／
または形状の断面を有する基材（例えば、パイ
プ）を接合するため有益に用いることができる。
従つて、例えば、小直径のパイプを大直径のパイ
プに接続することができる。パイプの寸法間の差
の限界はカツプラーの回復比によつて決まる。 他の好ましい方法において第１パイプの末端
は、 (1) 第２パイプの壁に孔を形成し、 (2) (a)第２パイプの壁に全体的に嵌合し、孔を有
する部分を有してなり、(b)カツプラーが加熱さ
れた時に孔の寸法が減少するように孔に隣接す
る領域において熱回復性であるカツプラーを第
２パイプに隣接して配置し、カツプラーの孔を
第２パイプの孔に軸合わせし、 (3) カツプラーの孔を通過して第１パイプの末端
を配置し、 (4) 導電性ポリマー要素に電流を流し、第１パイ
プに接触するようにカツプラーを回復させる ことを含んでなる方法によつて第２パイプに分岐
として接合できる。この方法において第１および
第２パイプそれぞれは、熱軟化性ポリマー組成物
からなることが好ましく、カツプラーは両方のパ
イプに融合することが好ましい。第１パイプの末
端は好ましくは滑り嵌めとして第２パイプの壁の
孔に通すことが好ましい。しかし、第２パイプの
壁の孔が第１パイプより小さいことも可能であ
り、第１パイプは第２パイプの壁に対して衝接さ
れる。第１パイプの末端は、第２パイプの壁に対
してきつちりとはまるような形状を有している。
この方法においてカツプラーは、一般に第２パイ
プの壁に初めに全体的に嵌合する部分を有してな
る。この部分は壁に始めに密接に嵌合する必要が
ないが、この方法が完了する前に嵌合しなければ
ならない。これは、第２パイプに隣接する部分が
半径方向収縮性のシリンダの少なくとも一部分で
あり、第２パイプに接触するように収縮するカツ
プラーによつて達成することが好ましい。そのよ
うなカツプラーは、例えば、割れシリンダを変形
することによつて、また第２パイプのまわりに回
復性シート部材を巻き付けて巻き付け末端を一体
に固定することによつて形成できる。あるいはま
たは加えて、物品は、第２パイプに密着するよう
に、導電性ポリマー内に熱を発生させながら、第
２パイプに向かつて物品を押し付ける固定部材
（例えば、弾性ストラツプ）によつて第２パイプ
に固定できる。 本発明の第５の要旨または本発明の他の要旨の
好ましい態様によれば、特に基材（例えば、パイ
プ）を一体に接合する場合、中空内部支持部材を
用いる。例えば、支持部材は、パイプの初期内部
寸法を実質的に保つようにのみ機能できる（例え
ば、そうしないからカツプラーによりゆがむ薄壁
プラスチツクパイプを接合する場合。）。支持部材
は、（例えば、支持部材の外表面上の周囲リブも
しくは他の突起の存在によつて、または中央部分
が末端部分より小さい寸法を有する支持部材の使
用によつて）パイプの形状を変えることにより接
続の強度を増加することができる。外突起を有す
るそのような支持の使用は、基材が物品に融合し
ないポリマー（例えば、架橋ポリエチレン）を含
んでなる場合に基材に接合、補強、補修または他
の改良を行う方法において特に好ましい。支持部
材は、パイプに対して接着剤を供給してもよく、
および／または１本もしくはそれ以上のパイプに
化学的に結合してもよい。支持部材は、パイプ末
端が衝接できる止めをも供給してよく、またはパ
イプを軸合わせする（または他の好ましい空間関
係にパイプを保つ）のを助けてもよい。支持部材
は、ジヨイントが実質的に可撓性である場合に屈
曲力が支持部材末端に集中しないように、カツプ
ラーより短いことが好ましい。支持部材は、基材
を挿入できる１つまたはそれ以上のポケツトを与
えるように物品に固定できる。 本発明は、少なくとも１本のパイプが有機ポリ
マー、特にポリエチレン、ポリプロピレンまたは
ポリ塩化ビニルを基本とする組成物からなる場合
に、２本またはそれ以上のパイプ（例えば、かん
がいパイプなどの天然ガスまたは水を配給するの
に用いるポリエチレンパイプ）を接合するのに特
に有用である。 本発明において用いる物品は、導電性ポリマー
組成物からなる要素、好ましくは熱回復性要素を
含んでなる（該要素からなつてよい）。熱は導電
性ポリマー組成物内に発生し、これは要素に電流
を流すことによつて行うことが好ましい。しか
し、内部熱発生の他の方法（例えば、誘導または
マイクロ波加熱）によつても行える。導電性ポリ
マー組成物はよく知られており、有機ポリマー、
および有機ポリマー成分に分散している粒状導電
性充填剤を含んでなる。本明細書において「粒
状」なる語句は、高いよび低いアスペクト比（例
えば、球状、板状または針状）の粒子を含むあら
ゆる形状の粒子を包含する。本発明において好ま
しい粒状充填剤はカーボンブラツクである。本発
明において用いる導電性ポリマーは23℃で0.5〜
100Ω・cmの抵抗率を有することが好ましく、こ
の範囲での特に好ましい値は、導電性ポリマーの
組成、物品の寸法、電極位置および電源に依存す
る。焼結導電性ポリマーを用いる場合、組成物は
1.5〜100Ω・cmの抵抗率を有することが好まし
い。これら係数は、満足な結果（例えば、物品の
回復、および適切ならば界面での融合）がかなり
短い時間（例えば、10分以内、好ましくは５分以
内）で得られるように選択することが好ましい。
適切な電源は、例えば、６、12、24もしくは48V
の直流電圧（この場合に0.5〜10Ω・cmの抵抗率
が好ましい。）および36〜40、110〜120もしくは
220〜240Vの交流電圧（この場合に高い抵抗率
（例えば、50〜100Ω・cm）が適切である。）を包
含する。物品の好ましい寸法がその所望用途に依
存するのは当然である。チユーブ状物品におい
て、物品の直径：壁厚の比は回復後に18：１（例
えば、２：１）より小さいことが好ましい。（回
復前に）少なくとも0.07インチ、好ましくは少な
くとも0.1インチのかなり大きい壁厚は、機械的
応力および内部圧力に耐えるように適切な強度を
確実に与えるため好ましいことが頻繁にある。物
品が（例えば、パイプの内表面を軟化することな
くプラスチツクパイプの外表面の急速な軟化を促
進するように）回復温度においてさえ高速度で発
熱することが好ましいことも頻繁にある。このた
め、組成物が回復温度までまたはこれより少し高
い温度（例えば、これより50℃まで高い温度）で
PTC挙動を示さないことが好ましく、23〜（TR
＋50）℃の温度（ここでTRは回復温度である。）
で、５より少ない、好ましくは２より少ない係数
で変化することが好ましい。 多くの導電性ポリマー組成物が知られており、
これらのほとんどは溶融混合法によつて製造され
る。充填剤充填は、かなり劣悪な物理的性質を典
型的に導く溶融ポリマー組成物での好ましい抵抗
率値を得るため必要である。例えば、少なくとも
1.2、好ましくは少なくとも1.5の拡張比は、（パ
イプの偏心を含む基材の寸法範囲に適合するた
め）本発明において好ましく、高充填剤充填で達
成するのが典型的に難しい。驚くべきことに、
150000〜600000の分子量の溶融加工高分子量ポリ
エチレンを用いる場合、充填剤充填を増加すると
ともに生じる物理的性質の変化は、低い分子量の
ポリエチレンより少なく、例えば、1.5の拡張比
が達成できる。この溶融加工高分子量ポリエチレ
ンは、本発明の導電性ポリマー組成物のため好ま
しい材料である。 高分子量ポリエチレンは、ポリマー粒子および
導電性充填剤を乾燥混合または溶融混合すること
によつて製造できる。所定抵抗率値を得るのに必
要な導電性充填剤の量は超高分子量ポリエチレン
の場合より多い。高分子量ポリエチレン組成物
は、カーボンブラツクまたは他の導電性充填剤を
26重量％より少なく、好ましくは24重量％より少
なく、特に18〜24重量％含むことが好ましい。 他の態様において、得られる有益さの点から、
本発明において溶融加工ポリマーより焼結導電性
ポリマーを用いることが好ましい。焼結組成物
は、 (a) 粒子が識別性を失うことなく癒着するように
一体に焼結している超高分子量ポリエチレンの
粒子から本質的になるマトリツクス、および (b) マトリツクスに分散しているが、癒着粒子の
境界付近でまたは境界でのみ実質的に存在する 粒状充填剤（好ましくはカーボンブラツク）を
含んでなる（好ましくはこれらから本質的にな
る）。そのような導電性ポリマーは、ポリマー粒
子および導電性充填剤の乾燥混合物を焼結するこ
とによつて製造できる。典型的な方法は、乾燥混
合物を圧縮し、ポリマーが軟化するが過剰に流動
しない温度で大気圧またはそれ以上の圧力で圧縮
混合物を焼結し、次いで加圧下で冷却することを
包含する。所定抵抗率値を得るため必要な導電性
充填剤の量は、溶融混合製品においてよりずつと
少ない。従つて、本発明において用いるのに好ま
しい焼結組成物はカーボンブラツクまたは他の導
電性充填剤を９体積％より少なく、好ましくは７
体積％より少なく、特に２〜６体積％含む。これ
ら充填において所望抵抗率値を得るためカーボン
ブラツク（または他の充填剤）を選択するのに注
意を要する。アクゾ・ケミーから市販されている
ケツチエンブラツク・イーシー（Ketjenblack
EC）を用いることによつて優れた結果が得られ
る。 好ましい溶融形成高分子量組成物においてまた
は焼結導電性ポリマー組成物において用いるポリ
マーは、溶融形成焼結温度でかなり高い粘度を有
するポリマーであることが好ましい。従つて、そ
の軟化点より50℃高い温度において５Kgの負荷で
0.3ｇ／10分より少ない、更に好ましくは0.1ｇ／
10分より少ない、特に0.05ｇ／10分より少ないメ
ルトフローインデツクス、および15Kgの負荷で
0.3ｇ／10分より少ない、更に好ましくは1.0ｇ／
10分より少ない、特に0.1ｇ／10分より少ないメ
ルトフローインデツクスを有するポリマーを用い
ることが好ましい。超高分子量ポリエチレン
（UHMWPE）、特に約150万より大きい、好まし
くは約30万より大きい分子量を有するそのような
ポリエチレンを用いることによつて特に良好な結
果が得られる。このことに関しては、本出願人に
よる1984年２月21日出願の米国特許出願第582105
号を参照されたい。焼結した場合に同様に挙動す
る他のポリマーはポリテトラフルオロエチレン
（PTFE）である。焼結できる他のポリマーは、
焼結条件下で、好ましい粘度より低い粘度である
が、ポリフエニレン10スルフイド（PPS）および
ポリイミドである。 溶融加工高分子量ポリマー、好ましくは高分子
量ポリエチレン（HMWPE）、特に約150000、好
ましくは200000より大きい分子量を有するそのよ
うなポリエチレンを用いることによつて特に良好
な結果が得られる。 分子量は種々の方法で測定できる。本発明にお
いて高分子量ポリエチレン（超高分子量ポリマー
でない。）で言う分子量値は、次のゲル透過クロ
マトグラフイー法を用いて測定した。 ポリエチレンを粉末に破砕し、ポリマーの劣化
を防止するため酸化防止剤を含む１，２，４−ト
リクロロベンゼン10mlを粉末30mgに加えた。窒素
気流下、撹拌しながら15分間加熱してポリエチレ
ンを溶解した。溶液を濾過し、温度145℃におい
て高温ゲル透過クロマトグラフイー装置（ウオー
ターズモデル150Cとして市販されている。）に注
入した。溶離液を示差屈折計によつてモニターし
た。クロマトグラフイー装置は、アメリカ合衆国
ナシヨナル・ビユーロー・オブ・スタンダードか
ら供給されている標準試料を用いて検量した。 ポリエチレン以外の材料をも本発明において用
いることができる。他の材料の例として、他のオ
レフイン（例えば、ポリプロピレンおよびオレフ
インコポリマー）、ポリエステル、例えば、ポリ
ビニリデンフルオライド、パーフルオロアルコキ
シポリマー、エチレンテトラフルオロエチレン、
フツ素化エチレンプロピレンおよびエチルクロロ
トリフルオロエチレンならびにアリーレン（例え
ば、ポリエーテルエーテルケトン）が挙げられ
る。好ましい分子量範囲は、本発明に従つて基材
に接合、修復、補強または他の改良を行うのに望
ましい性質（例えば、回復力および物理的性質）
を得るため、それぞれの種類のポリマーにおいて
異なつている。 １つの態様において、熱回復性にするため拡張
する前に回復性要素の組成物を架橋することが好
ましい。架橋は、例えば、高エネルギー電子線ま
たはガンマ線などにより組成物を照射することに
よつて行える。架橋による性質の変化を示すため
HMWPEの架橋試料および非架橋試料を種々の
比較試験を行つた。結果を第１表に示す。
【表】 明らかなように架橋によつて材料の全ての物理
的性質（特に靭性）が改良される。架橋材料を用
いる場合、その融点より低い温度で拡張しなけれ
ばならない非架橋試料において必要であるより少
ない拡張力が必要であるように、架橋材料をその
融点より高い温度で拡張することもできる。架橋
材料を用いることによつて高回復力を得ることも
できる。 熱回復性要素は全体にわたつて同じ組成からな
ることが好ましいが、異なつた部分において異な
つた導電性ポリマーからなつてよい。熱回復性要
素は導電性ポリマー要素の一部分または全部であ
つてよい。熱回復性要素は熱回復性物品の唯一の
熱回復性部分であることが好ましいが、物品は、
導電性ポリマーからならない第２熱回復性要素を
も含んでよい。熱回復性物品は、円筒状もしくは
他の閉鎖断面の半径方向収縮性チユーブ、または
そのようなチユーブの一部分（例えば、割れシリ
ンダ）を有してなることが好ましい。しかし、他
の形状、特に、基材に巻き付けて巻き付け末端を
固定することにより熱回復性エンクロージヤーに
形成するシート、または基材に一体に固定できる
２つもしくはそれ以上の部品（例えば、ハーフシ
エル）であつてよい。要素の抵抗率および／また
は形状は、基材に及ぼす残留応力および／または
回復力および／または加熱速度が場所によつて望
ましく変化するように変化してよい。 熱回復性要素は２つまたはそれ以上の層を有し
てなつてよい。層は同じ材料からなつてよいが、
異なつた材料からなることが好ましい。好ましい
態様において１つの層は、有機ポリマー、および
有機ポリマーに分散している粒状導電性充填剤を
含んでなり、電流の通過により熱を発生するよう
に設計されており、他の層は望ましい性質に応じ
て選択された非導電性材料を含んでなる。導電性
充填剤を含有する層は非導電性ポリマー層の内側
に位置してよく、この逆であつてもよい。充填剤
充填剤が熱回復性要素の内層を与える場合、下の
基材に結合させる熱は要素／基材界面でのみ必要
である。これは、カツプリングを回復するのに必
要な熱を好都合に低減する。このアレンジメント
において非導電性外層は絶縁層として働くように
適切な材料から選択してよく、環境の冷却効果を
低減する。これは、更に、要素の回復に必要な熱
を減少し、必要な熱の量を周囲温度に無関係にす
る。外層は支持または補強層として働いてもよ
く、代わりにそのように働いてもよい。例えば、
外層は要素の衝撃性質を改良するように、充填さ
れた導電性内層より靭性がある材料からなつてよ
い。逆のアレンジメントにおいて非導電性ポリマ
ー内層が、導電性充填剤を含む層の内側に位置す
る場合、非導電性ポリマー内層は良好な結合を形
成するように下にある基材と相溶するように選択
することが好都合である。例えば、内層は、容易
に流動して下にある基材に融合する非架橋ポリマ
ーを含んでなつてよい。例えば、ポリエチレンパ
イプを接続する場合、内相は非架橋ポリエチレン
を含んでなつてよい。 ２重または多層熱回復性要素は、あらゆる適切
な二次加工技術によつて製造してよい。例えば、
層は共押出または共成形してよく、次いで形成し
た２重または多層要素を全体として拡張すること
が好ましい。テープ巻き付けによつて要素を形成
する場合、２種またはそれ以上の異なつた材料か
らなるテープを用いてよい。一つのテープは導電
性ポリマー材料を含んでなり、他のテープは非導
電性材料を含んでなることが好ましい。（チユー
ブ構造において最も拡張された層である）内層が
非導電性ポリマー層であるアレンジメントにおい
て、内層は、高拡張比に耐えるように充填してい
ないポリマー材料を含んでなることが好ましい。
そのようなアレンジメントにおいて1.5程度の高
拡張比が得られる。 高回復性要素を製造するため押出を用いる場
合、種々の電極アレンジメントを用いてよい。例
えば、一列の軸方向に伸びる電極を用いてよく、
導電性ポリマーをその上に押出してよい。あるい
は環状電極を要素末端に配置してよい。 多くの場合、望ましい熱回復度を得るため、導
電性ポリマーを好ましくは（例えば、３〜20Mラ
ドの）照射によつて架橋することが望ましい（ま
たは必要である）。導電性ポリマーと基材の間の
融合を望む場合、架橋度はこれを可能にするよう
に選択すべきである。しかし、高分子量ポリエチ
レンまたは焼結UHMWPE導電性ポリマー組成
物を用いる場合、架橋が不可欠でないことが頻繁
にある。 導電性ポリマーを満足な電流が確実に流れるよ
うにあらゆる適切な電極を用い得る。よつて、電
極は、成形時に導電性ポリマーを含めることがで
き、成形要素の外表面に適用することができる。
電極は、要素の回復時に形状変化を必要としない
ように配置しなければならず、あるいは要素が回
復する時の形状変化に適合しなければならない。
（例えば、市販されている銀含有塗料を用いて）
チユーブ状要素の上に電極を塗り、要素が回復す
る時に銀塗布電極との接触を保つバネ負荷電気リ
ードを用いることによつて優れた効果が得られ
る。要すれば、電極を広げるため塗布電極を用い
て、導電性ポリマー要素にくぼみを形成し、可撓
性リードに取り付けられた電気コネクタでこれら
くぼみを塞ぐことも可能である。 １つの適切な電極システムは、本出願人による
米国特許出願第607991号に開示されている。ここ
で、電極は、要素が電極と要素の間に界面で電気
保全性を保つように回復する時にその形状および
寸法が変化するようになつている。 熱回復性要素は最適回復条件を制御する手段を
有してなつてよい。そのような手段は、例えば、
本出願人による米国特許出願第634241号および米
国特許出願第634242号に開示されている。 添付図面を参照して本発明を説明する。 第１図、および第１図のＡ−Ａ線での断面図で
ある第２図は、一直線に接合されている２本のプ
ラスチツクパイプ１および２の断面図を示す。パ
イプの末端は、導電性ポリマーからなる半径方向
回復性円筒状中空熱回復性カツプラー３の中央で
衝接している。銀塗布電極３１（これは実際、図
面に示すよりずつと薄い。）はカツプラーの環状
末端上に塗布されている。電極板４は、電源に接
続可能であり、固定ベアリング板４２を押し付け
る圧縮バネ４１によつて電極３１に押し付けられ
ている。電極板４を電源に接続する場合、カツプ
ラーはその収縮温度に発熱し、半径方向に収縮
し、パイプに接触する。同時に軸方向の収縮も生
じるが、バネ４１は電極板４を電極３１と接触し
た状態に保つ。好ましいことであるが、パイプ材
料が相互に相溶する場合、加熱はパイプがカツプ
ラーに融合するまで続けることが好ましい。 第３図は、第１図および第２図に示す方法によ
り形成したパイプジヨイントの断面図である。加
熱によつてパイプへのカツプラーの融合が生じる
が、パイプの軟化だけでなく収縮にも起因してパ
イプ末端でのゆがみが生じる。第３図に示すゆが
みの程度は望ましいものより多いが、ジヨイント
は完全に使用可能である。 第４図、および第４図のＢ−Ｂ線での断面図で
ある第５図は、パイプ１がパイプ２からの分岐で
あるように直角に接合するパイプ１および２の断
面図を示す。パイプ１の外径と同じ直径を持つ孔
がパイプ２の壁にあけられている。カツプラー３
は導電性ポリマーからなり、第２パイプに嵌合で
きる半径方向収縮性割れシリンダの形状である。
カツプラーの中央には、孔のまわりのカツプラー
領域が小さい寸法に熱回復するように、第２パイ
プの孔と同じ直径を持つており、カツプラーに小
さい孔をあけ望ましい直径に拡張して形成した孔
が存在する。カツプラー３は、孔が軸合わせされ
た状態でパイプ２に嵌合する。金属支持部材１２
がパイプ１の末端に配置され、カツプラーおよび
パイプ２の孔を通過して暗合し、滑り嵌めを形成
する。電流はカツプラー末端で銀塗布電極３１を
通過してカツプラーを流れ、カツプラーはパイプ
１に接触するように半径方向におよびパイプ２に
接触するように孔の中央に向かつて収縮する。出
来上がりのジヨイントは、カツプラーが回復した
後の第４図のＣ−Ｃ線での断面図として第６図に
示す。第４図および第５図に示す方法は、ある手
段が、カツプラーの発熱時にパイプ２との接触を
保ち続けてカツプラーに結合するように用いられ
る場合、孔のまわりでのみ回復性であるカツプラ
ーにおいても用いることができる。 第７図は、その末端よりその中央で小さい外径
を有しかつ外周囲リブ５１を有してなるチユーブ
状支持部材５を用いる以外は第１図と同様であ
る。支持部材は接続工程時にパイプを支持しかつ
パイプに係合し、第８図に示すジヨイントが形成
する。 第９図も、プラスチツクパイプ１を異なつた直
径の金属パイプ２に接合する本発明の使用を示
し、カツプラーが、金属パイプ２にカツプラーを
結合する非溶融接着剤層６の形態のインサートを
有してなる以外は第１図と同様である。支持部材
１２はプラスチツクパイプをも支持する。 第１０図は、２本のプラスチツクパイプ１およ
び２を接合するため共押出した２重層熱回復性カ
ツプラー３を使用する以外は第１図と同様であ
る。カツプラー３は、非導電性非充填高分子量ポ
リエチレンからなる外層３５、およびカーボンブ
ラツク充填高分子量ポリエチレンを含んでなる溶
融形成導電性ポリマーからなる内層３６を有して
なる。銀塗布電極３１は導電性層３６の環状末端
に塗布されている。電極が層３６を流れることに
よつて熱は実質的にカツプラー３とパイプ１およ
び２の間の結合線においてのみ発生する。よつて
回復に要する熱は最小である。層３５は加熱され
ず、補強および絶縁層として働く。 第１１図は、パイプ材料と相溶する焼結導電性
ポリマー組成物からなり、熱回復性でないパツチ
８を用いてプラスチツクパイプ１を修復すること
を示す。プラスチツクパイプ１は修復が必要な孔
１４を有する。パツチは孔の上に位置し、パツチ
およびテープのまわりに巻き付けられるテープ１
５によつて所定位置に保たれる。パツチが軟化し
パイプに融合するようにパツチに電流を流す。第
１２図は、第１１図のＤ−Ｄ線での出来上がつた
ものの断面図を示す。 第１３図は、パイプ末端が衝接する中央止め５
１を有する他のチユーブ状支持部材５を用いる以
外は第７図と同様である。止め５１は、パイプ末
端間の接着を促進するためホツトメルト接着剤か
らなり得て、および／またはパイプに嵌合するポ
ケツトを有する単一の物品を供給するためカツプ
ラーに固定できる。第１３図には、電気コネクタ
が嵌合できるくぼみ３２をも示す。 第１４図は、第７図および第１３図と同様であ
るが、パイプ末端が衝接する中央止め５１を有す
るチユーブ状支持５を用いる。止め５１はパイプ
１とパイプ２の間に空隙があるように、これら両
者を離す。接合すべきパイプ１および２はガラス
補強プラスチツクを含んでなり、その表面は加熱
時に軟化し、カツプラー３は超高分子量ポリエチ
レンを含んでなる。エポキシ接着性ガラスフイラ
メント補強テープ５５がジヨイントに数回巻き付
けられている。カツプラー３は、環状ワイヤ電極
３９が存在する末端において環状くぼみ３８を有
する。溝３８は銀塗料（図示せず。）で被覆され
ている。電流は電極３８および３９を通過してカ
ツプラー３を流れ、カツプラーはテープ５５に接
触するように回復し、エポキシテープ５５ならび
にパイプ１および２の表面は軟化する。回復力に
よつて、軟化した材料はパイプ１とパイプ２の間
の空隙を充填し、ここでエポキシは硬化してパイ
プ間に結合を形成する。よつて、パイプ末端の衝
接融合が行なわれる。カツプラーのくぼみ３９に
隣接するパイプ１および２の表面ならびにテープ
５５の部分は、カツプラーの本体に隣接する部分
より少なく加熱されるので、これら部分は軟化せ
ず、従つて、軟化した材料のカツプラー３の末端
からの流出を実質的に防止する。 ［実施例］ 以下に実施例を示し、本発明を更に詳しく説明
する。全ての実施例において２本のパイプを一体
に接続するためポリエチレンカツプラーを用い
た。実施例１および実施例３において
UHMWPEを用い、実施例２においてHMWPE
を用いた。実施例１および実施例２においてカツ
プラーはパイプと相溶したが、実施例３において
カツプラーはパイプに相溶せず、硬化性エポキシ
インサートをカツプラーとパイプの間に用いた。 実施例 １ 分子量約400万および平均粒子寸法約0.1mmの
UHMWPE粉末（ホスタレン（Hostalen）GUR
−413（商標名）、アメリカン・ヘキスト市販品）
95体積部、およびカーボンブラツク（ケツチエン
ブラツク・イーシー（Ketjen Black EC、商標
名）、アクゾ・ケミー市販品）５体積部を高速ブ
レンダーで完全に混合した。環状断面（内径0.8
インチ、外径1.2インチ）を有する円筒状型に混
合物を充填した。混合物を型内で、約15000psiの
圧力で室温で約５分間圧縮し、非常に低い圧力
（2psiまたはそれ以下）で約230℃で約60分間焼結
した。焼結完了後、約12000psiの圧力に保ちなが
ら焼結混合物を型内で約50℃に冷却した。次いで
型を開き、焼結製品を取出した。製品の長さは約
２インチであつた。 焼結製品は、約3Mラドの線量の照射によつて
架橋し、円錐台マンドレルを用いて120℃で内径
を約1.2インチに拡張して熱収縮性にした。拡張
した製品の環状末端に銀塗料電極を塗布した。電
極間での製品の抵抗率は約5Ωであり、導電性ポ
リマーの抵抗率は約3.8Ω・cmであつた。 外径約0.84インチおよび壁厚約0.11インチの２
本のポリエチレンパイプを一体に接続するため、
焼結製品を用いた。パイプ末端をカツプラー内に
配置し、パイプ末端をカツプラー中央で衝接させ
た。軸方向にバネ負荷されている金属板によつて
銀塗料電極を24交流Ｖ電源に接続した。カツプラ
ーは発熱し、その収縮温度に達した時（約30〜45
秒後）に収縮してパイプに接触した。バネ負荷金
属板は、カツプラーが収縮してもカツプラーと電
気接触を保つた。カツプラーに電流を更に１分間
流すと、パイプはカツプラーに融合した。 冷却後、ジヨイントを温度約80℃、内圧約
120psiに保つことによつ試験を行つた。500時間
後にジヨイントからの漏れはなく、試験を中断し
た。室温で引抜試験を行い、パイプの降伏が生じ
る場合に引抜試験を終えた。この時、ジヨイント
は正常なままであつた。 実施例 ２ HMWPEペレツト（マーレツクス（Marlex）
HXM50100（商標名）、フイリツプス・ケミカ
ル・シーオー市販品）74重量％、およびカーボン
ブラツク（ケツチエンブラツク・イーシー）25重
量％を、従来の混合を用いて（例えば、バンバリ
ー２ロールミルおよびペレツト製造押出機を用い
て）完全に混合した。混合物は、環状断面（内径
0.89インチ、外径1.2インチ）に連続的に押出し
た。 次いで円錐台マンドレルを用いて120℃で内径
約1.2インチに拡張することによつて押出製品を
熱回復性にした。拡張した製品の環状末端上に銀
塗料電極を塗布した。導電性ポリマーの抵抗率は
約0.5〜1.0Ω・cmであつた。 押出HMWPE製品を用いて、実施例１の
UHMWPEカツプラーにより接続したパイプと
同じである２本のポリエチレンパイプを接続し
た。アレンジメントは、弾性バンドにより軸方向
に負荷した金属板によつて電源に電極を接続する
以外はUHMWPEカツプラーで用いたのと同じ
であつた。接続したジヨイントは、UHMWPE
接続ジヨイントと同様にして試験した。
UHMWPE接続ジヨイントと同様に、500時間後
に漏れはなく、引抜試験の後にジヨイントは正常
なままであつた。 実施例 ３ UHMWPE（実施例１のものと同じであつた。）
93体積％とカーボンブラツク（実施例１のものと
同じであつた。）７体積％の乾燥混合物をラム押
出し、円筒状製品（内径1.8インチ、外径2.4イン
チ、長さ４インチ）を製造した。シリンダ内側の
末端に環状溝を付けた。 コバルト源にさらして約6Mラドの線量で照射
することによつてラム押出製品を架橋した。次い
で、130℃で内径を2.5インチにすることによつて
製品を熱収縮性にした。冷却後、銀塗料を溝に塗
布し、溝に電極を挿入した。 ２本のガラスフイラメント巻付エポキシパイプ
（外径1.9インチ、厚さ0.1インチ）を接続するた
めUHMWPEカツプラーを用いた。パイプの外
表面は、微細研摩紙で研摩して形成した。パイプ
を末端どうし軸合わせし、エポキシ接着性ガラス
フイラメントテープ（厚さ0.0075インチ、3M市
販品）を、ジヨイントの両側のパイプに約1.8イ
ンチにわたるようにジヨイントに巻き付けた。テ
ープは約８層で適用した。 UHMWPEカツプラーをテープの上に配置し、
ワイヤ電極を24V直流電源に接続した。カツプラ
ーは発熱し、収縮温度に達する（約４分）と収縮
してエポキシテープを把持した。24V電源からの
電流を更に10分間供給し、カツプラーを約200℃
にした。次いで電圧を10Vに下げ、更に70分間電
流を供給し、温度を200〜210℃に保つた。最後に
温度を230℃に上げ、この温度を更に10分間保つ
た。冷却後、テープを硬化した。 実施例１および２の方法と同様にしてジヨイン
トを試験した。漏れはなく、ジヨイントは正常の
ままであつた。
【図面の簡単な説明】
１，２……パイプ、３……カツプラー、４……
電極板、５，１２……支持部材、６……インサー
ト、８……パツチ、１４……孔、１５……テー
プ、３１……電極、３２……くぼみ、３５，３６
……層、４１……バネ、４２……ベアリング板、
５１……リブ。 第１図は本発明の方法によつてプラスチツクパ
イプを一直線に接合するアツセンブリを示す図、
第２図は第１図のＢ−Ｂ線での断面図、第３図は
第１図および第２図により示す方法によつて形成
した出来上がりのジヨイントを示す図、第４図お
よび第５図は１本のパイプが他のパイプに対して
分岐するようにプラスチツクパイプを接合するア
ツセンブリを示す図、第６図は第４図および第５
図により示す方法によつて形成した出来上がりの
ジヨイントを示す図、第７図は支持部材を用いて
２本のプラスチツクパイプを接合するアツセンブ
リを示す図、第８図は第６図および第７図により
示す方法によつて形成した出来上がりのジヨイン
トを示す図、第９図は金属パイプにプラスチツク
パイプを接合するアツセンブリを示す図、第１０
図は二重層カツプラーを用いてパイプを接合する
アツセンブリを示す図、第１１図はパイプの孔を
修復するアツセンブリを示す図、第１２図は第１
１図の方法により形成した修復パイプを示す図、
第１３図は２本のプラスチツクパイプを一直線に
接合する他のアツセンブリを示す図、第１４図
は、パイプと熱回復性要素の間のインサートを含
む、パイプを一直線に接合する他のアツセンブリ
を示す図である。

Claims (1)

  1. 【特許請求の範囲】 １ (A) 有機ポリマーを含んでなる熱軟化性組成
    物である第１組成物からなる外表面を有する基
    材、および (B) 熱回復性ではなく、 (a) 第１組成物と相溶し、 (b) 有機ポリマー、およびポリマーに分散する
    粒状導電性充填剤を含んでなり、 (c) その軟化点よりも50℃高い温度で５Kgの負
    荷で0.3ｇ／10未満のメルトフローインデツ
    クスを有し、その軟化点よりも50℃高い温度
    で15Kgの負荷で3.0ｇ／10分未満のメルトフ
    ローインデツクスを有する 第２組成物からなる導電性ポリマー要素を有し
    てなる物品 を一体に接合する方法であつて、 (1) 基材の外表面に直接に接触した状態に物品を
    配置し、 (2) 物品を基材と直接に接触させならが、電流を
    流すことによつて導電性ポリマー要素内に熱を
    発生させ、物品と基材の外表面との間に融合を
    生じさせる ことを含んでなる方法。 ２ (A) 第１組成物からなる外表面を有する基
    材、および (B) 熱回復性ではなく、 (a) 有機ポリマー、およびポリマーに分散する
    粒状導電性充填剤を含んでなり、 (b) その軟化点よりも50℃高い温度で５Kgの負
    荷で0.3ｇ／10分未満のメルトフローインデ
    ツクスを有し、その軟化点よりも50℃高い温
    度で15Kgの負荷で3.0ｇ／10分未満のメルト
    フローインデツクスを有する 第２組成物からなる導電性ポリマー要素を有し
    てなる物品 を一体に接合する方法であつて、 (1) 基材に隣接して物品を配置し、 (2) 熱により活性化された場合に基材への物品の
    取付強度を増加させる熱活性化インサートを物
    品と基材の間に配置し、 (3) インサートを介して基材に物品を間接的に接
    触させながら、電流を流すことによつて導電性
    ポリマー要素内に熱を発生させ、インサートを
    活性化させ、物品を基材に接合する ことを含んでなる方法。 ３ 第２組成物は、 (a) 有機ポリマー粒子がその識別性を完全に失う
    ことなく癒着するように一体に焼結した有機ポ
    リマー粒子から本質的になるマトリツクス、お
    よび (b) マトリツクスに分散しているが、癒着粒子の
    境界付近でまたは境界でのみ実質的に存在する
    粒状導電性充填剤 を含んでなる特許請求の範囲第１項または第２項
    に記載の方法。 ４ 第２組成物中の有機ポリマーが、150万以上、
    好ましくは300万以上、より好ましくは400万以上
    の分子量を有する焼結超高分子量ポリエチレンで
    あり、導電性充填剤が、カーボンブラツクであり
    組成物の２〜６体積％の量で存在する特許請求の
    範囲第１〜３項のいずれかに記載の方法。 ５ 第２組成物が、 (i) 少なくとも150000の分子量を有する溶融形成
    有機ポリマー、および (ii) ポリマー中に分散した粒状導電性充填剤 を含んでなる特許請求の範囲第１項または第２項
    に記載の方法。 ６ 第２組成物が、150000〜600000の分子量を有
    する溶融押出ポリエチレンを含んでなる特許請求
    の範囲第５項記載の方法。 ７ 基材は、第１組成物からなるパイプの形態で
    ある２つの基材であり、該物品を有してなるカツ
    プラーをパイプを一体に接合するために使用する
    特許請求の範囲第１〜６項のいずれかに記載の方
    法。 ８ 有機ポリマーを含んでなる熱軟化性組成物で
    ある外表面を少なくとも有する基材を改良する方
    法であつて、該方法が、 (1) 改良すべき基材の一部分、および熱回復性要
    素を有して成る物品を相互に隣接して配置し、
    熱回復性要素は、 (a) 第１組成物と相溶性であり、 (b) 有機ポリマー、および有機ポリマーに分散
    した粒状導電性充填剤を含んでなり、 (c) 23℃とTR＋50℃との間で、 （ただし、TRは回復温度である。） ５未満、好ましくは２未満の係数の抵抗率増
    加を示し、 (d) 融点よりも50℃高い温度において、５Kgの
    負荷で0.3ｇ／10分未満、および15Kgの負荷
    で3.0ｇ／10分未満のメルトフローインデツ
    クスを有し、 (e) 少なくとも2.54mm（0.1インチ）の厚さを
    有する 第２組成物からなり、 (2) 電流を流すことによつて要素内に熱を発生さ
    せ、要素を回復させ、改良すべき基材の一部分
    と接触させ、要素と該外表面との間の融合を生
    じさせる ことを含んでなる方法。 ９ 第２組成物は、 (a) 粒子が完全に識別性を失うことなく癒着する
    ように一体に焼結している有機ポリマー粒子か
    ら本質的になりマトリツクス、および (b) マトリツクスに分散しているが、癒着粒子の
    境界付近でまたは境界でのみ実質的に存在する
    粒状導電性充填剤 を含んでなる特許請求の範囲第８項記載の方法。 １０ (a) 粒子がその識別性を失うことなく癒着
    するように一体に焼結している有機ポリマー粒
    子から本質的になるマトリツクス、およびマト
    リツクス中に分散しているが癒着粒子の境界付
    近でまたは境界でのみ実質的に存在する粒状導
    電性充填剤を含んでなり、 (b) 23℃とTR＋50℃との間で、 （ただし、TRは回復温度である。） ５未満、好ましくは２未満の係数の抵抗率増
    加を示し、 (c) 融点よりも50℃高い温度において、５Kgの負
    荷で0.3ｇ／10分未満、および15Kgの負荷で3.0
    ｇ／10分未満のメルトフローインデツクスを有
    し、 (d) 少なくとも2.54mm（0.1インチ）の厚さを有
    する 導電性ポリマー組成物からなる熱回復性要素を有
    してなる熱回復性物品。 １１ 第２組成物が、23℃で１〜100Ω・cmの抵
    抗率を有し、粒状導電性充填剤を26重量％より少
    なく含む特許請求の範囲第１〜１０項のいずれか
    に記載の方法または物品。 １２ 熱回復性要素が、異なつた材料からなる２
    つまたはそれ以上の層を有してなり、１つの層は
    有機ポリマー、およびポリマーに分散している粒
    状導電性充填剤を含んでなり、他の層は非導電性
    層を有してなる第８〜１１項のいずれかに記載の
    方法。 １３ 第２組成物が、 (a) 23℃で１〜100Ω・cmの抵抗率を有し、 (b)(i) 粒子がその識別性を失うことなく癒着され
    ているように一体に焼結されている超高分子
    量ポリエチレンの粒子から本質的になるマト
    リツクス、および (ii) マトリツクスに分散されているが、ポリエ
    チレンの癒着粒子の境界付近でまたは境界で
    のみ実質的に存在する９体積％未満の粒状導
    電性充填剤 を含んでなる特許請求の範囲第８〜１２項のいず
    れかに記載の方法または物品。 １４ 有機ポリマーが400万より大きい分子量を
    有する超高分子量ポリエチレンを含んでなる特許
    請求の範囲第８〜１３項のいずれかに記載の方法
    または物品。 １５ (1)(a) 有機ポリマー、およびポリマーに分
    散した粒状導電性充填剤を含んでなり、 (b) 23℃とTR＋50℃との間で、 （ただし、TRは回復温度である。） ５未満、好ましくは２未満の係数の抵抗率
    増加を示し、 (c) 融点よりも50℃高い温度において、５Kgの
    負荷で0.3ｇ／10分未満、および15Kgの負荷
    で3.0ｇ／10分未満のメルトフローインデツ
    クスを有し、 (d) 少なくとも2.54mm（0.1インチ）の厚さを
    有する 導電性ポリマー組成物からなる熱回復性要素を
    有してなる物品を基材に隣接して配置し、 (2) 物品と基材との間にインサートを配置し、イ
    ンサートは、加熱された場合に変化を示し、し
    たがつて物品の基材への取り付けを促進し、 (3) 電流を流すことによつて熱回復性要素内で熱
    を生じさせ、物品を回復させて基材と間接的に
    接触させ、かつインサートを加熱し、物品を基
    材に付着させる ことを含んでなる基材を改良する方法。 １６ 導電性ポリマーが、粒子がその識別性を失
    うことなく癒着するように一体に焼結されている
    有機ポリマー粒子から本質的になるマトリツク
    ス、およびマトリツクス中に分散しているが癒着
    粒子の境界付近でまたは境界でのみ実質的に存在
    する粒状導電性充填剤を含んでなる特許請求の範
    囲第１５項記載の方法。 １７ その間に空〓が存在するように配置された
    少なくとも２つの基材を接合する方法であつて、
    有機ポリマーを含んでなる熱軟化性組成物からな
    る接触表面を有する基材と導電性ポリマー要素を
    直接に接触させ、(i)熱軟化性組成物を軟化させる
    のに充分な、および(ii)軟化した組成物を移動さ
    せ、基材の間の空〓を充填するのに充分な時間に
    わたつて、導電性ポリマー要素に電流を流す特許
    請求の範囲第１５項または第１６項に記載の方
    法。 １８ インサートが熱硬化性樹脂またはエポキシ
    樹脂を含んでなる特許請求の範囲第１５項または
    第１６項に記載の方法。 １９ 基材がガラス繊維補強プラスチツクパイプ
    を含んでなる特許請求の範囲第１８項記載の方
    法。 ２０ 異なつた組成物からなる２つまたはそれ以
    上のパイプを接合する特許請求の範囲第１〜１９
    項のいずれかに記載の方法または物品。
JP60070755A 1984-04-04 1985-04-02 熱回復性物品 Granted JPS60232932A (ja)