JPH04141025A - 農業用塩化ビニル系樹脂蛍光フィルム - Google Patents
農業用塩化ビニル系樹脂蛍光フィルムInfo
- Publication number
- JPH04141025A JPH04141025A JP2260884A JP26088490A JPH04141025A JP H04141025 A JPH04141025 A JP H04141025A JP 2260884 A JP2260884 A JP 2260884A JP 26088490 A JP26088490 A JP 26088490A JP H04141025 A JPH04141025 A JP H04141025A
- Authority
- JP
- Japan
- Prior art keywords
- fluorescent agent
- vinyl chloride
- wavelength region
- film
- average transmittance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は農業用塩化ビニル系樹脂蛍光フィルムに係り、
更に詳しくは、葉茎菜類の生育に良好な光環境を形成す
る農業用塩化ビニル系樹脂蛍光フィルムに関するもので
ある。
更に詳しくは、葉茎菜類の生育に良好な光環境を形成す
る農業用塩化ビニル系樹脂蛍光フィルムに関するもので
ある。
近年、植物の生育と光の波長との関係が研究され、青色
系及び赤色系の波長の光が植物の生育に有益であること
、また、紫外線が、植物の生育に害を与える場合のある
ことが知られている。
系及び赤色系の波長の光が植物の生育に有益であること
、また、紫外線が、植物の生育に害を与える場合のある
ことが知られている。
そこで、着色したフィルムや紫外線の透過を阻止するフ
ィルムを用いる方法があるが、前者の場合、曇天、低照
度時には光が不足気味にな゛るため、生育不良となり収
量が低下する傾向があり、また後者の場合、収量が増加
しても軟弱徒長気味となり、通常の無色透明フィルムを
使用した場合に比較して必ずしもを効ではない。
ィルムを用いる方法があるが、前者の場合、曇天、低照
度時には光が不足気味にな゛るため、生育不良となり収
量が低下する傾向があり、また後者の場合、収量が増加
しても軟弱徒長気味となり、通常の無色透明フィルムを
使用した場合に比較して必ずしもを効ではない。
本発明の目的は、葉茎菜の生育に良好な光環境を形成す
る農業用塩化ビニル系樹脂蛍光フィルムを供給するにあ
る。
る農業用塩化ビニル系樹脂蛍光フィルムを供給するにあ
る。
しかして、本発明の要旨とするところは、塩化ビニル系
樹脂に、紫外線で励起し 400〜500nmの波長域で発光する蛍光剤を配合し
フィルム化してなる ■ 320〜380nmの波長域の平均透過率が40%
以下であり、且つ ■ 透過光の400〜500nmの波長域のエネルギー
が、蛍光剤を配合しない場合に比して5%以上増加して
いる ことを特徴とする農業用塩化ビニル系樹脂蛍光フィルム
に存する。
樹脂に、紫外線で励起し 400〜500nmの波長域で発光する蛍光剤を配合し
フィルム化してなる ■ 320〜380nmの波長域の平均透過率が40%
以下であり、且つ ■ 透過光の400〜500nmの波長域のエネルギー
が、蛍光剤を配合しない場合に比して5%以上増加して
いる ことを特徴とする農業用塩化ビニル系樹脂蛍光フィルム
に存する。
以下に本発明の詳細な説明する。
本発明において塩化ビニル系樹脂とは、ポリ塩化ビニル
、塩化ビニルを主体とした他のコモノマーとの共重合体
、これらの混合物またはこれらと他の重合体あるいは共
重合体との混合物をいう。
、塩化ビニルを主体とした他のコモノマーとの共重合体
、これらの混合物またはこれらと他の重合体あるいは共
重合体との混合物をいう。
本発明の農業用塩化ビニル系樹脂蛍光フィルムは、柔軟
性を付与するために、塩化ビニル系樹脂100重量部に
対して、20〜60重量部の通常使用される可塑剤が配
合される。
性を付与するために、塩化ビニル系樹脂100重量部に
対して、20〜60重量部の通常使用される可塑剤が配
合される。
本発明において用いられる、紫外線で励起し400〜5
00 nmで発光する蛍光剤としては、ジアミノスチル
ベンジスルホン酸誘導体のようなスチルベン型蛍光剤;
ベンジジン系誘導体、ベンジジンスルホン酸誘導体、ジ
アミノフルオレン系誘導体のようなジアミノジフェニル
型蛍光剤;イミダゾール型蛍光剤;イミダシロン型蛍光
剤;トリアゾール型蛍光剤;チアゾール型蛍光剤;オキ
サゾール型蛍光剤;クマリン型蛍光剤;カルボスチリル
型蛍光剤;ナフタールイミド型蛍光剤;ピラプリン型蛍
光剤及びジヒドロピリジン型蛍光剤のように、現在市販
されている有機蛍光剤があげられる。
00 nmで発光する蛍光剤としては、ジアミノスチル
ベンジスルホン酸誘導体のようなスチルベン型蛍光剤;
ベンジジン系誘導体、ベンジジンスルホン酸誘導体、ジ
アミノフルオレン系誘導体のようなジアミノジフェニル
型蛍光剤;イミダゾール型蛍光剤;イミダシロン型蛍光
剤;トリアゾール型蛍光剤;チアゾール型蛍光剤;オキ
サゾール型蛍光剤;クマリン型蛍光剤;カルボスチリル
型蛍光剤;ナフタールイミド型蛍光剤;ピラプリン型蛍
光剤及びジヒドロピリジン型蛍光剤のように、現在市販
されている有機蛍光剤があげられる。
上記蛍光剤を塩化ビニル系樹脂に配合する割合は、透過
光の400〜500nmの波長域のエネルギーが、蛍光
剤を配合しない場合に比し、5%以上増加するように配
合する。実際の配合量は蛍光剤の種類、吸収/発光能等
によって適宜決定されるが、一般的には配合すべき塩化
ビニル系樹脂100重量部当り、0.01〜5重量部の
範囲で使用される。蛍光剤添加量が少なく400〜50
0nmの波長域の太陽光線透過エネルギーの増加が5%
未満であると本発明の目的は達せられない。
光の400〜500nmの波長域のエネルギーが、蛍光
剤を配合しない場合に比し、5%以上増加するように配
合する。実際の配合量は蛍光剤の種類、吸収/発光能等
によって適宜決定されるが、一般的には配合すべき塩化
ビニル系樹脂100重量部当り、0.01〜5重量部の
範囲で使用される。蛍光剤添加量が少なく400〜50
0nmの波長域の太陽光線透過エネルギーの増加が5%
未満であると本発明の目的は達せられない。
また、添加量が5重量部より多いときは、自己消光作用
を起こし、蛍光能を示さなくなるので好ましくない。
を起こし、蛍光能を示さなくなるので好ましくない。
また、本発明の農業用フィルムにおいて、320〜38
0nm平均透過率を40%以下とするために、紫外線で
励起する上記蛍光剤に加えて、紫外線吸収剤を配合して
もよい。
0nm平均透過率を40%以下とするために、紫外線で
励起する上記蛍光剤に加えて、紫外線吸収剤を配合して
もよい。
紫外線吸収剤としては、例えば、ベンゾトリアゾール系
、ベンゾエート系、ベンゾフェノン系、シアノアクリレ
ート系、フェニルサリシレート系が挙げられる。
、ベンゾエート系、ベンゾフェノン系、シアノアクリレ
ート系、フェニルサリシレート系が挙げられる。
紫外線吸収剤が多いと蛍光剤の励起に紫外線が充分に有
効活用できないため、紫外線吸収剤の配合量は、蛍光剤
の配合量以下とするのが好ましい。
効活用できないため、紫外線吸収剤の配合量は、蛍光剤
の配合量以下とするのが好ましい。
本発明においては、紫色系統の有機または無機顔料を配
合するのが好ましい、顔料としては、例えば、ジオキサ
ジン系の有機顔料やマンガン、コバルト等の無機顔料が
挙げられる。また、赤色系のアゾ系、キナクリドン等の
有機顔料と、青色系のフタロシアニン系、紺青、群青等
の有機、無機顔料を組み合せ、紫色系統に着色してもよ
い。
合するのが好ましい、顔料としては、例えば、ジオキサ
ジン系の有機顔料やマンガン、コバルト等の無機顔料が
挙げられる。また、赤色系のアゾ系、キナクリドン等の
有機顔料と、青色系のフタロシアニン系、紺青、群青等
の有機、無機顔料を組み合せ、紫色系統に着色してもよ
い。
これら紫色系統顔料の配合量は、530〜570nmの
波長域の平均透過率が80〜88%になるように適宜決
定されるが、一般的に塩化ビニル系樹脂100重量部に
対し、0.01〜5重量部である。
波長域の平均透過率が80〜88%になるように適宜決
定されるが、一般的に塩化ビニル系樹脂100重量部に
対し、0.01〜5重量部である。
紫色系統顔料の配合量が少なく、530〜570nm平
均透過率が88%を趙える場合は、平均透過率が80〜
88%の場合に比べ、葉茎菜の生育が相対的に劣り、ま
た、530〜5700m平均透過率が80%未満の場合
は、透過光量が不足気味になる傾向がある。
均透過率が88%を趙える場合は、平均透過率が80〜
88%の場合に比べ、葉茎菜の生育が相対的に劣り、ま
た、530〜5700m平均透過率が80%未満の場合
は、透過光量が不足気味になる傾向がある。
本発明の農業用塩化ビニル系樹脂蛍光フィルムには、上
記の配合物のほかに必要に応して、成形用の合成樹脂に
通常配合される公知の樹脂添加物を配合することができ
る。
記の配合物のほかに必要に応して、成形用の合成樹脂に
通常配合される公知の樹脂添加物を配合することができ
る。
これら樹脂添加物は、通常の配合量、例えば塩化ビニル
系樹脂100重量部に対し、10重量部以下で使用する
ことができる。
系樹脂100重量部に対し、10重量部以下で使用する
ことができる。
塩化ビニル系樹脂に上記の配合物を配合するには通常の
配合または混合技術を採用すればよい。
配合または混合技術を採用すればよい。
具体的には、例えばリボンブレンダー、バンバリーミキ
サ−、スーパーミキサーまたはその他の配合機もしくは
混合機を使用する方法を採用することができる。
サ−、スーパーミキサーまたはその他の配合機もしくは
混合機を使用する方法を採用することができる。
このようにして得られた軟質塩化ビニル系樹脂の組成物
からフィルムを製造するには、通常行われているフィル
ム製造法、例えばカレンダー成形法、押出成形法、イン
フレーション成形法などを適宜採用することができる。
からフィルムを製造するには、通常行われているフィル
ム製造法、例えばカレンダー成形法、押出成形法、イン
フレーション成形法などを適宜採用することができる。
本発明に係るフィルムの厚さは、強度、取り扱い作業等
を考慮し、0.03〜0.5 m好ましくは0.05〜
0.3閣の範囲にするのが良い。
を考慮し、0.03〜0.5 m好ましくは0.05〜
0.3閣の範囲にするのが良い。
次に、本発明を実施例に基づいて詳細に説明するが、本
発明はその要旨を超えない限り、以下の例に限定される
ものではない。
発明はその要旨を超えない限り、以下の例に限定される
ものではない。
実施例1〜2、比較例1〜6
ポリ塩化ビニル(P =1300) 100重量部ジオ
クチルフタレート 42 〃トリキシレニルホス
フェート 5 エポキシ樹脂 4 (商品名 エピコート828、ンエ4化学製)カルシウ
ム−亜鉛系液状安定剤 3 〃カルシウムー亜鉛系粉末
安定剤 2 ソルビタンモノパルミテート 1.5〃を基本組成と
し、これに表1に示す添加剤をそれぞれ配合した。
クチルフタレート 42 〃トリキシレニルホス
フェート 5 エポキシ樹脂 4 (商品名 エピコート828、ンエ4化学製)カルシウ
ム−亜鉛系液状安定剤 3 〃カルシウムー亜鉛系粉末
安定剤 2 ソルビタンモノパルミテート 1.5〃を基本組成と
し、これに表1に示す添加剤をそれぞれ配合した。
上記混合物を、180°Cに加温されたカレンダーロー
ルに供給し、混練したのち、常法により厚さ0.1■の
フィルム8種を作成した。
ルに供給し、混練したのち、常法により厚さ0.1■の
フィルム8種を作成した。
[ホウレン草の栽培試験」
表1に示す8種のフィルムをハウス16棟に各々2棟ず
つ展張してホウレン草(リード)の比較栽培を行い、表
2に示す結果を得た。
つ展張してホウレン草(リード)の比較栽培を行い、表
2に示す結果を得た。
[発明の効果]
本発明は葉茎菜類殊にホウレン草の生育に適し、葉厚が
厚く且つ葉緑素の多い良品が得られ、収量増にもなる。
厚く且つ葉緑素の多い良品が得られ、収量増にもなる。
出願人 三菱化成ビニル株式会社
Claims (2)
- (1)塩化ビニル系樹脂に、紫外線で励起し400〜5
00nmの波長域で発光する蛍光剤を配合しフィルム化
してなる [1]320〜380nmの波長域の平均透過率が40
%以下であり、且つ [2]透過光の400〜500nmの波長域のエネルギ
ーが、蛍光剤を配合しない場合に比し5%以上増加して
いる ことを特徴とする農業用塩化ビニル系樹脂蛍光フィルム
。 - (2)紫色系統の顔料を配合することにより、530〜
570nmの波長域の平均透過率を80〜88%とした
、特許請求の範囲第(1)項のフィルム。