JPH04113908U - 繊維板 - Google Patents
繊維板Info
- Publication number
- JPH04113908U JPH04113908U JP2540591U JP2540591U JPH04113908U JP H04113908 U JPH04113908 U JP H04113908U JP 2540591 U JP2540591 U JP 2540591U JP 2540591 U JP2540591 U JP 2540591U JP H04113908 U JPH04113908 U JP H04113908U
- Authority
- JP
- Japan
- Prior art keywords
- phytoncide
- wood
- fiberboard
- adhesive
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【目的】 防虫、防菌、芳香作用を兼ね備えた繊維板を
提供すること。 【構成】 フィトンチッドが塗布含浸された木質繊維を
接着剤を介して圧締成形一体化する。
提供すること。 【構成】 フィトンチッドが塗布含浸された木質繊維を
接着剤を介して圧締成形一体化する。
Description
【0001】
本考案は、防虫、防菌、芳香作用を兼ね備えた繊維板に関する。
【0002】
近年、建築工法や建築材料等の進歩によって、また防音、防火、省力エネルギ
ーの要求に伴って、家屋や各室の気密性が著しく向上されてきている。ところが
、気密性が向上されると、その反面、家屋や各室において空気が滞留し、湿度が
上昇するために、生活臭が抜けず、また結露が発生しやすくなる等の問題が生ず
る。これらの問題は、特に、台所、洗面所、風呂場、押入れ等の収納部、居室等
において顕著であり、生活臭による不快感を伴い、また結露・湿気によるカビ、
ダニ、細菌、ゴキブリ等の発生や繁殖に適した環境が作られることとなるために
これらの温床となり、人体に対しても有害であり、環境衛生及び健康に悪影響を
及ぼす原因となっていた。
【0003】
このような現状に鑑み、防虫・防腐薬剤で処理した建築材料が一部において提
供されているが、処理薬剤による人体への影響を考慮すると、必ずしも満足すべ
き解決手段とはなり得ないものであった。
【0004】
かかる問題を解決するために鋭意工夫の末に創案された本考案は、木材を解繊
して得られる木質繊維にフィトンチッドを塗布含浸して得られる処理繊維を、
接着剤を介して圧締接着して成ることを特徴とする繊維板である。
【0005】
本考案の繊維板を製造するための処理工程順序が図1に示されている。
【0006】
木質繊維は、例えばスギ、ヒノキ、ヒバ、マツ、シラカバ、マキ、ネズコ、ク
スノキ、クヌギ、イチョウ、ツバキ、ラワン、カポール、クリ、ポプラ、ヤナギ
等の針葉樹材、広葉樹材の一種又は複数種が適宜混合されたものを木材チップと
し、これを高温高圧蒸気で蒸煮して脱脂軟化処理した後、解繊装置によって解繊
して得られ、風送乾燥により所定含水率に調整される。木質繊維に代えて、サト
ウキビ、トウモロコシの茎、ヤシ殻等を解繊して得られるバヤスを代用すること
もできる。
【0007】
このようにして得られた木質繊維をダクトを介して風送乾燥しつつ混合装置に
搬送し、該混合装置内において、該木質繊維にフィトンチッドが塗布含浸される
。フィトンチッドとは、天然木(幹、枝、葉、根株、木皮、樹脂等)を蒸留、圧
搾、溶媒抽出等によって精製して得られる精油であって、具体的には、α−ピネ
ン、β−ピネン、ジペンテル、リモネン、テルピノレン等のモノテルペン、カジ
ネン、ロンギホレン等のセスキテルペン、カンホレン、ミレン等のジテルペン等
のテルペン=(C5H8)n=を主成分とするものであって、一般にテレピン油と
呼称されている。フィトンチッドの樹種は、スギ、ヒノキ、ヒバ、マツ、シラカ
バ、マキ、ネズコ、クスノキ、クヌギ、イチョウ、ツバキ等任意のものであって
良い。
【0008】
フィトンチッドは、精油状態(溶剤希釈する場合もある)のまま、又はエマル
ジョンタイプとして、或は精油を内部に封入したマイクロカプセルタイプのもの
を用いてこれを水、合成樹脂等に分散した状態で、木質繊維に塗布含浸される。
精油状態で使用されるフィトンチッドは大気中への放散が比較的早いため速効性
であって短期効果が大きく、またエマルジョンタイプやマイクロカプセルタイプ
として使用される場合は遅効性・持続性であって長期効果が期待できる。更に、
エマルジョンタイプやマイクロカプセルタイプの場合には、エマルジョン外皮又
はマイクロカプセル外殻を構成する物質や外皮・外殻の厚さを変えることにより
、フィトンチッドの放散量を適宜コントロールすることができる。
【0009】
フィトンチッドは、樹種によって多少異なるものの、殺菌、殺ダニ、殺虫、殺
綜虫、抗微生物、抗菌、薬理、脱臭、芳香、鎮静等の多くの作用を持つ。例えば
スギのフィトンチッドは特に殺菌、殺ダニ、脱臭作用に優れ、ヒバのフィトンチ
ッドは特に抗微生物、殺菌作用に優れ、ヒノキのフィトンチッドは特に抗菌、脱
臭作用に優れ、トガサワラ及びトドマツのフィトンチッドは特に殺虫、殺菌、殺
綜虫作用に優れ、シラカバのフィトンチッドは特に抗菌、殺虫作用に優れ、てい
る。またフィトンチッドは人体に対する森林浴効果を発揮し、環境衛生及び健康
上の効果も優れている。
【0010】
本考案において木質繊維に塗布含浸されるフィトンチッドは、該木質繊維と同
じ樹種材より得られるものであっても、又該木質繊維と異なる樹種材より得られ
る1種又は複数種のフィトンチッドであっても良く、更には該木質繊維と同じ樹
種材より得られるものと異なる樹種材より得られるものとを混合して用いても良
い。
【0011】
かくしてフィトンチッドを添加含浸して得られた処理繊維を必要に応じて乾燥
した後、混合装置にて接着剤を添加混合する。接着剤はまた、木材チップの解繊
時に解繊装置において添加しても良く、或は解繊後の風送中にダクト内に添加し
ても良い。
【0012】
接着剤としては尿素樹脂、フェノール樹脂、メラミン樹脂、エポキシ樹脂、酢
酸ビニル樹脂、エチレン−酢酸ビニル樹脂、或はそれらの変性樹脂接着剤、イソ
シアネート系接着剤、合成ゴム系接着剤等の熱硬化性又は熱可塑性の接着剤から
任意選択される一種又は複数種が用いられる。
【0013】
接着剤の塗布された処理繊維は風送乾燥ダクト中を風送搬送され、木質繊維マ
ットとされた後、定寸に裁断され、更にホットプレス、コールドプレス等の圧締
装置により圧締成形一体化されて、本考案の繊維板が得られる。
【0014】
【実施例】
本考案の繊維板を製造するための具体的方法の数例を以下に挙げる。
【0015】
トガサワラの木材チップを蒸煮装置を用いて高温高圧蒸気下で蒸煮して脱脂軟
化処理した後、解繊装置によって解繊して、トガサワラ木質繊維を得る。この木
質繊維を風送乾燥して含水率を調整しつつ混合装置に投入する。混合装置では、
該木質繊維樹木と同樹種材であるトガサワラより得られる精油をエマルジョンタ
イプとしたフィトンチッドを添加混合し、該木質繊維に塗布含浸する。かくして
得られた処理繊維を乾燥し或は乾燥することなく、混合装置にて接着剤を添加混
合し塗布する。接着剤の塗布された処理繊維を風送搬送して木質繊維マットを形
成し、定寸裁断し、圧締装置にて成形一体化して繊維板とする。
【0016】
ラワンの木材チップを上記と同様に処理してラワン木質繊維を得た後、混合装
置に投入して、該木質繊維樹木と異なる樹種材であるヒバより得られる精油を封
入して成るマイクロカプセルを添加混合する。この処理繊維に接着剤を塗布添加
した後、風送搬送して木質繊維マットを形成し、定寸裁断し、圧締装置にて成形
一体化して繊維板とする。
【0017】
上記と同様にして得られたラワン木質繊維を混合装置に投入して、該木質繊維
樹木と異なる樹種材であるヒバより得られる精油をエマルジョンタイプとしてフ
ィトンチッドと、スギより得られる精油をエマルジョンタイプとしたフィトンチ
ッドとの二種混合フィトンチッドを添加混合する。この処理繊維に接着剤を塗布
した後、風送搬送して木質繊維マットを形成し、定寸裁断し、圧締装置にて成形
一体化して繊維板とする。
【0018】
多くの優れた作用を有するフィトンチッドが塗布含浸された木質繊維が接着剤
を介して接着圧締成形一体化されて繊維板とされているので、木質繊維に塗布含
浸されたフィトンチッドが徐々に大気中に放散され、その作用が長期間に亙って
発揮される。木質繊維と同樹種材のフィトンチッドが塗布含浸される場合は、該
フィトンチッドの放散がより長期間に亙って行われる。木質繊維と異なる樹種材
のフィトンチッドが塗布含浸される場合は、その芳香効果によって異なる木質感
を表すことができる。例えば、広葉樹材の木質繊維を用いながら針葉樹材に或は
その逆に模したり、低級材を高級材に表したりすることができる。複数種のフィ
トンチッドを混合して木質繊維に塗布含浸することにより、各々のフィトンチッ
ドの有する作用を任意に組み合わせることができる。
【図1】 本考案による繊維板の製造工程を概略的に示
す図である。
す図である。
Claims (1)
- 【請求項1】 木材を解繊して得られる木質繊維にフ
ィトンチッドを塗布含浸して得られる処理繊維を、接着
剤を介して圧締接着して成ることを特徴とする繊維板。