JPH03190797A - 熱転写記録用受像シート - Google Patents
熱転写記録用受像シートInfo
- Publication number
- JPH03190797A JPH03190797A JP1334097A JP33409789A JPH03190797A JP H03190797 A JPH03190797 A JP H03190797A JP 1334097 A JP1334097 A JP 1334097A JP 33409789 A JP33409789 A JP 33409789A JP H03190797 A JPH03190797 A JP H03190797A
- Authority
- JP
- Japan
- Prior art keywords
- image
- image receiving
- thermal transfer
- recording
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
「産業上の利用分野」
本発明は、熱転写記録用受像シートに関し、特に熱昇華
性染料を利用した熱転写記録用受像シートの改良に関す
るもので、色濃度が高く転写抜けのない、美しい画像を
得ることが出来る熱転写記録用受像シートを提供するも
のである。
性染料を利用した熱転写記録用受像シートの改良に関す
るもので、色濃度が高く転写抜けのない、美しい画像を
得ることが出来る熱転写記録用受像シートを提供するも
のである。
「従来の技術」
入力信号と同時に記録像の得られる熱記録方式゛は、装
置が比較的簡単で安価なうえに低騒音であるため、ファ
クシミリ、計算機用端末プリンタ、測定機用プリンタ等
多方面に利用されている。
置が比較的簡単で安価なうえに低騒音であるため、ファ
クシミリ、計算機用端末プリンタ、測定機用プリンタ等
多方面に利用されている。
これらの熱記録方式に使用される記録媒体としては、加
熱により物理的、化学的変化を起こして発色する記録層
を設けた所謂、発色タイプ感熱記録紙が最も一般的に使
用されてきた。しかし、発色タイプ感熱記録紙は記録さ
れた像の保存安定性が劣っており、有機溶剤や化学薬品
等との接触によって褪色現象を起こしてしまう。
熱により物理的、化学的変化を起こして発色する記録層
を設けた所謂、発色タイプ感熱記録紙が最も一般的に使
用されてきた。しかし、発色タイプ感熱記録紙は記録さ
れた像の保存安定性が劣っており、有機溶剤や化学薬品
等との接触によって褪色現象を起こしてしまう。
そのため、発色タイプ感熱記録紙に代わる記録媒体とし
て、有色の色材そのものを利用した記録媒体を用いる記
録方法が提案されており、例えば特開昭51−1544
6号公報には、常温では固体又は半固体状である色材を
紙、ポリマーフィルム等の支持体上に塗布しておき、熱
記録ヘッドにより支持体上の色材を加熱して、選択的に
記録紙に色材を転移させて記録像を得る方法が提案され
ている。
て、有色の色材そのものを利用した記録媒体を用いる記
録方法が提案されており、例えば特開昭51−1544
6号公報には、常温では固体又は半固体状である色材を
紙、ポリマーフィルム等の支持体上に塗布しておき、熱
記録ヘッドにより支持体上の色材を加熱して、選択的に
記録紙に色材を転移させて記録像を得る方法が提案され
ている。
この記録方式では支持体上の色材を熱によって、溶融、
蒸発、昇華せしめ、記録紙に転移させて粘着、吸着、染
着によって記録像を得るものであり、記録紙として普通
紙が利用できる特徴があるとされている。そして、特に
色材として昇華性染料を用いる記録方式ではI調性に優
れた画像が得られるため、フルカラー記録用途への応用
が試みられている。
蒸発、昇華せしめ、記録紙に転移させて粘着、吸着、染
着によって記録像を得るものであり、記録紙として普通
紙が利用できる特徴があるとされている。そして、特に
色材として昇華性染料を用いる記録方式ではI調性に優
れた画像が得られるため、フルカラー記録用途への応用
が試みられている。
しかし、記録紙として普通紙を用いた場合には、特に染
着が起り難く、記録像の色濃度が低いばかりでなく、経
時によって著しい褪色現象を起こしてしまう。そのため
、特開昭57−107885号公報、特開昭59−16
5688号公報、米国特許第3601484号公報等に
記載の如く熱可塑性樹脂を主成分とする受像層を形成し
た受像シートが使用されている。
着が起り難く、記録像の色濃度が低いばかりでなく、経
時によって著しい褪色現象を起こしてしまう。そのため
、特開昭57−107885号公報、特開昭59−16
5688号公報、米国特許第3601484号公報等に
記載の如く熱可塑性樹脂を主成分とする受像層を形成し
た受像シートが使用されている。
また、特に階調性に富んだ画像の記録のためには特開昭
59−133092号公報、特開昭59187892号
公報に記載の如く、受像層表面の平滑性を高めて転写効
率を上げる、さらには、特開昭61−144394号公
報の記載の如く、クツション層を設けるといった提案も
なされている。
59−133092号公報、特開昭59187892号
公報に記載の如く、受像層表面の平滑性を高めて転写効
率を上げる、さらには、特開昭61−144394号公
報の記載の如く、クツション層を設けるといった提案も
なされている。
「発明が解決しようとする課題」
一般に昇華型の転写方式は、溶融型に比べ、階調性に富
んだ優れた画像が得られるが、色濃度の高い転写像を得
るには多くの熱エネルギーが必要であると言われ、従来
通り汎用のエネルギーを用いながら、転写効率を上げる
ことがこの方式の課題の1つとされてきた。上記の難点
を解決するべく、本発明者等は鋭意研究を重ねた結果、
受像層中に特定の物質を配合すると、染着性が高まり、
極めて優れた転写像を得ることのできる受像層を見出し
たものである。
んだ優れた画像が得られるが、色濃度の高い転写像を得
るには多くの熱エネルギーが必要であると言われ、従来
通り汎用のエネルギーを用いながら、転写効率を上げる
ことがこの方式の課題の1つとされてきた。上記の難点
を解決するべく、本発明者等は鋭意研究を重ねた結果、
受像層中に特定の物質を配合すると、染着性が高まり、
極めて優れた転写像を得ることのできる受像層を見出し
たものである。
「課題を解決するための手段」
本発明は、支持体上に、色材転写シートからの転写像を
受理する受像層を設けてなる熱転写記録用受像シートに
おいて、該受像層がエタノールアミンを含むことを特徴
とする熱転写記録用受像シートである。
受理する受像層を設けてなる熱転写記録用受像シートに
おいて、該受像層がエタノールアミンを含むことを特徴
とする熱転写記録用受像シートである。
「作用」
熱転写記録用受像シートとして、紙等の基材にクツショ
ン性、断熱性に富む、平滑なバリヤー層を予め設け、こ
の上に受像層を形成させることにより熱転写シートとの
密着性の向上、熱ヘツドから与えられる熱信号の高効率
化を図ることにより、転写波は及び発色濃度を改良しよ
うという試みがなされてきた。
ン性、断熱性に富む、平滑なバリヤー層を予め設け、こ
の上に受像層を形成させることにより熱転写シートとの
密着性の向上、熱ヘツドから与えられる熱信号の高効率
化を図ることにより、転写波は及び発色濃度を改良しよ
うという試みがなされてきた。
この場合、バリヤー層として、ポリウレタン、ポリブタ
ジェン、SBR,MBR等の合成樹脂エマルジョンを塗
抹することが提案されているが、このような合成樹脂層
を紙を基材とする表面に塗抹することは実際上かなり困
難である。これらの水性合成樹脂エマルジョンは紙に塗
抹された直後の数秒間に原紙の1〜1100aと大きい
繊維間の空孔に急速に浸透してしまい平滑性が得られな
い。
ジェン、SBR,MBR等の合成樹脂エマルジョンを塗
抹することが提案されているが、このような合成樹脂層
を紙を基材とする表面に塗抹することは実際上かなり困
難である。これらの水性合成樹脂エマルジョンは紙に塗
抹された直後の数秒間に原紙の1〜1100aと大きい
繊維間の空孔に急速に浸透してしまい平滑性が得られな
い。
また、塗被紙を基材とした場合には、合成樹脂エマルジ
ョンは塗抹後の乾燥工程の初期にまず塗抹樹脂層の表面
が成膜し、次いで内部の水が蒸発するという段階を経て
乾燥が終了する。その際、前述の合成樹脂は体質顔料で
ない為、乾燥時の体積変化が大きく、水分の蒸発によっ
て塗被直後の表面の平滑性が失われてしまう。
ョンは塗抹後の乾燥工程の初期にまず塗抹樹脂層の表面
が成膜し、次いで内部の水が蒸発するという段階を経て
乾燥が終了する。その際、前述の合成樹脂は体質顔料で
ない為、乾燥時の体積変化が大きく、水分の蒸発によっ
て塗被直後の表面の平滑性が失われてしまう。
なお、体質顔料として、炭酸カルシウム、カオリン、酸
化チタン、水酸化アルミニウム、硫酸バリウム等で代表
さるれ無機系顔料を添加し、平滑性を向上させることも
可能である。
化チタン、水酸化アルミニウム、硫酸バリウム等で代表
さるれ無機系顔料を添加し、平滑性を向上させることも
可能である。
しかし、このような無機系顔料によるバリヤー層を設け
たとき、一般に無機系顔料は合成樹脂に比べ熱伝導率が
高い為、熱ヘツドから加えられた熱がバリヤー層中の無
機系顔料を通過して逃げてしまい易く、結果として熱効
率の悪い熱転写記録用受像シートしか得られず、その発
色濃度は非常に低いものとなる。
たとき、一般に無機系顔料は合成樹脂に比べ熱伝導率が
高い為、熱ヘツドから加えられた熱がバリヤー層中の無
機系顔料を通過して逃げてしまい易く、結果として熱効
率の悪い熱転写記録用受像シートしか得られず、その発
色濃度は非常に低いものとなる。
また、合成樹脂で、体質顔料となりうる公知のものとし
ては、ポリオレフィン、ポリスチレン、ポリテトラフロ
ロエチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポ
リベンゾグアナミン、シリコーン樹脂等の重合体、共重
合体が存在する。これらの樹脂をバリヤー層に添加した
場合は無機系顔料を添加した場合に比べ、ある程度高い
発色濃度が得られるが、満足のいく状態ではなく、なお
、改善の余地を残している。
ては、ポリオレフィン、ポリスチレン、ポリテトラフロ
ロエチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポ
リベンゾグアナミン、シリコーン樹脂等の重合体、共重
合体が存在する。これらの樹脂をバリヤー層に添加した
場合は無機系顔料を添加した場合に比べ、ある程度高い
発色濃度が得られるが、満足のいく状態ではなく、なお
、改善の余地を残している。
本発明者等は、上記のことから、鋭意研究を重ねた結果
、エタノールアミンを公知の合成樹脂を主成分とする受
像層用塗液に添加し、受像層用塗液を調製し、この塗液
を公知の塗工用コーター等を用いて支持体上に塗抹、乾
燥して熱転写記録用受像シートを得た。この受像シート
を用いて印字試験を行った結果、優れた画質と高い発色
濃度の熱転写記録用受像シートが得られることを見出し
、本発明を完成するに至った。
、エタノールアミンを公知の合成樹脂を主成分とする受
像層用塗液に添加し、受像層用塗液を調製し、この塗液
を公知の塗工用コーター等を用いて支持体上に塗抹、乾
燥して熱転写記録用受像シートを得た。この受像シート
を用いて印字試験を行った結果、優れた画質と高い発色
濃度の熱転写記録用受像シートが得られることを見出し
、本発明を完成するに至った。
なお、受像層中に含まれるエタノールアミンの配合量は
、受像層固形分の3乃至20重量%の範囲で調製される
。因みに3重量%未満の場合には発色濃度向上の効果が
少なく、他方、20重量%を超えると紫外線照射時の退
色が大きく、さらに印画時に熱転写シートと熱転写記録
用受像シートの受像層が熱融着し易くなる傾向があり好
ましくない。
、受像層固形分の3乃至20重量%の範囲で調製される
。因みに3重量%未満の場合には発色濃度向上の効果が
少なく、他方、20重量%を超えると紫外線照射時の退
色が大きく、さらに印画時に熱転写シートと熱転写記録
用受像シートの受像層が熱融着し易くなる傾向があり好
ましくない。
受像層がエタノールアミンを含むことにより、高い発色
濃度をもつ熱転写記録用受像シートが得られる理由は必
ずしも明らかではないが、以下のように推定される。即
ち、 転写シートから受像シートに転移した染料がエタノール
アミンに分散し易い為、或いは、エタノールアミンが、
受像層樹脂中の染料を分散し易いようにする為に発色濃
度が高められるのではないかと思われる。
濃度をもつ熱転写記録用受像シートが得られる理由は必
ずしも明らかではないが、以下のように推定される。即
ち、 転写シートから受像シートに転移した染料がエタノール
アミンに分散し易い為、或いは、エタノールアミンが、
受像層樹脂中の染料を分散し易いようにする為に発色濃
度が高められるのではないかと思われる。
次に、本発明の熱転写記録用受像シートの基本構成を第
1図に基づいて述べる。即ち、基材(1)の上に、バリ
ヤー層(2)、受像層(3)が順次設けられており、基
材の裏面には必要に応じてカール防止層(4)を設けて
もよい。
1図に基づいて述べる。即ち、基材(1)の上に、バリ
ヤー層(2)、受像層(3)が順次設けられており、基
材の裏面には必要に応じてカール防止層(4)を設けて
もよい。
基材としては、アート紙、コート紙、軽量コート紙、微
塗工紙、キャストコート祇等の光沢タイプ、ダルタイプ
、マットタイプ等の塗工紙及び上質紙、中質紙、スーパ
ーキャレンダー処理紙等の非塗工紙が使用される。勿論
、熱転写記録用受像シートの用途、目的に応じて透明、
半透明、不透明のフィルムも使用される。
塗工紙、キャストコート祇等の光沢タイプ、ダルタイプ
、マットタイプ等の塗工紙及び上質紙、中質紙、スーパ
ーキャレンダー処理紙等の非塗工紙が使用される。勿論
、熱転写記録用受像シートの用途、目的に応じて透明、
半透明、不透明のフィルムも使用される。
バリヤー層としては、無機系顔料、水溶性合成樹脂の水
溶液又は合成樹脂の水性エマルジョン、水性サスペンシ
ョンの何れか、或いは、併用したものを含む塗液を、公
知のブレードコーター、エアナイフコーター、バーコー
ター、ロッドブレードコーター、ロールコータ−、グラ
ビアコーターカーテンコーター等を使用し、乾燥重量と
して3g/m2以上、望ましくは8〜30g/m”塗抹
することにより得ることができる。バリヤー層の目的は
、■ 基材の表面を平滑化し、又はクツション性を付与
し、転写シートとの密着性を高めることにより画質を向
上させる、 ■ バリヤー層の上に設けられる受像層が基材中に浸透
するのを抑えることにより画質を向上させる、 ■ 感熱ヘッドから加えられた熱が基材に逃げるのを抑
え、受像シートの熱効率を高める、等があるが、基材の
性質、又は受像シートに要求される品質によっては、全
く設けない場合もあり得るし、1層、或いは2〜3層の
構成をとることもあり得る。
溶液又は合成樹脂の水性エマルジョン、水性サスペンシ
ョンの何れか、或いは、併用したものを含む塗液を、公
知のブレードコーター、エアナイフコーター、バーコー
ター、ロッドブレードコーター、ロールコータ−、グラ
ビアコーターカーテンコーター等を使用し、乾燥重量と
して3g/m2以上、望ましくは8〜30g/m”塗抹
することにより得ることができる。バリヤー層の目的は
、■ 基材の表面を平滑化し、又はクツション性を付与
し、転写シートとの密着性を高めることにより画質を向
上させる、 ■ バリヤー層の上に設けられる受像層が基材中に浸透
するのを抑えることにより画質を向上させる、 ■ 感熱ヘッドから加えられた熱が基材に逃げるのを抑
え、受像シートの熱効率を高める、等があるが、基材の
性質、又は受像シートに要求される品質によっては、全
く設けない場合もあり得るし、1層、或いは2〜3層の
構成をとることもあり得る。
バリヤー層を構成する無機系顔料としては、炭酸カルシ
ウム、カオリン、酸化チタン、水酸化アルミニウム、硫
酸バリウム等が使用できる。また水溶性合成樹脂として
は、ポリアクリルアミド、カルボキシル基や水酸基を含
む各種の樹脂、例えばカルボキシル基含有ポリエチレン
、ポリ酢酸ビニル、ポリビニルアルコール、セルロース
樹脂等が使用でる。さらに、水性エマルジョン、水性サ
スペンションを構成する合成樹脂としては、ポリアクリ
ル酸エステル、ポリメタクリル酸エステル、ポリオレフ
ィン、ポリブタジェン、ポリスチレン、ポリ酢酸ビニル
、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリウレタン
、ポリエステル等のアルカリ可溶型、アルカリ膨潤型、
アルカリ非膨潤型、変成型の重合体及び共重合体等が使
用できる。
ウム、カオリン、酸化チタン、水酸化アルミニウム、硫
酸バリウム等が使用できる。また水溶性合成樹脂として
は、ポリアクリルアミド、カルボキシル基や水酸基を含
む各種の樹脂、例えばカルボキシル基含有ポリエチレン
、ポリ酢酸ビニル、ポリビニルアルコール、セルロース
樹脂等が使用でる。さらに、水性エマルジョン、水性サ
スペンションを構成する合成樹脂としては、ポリアクリ
ル酸エステル、ポリメタクリル酸エステル、ポリオレフ
ィン、ポリブタジェン、ポリスチレン、ポリ酢酸ビニル
、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリウレタン
、ポリエステル等のアルカリ可溶型、アルカリ膨潤型、
アルカリ非膨潤型、変成型の重合体及び共重合体等が使
用できる。
また、必要に応じ、澱粉、変成澱粉、蛋白質系接着剤等
の結着剤、酸化防止剤、染料、消泡剤、界面活性剤、そ
の他の助剤を添加しても良い。
の結着剤、酸化防止剤、染料、消泡剤、界面活性剤、そ
の他の助剤を添加しても良い。
次に、受像層は熱転写シートから移行してくる染料を受
容する働きをするものであり、具体的には次のような合
成樹脂を用いて構成される。
容する働きをするものであり、具体的には次のような合
成樹脂を用いて構成される。
■ エステル結合を有するもの
ポリエステル樹脂、ポリアクリル酸エステル樹脂、ポリ
カーボネート樹脂、ポリ酢酸ビニル樹脂、スチレンアク
リレート樹脂、ヒニルトルエンアクリレート樹脂等、 ■ ウレタン結合を有するもの ポリウレタン樹脂等、 ■ アミド結合を有するもの ポリアミド樹脂等、 ■ 尿素結合を有するもの 尿素樹脂等、 が用いられる。
カーボネート樹脂、ポリ酢酸ビニル樹脂、スチレンアク
リレート樹脂、ヒニルトルエンアクリレート樹脂等、 ■ ウレタン結合を有するもの ポリウレタン樹脂等、 ■ アミド結合を有するもの ポリアミド樹脂等、 ■ 尿素結合を有するもの 尿素樹脂等、 が用いられる。
なお、本発明における受像層は、これらの樹脂の内の何
れか一種、或いは、併用したものを含む樹脂液中に前述
したエタノールアミンを含有せしめた塗液を、公知のブ
レードコーター、エアナイフコーター、バーコーター、
ロットフレードコーター、ロールコータ−、グラビアコ
ーター、カーテンコーター等を使用し、乾燥重量として
Ig/m”以上、望ましくは2〜10g/m2塗抹する
ことにより得ることができる。なお、その他愛像層用塗
液中には必要に応じて消泡剤、滑剤、帯電防止剤、離型
剤、紫外線吸収剤、染料等を受像層のもつ作用効果を損
なわない範囲で適宜添加することもできる。
れか一種、或いは、併用したものを含む樹脂液中に前述
したエタノールアミンを含有せしめた塗液を、公知のブ
レードコーター、エアナイフコーター、バーコーター、
ロットフレードコーター、ロールコータ−、グラビアコ
ーター、カーテンコーター等を使用し、乾燥重量として
Ig/m”以上、望ましくは2〜10g/m2塗抹する
ことにより得ることができる。なお、その他愛像層用塗
液中には必要に応じて消泡剤、滑剤、帯電防止剤、離型
剤、紫外線吸収剤、染料等を受像層のもつ作用効果を損
なわない範囲で適宜添加することもできる。
さらに環境変化、即ち温度や湿度変化によるカールを防
止、或いは軽減する目的、所謂熱転写記録用受像シート
のプリンターに対する走行性を良好にするためにカール
防止層を受像シートの裏面に設けてもよい。また、カー
ル防止層には、プリンタの特性により、帯電防止、プリ
ンタのフィードロールとのスリップコントロール、印字
後のカールコントロールといった性質を持たせることも
できる。
止、或いは軽減する目的、所謂熱転写記録用受像シート
のプリンターに対する走行性を良好にするためにカール
防止層を受像シートの裏面に設けてもよい。また、カー
ル防止層には、プリンタの特性により、帯電防止、プリ
ンタのフィードロールとのスリップコントロール、印字
後のカールコントロールといった性質を持たせることも
できる。
「実施例」
以下に、本発明をより具体的に説明するために実施例を
記載するが、勿論これらに限定されるものではない。ま
た、文中の「部」及び「%」は特に断らない限り、それ
ぞれ「重量部」及び「重量%」を表す。
記載するが、勿論これらに限定されるものではない。ま
た、文中の「部」及び「%」は特に断らない限り、それ
ぞれ「重量部」及び「重量%」を表す。
実施例1
64g/m”の上質紙の表面に、次のように調製した塗
液を塗抹乾燥することによりバリヤー層を得た。即ち、 コーレス分散機により酸化チタン(商品名:FA−55
W、古河鉱業■製)10部を分散、これにポリオレフィ
ン樹脂顔料(商品名:ケミバールA−100、三井石油
化学■製)30部、ポリスチレン樹脂顔料(商品名:ロ
ーペイク0P−84J、日本アクリル■製)45部、ポ
リビニルアルコール(商品名: PVA−205、クラ
レ■製)5部、ポリスチレン・アクリル共重合ラテック
ス(商品名:セビアンA−4720、ダイセル−製)1
0部を添加し、固形分濃度37%の塗液を得た。
液を塗抹乾燥することによりバリヤー層を得た。即ち、 コーレス分散機により酸化チタン(商品名:FA−55
W、古河鉱業■製)10部を分散、これにポリオレフィ
ン樹脂顔料(商品名:ケミバールA−100、三井石油
化学■製)30部、ポリスチレン樹脂顔料(商品名:ロ
ーペイク0P−84J、日本アクリル■製)45部、ポ
リビニルアルコール(商品名: PVA−205、クラ
レ■製)5部、ポリスチレン・アクリル共重合ラテック
ス(商品名:セビアンA−4720、ダイセル−製)1
0部を添加し、固形分濃度37%の塗液を得た。
この塗液を64g/m2の上質紙の表面に乾燥重量が1
5g/m”となるように塗末、乾燥した。更に、この塗
工紙に下記条件でのスーパーキャレンダー処理を行った
。
5g/m”となるように塗末、乾燥した。更に、この塗
工紙に下記条件でのスーパーキャレンダー処理を行った
。
スーパーキャレンダー条件;
線圧 60kg/ cm
クロムメツキ金属ロール表面温度 25℃通紙速度 5
m/分 通紙回数 2回 次に、このバリヤー層の表面に以下の如く調製した受像
層用塗液を塗抹、乾燥し、熱転写記録用受像シートを得
た。即ち、 アルコール変成シリコーンオイル(商品名:トーレシリ
コーン5F−8427、トーレシリコーン■製)10部
にコロイダルシリカ(商品名ニアプライトAT−30A
、旭電化側製)15部、水性変成ウレタン樹脂(商品名
:ハイドランAP40、大日本インキ■製>100部、
エポキシ変成シリコーンオイル(商品名:ポーロンMF
−11B、信越化学■製)3部、架橋触媒(商品名:キ
ャタリストPi−20、大日本インキ■製)を加え、更
にモノエタノールアミン(試薬、キシダ化学■製)10
部を添加、水を加えて固形分濃度20%の受像層用塗液
を得た。これを、バリャー層の表面に乾燥重量が7 g
/m2となるようワイヤーバーで塗抹乾燥した後、下記
の如き条件でスーパーキャレンダー処理をして熱転写記
録用受像シートを得た。
m/分 通紙回数 2回 次に、このバリヤー層の表面に以下の如く調製した受像
層用塗液を塗抹、乾燥し、熱転写記録用受像シートを得
た。即ち、 アルコール変成シリコーンオイル(商品名:トーレシリ
コーン5F−8427、トーレシリコーン■製)10部
にコロイダルシリカ(商品名ニアプライトAT−30A
、旭電化側製)15部、水性変成ウレタン樹脂(商品名
:ハイドランAP40、大日本インキ■製>100部、
エポキシ変成シリコーンオイル(商品名:ポーロンMF
−11B、信越化学■製)3部、架橋触媒(商品名:キ
ャタリストPi−20、大日本インキ■製)を加え、更
にモノエタノールアミン(試薬、キシダ化学■製)10
部を添加、水を加えて固形分濃度20%の受像層用塗液
を得た。これを、バリャー層の表面に乾燥重量が7 g
/m2となるようワイヤーバーで塗抹乾燥した後、下記
の如き条件でスーパーキャレンダー処理をして熱転写記
録用受像シートを得た。
スーパーキャレンダー条件;
線圧 90kg/ cm
クロムメツキ金属ロール表面温度 70℃通紙速度 5
m、/分 通紙回数 2回 実施例2 実施例1において受像層塗液中に配合したモノエタノー
ルアミンを、トリエタノールアミン(試薬、キシダ化学
■製)に変更した以外は実施例1と同様にして熱転写記
録用受像シートを得た。
m、/分 通紙回数 2回 実施例2 実施例1において受像層塗液中に配合したモノエタノー
ルアミンを、トリエタノールアミン(試薬、キシダ化学
■製)に変更した以外は実施例1と同様にして熱転写記
録用受像シートを得た。
比較例1
受像層用塗液中にモノエタノールアミン(試薬、キシダ
化学側製)を配合しなかった以外は実施例1と同様にし
て熱転写記録用受像シートを得た。
化学側製)を配合しなかった以外は実施例1と同様にし
て熱転写記録用受像シートを得た。
かくして得られた3種類の熱転写記録用受像シートにつ
いて、以下の如く品質比較試験を行った。
いて、以下の如く品質比較試験を行った。
即ち、
昇華性分散染料(商品名: KST−B−136、日本
化薬■製)40部、ヒドロキシエチルセルロース601
をメチルエチルケトン/トルエン(重量比 1:1)中
にミキサーで撹拌しながら添加し、固形分濃度10%の
熱転写層形成用インキ組成物を得た。
化薬■製)40部、ヒドロキシエチルセルロース601
をメチルエチルケトン/トルエン(重量比 1:1)中
にミキサーで撹拌しながら添加し、固形分濃度10%の
熱転写層形成用インキ組成物を得た。
このようにして得たインキ組成物を、背面に耐熱処理を
施した厚み9μmのPETフィルムに、乾燥重量が1
g/m2となるようワイヤーバーで塗抹乾燥し、熱転写
シートを得た。
施した厚み9μmのPETフィルムに、乾燥重量が1
g/m2となるようワイヤーバーで塗抹乾燥し、熱転写
シートを得た。
次に、このようにして得られた熱転写シートと熱転写記
録用受像シートの受像層塗布面を重ね合せ、熱ヘツドに
より出力IW/ドツト、パルス幅0.3〜4.5m5e
c、ドツト密度3ドツト/mmの条件で熱を印加し、熱
転写記録像を形成した。このときの発色濃度、熱融着の
発生状態を、目視で評価してその結果を表−1に示した
。
録用受像シートの受像層塗布面を重ね合せ、熱ヘツドに
より出力IW/ドツト、パルス幅0.3〜4.5m5e
c、ドツト密度3ドツト/mmの条件で熱を印加し、熱
転写記録像を形成した。このときの発色濃度、熱融着の
発生状態を、目視で評価してその結果を表−1に示した
。
表−1
◎・・・非常に優れている
○・・・優れている
△・・・実用上問題なし
×・・・劣っている
「効果」
表−1の結果から明らかなように、本発明の実施例で得
られた熱転写記録用受像シートではいずれも良好な記録
画像が得られた。
られた熱転写記録用受像シートではいずれも良好な記録
画像が得られた。
第1図は熱転写記録用受像シートの基本構成を示す図で
ある。 (1)基材 (2)バリヤー層 (3)受像層(
4)カール防止層
ある。 (1)基材 (2)バリヤー層 (3)受像層(
4)カール防止層
Claims (1)
- 支持体上に、色材転写シートからの転写像を受理する
受像層を設けてなる熱転写記録用受像シートにおいて、
該受像層がエタノールアミンを含むことを特徴とする熱
転写記録用受像シート。