JPH02135299A - スコアリングパッド用洗浄剤組成物 - Google Patents
スコアリングパッド用洗浄剤組成物Info
- Publication number
- JPH02135299A JPH02135299A JP28986688A JP28986688A JPH02135299A JP H02135299 A JPH02135299 A JP H02135299A JP 28986688 A JP28986688 A JP 28986688A JP 28986688 A JP28986688 A JP 28986688A JP H02135299 A JPH02135299 A JP H02135299A
- Authority
- JP
- Japan
- Prior art keywords
- water
- weight
- scoring
- polyethylene glycol
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
1゜
3゜
〔産業上の利用分野〕
本発明は、優れた洗浄力、研暦力を有し、被洗浄面を傷
付けることがなく、使用後の防錆効果に優れ、かつ製造
時に乾燥工程を必要としないスコアリングパッド用洗浄
剤組成物に関する。
付けることがなく、使用後の防錆効果に優れ、かつ製造
時に乾燥工程を必要としないスコアリングパッド用洗浄
剤組成物に関する。
家庭内の台所の汚れ、例えば鍋、フライパン等に付着し
た煮ごぼれ、焦げつき汚れ、焼き付汚れ、ガスレンジ周
辺の焼き付き汚れ、換気扇のベタ付き油汚れ、タイル目
地の汚れなどは、どこの家庭にも存在し目立つものであ
るが、なかなか落としにくい汚れである。
た煮ごぼれ、焦げつき汚れ、焼き付汚れ、ガスレンジ周
辺の焼き付き汚れ、換気扇のベタ付き油汚れ、タイル目
地の汚れなどは、どこの家庭にも存在し目立つものであ
るが、なかなか落としにくい汚れである。
これらの汚れの洗浄手段として、スコアリングパッドの
使用が一般に行なわれている。
使用が一般に行なわれている。
このスコアリングパッドは、一般に金属タワシなどに洗
浄剤成分として石鹸を付着させてなるものである。スコ
アリングパッドの洗浄剤成分として石鹸が使用されてき
た背景には、安価であり、使用時の泡立ちも良く、金属
タワシなどに付着させる前に石鹸水溶液(高温溶解)に
てハンドリングし、水分を蒸散させることにより容易に
固化し、型崩れせず貯蔵安定性が良いという利点があっ
た。
浄剤成分として石鹸を付着させてなるものである。スコ
アリングパッドの洗浄剤成分として石鹸が使用されてき
た背景には、安価であり、使用時の泡立ちも良く、金属
タワシなどに付着させる前に石鹸水溶液(高温溶解)に
てハンドリングし、水分を蒸散させることにより容易に
固化し、型崩れせず貯蔵安定性が良いという利点があっ
た。
しかし従来のスコアリングパッドにおいては、洗浄力が
充分でない、製造時の乾燥工程に多大な労力、時間を要
し、作業環境が悪い等の問題点があった。
充分でない、製造時の乾燥工程に多大な労力、時間を要
し、作業環境が悪い等の問題点があった。
従って、製造時の乾燥工程を省略化でき、優れた洗浄力
、研暦力を有し、被洗浄面を傷付けることがないスコア
リングパッド用洗浄剤組成物の開発が望まれていた。
、研暦力を有し、被洗浄面を傷付けることがないスコア
リングパッド用洗浄剤組成物の開発が望まれていた。
そこで、本発明者らは上記課題を解決すべく種々検討し
た結果、洗浄剤成分に一定の分子量を有するポリエチレ
ングリコールを配合すれば洗浄力、研暦力が向上し、容
易に製造できることを見出し、本発明を完成した。
た結果、洗浄剤成分に一定の分子量を有するポリエチレ
ングリコールを配合すれば洗浄力、研暦力が向上し、容
易に製造できることを見出し、本発明を完成した。
すなわち、本発明は次の成分(A)〜 (C)、(A)
平均分子量が2.000〜13.000のポリエチレン
グリコール 10〜90重量%(B)界面活性
剤 1〜50重債%(C)水
0〜5重量%を含有することを特徴とするス
コアリングパッド用洗浄剤組成物を提供するものである
。
平均分子量が2.000〜13.000のポリエチレン
グリコール 10〜90重量%(B)界面活性
剤 1〜50重債%(C)水
0〜5重量%を含有することを特徴とするス
コアリングパッド用洗浄剤組成物を提供するものである
。
本発明において用いられる(^)成分のポリエチレング
リコールの平均分子1は2.000〜13、000、好
ましくは3.000〜a、 oooである。
リコールの平均分子1は2.000〜13、000、好
ましくは3.000〜a、 oooである。
配合量は10〜90重量%(以下、単に%で示す)、好
ましくは20〜80%である。
ましくは20〜80%である。
本発明において用いられる(B)成分の界面活性剤とし
ては陰イオン性界面活性剤、非イオン性界面活性剤、陽
イオン性界面活性剤、両性界面活性剤が使用されるが、
特に陰イオン性界面活性剤または非イオン性界面活性剤
が好ましい。
ては陰イオン性界面活性剤、非イオン性界面活性剤、陽
イオン性界面活性剤、両性界面活性剤が使用されるが、
特に陰イオン性界面活性剤または非イオン性界面活性剤
が好ましい。
本発明において使用される陰イオン性界面活性剤として
は、炭素数8〜22の脂肪酸塩、炭素数8〜22のアル
キル硫酸塩、アルキル基の炭素数が8〜16のアルキル
ベンゼンスルホン酸塩、アルキル基の炭素数が10〜2
0であり酸化エチレン付加モル数が1〜10であるポリ
オキシエチレンアルキルエーテル硫酸塩、アルキル基の
炭素数が8〜12で酸化エチレン付加モル数が1〜10
のポリオキシエチレンアルキルフェノール硫酸エステル
塩、炭素数8〜18のα−オレフィンをスルホン化して
得られるα−オレフィンスルホン酸塩、炭素数8〜20
のパラフィンから得られるアルカンスルホン酸塩などが
挙げられる。これらのうち、酸化エチレンを付加したも
の及び硫酸塩系の活性剤は、錆に対する影響が認められ
る場合があるので、その場合は防錆剤を併用するのが好
ましい。
は、炭素数8〜22の脂肪酸塩、炭素数8〜22のアル
キル硫酸塩、アルキル基の炭素数が8〜16のアルキル
ベンゼンスルホン酸塩、アルキル基の炭素数が10〜2
0であり酸化エチレン付加モル数が1〜10であるポリ
オキシエチレンアルキルエーテル硫酸塩、アルキル基の
炭素数が8〜12で酸化エチレン付加モル数が1〜10
のポリオキシエチレンアルキルフェノール硫酸エステル
塩、炭素数8〜18のα−オレフィンをスルホン化して
得られるα−オレフィンスルホン酸塩、炭素数8〜20
のパラフィンから得られるアルカンスルホン酸塩などが
挙げられる。これらのうち、酸化エチレンを付加したも
の及び硫酸塩系の活性剤は、錆に対する影響が認められ
る場合があるので、その場合は防錆剤を併用するのが好
ましい。
非イオン性界面活性剤としては、炭素数8〜20の高級
アルコールに酸化エチレン1〜20モルを付加したポリ
オキシエチレンアルキルエーテル、アルキル基の炭素数
が8〜12のアルキルフェノールに酸化エチレン1〜2
0モルを付加したポリオキシエチレンアルキルエ−テエ
゛−チル、炭素18〜20の脂肪酸とジェタノールアミ
ン、ジイソプロパツールアミンなどのアルカノールアミ
ンから導かれる脂肪酸アルカノールアミドなどが挙げら
れる。これらのうち、ポリオキシエチレンアルキルエー
テル、ポリオキシエチレンアルキルフェノールエーテル
等の酸化エチレンを付加した非イオン性界面活性剤は、
錆に対する影響が認められる場合があるので、その場合
は防錆剤を併用するのが好ましい。界面活性剤の配合量
は1〜50重量%、好ましくは5〜30重量%である。
アルコールに酸化エチレン1〜20モルを付加したポリ
オキシエチレンアルキルエーテル、アルキル基の炭素数
が8〜12のアルキルフェノールに酸化エチレン1〜2
0モルを付加したポリオキシエチレンアルキルエ−テエ
゛−チル、炭素18〜20の脂肪酸とジェタノールアミ
ン、ジイソプロパツールアミンなどのアルカノールアミ
ンから導かれる脂肪酸アルカノールアミドなどが挙げら
れる。これらのうち、ポリオキシエチレンアルキルエー
テル、ポリオキシエチレンアルキルフェノールエーテル
等の酸化エチレンを付加した非イオン性界面活性剤は、
錆に対する影響が認められる場合があるので、その場合
は防錆剤を併用するのが好ましい。界面活性剤の配合量
は1〜50重量%、好ましくは5〜30重量%である。
本発明は製造時の乾燥工程を省くことをその目的の一つ
とするものであり、したがって組成物中の水含量は5%
以下であることが必要である。
とするものであり、したがって組成物中の水含量は5%
以下であることが必要である。
本発明組成物には上記必須成分の池に、必要に応じて種
々の任意成分を配合することができる。特に水不溶性研
暦剤(D)を配合すれば、洗浄力をさらに向上させるこ
とができる。
々の任意成分を配合することができる。特に水不溶性研
暦剤(D)を配合すれば、洗浄力をさらに向上させるこ
とができる。
かかる水不溶性研磨剤としては、二酸化ケイ素、酸化ア
ルミニウム、水酸化アルミニウム、酸化マグネシウム、
酸化チタン、炭化ケイ素、炭酸カルシウム、リン酸カル
シウム、酸化クロム、合成ゼオライト、天然ゼオライト
、コランダム、エメリー、けい石、石英砂、カルサイト
、ドロマイト、あるいは塩化ビニル、ポリスチレン、ポ
リエチレン、ABSなどのポリマービーズなどが挙げら
れる。このうち、平均粒径1〜40μの二酸化ケイ素、
炭酸カルシウム、けい石がとくに好ましい。水不溶性研
磨剤の配合量は5〜50%、特に10〜40%が好まし
い。
ルミニウム、水酸化アルミニウム、酸化マグネシウム、
酸化チタン、炭化ケイ素、炭酸カルシウム、リン酸カル
シウム、酸化クロム、合成ゼオライト、天然ゼオライト
、コランダム、エメリー、けい石、石英砂、カルサイト
、ドロマイト、あるいは塩化ビニル、ポリスチレン、ポ
リエチレン、ABSなどのポリマービーズなどが挙げら
れる。このうち、平均粒径1〜40μの二酸化ケイ素、
炭酸カルシウム、けい石がとくに好ましい。水不溶性研
磨剤の配合量は5〜50%、特に10〜40%が好まし
い。
また本発明組成物には上記成分以外に、無機塩、着色剤
、香料、殺菌剤、防黴剤、防錆剤などを必要に応じて加
えることができる。
、香料、殺菌剤、防黴剤、防錆剤などを必要に応じて加
えることができる。
無機塩としては、炭酸ソーダ、炭酸カリなどの炭酸塩;
メタケイ酸ソーダ、2号ケイ酸ソーダなどのケイ酸塩、
ホウ砂、メタホウ酸ソーダなどのホウ酸塩;オルトリン
酸ソーダ、トリポリリン酸ソーダ、ピロリン酸ソーダな
どのリン酸塩が使用できる。硫酸ソーダ、硫酸カリウム
などの硫酸塩も使用できるが、錆に対する影響がみとめ
られる場合があるので、どの場合は防錆剤を併用するの
が好ましい。
メタケイ酸ソーダ、2号ケイ酸ソーダなどのケイ酸塩、
ホウ砂、メタホウ酸ソーダなどのホウ酸塩;オルトリン
酸ソーダ、トリポリリン酸ソーダ、ピロリン酸ソーダな
どのリン酸塩が使用できる。硫酸ソーダ、硫酸カリウム
などの硫酸塩も使用できるが、錆に対する影響がみとめ
られる場合があるので、どの場合は防錆剤を併用するの
が好ましい。
本発明組成物を用いてスコアリングパッドを製造するに
は、例えばまず研磨剤細線を適当な形に成形し、これに
ポリエチレングリコールの融点以上の温度で混合した本
発明組成物を注入、塗布、浸漬などの方法で付着させ、
放冷すればよい。
は、例えばまず研磨剤細線を適当な形に成形し、これに
ポリエチレングリコールの融点以上の温度で混合した本
発明組成物を注入、塗布、浸漬などの方法で付着させ、
放冷すればよい。
スコアリングパッドを構成する研磨剤細線には、普通、
鋼、ステンレス、真鍮などの金属細線や、ナイロン、ウ
レタンなどが用いられる。就中、新暦力、手の感触が良
い点からとくに鋼が好ましい。スコアリングパッドを構
成する細線は太すぎるとキズがつきやすく、手の感触が
悪いが、細すぎると新暦力がおちるので平均径1〜50
0μ、特に10〜70μが好ましく、断面の形状はいか
なるものでも良く、例えば三角、四角、円、偏平などを
用いることができる。細線の全体の形状は円形、正方形
、長方形、小判形、楕円形(いずれも厚みを持つ)、球
形などの形で使用することができる。
鋼、ステンレス、真鍮などの金属細線や、ナイロン、ウ
レタンなどが用いられる。就中、新暦力、手の感触が良
い点からとくに鋼が好ましい。スコアリングパッドを構
成する細線は太すぎるとキズがつきやすく、手の感触が
悪いが、細すぎると新暦力がおちるので平均径1〜50
0μ、特に10〜70μが好ましく、断面の形状はいか
なるものでも良く、例えば三角、四角、円、偏平などを
用いることができる。細線の全体の形状は円形、正方形
、長方形、小判形、楕円形(いずれも厚みを持つ)、球
形などの形で使用することができる。
次に実施例を挙げて本発明の詳細な説明するが、本発明
はこれに制約されるものではない。
はこれに制約されるものではない。
実施例1
(1) 平均直径20〜50μのスチール細線5gを
、直径7.5 am X 6.Ocm (厚さ1.5c
m)の小判形パッドに成型し、パッド内部に80℃で配
合した表−1に示す本発明組成物を5g注入成型し、放
冷してスコアリングパッドを製造でた。
、直径7.5 am X 6.Ocm (厚さ1.5c
m)の小判形パッドに成型し、パッド内部に80℃で配
合した表−1に示す本発明組成物を5g注入成型し、放
冷してスコアリングパッドを製造でた。
(2) 得られたスコアリングパッドについて、下記
の試験方法に従い、洗浄力、傷付は性、錆試験、しみ出
し性及び溶解性を試験した。その結果を表−1に示す。
の試験方法に従い、洗浄力、傷付は性、錆試験、しみ出
し性及び溶解性を試験した。その結果を表−1に示す。
く洗浄力〉
3 X 8amの鉄のテストピースに、ナタネ油/カー
ボンブラック(重量比+ 5/1)を1.0g塗布した
ものを180tで100分変性させたものを使用した。
ボンブラック(重量比+ 5/1)を1.0g塗布した
ものを180tで100分変性させたものを使用した。
評価法は、スコアリングパッドに水を含ませて、1 k
g / crlの荷重により30回洗浄した後の重量減
少率より相対洗浄率を求め、下記の通り5段階評価を行
なった。
g / crlの荷重により30回洗浄した後の重量減
少率より相対洗浄率を求め、下記の通り5段階評価を行
なった。
相対洗浄力(%)
5:81〜1000
4:61〜80
3:41〜60
2:21〜40
に 〇〜20
〔相対洗浄力(%):比較界Nα1
(表−1参照)の洗浄力を50とした〕〈傷付は性〉
スコアリングパッドに水を含ませて、浴槽や流し台の材
質であるステンレス表面を50回洗浄後、傷の有無を肉
眼観察し、評価を行なった。
質であるステンレス表面を50回洗浄後、傷の有無を肉
眼観察し、評価を行なった。
○:傷付けない。
△:やや傷付ける。
×:傷付ける。
く錆試験〉
スコアリングパッドに水を含ませて、浴槽や流し台の材
質であるステンレス表面を50回洗浄後、軽く絞り室温
に一昼夜放置し、錆の有無を肉眼観察し、評価を行なっ
た。
質であるステンレス表面を50回洗浄後、軽く絞り室温
に一昼夜放置し、錆の有無を肉眼観察し、評価を行なっ
た。
○:錆ない
△:やや錆る。
×;錆る。
くしみ出し性〉
スコアリングパッドを濾紙の上に乗せ、30℃、65%
RHに一週間保存し、しみ出しの有無を観察する。
RHに一週間保存し、しみ出しの有無を観察する。
○:しみ出さない。
△:ややしみ出す。
×ニジみ出す。
く溶解性〉
スコアリングパッドに水を含ませて、浴槽や流し台の材
質であるステンレス表面を洗浄する時の使い始めの状態
を観察する。
質であるステンレス表面を洗浄する時の使い始めの状態
を観察する。
○:使い始め、すぐに洗浄剤が溶は出す。
△:使い始め、少し揉むと洗浄剤が溶は出す。
×二使い始め、洗浄剤がなかなか溶は出さない。
以下余白
実施例2
表−2に示す本発明組成物を用いる以外は実施例1と同
様にしてスコアリングパッドを製造し、その評価をした
。その結果を表−2に示す。
様にしてスコアリングパッドを製造し、その評価をした
。その結果を表−2に示す。
以下余白
〔発明の効果〕
本発明のスコアリングパッド用洗浄剤組成物を使用すれ
ば、(fLれた洗浄力、研出力を有し、被洗浄面を傷つ
けることがなく、洗浄剤成分のしみ出しがなく、使用後
の防錆効果に優れたスコアリングパッドを、製造時に乾
燥工程を要せずに製造することができる。
ば、(fLれた洗浄力、研出力を有し、被洗浄面を傷つ
けることがなく、洗浄剤成分のしみ出しがなく、使用後
の防錆効果に優れたスコアリングパッドを、製造時に乾
燥工程を要せずに製造することができる。
以 上
出願人 花 王 株 式 会 社手続補正
書(自発) 平成元年1月91] 1、事件の表示 昭和63年特許願第289866号 2、発明の名称 スコアリングパッド用洗浄剤組成物 3、補正をする者 事件との関係 出願人 名 称 (091)花王株式会社 4、代理人 住 所 東京都中央区日本橋人形町1丁目3番6号(
〒103)7、′
書(自発) 平成元年1月91] 1、事件の表示 昭和63年特許願第289866号 2、発明の名称 スコアリングパッド用洗浄剤組成物 3、補正をする者 事件との関係 出願人 名 称 (091)花王株式会社 4、代理人 住 所 東京都中央区日本橋人形町1丁目3番6号(
〒103)7、′
Claims (1)
- 【特許請求の範囲】 1 次の成分(A)〜(C) (A)平均分子量が2,000〜13,000のポリエ
チレングリコール10〜90重量% (B)界面活性剤1〜50重量% (C)水0〜5重量% を含有することを特徴とするスコアリングパッド用洗浄
剤組成物。 2次の成分(A)〜(D) (A)平均分子量が2,000〜13,000のポリエ
チレングリコール10〜90重量% (B)界面活性剤1〜50重量% (C)水0〜5重量% (D)水不溶性研磨剤5〜50重量% を含有することを特徴とするスコアリングパッド用洗浄
剤組成物。