JP7479175B2 - スチレン系樹脂押出発泡体の製造方法 - Google Patents
スチレン系樹脂押出発泡体の製造方法 Download PDFInfo
- Publication number
- JP7479175B2 JP7479175B2 JP2020057065A JP2020057065A JP7479175B2 JP 7479175 B2 JP7479175 B2 JP 7479175B2 JP 2020057065 A JP2020057065 A JP 2020057065A JP 2020057065 A JP2020057065 A JP 2020057065A JP 7479175 B2 JP7479175 B2 JP 7479175B2
- Authority
- JP
- Japan
- Prior art keywords
- styrene
- weight
- based resin
- parts
- extruded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
<1>スチレン系樹脂を含有するスチレン系樹脂組成物の溶融物に発泡剤を添加し発泡性溶融物を調製する工程を有する、スチレン系樹脂押出発泡体の製造方法であって、前記発泡剤が(A)塩化アルキル、並びに、(B)水および/またはアルコールを含有し、前記(A)塩化アルキルと、前記(B)水および/またはアルコールとを分けて前記スチレン系樹脂に添加し溶融混練する、スチレン系樹脂押出発泡体の製造方法。
<2>スチレン系樹脂100重量部に対して、前記(A)塩化アルキルを、2.0重量部以上7.0重量部以下、前記(B)水および/またはアルコールを、0.5重量部以上1.5重量部以下添加する、<1>に記載のスチレン系樹脂押出発泡体の製造方法。
<3>前記(A)塩化アルキルが塩化エチルを含み、前記(B)水および/またはアルコールが水を含む、<1>または<2>に記載のスチレン系樹脂押出発泡体の製造方法。
<4>前記発泡剤が、さらに(C)ハイドロフルオロオレフィン及び/又はハイドロクロロフルオロオレフィンを含有する、<1>~<3>のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
<5>スチレン系樹脂100重量部に対して、前記(C)ハイドロフルオロオレフィンおよび/またはハイドロクロロオレフィンを、2.0重量部以上13.0重量部以下添加する、<4>に記載のスチレン系樹脂押出発泡体の製造方法。
<6>前記スチレン系樹脂100重量%において、スチレン-アクリロニトリル共重合体が10重量%以上100重量%以下含有される、<1>~<5>のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
<7>前記スチレン系樹脂押出発泡体が、前記スチレン系樹脂100重量部に対して熱線輻射抑制剤を0.5重量部以上5.0重量部以下含有する、<1>~<6>のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
<8>前記スチレン系樹脂押出発泡体の熱伝導率が0.0244W/mK以下である、<1>~<7>のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
<9>前記スチレン系樹脂押出発泡体の密度が20~60kg/m3である、<1>~<8>のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
<10>前記スチレン系樹脂押出発泡体の厚みが10mm以上150mm以下である、<1>~<9>のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
本発明の一実施形態に係るスチレン系樹脂押出発泡体の製造方法は、スチレン系樹脂を含有するスチレン系樹脂組成物の溶融物に発泡剤を添加し発泡性溶融物を調製する工程を有する、スチレン系樹脂押出発泡体の製造方法であって、前記発泡剤が(A)塩化アルキル、並びに、(B)水および/またはアルコールを含有し、前記(A)塩化アルキルと、前記(B)水および/またはアルコールとを分けて前記スチレン系樹脂に添加し溶融混練する。
本発明の一実施形態で用いるスチレン系樹脂としては、特に限定はなく、(i)スチレン、メチルスチレン、エチルスチレン、イソプロピルスチレン、ジメチルスチレン、ブロモスチレン、クロロスチレン、ビニルトルエン、ビニルキシレン等のスチレン系単量体の単独重合体または2種以上の単量体の組み合わせからなる共重合体や、(ii)前記スチレン系単量体と、ジビニルベンゼン、ブタジエン、アクリル酸、メタクリル酸、アクリル酸メチル、メタクリル酸メチル、アクリロニトリル、無水マレイン酸、無水イタコン酸などの共重合可能な他の単量体の1種または2種以上と、を共重合させた共重合体などが挙げられる。前記共重合可能な他の単量体は、製造されるスチレン系樹脂押出発泡体の圧縮強度等の物性を低下させない程度の量を用いることができる。また、本発明の一実施形態に用いるスチレン系樹脂は、前記スチレン系単量体の単独重合体または共重合体に限られず、前記スチレン系単量体の単独重合体または共重合体と、前記他の単量体の単独重合体または共重合体とのブレンド物であってもよい。例えば、本発明の一実施形態に用いるスチレン系樹脂は、前記スチレン系単量体の単独重合体もしくは共重合体と、ジエン系ゴム強化ポリスチレンまたはアクリル系ゴム強化ポリスチレンとのブレンド物であってもよい。更に、本発明の一実施形態で用いるスチレン系樹脂は、メルトフローレート(以下、MFRという。)、成形加工時の溶融粘度、溶融張力などを調整する目的で、分岐構造を有するスチレン系樹脂であってもよい。これらは単独で使用してもよく、また、共重合成分、分子量や分子量分布、分岐構造、及び/又はMFRなどの異なる2種以上を混合して使用してもよい。
本発明の一実施形態では、発泡剤として(A)塩化アルキル(以下、「発泡剤(A)」と称することがある。)と、(B)水及び/又はアルコール(以下、「発泡剤(B)」と称することがある。)とを使用する。
本発明の一実施形態に係る(B)水及び/又はアルコールの添加量は、スチレン系樹脂100重量部に対して0.5重量部以上2.0重量部以下が好ましく、0.5重量部以上1.8重量部以下がより好ましく、0.5重量部以上1.5重量部以下がさらに好ましい。(B)水及び/又はアルコールの添加量がスチレン系樹脂100重量部に対して0.5重量部より少ない場合には、水及び/又はアルコールによる厚み出し改善効果があまり期待できない。一方、(B)水及び/又はアルコールの添加量がスチレン系樹脂100重量部に対して2.0重量部を超える場合には、水及び/又はアルコールの量が多すぎるため、押出し機中で水及び/又はアルコールが樹脂に分散、溶解しきれなくなり、気孔が発生するなどして発泡体の外観が悪化する場合がある。
本発明の一実施形態では、スチレン系樹脂押出発泡体において、難燃剤を添加することにより、得られるスチレン系樹脂押出発泡体に難燃性を付与することができる。
本発明の一実施形態においては、難燃剤の安定剤を使用することが出来る。特に限定されるものでは無いが、安定剤の具体的な例としては、(i)ビスフェノールAジグリシジルエーテル型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、及びフェノールノボラック型エポキシ樹脂のようなエポキシ化合物、(ii)ペンタエリスリトール、ジペンタエリスリトール、トリペンタエリスリトール等の多価アルコールと、酢酸、プロピオン酸等の一価のカルボン酸、又は、アジピン酸、グルタミン酸等の二価のカルボン酸との反応物であるエステルであって、その分子中に一個以上の水酸基を持つエステルの混合物であり、原料の多価アルコールを少量含有することもある、多価アルコールエステル、(iii)トリエチレングリコール-ビス-3-(3-tert-ブチル-4-ヒドロキシ-5-メチルフェニル)プロピオネート、ペンタエリトリトールテトラキス[3-(3’,5’-ジ-tert-ブチル-4’-ヒドロキシフェニル)プロピオネート]、及びオクタデシル3-(3,5-ジ-tert-ブチル-4-ヒドロキシフェニル)プロピオナートのようなフェノール系安定剤、(iv)3,9-ビス(2,4-ジ-tert-ブチルフェノキシ)-2,4,8,10-テトラオキサ-3,9-ジホスファスピロ[5.5]ウンデカン、3,9-ビス(2,6-ジ-tert-ブチル-4-メチルフェノキシ)-2,4,8,10-テトラオキサ-3,9-ジホスファスピロ[5.5]ウンデカン、及びテトラキス(2,4-ジ-tert-ブチル-5-メチルフェニル)-4,4’-ビフェニレンジホスホナイト)のようなホスファイト系安定剤、などが発泡体の難燃性能を低下させることなく、かつ、発泡体の熱安定性を向上させることから、好適に用いられる。
本発明の一実施形態に係るスチレン系樹脂押出発泡体は、断熱性向上のため、熱線輻射抑制剤を添加してもよい。本発明の一実施形態としては、熱線輻射抑制剤としてグラファイトを使用できる。例えば、鱗(片)状黒鉛、土状黒鉛、球状黒鉛、人造黒鉛などが挙げられる。これらの中でも、熱線輻射抑制効果が高い点から、主成分が鱗(片)状黒鉛のものを用いることが好ましい。グラファイトは、固定炭素分が80%以上のものが好ましく、85%以上のものがより好ましい。固定炭素分を上記範囲とすることで高い断熱性を有する発泡体が得られる。
本発明の一実施形態では、必要に応じて、成形性改善剤として、多価アルコール脂肪酸エステル及び/または、ポリエチレングリコールを添加してもよい。これらを使用することにより、押出発泡体に美麗な表面を付与すること、押出発泡体の厚みを出すこと(つまり、押出発泡体の成形性を改善すること)が可能となる。
本発明の一実施形態においては、さらに、必要に応じて、本発明の一実施形態に係る効果を阻害しない範囲で、例えば、シリカ、ケイ酸カルシウム、ワラストナイト、カオリン、クレイ、マイカ、炭酸カルシウムなどの無機化合物、ステアリン酸ナトリウム、ステアリン酸カルシウム、ステアリン酸マグネシウム、ステアリン酸バリウム、流動パラフィン、オレフィン系ワックス、ステアリルアミド系化合物などの加工助剤、フェノール系抗酸化剤、リン系安定剤、窒素系安定剤、イオウ系安定剤、ベンゾトリアゾール類、ヒンダードアミン類などの耐光性安定剤、タルクなどの気泡径調整剤、前記以外の難燃剤、帯電防止剤、顔料などの着色剤、可塑剤などの添加剤がスチレン系樹脂に含有されてもよい。また、必要に応じ、本発明の一実施形態に係る効果を阻害しない範囲で、その他の樹脂をスチレン系樹脂と併用してもよい。
本発明の一実施形態に係るスチレン系樹脂押出発泡体の熱伝導率は特に限定はないが、例えば建築用断熱材、又は、保冷庫用若しくは保冷車用の断熱材として機能することを考慮した断熱性の観点から、平均温度23℃で測定した製造1週間後の熱伝導率が0.0284W/mK以下であることが好ましく、0.0244W/mK以下であることがより好ましく、0.0224W/mK以下であることが特に好ましい。
観察箇所毎の厚み方向の平均気泡径A(mm)=2×3/気泡の個数a
・・・(1)。
観察箇所毎の押出方向の平均気泡径B(mm)=2×3/気泡の個数b
・・・(2)。
観察箇所毎の幅方向の平均気泡径C(mm)=2×3/気泡の個数c
・・・(3)。
気泡変形率(単位なし)=A(平均値)/{〔B(平均値)+C(平均値)〕/2}・・・(4)。
本発明の一実施形態に係るスチレン系樹脂押出発泡体の製造方法は、スチレン系樹脂を含む樹脂組成物を加熱溶融し、発泡剤を添加して発泡性溶融物を調製する溶融工程と、上記溶融工程にて得られた発泡性溶融物をダイスリット部から低圧域に押し出して発泡させる発泡工程とを有するものであって、前記発泡剤が(A)塩化アルキル並びに(B)水及び/又はアルコールを含み、かつ、(A)塩化アルキルと(B)水及び/又はアルコールとは分けて添加されることを特徴とする。
実施例及び比較例において使用した原料は、次の通りである。
○基材樹脂
・スチレン-アクリロニトリル共重合体 [デンカ(株)製、デンカAS GR-AT-5S;アクリロニトリル成分量25重量%、MFR8.0g/10分]
・ポリスチレン [PSジャパン(株)製、680;MFR7.0g/10分]
○熱線輻射抑制剤
・グラファイト [(株)丸豊鋳材製作所製、M-885;鱗片状黒鉛、平均粒径5.5μm、固定炭素分89%]
○難燃剤
・テトラブロモビスフェノールA-ビス(2,3-ジブロモ-2-メチルプロピル)エーテル、及びテトラブロモビスフェノールA-ビス(2,3-ジブロモプロピル)エーテルの混合臭素系難燃剤[第一工業製薬(株)製、GR-125P]
○難燃助剤
・トリフェニルホスフィンオキシド [住友商事ケミカル]
○安定剤
・ビスフェノール-A-グリシジルエーテル [(株)ADEKA製、EP-13]
・ジペンタエリスリトール-アジピン酸反応混合物 [味の素ファインテクノ(株)製、プレンライザーST210]
・トリエチレングリコール-ビス-3-(3-tert-ブチル-4-ヒドロキシ-5-メチルフェニル)プロピオネート [Songwon Japan(株)製、ソンノックス2450FF]
○その他添加剤
・タルク [林化成(株)製、タルカンパウダーPK-Z]
・ステアリン酸カルシウム [堺化学工業(株)製、SC-P]
・ベントナイト [(株)ホージュン製、ベンゲルブライト11K]
・シリカ [エボニックデグサジャパン(株)製、カープレックスBS-304F]
・エチレンビスステアリン酸アミド [日油(株)製、アルフローH-50S]
・ステアリン酸モノグリセリド [理研ビタミン(株)製、リケマールS-100P]
○発泡剤
(A)
・塩化エチル [日本特殊化学工業(株)製]
(B)
・水 [大阪府摂津市水道水]
・エタノール [富士フイルム和光純薬(株)製、エタノール 試薬特級]
(C)
・HFO-1234ze [ハネウェルジャパン(株)製]
・HCFO-1233zd [ハネウェルジャパン(株)製]・
その他発泡剤
・イソブタン [三井化学(株)製]
実施例及び比較例では、下記の測定方法にしたがって、各種パラメータを、測定及び評価した。
後述する[押出発泡体の作製]にて得られた厚み60mm×幅1000mmである断面形状の押出発泡板において、ノギス[(株)ミツトヨ製、M型標準ノギスN30]を用いて、幅方向中央部、及び幅方向の一端から逆端方向に150mmの場所(幅方向両端について同じ場所)の厚み、計3点を測定した。3点の平均値をスチレン系樹脂押出発泡体の厚みとした。
得られたスチレン系樹脂押出発泡体の重量を測定すると共に、長さ寸法、幅寸法、厚み寸法を測定した。
見掛け密度(g/cm3)=発泡体重量(g)/発泡体体積(cm3)。
得られたスチレン系樹脂押出発泡体の幅方向中央部、幅方向の一端から逆端方向に150mmの場所、及び、幅方向の他端から逆端方向に150mmの場所の計3箇所から、厚さ40mm×長さ(押出方向)25mm×幅25mmの試験片を切り出した。当該試験片を用い、ASTM-D2856-70の手順Cに従って測定し、以下の式にて各試験片の独立気泡率を求め、3箇所における独立気泡率の平均値を、スチレン系樹脂押出発泡体の独立気泡率とした。
独立気泡率(%)=(V1-W/ρ)×100/(V2-W/ρ)
ここで、V1(cm3)は、空気比較式比重計[東京サイエンス(株)製、空気比較式比重計、型式1000型]を用いて測定した試験片の真の体積(独立気泡でない部分の容積が除かれる。)である。V2(cm3)は、ノギス[(株)ミツトヨ製、M型標準ノギスN30]を用いて測定した試験片の外側寸法より算出した、見掛けの体積である。W(g)は、試験片の全重量である。また、ρ(g/cm3)は、押出し発泡体を構成するスチレン系樹脂の密度であり、1.05(g/cm3)とした。
得られたスチレン系樹脂押出発泡体について、前述の通りマイクロスコープ[(株)KEYENCE製、DIGITAL MICROSCOPE VHX-900]を用いて、平均気泡径を測定し、測定した平均気泡径から気泡変形率を求めた。
JIS A 9521に準じて、厚さ50mm×長さ(押出方向)300mm×幅300mmにてスチレン系樹脂押出発泡体から切り出した試験片を用い、熱伝導率測定装置[英弘精機(株)、HC-074]を用いて、平均温度23℃での熱伝導率を測定した。具体的に、スチレン系樹脂押出発泡体の製造後、上記寸法の試験片を切り出し、当該試験片をJIS K 7100に規定された標準温度状態3級(23℃±5℃)、及び標準湿度状態3級(50+20、-10%R.H.)の条件下に静置した後、スチレン系樹脂押出発泡体の製造から1週間(7日間経過)後に、熱伝導率の測定を行った
JIS A 9521に準じて、厚さ10mm×長さ200mm×幅25mmの試験片を用い、以下の基準で燃焼性を評価した。製造されたスチレン系樹脂押出発泡体を、前記寸法の試験片に切削し、当該試験片を、JIS K 7100に規定された標準温度状態3級(23℃±5℃)、及び標準湿度状態3級(50+20、-10%R.H.)の条件下に静置した。スチレン系樹脂押出発泡体を製造してから1週間後(7日間経過後)に、試験片を用いて燃焼性を評価した。
○:「3秒以内に炎が消えて、残じんがなく、燃焼限界指示線を超えて燃焼しない」との基準を満たす。
×:上記基準を満たさない。
得られたスチレン系樹脂押出発泡体から厚み50mm×幅910mm×長さ1820mmの発泡板を切り出し、さらに、厚み10mm×幅910mm×長さ約300mmの試験片30枚に切り出した。当該試験片の表面を目視し、以下の基準で異物を評価した。
○:φ2mm以上の異物(未発泡部)が観察されない
×:φ2mm以上の異物(未発泡部)が観察される
実施例及び比較例について、グラファイトは、以下の手法に従って作製したマスターバッチにより添加した。
バンバリーミキサーに、基材樹脂であるポリスチレン[PSジャパン(株)製、680;MFR7.0g/10分]100重量部、並びに、基材樹脂100重量部に対して、グラファイト[(株)丸豊鋳材製作所製、M-885]102重量部、及びエチレンビスステアリン酸アミド[日油(株)製、アルフローH-50S]2.0重量部を投入して、5kgf/cm2の荷重をかけた状態で加熱冷却を行わずに20分間溶融混練した。この際、樹脂温度を測定したところ190℃であった。ルーダーに供給して先端に取り付けられた小穴を有するダイスを通して吐出量250kg/hrで押し出されたストランド状の樹脂を30℃の水槽で冷却固化させた後、切断してマスターバッチを得た。
[樹脂混合物の作製]
表1に示す材料(発泡剤以外の材料)を、表1に示す配合にてドライブレンドして、樹脂混合物を得た。
得られた樹脂組成物を、口径150mmの単軸押出機(第一押出機)、口径200mmの単軸押出機(第二押出機)、及び冷却機を直列に連結した押出機へ、約600kg/hrで供給した。
表1に示す製造条件を変更した以外は、実施例1と同様の操作により、押出発泡体を得た。得られた押出発泡体の物性を表1に示す。
表2に示す製造条件を変更した(発泡剤を全て第一押出機の先端付近で圧入した)以外は、実施例1と同様の操作により、押出発泡体を得た。得られた押出発泡体の物性を表2に示す。
Claims (10)
- スチレン系樹脂を含有するスチレン系樹脂組成物の溶融物に発泡剤を添加し発泡性溶融物を調製する工程を有する、スチレン系樹脂押出発泡体の製造方法であって、
前記発泡剤が(A)塩化アルキル、並びに、(B)水および/またはアルコールを含有し、
前記(A)塩化アルキルと、前記(B)水および/またはアルコールとを分けて前記スチレン系樹脂に添加し溶融混練する工程を備え、
前記溶融混練する工程において、前記(A)塩化アルキルを前記溶融物に添加し、前記(A)塩化アルキルと前記溶融物が混合された後に前記(B)水および/またはアルコールを前記溶融物に添加する、スチレン系樹脂押出発泡体の製造方法。 - スチレン系樹脂100重量部に対して、前記(A)塩化アルキルを、2.0重量部以上7.0重量部以下、前記(B)水および/またはアルコールを、0.5重量部以上1.5重量部以下添加する、請求項1に記載のスチレン系樹脂押出発泡体の製造方法。
- 前記(A)塩化アルキルが塩化エチルを含み、前記(B)水および/またはアルコールが水を含む、請求項1または請求項2に記載のスチレン系樹脂押出発泡体の製造方法。
- 前記発泡剤が、さらに(C)ハイドロフルオロオレフィン及び/又はハイドロクロロフルオロオレフィンを含有する、請求項1~3のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
- スチレン系樹脂100重量部に対して、前記(C)ハイドロフルオロオレフィンおよび/またはハイドロクロロオレフィンを、2.0重量部以上13.0重量部以下添加する、請求項4に記載のスチレン系樹脂押出発泡体の製造方法。
- 前記スチレン系樹脂100重量%において、スチレン-アクリロニトリル共重合体が10重量%以上100重量%以下含有される、請求項1~5のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
- 前記スチレン系樹脂押出発泡体が、前記スチレン系樹脂100重量部に対して熱線輻射抑制剤を0.5重量部以上5.0重量部以下含有する、請求項1~6のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
- 前記スチレン系樹脂押出発泡体の熱伝導率が0.0244W/mK以下である、請求項1~7のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
- 前記スチレン系樹脂押出発泡体の密度が20~60kg/m3である、請求項1~8のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。
- 前記スチレン系樹脂押出発泡体の厚みが10mm以上150mm以下である、請求項1~9のいずれか一項に記載のスチレン系樹脂押出発泡体の製造方法。