JP7417082B2 - ポリオレフィン系樹脂用の結晶核剤組成物、及び該結晶核剤組成物を含むポリオレフィン系樹脂組成物 - Google Patents
ポリオレフィン系樹脂用の結晶核剤組成物、及び該結晶核剤組成物を含むポリオレフィン系樹脂組成物 Download PDFInfo
- Publication number
- JP7417082B2 JP7417082B2 JP2020038436A JP2020038436A JP7417082B2 JP 7417082 B2 JP7417082 B2 JP 7417082B2 JP 2020038436 A JP2020038436 A JP 2020038436A JP 2020038436 A JP2020038436 A JP 2020038436A JP 7417082 B2 JP7417082 B2 JP 7417082B2
- Authority
- JP
- Japan
- Prior art keywords
- bis
- ion
- polyolefin resin
- nucleating agent
- crystal nucleating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明のポリオレフィン系樹脂用結晶核剤組成物は、(A)特定の構造の脂環式ジカルボン酸の金属塩と(B)特定の構造のジアセタール化合物を含んでなることを特徴とする。なお、該結晶核剤組成物には、本発明の効果を損なわない範囲で、本発明に係る結晶核剤成分である成分(A)及び成分(B)以外のその他の結晶核剤や一般的にポリオレフィン系樹脂に使われている各種添加剤を含有していても良い。その場合、結晶核剤中に占める本発明の結晶核剤成分である成分(A)及び成分(B)の含有量は、結晶核剤組成物全体を100質量%とした場合に、成分(A)と成分(B)の合計量で70質量%以上、好ましくは80質量%以上、より好ましくは90質量%以上、特に好ましくは95質量%以上であることが推奨される。
本発明の脂環式ジカルボン酸の金属塩は、下記一般式(1)又は一般式(2)で示される脂環式ジカルボン酸の金属塩であることを特徴とする。
本発明のジアセタール化合物は、下記一般式(3)で示されるジアセタール化合物であることを特徴とする。
-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-メトキシベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(p-メトキシカルボニルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-フルオロベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’-ブロモ-4’-エチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-ベンジリデン-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-メチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-エチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-メトキシベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-メトキシカルボニルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-エトキシカルボニルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-プロポキシカルボニルベンジリデン)-1-n-プロピルソルビトール、1,3-O-(p-n-プロピルベンジリデン)-2,4-O-(p-プロポキシベンジリデン)-1-n-プロピルソルビトール、1,3-O-(p-プロポキシベンジリデン)-2,4-O-(p-n-プロピルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-フルオロベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’-ブロモ-4’-エチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-プロペニルソルビトール、1,3:2,4-ビス-O-(p-エトキシカルボニルベンジリデン)-1-プロペニルソルビトール、1,3:2,4-ビス-O-(p-プロポキシカルボニルベンジリデン)-1-プロペニルソルビトール、1,3-O-(p-n-プロピルベンジリデン)-2,4-O-(p-プロポキシベンジリデン)-1-プロペニルソルビトール、1,3-O-(p-プロポキシベンジリデン)-2,4-O-(p-n-プロピルベンジリデン)-1-プロペニルソルビトール、1,3:2,4-ビス-O-ベンジリデン-1-アリルソルビトール、1,3:2,4-ビス-O-(p-メチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-エチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-エトキシカルボニルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-プロポキシカルボニルベンジリデン)-1-アリルソルビトール、1,3-O-(p-n-プロピルベンジリデン)-2,4-O-(p-プロポキシベンジリデン)-1-アリルソルビトール、1,3-O-(p-プロポキシベンジリデン)-2,4-O-(p-n-プロピルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-メトキシベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-メトキシカルボニルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-フルオロベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’-ブロモ-4’-エチルベンジリデン)-1-アリルソルビトール等。
本発明のポリオレフィン系樹脂組成物は、本発明に係る上記ポリオレフィン系樹脂用の結晶核剤組成物とポリオレフィン系樹脂とを、必要に応じてその他のポリオレフィン系樹脂用添加剤を加えて、室温にてドライブレンド後、所定の条件にて溶融混合することにより、容易に得ることができる。
上記ポリオレフィン系樹脂としては、本発明の効果を奏する限り特に限定されることなく、従来公知のポリオレフィン系樹脂が使用可能であり、例えば、ポリエチレン系樹脂、ポリプロピレン系樹脂、ポリブテン系樹脂、ポリメチルペンテン系樹脂、ポリブタジエン系樹脂などが例示される。より具体的には、高密度ポリエチレン、中密度ポリエチレン、直鎖状ポリエチレン、エチレン含量50質量%以上、好ましくは70質量%以上のエチレンコポリマー、プロピレンホモポリマー、プロピレン50質量%以上、好ましくは70質量%以上のプロピレンコポリマー、ブテンホモポリマー、ブテン含量50質量%以上、好ましくは70質量%以上のブテンコポリマー、メチルペンテンホモポリマー、メチルペンテン含量50質量%以上、好ましくは70質量%以上のメチルペンテンコポリマー、ポリブタジエン等が例示される。また、上記コポリマーはランダムコポリマーであってもよく、ブロックコポリマーであってもよい。更に、これらの樹脂の立体規則性がある場合は、アイソタクチックでもシンジオタクチックでもよい。上記コポリマーを構成し得るコモノマーとして、具体的にはエチレン、プロピレン、ブテン、ペンテン、ヘキセン、ヘプテン、オクテン、ノネン、デセン、ウンデセン、ドデセン等の炭素数2~12のα-オレフィン、1,4-エンドメチレンシクロヘキセン等のビシクロ型モノマー、(メタ)アクリル酸メチル、(メタ)アクリル酸エチル等の(メタ)アクリル酸エステル、酢酸ビニル等が例示される。
また、上述の通り、本発明のポリオレフィン系樹脂組成物には、その使用目的やその用途に応じて、本発明の効果を損なわない範囲でその他のポリオレフィン系樹脂用添加剤が含まれていてもよい。
本発明のポリオレフィン系樹脂成形体は、上記本発明のポリオレフィン系樹脂組成物を用いて、慣用されている成形方法に従って成形することにより得られる。前記成形方法としては、本発明の効果を奏する限り、特に制約はなく、射出成形、押出成形、ブロー成形、圧空成形、回転成形、フィルム成形等の従来公知の成形方法のいずれも採用できる。
(1)結晶化温度
示差走査熱量分析装置(パーキンエルマー社製、DSC8500)を用い、JISK7121(1987)に従って測定した。評価用試料には、各実施例・比較例のポリオレフィン樹脂組成物約6mgを使用した。その試料を装置にセットし、200℃で3分間保持した後、10℃/分の冷却速度で冷却し、吸熱ピークの頂点を結晶化温度(℃)とした。
示差走査熱量分析装置(同社製)を用い、JISK7121(1987)に従って測定した。評価用試料には、各実施例・比較例のポリオレフィン樹脂組成物約6mgを使用した。その試料を装置にセットし、200℃で3分間保持した後、750℃/分の冷却速度で140℃まで冷却し、その温度において等温結晶化を行った。等温結晶化工程開始から、時間と熱量との関係図において認められる結晶化に基づく発熱ピークの面積の 1/2 に到達するまでの所要時間を半結晶化時間(T1/2、秒)とした。
(3)曇り度(ヘイズ値)
日本電色工業(株)のヘイズメータ(NDH 7000)を用いて、JISK7136(2000)に準じた方法でヘイズ値(%)を測定した。評価試料には、0.5mm厚み射出成形品のオレフィン系樹脂成形体を使用した。得られたヘイズ値の数値が小さい程、透明性に優れていることを示す。
万能材料試験機(インストロン社製)を用い、JISK7171(2016)に準じた方法で曲げ弾性率を測定した。なお、試験温度は25℃、試験速度は10mm/分とした。
化合物1:4-メチルシクロヘキサンジカルボン酸のカルシウム塩(MH-Ca)、アルキル置換基とオキシカルボニル基の立体構造;シス体比率95%
化合物2:4-t-ブチルシクロヘキサンジカルボン酸のカルシウム塩(tBuH-Ca)、アルキル置換基とオキシカルボニル基の立体構造;シス体比率100%
化合物3:4-シクロヘキセンジカルボン酸のヒドロキシアルミニウム塩(TH-AlOH)、2つのオキシカルボニル基の立体構造;シス体比率100%
化合物4:シクロヘキサンジカルボン酸のカルシウム塩(HH-Ca)、
化合物5:1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトール(新日本理化(株)製、商品名「ゲルオールMD」)
化合物6:1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール(新日本理化(株)製、商品名「ゲルオールDXR」)
化合物7:1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-プロピルソルビトール(ミリケン社製、商品名「ミラッドNX8000」
「化合物1」1gと「化合物5」10gをミキサーに投入し、室温で均一にドライブレンドし、結晶核剤組成物を調製した。
「化合物1」の量を3gに変えた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物1」の量を5gに変えた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物1」の量を10gに変えた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物5」の量を5gに変えた以外は実施例4と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物5」の量を3gに変えた以外は実施例4と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物5」の量を1gに変えた以外は実施例4と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物5」を「化合物6」に変えた以外は実施例4と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物5」を「化合物7」に変えた以外は実施例4と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物1」を「化合物2」に変えた以外は実施例4と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
「化合物1」を「化合物3」に変えた以外は実施例4と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表1に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表1に示した。
本発明の結晶核剤組成物を用いずに、結晶核剤として「化合物1」10gを用いた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表2に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表2に示した。
本発明の結晶核剤組成物を用いずに、結晶核剤として「化合物2」10gを用いた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表2に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表2に示した。
本発明の結晶核剤組成物を用いずに、結晶核剤として「化合物3」10gを用いた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表2に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表2に示した。
本発明に係る「化合物1」を本発明の範囲外の「化合物4」に変えた以外は実施例4と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表2に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表2に示した。
本発明の結晶核剤組成物を用いずに、結晶核剤として「化合物5」10gを用いた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表2に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表2に示した。
本発明の結晶核剤組成物を用いずに、結晶核剤として「化合物6」10gを用いた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表2に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表2に示した。
本発明の結晶核剤組成物を用いずに、結晶核剤として「化合物7」10gを用いた以外は実施例1と同様に実施して、結晶核剤組成物、ポリオレフィン系樹脂組成物を調製した。得られたポリオレフィン系樹脂組成物の結晶化温度及び半結晶化時間を測定し、得られた結果を合わせて表2に示した。
続いて、得られたポリオレフィン系樹脂組成物を用いて、実施例1と同様に実施して、本発明のポリオレフィン系樹脂成形体(試験片)を得た。得られた試験片の曲げ弾性率及びヘイズ値を測定し、得られた結果を合わせて表2に示した。
Claims (10)
- (A)脂環式ジカルボン酸の金属塩と(B)ジアセタール化合物を含んでなるポリオレフィン系樹脂用の結晶核剤組成物であって、
成分(A)が、下記一般式(1)又は下記一般式(2)で示される脂環式ジカルボン酸の金属塩であり、
且つ、
成分(B)が、下記一般式(3)で示されるジアセタール化合物であることを特徴とするポリオレフィン系樹脂用の結晶核剤組成物。
- 成分(A)と成分(B)の比率(質量比)が、5/95~95/5の範囲である、請求項1に記載の結晶核剤組成物。
- 前項における一般式(1)中のR1が、メチル基又はtert-ブチル基であり、aが1又は2であり、更に、その置換位置が3位又は4位である、請求項3に記載の結晶核剤組成物。
- 核磁気共鳴分光分析で測定したシクロヘキサン環を介したR1基と金属塩を構成するオキシカルボニル基の立体異性体中、シス異性体の比率(モル比)が、70%以上である請求項3又は4に記載の結晶核剤組成物。
- 前項における一般式(2)中の2つのオキシカルボニル基が、シス配置である、請求項6に記載の結晶核剤組成物。
- M2がヒドロキシアルミニウムイオンである、請求項6又は7に記載の結晶核剤組成物。
- 請求項1~8の何れかに記載されたポリオレフィン系樹脂用の結晶核剤組成物を含むことを特徴とするポリオレフィン系樹脂組成物。
- 請求項9に記載されたポリオレフィン系樹脂組成物を原料とするポリオレフィン系樹脂成形体。