JP7361016B2 - 流動性ろう付け組成物及びそれを使用して金属物品を一緒にろう付けする方法 - Google Patents
流動性ろう付け組成物及びそれを使用して金属物品を一緒にろう付けする方法 Download PDFInfo
- Publication number
- JP7361016B2 JP7361016B2 JP2020505770A JP2020505770A JP7361016B2 JP 7361016 B2 JP7361016 B2 JP 7361016B2 JP 2020505770 A JP2020505770 A JP 2020505770A JP 2020505770 A JP2020505770 A JP 2020505770A JP 7361016 B2 JP7361016 B2 JP 7361016B2
- Authority
- JP
- Japan
- Prior art keywords
- flux
- brazing
- composition
- flowable
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本出願は、2017年8月7日出願の米国仮出願第62/542,158号の利益を主張し、更に2018年8月2日出願の米国出願第16/053,635号の利益を主張する。
技術分野は、概して、流動性ろう付け組成物及びそれを使用して金属物品を一緒にろう付けする方法に関し、より詳細には、優れた貯蔵安定性を呈する流動性ろう付け組成物及び流動性ろう付け組成物を使用して金属物品を一緒にろう付けする方法に関する。
米国特許第5,226,974号に開示の組成物によるろう付け組成物を、列挙された重量百分率で以下の成分を使用して調製した。
39.17重量%のアルミニウム-ケイ素合金粉末、
29.17重量%のフラックス粉末(少なくとも約97%の純度を有するHoneywell KAlF4 fine、物品番号01740)、
25.83重量%のプロピレングリコール、
5.84重量%のグリセリン。
ろう付け後フラックス残留物を低減する目的で、2の合金対フラックス比を有するこの配合の組成物を用いて、ろう付け組成物の別の比較例を調製した。比較例3は、列挙された重量百分率で以下の成分を使用して調製した。
44.83重量%のアルミニウム-ケイ素合金粉末、
22.41重量%のフラックス粉末(少なくとも約97%の純度を有するHoneywell KAlF4 fine、物品番号01740)、
26,72重量%のプロピレングリコール、
6.03重量%のグリセリン。
百分率が重量による、フラックスコーティングアルミニウム-ケイ素合金粉末及び以下の成分を使用して、3の合金対フラックス比を有する流動性ろう付け組成物を調製した。
75%のアルミニウムケイ素及び25%のHoneywell KAlF4 fineで調製され、1000μmの標準ふるいを少なくとも通過するのに十分に小さい微粒子径を有し、ふるい上に5%未満が残留する、67.44重量%のフラックス融解コーティングアルミニウム-ケイ素合金粉末、
15重量%のプロピレングリコール、
15重量%の2-メチル-2,4-ペンタンジオール(ヘキシレングリコール)。
百分率が重量による、フラックスコーティングアルミニウム-ケイ素合金粉末及び以下の成分を使用して、2.55の合金対フラックス比を有する流動性ろう付け組成物を調製した。
75%のアルミニウムケイ素及び25%のHoneywell KAlF4 fineで調製され、1000μmの標準ふるいを少なくとも通過するのに十分に小さい微粒子径を有し、ふるい上に5%未満が残留する、68.18重量%のフラックス融解コーティングアルミニウム-ケイ素合金粉末、
3.03重量%のフラックス粉末(少なくとも約97%の純度を有するHoneywell KAlF4 fine、物品番号01740)、
25.91重量%のプロピレングリコール、
2.88重量%の2-メチル-2,4-ペンタンジオール(ヘキシレングリコール)。
百分率が重量による、フラックスコーティングアルミニウム-ケイ素合金粉末及び以下の成分を使用して、2.33の合金対フラックス比を有する流動性ろう付け組成物を調製した。
75%のアルミニウムケイ素及び25%のHoneywell KAlF4 fineで調製され、1000μmの標準ふるいを少なくとも通過するのに十分に小さい微粒子径を有し、ふるい上に5%未満が残留する、59.72重量%のフラックス融解コーティングアルミニウム-ケイ素合金粉末、
4.27重量%のフラックス粉末(少なくとも約97%の純度を有するHoneywell KAlF4 fine、物品番号01740)、
28.82重量%のプロピレングリコール、
7.2重量%の2-メチル-2,4-ペンタンジオール(ヘキシレングリコール)。
百分率が重量による、フラックスコーティングアルミニウム-ケイ素合金粉末、及びろう付けプロセスに適合すると知られている増粘剤を次の成分と共に使用して、2.06の合金対フラックス比を有する流動性ろう付け組成物を調製した。
75%のアルミニウムケイ素及び25%のHoneywell KAlF4 fineで調製され、1000μmの標準ふるいを少なくとも通過するのに十分に小さい微粒子径を有し、ふるい上に5%未満が残留する、61.16重量%のフラックス融解コーティングアルミニウム-ケイ素合金粉末、
7.02重量%のフラックス粉末(少なくとも約97%の純度を有するHoneywell KAlF4 fine、物品番号01740)、
25.12重量%のプロピレングリコール、
6.28重量%の2-メチル-2,4-ペンタンジオール(ヘキシレングリコール)、
0.41パーセントのヒドロキシプロピルセルロース(増粘剤)。
Claims (4)
- 流動性ろう付け組成物であって、
非ポリマー性担体媒体であって、前記担体媒体が、少なくとも1つの極性有機溶剤を含み、周囲温度で液体である、非ポリマー性担体媒体と、
ろう材コア及び前記コア上に配置されているフラックスコーティングを含むフラックスコーティング粒子であって、前記ろう材コアが、前記フラックスコーティングとは異なる材料を含む、フラックスコーティング粒子と、を含み、
前記流動性ろう付け組成物が、前記流動性ろう付け組成物の総重量に基づいて、1.5重量%以下のポリマー性結合剤成分を有し、
前記組成物が、前記担体媒体中の前記フラックスコーティング粒子の安定な懸濁液であり、前記組成物が、35℃の温度で少なくとも25週間の期間にわたって目視可能な溶剤分離がない、
流動性ろう付け組成物。 - 前記ろう材コアが、Al-Si合金又はその前駆体を含み、前記フラックスコーティングが、金属ハロゲン化物又はその塩を含み、
前記少なくとも1つの極性有機溶剤が、ヘキシレングリコールを含み、
前記少なくとも1つの極性有機溶剤が、前記流動性ろう付け組成物の総重量に基づいて、少なくとも10重量%の量で存在し、
前記流動性ろう付け組成物が、前記フラックスコーティング粒子とは別個のフラックス粒子を更に含み、前記フラックス粒子が、前記流動性ろう付け組成物の総重量に基づいて、少なくとも3重量%の量で存在し、前記フラックス粒子のうちの少なくとも一部が、3乃至10の長さ対直径(L/D)比を有し、
前記ろう付け組成物が、検出可能な水を含まない、請求項1に記載の流動性ろう付け組成物。 - 前記フラックスコーティングが金属ハロゲン化物又はその塩を含む、請求項1に記載の流動性ろう付け組成物。
- 前記少なくとも1つの極性有機溶剤はC2-C10脂肪族グリコールを含む、請求項1に記載の流動性ろう付け組成物。