JP7105302B2 - 平鋼製品およびその製造方法 - Google Patents
平鋼製品およびその製造方法 Download PDFInfo
- Publication number
- JP7105302B2 JP7105302B2 JP2020517460A JP2020517460A JP7105302B2 JP 7105302 B2 JP7105302 B2 JP 7105302B2 JP 2020517460 A JP2020517460 A JP 2020517460A JP 2020517460 A JP2020517460 A JP 2020517460A JP 7105302 B2 JP7105302 B2 JP 7105302B2
- Authority
- JP
- Japan
- Prior art keywords
- flat steel
- martensite
- flat
- temperature
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
0.1~0.5%のC、
1.0~3.0%のMn、
0.5~2.0%のSi、
0.01~1.5%のAl、
0.001~0.008%のN、
最大0.02%のP、
最大0.005%のS
ならびに任意に次の元素の1つまたは複数:
0.01~1.0%のCr、
0.01~0.2%のMo、
0.001~0.01%のB
ならびに任意に合計で0.005~0.2%のV、TiおよびNb(ここで、Ti割合は0.10%以下である)、および残部として鉄と不可避的不純物からなる鋼からなり、ここで、平鋼製品は、
15面積%以下のフェライト、
5面積%以下のベイナイト、
少なくとも5体積%の残留オーステナイトおよび
少なくとも80面積%のマルテンサイトであって、そのうち少なくとも75面積%が焼戻しマルテンサイトであるマルテンサイト
からなる組織を有する。
%Si+0.5*%Al≧0.9重量%
式中
%Si:重量%での鋼のそれぞれのSi含有量
%Al:重量%での鋼のそれぞれのAl含有量。
a)鉄と不可避的不純物の他に、(重量%で)0.1~0.5%のC、1.0~3.0%のMn、0.5~2.0%のSi、0.01~1.5%のAl、0.001~0.008%のN、最大0.02%のP、最大0.005%のSならびに任意に次の元素の1つまたは複数:0.01~1.0%のCr、0.01~0.2%のMo、0.001~0.01%のBならびに任意に合計で0.005~0.2%のV、TiおよびNbからなる鋼からなり、ここで、Ti含有量は0.10%以下である、熱間圧延平鋼製品を準備する工程;
b)熱間圧延平鋼製品を酸洗する工程;
c)少なくとも37%の冷間圧延率で平鋼製品を冷間圧延する工程;
d)冷間圧延平鋼製品を、鋼のA3温度よりも高く、最大でも950℃である保持ゾーン温度THZに加熱し、ここで、5~50K/秒の加熱速度θH1で200~400℃の変態点温度TWまで加熱し、2~10K/秒の加熱速度θH2で変態点温度TWよりも高い温度に加熱する工程;
e)平鋼製品を保持ゾーン温度THZで5~15秒間保持する工程;
f)任意に、平鋼製品を、保持ゾーン温度THZから少なくとも620℃かつ最大でも720℃の中間温度TLKに30~300秒以内に冷却する工程;
g)平鋼製品を平均5K/秒を超える冷却速度θQで、マルテンサイト開始温度TMSとTMSよりも最大175℃低い温度との間にある冷却停止温度TABに冷却する工程;
h)平鋼製品を冷却停止温度TABで10~60秒間保持する工程;
i)平鋼製品を1~80K/秒の加熱速度θB1で350~500℃の処理温度TBに加熱し、任意に平鋼製品を処理温度TBに等温保持し、ここで、加熱と任意の等温保持の時間が合わせて10~1000秒である工程;
j)平鋼製品を5K/秒超500K/秒未満の冷却速度θB2で室温に冷却する工程;
k)任意に、平鋼製品を溶融浴で
k1)作業工程j)での冷却前に溶融浸漬コーティングによりコーティングする工程、
または
k2)作業工程j)での冷却後に電解コーティングによりコーティングする工程。
KWG=(h0-h1)/h0
式中、h0は冷間圧延前の平鋼製品の厚み(mm)であり、h1は冷間圧延後の平鋼製品の厚み(mm)である。平鋼製品が、酸洗後かつ作業工程d)での加熱前に複数の冷間圧延プロセスまたは冷間圧延工程を経る場合、KWGは総冷間圧延率に基づいており、すなわち、h0は最初の冷間圧延プロセス前または冷間圧延工程前の平鋼製品の厚み(mm)であり、h1は最後の冷間圧延プロセス後または冷間圧延工程後の平鋼製品の厚み(mm)である。少なくとも37%のKWGでの冷間圧延によって、機械的均質化だけでなく、粒度の減少ひいては細粒組織も設定される。高度の冷間圧延率ならびに析出プロセスおよびその結果生じる焼鈍前の微細な初期組織に基づき、冷却前に非常に細粒のオーステナイト組織が早くも存在することになる。この場合、結晶粒界は、マルテンサイトラスの成長に対する障害として機能し、微細組織における結晶粒界間の距離が短ければ、より短くてより狭いラスがもたらされる。急冷すると、残留オーステナイトが間に埋め込まれた超微細なマルテンサイトラスの組織が形成される。これにより、その後の処理工程では拡散経路が短くなり、そうして残留オーステナイトの局所安定化が可能になる。
A3[℃]=910-203*√%C-15.2%Ni+44.7%Si+31.5%Mo-21.1%Mn
式中、%C=重量%での鋼のC含有量、%Ni=重量%での鋼のNi含有量、%Si=重量%での鋼のSi含有量、%Mo=重量%での鋼のMo含有量、%Mn=重量%での鋼のMn含有量。
TMS[℃]=539℃+(-423%C-30.4%Mn-7.5%Si+30%Al)℃/重量%
式中、%C=重量%での鋼のC含有量、%Mn=重量%での鋼のMn含有量、%Si=重量%での鋼のSi含有量、%Al=重量%での鋼のAl含有量。
Claims (15)
- 焼付硬化処理に適した高強度の平鋼製品であって、(重量%で)
C:0.1~0.5%、
Si:0.5~2.0%、
Mn:1.0~3.0%、
Al:0.01~1.5%、
N:0.001~0.008%、
P:0.02%以下、
S:0.005%以下
ならびに任意に次の元素の1つまたは複数:
Cr:0.01~1.0%、
Mo:0.01~0.2%、
B:0.001~0.01%
ならびに任意に合計で0.005~0.2%のV、TiおよびNb(ここで、Ti割合は0.10%以下である)
を含み、残部が鉄と不可避的不純物である鋼からなり、
ここで、前記平鋼製品は、その組織全体が、
15面積%以下のフェライト、
5面積%以下のベイナイト、
少なくとも5体積%の残留オーステナイトおよび
少なくとも80面積%のマルテンサイトであって、そのうち少なくとも75面積%が焼戻しマルテンサイトであるマルテンサイト
からなり、
ここで、前記組織内のマルテンサイトの総割合に関して、前記マルテンサイトの少なくとも90%が、最大でも7.5μmのマルテンサイトラス長さと、最大でも1000nmのマルテンサイトラス幅とを有するラスマルテンサイトである、平鋼製品。 - 炭素含有量が少なくとも0.14重量%であることを特徴とする、請求項1に記載の平鋼製品。
- Si含有量とAl含有量の半分との合計が少なくとも0.9重量%であることを特徴とする、請求項1または2に記載の平鋼製品。
- Si含有量が少なくとも0.5重量%であることを特徴とする、請求項1から3のいずれか一項に記載の平鋼製品。
- Si含有量が少なくとも0.9重量%であることを特徴とする、請求項1から4のいずれか一項に記載の平鋼製品。
- 前記平鋼製品の前記鋼のAl含有量が少なくとも0.02重量%であることを特徴とする、請求項1から5のいずれか一項に記載の平鋼製品。
- 前記平鋼製品の前記鋼のAl含有量が最大でも0.2重量%であることを特徴とする、請求項1から6のいずれか一項に記載の平鋼製品。
- 700MPaを超える耐力Rp0.2または700MPaを超える降伏点ReH、950~1500MPaの引張強度Rm、7~25%の伸び率A80、ならびに2%の予変形およびDIN EN 10325:2006に従った170℃で20分間の焼戻し後に決定される、少なくとも80MPaのBH2値を有することを特徴とする、請求項1から7のいずれか一項に記載の平鋼製品。
- 少なくとも片側に亜鉛系腐食防止コーティングが設けられていることを特徴とする、請求項1から8のいずれか一項に記載の平鋼製品。
- 請求項1から9のいずれか一項に記載の焼付硬化処理に適した高強度の平鋼製品を製造するための方法であって、次の作業工程:
a)(重量%で)0.1~0.5%のC、1.0~3.0%のMn、0.5~2.0%のSi、0.01~1.5%のAl、0.001~0.008%のN、最大0.02%のP、最大0.005%のSならびに任意に次の元素の1つまたは複数:0.01~1.0%のCr、0.01~0.2%のMo、0.001~0.01%のBならびに任意に合計で0.005~0.2%のV、TiおよびNb(ここで、Ti含有量は0.10%以下である)を含み、残部が鉄と不可避的不純物である鋼からなる、熱間圧延平鋼製品を準備する工程;
b)前記熱間圧延平鋼製品を酸洗する工程;
c)少なくとも37%の冷間圧延率で前記平鋼製品を冷間圧延する工程;
d)冷間圧延平鋼製品を、前記鋼のA3温度よりも高く、最大でも950℃である保持ゾーン温度THZに加熱し、ここで、5~50K/秒の加熱速度θH1で200~400℃の変態点温度TWまで加熱し、2~10K/秒の加熱速度θH2で変態点温度TWよりも高い温度に加熱する工程;
e)前記平鋼製品を前記保持ゾーン温度THZで5~15秒間保持する工程;
f)任意に、前記平鋼製品を、前記保持ゾーン温度THZから少なくとも620℃かつ最大でも720℃の中間温度TLKに30~300秒以内に冷却する工程;
g)前記平鋼製品を平均5K/秒を超える冷却速度θQで、マルテンサイト開始温度TMSとTMSよりも最大175℃低い温度との間にある冷却停止温度TABに冷却する工程;
h)前記平鋼製品を前記冷却停止温度TABで10~60秒間保持する工程;
i)前記平鋼製品を1~80K/秒の加熱速度θB1で350~500℃の処理温度TBに加熱し、任意に前記平鋼製品を前記処理温度TBに等温保持し、ここで、前記加熱と任意の等温保持の時間が合わせて10~1000秒である工程;
j)前記平鋼製品を5K/秒超500K/秒未満の冷却速度θB2で室温に冷却する工程;
k)任意に、前記平鋼製品を溶融浴で
k1)作業工程j)での冷却前に溶融浸漬コーティングによりコーティングする工程、
または
k2)作業工程j)での冷却後に電解コーティングによりコーティングする工程
を含む、方法。 - 作業工程c)での前記冷間圧延率が少なくとも42%であることを特徴とする、請求項10に記載の方法。
- 前記平鋼製品が、作業工程k)で亜鉛系溶融浴を通過することを特徴とする、請求項10または11に記載の方法。
- 作業工程k)での溶融浴組成物が、1~2重量%のAl、1~2重量%のMg、残部の亜鉛と不可避的不純物からなることを特徴とする、請求項12に記載の方法。
- 作業工程k)での任意のコーティング処理が連続フローで行われることを特徴とする、請求項10から13のいずれか一項に記載の方法。
- 作業工程j)での前記冷却速度θB2が20K/秒を超えることを特徴とする、請求項10から14のいずれか一項に記載の方法。