JP6963666B2 - 排ガス浄化用組成物及びそれを含む排ガス浄化用触媒並びに排ガス浄化用触媒構造体 - Google Patents
排ガス浄化用組成物及びそれを含む排ガス浄化用触媒並びに排ガス浄化用触媒構造体 Download PDFInfo
- Publication number
- JP6963666B2 JP6963666B2 JP2020169018A JP2020169018A JP6963666B2 JP 6963666 B2 JP6963666 B2 JP 6963666B2 JP 2020169018 A JP2020169018 A JP 2020169018A JP 2020169018 A JP2020169018 A JP 2020169018A JP 6963666 B2 JP6963666 B2 JP 6963666B2
- Authority
- JP
- Japan
- Prior art keywords
- alumina
- exhaust gas
- gas purification
- mass
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ランタンの含有量が、第二アルミナよりも第一アルミナの方が高く、
粒径が、第一アルミナよりも第二アルミナの方が大きい、排ガス浄化用組成物を提供することによって、前記の課題を解決したものである。
更に、このように粒径の異なる2種のアルミナを用いることで、大きなアルミナ粒子の隙間に小さなアルミナ粒子が入り込み、大きなアルミナ粒子どうしだけでなく、小さなアルミナ粒子どうしの凝集も抑制することが可能となり、単純にアルミナをランタン修飾することで得られる熱的安定性以上の熱的安定性を確保することができる。
一方、第二アルミナに関しては、L2の値は、L1の値よりも小さいことを条件として、耐熱性とコストとのバランスの観点から、第二アルミナ中9質量%以下であることが好ましく、1質量%以上9質量%以下であることが更に好ましく、1質量%以上5質量%以下であることが一層好ましい。
一方、第二アルミナに関しては、D2の値は、D1の値よりも大きいことを条件として、耐熱性とコストとのバランスの観点から、20μm以上60μm以下であることが好ましく、20μm以上50μm以下であることが更に好ましく、20μm以上40μm以下であることが一層好ましい。なお、ランタンは、その含有量が少ないことから、ランタンを含有させる前後でのアルミナの粒径に実質的な違いはない。
一方、第一アルミナと第二アルミナとの合計の質量に対する第二アルミナの質量の割合は、20質量%以上80質量%以下であることが好ましく、30質量%以上70質量%以下であることが更に好ましく、30質量%以上50質量%以下であることが一層好ましい。
一方、本発明の排ガス浄化用組成物は、そのBET比表面積が、熱に曝された後の状態において、60m2/g以上150m2/g以下であることが好ましく、70m2/g以上120m2/g以下であることが更に好ましく、80m2/g以上100m2/g以下であることが一層好ましい。熱に曝された後の状態とは、10体積%の水を含む空気中で1100℃において4時間加熱処理を受けた状態のことである。BET比表面積がこのような値を有することで、本発明の排ガス浄化用組成物は、耐熱性が高く、しかもNOxの吸着性が向上したものとなる。このようなBET比表面積を達成するためには、例えば第一アルミナ及び第二アルミナの粒径を適切に調整したり、第一アルミナと第二アルミナとの混合比率を適切に調整したりすればよい。BET比表面積は、BET1点法で測定される。
また、OSC材の量は、耐熱性、NOx吸着性及びOSC発揮の観点から、排ガス浄化用触媒中に5質量%以上30質量%以下であることが好ましく、5質量%以上20質量%以下であることが一層好ましい。
本発明の排ガス浄化用触媒構造体を製造するには、例えば、前記のスラリーを、触媒支持体に塗布し、乾燥させ、焼成する方法が挙げられる。焼成は大気雰囲気下で450℃以上600℃以下の温度で、1時間以上3時間以下の時間にわたり行うことが好ましい。
また、本発明の排ガス浄化用触媒構造体は、タンデム型構造とすることができる。例えば、2つの触媒支持体を用意し、これらを排ガス流動方向に沿って直列に配置し、排ガスの流動方向上流側の触媒支持体の表面に上流側触媒層を形成し、下流側の触媒支持体の表面に下流側触媒層を形成した構成とし、この上流側触媒層又は下流側触媒層のいずれか一方又は両方に本発明の排ガス浄化用触媒を含有させることもできる。
一方で、下流側触媒層はエンジンからより遠くに位置するのでエンジンの熱が伝わりにくい環境となるところ、本発明の排ガス浄化用組成物によればNOx吸着性に優れるので、該組成物を含む排ガス浄化用触媒を下流側触媒層に適用した場合であっても、エンジン始動直後の低温環境下におけるNOx吸着性が従来と比較して優れたものとなる。
まず予備実験として、アルミナの粒径と、ランタンの含有量とが、耐熱性にどのように影響を及ぼすかを調べた。
フェレ径が8μmの球状γ−アルミナ粒子の粉体と、硝酸ランタンとを水に分散させてスラリーを得、このスラリーを蒸発乾固させた。次いで、残った固形分を600℃で3時間にわたり熱処理することによって、酸化ランタンで修飾された第一アルミナを得た。第一アルミナのフェレ径は8μmであった。この酸化ランタンの修飾量L1を種々変更することで、8種類の第一アルミナを調製した。
また、フェレ径が35μmの球状θ−アルミナ粒子の粉体と、硝酸ランタンとを水に分散させてスラリーを得、このスラリーを蒸発乾固させた。次いで、残った固形分を600℃で3時間にわたり熱処理することによって、酸化ランタンで修飾された第二アルミナを得た。第二アルミナのフェレ径は35μmであった。この酸化ランタンの修飾量L2を種々変更することで、8種類の第二アルミナを調製した。
このようにして得られた種々の第一アルミナ及び第二アルミナについて、製造直後のBET比表面積(S1)、及び1100℃で4時間加熱後(雰囲気は10vol%の水を含む空気)のBET比表面積(S2)を、それぞれ上述した方法で測定した。そして、S2/S1×100からBET比表面積の保持率を算出した。その結果を図1に示す。BET比表面積の保持率の値が大きいほど、耐熱性が高いと評価される。同図に示す結果から明らかなとおり、第一アルミナについては、酸化ランタンの修飾量が2〜12%の範囲において高い耐熱性が得られることが判る。第二アルミナについては、酸化ランタンの修飾量が9%以下の範囲において高い耐熱性が得られることが判る。
(1)第一アルミナ及び第二アルミナの用意
第一アルミナは上述の予備実験で作製した酸化ランタンの修飾量L1がアルミナと酸化ランタンの合計質量中9%のものを用意した。フェレ径は8μmである。一方、第二アルミナは酸化ランタンの修飾量L2がアルミナと酸化ランタンの合計質量中1%のものを用意した。フェレ径は35μmである。なお、第一アルミナ及び第二アルミナのフェレ径は、上述したSEMによって測定された値である。
第一アルミナ70部と第二アルミナ30部とを混合して排ガス浄化用組成物を得た。この組成物のBET比表面積(熱に曝される前)は133.3m2/gであった。
実施例1の(2)において、第一アルミナ50部と第二アルミナ50部とを混合して排ガス浄化用組成物を得た。これ以外は実施例1と同様とした。この組成物のBET比表面積(熱に曝される前)は136.0m2/gであった。
実施例1の(2)において、第一アルミナ30部と第二アルミナ70部とを混合して排ガス浄化用組成物を得た。これ以外は実施例1と同様とした。この組成物のBET比表面積(熱に曝される前)は143.2m2/gであった。
実施例1の(2)において、第二アルミナを用いなかった。これ以外は実施例1と同様とした。
実施例1の(2)において、第一アルミナを用いなかった。これ以外は実施例1と同様とした。
実施例2の(1)において、酸化ランタンを修飾していない第一アルミナを用意した。これ以外は実施例2と同様とした。
実施例2の(1)において、酸化ランタンを修飾していない第二アルミナを用意した。これ以外は実施例2と同様とした。
実施例2の(1)において、酸化ランタンの修飾量L1が1%の第一アルミナと、酸化ランタンの修飾量L2が9%の第二アルミナを用意した。これ以外は実施例2と同様とした。
実施例1−3及び比較例1−5で得られた排ガス浄化用組成物について、以下の耐熱性評価及びNOx吸着性評価を行った。その結果を図2、図3及び表1に示す。
製造直後の排ガス浄化用組成物のBET比表面積(SSA1)、及び1100℃で4時間加熱後(雰囲気は10体積%の水を含む空気)の排ガス浄化用組成物のBET比表面積(SSA2)を、それぞれ上述した方法で測定した。そして、SSA2/SSA1×100からBET比表面積の保持率を算出した。
1100℃で4時間加熱後(雰囲気は10体積%の水を含む空気)の排ガス浄化用組成物について、50℃でのNOxの吸着量をTPDによって測定した。TPDによって得られた面積値を吸着量とみなした。
TPDの測定条件としては、前処理として、He40mL/min、O210mL/minで600℃まで30分で昇温し、そのまま600℃で30分保持し、その後50℃まで10分で冷却した。次に、He50mL/minで10分保持した。次いで、He30mL/min、O210mL/min、NO(2%)+N2(98%)10mL/minで60分保持してNOxを吸着させた。その後、He50mL/minで5分保持した。TPDの測定は、He50mL/minで10℃/minにて50℃から650℃まで昇温させて行った。表1及び図2に示す相対値は比較例2を1とした場合の値である。
(3)排ガス浄化用触媒の調製
硝酸パラジウムと硝酸ロジウムが溶解した水溶液に、実施例1で製造した排ガス浄化用組成物及び、OSC材を加えて攪拌して排ガス浄化用触媒のスラリーを得た。Pdの量は排ガス浄化用組成物100質量%に対して、0.5質量%であった。Rhの量は排ガス浄化用組成物100質量%に対して、0.1質量%であった。OSC材としては、CeO2−ZrO2複合酸化物を用いた。排ガス浄化用組成物とOSC材との質量比は前者:後者で7:1であった。
(4)排ガス浄化用触媒の触媒支持体への配置
前記で作製したスラリーをハニカム触媒支持体(日本ガイシ製、直径25mm、軸方向長さ30mm、セル数600cpsi、体積0.015L)の表面に塗布した後、過剰量のスラリーを吹き払った。次に70℃の熱風がスラリー塗布面に直接当たるようにして乾燥後、450℃で1時間焼成して硝酸根を除去し、触媒層がハニカム触媒支持体上に形成された排ガス浄化用触媒構造体を得た。触媒層の量は触媒支持体体積に対して250g/Lであった。
実施例4の(3)において、実施例1で製造した排ガス浄化用組成物に代えて、比較例1で製造した排ガス浄化用組成物を用いた。これ以外は実施例4と同様にして、排ガス浄化用触媒構造体を製造した。
実施例4の(3)において、実施例1で製造した排ガス浄化用組成物に代えて、比較例2で製造した排ガス浄化用組成物を用いた。これ以外は実施例4と同様にして、排ガス浄化用触媒構造体を製造した。
実施例4並びに比較例6及び7で得られた排ガス浄化用触媒構造体について、以下のNOxの浄化性能を評価した。その結果を表2に示す。
先ず、実施例4並びに比較例6及び7で得られた排ガス浄化用触媒構造体を、大気雰囲気下、1000℃で25時間加熱した。
加熱後の排ガス浄化用触媒構造体について、下記条件のNOxのT50の測定を行い、NOxの浄化性能を評価した。結果を表2に示す。
<T50測定条件>
排ガス浄化用触媒構造体をガス流通経路に配置し、下記組成の模擬排ガスを流通させた。排ガス浄化用触媒構造体に流入するガス温度を常温から漸次上昇させていき、触媒構造体を通過する前及び通過した後の排ガスに含まれるNOx量を求め、A:触媒構造体を通過前のNOx検出量、B:触媒構造体を通過後のNOx検出量としたときに、下記式にてNOx浄化率を求めた。
NOx浄化率(%)=(A−B)/A×100
NOx浄化率が50%に達したときに触媒構造体に流入するガス温度をライトオフ温度T50と定義して求めた。
・模擬排ガス(組成は体積基準):CO:0.5%、C3H6:1200ppmC、NO:500ppm、O2:0.50%、CO2:14%、H2O:10%、H2:0.17%、N2:残部
・触媒前段空燃比:A/F=14.6
・昇温速度:20℃/分
・HC、NOx、CO量の測定:評価装置として堀場製作所社製MOTOR EXHAUST GAS ANALYZER MEXA7100を用いて行った。
比較例1の排ガス浄化用組成物のNOx吸着量が実施例1の排ガス浄化用組成物より優れているにもかかわらず、それを用いた排ガス浄化用触媒である比較例6のNOx浄化性能が実施例4より劣っているのは、比表面積の維持率が劣っているためであると考えられる。
Claims (5)
- アルミナにランタンが含有されてなる第一アルミナと、アルミナにランタンが含有されてなる第二アルミナとを含む排ガス浄化用組成物であって、
ランタンの含有量が、第二アルミナよりも第一アルミナの方が高く、
粒径が、第一アルミナよりも第二アルミナの方が大きく、
第一アルミナがγ−アルミナであり、第二アルミナがθ−アルミナであり、
第一アルミナにおけるランタンの含有量L 1 は、第二アルミナにおけるランタンの含有量L 2 に対する比率で表して、2以上18以下である排ガス浄化用組成物。 - 第一アルミナの粒径に対する第二アルミナの粒径の比率が、1.5以上15以下である、請求項1に記載の排ガス浄化用組成物。
- 第一アルミナと第二アルミナとの合計の質量に対する第一アルミナの質量の割合が20質量%以上80質量%以下であり、第二アルミナの質量の割合が80質量%以下20質量%以上である請求項1又は2に記載の排ガス浄化用組成物。
- 請求項1ないし3のいずれか一項に記載の排ガス浄化用組成物と触媒活性成分を含む排ガス浄化用触媒。
- 触媒支持体と、該触媒支持体の表面に形成された第一触媒層と、第一触媒層における該触媒支持体とは反対側の表面に形成された第二触媒層とを有し、
請求項4に記載の排ガス浄化用触媒が、第一触媒層に含有されている排ガス浄化用触媒構造体。