JP6611707B2 - コージエライト対ムライトの比率が高いコージエライト・ムライト・チタン酸アルミニウムマグネシウム組成物およびそれから構成されたセラミック物品 - Google Patents
コージエライト対ムライトの比率が高いコージエライト・ムライト・チタン酸アルミニウムマグネシウム組成物およびそれから構成されたセラミック物品 Download PDFInfo
- Publication number
- JP6611707B2 JP6611707B2 JP2016515458A JP2016515458A JP6611707B2 JP 6611707 B2 JP6611707 B2 JP 6611707B2 JP 2016515458 A JP2016515458 A JP 2016515458A JP 2016515458 A JP2016515458 A JP 2016515458A JP 6611707 B2 JP6611707 B2 JP 6611707B2
- Authority
- JP
- Japan
- Prior art keywords
- cordierite
- mullite
- phase
- ceramic
- ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
コージエライトI比 i比=I(110)/[I(110)+I(002)]
コージエライト方位指数 Icor=I(100)/[I(100)+I(002)]
AT方位指数 IATI=I(230)/[I(230)+I(101)](重複)
IATII=I(200)/[I(200)+I(101)](重複)
IATI=I(002)/[I(002)+I(200)](重複少ない)
IATI=I(101)/[I(101)+I(200)](重複少ない)
Iは、丸括弧内のミラー指数のピーク強度である。
110 第1の端面
120 第2の端面
130 外周壁
140 通路
150 多孔質壁
160 表皮層
Claims (8)
- セラミック物品において、
主にAl2(1-x)MgxTi(1+x)O(ただし、0.16≦x≦0.23)またはAl2TiO5−MgTi2O5固溶体を含む擬板チタン石相と、
コージエライトを含む第二相と、
ムライトを含む第三相と、
を有してなり、
コージエライト/ムライトの質量比としての相比が0.9以上かつ7以下である、
セラミック物品。 - 前記コージエライト/ムライトの質量比としての相比が1.3以上である、請求項1記載のセラミック物品。
- 前記コージエライト/ムライトの質量比としての相比が2.5以下である、請求項2記載のセラミック物品。
- 40体積%超の全気孔率、および25〜800℃の間で測定して、14×10-7/K以下の熱膨張係数を有する、請求項1から3いずれか1項記載のセラミック物品。
- 54質量%から77質量%の前記擬板チタン石相、14質量%から24質量%の前記第二相、および3.37質量%から15.53質量%の前記第三相を含む、請求項1から4いずれか1項記載のセラミック物品。
- セラミック物品を製造する方法において、
マグネシア源、シリカ源、アルミナ源、チタニア源、および少なくとも1種類の焼結助剤を含む無機バッチ組成物を提供する工程、
前記無機バッチ組成物を、可塑剤、滑剤、結合剤、および細孔形成剤からなる群より選択される1種類以上の加工助剤と共に混合して、可塑化セラミック前駆体バッチ組成物を形成する工程、
前記可塑化セラミック前駆体バッチ組成物を未焼成体に成形する工程、および
前記未焼成体を焼成して、該未焼成体を、主にAl2(1-x)MgxTi(1+x)O(ただし、0.16≦x≦0.23)またはAl2TiO5−MgTi2O5固溶体を含む擬板チタン石相と、コージエライトを含む第二相と、ムライトを含む第三相とを有するセラミック物品であって、コージエライト/ムライトの質量比としての相比が0.9以上かつ7以下であるセラミック物品に転化させる工程、
を有してなる方法。 - 前記コージエライト/ムライトの質量比としての相比が1.3以上である、請求項6記載の方法。
- 前記コージエライト/ムライトの質量比としての相比が2.5以下である、請求項7記載の方法。