JP6431968B2 - 透明導電性フィルム用粘着剤層、粘着剤層付き透明導電性フィルム、及びタッチパネル - Google Patents
透明導電性フィルム用粘着剤層、粘着剤層付き透明導電性フィルム、及びタッチパネル Download PDFInfo
- Publication number
- JP6431968B2 JP6431968B2 JP2017216227A JP2017216227A JP6431968B2 JP 6431968 B2 JP6431968 B2 JP 6431968B2 JP 2017216227 A JP2017216227 A JP 2017216227A JP 2017216227 A JP2017216227 A JP 2017216227A JP 6431968 B2 JP6431968 B2 JP 6431968B2
- Authority
- JP
- Japan
- Prior art keywords
- transparent conductive
- adhesive layer
- conductive film
- pressure
- sensitive adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
イソプレンゴム系粘着剤(SKダイン2563、綜研化学(株)製)を、片面をシリコーンで剥離処理した厚み38μmのポリエステルフィルム(商品名:ダイアホイルMRF、三菱樹脂(株)製)の剥離処理面に、最終的な厚みが100μmになるように塗布して塗布層を形成した。次いで、塗布層を85℃で5分乾燥させて、ゴム系粘着剤層を形成し、粘着シートを作製した。また、粘着シートの粘着面には、前記片面をシリコーンで剥離処理した厚み38μmのポリエステルフィルム(商品名:ダイアホイルMRF、三菱樹脂(株)製)を、剥離処理面前記と粘着剤層が接するように貼り合せた。粘着剤層の両面に被覆されたポリエステルフィルムは、剥離ライナーとして機能する。
(アクリル系ポリマー溶液の作製)
モノマー成分として、アクリル酸2−エチルヘキシル(2EHA)63重量部、N−ビニルピロリドン(NVP)15重量部、メタクリル酸メチル(MMA)9重量部、アクリル酸ヒドロキシエチル(HEA)13重量部、及び重合溶媒として酢酸エチル175重量部を、セパラブルフラスコに投入し、窒素ガスを導入しながら1時間攪拌した。このようにして重合系内の酸素を除去した後、重合開始剤として2,2’−アゾビスイソブチロニトリル0.2重量部を加え、65℃に昇温して5時間反応させた。その後70℃に昇温し、2時間反応させた。その後、酢酸エチルを加え、固形分濃度30重量%のアクリル系ポリマー溶液を得た。なお、上記アクリル系ポリマー溶液におけるアクリル系ポリマーの重量平均分子量は75万であった。
次に、上記アクリル系ポリマー溶液に、上記アクリル系ポリマー100重量部に対して、架橋剤(イソシアネート系架橋剤、商品名:タケネート D110N、三井化学(株)製)0.25重量部を加えて混合し、アクリル系粘着剤組成物を得た。
次に、上記アクリル系粘着剤組成物を、表面が剥離処理されたポリエチレンテレフタレートセパレーター(PETセパレーター)(商品名:MRF75、三菱樹脂(株)製)の剥離処理面上に、乾燥後の厚みが100μmとなるように塗布し、135℃で2分間の加熱乾燥を行い、さらに、23℃で120時間エージングを行って、粘着シート(アクリル系粘着剤層/剥離フィルムの構成を有する基材レス粘着シート)を得た。
(アクリル系ポリマー溶液の作製)
モノマー成分として、アクリル酸2−エチルヘキシル(2EHA)59重量部、N−ビニルピロリドン(NVP)10重量部、メタクリル酸メチル(MMA)21重量部、アクリル酸ヒドロキシエチル(HEA)10重量部、及び重合溶媒として酢酸エチル175重量部を、セパラブルフラスコに投入し、窒素ガスを導入しながら1時間攪拌した。このようにして重合系内の酸素を除去した後、重合開始剤として2,2’−アゾビスイソブチロニトリル0.2重量部を加え、65℃に昇温して5時間反応させた。その後70℃に昇温し、2時間反応させた。その後、酢酸エチルを加え、固形分濃度30重量%のアクリル系ポリマー溶液を得た。なお、上記アクリル系ポリマー溶液におけるアクリル系ポリマーの重量平均分子量は90万であった。
(アクリル系ポリマー溶液の作製)
モノマー成分として、アクリル酸2−エチルヘキシル(2EHA)61重量部、N−ビニルピロリドン(NVP)14重量部、アクリル酸4−ヒドロキシブチル(4HBA)22重量部、アクリル酸ヒドロキシエチル(HEA)3重量部、及び2種の光重合開始剤(商品名:イルガキュア184、BASF社製)0.05重量部及び光重合開始剤(商品名:イルガキュア651、BASF社製)0.05重量部を4つ口フラスコに投入してモノマー混合物を調製した。次いで、前記モノマー混合物を窒素雰囲気下で紫外線に曝露して部分的に光重合させることによって、重合率約10重量%の部分重合物(アクリル系ポリマーシロップ)を得た。
次いで、上記で調製したモノマー成分を、片面をシリコーンで剥離処理した厚み38μmのポリエステルフィルム(商品名:ダイアホイルMRF、三菱樹脂(株)製)の剥離処理面に、最終的な厚みが100μmになるように塗布して塗布層を形成した。次いで、塗布されたモノマー成分の表面に、片面をシリコーンで剥離処理した厚み38μmのポリエステルフィルム(商品名:ダイアホイルMRF、三菱樹脂(株)製)を、当該フィルムの剥離処理面が塗布層側になるようにして被覆した。これにより、モノマー成分の塗布層を酸素から遮断した。このようにして得られた塗布層を有するシートにケミカルライトランプ((株)東芝製)を用いて照度5mW/cm2(約350nmに最大感度をもつトプコンUVR−T1で測定)の紫外線を360秒間照射して、塗布層を硬化させて粘着剤層を形成し、粘着シートを作製した。粘着剤層の両面に被覆されたポリエステルフィルムは、剥離ライナーとして機能する。
実施例、及び比較例で得られた、粘着シートから10cm2(5cm×2cm)切り出し、両側セパレーターを付けたまま加温加湿室(60℃、95%R.H.)に120時間投入した。加温加湿室から取り出してセパレーターを剥がしてアルミ箔にはりつけて秤量(W1(μg))し、これを試験片とした。アルミ箔の重量は、粘着シートに貼付する前に予め測定しておいた(W2(μg))。
次いで、上記試験片を、下記の加熱気化装置に入れ、150℃で加熱した時に発生したガスを、下記の電量滴定式水分測定装置の滴定セル内に導入し、上記ガス中の水分量(μg)を測定して、60℃、95%R.H.の環境下に120時間保存後の粘着剤層中の水分量(W3(μg))を測定した。そして、下記式により60℃、95%R.H.の環境下で120時間保存した後の粘着剤層の水分率(重量%)を算出した。なお、測定回数(n数)は2回とし、平均値を算出した。
電量滴定式水分測定装置:(株)三菱化学アナリテック製、CA−200型
加熱気化装置:(株)三菱化学アナリテック製、VA−200型
(測定条件)
方法:加熱気化法/150℃加熱
陽極液:アクアミクロンAKK
陰極液:アクアミクロンCXU
透明導電性フィルム(HC(クリアハードコート)層/PET層(PET基材層)/ITO層の層構成を有するフィルム)を140℃の温度環境下に90分放置してITO層を結晶化させた。
◎:取り出し直後の試験片のヘイズが2.0%未満(極めて良好)
○:取り出し直後の試験片のヘイズが2.0%以上5.0%未満(良好)
×:取り出し直後の試験片のヘイズが5.0%以上(不良)
粘着剤層(粘着シートからシリコーン処理を施したPETフィルムを剥離したもの)を、銅箔と電極の間に挟み以下の装置により周波数100kHzにおける比誘電率を測定した。測定は3サンプルを作製し、それらの3サンプルの測定値の平均を誘電率とした。なお、粘着剤層の周波数100kHzでの比誘電率は、JIS K 6911に準じて、下記条件で測定した。
測定方法:容量法(装置:Agilent Technologies E4980A Precision LCR Meter使用)
電極構成:12.1mmΦ、0.5mm厚みのアルミ板
対向電極:3oz 銅板
測定環境:23℃、55%R.H.
測定環境(加湿条件):60℃、95%R.H.に、測定治具に粘着剤を固定した状態で30分放置し、30分後の誘電率を測定
2 透明導電性フィルム
3 透明導電性薄膜
4 透明プラスチックフィルム基材
5 機能層
6 静電容量方式タッチパネル
7 装飾パネル
8 透明導電性フィルム用粘着剤層
9 透明導電性フィルム
10 ハードコートフィルム
11 ITO層
12 PET基材層
13 HC層
14 ガラス
Claims (7)
- 透明プラスチックフィルム基材の一方の面に、金属酸化物により形成された透明導電性 薄膜を有し、他方の面に機能層を有する透明導電性フィルムの一方の面に、透明導電性フ ィルム用粘着剤層を有する粘着剤層付き透明導電性フィルムであって、
前記透明導電性フィルム用粘着剤層は、
ベースポリマーとしてイソプレン系ポリマーを含むイソプレンゴム系粘着剤から形成さ れた粘着剤層であって、
23℃、55%R.H.環境下の周波数100kHzの比誘電率が3.4以下であり、60℃、95%R.H.の環境下に120時間保存した後の水分率が1重量%以下であり 、かつ、60℃、95%R.H.の環境下における周波数100kHzの比誘電率が、2 3℃、55%R.H.環境下の周波数100kHzの比誘電率の1.2倍以下であることを特徴とする、粘着剤層付き透明導電性フィルム。 - 前記水分率が0.6重量%以下であることを特徴とする請求項1に記載の粘着剤層付き 透明導電性フィルム。
- 前記イソプレン系ポリマーが、イソプレン−スチレン共重合体を含むことを特徴とする 請求項1または2に記載の粘着剤層付き透明導電性フィルム。
- 前記イソプレン系ポリマーが、水添物であることを特徴とする請求項1〜3のいずれか に記載の粘着剤層付き透明導電性フィルム。
- 前記透明導電性フィルムの透明導電性薄膜上に、前記透明導電性フィルム用粘着剤層を有することを特徴とする請求項1〜4のいずれかに記載の粘着剤層付き透明導電性フィルム。
- 前記透明導電性フィルムの機能層上に、前記透明導電性フィルム用粘着剤層を有することを特徴とする請求項1〜4のいずれかに記載の粘着剤層付き透明導電性フィルム。
- 請求項1〜6のいずれかに記載の粘着剤層付き透明導電性フィルムを少なくとも1つ有することを特徴とするタッチパネル。