JP6430098B2 - タッチパネル電極の保護膜用感光性透明材 - Google Patents
タッチパネル電極の保護膜用感光性透明材 Download PDFInfo
- Publication number
- JP6430098B2 JP6430098B2 JP2013004451A JP2013004451A JP6430098B2 JP 6430098 B2 JP6430098 B2 JP 6430098B2 JP 2013004451 A JP2013004451 A JP 2013004451A JP 2013004451 A JP2013004451 A JP 2013004451A JP 6430098 B2 JP6430098 B2 JP 6430098B2
- Authority
- JP
- Japan
- Prior art keywords
- touch panel
- protective film
- photosensitive
- meth
- transparent material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明で用いるバインダーポリマーは、(メタ)アクリル酸に由来するカルボキシル基を有し、酸価が30〜190mgKOH/gであり、炭素数4〜18のアルキル基を有する(メタ)アクリル酸アルキルエステルを共重合させた(A)バインダーポリマーと、(B)少なくとも3つのエチレン性不飽和基を有し、酸価が5mgKOH/g以下である光重合性化合物と、(C)光重合開始剤とを含有する感光性樹脂組成物からなる感光層を設け、当該感光層の所定部分を活性光線の照射により硬化させた後に所定部分以外の感光層を除去し、上記電極の一部又は全部を被覆する厚みが好ましくは、10μm以下の上記感光性樹脂組成物の硬化物からなるタッチパネル電極の保護膜用感光性透明材を形成する。
また、本発明は、[3] 硬化膜を形成したときの比誘電率が3.1〜3.8である、上記[1]又は[2]に記載のタッチパネル電極の保護膜用感光性透明材に関する。
また、本発明は、[4] 前記バインダーポリマーの前記構造単位a1とa2の重合モル比がa1/a2=15/85〜40/60の範囲で重合されたバインダーポリマーを含む上記[1]〜[3]のいずれかに記載のタッチパネル電極の保護膜用感光性透明材に関する。
また、本発明は、[5] 前記(B)光重合性化合物が、ペンタエリスリトール由来の骨格を有する(メタ)アクリレート化合物、ジペンタエリスリトール由来の骨格を有する(メタ)アクリレート化合物、トリメチロールプロパン由来の骨格を有する(メタ)アクリレート化合物からなる群より選択される少なくとも1種の化合物を含む、上記[1]〜[4]のいずれかに記載のタッチパネル電極の保護膜用感光性透明材に関する。
上記のようにタッチパネルの視認性を充分に確保する観点から、上記感光層は可視光透過率が90%以上であることが好ましい。この場合、センシング領域の電極を被覆する保護膜の形成に好適である。
ここで(メタ)アクリル酸は、アクリル酸及びメタクリル酸を意味し、同様に(メタ)アクリル酸アルキルエステルは、アクリル酸アルキルエステル及びメタクリル酸アルキルエステルを意味する。
撹拌機、還流冷却機、不活性ガス導入口及び温度計を備えたフラスコに、表1に示した(1)を仕込み、窒素ガス雰囲気下で65℃に昇温し、反応温度を65℃±2℃に保ちながら、表1に示した(2)を3時間かけて均一に滴下した。(2)の滴下後、79℃±2℃で1時間撹拌を続け、重量平均分子量が約65900、酸価が163.8mgKOH/gのバインダーポリマーの溶液(A1)を得た。
上記(A1)と同様にし、重量平均分子量が約79500、酸価が151.4mgKOH/gのバインダーポリマーの溶液(A2)を得た。
上記(A1)と同様にし、重量平均分子量が約70200、酸価が140.8mgKOH/gのバインダーポリマーの溶液(A3)を得た。
上記(A1)と同様にし、重量平均分子量が約78000、酸価が133.7mgKOH/gのバインダーポリマーの溶液(A4)を得た。
上記(A1)と同様にし、重量平均分子量が約65000、酸価が109.0mgKOH/gのバインダーポリマーの溶液(A5)を得た。
上記(A1)と同様にし、重量平均分子量が約72000、酸価が186.6mgKOH/gのバインダーポリマーの溶液(A6)を得た。
上記(A1)と同様にし、重量平均分子量が約60400、酸価が174.5mgKOH/gのバインダーポリマーの溶液(A7)を得た。
[GPC条件]
ポンプ:DP−8020(東ソー株式会社)
カラム:Gelpack GL−W520―S、Gelpack GL−W530−S(日立化成株式会社)
溶離液:テトラヒドロフラン
測定温度:25℃
流量:1.00mL/分
検出器:RI−8020(東ソー株式会社)
[感光性樹脂組成物溶液の作製]
表2に示した材料を、攪拌機を用いて15分間混合し、感光性樹脂組成物溶液を作製した。
支持フィルムとして厚さ16μmのポリエチレンテレフタレートフィルムを使用し、前記感光性樹脂組成物溶液を支持フィルム上にアプリケーターを用いて均一に塗布し、100℃の無塵乾燥機で4分間乾燥して溶剤を除去し、感光性樹脂組成物からなる感光層(感光性樹脂組成物層)を形成した。得られた感光層の厚さは10μmであった。
次いで、得られた感光性エレメントを厚さ0.5mmで縦4cm×横4cmのガラス基板上に、感光層が接するようにラミネータ(日立化成テクノプラント株式会社製、HLM−1500型)を用いて、ロール温度110℃、基板送り速度0.5m/分、圧着圧力(シリンダ圧力)0.3MPaの条件でラミネートしガラス基板上に、感光層及び支持フィルムが積層された積層体を作製した。
得られた感光性エレメントを厚さ0.5mmで縦4cm×横4cmのガラス基板上に、感光層が接するようにラミネータ(日立化成テクノプラント株式会社製、HLM−1500型)を用いて、ロール温度110℃、基板送り速度0.5m/分、圧着圧力(シリンダ圧力)0.3MPaの条件でラミネートしガラス基板上に、感光層及び支持フィルムが積層された積層体を作製した。
得られた感光性エレメントを厚さ0.5mmで縦4cm×横4cmのp型シリコンウェハ基板上に、感光層が接するようにラミネータ(日立化成テクノプラント株式会社製、HLM−1500型)を用いて、ロール温度110℃、基板送り速度0.5m/分、圧着圧力(シリンダ圧力)0.3MPaの条件でラミネートし、p型シリコンウェハ基板上に、感光層及び支持フィルムが積層された積層体を作製した。
表3(表中の数値の単位は質量部)に示した感光性樹脂組成物溶液を用いて、実施例1と同様に感光性エレメントを作製し、全光線、400nmの透過率の測定、解像度測定、比誘電率測定を行い、その測定結果を纏めて表4に示した。
(A2):メタクリル酸/メタクリル酸メチル/メタクリル酸ブチル=30/35/35(モル比)、酸価151.4(mgKOH/g)
(A3):メタクリル酸/メタクリル酸メチル/メタクリル酸ブチル=30/15/55(モル比)、酸価140.8(mgKOH/g)
(A4):メタクリル酸/メタクリル酸ブチル=30/70(モル比)、酸価133.7(mgKOH/g)
(A5):メタクリル酸/メタクリル酸ブチル=25/75(モル比)、酸価109.0(mgKOH/g)
(A6):メタクリル酸/メタクリル酸ブチル=40/60(モル比)、酸価186.6(mgKOH/g)
(A7):メタクリル酸/メタクリル酸メチル=30/70(モル比)、酸価174.5(mgKOH/g)
TMP−A:ペンタエリスリトールテトラアクリレート(共栄社化学株式会社製、酸価5mgKOH/g以下)
Irg−OXE01:1,2−オクタンジオン,1−[4−(フェニルチオ)−,2−(O−ベンゾイルオキシム)](BASF社)
AO−80:3,9−ビス[1,1−ジメチル−2−[ベータ−(3−t−ブチル−4−ヒドロキシ−5−メチルフィエニル)プロピオニルオキシ]エチル]2,4,8,10−テトラオキサスピロ[5,5]−ウンデカン(株式会社ADEKA)
KBM−503:3−メタクリロキシプロピルトリエトキシシラン(信越化学工業株式会社)
PGMEA:プロピレングリコール−1−メチルエーテルアセテート
本発明で用いる炭素数4〜18のアルキル基を有する(メタ)アクリル酸アルキルエステルに対して炭素数1のアルキル基を共重合させた(A7)を用いた比較例1は、光線透過率には優れるが、比誘電率が高い。本発明は、バインダーポリマーとして、(メタ)アクリル酸と、炭素数4〜18のアルキル基を有する(メタ)アクリル酸アルキルエステルを含む共重合体とし、少なくとも3つのエチレン性不飽和基を有する光重合性化合物を用いることで、光線透過率が同等であり、上記実施例で比誘電率を2.7〜13.5%も低下させたタッチパネル電極の保護膜用感光性透明材を提供することが出来る。
構造単位a1と((メタ)アクリル酸)a2(炭素数4〜18のアルキル基を有する(メタ)アクリル酸アルキルエステル)の重合モル比がa1/a2=15/85〜40/60の範囲である実施例3〜6では比誘電率がより低下する。
Claims (4)
- タッチパネル電極の保護膜用感光性透明材であって、
(A)(メタ)アクリル酸に由来する構造単位a1と、炭素数4〜18のアルキル基を有する(メタ)アクリル酸アルキルエステルに由来する構造単位a2とを含み、且つ、前記構造単位a1とa2の重合モル比がa1/a2=15/85〜35/65の範囲で重合されたバインダーポリマー、
(B)少なくとも3つのエチレン性不飽和基を有し、酸価が5mgKOH/g以下である光重合性化合物、及び、
(C)光重合開始剤を含み、
前記(A)バインダーポリマーの重量平均分子量が30,000以上であり、
前記(B)光重合性化合物が、ペンタエリスリトール由来の骨格を有する(メタ)アクリレート化合物を含有する、タッチパネル電極の保護膜用感光性透明材。 - 厚み10μmの膜を形成したときの可視光透過率が90%以上である、請求項1に記載のタッチパネル電極の保護膜用感光性透明材。
- 硬化膜を形成したときの比誘電率が3.1〜3.8である、請求項1又は2に記載のタッチパネル電極の保護膜用感光性透明材。
- 前記(C)光重合開始剤が、オキシムエステル化合物、又はホスフィンオキサイド化合物を含有する、請求項1〜3のいずれかに記載のタッチパネル電極の保護膜用感光性透明材。