JP6326575B2 - Wave forming agent containing shellac, and wave forming method using the same - Google Patents
Wave forming agent containing shellac, and wave forming method using the same Download PDFInfo
- Publication number
- JP6326575B2 JP6326575B2 JP2013218480A JP2013218480A JP6326575B2 JP 6326575 B2 JP6326575 B2 JP 6326575B2 JP 2013218480 A JP2013218480 A JP 2013218480A JP 2013218480 A JP2013218480 A JP 2013218480A JP 6326575 B2 JP6326575 B2 JP 6326575B2
- Authority
- JP
- Japan
- Prior art keywords
- hair
- wave
- shellac
- agent
- wave forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、ウエーブ形成剤、及びこれを用いたウエーブ形成方法に係り、更に詳しくは、例えばロングヘアの毛先などダメージを受けた毛髪に思い通りのウエーブを形成させることができる、セラックを含有するウエーブ形成剤、及びこれらを用いたウエーブ形成方法に関する。 The present invention relates to a wave forming agent and a wave forming method using the same, and more particularly, a wave containing shellac that can form a desired wave on damaged hair such as a long hair tip. The present invention relates to a forming agent and a wave forming method using the same.
従来より、ウエーブ形成剤としては、チオグリコール酸塩、システイン、システアミン、亜硫酸ナトリウム等の還元剤を主成分とする第１剤と、臭素酸ナトリウムや過酸化水素の酸化剤を主成分とする第２剤からなるパーマネントウエーブ剤（以下、パーマ剤と称することがある）が使用されている。このパーマ剤は、毛髪をロッドに巻きつけてから、第１剤で毛髪を構成するケラチン繊維内のシスチン結合を切断し、この状態で第２剤を用いて所望の形状でシスチン結合を再生させることにより、パーマネントウエーブ（以下、単にパーマと称することがある）を形成する薬剤である。 Conventionally, as a wave forming agent, a first agent mainly composed of a reducing agent such as thioglycolate, cysteine, cysteamine, sodium sulfite, and a first agent mainly composed of an oxidizing agent such as sodium bromate or hydrogen peroxide. A permanent wave agent composed of two agents (hereinafter sometimes referred to as a permanent agent) is used. In this permanent agent, after winding hair around a rod, the first agent cuts cystine bonds in the keratin fibers constituting the hair, and in this state, the second agent is used to regenerate the cystine bonds in a desired shape. By this, it is a chemical | medical agent which forms a permanent wave (Hereafter, it may only be called a permanent.).
しかしながら、ケラチン繊維はパーマ剤やヘヤカラー剤によるケミカルダメージ、ブラッシングやドライヤーなどによるフィジカルダメージ、毛髪を長時間日光に晒すことによるダメージ等を受けて次第に柔らかくなり、従来のパーマ剤によるパーマがかかりにくくなる。即ち、同じように施術したとしても、ダメージ毛と健康毛ではパーマのかかり方が異なり、例えば毛髪のダメージが思ったより大きければウエーブのかかり方が弱くなり、それを見越して強くパーマをかけるとウエーブのかかり方が強すぎたりすることがある。どのくらい強くパーマをかけるかの調節は、施術者の感覚が頼りなので、思い通りのウエーブを形成するのは極めて困難である。 However, keratin fibers are gradually softened due to chemical damage due to permanents and hair coloring agents, physical damage due to brushing and dryers, and damage caused by exposure of the hair to sunlight for a long time, making it less likely to become permanent with conventional permanents. . In other words, even if the same treatment is performed, the way of applying perm differs between damaged hair and healthy hair.For example, if the damage of the hair is larger than expected, the way of applying the wave becomes weaker. May be too strong. It is very difficult to form the wave as you want because the perception of the practitioner depends on how strongly the perm is applied.
特に、ロングヘアーの場合、毛先がはねて広がりやすくなっているため、これを防止して毛先をまとめるため、毛先にだけウエーブをかける処理が施されることがある。しかしながら、毛先は長期間にわたる日光の照射や、たび重なるパーマネントウエーブ処理や染毛処理のためにダメージが蓄積していることが多いため、通常のパーマ処理では十分にウエーブが形成されないことがある。 In particular, in the case of long hair, the tip of the hair tends to splash and spread, and therefore, in order to prevent this and collect the tip of the hair, a treatment for applying a wave only to the tip of the hair may be performed. However, since the hair ends often accumulate damage due to long-term sunlight irradiation, repeated permanent wave treatment or hair dyeing treatment, the wave may not be sufficiently formed by normal permanent treatment. .
このような不都合を避けるため、例えば特許文献１に記載されているように、第２剤における酸化剤として、ナノバブル水のように反応が穏やかな物質を使用することにより、毛髪へのダメージを抑える技術が報告されている。しかしながら、既にダメージを受けた毛髪に好適なウエーブをかける方法については報告されていない。 In order to avoid such inconvenience, for example, as described in Patent Document 1, as a oxidant in the second agent, a substance with a mild reaction such as nanobubble water is used to suppress damage to hair. Technology has been reported. However, no method for applying a suitable wave to hair that has already been damaged has been reported.
本発明者らはダメージを受けた毛髪に十分なウエーブを形成する方法について鋭意研究の結果、ダメージを受けた毛髪は髪質が柔らかくなっており、弾力が失われている点に着目し、外側を補強剤で被覆して毛髪の剛性を回復することにより、ダメージを受けた毛髪に十分なウエーブを形成させることができるとの着想を得た。そして、毛髪の補強剤として適している物質について研究を続けた結果、セラックが最も好ましいことを見出し、本発明を完成するに至った。
即ち本発明は、上記従来技術の問題点を解消し、ダメージを受けている毛髪に十分なウエーブを形成することができる毛髪処理方法、及びそれに用いるウエーブ形成剤を提供することを目的とする。
As a result of diligent research on a method of forming a sufficient wave on damaged hair, the inventors of the present invention have noticed that the damaged hair is soft in hair quality and loses elasticity. The idea was that a sufficient wave could be formed on damaged hair by covering the hair with a reinforcing agent to restore the rigidity of the hair. And as a result of continuing research on a substance suitable as a hair reinforcing agent, it was found that shellac was most preferable, and the present invention was completed.
That is, an object of the present invention is to solve the above-mentioned problems of the prior art and to provide a hair treatment method capable of forming a sufficient wave on damaged hair and a wave forming agent used therefor.
即ち、本発明の特徴は、染料を含有する染毛剤により処理しダメージを受けた毛髪を、セラックを含有し還元剤を含有しないウエーブ形成剤で処理し、その後に、毛髪が所望の形状で保持された状態でセラックを硬化させることにより、ウエーブを形成するとともに染料の退色を防止することを特徴とするウエーブ形成方法である。 That is, the feature of the present invention, the hair that was damaged by Risho management by the hair dye containing a dye, and processed by waving agent that does not contain contain shellac reducing agent, thereafter, the hair by curing the condition Dese rack held in the desired shape, a wave forming method comprising preventing fading of dye to form a wave.
本発明の他の特徴は、毛髪が所望の形状で保持された状態で、当該毛髪を一定時間保持することによりセラックを硬化させる上記のウエーブ形成方法である。 Another feature of the present invention is the above-described wave forming method in which shellac is cured by holding the hair for a predetermined time while the hair is held in a desired shape .
本発明の更に他の特徴は、ｐＨが７〜１３である上記のウエーブ形成方法である。 Still another feature of the present invention is the above-described wave forming method having a pH of 7 to 13 .
本発明の更に他の特徴は、セラックの濃度が０．０１〜５重量％である上記のウエーブ形成方法である。
本発明の更に他の特徴は、染料が酸化染料である上記のウエーブ形成方法である。
Still another feature of the present invention is the above-described wave forming method, wherein the shellac concentration is 0.01 to 5% by weight.
Still another feature of the present invention is the above-described wave forming method, wherein the dye is an oxidation dye.
本発明によれば、ダメージを受けてパーマがかかりにくく且つ髪質が柔らかくなっている場合でも、セラックによりダメージ毛をカールした形状に固めることにより、ウエーブを形成させることができる。
また、ダメージにより髪から失われた弾力をセラックにより補強することができるので、大きなウエーブを形成させても、ダレたりせず、くっきりと立体感のあるウエーブを形成させることができる。
According to the present invention, a wave can be formed by hardening damaged hair with a shellac into a curled shape even when the hair is softened due to damage.
Further, since the elasticity lost from the hair due to damage can be reinforced by shellac, even when a large wave is formed, a wave having a clear and three-dimensional effect can be formed without sagging.
本発明において用いるセラックとは、インド・タイ・ビルマ・インドシナ等を原産地とするラックカイガラ虫から分泌された樹脂状物質を精製して得られる物質であり、酸や熱により硬化する性質を有する。また、本発明におけるセラックは、ＪＩＳ規格においてＪＩＳ Ｋ ５９０９でセラックとして規定されているものと、ＪＩＳ Ｋ ５９１１で白ラックとして規定されているものを含む。市販品としては、日本シェラック工業（株）製のＢ. Ｄ. Ｓ. 、ラックコート３０ＥＡ等が例示できる。 The shellac used in the present invention is a substance obtained by refining a resinous substance secreted from a silkworm that originates in India, Thailand, Burma, Indochina, etc., and has a property of being cured by acid or heat. The shellac in the present invention includes those defined as shellac in JIS K 5909 in the JIS standard and those defined as white rack in JIS K5911. Examples of commercially available products include BDS from Nippon Shellac Industry Co., Ltd., rack coat 30EA, and the like.
本発明においては、前記のセラックで毛髪を被覆して、さらに毛髪を所望の形状で保持し、この状態でセラックを硬化させることにより、ダメージを受けて通常のパーマ剤ではウエーブを形成できなくなった毛髪に、ウエーブを形成させることができる。なお、ここでいう通常のパーマ剤とは、還元剤を含む第１剤と、酸化剤を含む第２剤からなるパーマ剤をいう。
使用するセラックの量は特に限定されないが、ダメージを受けて弾力を失った毛髪がウエーブを保持した状態で固まる程度の量であって、このダメージを受けた毛髪が硬くなり過ぎない程度の量とするのが好ましく、具体的にはセラックを溶媒に溶解させる場合は、セラックの濃度が０．０１〜５重量％、更には０．０５〜４重量％、特には０．１〜３重量％とするのが好ましい。セラックの量が少なすぎると、ダメージ毛にウエーブを形成させることができない傾向があり、セラックの量が多すぎると、毛髪が硬くなりすぎ、外観が硬質で不自然になる傾向がある。
In the present invention, the hair is covered with the shellac, and the hair is further held in a desired shape, and the shellac is cured in this state, so that the wave cannot be formed with a normal permanent agent due to damage. Waves can be formed on the hair. In addition, the normal permanent agent here means the permanent agent which consists of the 1st agent containing a reducing agent and the 2nd agent containing an oxidizing agent.
The amount of shellac to be used is not particularly limited, but it is an amount that the damaged hair loses its elasticity and solidifies while holding the wave, and the amount that the damaged hair does not become too hard. Specifically, when shellac is dissolved in a solvent, the concentration of shellac is 0.01 to 5% by weight, further 0.05 to 4% by weight, and particularly 0.1 to 3% by weight. It is preferable to do this. If the amount of shellac is too small, there is a tendency that the damaged hair cannot form a wave. If the amount of shellac is too large, the hair becomes too hard and the appearance tends to be hard and unnatural.
セラックは酸性条件下で硬化する性質があるので、使用前に硬化するのを防ぐため、本発明のウエーブ形成剤のｐＨは中性又はアルカリ性が好ましく、また、セラックはアルカリ条件下で溶解しやすくなる性質があるのでアルカリ性のほうがより好ましく、具体的なｐＨは７〜１３、さらには７〜１０、特には７．５〜９．５とするのが好ましい。
ｐＨを調整する方法については定法でよく、トリエタノールアミンやアンモニア水等のアルカリ剤を適量加えればよい。
Since shellac has a property of curing under acidic conditions, the pH of the wave forming agent of the present invention is preferably neutral or alkaline to prevent curing before use, and shellac is easily soluble under alkaline conditions. The alkaline pH is more preferable, and the specific pH is preferably 7 to 13, more preferably 7 to 10, and particularly preferably 7.5 to 9.5.
The method for adjusting the pH may be a conventional method, and an appropriate amount of an alkaline agent such as triethanolamine or aqueous ammonia may be added.
本発明のウエーブ形成剤には、パーマ剤に通常含有される他の添加剤、例えば基剤、湿潤剤、帯電防止剤、可溶化剤、防腐剤、着色剤、着香剤等の１種又は２種以上を含有させることができる。 The wave forming agent of the present invention may be one of other additives usually contained in a permanent agent, such as a base, a wetting agent, an antistatic agent, a solubilizer, an antiseptic, a coloring agent, a flavoring agent, etc. Two or more kinds can be contained.
以下、上記のウエーブ形成剤を用いてウエーブを形成させる本発明の方法について説明する。 Hereinafter, the method of the present invention for forming a wave using the above-described wave forming agent will be described.
まず、毛髪が所望の形状で保持された状態で、本発明のウエーブ形成剤で毛髪が処理される。これにより毛髪はウエーブ形成剤に含有されるセラックで被覆された状態になる。なお、単に本発明のウエーブ形成剤で処理しただけでは、まだセラックは硬化されておらず、毛髪にもウエーブは形成されていない。従って、先に毛髪を所望の状態で保持してから本発明のウエーブ形成剤で処理してもよいし、本発明のウエーブ形成剤で毛髪を処理してから、毛髪を所望の状態で保持してもよい。なお、毛髪を先に本発明のウエーブ形成剤で処理してから所望の形状で保持したほうが、毛髪をセラックで均一に被覆できるが、毛髪を所望の形状に保持するために数十分かかるような場合には、ウエーブ形成剤による毛髪処理を後にするほうが好ましい。 First, the hair is treated with the wave forming agent of the present invention while the hair is held in a desired shape. As a result, the hair is covered with shellac contained in the wave forming agent. In addition, the shellac is not hardened | cured only by processing with the wave formation agent of this invention, and the wave is not formed also in hair. Therefore, the hair may be first held in a desired state and then treated with the wave forming agent of the present invention, or the hair is treated with the wave forming agent of the present invention and then the hair is held in a desired state. May be. It should be noted that, if the hair is first treated with the wave forming agent of the present invention and then held in the desired shape, the hair can be uniformly coated with shellac, but it may take several tens of minutes to keep the hair in the desired shape. In such a case, it is preferable to perform hair treatment with a wave forming agent later.
上述の処理の後、毛髪がセラックで被覆されている状態で、セラックを硬化させる。セラックを硬化させることにより、硬化したセラックが毛髪を保持し、所望の形状が維持される。なお、ダメージを受けた毛髪は弾力が失われているので、セラックが硬化した程度の力で、毛髪を所望の形状に維持することができる。 After the above treatment, the shellac is cured while the hair is covered with shellac. By curing the shellac, the cured shellac holds the hair and maintains the desired shape. In addition, since the damaged hair loses elasticity, the hair can be maintained in a desired shape with the force of the degree to which shellac is cured.
硬化させる方法としては、セラックで被覆された毛髪を、所定の形状に保持したまま一定時間以上放置する方法、酸性の薬剤で処理する方法、熱処理する方法が例示できる。
所定の形状に保持したまま一定時間放置する場合、セラックの濃度にもよるが、放置しておく時間は通常５〜２５分程度である。
酸性の薬剤で処理する場合、ｐＨ７未満、好ましくは１〜６．９、更に好ましくは３〜６．９の薬剤に、５〜１５分程度晒せばよい。
熱処理する場合は、５０〜２４０℃で１秒〜２０分程度、好ましくは８０〜２００℃で１秒〜１５分程度毛髪を処理する。
なお、使用するセラックの量が少ない場合は一定時間放置する方法では効果が比較的小さくなる傾向があり、セラックの量が多い場合は酸性の薬剤で処理する方法では効果が比較的小さくなる傾向があり、熱処理する方法では毛髪へのダメージがさらに大きくなる傾向があるので、状況に応じてこれらの方法を使い分ければよい。即ち、セラックの量が少ない場合は酸処理か熱処理が好ましく、セラックの量が多い場合は一定時間放置する方法か熱処理が好ましく、毛髪へのダメージを避けたい場合には一定時間放置する方法か酸処理が好ましい。
Examples of the curing method include a method in which hair covered with shellac is left in a predetermined shape for a certain period of time, a method in which treatment is performed with an acidic chemical, and a method in which heat treatment is performed.
When it is left for a predetermined time while being held in a predetermined shape, although it depends on the concentration of shellac, the time to leave is usually about 5 to 25 minutes.
When treating with an acidic drug, it may be exposed to a drug having a pH of less than 7, preferably 1 to 6.9, and more preferably 3 to 6.9 for about 5 to 15 minutes.
In the case of heat treatment, the hair is treated at 50 to 240 ° C. for about 1 second to 20 minutes, preferably at 80 to 200 ° C. for about 1 second to 15 minutes.
When the amount of shellac used is small, the method of leaving for a certain period of time tends to have a relatively small effect, and when the amount of shellac is large, the method of treating with an acidic chemical tends to be relatively small. There is a tendency that damage to the hair tends to be further increased by the method of heat treatment, so these methods may be properly used depending on the situation. That is, when the amount of shellac is small, acid treatment or heat treatment is preferable. When the amount of shellac is large, a method of leaving for a certain period of time or heat treatment is preferable. Treatment is preferred.
本発明のウエーブ形成剤は、酸化染料を主成分とする染毛剤や脱毛剤と併用することができる。但し、従来の還元剤及び酸化剤からなるパーマネントウエーブ剤と染毛剤を併用する場合、先にパーマネントウエーブ剤によるウエーブ形成を行ってから染毛剤を用いる（先に染毛を行えば、従来のパーマネントウエーブ剤の還元剤が酸化重合した染料を退色させる）が、本発明のウエーブ形成剤は酸化重合した染料を退色させないので、染毛とウエーブ形成処理のいずれを先に行ってもよい。
なお、上述の通り、本発明のウエーブ形成剤はセラックが毛髪の表面に被覆した状態で硬化されるので、染毛を施した後に本発明のウエーブ形成処理を行えば、硬化したセラックが染色された毛髪の表面に被覆され、毛髪だけでなく染料も硬化したセラックにより保護されることになるので、染色された毛髪の退色を好適に防ぐことができる。
The wave forming agent of the present invention can be used in combination with a hair dye or a hair remover mainly composed of an oxidation dye. However, when a permanent wave agent and a hair dye composed of a conventional reducing agent and an oxidizing agent are used in combination, a hair dye is used after first forming a wave with a permanent wave agent. However, the permanent wave reducing agent of the present invention fades the oxidatively polymerized dye). However, since the wave forming agent of the present invention does not discolor the oxidatively polymerized dye, either the hair dyeing or the wave forming treatment may be carried out first.
As described above, since the wave forming agent of the present invention is cured in a state where shellac is coated on the surface of the hair, the cured shellac is dyed if the wave forming treatment of the present invention is performed after hair coloring. In addition, since not only the hair but also the dye is protected by the coated shellac, the fading of the dyed hair can be suitably prevented.
以下、実施例及び比較例を挙げて本発明を更に詳細に説明するが、本発明はこれらにより何ら制限されないことは云うまでもない。なお、以下の記載において、％は重量％を意味する。 EXAMPLES Hereinafter, although an Example and a comparative example are given and this invention is demonstrated in detail, it cannot be overemphasized that this invention is not restrict | limited at all by these. In the following description, “%” means “% by weight”.
ウエーブ形成剤の調整：
セラックとトリエタノールアミンの１対１混合物を、セラックの濃度がそれぞれ０．０１％（Ｎｏ．１）、０．１％（Ｎｏ．２）、１．０％（Ｎｏ．３）、５．０％（Ｎｏ．４）、１０．０％（Ｎｏ．５）になるように精製水で希釈することにより、５種類のウエーブ形成剤を調整した。
また、ウエーブ形成剤Ｎｏ．４におけるトリエタノールアミンに代えて２８％アンモニア水を用いたものをＮｏ．６のウエーブ形成剤とした。
なお、比較例として、精製水、トリエタノールアミンの５．０％水溶液、２８％アンモニア水の５．０％希釈液を用いた。以下、便宜上これらをウエーブ形成剤Ｎｏ．７（精製水）、Ｎｏ．８（トリエタノールアミン水溶液）、Ｎｏ．９（アンモニア水希釈液）と称することがある。各ウエーブ形成剤の組成を表１に示す。
Adjustment of the wave forming agent:
A one-to-one mixture of shellac and triethanolamine has a shellac concentration of 0.01% (No. 1), 0.1% (No. 2), 1.0% (No. 3), 5.0. % (No. 4) and 10.0% (No. 5) were diluted with purified water to prepare 5 types of wave forming agents.
In addition, the wave forming agent No. No. 4 using 28% aqueous ammonia instead of triethanolamine. No. 6 wave forming agent.
As comparative examples, purified water, a 5.0% aqueous solution of triethanolamine, and a 5.0% diluted solution of 28% ammonia water were used. Hereinafter, for the sake of convenience, these are designated as wave forming agents No. 7 (purified water), no. 8 (Triethanolamine aqueous solution), No. 8 9 (ammonia water diluted solution). Table 1 shows the composition of each wave forming agent.
試験用毛髪の調整：
ビューラックス社製の同一人毛束（商品名：人毛黒髪）を、下記のブリーチ剤中に浸漬し３０分間放置した後、流水で２分間洗浄した。このブリーチ剤への浸漬と流水での洗浄を計５回繰り返した後、得られた毛髪から１５ｃｍの毛髪を３０本取り出して束ね、試験用ダメージ毛束とし、以下の試験に使用した。
なおブリーチ剤としては、２８％アンモニア水を５重量部、３５％過酸化水素水を８．５重量部含み、全体が１００重量部となるように精製水を加えて得られた液を用いた。
Preparation of test hair:
The same human hair bundle (trade name: human hair black hair) manufactured by Beaulux was immersed in the following bleaching agent and allowed to stand for 30 minutes, and then washed with running water for 2 minutes. After dipping in this bleaching agent and washing with running water a total of 5 times, 30 hairs of 15 cm were taken out from the obtained hair and bundled to obtain a damaged hair bundle for testing, which was used in the following tests.
As the bleaching agent, a solution obtained by adding purified water to 5 parts by weight of 28% ammonia water and 8.5 parts by weight of 35% hydrogen peroxide and adding 100 parts by weight as a whole was used. .
〈セラックの硬化１〉
実施例１
試験用毛髪にウエーブ形成剤Ｎｏ．４（セラック５．０％、アルカリ剤：トリエタノールアミン）を塗布して５分間放置後、ウエーブ形成剤が塗布された試験用毛髪を５０ｇの負荷でロッドに巻き、その状態で１０分間放置してから、該試験用毛髪をロッドから外した。
ロッドから外した試験用毛髪については、一旦ウエーブのかかり具合を観察してから精製水で濡らし、濡れた状態で再度ウエーブのかかり具合を観察した。使用したウエーブ形成剤及び観察結果を表２に示す。
<Curing shellac 1>
Example 1
Wave forming agent no. 4 (shellac 5.0%, alkali agent: triethanolamine) was applied and allowed to stand for 5 minutes, and then the test hair coated with the wave forming agent was wound on a rod with a load of 50 g and left in that state for 10 minutes. The test hair was then removed from the rod.
For the test hair removed from the rod, the condition of the wave was once observed, then wetted with purified water, and the condition of the wave was observed again in the wet state. Table 2 shows the wave forming agents used and the observation results.
実施例２、比較例１〜３
ウエーブ形成剤としてＮｏ．６（セラック５．０％、アルカリ剤：アンモニア水）、Ｎｏ．７（精製水）、Ｎｏ．８（セラック無し、アルカリ剤：トリエタノールアミン）、Ｎｏ．９（セラック無し、アルカリ剤：アンモニア水）を用いた他は実施例１と同様にして、実施例２、比較例１〜３の毛束を得て、ウエーブのかかり具合を観察した。使用したウエーブ形成剤及び観察結果を表２に示す。
Example 2, Comparative Examples 1-3
No. as a wave forming agent. 6 (shellac 5.0%, alkaline agent: aqueous ammonia), No. 6 7 (purified water), no. 8 (no shellac, alkaline agent: triethanolamine), No. The hair bundles of Example 2 and Comparative Examples 1 to 3 were obtained in the same manner as in Example 1 except that 9 (no shellac, alkaline agent: aqueous ammonia) was used, and the degree of wave application was observed. Table 2 shows the wave forming agents used and the observation results.
なお、ウエーブのかかり具合の観察において、ウエーブがかからない場合は×、ウエーブがかかるがダレ気味である場合は△、ウエーブがかかりダレがない場合は○、しっかりしたウエーブがかかる場合は◎で示した。以下、全ての実施例においても、評価基準は同じである。 In addition, in the observation of the degree of wave application, it was indicated by × when the wave was not applied, △ when the wave was applied but drooping, ◯ when the wave was applied and there was no sag, and ◎ when the wave was solid . Hereinafter, the evaluation criteria are the same in all the examples.
表２の結果より、ウエーブ形成剤に含まれるセラックは１０分間放置することにより十分硬化し、好適なウエーブを形成でき、精製水で濡らしてもウエーブが崩れないことが判る。この効果は使用するアルカリ剤種の影響を受けない。なお、ロッドから外した直後にはセラック使用の有無にかかわらずウエーブが形成されているが、セラックを使用しない場合は、いわゆる寝癖と同様、水で濡らすことにより直ぐにウエーブがとれる。 From the results in Table 2, it can be seen that the shellac contained in the wave forming agent is sufficiently cured by allowing it to stand for 10 minutes to form a suitable wave, and the wave does not collapse even when wet with purified water. This effect is not affected by the type of alkaline agent used. Note that a wave is formed immediately after removal from the rod regardless of whether or not shellac is used, but when shellac is not used, the wave can be taken immediately by wetting with water, as in the case of so-called bedding.
〈セラックの硬化２〉
実施例３〜８
リン酸ナトリウム、リン酸２ナトリウム、リン酸、トリエタノールアミン、精製水を適量使用し、ｐＨがそれぞれ３（実施例３）、４（実施例４）、５（実施例５）、６（実施例６）、９（実施例７）、１０（実施例８）の第２液を作成した。
そして、実施例１におけるウエーブ形成剤Ｎｏ．４（セラック濃度５．０％、アルカリ剤：トリエタノールアミン）を塗布して５分間放置する工程の後に、上記の第２液を毛束に塗布する工程を加えた他は、実施例１と同様にして実施例３〜８の毛束を得て、精製水で濡らした後のウエーブのかかり具合を観察した。使用した第２液のｐＨ及びウエーブのかかり具合を表３に示す。
<Curing shellac 2>
Examples 3-8
Sodium phosphate, disodium phosphate, phosphoric acid, triethanolamine, and purified water are used in appropriate amounts, and the pH is 3 (Example 3), 4 (Example 4), 5 (Example 5), and 6 (implemented). The second liquids of Examples 6), 9 (Example 7) and 10 (Example 8) were prepared.
And the wave forming agent No. 1 in Example 1 was used. Example 1 except that a step of applying the second liquid to the hair bundle was added after the step of applying 4 (shellac concentration of 5.0%, alkaline agent: triethanolamine) and allowing to stand for 5 minutes. Similarly, the hair bundles of Examples 3 to 8 were obtained, and the degree of wave application after wetting with purified water was observed. Table 3 shows the pH of the second liquid used and the degree of wave application.
表３の結果より、一般的にセラックは酸で硬化し、アルカリに溶解するといわれているが、上記実施例３〜８の結果からは、セラックを酸性またはアルカリ性の第２液で処理した影響は見られない。このことから、セラックを比較的高濃度（実施例３〜８では５．０％）で使用した場合には、セラックを硬化させる方法として、酸処理はあまり有効ではないこと、及び実施例１に示すように、一定時間以上（本試験例では１０分）放置する方法が有効であることがわかる。 From the results in Table 3, shellac is generally said to be cured with an acid and dissolved in an alkali. From the results of Examples 3 to 8, the effect of treating shellac with an acidic or alkaline second liquid is can not see. From this, when shellac is used at a relatively high concentration (5.0% in Examples 3 to 8), acid treatment is not very effective as a method for curing shellac. As shown, it can be seen that a method of leaving for a certain time or longer (10 minutes in this test example) is effective.
〈セラックの硬化３〉
実施例９
セラックをデジタルパーマ用ロッドを用いた熱処理により硬化させた他は、実施例１と同様にして実施例９の毛束を得た。
即ち、まず試験用毛髪にウエーブ形成剤Ｎｏ．４（セラック５．０％、アルカリ剤：トリエタノールアミン）を塗布して５分間放置後、ウエーブ形成剤が塗布された試験用毛髪を５０ｇの負荷でデジタルパーマ用ロッドに巻き、１２０℃で５分間放置してから、該試験用毛髪をロッドから外した。
ロッドから外した試験用毛髪については、一旦ウエーブのかかり具合を観察してから精製水で濡らし、濡れた状態で再度ウエーブのかかり具合を観察した。使用したウエーブ形成剤及び観察結果を表４に示す。
<Curing shellac 3>
Example 9
A hair bundle of Example 9 was obtained in the same manner as in Example 1 except that shellac was cured by heat treatment using a digital permanent rod.
That is, first, a wave-forming agent no. 4 (shellac 5.0%, alkali agent: triethanolamine) was applied and allowed to stand for 5 minutes, and then the test hair coated with the wave forming agent was wound around a digital permanent rod under a load of 50 g, and 5% at 120 ° C. After leaving for a minute, the test hair was removed from the rod.
For the test hair removed from the rod, the condition of the wave was once observed, then wetted with purified water, and the condition of the wave was observed again in the wet state. Table 4 shows the wave forming agents used and the observation results.
実施例１０、比較例４〜６
ウエーブ形成剤としてＮｏ．６（セラック５．０％、アルカリ剤：アンモニア水）、Ｎｏ．７（精製水）、Ｎｏ．８（セラック無し、アルカリ剤：トリエタノールアミン）、Ｎｏ．９（セラック無し、アルカリ剤：アンモニア水）を用いた他は実施例９と同様にして、実施例１０、比較例４〜６の毛束を得て、ウエーブのかかり具合を観察した。使用したウエーブ形成剤及び観察結果を表４に示す。
Example 10, Comparative Examples 4-6
No. as a wave forming agent. 6 (shellac 5.0%, alkaline agent: aqueous ammonia), No. 6 7 (purified water), no. 8 (no shellac, alkaline agent: triethanolamine), No. The hair bundles of Example 10 and Comparative Examples 4 to 6 were obtained in the same manner as in Example 9 except that 9 (no shellac, alkaline agent: aqueous ammonia) was used, and the degree of wave application was observed. Table 4 shows the wave forming agents used and the observation results.
表４の結果より、ウエーブ形成剤に含まれるセラックは、１２０℃で５分間熱処理することにより十分に硬化し、好適なウエーブを形成でき、精製水で濡らしてもウエーブがとれないことが判る。この効果は使用するアルカリ剤の影響を受けない。 From the results of Table 4, it can be seen that shellac contained in the wave forming agent is sufficiently cured by heat treatment at 120 ° C. for 5 minutes to form a suitable wave, and the wave cannot be removed even when wet with purified water. This effect is not affected by the alkaline agent used.
〈虐待処理１〉
実施例１１
ラウレス硫酸ナトリウムによる洗浄処理を加えた他は実施例１と同様にして実施例１１の毛束を得た。
即ち、まず、試験用毛髪にウエーブ形成剤Ｎｏ．４（セラック濃度５．０％、実施例１１）を塗布して５分間放置後、ウエーブ形成剤が塗布された試験用毛髪を５０ｇの負荷でロッドに巻き、その状態で１０分間放置してから、該試験用毛髪をロッドから外した。
ロッドから外した試験用毛髪については、一旦ウエーブのかかり具合を観察してから精製水で濡らし、濡れた状態で再度ウエーブのかかり具合を観察した。この濡れた毛束を、液温４０℃に調整したラウレス硫酸ナトリウムの１０％水溶液に３０分間浸漬し、引き上げ後に水洗してから（以後、このラウレス硫酸ナトリウムによる洗浄処理を虐待処理と称することがある）、ウエーブのかかり具合を観察した。使用したウエーブ形成剤及び観察結果を表５に示す。
<Abuse treatment 1>
Example 11
A hair bundle of Example 11 was obtained in the same manner as in Example 1 except that washing treatment with sodium laureth sulfate was added.
That is, first, the wave forming agent No. 4 (shellac concentration 5.0%, Example 11) was applied and allowed to stand for 5 minutes, and then the test hair coated with the wave forming agent was wound around the rod with a load of 50 g, and left in that state for 10 minutes. The test hair was removed from the rod.
For the test hair removed from the rod, the condition of the wave was once observed, then wetted with purified water, and the condition of the wave was observed again in the wet state. The wet hair bundle is immersed in a 10% aqueous solution of sodium laureth sulfate adjusted to a liquid temperature of 40 ° C. for 30 minutes, and after being pulled up, washed with water (hereinafter, this washing treatment with sodium laureth sulfate is referred to as abuse treatment). Yes, the degree of wave application was observed. Table 5 shows the wave forming agents used and the observation results.
実施例１２〜１５
ウエーブ形成剤Ｎｏ．４（セラック濃度５．０％、実施例１１）に代えて、Ｎｏ．１（セラック濃度０．０１％、実施例１２）、Ｎｏ．２（セラック濃度０．１％、実施例１３）、Ｎｏ．３（セラック濃度１．０％、実施例１４）、Ｎｏ．５（セラック濃度１０．０％、実施例１５）を使用した他は実施例１１と同様にして実施例１２〜１５の毛束を得て、ロッドから外した直後、濡れた状態、及び虐待処理後のウエーブのかかり具合をそれぞれ観察した。使用したウエーブ形成剤及び観察結果を表５に示す。
尚、表５において、実施例１１〜１５はセラック濃度の順に並べた。
Examples 12-15
Wave forming agent no. 4 (shellac concentration 5.0%, Example 11) 1 (shellac concentration 0.01%, Example 12), No. 1 2 (shellac concentration 0.1%, Example 13), No. 2 3 (shellac concentration 1.0%, Example 14), No. 3 5 (shellac concentration 10.0%, Example 15) was used in the same manner as in Example 11 to obtain the hair bundles of Examples 12 to 15 and immediately after removal from the rod, the wet state, and the abuse treatment The degree of the subsequent wave was observed. Table 5 shows the wave forming agents used and the observation results.
In Table 5, Examples 11 to 15 are arranged in the order of shellac concentration.
表５の結果より、１０分間の放置処理によりセラックを硬化させる場合、少なくともセラックの濃度が０．０１〜１０. ０％の範囲において、試験用毛束にウエーブを形成できることが判る。但し、セラック濃度が１０. ０％であるウエーブ形成剤Ｎｏ．５により処理した実施例１５では、毛束の手触りが明らかに硬くなっており、やや不自然さが感じられた。また、ウエーブ形成剤Ｎｏ．１（セラック濃度０．０１％）により処理した実施例１２、及びウエーブ形成剤Ｎｏ．２（セラック濃度０．１％）により処理した実施例１３では、虐待処理を施すことにより、形成されたウエーブがダレ気味になった。 From the results in Table 5, it can be seen that when shellac is cured by standing treatment for 10 minutes, a wave can be formed on the test hair bundle at least when the concentration of shellac is in the range of 0.01 to 10.0%. However, a wave former No. having a shellac concentration of 10.0% was used. In Example 15 treated by No. 5, the feel of the hair bundle was clearly hard and a little unnatural was felt. In addition, the wave forming agent No. No. 1 treated with a shellac concentration of 0.01%, and the wave forming agent No. In Example 13 treated with 2 (shellac concentration 0.1%), the formed wave became dull as a result of the abuse treatment.
〈虐待処理２〉
実施例１６
セラックをデジタルパーマ用ロッドを用いた熱処理により硬化させた他は、実施例１１と同様にして実施例１６の毛束を得た。
即ち、まず試験用毛髪にウエーブ形成剤Ｎｏ．４（セラック濃度５．０％、実施例１６）を塗布して５分間放置後、ウエーブ形成剤が塗布された試験用毛髪を５０ｇの負荷でデジタルパーマ用ロッドに巻き、１２０℃で５分間放置してから、該試験用毛髪をロッドから外した。
ロッドから外した試験用毛髪については、一旦ウエーブのかかり具合を観察してから精製水で濡らし、濡れた状態で再度ウエーブのかかり具合を観察した。この濡れた毛束を、液温４０℃に調整したラウレス硫酸ナトリウムの１０％水溶液に３０分間浸漬し、引き上げ後に水洗してから（虐待処理）、ウエーブのかかり具合を観察した。使用したウエーブ形成剤及び観察結果を表６に示す。
<Abuse treatment 2>
Example 16
A hair bundle of Example 16 was obtained in the same manner as in Example 11 except that shellac was cured by heat treatment using a digital perm rod.
That is, first, a wave-forming agent no. 4 (shellac concentration 5.0%, Example 16) was applied and allowed to stand for 5 minutes, and then the test hair coated with the wave forming agent was wound around a digital permanent rod under a load of 50 g and left at 120 ° C. for 5 minutes. The test hair was then removed from the rod.
For the test hair removed from the rod, the condition of the wave was once observed, then wetted with purified water, and the condition of the wave was observed again in the wet state. The wet hair bundle was immersed in a 10% aqueous solution of sodium laureth sulfate adjusted to a liquid temperature of 40 ° C. for 30 minutes, and after being pulled up and washed with water (abuse treatment), the degree of wave application was observed. Table 6 shows the wave forming agents used and the observation results.
実施例１７〜２０
ウエーブ形成剤Ｎｏ．４（セラック濃度５．０％、実施例１６）に代えて、Ｎｏ．１（セラック濃度０．０１％、実施例１７）、Ｎｏ．２（セラック濃度０．１％、実施例１８）、Ｎｏ．３（セラック濃度１．０％、実施例１９）、Ｎｏ．５（セラック濃度１０．０％、実施例２０）を使用した他は実施例１６と同様にして実施例１７〜２０の毛束を得て、ロッドから外した直後、濡れた状態、及び虐待処理後のウエーブのかかり具合をそれぞれ観察した。使用したウエーブ形成剤及び観察結果を表６に示す。
尚、表６において、実施例１６〜２０はセラック濃度の順に並べた。
Examples 17-20
Wave forming agent no. 4 (shellac concentration 5.0%, Example 16) 1 (shellac concentration 0.01%, Example 17), No. 1 2 (shellac concentration 0.1%, Example 18), No. 2 3 (shellac concentration 1.0%, Example 19), No. 3 5 (shellac concentration 10.0%, Example 20) was used in the same manner as in Example 16 to obtain the hair bundles of Examples 17 to 20, immediately after removal from the rod, and in a wet state, and abuse treatment The degree of the subsequent wave was observed. Table 6 shows the wave forming agents used and the observation results.
In Table 6, Examples 16 to 20 are arranged in the order of shellac concentration.
表６の結果より、１２０℃５分間の熱処理によりセラックを硬化させる場合、少なくともセラックの濃度が０．０１〜１０. ０％の範囲において、試験用毛束にウエーブを形成できることが判る。但し、ウエーブ形成剤Ｎｏ．５（セラック濃度１０. ０％）により処理した実施例２０では、毛束の手触りが明らかに硬くなっており、やや不自然さが感じられた。また、ウエーブ形成剤Ｎｏ．１（セラック濃度０．０１％）により処理した実施例１７、及びウエーブ形成剤Ｎｏ．２（セラック濃度０．１％）により処理した実施例１８では、虐待処理を施すことにより、形成されたウエーブがダレ気味になった。 From the results of Table 6, it can be seen that when shellac is cured by heat treatment at 120 ° C. for 5 minutes, a wave can be formed on the test hair bundle at least in the range of 0.01 to 10.0% shellac. However, the wave forming agent No. In Example 20, which was treated with 5 (shellac concentration of 10.0%), the feel of the hair bundle was clearly hard and a little unnatural was felt. In addition, the wave forming agent No. No. 1 treated with a shellac concentration of 0.01%, and the wave forming agent No. In Example 18 treated with 2 (shellac concentration of 0.1%), the formed wave became dull as a result of the abuse treatment.
〈退色〉
試験用染毛の作成：
下記表７に処方を示すヘアカラー１剤と、下記表８に処方を示すヘアカラー２剤を１対１で混合し、得られた混合物を、ビューラック社製ヤク毛１００％毛束に塗布した。塗布後温度を３０℃に保ちつつ２０分間放置し、その後、ラウレス硫酸ナトリウム１０％溶液にて１分間洗浄し、その後に４０℃の流水で１分間洗浄することにより、試験用染毛を得た。
<Fade>
Creating test hair dye:
One hair color agent whose formulation is shown in the following Table 7 and two hair color agents whose formulation is shown in the following Table 8 are mixed on a one-to-one basis, and the resulting mixture is applied to 100% yak hair bundle made by Beaulac. did. After application, the hair was left for 20 minutes while maintaining the temperature at 30 ° C., then washed with 10% sodium laureth sulfate solution for 1 minute, and then washed with running water at 40 ° C. for 1 minute to obtain a test hair dye. .
実施例２１
ウエーブ形成剤Ｎｏ．４（セラック濃度５．０％）を１０ｍＬ、上記試験用染毛に塗布して１５分間放置し、その後ラウレス硫酸ナトリウム１０％溶液にて１分間洗浄し、次いで４０℃流水にて１分間洗浄した。
得られた毛束について、ＫＯＮＩＫＡ ＭＩＮＯＬＴＡ社製分光測色計ＣＭ−２６００ｄを用いて上記試験用染毛との色差を測定した。
測定後、液温４０℃に調整したラウレス硫酸ナトリウムの１０％水溶液に３０分間浸漬し、引き上げ後に水洗してから（虐待処理）、再度試験用染毛との色差を測定した。
使用したウエーブ形成剤及び測定した色差を表９に示す。
Example 21
Wave forming agent no. 4 (shellac concentration 5.0%) was applied to the test hair dye and left for 15 minutes, then washed with 10% sodium laureth sulfate solution for 1 minute, and then washed with running water at 40 ° C. for 1 minute. .
About the obtained hair bundle, the color difference with the said test hair dye was measured using the spectrocolorimeter CM-2600d by KONIKA MINOLTA.
After the measurement, the sample was immersed in a 10% aqueous solution of sodium laureth sulfate adjusted to a liquid temperature of 40 ° C. for 30 minutes, and after being pulled up and washed with water (abuse treatment), the color difference from the test hair color was measured again.
Table 9 shows the wave forming agents used and the measured color differences.
比較例７
ウエーブ形成剤としてＮｏ．７（セラック濃度０％＝精製水）を使用した他は、実施例２１と同様にして比較例７の毛束を得て、色差を測定した。使用したウエーブ形成剤及び測定した色差を表９に示す。
Comparative Example 7
No. as a wave forming agent. A hair bundle of Comparative Example 7 was obtained in the same manner as in Example 21 except that 7 (shellac concentration 0% = purified water) was used, and the color difference was measured. Table 9 shows the wave forming agents used and the measured color differences.
比較例８
ウエーブ形成剤として表１０に組成を示す、従来の還元剤を含むパーマ１剤と酸化剤を含むパーマ２剤からなるものを使用した他は、実施例２１と同様にして比較例８の毛束を得て、色差を測定した。使用したウエーブ形成剤及び測定した色差を表９に示す。
Comparative Example 8
The hair bundle of Comparative Example 8 was used in the same manner as in Example 21 except that a wave forming agent comprising a conventional permanent agent containing a reducing agent and two permanent agents containing an oxidizing agent was used. And the color difference was measured. Table 9 shows the wave forming agents used and the measured color differences.
表９の結果より、本発明のウエーブ形成剤によりウエーブを形成させても退色は殆ど生じないことが判る。これに対し従来の還元剤及び酸化剤を含むウエーブ形成剤でウエーブを形成させた場合には大きく退色している。これは、従来のウエーブ形成剤で処理した場合、還元剤が酸化重合した染料を退色させているのに対し、本発明のウエーブ形成剤は還元剤を含まないからだと考えられる。
また、本発明のウエーブ形成剤で処理した毛束は、虐待処理を施しても殆ど退色していない。これは、本発明においては毛髪が硬化したセラックにより覆われているので、染料が毛束から抜け落ちにくくなっているためと考えられる。
From the results of Table 9, it can be seen that even when the wave is formed by the wave forming agent of the present invention, the fading hardly occurs. On the other hand, when a wave is formed with a conventional wave forming agent containing a reducing agent and an oxidizing agent, the color is greatly faded. This is considered to be because when the treatment is performed with a conventional wave forming agent, the reducing agent discolors the dye that has undergone oxidative polymerization, whereas the wave forming agent of the present invention does not contain a reducing agent.
In addition, the hair bundle treated with the wave forming agent of the present invention is hardly discolored even when it is abused. This is presumably because in the present invention, since the hair is covered with the cured shellac, it is difficult for the dye to fall out of the hair bundle.
〈非パーマ毛束とストレートパーマ毛束〉
試験用非パーマ毛束の作成：
まず、ビューラックス社製黒色同一人毛束（商品名：人毛黒髪）をラウレス硫酸ナトリウム１０％溶液で洗浄し、根元から２００ｍｍで揃え、３０本を１束にして試験用非パーマ毛束を得た。
<Non-perm hair bundle and straight perm hair bundle>
Creating a non-perm hair bundle for testing:
First, the same human hair bundle (trade name: human hair black hair) manufactured by Beaulux Co., Ltd. is washed with a 10% sodium laureth sulfate solution, aligned at 200 mm from the root, and 30 non-perm hair bundles are made into one bundle. Obtained.
試験用ストレートパーマ毛束の作成：
上記のように得られた試験用非パーマ毛束に、上記表１０に記載したパーマ１剤を１０ｍＬ塗布し、１５分間放置後、流水で１分間すすぎ、ドライヤーで乾燥させてから１８０℃のヘアアイロンで処理した。その後、上記表１０に記載したパーマ２剤を１０ｍＬ塗布し、１０分間放置後、流水で１分間すすぎ、ドライヤーで乾燥させて、試験用ストレートパーマ毛束を得た。
Creating a straight perm hair bundle for testing:
Apply 10 mL of the permanent 1 listed in Table 10 to the test non-perm hair bundle obtained as described above, leave it for 15 minutes, rinse with running water for 1 minute, dry with a dryer, and then hair at 180 ° C. Treated with iron. Thereafter, 10 mL of the permanent 2 listed in Table 10 above was applied, allowed to stand for 10 minutes, rinsed with running water for 1 minute, and dried with a drier to obtain a straight perm hair bundle for testing.
実施例２２
上記のように得られた試験用ストレートパーマ毛束にウエーブ形成剤Ｎｏ．４（セラック濃度５．０％）を１０ｍＬ塗布して５分間放置後、当該試験用ストレート毛束を５０ｇの負荷でロッドに巻き、その状態で１０分間保持してから毛束をロッドから外した。ロッドから外した毛束についてウエーブのかかり具合を観察してから精製水で濡らし、濡れた状態で再度ウエーブのかかり具合を観察した。使用した毛束の種類、ウエーブ形成剤及び観察結果を表１１に示す。
Example 22
A wave-forming agent No. was added to the test straight perm hair bundle obtained as described above. After applying 10 mL of 4 (shellac concentration of 5.0%) and leaving it for 5 minutes, the test straight hair bundle was wound around the rod with a load of 50 g, held in that state for 10 minutes, and then the hair bundle was removed from the rod. . The hair bundle removed from the rod was observed for the degree of wave application, then wet with purified water, and the condition of the wave application was observed again in the wet state. Table 11 shows the type of hair bundle used, the wave forming agent, and the observation results.
実施例２３
試験用ストレートパーマ毛束に代えて試験用非パーマ毛束を使用した他は実施例２２と同様にして実施例２３の毛束を得て、ロッドから外した後及び濡れた状態でのウエーブのかかり具合を観察した。使用した毛束の種類、ウエーブ形成剤及び観察結果を表１１に示す。
Example 23
The hair bundle of Example 23 was obtained in the same manner as in Example 22 except that the test non-perm hair bundle was used instead of the test straight perm hair bundle, and after removing the hair bundle from the rod and in the wet state, The condition was observed. Table 11 shows the type of hair bundle used, the wave forming agent, and the observation results.
比較例９
ウエーブ形成剤としてＮｏ．７（セラック濃度０％＝精製水）を使用した他は、実施例２２と同様にして比較例９の毛束を得て、ロッドから外した後及び濡れた状態でのウエーブのかかり具合を観察した。使用した毛束の種類、ウエーブ形成剤及び観察結果を表１１に示す。
Comparative Example 9
No. as a wave forming agent. Except that 7 (shellac concentration 0% = purified water) was used, the hair bundle of Comparative Example 9 was obtained in the same manner as in Example 22, and the condition of the wave after being removed from the rod and wet was observed. did. Table 11 shows the type of hair bundle used, the wave forming agent, and the observation results.
比較例１０
試験用ストレートパーマ毛束に代えて試験用非パーマ毛束を使用した他は比較例９と同様にして比較例１０の毛束を得て、ロッドから外した後及び濡れた状態でのウエーブのかかり具合を観察した。使用した毛束の種類、ウエーブ形成剤及び観察結果を表１１に示す。
Comparative Example 10
The hair bundle of Comparative Example 10 was obtained in the same manner as in Comparative Example 9 except that a non-perm hair bundle for testing was used instead of the straight perm hair bundle for testing, and after removing the hair bundle from the rod and in the wet state, The condition was observed. Table 11 shows the type of hair bundle used, the wave forming agent, and the observation results.
表１１の結果より、本発明のウエーブ形成剤を用いれば、ストレートパーマを施した毛髪にも、パーマを施さない毛髪にもウエーブを形成できることがわかる。 From the results shown in Table 11, it can be seen that if the wave forming agent of the present invention is used, a wave can be formed on hair with a straight perm applied or on hair without a perm applied.
本発明のウエーブ形成剤、及びウエーブ形成方法によれば、毛髪の表面に被覆したセラックを、毛髪をカールさせた形状で硬化させることにより、通常のパーマ剤を用いたパーマ処理ではウエーブを形成させにくいダメージ毛であっても、健康毛と同程度のウエーブを形成させることができる。 According to the wave forming agent and the wave forming method of the present invention, the shellac coated on the surface of the hair is cured in a curled shape of the hair, so that a wave is formed in a permanent treatment using a normal permanent agent. Even a hard damaged hair can form a wave similar to a healthy hair.
Claims (5)