JP6154710B2 - 炭酸アパタイト成形体の製造方法、及び、それにより製造される炭酸アパタイト成形体 - Google Patents
炭酸アパタイト成形体の製造方法、及び、それにより製造される炭酸アパタイト成形体 Download PDFInfo
- Publication number
- JP6154710B2 JP6154710B2 JP2013202085A JP2013202085A JP6154710B2 JP 6154710 B2 JP6154710 B2 JP 6154710B2 JP 2013202085 A JP2013202085 A JP 2013202085A JP 2013202085 A JP2013202085 A JP 2013202085A JP 6154710 B2 JP6154710 B2 JP 6154710B2
- Authority
- JP
- Japan
- Prior art keywords
- carbonate
- phosphate
- carbonate apatite
- calcium
- molded body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
まず、炭酸アパタイト顆粒10の第1の製造方法について説明する。
まず、カルシウム化合物及びリン酸塩の少なくとも一方に炭酸基を含み、カルシウム化合物に充填剤が分散されたカルシウム化合物成形体とリン酸塩を含有するリン酸塩溶液とを準備する。本例では、カルシウム化合物として炭酸カルシウム(CaCO3)を用いて、充填剤として塩化ナトリウム(NaCl)を用いて、リン酸塩溶液としてリン酸水素二ナトリウム(Na2HPO4)の水溶液を用いる。
次に充填剤を溶解する溶媒を用いて充填剤を溶解することで、複数のポーラスが形成されたカルシウム化合物成形体を得る。
次に複数のポーラスが形成されたカルシウム化合物成形体の一部を酸で溶解して、複数のポーラスを互いに連通する。本例では、ポーラスが形成された炭酸カルシウム顆粒を酸に浸漬することで、ポーラス間の炭酸カルシウムを溶解して、ポーラス同士を連通する。
次に、複数のポーラスが連通したカルシウム化合物成形体とリン酸塩溶液とを接触させて炭酸アパタイトを生成する。本例では、ポーラスが連通した炭酸カルシウム顆粒を準備工程P101で準備したリン酸水素二ナトリウム水溶液中に浸漬して、炭酸カルシウムとリン酸水素二ナトリウムを反応させる。こうして炭酸ナトリウムを前駆体とした炭酸アパタイトが生成され、図1に示す炭酸アパタイト顆粒10が得られる。
次に、炭酸アパタイト顆粒10の第2の製造方法について説明する。
本例の準備工程P201、及び、ポーラス形成工程P202は、それぞれ第1の製造方法における準備工程P101、及び、ポーラス形成工程P102と同様に行う。
次に、複数のポーラスが形成されたカルシウム化合物成形体とリン酸塩溶液とを接触させて炭酸アパタイトを生成する。本例では、ポーラスが形成された炭酸カルシウム顆粒を準備工程P201で準備したリン酸水素二ナトリウム水溶液中に浸漬して、炭酸カルシウムとリン酸水素二ナトリウムを反応させる。こうしてポーラスが形成された炭酸アパタイトが得られる。このポーラスが形成された炭酸アパタイト顆粒を図6に示す。図6に示すように直径が約0.5mm〜約1.5mmの炭酸アパタイト顆粒13中に約100μm〜約300μmのポーラスPOが形成されている。
次に炭酸アパタイト顆粒13の一部を酸で溶解して、複数のポーラスPOを連通する。具体的には、ポーラスPOが形成された炭酸アパタイト顆粒13を酸に浸漬することで、ポーラスPO間の炭酸アパタイトを溶解して、ポーラスPO同士を連通する。
まず、次の様にα型リン酸三カルシウム成形体、及び、炭酸ナトリウムとリン酸水素二ナトリウムとを懸濁させた水溶液を準備する。
次に、α型リン酸三カルシウム顆粒を水に浸漬して、α型リン酸三カルシウム顆粒内に分散されている塩化ナトリウムを上記実施形態と同様に溶解する。こうしてα型リン酸三カルシウム顆粒中に除去された塩化ナトリウムに相当するポーラスが形成される。形成されるポーラスの大きさは上記実施形態におけるポーラスを同様とされる。
次に上記実施形態の第1の製造方法のように、ポーラス形成工程の後に連通工程を行う。本例では、複数のポーラスが形成されたα型リン酸三カルシウム顆粒を酸に浸漬することで、ポーラス間のα型リン酸三カルシウムを溶解して、ポーラス同士を連通する。本例で用いることのできる酸としては、上記実施形態の連通工程で用いる酸と同様の酸を用いることができる。こうしてポーラスが連通したα型リン酸三カルシウム顆粒が得られる。
次に、複数のポーラスが連通したα型リン酸三カルシウム顆粒を準備工程で準備した炭酸ナトリウムとリン酸水素二ナトリウムとを懸濁させた水溶液中に浸漬する。このとき、炭酸基が離脱しない温度で水熱処理を施すことが好ましい。こうしてα型リン酸三カルシウムを前駆体として炭酸アパタイトが生成され、連通孔が形成された炭酸アパタイト顆粒が得られる。
11・・・炭酸カルシウムブロック
12・・・炭酸カルシウム顆粒
13・・・ポーラスが形成された炭酸アパタイト顆粒
P101・・・準備工程
P102・・・ポーラス形成工程
P103・・・連通工程
P104・・・炭酸アパタイト生成工程
P201・・・準備工程
P202・・・ポーラス形成工程
P203・・・炭酸アパタイト形成工程
P204・・・連通工程
H・・・連通孔
PO・・・ポーラス
Claims (3)
- カルシウム化合物及びリン酸塩の少なくとも一方に炭酸基を含み、前記カルシウム化合物に充填剤が分散されたカルシウム化合物成形体と前記リン酸塩を含有するリン酸塩溶液とを準備する準備工程と、
前記充填剤を溶解する溶媒を用いて前記充填剤を溶解することで、複数のポーラスが形成されたカルシウム化合物成形体を得るポーラス形成工程と、
前記複数のポーラスが形成されたカルシウム化合物成形体の一部を酸で溶解して、前記複数のポーラスを連通する連通工程と、
前記複数のポーラスが連通したカルシウム化合物成形体と前記リン酸塩溶液とを接触させて炭酸アパタイトを生成する炭酸アパタイト生成工程と、
を備える炭酸アパタイト成形体の製造方法。 - カルシウム化合物及びリン酸塩の少なくとも一方に炭酸基を含み、前記カルシウム化合物に充填剤が分散されたカルシウム化合物成形体と前記リン酸塩を含有するリン酸塩溶液とを準備する準備工程と、
前記充填剤を溶解する溶媒を用いて前記充填剤を溶解することで、複数のポーラスが形成されたカルシウム化合物成形体を得るポーラス形成工程と、
前記複数のポーラスが形成されたカルシウム化合物成形体と前記リン酸塩溶液とを接触させて炭酸アパタイトを生成する炭酸アパタイト生成工程と、
前記炭酸アパタイトの一部を酸で溶解して、前記複数のポーラスを連通する連通工程と、
を備える炭酸アパタイト成形体の製造方法。 - 前記カルシウム化合物は、炭酸カルシウムである請求項1または2に記載の炭酸アパタイト成形体の製造方法。