JP5996427B2 - 混合硬化でのマルテンサイト系鋼の低温処理 - Google Patents
混合硬化でのマルテンサイト系鋼の低温処理 Download PDFInfo
- Publication number
- JP5996427B2 JP5996427B2 JP2012518125A JP2012518125A JP5996427B2 JP 5996427 B2 JP5996427 B2 JP 5996427B2 JP 2012518125 A JP2012518125 A JP 2012518125A JP 2012518125 A JP2012518125 A JP 2012518125A JP 5996427 B2 JP5996427 B2 JP 5996427B2
- Authority
- JP
- Japan
- Prior art keywords
- steel
- temperature
- trace
- ppm
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
この熱処理方法は、
(a)鋼の全体をそのオーステナイト化温度AC3よりも上に加熱するステップと、
(b)前記鋼をおよそ周囲温度に冷却するステップと、
(c)前記鋼を温度T1の低温媒体中に配置するステップと、
を含む。
Claims (7)
- マルテンサイト系鋼が0.4%〜3%のAl含有量で、および0℃未満のマルテンサイト変態温度Mfで金属間化合物および炭化析出物によって硬化されることができるように、ある含有量の他の金属を含むマルテンサイト系鋼を製造する方法であって、
この熱処理方法は、
(a)鋼の全体をそのオーステナイト化温度よりも上に加熱するステップと、
(b)前記鋼を室温に冷却するステップと、
(c)前記鋼を温度T1の低温媒体中に配置するステップと、
を含み、
温度T1が、マルテンサイト変態温度Mf未満であり、任意の温度T1について、鋼の最も熱い部分が、マルテンサイト変態温度Mfより低い温度に達した瞬間から前記低温媒体中に前記鋼を保持するための時間が、少なくともゼロ以外の時間t1に等しく、温度T1(+/−5℃の許容範囲の℃で)および時間t1(その単位は時間単位であり、その許容範囲は+/−5%である)が、式T1=f(t1)によって関連付けされており、関数fが、f(t)=57.666×(1−1/(t0.3−0.14)1.5)−97.389によって与えられることを特徴とする、方法。 - 前記鋼が、組成に関して、0.18〜0.3%のC、5〜7%のCo、2〜5%のCr、1〜2%のAl、1〜4%のMo+W/2、痕跡量から0.3%までのV、痕跡量から0.1%までのNb、痕跡量から50ppmまでのB、10.5〜15%のNi(但、Ni≧7+3.5Al)、痕跡量から0.4%までのSi、痕跡量から0.4%までのMn、痕跡量から500ppmまでのCa、痕跡量から500ppmまでの希土類元素、痕跡量から500ppmまでのTi、溶融金属から発生されたなら痕跡量から50ppmまでのO、または粉末冶金によって発生されたなら痕跡量から200ppmまでのO、痕跡量から100ppmまでのN、痕跡量から50ppmまでのS、痕跡量から1%までのCu、痕跡量から200ppmまでのP、残部のFeからなることを特徴とする、請求項1に記載の方法。
- 0.200%〜0.250%のC、12.00%〜14.00%のNi、5.00%〜7.00%のCo、2.5%〜4.00%のCr、1.30%〜1.70%のAl、1.00%〜2.00%のMoとすることを特徴とする、請求項2に記載の方法。
- 必要な最小維持時間t1が、1時間より長いことを特徴とする、請求項1から3のいずれか一項に記載の方法。
- ステップ(b)で、前記鋼が、空気と等しいまたは空気より高い弾性を有する媒体中で急冷することによって、室温に冷却されることを特徴とする、請求項1から4のいずれか一項に記載の方法。
- ステップ(b)における冷却の間の部品の表面温度が、80℃の温度に達した瞬間後70時間未満に、前記鋼が前記低温媒体中に配置されることを特徴とする、請求項1から5のいずれか一項に記載の方法。
- 前記鋼中の残留オーステナイトレベルが3%未満であることを特徴とする、請求項1から6のいずれか一項に記載の方法。