JP5903364B2 - 刺繍用シート - Google Patents
刺繍用シート Download PDFInfo
- Publication number
- JP5903364B2 JP5903364B2 JP2012228330A JP2012228330A JP5903364B2 JP 5903364 B2 JP5903364 B2 JP 5903364B2 JP 2012228330 A JP2012228330 A JP 2012228330A JP 2012228330 A JP2012228330 A JP 2012228330A JP 5903364 B2 JP5903364 B2 JP 5903364B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- embroidery
- sheet
- pressure
- sensitive adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
特許文献1によれば、安価な構成で、布地にクロスステッチ等の刺繍を容易に形成できるとともに、型紙を使用することなく、容易かつ迅速に、模様の刺繍を行うことができるとされている。
本発明は下記態様を含む。
[2] 前記剥離紙のガーレー剛度が0.1〜10(mN)である[1]の刺繍用シート。
[3] 前記表面基材にエンボス加工が施されている[1]又は[2]の刺繍用シート。
また、本発明の粘着シートを刺繍用シートに適用すれば、基布に貼着する前の表面基材への図柄の描画が容易で、美麗で図柄の自由度の高い刺繍を施すことが可能となる。
なお、本明細書において説明する不透明度とは、JIS P 8149に準拠した方法で測定されるものであり、本明細書中においては、粘着シート(刺繍用シート)のシートの厚み方向全体での不透明度を示す指標としている。
本実施形態の刺繍用シート(粘着シート)1は、図2に示すように、剥離紙(セパレータ)4と、粘着剤層3と、表面基材2とがこの順で積層されてなる。上記の粘着剤層3は、水溶性あるいは水分散性を有する粘着剤から形成され、かつ、上記の表面基材2は、水溶性あるいは水分散性を有する透明または半透明フィルムから形成されてなる。そして、刺繍用シート1は、シート全体におけるJIS P 8149に準拠した不透明度が20%以下とされ、概略構成されている。
さらに、表面基材2の裏面2Bには、粘着剤層3を保護するとともに、刺繍用シート1を使用する際に剥離できる剥離紙4が貼付されている。
表面基材2は、上述したように、水溶性を有する透明または半透明フィルムから形成される。表面基材2をなす水溶性の透明または半透明フィルムの材料としては、ポリビニルアルコール系樹脂であることが、筆記性に優れる点で特に好ましい。
水溶性可塑剤の含有量が、ポリビニルアルコール100重量部に対して30部を超えると、表面基材が柔らかくなり過ぎて寸法安定性が低下する。一方、水溶性可塑剤の含有量がポリビニルアルコール100重量部に対して1部未満だと、表面基材の柔軟性が不足するため、刺繍用シートを用いて刺繍作業を行う際の糸切れや、表面基材における針穴からの破断等が生じるおそれがある。
粘着剤層3は、上述したように、水溶性あるいは水分散性を有する粘着剤から形成される。
本実施形態では、粘着剤層3をなす粘着剤として水溶性のものを用いる場合には、ポリ(メタ)アクリルアミドを主成分とし、さらに、該主成分の柔軟化剤として水溶性可塑剤を含有する粘着剤を採用することができる。
また、粘着剤層3をなす粘着剤として水分散性のものを用いる場合には、アクリル酸を主成分とし、さらに、該主成分の柔軟化剤として水溶性可塑剤を含有するとともに、凝集力向上のための架橋剤を含有する粘着剤を採用することができる。
本実施形態において、粘着剤層3に用いる水溶性の粘着剤について以下に詳述する。
水溶性の粘着剤としては、特に限定されないが、従来からこの分野で使用されている水溶性の粘着剤を何ら制限無く用いることができ、例えば、特開2000−109774号公報に記載されたものを用いることができる。
本実施形態において、粘着剤層3に用いる水分散性の粘着剤について以下に詳述する。
水分散性の粘着剤としては、特に限定されないが、例えば、特開平11−140407号公報に記載されたものを用いることが可能であり、カルボキシル基含有モノマーおよび特定のアクリル系モノマーを主成分として乳化共重合して得られた共重合体に、中和アルカリと塩基性リン酸塩および特定の界面活性剤を含有してなる水分散液を用いることができる。
本発明においては、上述した表面基材2に水溶性ポリビニルアルコール(PVA)系樹脂を主成分とするフィルムを用い、さらに、粘着剤層3にも水溶性あるいは水分散性の粘着剤を用いる。この場合、例えば、表面基材2および粘着剤層3の両方を、水溶性あるいは水分散性で統一してもよいし、または、粘着剤層3が水分散性であっても良い。いずれの組み合わせであっても、本発明の刺繍用シート1を用いて使用者が刺繍を施した後、水あるいは温水に浸漬させた際に充分な溶解性が得られる。
剥離紙(セパレータ)4は、本発明に係る刺繍用シート(粘着シート)1において、粘着剤層3を保護するとともに台紙として機能するセパレータである。このような剥離紙4は、後述するシート全体における不透明度の観点から、透明材料等で構成することが好ましい。
剥離紙の縦方向のガーレー剛度が0.1(mN)未満だと、剥離紙としてのコシの強さが不足するため、粘着シートの取り扱いが難しくなるとともに、表面基材の収縮を剥離紙で抑えきることができず、表面基材側へのカール(反り、曲がり)が発生し易くなる。また、剥離紙の縦方向のガーレー剛度が10(mN)以下であれば、粘着シートとしての充分な取り扱い性、及び、カール抑制の効果が得られる一方、ガーレー剛度が10(mN)を超えると製造コスト等の点で不経済であることから、これを上限とすることが好ましい。
本発明に係る刺繍用シート(粘着シート)1は、シート全体におけるJIS P 8149に準拠した不透明度が20%以下に規定される。
また、刺繍用シート1における表面基材2の表面に、格子パターン等を印刷した場合は、その印刷部以外の不透明度が20%以下であれば良い。すなわち、刺繍用シート1を図柄の上に重ね合わせた際に、表面基材2の表面側から図柄が明瞭に視認できる必要があり、これは、表面基材2の表面に、後述のエンボス等を設けた場合も同様である。
また、不透明度のより好ましい範囲は、0.1〜10%である。
本実施形態の刺繍用シート1を使用する場合には、まず、刺繍用シート1を所望の図柄が表示された印刷物等に重ね合わせ、表面基材2上に、印刷物等の図柄と同等の図柄52(図3を参照)をトレースして書き込む。
次いで、図3に示すように、刺繍を施そうとする布材50の表面の所定箇所に、剥離紙4から剥離させた表面基材2及び粘着剤層3を貼着して固定する。その後、刺繍糸で、図柄52に沿った刺繍(図示略)を形成する。
この際、上記の水または温水を用いた一般的な水洗方法以外に、例えば、超音波洗浄や、ウォータージェット法などを用いることも可能である。
以上説明したように、本発明の刺繍用シート(粘着シート)1によれば、表面基材2および粘着剤層3の両方を水溶性あるいは水分散性を有する材料から構成し、さらに、シート全体の不透明度を適正範囲に規定することで、基布50に貼着する前の表面基材2への図柄の描画が容易となる。従って、使用性が顕著に向上し、美麗で図柄の自由度の高い刺繍を施すことが可能となる。
また、本発明の刺繍用シート(粘着シート)1によれば、剥離紙4のガーレー剛度を適正に規定することで、生産過程における反りを抑制でき、生産効率の向上が実現できる。
[実施例1]
まず、市販のセパレータ;剥離紙(王子タック(株)製;透明PETセパレータ 38μm)の上に、水分散性アクリル系粘着剤(サイデン化学(株)製;商品名:AT−813)を塗工し、110℃の熱風乾燥機で90秒間乾燥させ、厚みが20μmの水溶性の粘着剤層を形成した。
さらに、上記水溶性の粘着剤層上に、水溶性PVAフィルム;表面基材(日本合成化学工業(株)製;ハイセロン(登録商標)/完溶温度2〜5℃、エンボス処理あり)を貼り合わせることにより、粘着シートを作製した。
セパレータとして、「王子特殊紙(株)製;透明OPPセパレータ 60μm」を用いた点以外は、実施例1と同様にして粘着シートを作製した。
表面基材として、水溶性PVAフィルム(日本合成化学工業(株)製;ハイセロン(登録商標)/完溶温度2〜5℃、エンボス処理なし)を用い、セパレータとして「王子特殊紙(株)製;透明OPPセパレータ 60μm」を用いた点以外は、全て実施例1と同様にして粘着シートを作製した。
粘着剤として、水溶性アクリル系粘着剤(ビックテクノス(株)製;商品名:AR2090)を用い、セパレータとして、「王子特殊紙(株)製;透明PETセパレータ 75μm」を用いた点以外は、全て実施例1と同様にして粘着シートを作製した。
セパレータ基材として、「王子特殊紙(株)製;グラシン紙30g/m2」を用いた点以外は、実施例1と同様にして粘着シートを作製した。
セパレータ基材として、「王子タック(株)製;両ポリ上質紙110g/m2」を用いた点以外は、実施例1と同様にして粘着シートを作製した。
表面基材として、水溶性PVAフィルム(日本合成化学工業(株)製;ハイセロン(登録商標)/完溶温度2〜5℃、エンボス処理なし)を用い、セパレータ基材として、「王子特殊紙(株)製;グラシン紙30g/m2」を用いた点以外は、実施例1と同様にして粘着シートを作製した。
表面基材として、透明PETフィルム(東レ(株)製;商品名:ルミラーS10(登録商標)/50μm)を用いた点以外は、実施例1と同様にして粘着シートを作製した。
[水溶性または水分散性の評価試験]
上記実施例および比較例で作製した粘着シートから、50mm×50mm角のサンプルシートを切り取り、このサンプルシートを、刺繍布(商品名:コスモ綿刺繍布;オックスフォード#8000オフホワイト)に、2kgロールにて一往復することで圧着した。
上記条件による圧着の後、温度23℃、湿度50%の環境下にて7日間(168hr)放置し、試験片を得た。
上記実施例および比較例で作製した粘着シートについて、そのシート厚み方向全体における不透明度を、日本工業規格:JIS P 8149に準拠して測定し、結果を下記表1に示した。
テスト画像(図柄)上に、上記実施例および比較例で作製した粘着シート(セパレータ付き)を重ね合わせ、水性ペンを用いて、フリーハンドで画像を書き写した。この際の書き易さ(描画の容易性)を、以下に示す5段階で評価し、結果を下記表1に示した。
(5点):細部まではっきり書き写すことができ、非常に良好。
(4点):実用上問題なく書き写すことができ、良好。
(3点):細部がぼやけ、正確に書き写すことが難しい。
(2点):輪郭がぼやけ、形状が分かり難い。
(1点):画像がほとんど見えない。
上記実施例および比較例で用いたセパレータについて、その縦方向のガーレー剛度(mN)を、『J.TAPPI 紙パルプ試験方法(No.40−83)「荷重曲げ法による紙及び板紙のこわさ試験方法(ガーレー法)」』に準拠した方法で測定し、結果を下記表1に示した。
上記実施例および比較例で作製した粘着シートについて、この粘着シートを10cm角にカットし、23℃・50%RH環境下に10分間放置した後、粘着シートを平板状に載置して、カールした状態での形状を確認するとともに、四隅の平均値を測定し、取り扱い易さの評価指標とした。
表1に示すように、本発明の請求項1で規定した構成を有する実施例1〜4の粘着シート(刺繍用シート)は、上記条件で試験片が完全溶解するか分散するまでの時間が、全て20秒以下となっており、また、JIS P 8149に準拠する不透明度が、全て6.5%以下となっている。
また、実施例1〜4の粘着シートは、上記条件による描画性の評価が、全て4点以上となっている。
また、実施例1〜4の粘着シートは、そのガーレー剛度(縦方向)が、0.18から0.96(mN)であり、実用上、充分な剛度を有していることが確認できた。
また、実施例1〜4の粘着シートは、上記のガーレー剛度を有することにより、カールが20mm以内に抑えられており、実用上問題ないことが確認できた。
2…表面基材、
2A…表面、
2B…裏面、
3…粘着剤層、
4…剥離紙、
50…布剤、
52…図柄、
Claims (3)
- 剥離紙と、粘着剤層と、表面基材とがこの順で積層されてなり、刺繍を施そうとする布材に貼着して使用する刺繍用シートであって、
前記粘着剤層が、水溶性を有する粘着剤から形成され、前記粘着剤がポリ(メタ)アクリルアミドを主成分とし、さらに水溶性可塑剤を含有し、
前記表面基材が、水溶性ポリビニルアルコール(PVA)系樹脂を主成分とし、ポリビニルアルコール100重量部に対して1部〜30部の水溶性可塑剤を含有する透明または半透明フィルムから形成されてなり、
さらに、シート全体におけるJIS P 8149に準拠した不透明度が20%以下であることを特徴とする刺繍用シート。 - 前記剥離紙のガーレー剛度が0.1〜10(mN)である請求項1に記載の刺繍用シート。
- 前記表面基材にエンボス加工が施されている請求項1又は請求項2に記載の刺繍用シート。