JP5678121B2 - 塗工装置、及び塗工方法 - Google Patents
塗工装置、及び塗工方法 Download PDFInfo
- Publication number
- JP5678121B2 JP5678121B2 JP2013085157A JP2013085157A JP5678121B2 JP 5678121 B2 JP5678121 B2 JP 5678121B2 JP 2013085157 A JP2013085157 A JP 2013085157A JP 2013085157 A JP2013085157 A JP 2013085157A JP 5678121 B2 JP5678121 B2 JP 5678121B2
- Authority
- JP
- Japan
- Prior art keywords
- base film
- film
- resin coating
- coating
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
液を塗工することにより傷やロール跡のない樹脂塗工フィルムを製造する際に好適な塗工
装置及び塗工方法に関する。
基材フィルムがガイドロールから浮上してしまうと、基材フィルムがばたついたりガイドロールが空回りするといった現象が起こり、そして、ばたついた基材フィルムがガイドロールに接触すると、基材フィルムに傷が入る原因となる。
また、本発明に係る塗工方法は、連続的に搬送される基材フィルム上に樹脂塗工液を塗工し、樹脂塗工液の塗工された前記基材フィルムを1又は2以上のロールで支持しながら搬送して、前記基材フィルム上に前記樹脂塗工液を塗工することによって光学フィルムを製造する塗工方法であって、前記基材フィルムにおける前記樹脂塗工液が塗工される面とは反対側の面が前記ロールと接しており、前記塗工された樹脂塗工液の粘度が1000mPa・s以下である範囲内で該基材フィルムと接する少なくとも1以上の前記ロールの表面には、幅0.5mm未満の溝が形成されていることを特徴とする。
なお、図1の基材フィルムIに示される矢印は、基材フィルムの搬送方向を示す。
図2は、該ガイドロール2aの表面を展開して示した図である。該図2に示したように、本実施形態におけるガイドロール2aの表面には、幅0.5mm未満の溝10がロールの全幅に亘って形成されている。また、該溝10は、ロールの円周方向、即ちロールの回転方向に対して、好ましくは0〜60°の角度を成して形成され、本実施形態では、約45°の角度を成して、いわゆる螺旋状に形成されている。
このような幅で溝を形成することにより、基材フィルムの浮上がより確実に防止され、しかも樹脂塗工膜に溝跡が形成されることについても、より一層確実に防止される。
好ましくは、塗工された樹脂塗工液の粘度が800mPa・s以下である範囲内に設置されるガイドロール2aの少なくとも一つを上記のような構成とし、より好ましくは、塗工された樹脂塗工液の粘度が1000mPa・s以下である範囲内全てのガイドロール2aを上述の如く構成するものとし、これにより、上記効果がより一層顕著なものとなる。
このような樹脂の中でも、透明性、配向性及び延伸性に優れるという観点から、ポリイミドを好適に使用することができる。
上記溶剤の中では、メチルイソブチルケトンが樹脂組成物の溶解性に優れ、且つ、基材フィルムを浸食することがないので特に好ましい。
これら溶剤は、1種又は2種以上を任意に組み合わせて使用することができる。
・基材フィルムI:トリアセチルセルロースフィルム。
・樹脂塗工液A:ポリエステル系ポリウレタン樹脂(東洋紡製「VYRON UR−1400」)を、溶媒としてメチルイソブチルケトンを用いて溶解し、ポリエステル系ポリウレタン樹脂の濃度が5重量%、粘度が5mPa・sとなるように調整したもの。
・樹脂塗工液B:2,2’−ビス(3,4−ジカルボキシフェニル)ヘキサフルオロプロパンおよび2,2−ビス(トリフルオロメチル)−4,4’ジアミノビフェニルから合成されたポリイミドを、溶媒としてメチルイソブチルケトンを用いて溶解し、粘度が700mPa・sとなるように調整したもの。
図1に示したような前記実施形態の塗工装置を用い、基材フィルムI上に樹脂塗工液A(粘度5mPa・s)を塗工し、樹脂塗工膜を形成した。具体的には、ダイコータ5によって樹脂塗工液を基材フィルムIの一面に塗工し、表面全体に幅0.1mm、深さ0.05mmの溝が0.25mm間隔で格子状に形成されたガイドロール2a(半径50mm)を経由させた後、120℃で3分間熱処理を行い、次いで、テンター延伸機にて樹脂膜層を有する基材フィルムIの幅方向の端部を把持し、160℃で1.15倍に延伸し、樹脂塗工膜を有する透明の樹脂塗工フィルムを作製した。
幅0.1mm、深さ0.05mmの溝が0.25mm間隔で螺旋状に形成されたガイドロール2aを使用することを除き、他は実施例1の条件と同様にして樹脂塗工フィルムを作製した。
樹脂塗工液B(粘度700mPa・s)を使用することを除き、他は実施例1の条件と同様にして樹脂塗工フィルムを作製した。
幅0.1mm、深さ0.05mmの溝が0.25mm間隔で螺旋状に形成されたガイドロール2aを使用し、且つ樹脂塗工液B(粘度700mPa・s)を使用することを除き、他は実施例1の条件と同様にして樹脂塗工フィルムを作製した。
幅0.5mm、深さ0.5mmの溝が12mm間隔で格子状に形成されたガイドロール2aを使用することを除き、他は実施例1の条件と同様にして樹脂塗工フィルムを作製した。
幅0.5mm、深さ0.5mmの溝が12mm間隔で螺旋状に形成されたガイドロール2aを使用することを除き、他は実施例1の条件と同様にして樹脂塗工フィルムを作製した。
幅0.5mm、深さ0.5mmの溝が12mm間隔で格子状に形成されたガイドロール2aを使用し、且つ樹脂塗工液B(粘度700mPa・s)を使用することを除き、他は実施例1の条件と同様にして樹脂塗工フィルムを作製した。
幅0.5mm、深さ0.5mmの溝が12mm間隔で螺旋状に形成されたガイドロール2aを使用し、且つ樹脂塗工液B(粘度700mPa・s)を使用することを除き、他は実施例1の条件と同様にして樹脂塗工フィルムを作製した。
溝が形成されていないガイドロール2aを使用することを除き、他は実施例1の条件と同様にして樹脂塗工フィルムを作製した。
レーザ変位計(キーエンス社製、LT−9000)を用い、停止状態におけるガイドロール2a上の基材フィルム位置と、運転状態における位置とを比較し、変位があれば浮きが発生していると判断した。
ガイドロール2aと基材フィルムとの接触状態を目視により確認した。
得られた樹脂塗工フィルムを100mm×100mmの大きさに裁断し、試験片を作成した。その試験片の、基材フィルム側(樹脂塗工膜が形成されていない側)に粘着材を用いて黒色板を貼り付け、樹脂塗工膜側から蛍光灯を用いて可視光線を照射し、その反射状態を目視により評価することにより、溝跡の有無の評価を行った。尚、その際に撮影した写真を、図4〜図11に示す。
これに対し、溝幅0.1の溝を有するガイドーロールを用いた実施例1〜4では、何れも基材フィルムの浮上を防止しつつ、また、図4〜図7に示すように、樹脂塗工膜にも溝跡が形成されなかったことが認められた。
1 塗工装置
2a、2b ガイドロール
3 バックアップロール
4 ダイコーター
10 溝
Claims (6)
- 連続的に搬送される基材フィルム上に樹脂塗工液を塗工する塗工手段と、該塗工手段により樹脂塗工液の塗工された前記基材フィルムと接する1又は2以上のロールとを備え、前記基材フィルム上に前記樹脂塗工液を塗工することによって光学フィルムを製造する塗工装置であって、
前記基材フィルムにおける前記樹脂塗工液が塗工される面とは反対側の面が前記ロールと接しており、
前記塗工された樹脂塗工液の粘度が1000mPa・s以下である範囲内で該基材フィルムと接する少なくとも1以上の前記ロールの表面には、幅0.5mm未満の溝が形成されていることを特徴とする塗工装置。 - 前記溝が、前記基材フィルムと接する幅全域に亘って前記ロール表面に形成されていることを特徴とする請求項1記載の塗工装置。
- 前記溝が、格子状、または、一端側から他端側に向かう螺旋状に形成されていることを特徴とする請求項1または2に記載の塗工装置。
- 連続的に搬送される基材フィルム上に樹脂塗工液を塗工し、樹脂塗工液の塗工された前記基材フィルムを1又は2以上のロールで支持しながら搬送して、前記基材フィルム上に前記樹脂塗工液を塗工することによって光学フィルムを製造する塗工方法であって、
前記基材フィルムにおける前記樹脂塗工液が塗工される面とは反対側の面が前記ロールと接しており、
前記塗工された樹脂塗工液の粘度が1000mPa・s以下である範囲内で該基材フィルムと接する少なくとも1以上の前記ロールの表面には、幅0.5mm未満の溝が形成されていることを特徴とする塗工方法。 - 前記溝が、前記基材フィルムと接する幅全域に亘って前記ロール表面に形成されていることを特徴とする請求項4記載の塗工方法。
- 前記溝が、格子状、または、一端側から他端側に向かう螺旋状に形成されていることを特徴とする請求項4または5に記載の塗工方法。