JP5642211B2 - 固体酸触媒 - Google Patents
固体酸触媒 Download PDFInfo
- Publication number
- JP5642211B2 JP5642211B2 JP2013022197A JP2013022197A JP5642211B2 JP 5642211 B2 JP5642211 B2 JP 5642211B2 JP 2013022197 A JP2013022197 A JP 2013022197A JP 2013022197 A JP2013022197 A JP 2013022197A JP 5642211 B2 JP5642211 B2 JP 5642211B2
- Authority
- JP
- Japan
- Prior art keywords
- monolith
- skeleton
- ion exchanger
- exchanger
- continuous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
孔容積が1〜50ml/gであり、陽イオン交換基が均一に分布され、陽イオン交換容量が0.5mg 当量/g乾燥多孔質体以上の多孔質イオン交換体からなる固体酸触媒(特開2002−346392号公報)が提案されている。この固体酸触媒によれば、陽イオン交換基密度が高く、大きな細孔容積および比表面積を有するため、高い触媒活性を示すと共に、原料または生成物、あるいはその混合物からなる気体や液体の透過性に優れ、有機反応を効率良く短時間で、かつ高い反応率で進行させ得ることができる。なお、特開2002−306976号にはこの多孔質イオン交換体の製造方法の詳細が開示されている。
オン交換基が該多孔質イオン交換体中に均一に分布しており、且つ該連続マクロポア構造体(乾燥体)の切断面のSEM画像において、断面に表れる骨格部面積が、画像領域中25〜50%である有機多孔質イオン交換体からなる固体酸触媒を提供するものである。
〜5mg当量/g乾燥多孔質体であり、陽イオン交換基が該多孔質イオン交換体中に均一
に分布している有機多孔質イオン交換体からなる固体酸触媒固体酸触媒を提供するものである。
第1のモノリスイオン交換体は、モノリスに陽イオン交換基を導入することで得られるものであり、気泡状のマクロポア同士が重なり合い、この重なる部分が水湿潤状態で平均直径30〜300μm、好ましくは30〜200μm、特に35〜150μmの開口(メソポア)となる連続マクロポア構造体である。モノリスイオン交換体の開口の平均直径は、モノリスに陽イオン交換基を導入する際、モノリス全体が膨潤するため、モノリスの開口の平均直径よりも大となる。開口の平均直径が30μm未満であると、液体や気体の透過時の圧力損失が大きくなってしまうため好ましくなく、開口の平均直径が大き過ぎると、液体や気体とモノリスイオン交換体との接触が不十分となり、その結果、触媒による反応効率が低下してしまうため好ましくない。なお、本発明では、乾燥状態のモノリス中間体の開口の平均直径、乾燥状態のモノリスの開口の平均直径及び乾燥状態のモノリスイオン交換体の開口の平均直径は、水銀圧入法により測定される値である。また、水湿潤状態のモノリスイオン交換体の開口の平均直径は、乾燥状態のモノリスイオン交換体の開口の平均直径に、膨潤率を乗じて算出される値である。具体的には、水湿潤状態のモノリスイオン交換体の直径がx1(mm)であり、その水湿潤状態のモノリスイオン交換体を乾燥させ、得られる乾燥状態のモノリスイオン交換体の直径がy1(mm)であり、この乾燥状態のモノリスイオン交換体を水銀圧入法により測定したときの開口の平均直径がz1(μm)であったとすると、水湿潤状態のモノリスイオン交換体の開口の平均直径(μm)は、次式「水湿潤状態のモノリスイオン交換体の開口の平均直径(μm)=z1×(x1/y1)」で算出される。また、イオン交換基導入前の乾燥状態のモノリスの開口の平均直径、及びその乾燥状態のモノリスにイオン交換基導入したときの乾燥状態のモノリスに対する水湿潤状態のモノリスイオン交換体の膨潤率がわかる場合は、乾燥状態のモノリスの開口の平均直径に、膨潤率を乗じて、モノリスイオン交換体の空孔の水湿潤状態の平均直径を算出することもできる。
数」と言う。)で示すと、0.001〜0.1MPa/m・LVの範囲、特に0.001〜0.05MPa/m・LVであることが好ましい。差圧係数および全細孔容積がこの範囲にあれば、これを固体酸触媒として用いた場合、液体または気体との接触面積が大きく、かつ液体や気体の円滑な流通が可能となる上に、十分な機械的強度を有しているため好ましい。
しくは3〜5mg当量/g乾燥多孔質体である。特開2002−306976号に記載されているような本発明とは異なる連続マクロポア構造を有する従来型のモノリス状有機多孔質イオン交換体では、実用的に要求される低い圧力損失を達成するために、開口径を大きくすると、全細孔容積もそれに伴って大きくなってしまうため、体積当りのイオン交換容量が低下する、体積当りの交換容量を増加させるために全細孔容積を小さくしていくと、開口径が小さくなってしまうため圧力損失が増加するといった欠点を有していた。それに対して、本発明のモノリスイオン交換体は、開口径を更に大きくすると共に、連続マクロポア構造体の骨格を太くする(骨格の壁部を厚くする)ことができるため、透過時の圧力損失を低く押さえたままで触媒活性を飛躍的に大きくすることができる。なお、イオン交換基が表面のみに導入された多孔質体のイオン交換容量は、多孔質体やイオン交換基の種類により一概には決定できないものの、せいぜい500μg当量/gである。
ルエン、ポリビニルベンジルクロライド、ポリビニルビフェニル、ポリビニルナフタレン等の芳香族ビニルポリマー;ポリエチレン、ポリプロピレン等のポリオレフィン;ポリ塩化ビニル、ポリテトラフルオロエチレン等のポリ(ハロゲン化ポリオレフィン);ポリアクリロニトリル等のニトリル系ポリマー;ポリメタクリル酸メチル、ポリメタクリル酸グリシジル、ポリアクリル酸エチル等の(メタ)アクリル系ポリマー等の架橋重合体が挙げられる。上記ポリマーは、単独のビニルモノマーと架橋剤を共重合させて得られるポリマーでも、複数のビニルモノマーと架橋剤を重合させて得られるポリマーであってもよく、また、二種類以上のポリマーがブレンドされたものであってもよい。これら有機ポリマー材料の中で、連続マクロポア構造形成の容易さ、イオン交換基導入の容易性と機械的強度の高さ、および酸・アルカリに対する安定性の高さから、芳香族ビニルポリマーの架橋重合体が好ましく、特に、スチレン−ジビニルベンゼン共重合体やビニルベンジルクロライド−ジビニルベンゼン共重合体が好ましい材料として挙げられる。
第1のモノリスイオン交換体は、イオン交換基を含まない油溶性モノマー、界面活性剤及び水の混合物を撹拌することにより油中水滴型エマルジョンを調製し、次いで油中水滴型エマルジョンを重合させて全細孔容積が5〜16ml/gの連続マクロポア構造のモノ
リス状の有機多孔質中間体を得るI工程、ビニルモノマー、一分子中に少なくとも2個以上のビニル基を有する架橋剤、ビニルモノマーや架橋剤は溶解するがビニルモノマーが重合して生成するポリマーは溶解しない有機溶媒及び重合開始剤からなる混合物を調製するII工程、II工程で得られた混合物を静置下、且つ該I工程で得られたモノリス状の有機多孔質中間体の存在下に重合を行い、該有機多孔質中間体の骨格より太い骨格を有する骨太有機多孔質体を得るIII工程、該III工程で得られた骨太有機多孔質体に陽イオン交換基を導入するIV工程、を行なうことにより得られる。
ェニル、ビニルナフタレン等の芳香族ビニルモノマー;エチレン、プロピレン、1-ブテ
ン、イソブテン等のα-オレフィン;ブタジエン、イソプレン、クロロプレン等のジエン
系モノマー;塩化ビニル、臭化ビニル、塩化ビニリデン、テトラフルオロエチレン等のハロゲン化オレフィン;アクリロニトリル、メタクリロニトリル等のニトリル系モノマー;酢酸ビニル、プロピオン酸ビニル等のビニルエステル;アクリル酸メチル、アクリル酸エチル、アクリル酸ブチル、アクリル酸2-エチルヘキシル、メタクリル酸メチル、メタク
リル酸エチル、メタクリル酸プロピル、メタクリル酸ブチル、メタクリル酸2−エチルヘキシル、メタクリル酸シクロヘキシル、メタクリル酸ベンジル、メタクリル酸グリシジル等の(メタ)アクリル系モノマーが挙げられる。これらモノマーは、1種単独又は2種以上を組み合わせて使用することができる。本発明で好適に用いられるビニルモノマーは、スチレン、ビニルベンジルクロライド等の芳香族ビニルモノマーである。
時に共存させるモノリス中間体の架橋密度とほぼ等しくなるように用いることが好ましい。両者の使用量があまりに大きくかけ離れると、生成したモノリス中で架橋密度分布の偏りが生じ、イオン交換基導入反応時にクラックが生じやすくなる。
メチルバレロニトリル)、2,2’-アゾビス(2−メチルブチロニトリル)、2,2’-アゾビス(4-メトキシ-2,4-ジメチルバレロニトリル)、2,2’-アゾビスイソ酪酸ジメチル、4,4’-アゾビス(4-シアノ吉草酸)、1,1’-アゾビス(シクロヘキサ
ン-1-カルボニトリル)、過酸化ベンゾイル、過酸化ラウロイル、過硫酸カリウム、過硫
酸アンモニウム、テトラメチルチウラムジスルフィド等が挙げられる。重合開始剤の使用量は、モノマーの種類や重合温度等によって大きく変動するが、ビニルモノマーと架橋剤の合計量に対して、約0.01〜5%の範囲で使用することができる。
ジメチルバレロニトリル)、過酸化ベンゾイル、過酸化ラウロイル、過硫酸カリウム等を用いたときには、不活性雰囲気下の密封容器内において、30〜100℃で1〜48時間加熱重合させればよい。加熱重合により、モノリス中間体の骨格に吸着、分配したビニルモノマーと架橋剤が該骨格内で重合し、該骨格を太らせる。重合終了後、内容物を取り出し、未反応ビニルモノマーと有機溶媒の除去を目的に、アセトン等の溶剤で抽出して骨太のモノリスを得る。
濃硫酸、発煙硫酸を用いてスルホン化する方法;モノリスに均一にラジカル開始基や連鎖移動基を骨格表面及び骨格内部に導入し、スチレンスルホン酸ナトリウムやアクリルアミド−2−メチルプロパンスルホン酸をグラフト重合する方法;同様にグリシジルメタクリレートをグラフト重合した後、官能基変換によりスルホン酸基を導入する方法等が挙げられる。これらの方法のうち、スルホン酸基を導入する方法については、クロロ硫酸を用いてスチレン-ジビニルベンゼン共重合体にスルホン酸基を導入する方法が、陽イオン交換
基を均一かつ定量的に導入できる点で好ましい。なお、導入するイオン交換基としては、カルボン酸基、イミノ二酢酸基、スルホン酸基、リン酸基、リン酸エステル基等のカチオン交換基が挙げられる。
第2のモノリスイオン交換体は、イオン交換基が導入された全構成単位中、架橋構造単位を0.3〜5.0モル%含有する芳香族ビニルポリマーからなる太さが1〜60μmの三次元的に連続した骨格と、その骨格間に直径が10〜100μmの三次元的に連続した空孔とからなる共連続構造体であって、全細孔容積が0.5〜5ml/gであり、イオン
交換容量が1〜5mg当量/g乾燥多孔質体であり、陽イオン交換基が該多孔質イオン交
換体中に均一に分布している。
数」と言う。)で示すと、0.001〜0.5MPa/m・LVの範囲、特に0.001〜0.1MPa/m・LVである。差圧係数および全細孔容積がこの範囲にあれば、これを固体酸触媒として用いた場合、液体または気体との接触面積が大きく、かつ液体や気体の円滑な流通が可能となる上に、十分な機械的強度を有しているため好ましい。
ベンジルクロライド、ポリビニルビフェニル、ポリビニルナフタレン等が挙げられる。上記ポリマーは、単独のビニルモノマーと架橋剤を共重合させて得られるポリマーでも、複数のビニルモノマーと架橋剤を重合させて得られるポリマーであってもよく、また、二種類以上のポリマーがブレンドされたものであってもよい。これら有機ポリマー材料の中で、共連続構造形成の容易さ、イオン交換基導入の容易性と機械的強度の高さ、および酸・アルカリに対する安定性の高さから、スチレン−ジビニルベンゼン共重合体やビニルベンジルクロライド−ジビニルベンゼン共重合体が好ましい。
第2のモノリスイオン交換体は、イオン交換基を含まない油溶性モノマー、界面活性剤及び水の混合物を撹拌することにより油中水滴型エマルジョンを調製し、次いで油中水滴型エマルジョンを重合させて全細孔容積が16ml/gを超え、30ml/g以下の連続マクロポア構造のモノリス状の有機多孔質中間体を得るI工程、芳香族ビニルモノマー、一分子中に少なくとも2個以上のビニル基を有する全油溶性モノマー中、0.3〜5モル%の架橋剤、芳香族ビニルモノマーや架橋剤は溶解するが芳香族ビニルモノマーが重合して生成するポリマーは溶解しない有機溶媒及び重合開始剤からなる混合物を調製するII工程、II工程で得られた混合物を静置下、且つI工程で得られたモノリス状の有機多孔質中間体の存在下に重合を行い、共連続構造体を得るIII工程、該III工程で得られた共連続構造体にイオン交換基を導入するIV工程を行うことで得られる。
フェニル、ビニルナフタレン等の芳香族ビニルモノマー;エチレン、プロピレン、1-ブ
テン、イソブテン等のα-オレフィン;ブタジエン、イソプレン、クロロプレン等のジエ
ン系モノマー;塩化ビニル、臭化ビニル、塩化ビニリデン、テトラフルオロエチレン等のハロゲン化オレフィン;アクリロニトリル、メタクリロニトリル等のニトリル系モノマー;酢酸ビニル、プロピオン酸ビニル等のビニルエステル;アクリル酸メチル、アクリル酸エチル、アクリル酸ブチル、アクリル酸2-エチルヘキシル、メタクリル酸メチル、メタ
クリル酸エチル、メタクリル酸プロピル、メタクリル酸ブチル、メタクリル酸2-エチル
ヘキシル、メタクリル酸シクロヘキシル、メタクリル酸ベンジル、メタクリル酸グリシジル等の(メタ)アクリル系モノマーが挙げられる。これらモノマーの中で、好適なものとしては、芳香族ビニルモノマーであり、例えばスチレン、α−メチルスチレン、ビニルトルエン、ビニルベンジルクロライド、ジビニルベンゼン等が挙げられる。これらモノマーは、1種単独又は2種以上を組み合わせて使用することができる。ただし、ジビニルベンゼン、エチレングリコールジメタクリレート等の架橋性モノマーを少なくとも油溶性モノマーの一成分として選択し、その含有量を全油溶性モノマー中、0.3〜5モル%、好ましくは0.3〜3モル%とすることが、後の工程でイオン交換基量を多く導入するに際して必要な機械的強度が得られる点で好ましい。
ビス(イソブチロニトリル)、2,2’-アゾビス(2,4-ジメチルバレロニトリル)、2,2’-アゾビス(2−メチルブチロニトリル)、2,2’-アゾビス(4-メトキシ-2,4-ジメチルバレロニトリル)、2,2’-アゾビスイソ酪酸ジメチル、4,4’-アゾ
ビス(4-シアノ吉草酸)、1,1’-アゾビス(シクロヘキサン-1-カルボニトリル)、
過酸化ベンゾイル、過酸化ラウロイル、過硫酸カリウム、過硫酸アンモニウム、テトラメチルチウラムジスルフィド、過酸化水素−塩化第一鉄、過硫酸ナトリウム−酸性亜硫酸ナトリウム等が挙げられる。
連続構造を形成させるため、架橋構造単位は3モル未満とすることが好ましい。
レン、ビニルトルエン、ビニルベンジルクロライド、ビニルビフェニル、ビニルナフタレン等が挙げられる。これらモノマーは、1種単独又は2種以上を組み合わせて使用することができる。本発明で好適に用いられる芳香族ビニルモノマーは、スチレン、ビニルベンジルクロライド等である。
共存させるモノリス中間体の架橋密度とほぼ等しくなるように用いることが好ましい。両者の使用量があまりに大きくかけ離れると、生成したモノリス中で架橋密度分布の偏りが生じ、イオン交換基導入反応時にクラックが生じやすくなる。
ール、テトラメチレングリコール等のアルコール類;ジエチルエーテル、ブチルセロソルブ、ポリエチレングリコール、ポリプロピレングリコール、ポリテトラメチレングリコール等の鎖状(ポリ)エーテル類;ヘキサン、ヘプタン、オクタン、イソオクタン、デカン、ドデカン等の鎖状飽和炭化水素類;酢酸エチル、酢酸イソプロピル、酢酸セロソルブ、プロピオン酸エチル等のエステル類が挙げられる。また、ジオキサンやTHF、トルエンのようにポリスチレンの良溶媒であっても、上記貧溶媒と共に用いられ、その使用量が少ない場合には、有機溶媒として使用することができる。これら有機溶媒の使用量は、上記芳香族ビニルモノマーの濃度が30〜80重量%となるように用いることが好ましい。有機溶媒使用量が上記範囲から逸脱して芳香族ビニルモノマー濃度が30重量%未満となると、重合速度が低下したり、重合後のモノリス構造が本発明の範囲から逸脱してしまうため好ましくない。一方、芳香族ビニルモノマー濃度が80重量%を超えると、重合が暴走する恐れがあるため好ましくない。
次に、実施例を挙げて本発明を具体的に説明するが、これは単に例示であって、本発明を制限するものではない。
(I工程;モノリス中間体の製造)
スチレン19.2g、ジビニルベンゼン1.0g、ソルビタンモノオレエート(以下SMOと略す)1.0gおよび2,2’-アゾビス(イソブチロニトリル)0.26gを混合し、均一に溶解させた。次に,当該スチレン/ジビニルベンゼン/SMO/2,2’-アゾビ
ス(イソブチロニトリル)混合物をTHF1.8mlを含有する180gの純水に添加し、遊星式撹拌装置である真空撹拌脱泡ミキサー(イーエムイー社製)を用いて5〜20℃の温度範囲において減圧下撹拌して、油中水滴型エマルションを得た。このエマルションを反応容器に速やかに移し、密封後静置下で60℃、24時間重合させた。重合終了後、内容物を取り出し、イソプロパノールで抽出した後、減圧乾燥して、連続マクロポア構造を有するモノリス中間体を製造した。水銀圧入法により測定した該モノリス中間体のマクロポアとマクロポアが重なる部分の開口(メソポア)の平均直径は56μm、全細孔容積は7.5ml/gであった。
次いで、スチレン49.0g、ジビニルベンゼン1.0g、1-デカノール50g、2,2’-アゾビス(2,4-ジメチルバレロニトリル)0.5gを混合し、均一に溶解させた
(II工程)。次に上記モノリス中間体を外径70mm、厚さ約20mmの円盤状に切断して、7.6g分取した。分取したモノリス中間体を内径90mmの反応容器に入れ、当該スチレン/ジビニルベンゼン/1-デカノール/2,2’-アゾビス(2,4-ジメチルバレロニトリル)混合物に浸漬させ、減圧チャンバー中で脱泡した後、反応容器を密封し、静置下60℃で24時間重合させた。重合終了後、厚さ約30mmのモノリス状の内容物を取り出し、アセトンでソックスレー抽出した後、85℃で一夜減圧乾燥した(III工程)。
3モル%含有したモノリス(乾燥体)の内部構造を、SEMにより観察した結果を図1に示す。図1のSEM画像は、モノリスを任意の位置で切断して得た切断面の任意の位置における画像である。図1から明らかなように、当該モノリスは連続マクロポア構造を有しており、連続マクロポア構造体を構成する骨格が従来のモノリスの図12のものと比べて遥かに太く、また、骨格を構成する壁部の厚みが厚いものであった。
、仕込み欄は左から順に、II工程で用いたビニルモノマー、架橋剤、I工程で得られたモノリス中間体、II工程で用いた有機溶媒を示す。
上記の方法で製造したモノリスを、外径70mm、厚み約15mmの円盤状に切断した。モノリスの重量は27gであった。これにジクロロメタン1500mlを加え、35℃で1時間加熱した後、10℃以下まで冷却し、クロロ硫酸145gを徐々に加え、昇温して35℃で24時間反応させた。その後、メタノールを加え、残存するクロロ硫酸をクエンチした後、メタノールで洗浄してジクロロメタンを除き、更に純水で洗浄して連続マクロポア構造を有するモノリスカチオン交換体を得た。
(モノリスの製造)
スチレンの使用量、架橋剤の種類と使用量、有機溶媒の種類と使用量、スチレン及びジビニルベンゼン含浸重合時に共存させるモノリス中間体の多孔構造、架橋密度および使用量を表1に示す配合量に変更した以外は、実施例1と同様の方法でモノリスを製造した。その結果を表1及び表2に示す。なお、実施例2〜11のSEM画像(不図示)及び表2から、実施例2〜11のモノリスの開口の平均直径は22〜70μmと大きく、骨格を構成する壁部の平均厚みも25〜50μmと厚く、骨格部面積はSEM画像領域中26〜44%と骨太のモノリスであった。
上記の方法で製造したモノリスを、それぞれ実施例1と同様の方法でクロロ硫酸と反応させ、連続マクロポア構造を有するモノリスカチオン交換体を製造した。その結果を表2に示す。実施例2〜11のモノリスカチオン交換体の開口の平均直径は46〜138μmであり、骨格を構成する壁部の平均厚みも45〜110μmと厚く、骨格部面積はSEM画像領域中26〜44%である。イオン交換帯長さは20〜25mmと従来のモノリスより小さな値を示した。また、実施例8のモノリスカチオン交換体については、機械的特性の評価も行なった。
実施例8で得られたモノリスカチオン交換体を、水湿潤状態で4mm×5mm×10mmの短冊状に切り出し、引張強度試験の試験片とした。この試験片を引張試験機に取り付け、ヘッドスピードを0.5mm/分に設定し、水中、25℃にて試験を行った。その結
果、引張強度、引張弾性率はそれぞれ45kPa、50kPaであり、従来のモノリスカチオン交換体に比べて格段に大きな値を示した。また、引張破断伸びは25%であり、従来のモノリスカチオン交換体よりも大きな値であった。
(I工程;モノリス中間体の製造)
スチレン5.4g、ジビニルベンゼン0.17g、ソルビタンモノオレエート(以下SMOと略す)1.4gおよび2,2’-アゾビス(イソブチロニトリル)0.26gを混合し、均一に溶解させた。次に、当該スチレン/ジビニルベンゼン/SMO/2,2’-アゾビ
ス(イソブチロニトリル)混合物を180gの純水に添加し、遊星式撹拌装置である真空撹拌脱泡ミキサー(イーエムイー社製)を用いて5〜20℃の温度範囲において減圧下撹拌して、油中水滴型エマルションを得た。このエマルションを速やかに反応容器に移し、密封後静置下で60℃、24時間重合させた。重合終了後、内容物を取り出し、メタノールで抽出した後、減圧乾燥して、連続マクロポア構造を有するモノリス中間体を製造した。このようにして得られたモノリス中間体(乾燥体)の内部構造をSEM画像(図7)により観察したところ、隣接する2つのマクロポアを区画する壁部は極めて細く棒状であるものの、連続気泡構造を有しており、水銀圧入法により測定したマクロポアとマクロポアが重なる部分の開口(メソポア)の平均直径は70μm、全細孔容積は21.0ml/g
であった。
次いで、スチレン76.0g、ジビニルベンゼン4.0g、1-デカノール120g、
2,2’-アゾビス(2,4-ジメチルバレロニトリル)0.8gを混合し、均一に溶解させた(II工程)。次に上記モノリス中間体を直径70mm、厚さ約40mmの円盤状に切断して4.1gを分取した。分取したモノリス中間体を内径75mmの反応容器に入れ、当該スチレン/ジビニルベンゼン/1-デカノール/2,2’-アゾビス(2,4-ジメチルバレ
ロニトリル)混合物に浸漬させ、減圧チャンバー中で脱泡した後、反応容器を密封し、静置下60℃で24時間重合させた。重合終了後、厚さ約60mmのモノリス状の内容物を取り出し、アセトンでソックスレー抽出した後、85℃で一夜減圧乾燥した(III工程)。
2モル%含有したモノリス(乾燥体)の内部構造をSEMにより観察したところ、当該モノリスは骨格及び空孔はそれぞれ3次元的に連続し、両相が絡み合った共連続構造であった。また、SEM画像から測定した骨格の太さは10μmであった。また、水銀圧入法により測定した当該モノリスの三次元的に連続した空孔の大きさは17μm、全細孔容積は2.9ml/gであった。その結果を表3及び4にまとめて示す。表4中、骨格の太さは
骨格の直径で表した。
上記の方法で製造したモノリスを、直径75mm、厚み約15mmの円盤状に切断した。モノリスの重量は18gであった。これにジクロロメタン1500mlを加え、35℃で1時間加熱した後、10℃以下まで冷却し、クロロ硫酸99gを徐々に加え、昇温して35℃で24時間反応させた。その後、メタノールを加え、残存するクロロ硫酸をクエンチした後、メタノールで洗浄してジクロロメタンを除き、更に純水で洗浄して共連続構造を有するモノリスカチオン交換体を得た。
潤状態でのモノリスの連続空孔の大きさを、モノリスの値と水湿潤状態のカチオン交換体の膨潤率から見積もったところ24μmであり、骨格の直径は14μm、全細孔容積は2.9ml/gであった。
(共連続構造を有するモノリスの製造)
スチレンの使用量、架橋剤の使用量、有機溶媒の使用量、スチレン及びジビニルベンゼン含浸重合時に共存させるモノリス中間体の多孔構造、架橋密度及び使用量を表3に示す配合量に変更した以外は、実施例12と同様の方法で共連続構造を有するモノリスを製造した。なお、実施例15は内径75mmの反応容器に代えて、内径110mmの反応容器を用いた以外は、実施例12と同様の方法で行ったものである。その結果を表3及び表4に示す。
上記の方法で製造したモノリスを、それぞれ実施例12と同様の方法でクロロ硫酸と反応させ、共連続構造を有するモノリスカチオン交換体を製造した。その結果を表4に示す。また、得られた共連続構造を有するモノリスカチオン交換体の内部構造は、不図示のSEM画像及び表4から実施例13から15で得られたモノリスカチオン交換体は差圧係数が小さい、体積当りの交換容量が大きい、イオン交換帯長さが短いといった優れた特性を示した。すなわち、イオン交換帯長さは14〜16mmと従来のモノリスより小さな値を示した。
実施例13で得られたモノリスカチオン交換体を、水湿潤状態で4mm×5mm×10mmの短冊状に切り出し、引張強度試験の試験片とした。この試験片を引張試験機に取り付け、ヘッドスピードを0.5mm/分に設定し、水中、25℃にて試験を行った。その
結果、引張強度、引張弾性率はそれぞれ23kPa、15kPaであり、従来のモノリスカチオン交換体に比べて格段に大きな値を示した。また、引張破断伸びは50%であり、従来のモノリスカチオン交換体よりも大きな値であった。
(モノリス状有機多孔質体(公知品)の製造)
特開2002−306976号記載の製造方法に準拠して連続マクロポア構造を有するモノリス状有機多孔質体を製造した。すなわち、スチレン19.2g、ジビニルベンゼン1.0g、SMO1.0gおよび2,2’-アゾビス(イソブチロニトリル)0.26gを混合し、均一に溶解させた。次に、当該スチレン/ジビニルベンゼン/SMO/2,2’-ア
ゾビス(イソブチロニトリル)混合物を180gの純水に添加し、遊星式撹拌装置である真空撹拌脱泡ミキサー(イーエムイー社製)を用いて5〜20℃の温度範囲において減圧下撹拌して、油中水滴型エマルションを得た。このエマルションを反応容器に速やかに移し、密封後静置下で60℃、24時間重合させた。重合終了後、内容物を取り出し、イソプロパノールで抽出した後、減圧乾燥して、連続マクロポア構造を有するモノリス状有機多孔質体を製造した。
中、メソポア直径は開口の平均直径を意味する。また、表1〜5中、厚み、骨格直径、空孔の値はそれぞれ平均を示す。
上記の方法で製造した有機多孔質体を、外径70mm、厚み約15mmの円盤状に切断した。有機多孔質体の重量は6gであった。これにジクロロメタン1000mlを加え、35℃で1時間加熱した後、10℃以下まで冷却し、クロロ硫酸30gを徐々に加え、昇温して35℃で24時間反応させた。その後、メタノールを加え、残存するクロロ硫酸をクエンチした後、メタノールで洗浄してジクロロメタンを除き、更に純水で洗浄して連続マクロポア構造を有するモノリス状多孔質カチオン交換体を得た。得られたカチオン交換体の反応前後の膨潤率は1.6倍であり、体積当りのイオン交換容量は、水湿潤状態で0.22mg当量/mlと実施例品に比べて小さな値を示した。水湿潤状態での有機多孔質
イオン交換体のメソポアの平均直径を、有機多孔質体の値と水湿潤状態のカチオン交換体の膨潤率から見積もったところ46μmであり、骨格を構成する壁部の平均厚み8μm、骨格部面積はSEM画像領域中10%、全細孔容積は、8.6ml/gであった。また、
水を透過させた際の圧力損失の指標である差圧係数は、0.013MPa/m・LVであ
った。結果を表5にまとめて示す。また、比較例1で得られたモノリスカチオン交換体については、機械的特性の評価も行なった。
比較例1で得られたモノリスカチオン交換体について、実施例8の評価方法と同様の方法で引張試験を行った。その結果、引張強度、引張弾性率はそれぞれ28kPa、12kPaであり、実施例8のモノリスカチオン交換体に比べて低い値であった。また、引張破断伸びも17%であり、本発明のモノリスカチオン交換体よりも小さかった。
(連続マクロポア構造を有するモノリス状有機多孔質体の製造)
スチレンの使用量、ジビニルベンゼンの使用量、SMOの使用量を表5に示す配合量に変更した以外は、比較例1と同様の方法で、従来技術により連続マクロポア構造を有するモノリス状有機多孔質体を製造した。結果を表5に示す。また、比較例4のモノリスの内部構造は不図示のSEMにより観察した。なお、比較例4は全細孔容積を最小とする条件であり、油相部に対してこれ以下の水の配合では、開口が形成できない。比較例2〜4のモノリスはいずれも、開口径が9〜18μmと小さく、骨格を構成する壁部の平均厚みも15μmと薄く、また、骨格部面積はSEM画像領域中最大でも22%と少なかった。
上記の方法で製造した有機多孔質体を、実施例13と同様の方法でクロロ硫酸と反応させ、連続マクロポア構造を有するモノリス状多孔質カチオン交換体を製造した。結果を表5に示す。開口直径を大きくしようとすると壁部の厚みが小さくなったり、骨格が細くなったりする。一方、壁部を厚くしたり、骨格を太くしようとすると開口の直径が減少する傾向が認められた。その結果、差圧係数を低く押さえると体積当りのイオン交換容量が減少し、イオン交換容量を大きくすると差圧係数が増大した。
(モノリス状有機多孔質陽イオン交換体の製造(公知品))
スチレン27.7g、ジビニルベンゼン6.9g、ソルビタンモノオレエート3.8gおよびアゾビスイソブチロニトリル0.14gを混合し、均一に溶解させた。次に当該スチレン/ジビニルベンゼン/ソルビタンモノオレエート/アゾビスイソブチロニトリル混合物を450mlの純水に添加し、ホモジナイザーを用いて20,000回転/分で2分間攪拌し、油中水滴型エマルジョンを得た。乳化終了後、油中水滴型エマルジョンをオートクレーブに移し、窒素で十分置換した後密封し、静置下60℃で24時間重合させた。重合終了後、内容物を取り出し、イソプロパノールで18時間ソックスレー抽出し、未反応モノマーとソルビタンモノオレエートを除去した後、40℃で一昼夜減圧乾燥した。この様にして得られたスチレン/ジビニルベンゼン共重合体よりなる架橋成分を14モル%含有した多孔質体30gを分取し、テトラクロロエタン2リットルを加え60℃で30分加熱した後、室温まで冷却し、クロロ硫酸120gを徐々に加え、室温で4時間反応させた。その後、酢酸を加え、多量の水中に反応物を投入し、水洗、乾燥して多孔質陽イオン交換体を得た。この多孔質体のイオン交換容量は、乾燥多孔質体換算で4.0mg当量/
gであり、EPMAを用いた硫黄原子のマッピングにより、スルホン酸基が多孔質体に均一に導入されていることを確認した。この多孔質体の内部構造は、連続気泡構造を有しており、平均径30μm のマクロポアの大部分が重なり合い、マクロポアとマクロポアの
重なりで形成されるメソポアの直径の平均値は5μm 、全細孔容積は、10.1ml/gであった。内部構造をSEMにより観察した結果、図12と同様であった。また、上記多孔質体を10mmの厚みに切り出し、水透過速度および空気透過速度を測定したところ、それぞれ14,000L/分・m2・MPa、3,600m3/ 分・m2・MPaであっ
た。また、イオン交換帯長さは41mmであった。
(反応蒸留による酢酸メチルの加水分解反応(その1)
内径25mmのジャケット付カラムを反応蒸留塔として用い、下部に直径4mmのガラス製へリックスを高さ800mmにわたって充填して回収部とし、その上部に実施例5で得られた多孔質陽イオン交換体を直径25mm、高さ800mmの大きさに切り出して固体酸触媒として充填し、反応部とした。充填量は、乾燥重量で27.5gであった。この反応蒸留塔に、酢酸メチル/ メタノール混合液(モル比1.0/0.4 )を反応部の下
端から100g/時間の速度で供給し、一方、水を反応部の上端から100g/時間の速度で供給し、反応を行った。なお、供給液はいずれも65℃に加温して供給し、反応蒸留塔のジャケットには65℃の温水を循環させ、スチル中の液は85℃に加熱して全還流で運転した。反応が安定した後、加水分解率(反応率)を測定したところ、平均で99%の反応率が得られた。
実施例5で得られた多孔質陽イオン交換体に代えて、実施例15で得られた多孔質陽イオン交換体を使用した以外は、反応蒸留による酢酸メチルの加水分解反応(その1)と同様の方法により行なった。その結果、平均で99%の反応率が得られた。
実施例5で得られた多孔質陽イオン交換体に代えて、比較例1で得られた多孔質陽イオン交換体を使用した以外は、反応蒸留による酢酸メチルの加水分解反応(その1)と同様の方法により行なった。その結果、平均で97%の反応率が得られた。
Claims (2)
- イオン交換基が導入された全構成単位中、架橋構造単位を0.3〜5.0モル%含有する芳香族ビニルポリマーからなる太さが1〜60μmの三次元的に連続した骨格と、その骨格間に直径が10〜100μmの三次元的に連続した空孔とからなる共連続構造体であって、全細孔容積が0.5〜5ml/gであり、陽イオン交換容量が1〜5mg当量/g乾燥多孔質体であり、陽イオン交換基が多孔質体中に均一に分布している有機多孔質イオン交換体からなることを特徴とする固体酸触媒。
- 反応蒸留法に使用されることを特徴とする請求項1記載の固体酸触媒。