JP5519181B2 - Exhaust gas purification device for internal combustion engine - Google Patents
Exhaust gas purification device for internal combustion engine Download PDFInfo
- Publication number
- JP5519181B2 JP5519181B2 JP2009116421A JP2009116421A JP5519181B2 JP 5519181 B2 JP5519181 B2 JP 5519181B2 JP 2009116421 A JP2009116421 A JP 2009116421A JP 2009116421 A JP2009116421 A JP 2009116421A JP 5519181 B2 JP5519181 B2 JP 5519181B2
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- internal combustion
- combustion engine
- purification catalyst
- exhaust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、内燃機関の排気浄化装置に関する。詳しくは、内燃機関から排出される排気中の粒子状物質を捕捉するとともに、捕捉した粒子状物質を浄化するための浄化触媒を有するフィルタを備えた内燃機関の排気浄化装置に関する。 The present invention relates to an exhaust emission control device for an internal combustion engine. More specifically, the present invention relates to an exhaust gas purification apparatus for an internal combustion engine that includes a filter having a purification catalyst for purifying particulate matter in exhaust gas discharged from the internal combustion engine and purifying the captured particulate matter.
自動車などに搭載される内燃機関、特に圧縮着火式内燃機関においては、排出される排気中に多量の粒子状物質が含まれる。この粒子状物質は人体に有害であり、またエミッション規制対象物質である。このため、粒子状物質を除去するためのフィルタが、上記内燃機関の排気通路に設けられているのが一般的である。 In an internal combustion engine mounted on an automobile or the like, particularly a compression ignition type internal combustion engine, a large amount of particulate matter is contained in the exhaust gas discharged. This particulate matter is harmful to the human body and is subject to emissions regulations. For this reason, a filter for removing particulate matter is generally provided in the exhaust passage of the internal combustion engine.
上記フィルタとしては、DPF(Diesel Particulate Filter)に、捕捉した粒子状物質を浄化するための浄化触媒を担持させたもの(Catalyzed Soot Filter、CSFともいう)などが用いられている。このようなフィルタでは、粒子状物質が捕捉されて堆積すると、フィルタの上流側と下流側との間で差圧が生じ、出力の低下や燃費の悪化を招く。従って、粒子状物質がある程度堆積した段階で、堆積した粒子状物質を燃焼除去する再生処理を実行する必要があるため、粒子状物質を効率良く燃焼除去できる浄化触媒の開発が進められている。 As the filter, a DPF (Diesel Particulate Filter) carrying a purification catalyst for purifying the trapped particulate matter (also referred to as a catalyzed soot filter, CSF) or the like is used. In such a filter, when the particulate matter is captured and accumulated, a differential pressure is generated between the upstream side and the downstream side of the filter, leading to a decrease in output and a deterioration in fuel consumption. Therefore, since it is necessary to execute a regeneration process for burning and removing the accumulated particulate matter when the particulate matter is accumulated to some extent, development of a purification catalyst capable of efficiently removing and removing the particulate matter is in progress.
例えば、担体と、該担体上に形成された触媒層と、を少なくとも備え、触媒層中に空隙を有する浄化触媒が開示されている(特許文献1参照)。この特許文献1に開示された浄化触媒によれば、触媒層中に空隙を形成することにより、排気の拡散性が良好となり、粒子状物質の燃焼を促進させることができるとされている。 For example, a purification catalyst having at least a carrier and a catalyst layer formed on the carrier and having voids in the catalyst layer is disclosed (see Patent Document 1). According to the purification catalyst disclosed in Patent Document 1, it is said that by forming voids in the catalyst layer, the diffusibility of exhaust gas becomes good and combustion of particulate matter can be promoted.
また、フィルタ担体の表面にアンダーコート層を介して触媒層を設けるとともに、触媒層の平均空孔径を0.1μm以上0.2μm未満とし、アンダーコート層の平均空孔径を触媒層の平均空孔径よりも小さく設定した浄化触媒が開示されている(特許文献2参照)。この特許文献2に開示された浄化触媒によれば、多孔質の触媒層をフィルタ担体の表面に設けた場合に生じていた触媒層の剥離を抑制でき、粒子状物質の浄化率を向上させることができるとされている。 In addition, a catalyst layer is provided on the surface of the filter carrier via an undercoat layer, the average pore diameter of the catalyst layer is 0.1 μm or more and less than 0.2 μm, and the average pore diameter of the undercoat layer is the average pore diameter of the catalyst layer. The purification catalyst set smaller than this is disclosed (refer patent document 2). According to the purification catalyst disclosed in Patent Document 2, it is possible to suppress the separation of the catalyst layer that has occurred when the porous catalyst layer is provided on the surface of the filter carrier, and to improve the purification rate of the particulate matter. It is supposed to be possible.
しかしながら、粒子状物質の燃焼除去には、550℃〜650℃の高温が必要であるとされており、上記従来技術のような浄化触媒を用いた場合であっても、粒子状物質を低温で効率良く燃焼できていないのが現状である。このような高温下での再生処理は、燃費の悪化、フィルタの溶損、触媒の劣化などを引き起こす。従って、フィルタに捕捉されて堆積した粒子状物質を、従来よりも低温下で効率良く燃焼させることができる浄化触媒を備えた排気浄化装置の開発が望まれている。 However, it is said that a high temperature of 550 ° C. to 650 ° C. is necessary for the combustion removal of the particulate matter, and even when the purification catalyst as in the above prior art is used, the particulate matter is kept at a low temperature. The current situation is that combustion is not efficient. Such a regeneration treatment at a high temperature causes deterioration of fuel consumption, filter melting, catalyst deterioration, and the like. Therefore, it is desired to develop an exhaust emission control device including a purification catalyst that can burn particulate matter trapped and deposited by a filter more efficiently at a lower temperature than in the past.
本発明は上記課題に鑑みてなされたものであり、その目的は、従来よりも低温下で効率良く粒子状物質を燃焼させることができる浄化触媒を備えた排気浄化装置を提供することにある。 The present invention has been made in view of the above problems, and an object of the present invention is to provide an exhaust purification device including a purification catalyst capable of burning particulate matter more efficiently at a lower temperature than in the past.
上記目的を達成するため請求項1記載の発明は、内燃機関の排気通路に設けられ、当該内燃機関の排気中の粒子状物質を捕捉するとともに、捕捉した粒子状物質を浄化するための浄化触媒を有するフィルタを備えた内燃機関の排気浄化装置において、前記浄化触媒は、当該浄化触媒の粒度分布における小粒径側からの累積分布が90%となるときの粒子径D90が2μm以下であることを特徴とする。 In order to achieve the above object, an invention according to claim 1 is provided in an exhaust passage of an internal combustion engine and captures particulate matter in exhaust gas of the internal combustion engine and purifies the captured particulate matter. In the exhaust gas purification apparatus for an internal combustion engine provided with a filter having the above, the purification catalyst has a particle diameter D90 of 2 μm or less when the cumulative distribution from the small particle size side in the particle size distribution of the purification catalyst is 90%. It is characterized by.
請求項1記載の発明では、浄化触媒の粒度分布における小粒径側からの累積分布が90%となるときの粒子径D90が2μm以下であることにより、フィルタ表面を緻密な浄化触媒からなる層で被覆できる。また、浄化触媒と粒子状物質の接触面積を増大でき、浄化触媒と粒子状物質との接触性を向上させることができるため、粒子状物質の燃焼性能を向上させることができる。
また、本発明によれば、従来よりも低温下で効率良く粒子状物質を燃焼させてフィルタを再生することができ、フィルタの再生処理に伴う燃費ロスや触媒の劣化を抑制できる。また、通常走行時においても粒子状物質を連続燃焼させ得るため、再生頻度を低減でき、燃費の悪化を低減できる。さらには、低温下でフィルタを再生できるため、排気系レイアウトの自由度が高く、例えば車両床下にフィルタを配置することもできる。
In the first aspect of the present invention, the filter surface is a layer composed of a dense purification catalyst because the particle diameter D90 when the cumulative distribution from the small particle size side in the particle size distribution of the purification catalyst is 90% is 2 μm or less. Can be covered. Further, the contact area between the purification catalyst and the particulate matter can be increased, and the contact property between the purification catalyst and the particulate matter can be improved, so that the combustion performance of the particulate matter can be improved.
Further, according to the present invention, it is possible to regenerate the filter by burning the particulate matter more efficiently at a lower temperature than in the past, and it is possible to suppress fuel consumption loss and catalyst deterioration associated with filter regeneration processing. In addition, since particulate matter can be continuously burned even during normal travel, the regeneration frequency can be reduced, and deterioration of fuel consumption can be reduced. Furthermore, since the filter can be regenerated at a low temperature, the degree of freedom of the exhaust system layout is high. For example, the filter can be arranged under the vehicle floor.
請求項2記載の発明は、請求項1記載の内燃機関の排気浄化装置において、前記浄化触媒は、3μm〜10μmの空隙を有することを特徴とする。 According to a second aspect of the present invention, in the exhaust gas purification apparatus for an internal combustion engine according to the first aspect, the purification catalyst has a gap of 3 μm to 10 μm.
請求項2記載の発明では、3μm〜10μmの空隙を設けて浄化触媒をフィルタに担持させることにより、浄化触媒をフィルタ表面に均一に担持させることができる。このため、浄化触媒と粒子状物質との接触性をより向上させることができ、粒子状物質の燃焼性能をより向上させることができる。また、3μm〜10μmの空隙の存在によって排気の拡散性が良好となるため、この点からも粒子状物質の燃焼性能の向上に寄与できる。 According to the second aspect of the present invention, the purification catalyst can be uniformly supported on the filter surface by providing a clearance of 3 μm to 10 μm and supporting the purification catalyst on the filter. For this reason, the contact property between the purification catalyst and the particulate matter can be further improved, and the combustion performance of the particulate matter can be further improved. Moreover, since the diffusibility of the exhaust gas becomes good due to the presence of the 3 μm to 10 μm voids, it is possible to contribute to the improvement of the combustion performance of the particulate matter from this point.
請求項3記載の発明は、請求項1又は2記載の内燃機関の排気浄化装置において、前記フィルタの表面における前記浄化触媒の被覆率が30%以上であることを特徴とする。 According to a third aspect of the present invention, in the exhaust gas purification apparatus for an internal combustion engine according to the first or second aspect, the coverage of the purification catalyst on the surface of the filter is 30% or more.
請求項3記載の発明によれば、フィルタの表面における浄化触媒の被覆率が30%以上であるため、浄化触媒と粒子状物質との良好な接触状態を確保できる。このため、粒子状物質の燃焼性能をより向上させることができ、上記発明の効果をより高めることができる。 According to the third aspect of the invention, since the coverage of the purification catalyst on the surface of the filter is 30% or more, a good contact state between the purification catalyst and the particulate matter can be ensured. For this reason, the combustion performance of a particulate matter can be improved more and the effect of the said invention can be improved more.
請求項4記載の発明は、請求項1から3いずれか記載の内燃機関の排気浄化装置において、前記浄化触媒は、水銀ポロシメータにより測定された孔径分布において、4μm〜8μmのピークを有することを特徴とする。 According to a fourth aspect of the present invention, in the exhaust gas purification apparatus for an internal combustion engine according to the first to third aspects, the purification catalyst has a peak of 4 μm to 8 μm in the pore size distribution measured by a mercury porosimeter. And
請求項4記載の発明によれば、4μm〜8μmの空隙のピークを設けて浄化触媒をフィルタに担持させることにより、浄化触媒の担持量を増加することなく、フィルタの表面全体を浄化触媒で被覆することができる。このため、粒子状物質の燃焼性能をより向上させることができ、上記発明の効果をより高めることができる。 According to the fourth aspect of the present invention, the entire surface of the filter is covered with the purifying catalyst without increasing the amount of the purifying catalyst supported by providing the purifying catalyst on the filter by providing a peak of a gap of 4 μm to 8 μm. can do. For this reason, the combustion performance of a particulate matter can be improved more and the effect of the said invention can be improved more.
請求項5記載の発明は、請求項1から4いずれか記載の内燃機関の排気浄化装置において、前記浄化触媒がAgを含むことを特徴とする。 According to a fifth aspect of the present invention, in the exhaust gas purification apparatus for an internal combustion engine according to any one of the first to fourth aspects, the purification catalyst contains Ag.
上述したように、上記発明によれば、浄化触媒と粒子状物質の接触性を向上させることができるため、浄化触媒が本来に有する優れた燃焼性能を十分に発揮させることができる。ここで、Agを含むAg系触媒は、最も低温で粒子状物質を燃焼できる材料であるとされている。例えば、Ag系触媒において、粒子状物質との良好な接触性が確保できれば、粒子状物質を200℃以下で着火させることができ、400℃で燃焼させることができるとされている。
この点、本発明では、Agを含む浄化触媒を用いることにより、Ag系触媒が本来有する優れた燃焼性能を十分に発揮できるため、低温下においても効率良く粒子状物質を燃焼除去できる。また、約600℃の高温域での再生処理においては、瞬時に粒子状物質を燃焼除去することができ、通常走行の加速時など温度が約350℃に達した場合にも、特別な制御無しに粒子状物質の一部を燃焼させることができる。
As described above, according to the above-described invention, the contact property between the purification catalyst and the particulate matter can be improved, so that the excellent combustion performance inherent in the purification catalyst can be sufficiently exhibited. Here, the Ag-based catalyst containing Ag is said to be a material that can burn particulate matter at the lowest temperature. For example, in an Ag-based catalyst, if good contact with the particulate matter can be ensured, the particulate matter can be ignited at 200 ° C. or lower and combusted at 400 ° C.
In this regard, in the present invention, by using the purification catalyst containing Ag, the excellent combustion performance inherent to the Ag-based catalyst can be sufficiently exhibited, so that the particulate matter can be efficiently removed by combustion even at low temperatures. In the regeneration process at a high temperature range of about 600 ° C, particulate matter can be burned and removed instantly, and no special control is required even when the temperature reaches about 350 ° C, such as during normal driving acceleration. A part of the particulate matter can be burned.
請求項6記載の発明は、請求項5記載の内燃機関の排気浄化装置において、前記Agの結晶子径が42nm未満であることを特徴とする。 The invention according to claim 6 is the exhaust gas purification apparatus for an internal combustion engine according to claim 5, wherein the crystallite diameter of the Ag is less than 42 nm.
後述するように、Ag系触媒の表面には、酸素脱離開始温度が最も低く、粒子状物質との反応性に最も優れたAg2Oが存在する。ところが、浄化触媒中に含まれるAgの結晶子径が大きい場合には、粒子状物質との接触性が低下してしまうとともに、表面に存在するAg2O量が減少して酸素供給の律速となる結果、粒子状物質の燃焼反応の進行が阻害される。この点、本発明では、Agの結晶子径が42nm以下で小さいため、上記不具合を回避でき、粒子状物質を低温下で効率良く燃焼させることができる。 As will be described later, Ag 2 O having the lowest oxygen desorption start temperature and the highest reactivity with the particulate matter exists on the surface of the Ag-based catalyst. However, when the crystallite diameter of Ag contained in the purification catalyst is large, the contact property with the particulate matter is lowered, and the amount of Ag 2 O present on the surface is reduced, so that the rate of oxygen supply is controlled. As a result, the progress of the combustion reaction of the particulate matter is inhibited. In this respect, in the present invention, since the crystallite diameter of Ag is as small as 42 nm or less, the above problems can be avoided, and the particulate matter can be efficiently burned at a low temperature.
請求項7記載の発明は、請求項5又は6記載の内燃機関の排気浄化装置において、前記Agは、酸素放出能を有する複合酸化物に担持されており、前記複合酸化物は、アルカリ土類金属元素、遷移金属元素、第12族元素、及び第13族元素からなる群より選択される少なくとも2種以上を構成元素として含むことにより、構成元素の価数を変化させて酸素の吸収及び放出を行うことを特徴とする。 According to a seventh aspect of the present invention, in the exhaust gas purification apparatus for an internal combustion engine according to the fifth or sixth aspect, the Ag is supported on a complex oxide having an oxygen releasing ability, and the complex oxide is an alkaline earth By including at least two or more selected from the group consisting of metal elements, transition metal elements, group 12 elements, and group 13 elements as constituent elements, absorption and release of oxygen by changing the valence of the constituent elements It is characterized by performing.
請求項7記載の発明では、アルカリ土類金属元素、遷移金属元素、第12族元素、及び第13族元素からなる群より選択される少なくとも2種以上を構成元素として含む複合酸化物を用いることにより、構成元素の価数を変化させて酸素の吸収及び放出を行うことができる。また、このような酸素放出能を有する複合酸化物にAgを担持させることにより、複合酸化物の酸素放出能をより低温下で発揮させることができる。このため、粒子状物質をより低温下で効率良く燃焼させることができる。 In the invention of claim 7, a composite oxide containing at least two or more selected from the group consisting of alkaline earth metal elements, transition metal elements, group 12 elements, and group 13 elements as constituent elements is used. Thus, oxygen can be absorbed and released by changing the valence of the constituent elements. In addition, by supporting Ag on the composite oxide having such an oxygen releasing ability, the oxygen releasing ability of the composite oxide can be exhibited at a lower temperature. For this reason, the particulate matter can be efficiently burned at a lower temperature.
請求項8記載の発明は、請求項7記載の内燃機関の排気浄化装置において、前記浄化触媒は、前記Agとともに前記複合酸化物に担持された、Ru、Pd、及びPtからなる群より選択される少なくとも1種の貴金属をさらに含むことを特徴とする。 According to an eighth aspect of the present invention, in the exhaust gas purification apparatus for an internal combustion engine according to the seventh aspect, the purification catalyst is selected from the group consisting of Ru, Pd, and Pt supported on the composite oxide together with the Ag. And further comprising at least one noble metal.
請求項8記載の発明では、Ru、Pd、及びPtからなる群より選択される少なくとも1種の貴金属を、Agとともに複合酸化物に共担時させることにより、貴金属による酸素供給能の増加、及び貴金属によるブロッキング効果により、Agの微粒子化が可能となる。このため、酸素放出能を有する複合酸化物の酸素放出能を大幅に向上させることができ、粒子状物質の燃焼性能をより向上させることができる。 In the invention according to claim 8, at least one kind of noble metal selected from the group consisting of Ru, Pd, and Pt is added to the composite oxide together with Ag, thereby increasing the oxygen supply capacity by the noble metal, and Due to the blocking effect of the noble metal, it is possible to make Ag fine particles. For this reason, the oxygen releasing ability of the complex oxide having oxygen releasing ability can be greatly improved, and the combustion performance of the particulate matter can be further improved.
請求項9記載の発明は、請求項1から8いずれか記載の内燃機関の排気浄化装置において、前記浄化触媒が還元法により調製されたことを特徴とする。 The invention according to claim 9 is the exhaust gas purification apparatus for an internal combustion engine according to any one of claims 1 to 8, wherein the purification catalyst is prepared by a reduction method.
請求項9記載の発明では、還元法により浄化触媒を調製することにより、微細で均一なAgイオンを高濃度で得ることができ、Agの凝集を効果的に抑制できる。このため、触媒粒子の微細化が可能となり、粒子状物質の燃焼性能をより向上させることができる。 In the ninth aspect of the invention, by preparing the purification catalyst by the reduction method, fine and uniform Ag ions can be obtained at a high concentration, and aggregation of Ag can be effectively suppressed. For this reason, the catalyst particles can be miniaturized, and the combustion performance of the particulate matter can be further improved.
請求項10記載の発明は、請求項9記載の内燃機関の排気浄化装置において、前記浄化触媒が、還元剤として、トリエチルアミン、エチレングリコール、又はエタノールを用いて調製されたことを特徴とする。 A tenth aspect of the present invention is the exhaust gas purification apparatus for an internal combustion engine according to the ninth aspect, wherein the purification catalyst is prepared using triethylamine, ethylene glycol, or ethanol as a reducing agent.
請求項10記載の発明では、アミン還元法の還元剤としてトリエチルアミンを用い、あるいはアルコール還元法の還元剤としてエチレングリコール又はエタノールを用いることにより、Agイオンの還元化を効果的に進行させることができるとともに、Agを微細化できる。このため、触媒粒子の微細化が可能となり、粒子状物質の燃焼性能をより向上させることができる。 In the invention according to claim 10, the reduction of Ag ions can be effectively advanced by using triethylamine as the reducing agent in the amine reduction method or by using ethylene glycol or ethanol as the reducing agent in the alcohol reduction method. At the same time, Ag can be miniaturized. For this reason, the catalyst particles can be miniaturized, and the combustion performance of the particulate matter can be further improved.
請求項11記載の発明は、請求項1から10いずれか記載の内燃機関の排気浄化装置において、前記フィルタが、排気中のNOからNO2を生成するNO2生成触媒をさらに有することを特徴とする。 The invention according to claim 11 is the exhaust gas purification apparatus for an internal combustion engine according to any one of claims 1 to 10, wherein the filter further includes a NO 2 generation catalyst for generating NO 2 from NO in the exhaust gas. To do.
酸素放出能を有する複合酸化物は、NO2吸着能が高いことが知られている。この点、本発明では、NO2生成触媒を共存させることにより、生成したNO2が酸素放出能を有する複合酸化物の表面に吸着し、表面のNO2濃度が高く保たれる。このため、浄化触媒による酸素と粒子状物質の反応に加えて、AgによるNO2と粒子状物質の反応が促進され、粒子状物質を低温下で効率良く燃焼させることができる。 It is known that a complex oxide having oxygen releasing ability has high NO 2 adsorption ability. In this regard, in the present invention, by making the NO 2 production catalyst coexist, the produced NO 2 is adsorbed on the surface of the complex oxide having oxygen releasing ability, and the surface NO 2 concentration is kept high. For this reason, in addition to the reaction of oxygen and particulate matter by the purification catalyst, the reaction of NO 2 and particulate matter by Ag is promoted, and the particulate matter can be efficiently burned at a low temperature.
請求項12記載の発明は、請求項11記載の内燃機関の排気浄化装置において、前記NO2生成触媒が、Pt、Pd、及びRhからなる群より選択される少なくとも1種の貴金属を含むことを特徴とする。 According to a twelfth aspect of the present invention, in the exhaust gas purification apparatus for an internal combustion engine according to the eleventh aspect, the NO 2 production catalyst contains at least one noble metal selected from the group consisting of Pt, Pd, and Rh. Features.
請求項12記載の発明では、Pt、Pd、及びRhからなる群より選択される少なくとも1種の貴金属を含むNO2生成触媒を用いることにより、効果的にNO2を生成できるため、請求項11記載の発明の効果がより高められる。 In the invention of claim 12, NO 2 can be effectively produced by using a NO 2 production catalyst containing at least one kind of noble metal selected from the group consisting of Pt, Pd, and Rh. The effects of the described invention are further enhanced.
以下、本発明の実施形態について図面を参照しながら詳細に説明する。 Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.
本発明の一実施形態に係る内燃機関の排気浄化装置は、内燃機関(以下、「エンジン」という)の排気通路に設けられている。エンジンは、各気筒の燃焼室内に燃料を直接噴射するディーゼルエンジンである。また、本実施形態の排気浄化装置は、当該エンジンの排気中の粒子状物質(Particulate Matter、以下、「PM」という)を捕捉するとともに、捕捉したPMを浄化するための浄化触媒を有するフィルタ(Diesel Particulate Filter、以下、「DPF」という)を備える。 An exhaust emission control device for an internal combustion engine according to an embodiment of the present invention is provided in an exhaust passage of an internal combustion engine (hereinafter referred to as “engine”). The engine is a diesel engine that directly injects fuel into the combustion chamber of each cylinder. In addition, the exhaust purification apparatus of the present embodiment captures particulate matter (Particulate Matter, hereinafter referred to as “PM”) in the exhaust of the engine and a filter having a purification catalyst for purifying the captured PM ( Diesel Particulate Filter (hereinafter referred to as “DPF”).
本実施形態で用いるDPFは、三次元網目構造を有し、PM捕集機能を有する発泡金属や発泡セラミックス、又は金属やセラミックス繊維を重ね合わせた不織布、ウォールフロータイプのフィルタなど、如何なる形態でも使用可能である。これらのうち、ウォールフロータイプのハニカム構造のフィルタが、捕集効率、及びPMと浄化触媒との接触性の観点から好ましく用いられる。 The DPF used in the present embodiment has a three-dimensional network structure and is used in any form such as foam metal or foam ceramic having a PM trapping function, a nonwoven fabric in which metal or ceramic fibers are superimposed, or a wall flow type filter. Is possible. Among these, a wall flow type honeycomb structure filter is preferably used from the viewpoints of collection efficiency and contact between PM and the purification catalyst.
図1は、本実施形態で好ましく用いられるDPF1を、排気の流入側から見た図である。また、図2は、DPF1を、排気の流れ方向に平行な面で切断したときの断面図である。図1及び2に示されるように、DPF1は、互いに平行に延びる多数の排気流入路2と排気流出路3とを備えている。下流端が目封止材4により閉塞された排気流入路2と、上流端が目封止材4により閉塞された排気流出路3と、が交互に設けられおり、排気流入路2と排気流出路3とは、薄肉の隔壁5を介して隔てられている。 FIG. 1 is a view of a DPF 1 preferably used in the present embodiment as viewed from the exhaust inflow side. FIG. 2 is a cross-sectional view of the DPF 1 cut along a plane parallel to the exhaust flow direction. As shown in FIGS. 1 and 2, the DPF 1 includes a large number of exhaust inflow passages 2 and exhaust exhaust passages 3 that extend in parallel to each other. The exhaust inflow passage 2 whose downstream end is blocked by the plugging material 4 and the exhaust outflow passage 3 whose upstream end is blocked by the plugging material 4 are alternately provided, and the exhaust inflow passage 2 and the exhaust outflow The passage 3 is separated by a thin partition wall 5.
DPF1は、炭化珪素やコージェライトなどの多孔質材料から形成され、排気流入路2内に流入した排気は、図2の矢印で示したように、周囲の隔壁5を通過して、隣接する排気流出路3内に流入する。
図3は、図2における隔壁5の部分拡大図である。図3に示されるように、隔壁5は、排気流入路2と排気流出路3とを連通する微細な細孔6を有し、この細孔6を排気が流通する。また、排気流入路2、排気流出路3、及び細孔6から構成される排気流路の壁面には、浄化触媒層7が設けられている。
浄化触媒層7は、後述する浄化触媒により構成されており、DPF1により捕捉されて排気中のPMを浄化する機能を有する。
The DPF 1 is made of a porous material such as silicon carbide or cordierite, and the exhaust gas flowing into the exhaust inflow passage 2 passes through the surrounding partition walls 5 as shown by the arrows in FIG. It flows into the outflow passage 3.
FIG. 3 is a partially enlarged view of the partition wall 5 in FIG. As shown in FIG. 3, the partition wall 5 has fine pores 6 communicating the exhaust inflow passage 2 and the exhaust outflow passage 3, and the exhaust gas flows through the pores 6. Further, a purification catalyst layer 7 is provided on the wall surface of the exhaust flow path constituted by the exhaust inflow path 2, the exhaust outflow path 3, and the pores 6.
The purification catalyst layer 7 is composed of a purification catalyst, which will be described later, and has a function of purifying PM in the exhaust gas captured by the DPF 1.
次に、本実施形態で用いる浄化触媒について詳細に説明する。
本実施形態で用いる浄化触媒は、Agを含むことが好ましい。以下、その理由について詳しく説明する。
Next, the purification catalyst used in the present embodiment will be described in detail.
The purification catalyst used in the present embodiment preferably contains Ag. Hereinafter, the reason will be described in detail.
Agを含むAg系触媒は、現状、PMの燃焼に最も有効な触媒であると考えられている。上述したように、PMとの接触性が良好(以下、「タイトコンタクト」という)であれば、200℃以下からPMを着火させることができ、400℃でPMの燃焼を完了させることができる。しかしながら、エンジンの排気通路に配置されたDPF上でのPMと浄化触媒の接触性は低く(以下、「ルーズコンタクト」という)、浄化触媒が本来有する優れたPM燃焼性能を発揮できていないのが現状である。 Ag-based catalysts containing Ag are currently considered to be the most effective catalysts for PM combustion. As described above, if the contact property with PM is good (hereinafter referred to as “tight contact”), PM can be ignited from 200 ° C. or less, and combustion of PM can be completed at 400 ° C. However, the contact property between the PM and the purification catalyst on the DPF arranged in the exhaust passage of the engine is low (hereinafter referred to as “loose contact”), and the excellent PM combustion performance inherent in the purification catalyst cannot be exhibited. Currently.
また、PMの燃焼に対して最も有効な化合物として、Ag2Oが挙げられる。このAg2Oは、酸素脱離エネルギーが最も小さく、PMとの反応性に優れているためである。図4は、O2−TPD法(Temperature Programmed Desorption:昇温脱離法)により得られた、Ag2Oの酸素脱離開始温度とPM燃焼ピーク温度との関係を示す図である。図4に示すように、Ag2Oの酸素脱離開始温度は最も低く、酸素脱離エネルギーが最も小さいことが分かる。
しかしながら、Ag2Oは、400℃程度で分解してAgメタルとなるため、触媒としての繰り返し耐久性に乏しい。このため、Ag2Oを用いる場合には、Ag2Oの安定性の確保が不可欠であると言える。
Moreover, Ag 2 O is mentioned as the most effective compound for PM combustion. This is because Ag 2 O has the lowest oxygen desorption energy and is excellent in reactivity with PM. FIG. 4 is a diagram showing the relationship between the oxygen desorption start temperature of Ag 2 O and the PM combustion peak temperature obtained by the O 2 -TPD method (Temperature Programmed Desorption). As shown in FIG. 4, it can be seen that the oxygen desorption start temperature of Ag 2 O is the lowest and the oxygen desorption energy is the lowest.
However, Ag 2 O decomposes at about 400 ° C. to become Ag metal, so that it has poor repeated durability as a catalyst. Therefore, in the case of using the Ag 2 O is ensuring the stability of the Ag 2 O is said to be essential.
一方、酸素放出能が高い材料として、複合酸化物などの酸素貯蔵(Oxygen Storage Component、以下、「OSC」という)材が知られている。ところが、CeO2やCeZrO2などのOSC材は、図4に示すように酸素脱離開始温度が高く、PM燃焼に対してそれほど有効ではないことが分かる。 On the other hand, oxygen storage (Oxygen Storage Component, hereinafter referred to as “OSC”) materials such as composite oxides are known as materials having a high oxygen releasing ability. However, it can be seen that OSC materials such as CeO 2 and CeZrO 2 have a high oxygen desorption start temperature as shown in FIG. 4 and are not so effective for PM combustion.
そこで、本実施形態で好ましく用いられる浄化触媒は、上記のような特性を有するAg2OとOSC材とを組み合わせたものである。即ち、両者を組み合わせることにより、Ag2Oの安定性が確保できるとともに、酸素脱離開始温度の低温化が可能となっている。
具体的には、本実施形態では、酸素放出能を有する複合酸化物にAgを担持させた浄化触媒を用いることが好ましい。例えば、CeO2に、Agを含浸させることにより得られるAg/CeO2が好ましく用いられる。また、CeZrO2に、Ag及びPdを含浸させることにより得られるPdAg/CeZrO2なども好ましく用いられ、これにより酸素脱離開始温度の大幅な低温化が可能となる(図4参照)。
なお、これら浄化触媒の表面付近のAgは、酸化雰囲気下ではAg2Oとして存在し、上述の機能を発揮する。この点については、後段で詳述する。
Therefore, the purification catalyst preferably used in the present embodiment is a combination of Ag 2 O having the above characteristics and an OSC material. That is, by combining both, stability of Ag 2 O can be ensured and the oxygen desorption start temperature can be lowered.
Specifically, in this embodiment, it is preferable to use a purification catalyst in which Ag is supported on a complex oxide having oxygen releasing ability. For example, the CeO 2, Ag / CeO 2 obtained by impregnating the Ag is preferably used. Further, the CeZrO 2, etc. PdAg / CeZrO 2 obtained by impregnating the Ag and Pd also preferably used, thereby it is possible to significantly lowering the oxygen desorption start temperature (see FIG. 4).
Note that Ag in the vicinity of the surface of these purification catalysts exists as Ag 2 O in an oxidizing atmosphere, and exhibits the above-described functions. This will be described in detail later.
次に、本実施形態で好ましく用いられる浄化触媒のPM燃焼メカニズムについて説明する。
図5は、PdAg/CeZrO2のXRD(X線回折)スペクトル図である。図5において、Ag0と表示されたピークは、Agメタル由来のピークを表している。この図5から明らかであるように、PdAg/CeZrO2中に含まれるAgは、主にAgメタルとして存在することが分かる。
図6は、PdAg/CeZrO2を酸化雰囲気下に置いたときと、還元雰囲気下に置いたときのXPS(X線光電子分光)スペクトル図である。図6から明らかであるように、酸化雰囲気下では、浄化触媒の表面のAgはAg2Oとして存在し、還元雰囲気下では、Agメタルとして存在していることが分かる。これは、PM燃焼に対して活性が低いAg/α−Al2O3では、酸化雰囲気下においても表面のAgがAgメタルとして存在していることからも、本実施形態で好ましく用いられる浄化触媒特有の構成であると言える。
Next, the PM combustion mechanism of the purification catalyst preferably used in this embodiment will be described.
FIG. 5 is an XRD (X-ray diffraction) spectrum diagram of PdAg / CeZrO 2 . In FIG. 5, the peak displayed as Ag 0 represents a peak derived from Ag metal. As is apparent from FIG. 5, it can be seen that Ag contained in PdAg / CeZrO 2 exists mainly as Ag metal.
FIG. 6 is an XPS (X-ray photoelectron spectroscopy) spectrum diagram when PdAg / CeZrO 2 is placed in an oxidizing atmosphere and in a reducing atmosphere. As is apparent from FIG. 6, it can be seen that Ag on the surface of the purification catalyst exists as Ag 2 O in an oxidizing atmosphere and exists as Ag metal in a reducing atmosphere. This is because, in Ag / α-Al 2 O 3 , which has low activity with respect to PM combustion, Ag on the surface exists as Ag metal even in an oxidizing atmosphere, and therefore, a purification catalyst that is preferably used in this embodiment. It can be said that this is a unique configuration.
以上を踏まえ、本実施形態で好ましく用いられる浄化触媒、即ち、酸素放出能を有する複合酸化物にAgを担持させた浄化触媒のPM燃焼メカニズムを、図7を参照しながら説明する。
図7は、Ag/CeZrO2の表面状態を模式的に示した図である。図7に示すように、酸素供給材としてのCeZrO2から、表面付近のAgメタル(図7においてAg0と表示されている粒子を意味する)に酸素が供給されると、Agメタルは活性種であるAg2O(図7においてAg+と表示されている粒子とO*と表示されている粒子を意味する)に変換される。そして、このAg2Oは、PMと反応することによりAgメタルに戻るものの、直ちにCeZrO2からの酸素がAgメタルに供給される結果、常に表面付近のAgは、Ag2Oの状態で存在すると考えられる。
従って、本実施形態で好ましく用いられる浄化触媒、即ち、酸素放出能を有する複合酸化物にAgを担持させた浄化触媒によれば、表面付近に存在する活性種Ag2Oの作用によって、低温下で効率良くPMを燃焼除去できると考えられる。
Based on the above, the PM combustion mechanism of the purification catalyst preferably used in the present embodiment, that is, the purification catalyst in which Ag is supported on the complex oxide having oxygen releasing ability will be described with reference to FIG.
FIG. 7 is a diagram schematically showing the surface state of Ag / CeZrO 2 . As shown in FIG. 7, when oxygen is supplied from CeZrO 2 as an oxygen supply material to Ag metal in the vicinity of the surface (meaning particles denoted as Ag 0 in FIG. 7), Ag metal becomes active species. Are converted to Ag 2 O (meaning particles indicated as Ag + and particles indicated as O * in FIG. 7). Then, the Ag 2 O, although returns to Ag metal by reacting with PM, results immediately oxygen from CeZrO 2 is supplied to the Ag metal, always Ag near the surface, when present in the form of Ag 2 O Conceivable.
Therefore, according to the purification catalyst preferably used in the present embodiment, that is, the purification catalyst in which Ag is supported on the complex oxide having oxygen releasing ability, the action of the active species Ag 2 O existing in the vicinity of the surface reduces the temperature. It is considered that PM can be burned and removed efficiently.
ここで、上記Agの結晶子径は、42nm未満であることが好ましい。Agの結晶子径が42nm以上である場合には、PMとの接触性が低下してしまうとともに、表面に存在するAg2O量が減少して酸素供給の律速となる結果、PMの燃焼反応の進行が阻害されるからである。
なお、Agの結晶子径は、例えばX線回折装置により測定可能である。
Here, the crystallite diameter of the Ag is preferably less than 42 nm. When the Ag crystallite diameter is 42 nm or more, the contact property with PM is lowered, and the amount of Ag 2 O present on the surface is reduced to control the rate of oxygen supply. As a result, the combustion reaction of PM This is because the progression of is inhibited.
The crystallite diameter of Ag can be measured by, for example, an X-ray diffractometer.
ところで、酸素放出能を有する複合酸化物としては、ペロブスカイト型、スピネル型、ルチル型、デラフォサイト型、マグネトプランバイト型、イルメナイト型、及びフルオライト型からなる群より選択される少なくとも1種を用いることができる。これらの中でも、酸素放出能の観点から、フルオライト型の複合酸化物が好ましく用いられる。
また、複合酸化物は、アルカリ土類金属元素、遷移金属元素、第12族元素、及び第13族元素からなる群より選択される少なくとも2種以上を構成元素として含むことにより、構成元素の価数を変化させて酸素の吸収及び放出を行うものが好ましい。
また、複合酸化物が酸素放出能を有するために、多原子価を持つ元素が少なくとも1種含まれていることが好ましい。具体的には、Zr、V、Cr、Mn、Fe、Co、Cu、Nb、Ta、Mo、W、Ce、Pr、Sm、Eu、Tb、Yb、Pt、Pd、Rh、Ir、Ruなどの遷移金属元素が少なくとも1種含まれていることが好ましい。酸素放出は、複合酸化物を構成する元素の価数の変化に応じて、電荷のバランスを保つために複合酸化物の格子中の酸素が脱離する現象である。このため、Agとの組合せによる酸素放出能の観点から、上記遷移金属元素のうち、Ce、Zr、Pr、La、及びYが特に好ましい。
By the way, the complex oxide having oxygen releasing ability includes at least one selected from the group consisting of perovskite type, spinel type, rutile type, delafossite type, magnetoplumbite type, ilmenite type, and fluorite type. Can be used. Among these, a fluorite-type complex oxide is preferably used from the viewpoint of oxygen releasing ability.
In addition, the composite oxide contains at least two kinds selected from the group consisting of alkaline earth metal elements, transition metal elements, Group 12 elements, and Group 13 elements as constituent elements. What absorbs and discharge | releases oxygen by changing a number is preferable.
In addition, since the composite oxide has an oxygen releasing ability, it is preferable that at least one element having a polyvalence is included. Specifically, Zr, V, Cr, Mn, Fe, Co, Cu, Nb, Ta, Mo, W, Ce, Pr, Sm, Eu, Tb, Yb, Pt, Pd, Rh, Ir, Ru, etc. It is preferable that at least one transition metal element is contained. Oxygen release is a phenomenon in which oxygen in the lattice of the composite oxide is desorbed in order to maintain a charge balance in accordance with a change in the valence of the elements constituting the composite oxide. For this reason, Ce, Zr, Pr, La, and Y are particularly preferable among the above transition metal elements from the viewpoint of oxygen releasing ability in combination with Ag.
また、本実施形態で用いる浄化触媒は、Ru、Pd、及びPtからなる群より選択される少なくとも1種の貴金属を、Agとともに上記複合酸化物に共担持するものであることが好ましい。
上記貴金属の担持量は、浄化触媒に対して0.1質量%〜3質量%と微量であることが好ましい。より好ましくは0.5質量%〜2質量%である。0.5質量%より少ない場合は、酸素放出能が低下し、2質量%より多い場合は、貴金属と複合酸化物の相互作用が強くなる結果、Agの担持効果が損なわれてしまう。
Moreover, it is preferable that the purification catalyst used in the present embodiment co-supports at least one noble metal selected from the group consisting of Ru, Pd, and Pt together with Ag on the composite oxide.
The amount of the precious metal supported is preferably a very small amount of 0.1% by mass to 3% by mass with respect to the purification catalyst. More preferably, it is 0.5 mass%-2 mass%. When the amount is less than 0.5% by mass, the oxygen releasing ability is lowered. When the amount is more than 2% by mass, the interaction between the noble metal and the composite oxide is strengthened, and as a result, the effect of supporting Ag is impaired.
本実施形態で用いる浄化触媒の調製方法は特に限定されないが、還元法により調製されたものであることが好ましい。還元法は、粒径制御されたAgイオン粒子を、DPF1上に高濃度で均一に担持させるために、湿式でAgコロイドとして合成する手法である。還元法では、金属イオン、還元剤、保護剤を使用し、金属イオンを0価に還元して、金属ナノ粒子を生成させる。保護剤は、粒子の成長を抑制し、金属粒子コアの周囲に保護基として結合して安定化するもので、チオール、ホスフィン、4級アンモニウム塩、ポリビニルアルコール、ポリビニルピロリドンなどが用いられる。また、還元剤としては、クエン酸、ヒドラジン、アミン、SBH、アルコール、アミノ酸などが用いられる。
また、本実施形態では、アミン還元法又はアルコール還元法がより好ましく用いられる。アミン還元法を用いる場合には、還元剤として、トリエチルアミンが好ましく用いられる。また、アルコール還元法を用いる場合には、還元剤として、エチレングリコールやエタノールが好ましく用いられる。
なお、浄化触媒を構成する複合酸化物の調製方法も特に限定されず、硝酸塩分解法、有機酸錯体重合法など従来公知の調製方法を用いることができる。
The method for preparing the purification catalyst used in the present embodiment is not particularly limited, but is preferably prepared by a reduction method. The reduction method is a method of synthesizing Ag ion particles having a controlled particle size as Ag colloids in a wet manner in order to uniformly support them on the DPF 1 at a high concentration. In the reduction method, metal ions, a reducing agent, and a protective agent are used, and metal ions are reduced to zero valence to generate metal nanoparticles. The protective agent suppresses the growth of the particles and binds and stabilizes as a protective group around the metal particle core, and thiol, phosphine, quaternary ammonium salt, polyvinyl alcohol, polyvinylpyrrolidone and the like are used. As the reducing agent, citric acid, hydrazine, amine, SBH, alcohol, amino acid and the like are used.
In this embodiment, an amine reduction method or an alcohol reduction method is more preferably used. When the amine reduction method is used, triethylamine is preferably used as the reducing agent. When using the alcohol reduction method, ethylene glycol or ethanol is preferably used as the reducing agent.
In addition, the preparation method of the composite oxide which comprises a purification catalyst is not specifically limited, either conventionally well-known preparation methods, such as a nitrate decomposition method and an organic acid complex polymerization method, can be used.
また、本実施形態で用いる浄化触媒では、複合酸化物にAgや貴金属を担持させる方法については特に限定されないが、一般的なディッピング法の他、発泡法が好ましく用いられる。
ディッピング法では、例えば、浄化触媒を構成する材料を所定量含むスラリーを湿式粉砕などにより作製し、作製したスラリー中にDPFを浸漬させた後、DPFを引き上げて所定の温度条件で焼成を行うことにより、DPFに浄化触媒を担持させることができる。
また、発泡法では、上記ディッピング法で作製したスラリー中に、クエン酸などの有機酸を添加することにより、焼成時に触媒粒子を発泡させ、分散させることができる。このため、発泡法によれば、触媒粒子を全体に分散させることができるため、DPF表面に触媒を均一に担持させることができる。
In the purification catalyst used in the present embodiment, the method of supporting Ag or noble metal on the composite oxide is not particularly limited, but a foaming method is preferably used in addition to a general dipping method.
In the dipping method, for example, a slurry containing a predetermined amount of a material constituting the purification catalyst is prepared by wet pulverization, and after the DPF is immersed in the prepared slurry, the DPF is pulled up and fired at a predetermined temperature condition. Thus, the purification catalyst can be supported on the DPF.
Further, in the foaming method, catalyst particles can be foamed and dispersed during firing by adding an organic acid such as citric acid to the slurry produced by the dipping method. For this reason, according to the foaming method, since the catalyst particles can be dispersed throughout, the catalyst can be uniformly supported on the DPF surface.
次に、浄化触媒とPMとの接触性がPM燃焼特性に及ぼす影響について説明するとともに、浄化触媒の好ましい粒子径、被覆率、空隙の大きさについて説明する。 Next, the influence of the contact between the purification catalyst and PM on the PM combustion characteristics will be described, and the preferable particle diameter, coverage, and void size of the purification catalyst will be described.
図8は、PdAg/CeZrO2のTG−DTAチャート図であり、このTG−DTAチャート図は、PdAg/CeZrO2のPM燃焼特性を示している。具体的には、昇温条件を、乾燥空気200ml/分の雰囲気下で20℃/分とし、浄化触媒に対するPM量を5質量%として、乳鉢と乳棒を用いてタイトコンタクト化させたときのPM燃焼特性を示している。また、図8において、TGは、タイトコンタクト化した浄化触媒とPMとを昇温したときの重量減少曲線を表しており、DTGは、TGの一次微分曲線である。
図8に示すように、重量減少の開始が200℃付近であり、重量減少の終了が400℃付近であることから、200℃からPMが着火し、400℃でPMの燃焼が終了することが分かる。このように、接触性が良好なときのPM燃焼特性を、浄化触媒のポテンシャルと定義すると、PdAg/CeZrO2は、200℃〜400℃でPMを燃焼可能なポテンシャルを有すると言える。
FIG. 8 is a TG-DTA chart of PdAg / CeZrO 2 , and this TG-DTA chart shows the PM combustion characteristics of PdAg / CeZrO 2 . Specifically, the temperature rise condition is 20 ° C./min in an atmosphere of dry air 200 ml / min, the PM amount with respect to the purification catalyst is 5 mass%, and the PM when tight contact is made using a mortar and pestle It shows combustion characteristics. In FIG. 8, TG represents a weight reduction curve when the temperature of the purified catalyst and PM that are tightly contacted is raised, and DTG is a primary differential curve of TG.
As shown in FIG. 8, since the start of weight reduction is around 200 ° C. and the end of weight reduction is around 400 ° C., PM ignites from 200 ° C., and combustion of PM ends at 400 ° C. I understand. Thus, if the PM combustion characteristic when the contactability is good is defined as the potential of the purification catalyst, it can be said that PdAg / CeZrO 2 has a potential capable of burning PM at 200 ° C. to 400 ° C.
図9は、PdAg/CeZrO2について強制再生試験を実施したときの時間とPM残存率との関係を示す図である。具体的には、500℃定常試験を実施して得られた図である。本試験では、先ず、15ccのテストパネルにPdAg/CeZrO2をコートする。浄化触媒がコートされたテストパネルをディーゼルエンジンの排気流通下にセットし、上流側には酸化触媒PtPd/Al2O3を配置させる。次いで、ディーゼルエンジンの運転を実施し、PMの捕集量が4g/LになるようにPMを捕集させる。その後、N2中で昇温させ、500℃に達したところで700ppmのNO、5%のO2、及びN2バランスガスからなるモデルガスを線速度SV=100000h−1で導入する。このような手順により、強制再生試験を実施したときのPM残存率を調べた結果が図9である。
図9は、500℃定常時のPM燃焼速度を表しており、燃焼終了時間が短いほどPM燃焼速度は速くなることを意味する。浄化触媒PdAg/CeZrO2のポテンシャルとしては、上述したように400℃以下でPMを燃焼できるため、500℃であれば瞬時にPMの燃焼が終了してもよいはずである。ところが、図9に示すように、90%のPMの燃焼が完了するまでの時間(以下、「T90」という)は、およそ20分と長時間を要することが分かる。これは、実際にディーゼルエンジンの排気流通下に配置した場合には、PMと浄化触媒との接触性が良好でないことが原因であると考えられ、これにより浄化触媒のポテンシャルが十分に発揮できていないと考えられる。
FIG. 9 is a diagram showing the relationship between the time when the forced regeneration test is performed on PdAg / CeZrO 2 and the PM residual ratio. Specifically, it is the figure obtained by implementing a 500 degreeC steady state test. In this test, first, PdAg / CeZrO 2 is coated on a 15 cc test panel. A test panel coated with a purification catalyst is set under the exhaust flow of the diesel engine, and an oxidation catalyst PtPd / Al 2 O 3 is disposed upstream. Next, the diesel engine is operated to collect PM so that the amount of PM collected is 4 g / L. Thereafter, the temperature is raised in N 2 , and when the temperature reaches 500 ° C., a model gas composed of 700 ppm NO, 5% O 2 , and N 2 balance gas is introduced at a linear velocity SV = 100000 h −1 . FIG. 9 shows the result of examining the PM remaining rate when the forced regeneration test is performed by such a procedure.
FIG. 9 shows the PM combustion rate at a steady temperature of 500 ° C., which means that the shorter the combustion end time, the faster the PM combustion rate. As described above, the potential of the purification catalyst PdAg / CeZrO 2 can be combusted at 400 ° C. or lower, so that if it is 500 ° C., the combustion of PM should be completed instantaneously. However, as shown in FIG. 9, it can be seen that the time required to complete the combustion of 90% PM (hereinafter referred to as “T90”) takes approximately 20 minutes. This is considered to be caused by poor contact between the PM and the purification catalyst when it is actually placed under the exhaust flow of the diesel engine. It is not considered.
以下、浄化触媒とPMとの接触性について、マクロレベル、ミクロレベル、及びナノレベルで調査を行った結果を踏まえて説明する。 Hereinafter, the contact property between the purification catalyst and PM will be described based on the results of investigations at a macro level, a micro level, and a nano level.
先ずは、マクロレベルでの調査として、浄化触媒表面における触媒粒子の分布状態の調査である。図10は、ディッピング法によりPdAg/CeZrO2を担持させたDPF表面(後述する比較例2に相当。即ち、PM燃焼性能は劣る。)のSEM像である。この結果から、ディッピング法の場合には、その条件によっては、触媒粒子が偏っていたり、細孔が埋まっていたり埋まっていなかったりと不均一であることが分かる。PMの堆積は、初期はDPFの細孔内で起こり、堆積量が多くなるとDPF表層全面に堆積していくため、PMが堆積する部分によっては触媒が存在しない場合が生じる。従って、DPFの表面に浄化触媒を均一に担持させることが重要であると言える。 First, as an investigation at a macro level, a distribution state of catalyst particles on the purification catalyst surface is investigated. FIG. 10 is an SEM image of the DPF surface (corresponding to Comparative Example 2 described later, ie, the PM combustion performance is inferior) carrying PdAg / CeZrO 2 by the dipping method. From this result, it can be seen that, in the case of the dipping method, depending on the conditions, the catalyst particles are uneven and the pores are buried or not filled. PM is initially deposited in the pores of the DPF, and when the amount of deposition increases, the PM is deposited on the entire surface of the DPF. Therefore, depending on the portion where PM is deposited, the catalyst may not exist. Therefore, it can be said that it is important to uniformly carry the purification catalyst on the surface of the DPF.
次いで、ミクロレベルでの調査として、浄化触媒の粒子径の調査である。図11は、図10の部分拡大図である。図11に示すように、ディッピング法では、その条件によっては触媒粒子の粒子径が大きいことが分かる。具体的には、HORIBA製粒度分布装置「LA920」を用いて測定したところ、平均粒子径(D50:メジアン径)は約5μm、触媒粒子の粒度分布における小粒径側からの累積分布が90%となるときの粒子径D90は約10μmであり、大きな触媒粒子である。従って、浄化触媒の粒子径を微細化して接触面積を増大させ、PMとの接触性を向上させることが重要であると言える。 Next, as a survey at the micro level, the particle size of the purification catalyst is investigated. FIG. 11 is a partially enlarged view of FIG. As shown in FIG. 11, in the dipping method, the particle diameter of the catalyst particles is large depending on the conditions. Specifically, when measured using a particle size distribution device “LA920” manufactured by HORIBA, the average particle size (D50: median size) is about 5 μm, and the cumulative distribution from the small particle size side in the particle size distribution of the catalyst particles is 90%. The particle diameter D90 is about 10 μm, which is a large catalyst particle. Therefore, it can be said that it is important to refine the particle size of the purification catalyst to increase the contact area and improve the contact property with PM.
さらに、ナノレベルでも、活性種Agの接点数が、PMとの接触性向上の観点から重要であると考えられる。即ち、活性種Agの微細化を行うことにより、活性種Agの接点数を増加させることが重要であると言える。 Furthermore, even at the nano level, the number of contacts of the active species Ag is considered to be important from the viewpoint of improving the contact property with PM. That is, it can be said that it is important to increase the number of contacts of the active species Ag by miniaturizing the active species Ag.
以上、詳しく述べたように、浄化触媒とPMとの接触性は、PM燃焼特性に重大な影響を及ぼすことから、本実施形態で用いる浄化触媒は、PMとの良好な接触性を確保すべく、以下のような構成を備える。
具体的には、本実施形態で用いる浄化触媒は、上記D90が2μm以下であることを特徴とする。D90が2μm以下であることにより、浄化触媒とPMとの接触性を向上させることができる。なお、D90は、粒度分布測定装置により測定可能であり、例えば、HORIBA製粒度分布測定装置「LA−920」により測定可能である。
また、本実施形態で用いる浄化触媒は、3μm〜10μmの空隙を有することが好ましい。この範囲の大きさの空隙を有することにより、浄化触媒をDPF表面に均一に担持させることができ、浄化触媒とPMとの接触性をより向上させることができる。さらには、水銀ポロシメータにより測定された孔径分布において、4μm〜8μmのピークを有することがより好ましい。なお、空隙の大きさは、水銀ポロシメータにより測定可能であり、例えば、島津製作所製水銀ポロシメータ「ポアサイザ9320」を用いて測定可能である。
また、DPF表面における浄化触媒の被覆率が30%以上であることが好ましい。被覆率が30%以上であれば、浄化触媒とPMとの良好な接触状態を確保できる。より好ましい被覆率は、70%以上である。なお、被覆率は、SEM観察により得られたSEM画像において、コントラストを強調させて白色部分(浄化触媒に相当)と黒色部分(DPFに相当)に分けた後、白色部分と黒色部分の面積を算出し、算出した面積値から求めることができる。
As described above in detail, the contact between the purification catalyst and the PM has a significant effect on the PM combustion characteristics. Therefore, the purification catalyst used in this embodiment should ensure good contact with the PM. The following configuration is provided.
Specifically, the purification catalyst used in the present embodiment is characterized in that the D90 is 2 μm or less. When D90 is 2 μm or less, the contact property between the purification catalyst and PM can be improved. D90 can be measured by a particle size distribution measuring device, for example, by a HORIBA particle size distribution measuring device “LA-920”.
Moreover, it is preferable that the purification catalyst used by this embodiment has a space | gap of 3 micrometers-10 micrometers. By having the voids in this range, the purification catalyst can be uniformly supported on the DPF surface, and the contact between the purification catalyst and PM can be further improved. Furthermore, it is more preferable that the pore size distribution measured by a mercury porosimeter has a peak of 4 μm to 8 μm. The size of the gap can be measured by a mercury porosimeter, for example, by using a mercury porosimeter “Pore Sizer 9320” manufactured by Shimadzu Corporation.
In addition, the coverage of the purification catalyst on the DPF surface is preferably 30% or more. If the coverage is 30% or more, a good contact state between the purification catalyst and PM can be secured. A more preferable coverage is 70% or more. In the SEM image obtained by SEM observation, the coverage is divided into a white part (corresponding to the purification catalyst) and a black part (corresponding to the DPF) by enhancing the contrast, and then the area of the white part and the black part is calculated. It can be calculated and obtained from the calculated area value.
なお、浄化触媒とPMとの接触性の向上については、以下の指標を用いて評価することが好ましい。
図12は、強制再生を実施したときの時間とPM残存率との関係の一例を示す図である。図12に示すように、500℃強制再生試験を実施した場合、初期はある程度の量のPMが瞬時に燃え、その後燃焼が穏やかになる。これは、初期においては、浄化触媒とPMとが良好に接触している部分については瞬時に燃焼するためである。そして、PMが燃焼した部分にはPMが存在しなくなる結果、浄化触媒とPMとの間に隙間が形成され、PMの燃焼反応の進行が遅くなる。このことから、試験開始〜30秒の間でのPM燃焼を初期燃焼と定義し、試験開始後30秒経過後の穏やかなPM燃焼をルーズコンタクト燃焼と定義する。また、浄化触媒とPMとの接触比率を、下記の数式(1)により算出し、この接触比率の増加により、接触性の向上を確認することができる。
[数1]
接触比率=初期燃焼量/全体PM量 ・・・(1)
In addition, about the improvement of the contact property of a purification catalyst and PM, it is preferable to evaluate using the following parameters | indexes.
FIG. 12 is a diagram illustrating an example of the relationship between the time when forced regeneration is performed and the PM remaining rate. As shown in FIG. 12, when the 500 ° C. forced regeneration test is performed, a certain amount of PM burns instantaneously in the initial stage, and then the combustion becomes gentle. This is because, in the initial stage, the portion where the purification catalyst and PM are in good contact is burned instantaneously. As a result of the absence of PM in the part where PM is burned, a gap is formed between the purification catalyst and PM, and the progress of the combustion reaction of PM is slowed. From this, PM combustion between the start of the test and 30 seconds is defined as initial combustion, and mild PM combustion after 30 seconds from the start of the test is defined as loose contact combustion. Further, the contact ratio between the purification catalyst and PM is calculated by the following mathematical formula (1), and the improvement in the contact property can be confirmed by the increase in the contact ratio.
[Equation 1]
Contact ratio = initial combustion amount / total PM amount (1)
以上、本実施形態で好ましく用いられる浄化触媒について詳しく説明したが、本実施形態のDPF1は、上記の浄化触媒に加えて、排気中のNOからNO2を生成するNO2生成触媒をさらに有することが好ましい。
NO2生成触媒としては特に限定はされないが、Pt、Pd、及びRhからなる群より選択される少なくとも1種の貴金属を含むことが好ましい。
また、DPF1に上記触媒を担持させる際には、先ず下層として浄化触媒を担持させた後、上層としてNO2生成触媒を担持させることが好ましい。
Although the purification catalyst preferably used in the present embodiment has been described in detail above, the DPF 1 of the present embodiment further includes a NO 2 generation catalyst that generates NO 2 from NO in the exhaust in addition to the above purification catalyst. Is preferred.
There are no particular limitations on the NO 2 generation catalysts, Pt, preferably contains at least one noble metal selected from the group consisting of Pd, and Rh.
Further, when the DPF 1 supports the catalyst, it is preferable to first support the purification catalyst as the lower layer and then support the NO 2 generation catalyst as the upper layer.
上記の構成を備える本実施形態によれば、以下の効果が奏される。
本実施形態によれば、浄化触媒の粒度分布における小粒径側からの累積分布が90%となるときの粒子径D90が2μm以下であることにより、DPF1の表面を緻密な浄化触媒からなる層で被覆できる。また、浄化触媒とPMの接触面積を増大でき、浄化触媒とPMとの接触性を向上させることができるため、PMの燃焼性能を向上させることができる。
また、本実施形態によれば、従来よりも低温下で効率良くPMを燃焼させてDPF1を再生することができ、DPF1の再生処理に伴う燃費ロスや浄化触媒の劣化を抑制できる。また、通常走行時においてもPMを連続燃焼させ得るため、再生頻度を低減でき、燃費の悪化を低減できる。さらには、低温下でDPF1を再生できるため、排気系レイアウトの自由度が高く、例えば車両床下にDPF1を配置することもできる。
According to the present embodiment having the above configuration, the following effects can be obtained.
According to this embodiment, the particle diameter D90 when the cumulative distribution from the small particle diameter side in the particle size distribution of the purification catalyst is 90% is 2 μm or less, so that the surface of the DPF 1 is made of a dense purification catalyst. Can be covered. Further, the contact area between the purification catalyst and PM can be increased, and the contact property between the purification catalyst and PM can be improved, so that the PM combustion performance can be improved.
Further, according to the present embodiment, it is possible to regenerate DPF 1 by efficiently burning PM at a lower temperature than in the past, and it is possible to suppress fuel consumption loss and deterioration of the purification catalyst due to DPF 1 regeneration processing. Further, since PM can be continuously burned even during normal travel, the regeneration frequency can be reduced, and deterioration of fuel consumption can be reduced. Furthermore, since the DPF 1 can be regenerated at a low temperature, the degree of freedom of the exhaust system layout is high. For example, the DPF 1 can be arranged under the vehicle floor.
また、本実施形態によれば、3μm〜10μmの空隙を設けて浄化触媒をDPF1に担持させることにより、浄化触媒をDPF1の表面に均一に担持させることができる。このため、浄化触媒とPMとの接触性をより向上させることができ、PMの燃焼性能をより向上させることができる。また、3μm〜10μmの空隙の存在によって排気の拡散性が良好となるため、この点からもPMの燃焼性能の向上に寄与できる。 Further, according to the present embodiment, the purification catalyst can be uniformly supported on the surface of the DPF 1 by providing the gap of 3 μm to 10 μm and supporting the purification catalyst on the DPF 1. For this reason, the contact property of a purification catalyst and PM can be improved more, and the combustion performance of PM can be improved more. Moreover, since the diffusibility of the exhaust gas is improved due to the presence of the gaps of 3 μm to 10 μm, it is possible to contribute to the improvement of PM combustion performance from this point.
また、本実施形態によれば、DPF1の表面における浄化触媒の被覆率が30%以上であるため、浄化触媒とPMとの良好な接触状態を確保できる。このため、PMの燃焼性能をより向上させることができ、上記の効果をより高めることができる。 Moreover, according to this embodiment, since the coverage of the purification catalyst on the surface of the DPF 1 is 30% or more, it is possible to ensure a good contact state between the purification catalyst and PM. For this reason, the combustion performance of PM can be improved more and said effect can be heightened more.
また、本実施形態によれば、4μm〜8μmの空隙のピークを設けて浄化触媒をDPF1に担持させることにより、浄化触媒の担持量を増加することなく、DPF1の表面全体を浄化触媒で被覆することができる。このため、PMの燃焼性能をより向上させることができ、上記の効果をより高めることができる。 Further, according to the present embodiment, the entire surface of the DPF 1 is coated with the purification catalyst without increasing the amount of the purification catalyst supported by providing the DPF 1 with the purification catalyst by providing a peak of the gap of 4 μm to 8 μm. be able to. For this reason, the combustion performance of PM can be improved more and said effect can be heightened more.
また、本実施形態によれば、Agを含む浄化触媒を用いることにより、Ag系触媒が本来有する優れた燃焼性能を十分に発揮できるため、低温下においても効率良くPMを燃焼除去できる。また、約600℃の高温域での再生処理においては、瞬時にPMを燃焼除去することができ、通常走行の加速時など温度が約350℃に達した場合にも、特別な制御無しにPMの一部を燃焼させることができる。 Moreover, according to this embodiment, by using the purification catalyst containing Ag, the excellent combustion performance inherent to the Ag-based catalyst can be sufficiently exhibited, so that PM can be efficiently removed by combustion even at low temperatures. In the regeneration process in the high temperature range of about 600 ° C, PM can be burnt and removed instantaneously, and even when the temperature reaches about 350 ° C, such as during normal running acceleration, PM can be obtained without special control. A part of can be burned.
また、本実施形態によれば、アルカリ土類金属元素、遷移金属元素、第12族元素、及び第13族元素からなる群より選択される少なくとも2種以上を構成元素として含む複合酸化物を用いることにより、構成元素の価数を変化させて酸素の吸収及び放出を行うことができる。また、このような酸素放出能を有する複合酸化物にAgを担持させることにより、複合酸化物の酸素放出能をより低温下で発揮させることができる。このため、PMをより低温下で効率良く燃焼させることができる。 In addition, according to the present embodiment, a composite oxide containing at least two or more selected from the group consisting of alkaline earth metal elements, transition metal elements, Group 12 elements, and Group 13 elements as constituent elements is used. Thus, oxygen can be absorbed and released by changing the valence of the constituent elements. In addition, by supporting Ag on the composite oxide having such an oxygen releasing ability, the oxygen releasing ability of the composite oxide can be exhibited at a lower temperature. For this reason, PM can be efficiently burned at a lower temperature.
また、本実施形態によれば、Agの結晶子径が42nm以下で小さいため、表面に存在するAg2O量が減少して酸素供給の律速となってPMの燃焼反応の進行が阻害されることがない。このため、PMを低温下で効率良く燃焼させることができる。 Further, according to the present embodiment, since the crystallite diameter of Ag is small at 42 nm or less, the amount of Ag 2 O present on the surface is reduced, the rate of oxygen supply is limited, and the progress of the PM combustion reaction is inhibited. There is nothing. For this reason, PM can be burned efficiently at low temperatures.
また、本実施形態によれば、Ru、Pd、及びPtからなる群より選択される少なくとも1種の貴金属を、Agとともに複合酸化物に共担時させることにより、貴金属による酸素供給能の増加、及び貴金属によるブロッキング効果により、Agの微粒子化が可能となる。このため、酸素放出能を有する複合酸化物の酸素放出能を大幅に向上させることができ、PMの燃焼性能をより向上させることができる。 Further, according to the present embodiment, at least one kind of noble metal selected from the group consisting of Ru, Pd, and Pt is added to the composite oxide together with Ag, thereby increasing the oxygen supply capability by the noble metal, And the blocking effect by the noble metal makes it possible to make Ag fine particles. For this reason, the oxygen releasing ability of the complex oxide having oxygen releasing ability can be greatly improved, and the combustion performance of PM can be further improved.
また、本実施形態によれば、還元法により浄化触媒を調製することにより、微細で均一なAgイオンを高濃度で得ることができ、Agの凝集を効果的に抑制できる。このため、触媒粒子の微細化が可能となり、PMの燃焼性能をより向上させることができる。 Moreover, according to this embodiment, by preparing the purification catalyst by a reduction method, fine and uniform Ag ions can be obtained at a high concentration, and Ag aggregation can be effectively suppressed. For this reason, the catalyst particles can be miniaturized, and the PM combustion performance can be further improved.
また、本実施形態によれば、アミン還元法の還元剤としてトリエチルアミンを用い、あるいはアルコール還元法の還元剤としてエチレングリコール又はエタノールを用いることにより、Agイオンの還元化を効果的に進行させることができるとともに、Agを微細化できる。このため、触媒粒子の微細化が可能となり、PMの燃焼性能をより向上させることができる。 Further, according to the present embodiment, the reduction of Ag ions can be effectively advanced by using triethylamine as a reducing agent in the amine reduction method or using ethylene glycol or ethanol as the reducing agent in the alcohol reduction method. In addition, Ag can be made finer. For this reason, the catalyst particles can be miniaturized, and the PM combustion performance can be further improved.
また、本実施形態によれば、NO2生成触媒を共存させることにより、生成したNO2が酸素放出能を有する複合酸化物の表面に吸着し、表面のNO2濃度が高く保たれる。このため、浄化触媒による酸素とPMの反応に加えて、AgによるNO2とPMの反応が促進され、PMを低温下で効率良く燃焼させることができる。 Further, according to this embodiment, in the coexistence of the NO 2 generation catalyst, resulting NO 2 is adsorbed on the surface of the composite oxide having oxygen release capacity, NO 2 concentration on the surface is kept high. For this reason, in addition to the reaction of oxygen and PM by the purification catalyst, the reaction of NO 2 and PM by Ag is promoted, and PM can be efficiently burned at a low temperature.
また、本実施形態によれば、Pt、Pd、及びRhからなる群より選択される少なくとも1種の貴金属を含むNO2生成触媒を用いることにより、効果的にNO2を生成できるため、AgによるNO2とPMの反応がより促進され、PMを低温下で効率良く燃焼させることができる。 In addition, according to the present embodiment, NO 2 can be effectively generated by using the NO 2 generation catalyst containing at least one kind of noble metal selected from the group consisting of Pt, Pd, and Rh. The reaction between NO 2 and PM is further promoted, and PM can be efficiently burned at a low temperature.
なお、本発明は上記実施形態に限定されるものではなく、本発明の目的を達成できる範囲での変形、改良などは本発明に含まれる。 It should be noted that the present invention is not limited to the above-described embodiment, and modifications, improvements, etc. within a scope that can achieve the object of the present invention are included in the present invention.
次に本発明の実施例について説明するが、本発明はこれら実施例に限定されるものではない。 Next, examples of the present invention will be described, but the present invention is not limited to these examples.
<実施例1>
[1質量%Pd30質量%Ag/CeZrO2、D90=2μm以下]
市販の特級試薬である、硝酸銀、硝酸パラジウム、CeZrO2(阿南化成製、Ce/Zr=2/8)、及びH2Oを、所定の組成となるように秤量して混合した。次いで、これをエバポレータにて減圧乾固し、200℃×2時間乾燥させた後、700℃×2時間の大気焼成を行うことにより、触媒粉末Aを得た。
上記で得た触媒粉末A、市販のSiO2ゾル、及びH2Oを、所定の組成となるように秤量して混合した。そこに、φ2mmのZrボールを、容器に対して50%の量混入し、ボールミルにて3日間、湿式粉砕を行うことにより、スラリーAを得た。
得られたスラリーAを、SiC製DPFにディッピング担持させた後、700℃×2時間の焼成を行うことにより得られたCSFを、実施例1とした。触媒の担持量は、60g/Lとした。
<Example 1>
[1% by mass Pd 30% by mass Ag / CeZrO 2 , D90 = 2 μm or less]
Commercially available special grade silver nitrate, palladium nitrate, CeZrO 2 (manufactured by Anan Kasei, Ce / Zr = 2/8), and H 2 O were weighed and mixed so as to have a predetermined composition. Next, this was dried under reduced pressure using an evaporator, dried at 200 ° C. for 2 hours, and then fired in the atmosphere at 700 ° C. for 2 hours to obtain catalyst powder A.
Catalyst powder A obtained above, commercially available SiO 2 sol, and H 2 O were weighed and mixed so as to have a predetermined composition. Thereto, a Zr ball having a diameter of 2 mm was mixed in an amount of 50% with respect to the container, and wet pulverization was performed in a ball mill for 3 days to obtain slurry A.
The obtained slurry A was dipped and supported on a SiC DPF, and then CSF obtained by firing at 700 ° C. for 2 hours was defined as Example 1. The catalyst loading was 60 g / L.
<実施例2>
[1質量%Pd30質量%Ag/CeZrO2、D90=2μm以下、発泡法]
φ10mmのZrボールを、容器に対して10%の量混入し、ボールミルにて12時間、湿式粉砕した後、クエン酸を触媒量に対して4倍量添加した以外は、実施例1と同様の操作を行うことにより得られたCSFを、実施例2とした。触媒の担持量は、60g/Lとした。
<Example 2>
[1% by mass Pd 30% by mass Ag / CeZrO 2 , D90 = 2 μm or less, foaming method]
The same amount as in Example 1 except that 10% of a Zr ball having a diameter of 10 mm was mixed in a container, wet-ground by a ball mill for 12 hours, and then citric acid was added 4 times the amount of the catalyst. The CSF obtained by performing the operation was taken as Example 2. The catalyst loading was 60 g / L.
<実施例3>
[1質量%Pd30質量%Ag/CeZrO2、D90=2μm以下、発泡法]
スラリーAに、クエン酸を触媒量に対して4倍量添加した以外は、実施例1と同様の操作を行うことにより得られたCSFを、実施例3とした。触媒の担持量は、60g/Lとした。
<Example 3>
[1% by mass Pd 30% by mass Ag / CeZrO 2 , D90 = 2 μm or less, foaming method]
CSF obtained by performing the same operation as in Example 1 except that citric acid was added in an amount of 4 times the amount of catalyst to the slurry A was defined as Example 3. The catalyst loading was 60 g / L.
<実施例4>
[下層:1質量%Pd30質量%Ag/CeZrO2、D90=2μm以下、発泡法]
[上層:14質量%PtPd/Al2O3]
市販の特級試薬であるジニトロジアミン白金硝酸溶液、硝酸パラジウム、Al2O3(住友金属化学製)、及びH2Oを、所定の組成となるように秤量して混合した。次いで、これを、エバポレータにて減圧乾固し、200℃×2時間乾燥させた後、700℃×2時間の大気焼成を行うことにより、NO2生成触媒である触媒粉末Bを得た。
上記で得た触媒粉末B、市販のSiO2ゾル、及びH2Oを所定の組成となるように秤量して混合した。そこに、φ10mmのZrボールを容器に対して10%の量混入し、ボールミルにて12時間、湿式粉砕を行うことにより、スラリーBを得た。
実施例3で作製したCSFに、スラリーBをディッピング担持させた後、700℃×2時間の焼成を行うことにより得られたCSFを、実施例4とした。触媒の担持量は、上層60g/L、下層10g/Lとした。
<Example 4>
[Lower layer: 1% by mass Pd 30% by mass Ag / CeZrO 2 , D90 = 2 μm or less, foaming method]
[Upper layer: 14% by mass PtPd / Al 2 O 3 ]
A commercially available special grade reagent, dinitrodiamine platinum nitric acid solution, palladium nitrate, Al 2 O 3 (manufactured by Sumitomo Metal Chemical), and H 2 O were weighed and mixed so as to have a predetermined composition. Next, this was dried under reduced pressure with an evaporator, dried at 200 ° C. for 2 hours, and then fired in the air at 700 ° C. for 2 hours to obtain catalyst powder B as a NO 2 production catalyst.
The catalyst powder B obtained above, a commercially available SiO 2 sol, and H 2 O were weighed and mixed so as to have a predetermined composition. Thereto, Zr balls having a diameter of 10 mm were mixed in an amount of 10% with respect to the container, and wet pulverization was performed for 12 hours in a ball mill to obtain slurry B.
The CSF obtained by dipping and supporting the slurry B on the CSF produced in Example 3 and then firing at 700 ° C. for 2 hours was defined as Example 4. The amount of catalyst supported was 60 g / L for the upper layer and 10 g / L for the lower layer.
<実施例5>
[下層:1質量%Pd30質量%Ag/CeZrO2、D90=2μm以下、発泡法、アミン還元法]
[上層:14質量%PtPd/Al2O3]
市販の特級試薬である硝酸銀、ジニトロジアミンパラジウム、トリエチルアミン、ミリスチン酸を、所定の組成となるように秤量して混合溶液を作製した。この混合溶液に、CeZrO2(阿南化成製、Ce/Zr=2/8)を所定の組成となるように添加し、80℃×2時間混合した。次いで、メタノールにて洗浄ろ過を行い、60℃×12時間乾燥後、700℃×2時間の大気焼成を行うことにより、触媒粉末Cを得た。
上記で得た触媒粉末Cにより下層を形成する以外は、実施例4と同様の操作を行うことにより得られたCSFを、実施例5とした。触媒の担持量は、上層60g/L、下層10g/Lとした。
<Example 5>
[Lower layer: 1% by mass Pd 30% by mass Ag / CeZrO 2 , D90 = 2 μm or less, foaming method, amine reduction method]
[Upper layer: 14% by mass PtPd / Al 2 O 3 ]
Commercially available special grade silver nitrate, dinitrodiamine palladium, triethylamine, and myristic acid were weighed so as to have a predetermined composition to prepare a mixed solution. CeZrO 2 (manufactured by Anan Kasei, Ce / Zr = 2/8) was added to the mixed solution so as to have a predetermined composition, and mixed at 80 ° C. for 2 hours. Next, the catalyst powder C was obtained by washing and filtering with methanol, drying at 60 ° C. for 12 hours, and then firing in air at 700 ° C. for 2 hours.
CSF obtained by performing the same operation as in Example 4 except that the lower layer was formed with the catalyst powder C obtained above was taken as Example 5. The amount of catalyst supported was 60 g / L for the upper layer and 10 g / L for the lower layer.
<比較例1>
[14質量%PtPd/Al2O3]
スラリーBを、SiC製DPFにディッピング担持させ、700℃×2時間の焼成を行うことにより得られたCSFを、比較例1とした。触媒の担持量は、35g/Lとした。
<Comparative Example 1>
[14% by mass PtPd / Al 2 O 3 ]
The CSF obtained by dipping and supporting the slurry B on a SiC DPF and firing at 700 ° C. for 2 hours was defined as Comparative Example 1. The catalyst loading was 35 g / L.
<比較例2>
[1質量%Pd30質量%Ag/CeZrO2]
クエン酸を添加しない以外は、実施例2と同様の操作を行うことにより得られたCSFを、比較例2とした。触媒の担持量は、60g/Lとした。
<Comparative example 2>
[1% by mass Pd 30% by mass Ag / CeZrO 2 ]
CSF obtained by performing the same operation as in Example 2 except that citric acid was not added was used as Comparative Example 2. The catalyst loading was 60 g / L.
<参考例1>
触媒粉末A、市販のSiO2ゾル、及びH2Oを、所定の組成となるように秤量し、さらにφ10mmのZrボールを容器に対して10%の量混入し、ボールミルにて12時間湿式粉砕を行うことにより、スラリーCを得た。
スラリーCを200℃で攪拌しながら蒸発乾固させた粉末を、参考例1とした。
<Reference Example 1>
Catalyst powder A, commercially available SiO 2 sol, and H 2 O are weighed so as to have a predetermined composition, and 10% of Zr balls with a diameter of 10 mm are mixed into the container, and wet pulverized in a ball mill for 12 hours. The slurry C was obtained by performing.
A powder obtained by evaporating and drying the slurry C at 200 ° C. while stirring was used as Reference Example 1.
<参考例2>
スラリーCを、φ0.1mmZrビーズを用いたビーズミル装置Aにより2時間湿式粉砕した後、200℃で攪拌しながら蒸発乾固させた粉末を、参考例2とした。
<Reference Example 2>
The slurry C was wet pulverized for 2 hours by a bead mill apparatus A using φ0.1 mmZr beads and then evaporated to dryness while stirring at 200 ° C. as Reference Example 2.
<参考例3>
スラリーCを、φ0.1mmZrビーズを用いたビーズミル装置B(ビーズミル装置Aよりも7〜8倍の粉砕エネルギを持つと考えられている)により45分間湿式粉砕した後、200℃で攪拌しながら蒸発乾固させた粉末を、参考例3とした。
<Reference Example 3>
Slurry C was wet pulverized for 45 minutes with a bead mill B using φ0.1 mmZr beads (considered to have a pulverization energy 7 to 8 times that of bead mill A) and then evaporated with stirring at 200 ° C. The dried powder was designated as Reference Example 3.
<参考例4>
スラリーCを、φ0.1mmZrビーズを用いたビーズミル装置Bにより45分間湿式粉砕した後、さらに湿式の高圧せん断装置にて50MPa/3Passしたものを200℃で攪拌しながら蒸発乾固させた粉末を、参考例4とした。
<Reference Example 4>
After the slurry C was wet pulverized for 45 minutes by a bead mill apparatus B using φ0.1 mmZr beads, the powder obtained by evaporating to dryness while stirring at 200 ° C. with 50 MPa / 3 Pass by a wet high-pressure shearing apparatus, It was set as Reference Example 4.
<参考例5>
スラリーAの湿式粉砕時間を12時間とし、200℃で攪拌しながら蒸発乾固させた粉末を、参考例5とした。
<Reference Example 5>
A slurry obtained by evaporating and drying the slurry A with a wet pulverization time of 12 hours and stirring at 200 ° C. was defined as Reference Example 5.
<参考例6>
スラリーAを200℃で攪拌しながら蒸発乾固させた粉末を、参考例6とした。
<Reference Example 6>
A powder obtained by evaporating and drying the slurry A while stirring at 200 ° C. was used as Reference Example 6.
<参考例7>
触媒粉末Aを、参考例7とした。
<Reference Example 7>
The catalyst powder A was designated as Reference Example 7.
<参考例8>
触媒粉末Cを、参考例8とした。
<Reference Example 8>
The catalyst powder C was referred to as Reference Example 8.
<参考例9>
市販の特級試薬である硝酸銀、ジニトロジアミンパラジウム、エチレングリコール、ポリビニルピロリドン(PVP)を、所定の組成となるように秤量して混合溶液を作製した。この混合溶液に、CeZrO2(阿南化成製、Ce/Zr=2/8)を所定の組成となるように添加し、150℃×2時間、混合した。次いで、洗浄ろ過を行い、60℃×12時間乾燥後、700℃×2時間の大気焼成を行うことにより得られた触媒粉末を、参考例9とした。
<Reference Example 9>
Commercially available special grade silver nitrate, dinitrodiamine palladium, ethylene glycol, and polyvinylpyrrolidone (PVP) were weighed so as to have a predetermined composition to prepare a mixed solution. CeZrO 2 (manufactured by Anan Kasei, Ce / Zr = 2/8) was added to the mixed solution so as to have a predetermined composition, and mixed at 150 ° C. for 2 hours. Subsequently, the catalyst powder obtained by carrying out washing filtration, drying at 60 ° C. for 12 hours, and then firing in the atmosphere at 700 ° C. for 2 hours was defined as Reference Example 9.
<参考例10>
市販の特級試薬である硝酸銀、硝酸パラジウム、エタノール、ポリビニルピロリドン(PVP)を。所定の組成となるように秤量して混合溶液を作製した。この混合溶液に、CeZrO2(阿南化成製、Ce/Zr=2/8)を所定の組成となるように添加し、150℃×2時間の加熱、還流を行った。次いで、真空乾燥を行い、700℃×2時間の大気焼成を行うことにより得られた触媒粉末を、参考例10とした。
<Reference Example 10>
Silver nitrate, palladium nitrate, ethanol, and polyvinylpyrrolidone (PVP), which are commercially available special grade reagents. A mixed solution was prepared by weighing to a predetermined composition. To this mixed solution, CeZrO 2 (manufactured by Anan Kasei, Ce / Zr = 2/8) was added so as to have a predetermined composition, followed by heating and refluxing at 150 ° C. for 2 hours. Next, the catalyst powder obtained by performing vacuum drying and performing atmospheric baking at 700 ° C. for 2 hours was used as Reference Example 10.
<評価>
実施例1〜5、及び比較例1〜2について、500℃強制再生試験を実施した結果、得られたT90を表1に示す。強制再生試験では、先ず、15ccのテストパネルに各浄化触媒をコートした。浄化触媒がコートされたテストパネルをディーゼルエンジンの排気流通下にセットし、上流側には酸化触媒PtPd/Al2O3を配置させた。次いで、ディーゼルエンジンの運転を実施し、PMの捕集量が4g/LになるようにPMを捕集させた。その後、N2中で昇温させ、500℃に達したところで700ppmのNO、5%のO2、及びN2バランスガスからなるモデルガスを線速度SV=100000h−1で導入した。このような手順により、強制再生試験を実施したときのPM残存率を調べた。
なお、各触媒のD90、接触比率についても併せて記載するが、これらについては後述する。
<Evaluation>
Table 1 shows T90 obtained as a result of conducting a 500 ° C. forced regeneration test for Examples 1 to 5 and Comparative Examples 1 and 2. In the forced regeneration test, first, each purification catalyst was coated on a 15 cc test panel. A test panel coated with a purification catalyst was set under the exhaust flow of a diesel engine, and an oxidation catalyst PtPd / Al 2 O 3 was disposed upstream. Next, the diesel engine was operated to collect PM so that the amount of PM collected was 4 g / L. Thereafter, the temperature was raised in N 2 , and when the temperature reached 500 ° C., a model gas composed of 700 ppm NO, 5% O 2 , and N 2 balance gas was introduced at a linear velocity SV = 100000 h −1 . By such a procedure, the PM residual rate when the forced regeneration test was performed was examined.
In addition, although D90 of each catalyst and a contact ratio are described collectively, these are mentioned later.
[比較例1〜2]
比較例1は、現在、量産されている貴金属系触媒で構成されたCSFである。この比較例1で用いた浄化触媒は、COやHCの浄化目的で使用されるものであるが、実際にはある程度の高温下であれば多少のPMを燃焼させることができる。貴金属系のPM燃焼メカニズムは、NOから生成されたNO2とPMとの反応であるため、非接触でも燃焼が進むのが特徴である。しかしながら、表1から明らかであるように、比較例1のT90は、約30分であり、燃焼速度はかなり遅い。また、接触比率は、9%と非常に低い。
これに対し、比較例2で用いたAg系触媒は、比較例1と同様にディッピング法により担持されたものである。また、触媒調製方法も、量産と同様の方法を用いたものであるが、比較例2のT90は、約20分であり、比較例1の貴金属系触媒より燃焼速度が速くなっている。PMの捕集状態、触媒の担持方法などは比較例1と同様であることから、Ag系触媒を用いることで、PMと浄化触媒とが接触している部位の燃焼速度が速くなり、全体の燃焼速度が速くなったものと考えられた。これこそがAg系触媒の特徴であり、接触性が低い状態でも貴金属系触媒よりは十分に速い速度でPMを燃焼させることができる。しかしながら、比較例2のAg系触媒では、接触比率が低いために、触媒のポテンシャルを十分に発揮できてはいない。
[Comparative Examples 1-2]
Comparative Example 1 is a CSF composed of a noble metal catalyst currently mass-produced. The purification catalyst used in Comparative Example 1 is used for the purpose of purifying CO and HC, but in practice, some PM can be combusted at a certain high temperature. The precious metal-based PM combustion mechanism is a reaction between NO 2 generated from NO and PM, and therefore, the combustion proceeds without contact. However, as is clear from Table 1, T90 of Comparative Example 1 is about 30 minutes, and the burning rate is considerably slow. Further, the contact ratio is as low as 9%.
On the other hand, the Ag-based catalyst used in Comparative Example 2 is supported by the dipping method as in Comparative Example 1. The catalyst preparation method is also the same as that for mass production, but T90 of Comparative Example 2 is about 20 minutes, and the combustion rate is higher than that of the noble metal catalyst of Comparative Example 1. Since the PM collection state, catalyst loading method, and the like are the same as those in Comparative Example 1, the use of an Ag-based catalyst increases the combustion rate at the site where the PM and the purification catalyst are in contact with each other. It was thought that the burning rate became faster. This is the feature of Ag-based catalysts, and PM can be burned at a sufficiently higher rate than noble metal-based catalysts even in a low contact state. However, the Ag-based catalyst of Comparative Example 2 has a low contact ratio, so that the potential of the catalyst cannot be fully exhibited.
[実施例1、比較例2]
実施例1と比較例2の浄化触媒について、D50、D90、及び比表面積を測定した結果を表2に示す。測定には、HORIBA製粒度分布測定装置「LA−920」を用いた。
[Example 1, Comparative Example 2]
Table 2 shows the results of measurement of D50, D90, and specific surface area of the purification catalyst of Example 1 and Comparative Example 2. For the measurement, a particle size distribution measuring device “LA-920” manufactured by HORIBA was used.
実施例1は、比較例2の触媒粒子を、湿式粉砕にて微細化した場合に相当するが、比較例2の触媒粒子に対して、D90が9.7μmから0.6μmと大幅に微細化できていることが確認された。また、比較例2に比して実施例1の比表面積が、40m2/gから50m2/gに増大していることも確認された。
ここで、実施例1と比較例2のCSFについて、SEM観察を実施し、表面状態の比較検討も併せて行った。比較例2のSEM像は、既に図11に示した通りである。この図11から明らかであるように、比較例2のCSF表面に大きな触媒粒子が確認できる。これに対して、図13が実施例1のCSF表面のSEM像であり、図14が実施例1のDPF細孔内のSEM像である。図13のCSF表面のSEM像から、実施例1では、触媒粒子が小さいうえ、DPFの表面が露出している部分があることが判った。また、図14のDPF細孔内のSEM像から、実施例1では、DPF細孔内に触媒粒子が多く担持されていることが判った。これらの結果から、実施例1では、触媒粒子が小さすぎるために、その多くがDPF細孔内に担持されているものと考えられた。
また、実施例1と比較例2のT90については、表1に示した通りであり、両者の燃焼速度はほぼ同等であるものの、接触比率については、実施例1の方が比較例2に比して良好であることが判った。即ち、DPF細孔内など微細な触媒粒子が数多く存在する部分では、微細化効果によって触媒とPMとの接触比率が向上するものと考えられた。ただし、ルーズコンタクト燃焼領域では、良好な接触性が保たれず、燃焼速度が悪化することから、微細な触媒粒子をDPF表面に均一に担持させる必要があると考えられた。
Example 1 corresponds to the case where the catalyst particles of Comparative Example 2 were refined by wet pulverization, but D90 was significantly refined from 9.7 μm to 0.6 μm with respect to the catalyst particles of Comparative Example 2. It was confirmed that it was made. The specific surface area of Example 1 than in Comparative Example 2, it was confirmed that has increased from 40 m 2 / g to 50 m 2 / g.
Here, SEM observation was implemented about the CSF of Example 1 and Comparative Example 2, and the comparative examination of the surface state was also performed. The SEM image of Comparative Example 2 is as shown in FIG. As is clear from FIG. 11, large catalyst particles can be confirmed on the CSF surface of Comparative Example 2. On the other hand, FIG. 13 is an SEM image of the CSF surface of Example 1, and FIG. 14 is an SEM image inside the DPF pores of Example 1. From the SEM image of the CSF surface in FIG. 13, it was found that in Example 1, there was a portion where the catalyst particles were small and the surface of the DPF was exposed. Further, from the SEM image in the DPF pores of FIG. 14, it was found that in Example 1, many catalyst particles were supported in the DPF pores. From these results, in Example 1, since the catalyst particles were too small, it was considered that most of them were supported in the DPF pores.
Further, T90 of Example 1 and Comparative Example 2 is as shown in Table 1, and although the burning speeds of both are almost equal, the contact ratio of Example 1 is comparable to that of Comparative Example 2. And found to be good. That is, it was considered that the contact ratio between the catalyst and PM was improved by the refinement effect in a portion where there are many fine catalyst particles such as in the DPF pores. However, in the loose contact combustion region, good contactability is not maintained, and the combustion speed is deteriorated. Therefore, it was considered necessary to uniformly support fine catalyst particles on the DPF surface.
[実施例2、比較例2]
実施例2は、比較例2の触媒材料を変えずに、ディッピング法ではなく発泡法を用いて触媒を担持させたCSFである。図15は、実施例2と比較例2のCSF表面に存在する空隙の大きさを、島津製作所製水銀ポロシメータ「ポアサイザ9320」を用いて測定した結果を示す図である。図15に示すように、実施例2のCSF表面には、比較例2には見られない3μm〜10μmの空隙が存在することが判った。これは、有機酸の発泡効果によるものと考えられた。また、比較例2のCSF表面には、0.6μm〜0.8μm程度の空隙のピークが存在するのに対して、実施例2のCSF表面では、空隙のピークが4μm〜8μmにシフトしていることが判った。
また、実施例2のCSFについて、SEM観察を実施し、表面状態の評価も併せて行った。図16は、実施例2のCSF表面のSEM像である。図16から明らかであるように、発泡法により触媒が分散して、全体的に均一に触媒が担持されていることが確認された。このように、全体的に均一に触媒が担持された実施例2のCSFでは、表1に示すように、接触比率が28%と比較例2に比して高く、T90も16分に短時間化されており、比較例2に比してPM燃焼性能が向上していることが確認された。
[Example 2, Comparative Example 2]
Example 2 is a CSF in which the catalyst is supported using the foaming method instead of the dipping method without changing the catalyst material of Comparative Example 2. FIG. 15 is a diagram showing the results of measuring the size of the voids existing on the CSF surfaces of Example 2 and Comparative Example 2 using a mercury porosimeter “Pore Sizer 9320” manufactured by Shimadzu Corporation. As shown in FIG. 15, it was found that 3 μm to 10 μm voids not found in Comparative Example 2 exist on the CSF surface of Example 2. This was thought to be due to the foaming effect of the organic acid. Moreover, on the CSF surface of Comparative Example 2, there is a void peak of about 0.6 μm to 0.8 μm, whereas on the CSF surface of Example 2, the void peak is shifted to 4 μm to 8 μm. I found out.
Moreover, about the CSF of Example 2, SEM observation was implemented and surface state evaluation was also performed collectively. FIG. 16 is an SEM image of the CSF surface of Example 2. As is clear from FIG. 16, it was confirmed that the catalyst was dispersed by the foaming method, and the catalyst was supported uniformly throughout. Thus, as shown in Table 1, the CSF of Example 2 in which the catalyst is uniformly supported as a whole has a contact ratio of 28%, which is higher than that of Comparative Example 2, and T90 is also short in 16 minutes. It was confirmed that the PM combustion performance was improved as compared with Comparative Example 2.
[実施例3]
上述したように、実施例1と実施例2それぞれの接触比率は、比較例2に比して優れていることが判ったが、実施例3は、これら実施例1と実施例2の組合せ、即ち発泡法と触媒の微細化とを組み合わせたものである。この実施例3のCSFについて、SEM観察を実施し、表面状態の評価を行った。図17は、実施例3のCSF表面のSEM像である。また、図18は、図17の部分拡大図である。図17に示すように、実施例3のCSFでは、DPF細孔を塞ぐことなく、DPFの表面全体が触媒により均一に被覆されていることが判った。また、図18の部分拡大図から、微細な触媒粒子が密集して担持されていることが判った。
このように、発泡法と触媒の微細化との組合せにより、微細な触媒粒子をDPFの表面全体に均一に担持できる実施例3のCSFでは、表1に示すように接触比率が36%であり、実施例1や実施例2に比して接触性が向上していることが判った。また、接触性の向上により、T90が14分に時間化され、PMがより効率良く燃焼できていることが確認された。
[Example 3]
As described above, it was found that the contact ratio of each of Example 1 and Example 2 was superior to that of Comparative Example 2, but Example 3 is a combination of Example 1 and Example 2, In other words, this is a combination of the foaming method and catalyst refinement. About CSF of this Example 3, SEM observation was implemented and the surface state was evaluated. FIG. 17 is an SEM image of the CSF surface of Example 3. FIG. 18 is a partially enlarged view of FIG. As shown in FIG. 17, in the CSF of Example 3, it was found that the entire surface of the DPF was uniformly coated with the catalyst without blocking the DPF pores. Further, from the partially enlarged view of FIG. 18, it was found that fine catalyst particles are densely supported.
Thus, in the CSF of Example 3 that can uniformly support fine catalyst particles on the entire surface of the DPF by a combination of the foaming method and the refinement of the catalyst, the contact ratio is 36% as shown in Table 1. It was found that the contactability was improved as compared with Example 1 and Example 2. In addition, it was confirmed that T90 was timed to 14 minutes due to the improved contactability, and PM was combusted more efficiently.
[実施例4]
実施例4は、実施例3にNO2生成触媒をさらに含有させたものであり、発泡法及び触媒の微細化による接触性の向上に、NO2生成触媒を組み合わせたものである。表1に示したように、実施例4のCSFの接触比率は52%であり、実施例3に比して接触性がさらに向上していることが判った。接触比率が52%であるということは、再生開始後30秒の間に、堆積したPMの52%が燃焼除去されることを意味しており、PMが非常に効率良く燃焼除去されていることが判る。また、T90がさらに12分に短時間化されていることも確認された。
[Example 4]
In Example 4, the NO 2 production catalyst is further added to Example 3, and the NO 2 production catalyst is combined with the improvement of the contact property by the foaming method and the refinement of the catalyst. As shown in Table 1, the contact ratio of the CSF of Example 4 was 52%, and it was found that the contactability was further improved as compared with Example 3. The contact ratio of 52% means that 52% of the accumulated PM is burned and removed within 30 seconds after the start of regeneration, and PM is burned and removed very efficiently. I understand. It was also confirmed that T90 was further shortened to 12 minutes.
[実施例5]
実施例5は、実施例4のAg系触媒の調製方法をアミン還元法に変更したものである。このアミン還元法を用いて調製した実施例5と、含浸法を用いて調製した比較例2について、Ag結晶子径の測定を実施した。結果を表3に示す。なお、Ag結晶子径の測定には、リガク製X線回折装置「XRD−RINT III」を用いた。
[Example 5]
In Example 5, the method for preparing the Ag-based catalyst in Example 4 is changed to an amine reduction method. Ag crystallite diameter was measured for Example 5 prepared using this amine reduction method and Comparative Example 2 prepared using the impregnation method. The results are shown in Table 3. For the measurement of the Ag crystallite diameter, a Rigaku X-ray diffraction apparatus “XRD-RINT III” was used.
表3に示すように、比較例2のAg結晶子径は42nmであったのに対して、実施例5のAg結晶子径は34nmであり、比較例2に比して活性種Agが微細化されていることが判った。
また、表1に示したように、実施例5の接触比率は56%で非常に良好な接触性が得られたのは、活性種Agの微細化によりPMの接触性が向上したためであると考えられた。また、接触性が良好であるため、T90はさらに11.2分に短時間化されており、PMが非常に効率良く燃焼できていることが確認された。
As shown in Table 3, the Ag crystallite diameter of Comparative Example 2 was 42 nm, whereas the Ag crystallite diameter of Example 5 was 34 nm, and the active species Ag was finer than that of Comparative Example 2. It was found that
In addition, as shown in Table 1, the contact ratio of Example 5 was 56%, and very good contactability was obtained because the contactability of PM was improved by the refinement of active species Ag. it was thought. Further, since the contactability is good, T90 is further shortened to 11.2 minutes, and it was confirmed that PM can be burned very efficiently.
[参考例1〜6]
参考例1〜6について、D90と酸素脱離開始温度の測定を行った結果を表4に示す。また、これらの測定結果を元に、D90と酸素脱離開始温度との関係を図19に示した。なお、D90の測定には、HORIBA製粒度分布測定装置「LA−920」を用い、酸素脱離開始温度の測定には昇温脱離装置(O2−TPD)を用いた。
[Reference Examples 1 to 6]
Table 4 shows the results of measuring D90 and the oxygen desorption start temperature for Reference Examples 1 to 6. Further, based on these measurement results, the relationship between D90 and the oxygen desorption start temperature is shown in FIG. Incidentally, the measurement of the D90, using a HORIBA Ltd. particle size distribution measuring apparatus "LA-920", for the measurement of oxygen desorption start temperature using the thermal desorption unit (O 2 -TPD).
図19において、D90は、小さいほど接触性が向上することを意味し、酸素脱離開始温度は、低温であるほどPM燃焼性能が優れていることを意味する。
表4に示すように、参考例2の酸素脱離開始温度は、参考例1に比して高温化していた。これは、湿式粉砕時のエネルギが強力であるために、活性種Agの剥離や触媒粒子表面への物理的打撃による活性の低下によるものと考えられた。従って、中程度の微細化は好ましくないことが判った。
また、参考例3及び参考例4の酸素脱離開始温度は、参考例1とほぼ同等であった。これは、参考例3及び参考例4は、参考例2をさらに微細化したものに相当するところ、上述の参考例2と同様の現象が生じるものの、さらなる微細化でD90を0.6μm以下にした場合にあっては、触媒表面積の増大によってPM燃焼性能が向上したためであると考えられた。
また、参考例5及び参考例6の酸素脱離開始温度は、参考例1に比して低温化していた。これは、参考例5及び参考例6では、微細化エネルギが弱いため微細化の程度は小さく、参考例3や参考例4に比して触媒粒子の大きさは大きいものの、Ag剥離や表面活性の低下が起こらない結果、触媒表面積の増大によってPM燃焼性能が向上したためであると考えられた。
以上の結果から、D90が2μm以下であれば、接触性を向上させつつ、優れたPM燃焼性能が得られることが確認された。
In FIG. 19, D90 means that the smaller the contact, the better the contactability, and the lower the oxygen desorption start temperature, the better the PM combustion performance.
As shown in Table 4, the oxygen desorption start temperature of Reference Example 2 was higher than that of Reference Example 1. This was thought to be due to the decrease in activity due to the separation of the active species Ag and physical impact on the catalyst particle surface due to the strong energy during wet pulverization. Therefore, it has been found that moderate refinement is not preferable.
In addition, the oxygen desorption start temperatures of Reference Example 3 and Reference Example 4 were almost the same as those of Reference Example 1. This corresponds to Reference Example 3 and Reference Example 4 which are obtained by further miniaturizing Reference Example 2, and although the same phenomenon as Reference Example 2 described above occurs, D90 is reduced to 0.6 μm or less by further miniaturization. In this case, it was considered that the PM combustion performance was improved by increasing the catalyst surface area.
In addition, the oxygen desorption start temperature in Reference Example 5 and Reference Example 6 was lower than that in Reference Example 1. This is because in Reference Example 5 and Reference Example 6, the degree of miniaturization is small because the energy for miniaturization is weak, and although the size of the catalyst particles is larger than those in Reference Example 3 and Reference Example 4, Ag delamination and surface activity. As a result, the PM combustion performance was considered to be improved by increasing the catalyst surface area.
From the above results, it was confirmed that when PM90 is 2 μm or less, excellent PM combustion performance can be obtained while improving contactability.
[実施例3〜4、比較例2]
実施例3〜4と比較例2のCSFについて、DPF表面における浄化触媒の被覆率の測定を実施した。結果を表5に示す。なお、DPF表面における浄化触媒の被覆率は、SEM観察により得られたSEM画像において、コントラストを強調させて白色部分(浄化触媒に相当)と黒色部分(DPFに相当)に分けた後、白色部分と黒色部分の面積を算出し、算出した面積値から求めた。
[Examples 3 to 4, Comparative Example 2]
For the CSFs of Examples 3 to 4 and Comparative Example 2, the coverage of the purification catalyst on the DPF surface was measured. The results are shown in Table 5. Note that the coverage of the purification catalyst on the DPF surface is determined by dividing the white portion (corresponding to the purification catalyst) and the black portion (corresponding to the DPF) by enhancing the contrast in the SEM image obtained by SEM observation. And the area of the black part was calculated and obtained from the calculated area value.
表5に示すように、ディッピング法により浄化触媒を担持させた比較例2では、被覆率は29%と低かった。これに対して、実施例3及び実施例4では、発泡法と触媒の微細化との組合せにより、被覆率はそれぞれ73%及び86%と大幅に向上していた。これらの結果と上記表1の結果とから、被覆率が高いほど接触比率が高く、PM燃焼性能が高いことが判った。従って、DPF表面における浄化触媒の被覆率が30%以上であることが好ましく、70%以上であることがさらに好ましいことが確認された。 As shown in Table 5, in Comparative Example 2 in which the purification catalyst was supported by the dipping method, the coverage was as low as 29%. On the other hand, in Example 3 and Example 4, the coverage was significantly improved to 73% and 86%, respectively, by the combination of the foaming method and catalyst refinement. From these results and the results shown in Table 1, it was found that the higher the coverage, the higher the contact ratio and the higher the PM combustion performance. Therefore, it was confirmed that the coverage of the purification catalyst on the DPF surface is preferably 30% or more, and more preferably 70% or more.
[参考例7〜10]
浄化触媒の調製方法として、含浸法を用いた参考例7、アミン還元法を用いた参考例8、アルコール還元法を用いた参考例9及び参考例10について、Ag結晶子径とPM燃焼ピーク温度の測定を実施した。結果を表6に示す。なお、Ag結晶子径の測定には、リガク製X線回折装置「XRD−RINT III」を用いた。また、PM燃焼ピーク温度の測定にはTG−DTA測定装置を用いた。
[Reference Examples 7 to 10]
As the preparation method of the purification catalyst, the Ag crystallite diameter and PM combustion peak temperature were obtained for Reference Example 7 using the impregnation method, Reference Example 8 using the amine reduction method, Reference Example 9 and Reference Example 10 using the alcohol reduction method. The measurement of was carried out. The results are shown in Table 6. For the measurement of the Ag crystallite diameter, a Rigaku X-ray diffraction apparatus “XRD-RINT III” was used. Moreover, the TG-DTA measuring apparatus was used for the measurement of PM combustion peak temperature.
表6に示すように、参考例8〜10はいずれも、参考例7に比してAg結晶子径が小さく、それに伴ってPM燃焼ピーク温度も低温化していた。これは、活性種Agの結晶子径が小さいことにより、PMと触媒との接触性が向上し、PM燃焼性能が向上するためであると考えられた。
この結果から、Ag結晶子径は42nmより小さいことが好ましいことが確認された。また、浄化触媒の調製方法としては、含浸法よりも還元法が好ましいことが確認された。さらには、還元法で用いる還元剤としては、トリエチルアミンやエチレングリコール、エタノールを好ましく用いることができることが確認された。
As shown in Table 6, in each of Reference Examples 8 to 10, the Ag crystallite diameter was smaller than that in Reference Example 7, and the PM combustion peak temperature was also lowered accordingly. This is considered to be because the contact property between PM and the catalyst is improved and the PM combustion performance is improved due to the small crystallite size of the active species Ag.
From this result, it was confirmed that the Ag crystallite diameter is preferably smaller than 42 nm. Further, it was confirmed that the reduction method is preferable to the impregnation method as a method for preparing the purification catalyst. Furthermore, it was confirmed that triethylamine, ethylene glycol, and ethanol can be preferably used as the reducing agent used in the reduction method.
1…DPF
2…排気流入路
3…排気流出路
4…目封止材
5…隔壁
6…細孔
7…浄化触媒層
1 ... DPF
2 ... Exhaust inflow path 3 ... Exhaust outflow path 4 ... Plugging material 5 ... Partition wall 6 ... Fine pore 7 ... Purification catalyst layer
Claims (10)
前記浄化触媒層中の触媒粒子の粒度分布における小粒径側からの累積分布が90%となるときの粒子径D90が2μm以下であり、
前記浄化触媒層は、孔径が3μm〜10μmの空隙を有し且つ水銀ポロシメータにより測定された孔径分布において4μm〜8μmのピークを有することを特徴とする内燃機関の排気浄化装置。 Provided in an exhaust passage of the internal combustion engine is provided with a filter having on its surface a purification catalyst layer constituted by a purification catalyst for capturing particulate matter in the exhaust of the internal combustion engine and purifying the captured particulate matter. In an internal combustion engine exhaust gas purification device,
Ri Der particle diameter D90 of 2μm or less when the cumulative distribution is 90% from the smaller particle size side in the particle size distribution of the catalyst particles of the purifying catalyst layer,
The exhaust purification device of an internal combustion engine, wherein the purification catalyst layer has a void having a pore diameter of 3 μm to 10 μm and has a peak of 4 μm to 8 μm in a pore diameter distribution measured by a mercury porosimeter .
前記複合酸化物は、アルカリ土類金属元素、遷移金属元素、第12族元素、及び第13族元素からなる群より選択される少なくとも2種以上を構成元素として含むことにより、構成元素の価数を変化させて酸素の吸収及び放出を行うことを特徴とする請求項3又は4記載の内燃機関の排気浄化装置。 The Ag is supported on a complex oxide having oxygen releasing ability,
The composite oxide includes at least two or more selected from the group consisting of alkaline earth metal elements, transition metal elements, Group 12 elements, and Group 13 elements as constituent elements. The exhaust gas purification apparatus for an internal combustion engine according to claim 3 or 4, wherein oxygen is absorbed and released by changing the pressure.