JP5401350B2 - 無機系部材からなる基材の表面のメンテナンス方法 - Google Patents
無機系部材からなる基材の表面のメンテナンス方法 Download PDFInfo
- Publication number
- JP5401350B2 JP5401350B2 JP2010019960A JP2010019960A JP5401350B2 JP 5401350 B2 JP5401350 B2 JP 5401350B2 JP 2010019960 A JP2010019960 A JP 2010019960A JP 2010019960 A JP2010019960 A JP 2010019960A JP 5401350 B2 JP5401350 B2 JP 5401350B2
- Authority
- JP
- Japan
- Prior art keywords
- protective coating
- base material
- silane coupling
- coating agent
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(a)アクリル系共重合物のエマルジョン
(b)水性ウレタン系樹脂
そして、この保護用コーティング剤の塗布にあっては、先ず、基材の表面にプライマーとして有機官能基がエポキシ基であるシランカップリング剤を塗布し、その後に保護用コーティング剤を塗布するので、水系である保護用コーティング剤がシランカップリング剤の塗膜を介して基材の表面に密着し、汚れが付着した保護用コーティング剤の塗膜を水拭きしても剥がれることなく、保護用コーティング剤の塗膜から汚れを落とすことができる。
また、形成された保護用コーティング剤の塗膜は、傷等により補修の必要性が生じた際にはアルカリ性洗剤で容易に除去することができる。
本例は、先ず、基材の表面にプライマーとして有機官能基がエポキシ基であるシランカップリング剤を塗布する。
シランカップリング剤は、一つの分子中に有機物との反応や相互作用が期待できる有機官能基「Y」と加水分解性基「−OR]の両者を併せ持つ有機化合物である。
本発明で使用するシランカップリング剤としては極性を有する水、エチルアルコール等の溶媒に溶解できるものを選択する。
ここで使用するシランとして、3−グリシドキシプロピルトリメトキシシラン、3−グリシドキシプロピルトリエトキシシラン、3−グリシドキシプロピルメチルジメトキシシラン、3−グリシドキシプロピルメチルジエトキシシラン、2−(3,4−エポキシシクロヘキシル)エチルトリメトキシシランのいずれか1つが使用されるが、特に好ましいのは、3−グリシドキシプロピルトリメトキシシラン、3−グリシドキシプロピルトリエトキシシランである。
かかるシランをエチルアルコールで希釈してプライマーとし、これを基材表面に塗布する。シランをエチルアルコールで希釈したシランカップリング剤の濃度は、2%〜10%が好ましく、2%〜5%が特に好ましい。
(a)アクリル系共重合物のエマルジョン
(b)水性ウレタン系樹脂
アクリル系共重合物のエマルジョンや水性ウレタン系樹脂の屈折率[n]は、1.48〜1.50であり、指紋成分の屈折率[n](1.46〜1.52程度)とほぼ同程度である。
前記ワックスエマルジョンとしては、植物系のキャンデリラワックス、カルナバワックス、ライスワックス、木ロウなど、動物系の蜜ロウ、ラノリン、鯨ロウなど、鉱物系のモンタンワックス、オゾケライト、セレシンなど、石油系のパラフィンワックス、マイクロクリスタリンワックス、ペトロラタムなど、合成炭化水素系のフィッシャートロプシュワックス、酸化ポリエチレンワックス、ポリエチレンワックス、アクリル−エチレン共重合体ワックスなど、変性ワックス系のモンタンワックス誘導体、パラフィンワックス誘導体、マイクロクリスタリンワックス誘導体、水素添加ヒマシ油などのワックスを乳化分散したものが利用できる。
アルカリ可溶性樹脂としては、スチレン−無水マレイン酸共重合樹脂や、フェノール系樹脂、アルキッド樹脂、アクリル系樹脂などがあるが、スチレン−無水マレイン酸共重合樹脂がより好ましい。
造膜助剤としては、エチルカルビトール、メチルカルビトール、ブチルカルビトール等、可塑剤としては、ジブチルフタレート、トリブトキシエチルフォスフェート等がある。
表2は水系である保護用コーティング剤の実施例1〜5を示し、表3は水系である保護用コーティング剤の実施例6〜8を示す。
表注の数字は重量%を示す。
濡れ剤: セイミケミカル社製 サーフロンS−111N
消泡剤: ワッカーシリコーン社製 SE−21
造膜助剤: 日本触媒社製 シーホゾールDG
可塑剤: 大八化学社製 TBXP
アクリル系共重合物エマルジョン(1):
ローム&ハース社製 プライマルNT−6035、固形分;38%
アクリル系共重合物エマルジョン(2):
ローム&ハース社製 プライマルB−924、固形分;38%
アクリル系共重合物エマルジョン(3):
ローム&ハース社製 プライマルB−505、固形分;40%
水性ウレタン系樹脂(1):
DSMネオレジン社製 ネオレッツR−9603、固形分;34%
水性ウレタン系樹脂(2):
DSMネオレジン社製 ネオレッツR−970、固形分;39%
ポリエチレンワックスエマルジョン(1):
東邦化学工業社製 ハイテックE−4000、固形分;40%
ポリエチレンワックスエマルジョン(2):
表4で示す配合で調製した。
(1)シランカップリング剤と保護用コーティング剤との密着性試験
表1の実施例1,2に示す組成を有するシランカップリング剤を調製し、このシランカップリング剤をステンレスに均一に塗布し、アルコールが揮発する短時間を待って、表1,2に示す保護用コーティング剤を重ね塗りした。
塗布後、15時間経過後に水拭きを行い密着性試験をしたところ、実施例1,2のいずれにも保護用コーティング剤の剥離は認められなかった。
(2)保護用コーティング剤の乾燥塗膜の乾燥光沢試験
シランカップリング剤の塗膜に重ね塗りをした保護用コーティング剤の乾燥塗膜の状態を目視で観察したところ、ステンレスの未塗布状態と比較して、同等或いは同等に近い光沢であった。
(3)保護用コーティング剤の乾燥塗膜の指紋付着性試験
保護用コーティング剤の乾燥塗膜上に人の指を押しつけた後、その目立ち易さを目視で観察したところ、ステンレスの未塗布状態と比較して、明らかに目立たなかった。
(4)保護用コーティング剤の指紋の拭き取り易さ試験
保護用コーティング剤の乾燥塗膜に指紋を付け、乾いた綿の布を使用して指紋上を拭いて、指紋の除去性を調べたところ、ステンレスと比較して遙かにふき取りやすく、1回或いは数回の拭き上げで容易に除去できた。
(5)保護用コーティング剤の乾燥塗膜の除去性試験
アルカリ性洗剤(リンレイ「ギガパワープロ」)を希釈した洗浄液(10倍)で表面を濡らし、綿ガーゼで軽く表面を擦り塗膜の除去性を調べたところ、容易に除去できる。
Claims (2)
- 物体の内外装に備えられた無機系部材からなる基材の表面のメンテナンス方法であって、先ず、基材の表面にプライマーとして有機官能基がエポキシ基であるシランカップリング剤を塗布し、その後、有効成分として、下記(a)、(b)を含有し、全固形分中の(a)+(b)の重量%が、100重量%以下40重量%以上で、(a)と(b)の混合比率が、(a)が0%〜100%、(b)が0%〜100%である保護用コーティング剤を塗布することを特徴とする無機系部材からなる基材の表面のメンテナンス方法。
(a)アクリル系共重合物のエマルジョン
(b)水性ウレタン系樹脂 - 前記シランカップリング剤は、3−グリシドキシプロピルトリメトキシシラン、3−グリシドキシプロピルトリエトキシシラン、3−グリシドキシプロピルメチルジメトキシシラン、3−グリシドキシプロピルメチルジエトキシシラン、2−(3,4−エポキシシクロヘキシル)エチルトリメトキシシランのいずれか1つであることを特徴とする請求項1に記載の無機系部材からなる基材の表面のメンテナンス方法。