JP5376391B2 - Dissimilar metal joining method and joining structure - Google Patents
Dissimilar metal joining method and joining structure Download PDFInfo
- Publication number
- JP5376391B2 JP5376391B2 JP2007307345A JP2007307345A JP5376391B2 JP 5376391 B2 JP5376391 B2 JP 5376391B2 JP 2007307345 A JP2007307345 A JP 2007307345A JP 2007307345 A JP2007307345 A JP 2007307345A JP 5376391 B2 JP5376391 B2 JP 5376391B2
- Authority
- JP
- Japan
- Prior art keywords
- interface
- dissimilar
- metal
- joining
- nugget
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、例えば鋼材とアルミニウム合金材など、異種金属材料の抵抗溶接による接合技術に係わり、特に異種金属から成る被接合材を少なくとも3枚重ねて成り、異種材界面と同種材界面とが混在する場合に適用される異種金属の接合方法と、このような方法によって得られる接合構造に関するものである。 The present invention relates to a joining technique by resistance welding of dissimilar metal materials such as steel and aluminum alloy materials, and in particular, is formed by stacking at least three to-be-joined materials made of dissimilar metals, and a heterogeneous material interface and a homogeneous material interface are mixed. The present invention relates to a joining method of dissimilar metals applied in this case, and a joining structure obtained by such a method.
異種金属を接合する場合、同種材同士の溶接の場合と同様に両方の被接合材を溶融させてしまうと、脆弱な金属間化合物が形成され、十分な継手強度が得られないことがある。
例えば、アルミニウム合金と鋼材とを溶接する場合、高硬度で脆弱なFe2Al5やFeAl3などの金属間化合物が形成されるため、継手強度を確保するためには、これら金属間化合物の制御が必要となる。
When joining dissimilar metals, if both materials to be joined are melted in the same manner as in the case of welding the same kind of materials, a brittle intermetallic compound may be formed, and sufficient joint strength may not be obtained.
For example, when an aluminum alloy and a steel material are welded, intermetallic compounds such as Fe 2 Al 5 and FeAl 3 that are brittle and hard are formed. Therefore, in order to ensure joint strength, control of these intermetallic compounds is required. Is required.
しかし、アルミニウム合金表面には、緻密で強固な酸化皮膜が形成されており、それを除去するためには接合時に大きな熱量を投与することが必要となる結果、厚い金属間化合物層が成長し、接合部の強度が低くなってしまうという問題があった。 However, a dense and strong oxide film is formed on the aluminum alloy surface, and in order to remove it, it is necessary to administer a large amount of heat at the time of bonding. As a result, a thick intermetallic compound layer grows, There was a problem that the strength of the joint portion was lowered.
そこで、従来では、このような異種金属材料を組合わせて使用する場合には、ボルトやリベットなどによる機械的締結によってこれら材料を接合するようにしていたが、この場合には重量やコストが増加する点に問題があった。 Therefore, in the past, when such dissimilar metal materials were used in combination, these materials were joined by mechanical fastening with bolts or rivets, but in this case the weight and cost increased. There was a problem with that.
また、このような異種金属の接合には、摩擦圧接が一部の部品において実用化されているが、このような摩擦圧接方法は対称性のよい回転体同士の接合など、その用途が限られている。
さらに、爆着や熱間圧延などによる接合も知られているが、設備面や能率面での問題が多く、一般の異種金属接合に広く適用することはできないという問題がある。
In addition, friction welding is practically used in some parts for joining dissimilar metals, but such a friction welding method has limited applications such as joining of rotating bodies with good symmetry. ing.
Furthermore, although joining by explosive bonding or hot rolling is also known, there are many problems in terms of equipment and efficiency, and there is a problem that it cannot be widely applied to general dissimilar metal joining.
このような異種金属接合の改善例として、接合しようとする異種金属材料の間に、これら異種金属と同じ2種の材料から成るクラッド材をそれぞれ同種材同士が接するように介在させた状態で、10ms以下の通電時間で抵抗溶接を行うようにする方法が提案されている(特許文献1参照)。 As an improvement example of such dissimilar metal bonding, between the dissimilar metal materials to be bonded, clad materials made of the same two kinds of materials as these dissimilar metals are interposed so that the same kind of materials are in contact with each other, A method of performing resistance welding with an energization time of 10 ms or less has been proposed (see Patent Document 1).
また、アルミニウムと鋼の抵抗溶接において、アルミニウム材と接する鋼表面に、Al含有量が20wt%以上のアルミニウム合金又は純アルミニウムを2μm以上の厚さとなるようにめっきし、該めっき面をアルミニウム材に重ねて通電し、めっき層を優先的に溶融させ、鋼材側をほとんど溶融させないようにして、これら材料を接合する方法が開示されている(特許文献2参照)。
しかしながら、特許文献1に記載の、クラッド材を用いる方法の場合、2枚の板を接合すべきところが3枚の接合ということになってしまう。実際の施工を考えた場合には、クラッド材の挿入と共に、これらを固定する工程が必要となって、現状の溶接ラインに新たな設備を組み入れなければならなくなり、コストアップの要因となる。また、例えばアルミニウムと鋼を接合する場合、アルミニウムクラッド鋼自体も異種材同士を接合することにより製造されるため、製造条件が厳しく、安価で性能の安定したクラッド材を入手することが困難であるという問題がある。 However, in the case of the method using the clad material described in Patent Document 1, the place where the two plates should be joined is the joining of the three sheets. When considering actual construction, it is necessary to insert a clad material and a process for fixing the clad material, and it is necessary to incorporate new equipment into the current welding line, which causes an increase in cost. For example, when aluminum and steel are joined, aluminum clad steel itself is also produced by joining dissimilar materials to each other, so that it is difficult to obtain a clad material with strict production conditions, inexpensive and stable performance. There is a problem.
一方、特許文献2に記載の、鋼表面にアルミニウムめっきを施した状態で抵抗溶接する方法においては、アルミニウムめっき面とアルミニウム材を接合する際、表面の強固な酸化皮膜を破壊するために大きな熱を投入することが必要となって、アルミニウムめっきと鋼の界面に脆い金属間化合物が形成され、これから破壊が生じる可能性があるという問題がある。
On the other hand, in the method of resistance welding in a state where the steel surface is subjected to aluminum plating described in
また、3枚以上の異種材を抵抗溶接する場合には、接合すべき界面として、異種材界面と、同種材界面が共存することがある。特に異種材界面における抵抗発熱が同種材界面より小さくなるような場合には、その抵抗発熱差により同種材界面にナゲットが優先的に形成され、異種材界面にはナゲットが形成されにくくなる。この場合、それぞれの界面について十分な接合強度を得るためには、ナゲットが形成されにくい異種材界面側が所望のナゲット径となるような熱を投入する必要がある。しかし、同種材界面を形成する金属材料の融点よりも、同種材界面を形成しない金属材料(異種材界面においてのみ形成される金属材料)の融点が低いような組合せの重ね接合においては、同種材界面の接合強度が十分となる程度の低い入熱量では、異種材界面で接合強度が十分となる程度のナゲットが形成されにくい。一方、異種材界面の接合強度が十分となる程度の高い入熱量では、同種材界面における抵抗発熱が過多となることで、該抵抗発熱により低融点側材料、上記したアルミニウムと鋼の接合例ではアルミニウム材の側に著しい減肉が生じるという問題がある。 When three or more dissimilar materials are resistance-welded, the dissimilar material interface and the same material interface may coexist as interfaces to be joined. In particular, when resistance heat generation at the interface between different materials is smaller than that at the same material interface, nuggets are preferentially formed at the same material interface due to the difference in resistance heat generation, and nuggets are less likely to be formed at the different material interfaces. In this case, in order to obtain a sufficient bonding strength for each interface, it is necessary to input heat so that the interface between the different materials where the nugget is difficult to be formed has a desired nugget diameter. However, the same kind of material is used in a lap joint where the melting point of the metal material that does not form the homogeneous material interface (the metal material formed only at the different material interface) is lower than the melting point of the metallic material that forms the homogeneous material interface. When the heat input is so low that the bonding strength at the interface is sufficient, it is difficult to form a nugget with sufficient bonding strength at the dissimilar material interface. On the other hand, when the heat input is high enough that the bonding strength of the dissimilar material interface is sufficient, the resistance heat generation at the interface of the same material becomes excessive. There is a problem that significant thinning occurs on the aluminum material side.
本発明は、従来の異種金属の接合における上記課題に鑑みてなされたものであって、その目的とするところは、抵抗溶接によって異種金属から成る3枚以上の被接合材を重ね接合するに際して、異種材界面と同種材界面が混在すると共に、両界面の接触抵抗の相違によって、異種材界面での抵抗発熱が同種材界面の抵抗発熱よりも小さくなるような被接合材の組合せであっても、低融点側材料の減肉を抑制しつつ、各界面に所望のナゲット径をそれぞれ形成することができ、各界面における接合強度をそれぞれ十分に確保することができる接合方法と、このような接合方法によって得られる接合構造を提供することにある。 The present invention has been made in view of the above-described problems in the joining of conventional dissimilar metals, and the purpose thereof is to lap-join three or more materials to be joined made of dissimilar metals by resistance welding. Even when the dissimilar material interface and the same material interface coexist, and due to the difference in contact resistance between both interfaces, the resistance heat generation at the dissimilar material interface is smaller than the resistance heat generation at the same material interface, A bonding method capable of forming a desired nugget diameter at each interface while suppressing thinning of the low melting point side material, and ensuring sufficient bonding strength at each interface, and such bonding It is to provide a joint structure obtained by the method.
本発明者らは、上記目的の達成に向けて、被接合材料の組合せや通電条件などについて鋭意検討を重ねた結果、小電流の通電によって同種材界面に優先的にナゲットを形成して、同種材界面の抵抗を減じた上で、大電流を通電して異種材界面にナゲットを形成するようになすことによって、上記課題が解決できることを見出し、本発明を完成するに到った。 As a result of intensive investigations on the combination of materials to be joined and energization conditions in order to achieve the above object, the present inventors preferentially formed nuggets at the same kind material interface by energizing a small current, The present inventors have found that the above problems can be solved by reducing the resistance at the material interface and forming a nugget at the interface between different materials by supplying a large current to the present invention.
本発明は上記知見に基づくものであって、本発明の異種金属の接合方法においては、第1の金属材料から成る少なくとも2枚の板材と、第1の金属材料よりも低い融点を有する第2の金属材料から成る少なくとも1枚の板材を重ね合わせた異種金属材料の重ね継手であって、異種材界面と同種材界面を有し、異種材界面における接触抵抗が同種材界面における接触抵抗よりも小さい重ね継手を抵抗溶接により形成するに際して、重ね合わせた少なくとも3枚の板材の間に、第1の電流を通電して同種材界面におけるナゲットを優先的に形成させた後、第1の電流よりも大きい第2の電流を通電して異種材界面にナゲットを形成して接合することを特徴としている。 The present invention is based on the above knowledge, and in the dissimilar metal joining method of the present invention, at least two plate members made of the first metal material and a second melting point lower than that of the first metal material. A lap joint of dissimilar metal materials in which at least one plate material made of the above metal material is overlapped, and has a dissimilar material interface and a homogeneous material interface, and the contact resistance at the dissimilar material interface is higher than the contact resistance at the homogeneous material interface When forming a small lap joint by resistance welding, a first current is energized between at least three stacked plates to preferentially form a nugget at the same kind material interface, and then the first current is applied. The method is characterized in that a large second current is applied to form a nugget at the interface between different materials and join .
また、本発明の異種金属の接合構造は、上記した接合方法によって得られるものであって、第1の金属材料から成る少なくとも2枚の板材と、第1の金属材料よりも低い融点を有する第2の金属材料から成る少なくとも1枚の板材を重ね合わせて成る異種金属材料の抵抗溶接による重ね接合構造において、異種材界面と同種材界面を有し、異種材界面における接触抵抗が同種材界面における接触抵抗よりも小さく、上記異種材界面には、当該界面を形成する各異種材料の単位面積あたりの強度と板厚の積が小さい方の板厚をt1(mm)としたとき、4.4√t1<Dd<12√t1の範囲の径Dd(mm)を有するナゲットが形成され、上記同種材界面には、当該界面を形成する各同種材料の単位面積あたりの強度と板厚の積が小さい方の板厚をt2(mm)としたとき、4√t2<Ds<7√t2の範囲の径Ds(mm)を有するナゲットが形成されていることを特徴とする。
また、本発明の自動車用部品は、本発明の上記異種金属の接合構造を備えたことを特徴としている。
The dissimilar metal bonding structure of the present invention is obtained by the above-described bonding method, and includes at least two plate members made of the first metal material and a first melting point lower than that of the first metal material. In a lap joint structure by resistance welding of dissimilar metal materials formed by overlapping at least one plate material made of two metal materials, the dissimilar material interface has the same kind of material interface, and the contact resistance at the dissimilar material interface is at the same kind of material interface. 4.4. When the thickness of the dissimilar material interface, which is smaller than the contact resistance and t1 (mm), is the thickness of the material with the smaller product of the strength per unit area and the thickness of each dissimilar material forming the interface, 4.4. A nugget having a diameter Dd (mm) in a range of √t1 <Dd <12√t1 is formed, and the product of the strength and the plate thickness per unit area of each of the same material forming the interface is formed on the same material interface. The smaller one Thickness when was the t2 (mm), wherein the nugget has a 4√t2 <Ds <7√t2 ranging diameter Ds (mm) is formed.
In addition, an automotive part of the present invention is characterized by including the above-described dissimilar metal joint structure of the present invention.
本発明によれば、異種材界面と同種材界面が混在し、異種材界面における接触抵抗が同種材接合における接触抵抗よりも小さく、融点差がある3枚以上の異種金属材料を抵抗溶接によって重ね接合するに際して、重ね合わせた材料間に、比較的小さい第1の電流を通電して同種材界面にナゲットを優先的に形成させた後、第1の電流よりも大きな第2の電流を通電するようにしている。したがって、ナゲットの優先形成によって同種材界面の抵抗が小さくなった状態で、異種材界面にナゲットが形成されることから、各界面に所望のナゲット径を形成することができ、低融点側材料の減肉を抑えながら、各界面における接合強度をそれぞれ十分に確保することができる。 According to the present invention, the dissimilar material interface and the dissimilar material interface are mixed, the contact resistance at the dissimilar material interface is smaller than the contact resistance in the same material joint, and three or more dissimilar metal materials having a melting point difference are overlapped by resistance welding. When joining, a relatively small first current is passed between the stacked materials to form a nugget preferentially at the same kind material interface, and then a second current larger than the first current is passed. I am doing so. Therefore, the nugget is formed at the different material interface in the state where the resistance of the same material interface is reduced by the preferential formation of the nugget, so that a desired nugget diameter can be formed at each interface. Sufficient bonding strength at each interface can be ensured while suppressing thinning.
以下に、本発明の異種金属の接合方法及び接合構造について、さらに詳細かつ具体的に説明する。 The dissimilar metal bonding method and bonding structure of the present invention will be described in more detail and specifically below.
本発明の異種金属の接合方法は、上記したように、異種材界面と同種材界面を有し、異種材界面における接触抵抗が同種材界面における接触抵抗よりも小さい3枚以上の金属板材の抵抗溶接による重ね接合に関するものである。このような異種金属材料の具体的な組合せ、すなわち異種材界面における接触抵抗が同種材界面における接触抵抗よりも小さくなるような3枚以上の被接合材の組合せとしては、鋼材−鋼材−アルミニウム合金材、鋼材−鋼材−マグネシウム合金材の各組合せを典型例として挙げることができる。
すなわち、鋼材−アルミニウム合金材−アルミニウム合金材や、鋼材−マグネシウム合金材−マグネシウム合金材の組合せについては、異種材界面における抵抗発熱が同種材界面における抵抗発熱よりも大きくなることから、本発明の対象外となる。
As described above, the dissimilar metal bonding method of the present invention has a dissimilar material interface and a similar material interface, and the contact resistance at the dissimilar material interface is smaller than the contact resistance at the same material interface. It relates to lap joint by welding. As a specific combination of such different metal materials, that is, a combination of three or more materials to be joined such that the contact resistance at the interface between the different materials is smaller than the contact resistance at the interface between the same materials, a steel material-steel material-aluminum alloy is used. As a typical example, combinations of materials, steel materials-steel materials-magnesium alloy materials can be given.
That is, regarding the combination of steel material-aluminum alloy material-aluminum alloy material and steel material-magnesium alloy material-magnesium alloy material, the resistance heat generation at the dissimilar material interface is larger than the resistance heat generation at the same material interface. Not applicable.
なお、本発明において、『同種材』とは、成分系や金属組織が同じものを意味し、必ずしも同一規格に属するもの同士に限定されるものではない。
例えば、鋼材の場合、炭素鋼と合金鋼、軟鋼と抗張力鋼などのように別規格に属するものであっても、フェライト組織である限り、本発明においては『同種材』とみなす。
また、本発明において、『同種材界面』とは、同種材同士の接合界面を意味し、『異種材界面』とは、異種材同士の接合界面を意味する。
In the present invention, the “same material” means the same component system and metal structure, and is not necessarily limited to those belonging to the same standard.
For example, in the case of steel materials, even if they belong to different standards such as carbon steel and alloy steel, mild steel and tensile steel, etc., they are regarded as “same materials” in the present invention as long as they have a ferrite structure.
In the present invention, the “similar material interface” means a joint interface between the same materials, and the “foreign material interface” means a joint interface between the different materials.
本発明の異種金属の接合方法には、図1(a)に示すような交流電源タイプのスポット溶接装置が用いられ、図示するように、例えば3枚の板材A、B、C(BとCが同種材)を1対の溶接電極E1、E2により加圧及び通電することによって重ね溶接が行われる。 In the method for joining dissimilar metals according to the present invention, an AC power source type spot welding apparatus as shown in FIG. 1A is used. As shown in the figure, for example, three plate materials A, B, C (B and C Lap welding is performed by pressurizing and energizing a pair of welding electrodes E1 and E2.
そして、本発明の異種金属の接合方法においては、重ね合わせた材料間に、比較的小さい第1の電流を通電して同種材界面におけるナゲットを優先的に形成を優先させた後、第1の電流よりも大きな第2の電流を通電するようにしている。
すなわち、接合の初期段階において比較的小さな電流で通電することによって、接触抵抗が大きく、抵抗発熱が大きい同種材界面に優先的にナゲットを形成させる。そして、同種材界面が接合されることにより電気の導通が確保されて、同種材界面における抵抗が低下することから、同種材界面におけるナゲット形成後には異種材界面における抵抗発熱が十分なものとなり、当該異種材界面に所望のナゲット径を形成することが可能となる。
In the dissimilar metal joining method of the present invention, a relatively small first current is applied between the stacked materials to prioritize formation of nuggets at the same kind material interface, A second current larger than the current is applied.
That is, by applying a current with a relatively small current in the initial stage of bonding, a nugget is preferentially formed at the same material interface having a large contact resistance and a large resistance heat generation. And, by connecting the same material interface, electrical conduction is ensured and the resistance at the same material interface decreases, so after the nugget formation at the same material interface, the resistance heat generation at the different material interface becomes sufficient, A desired nugget diameter can be formed at the interface between the different materials.
このとき、図1(b)に示すように、接触抵抗をモニタリングするための電流計や電圧計を内蔵する、接触抵抗モニタリング装置を用いて、重ね合わせた板材における同種材界面の接触抵抗をモニタリングしながら接合し、同種材界面における抵抗値の変化に応じて第1の電流をこれより大きな第2の電流に切換えるようにすることが望ましい。 At this time, as shown in FIG. 1 (b), the contact resistance at the same material interface in the overlapped plate material is monitored using a contact resistance monitoring device incorporating an ammeter and a voltmeter for monitoring the contact resistance. It is desirable that the first current is switched to a larger second current in accordance with a change in the resistance value at the interface of the same material.
なお、図示しないが、上記の他に、図1(b)における板材A及び板材C間の接触抵抗をモニタリングして第1の電流を第2の電流に切り替えるようにしてもかまわない。この場合、板材A及び板材B間の接触抵抗に比べ、板材B及び板材C間の接触抵抗の方が大きいため、板材A及び板材C間の接触抵抗の低下をモニタリングすることによっても、同種材界面の接触抵抗が低下したことが分かる。
また、同種材界面の接触抵抗と同時に異種材界面の接触抵抗をもモニタリングし、同種材界面の接触抵抗値が異種材界面の抵抗値と同等となったタイミングで、第1の電流をこれより大きな第2の電流に切換えるようにすることもできる。
Although not shown, in addition to the above, the contact resistance between the plate A and the plate C in FIG. 1B may be monitored to switch the first current to the second current. In this case, since the contact resistance between the plate material B and the plate material C is larger than the contact resistance between the plate material A and the plate material B, the same kind of material can be obtained by monitoring the decrease in the contact resistance between the plate material A and the plate material C. It can be seen that the contact resistance at the interface has decreased.
In addition, the contact resistance at the same kind material interface and the contact resistance at the same kind material interface are monitored at the same time, and at the timing when the contact resistance value at the same kind material interface becomes equal to the resistance value at the different kind material interface, the first current is It is also possible to switch to a large second current.
本発明の異種金属の接合方法においては、異種材界面と同種材界面の接触抵抗のバランスを良好なものとして、通電時の抵抗発熱差を少なくする観点から、異種材界面を形成する少なくとも一方の板材の表面粗さを同種材界面を形成する板材表面のいずれよりも粗くすることや、この逆に同種材界面を形成する少なくとも一方の板材の表面粗さを異種材界面を形成する板材のいずれの表面よりも細かくすることが望ましい。
板材表面を粗くする方法しては、例えば目の粗いヤスリでこすったり、エッチングやショットブラストを施したりすることができる。また、表面粗度を改善(細かく平滑にする)には、仕上加工用の砥石研摩やバフ研摩が考えられる。
In the method for joining dissimilar metals of the present invention, the balance of contact resistance between the dissimilar material interface and the dissimilar material interface is good, and from the viewpoint of reducing the difference in resistance heat generation during energization, at least one of the dissimilar material interfaces is formed. Either the surface roughness of the plate material is made rougher than any of the plate material surfaces forming the homogeneous material interface, and conversely, the surface roughness of at least one plate material forming the homogeneous material interface is any of the plate materials forming the dissimilar material interface It is desirable to make it finer than the surface.
As a method for roughening the surface of the plate material, for example, rubbing with a coarse file, etching or shot blasting can be performed. Further, in order to improve the surface roughness (to make it fine and smooth), grinding stone polishing or buffing for finishing can be considered.
また、同様の目的で、異種材界面に当該界面の電気抵抗を高める材料を介在させることも望ましく、具体的には、表面にアルミナペーストを塗布したり、カーボン材やセラミックス、導電性樹脂などを介在させたりすることができる。 For the same purpose, it is also desirable to interpose a material that increases the electrical resistance of the interface at the dissimilar material interface. Specifically, an alumina paste is applied to the surface, carbon material, ceramics, conductive resin, etc. It can be interposed.
さらに、本発明の異種金属の接合方法においては、異種材界面にシール材を介在させることができ、異種金属が直接接触することによって生じる電食を防止して、異材継手の耐食性を向上させることができる。また、これによって異種材界面における抵抗発熱が促進され、当該界面のナゲット径を拡大させることができるという2次的な効果も期待することができる。 Further, in the dissimilar metal joining method of the present invention, a seal material can be interposed at the dissimilar material interface, and the electrolytic corrosion caused by the direct contact of the dissimilar metal can be prevented to improve the corrosion resistance of the dissimilar material joint. Can do. In addition, it is possible to expect a secondary effect that resistance heat generation at the interface between different materials is promoted and the nugget diameter at the interface can be increased.
加えて、本発明の異種金属の接合方法においては、異種材界面に当該界面を形成する異種金属材料の少なくとも一方と共晶溶融を生じる第3の金属材料を介在させることが望ましく、これによって接合表面に強固な酸化皮膜が形成されていたとしても、接合界面から容易に排出することができるようになる。 In addition, in the dissimilar metal joining method of the present invention, it is desirable to interpose at least one of the dissimilar metal materials forming the interface at the dissimilar material interface with a third metal material that causes eutectic melting. Even if a strong oxide film is formed on the surface, it can be easily discharged from the bonding interface.
すなわち、図2は、共晶反応を生じる合金の一例として、Al−Zn系2元状態図を示すものであって、図に示すようにAl−Zn系における共晶点(Te)は、655Kであり、Alの融点933Kよりもはるかに低い温度で共晶反応が生じる。
したがって、図に示した共晶点を利用してAlとZnの共晶溶融を作り出し、アルミニウム材の接合時における酸化皮膜除去や相互拡散などの接合作用に利用することによって、低温接合が実施できるため、Fe2Al5やFeAl3などの金属間化合物の接合界面における成長を極めて効果的に抑制することができる。
That is, FIG. 2 shows an Al—Zn binary phase diagram as an example of an alloy that causes a eutectic reaction. As shown in the figure, the eutectic point (Te) in the Al—Zn system is 655K. The eutectic reaction occurs at a temperature much lower than the melting point of 933 K of Al.
Therefore, by using the eutectic points shown in the figure to create eutectic melting of Al and Zn, and using them for bonding actions such as oxide film removal and interdiffusion during bonding of aluminum materials, low temperature bonding can be performed. Therefore, it is possible to extremely effectively suppress the growth at the joint interface of intermetallic compounds such as Fe 2 Al 5 and FeAl 3 .
ここで、共晶溶融とは共晶反応を利用した溶融であって、2つの金属(又は合金)が相互拡散して生じた相互拡散域の組成が共晶組成となった場合に、保持温度が共晶温度以上であれば共晶反応により液相が形成される。例えばアルミニウムと亜鉛の場合、アルミニウムの融点は933K、亜鉛の融点は692.5Kであり、この共晶金属はそれぞれの融点より低い655Kにて溶融する。
したがって、両金属の清浄面を接触させ、655K以上に加熱保持すると反応が生じる。これを共晶溶融といい、Al−95%Znが共晶組成となるが、共晶反応自体は合金成分に無関係な一定の変化であり、合金組成は共晶反応の量を増減するに過ぎない。
Here, eutectic melting is melting using a eutectic reaction, and when the composition of an interdiffusion region formed by mutual diffusion of two metals (or alloys) becomes a eutectic composition, the holding temperature If is equal to or higher than the eutectic temperature, a liquid phase is formed by the eutectic reaction. For example, in the case of aluminum and zinc, the melting point of aluminum is 933 K, the melting point of zinc is 692.5 K, and this eutectic metal melts at 655 K which is lower than the respective melting points.
Therefore, a reaction occurs when the clean surfaces of both metals are brought into contact and heated to 655K or higher. This is called eutectic melting, and Al-95% Zn has a eutectic composition, but the eutectic reaction itself is a constant change unrelated to the alloy components, and the alloy composition only increases or decreases the amount of eutectic reaction. Absent.
一方、アルミニウム材の表面には強固な酸化皮膜が存在するが、これは抵抗溶接時の通電と加圧によってアルミニウム材に塑性変形が生じることにより物理的に破壊されることになる。
すなわち、加圧によって材料表面の微視的な凸部同士が擦れ合うことから、一部の酸化皮膜の局所的な破壊によってアルミニウムと亜鉛が接触した部分から共晶溶融が生じ、この液相の形成によって近傍の酸化皮膜が破砕、分解されてさらに共晶溶融が全面に拡がる反応の拡大によって、酸化皮膜破壊の促進と液相を介した接合が達成される。
On the other hand, a strong oxide film is present on the surface of the aluminum material, which is physically destroyed by plastic deformation of the aluminum material caused by energization and pressurization during resistance welding.
That is, since the microscopic projections on the surface of the material rub against each other by pressurization, eutectic melting occurs from the part where aluminum and zinc are in contact due to local destruction of some oxide films, and this liquid phase formation By accelerating the reaction in which the nearby oxide film is crushed and decomposed and further eutectic melting spreads over the entire surface, the destruction of the oxide film and the joining via the liquid phase are achieved.
共晶組成は相互拡散によって自発的に達成されるため、組成のコントロールは必要ない。必須条件は2種の金属あるいは合金の間に、低融点の共晶反応が存在することであり、アルミニウムと亜鉛の共晶溶融の場合、亜鉛に代えてZn−Al合金を用いる場合には、少なくとも亜鉛が95%以上の組成でなければならない。 Since the eutectic composition is spontaneously achieved by interdiffusion, it is not necessary to control the composition. The essential condition is that a low melting eutectic reaction exists between the two metals or alloys. In the case of eutectic melting of aluminum and zinc, when using Zn-Al alloy instead of zinc, The composition must be at least 95% zinc.
図3(a)〜(f)は、異種材界面にシール材を介在させた状態で、共晶溶融を利用した接合プロセスを示す概略図である。
まず、図3(a)に示すように、その表面に、Alと共晶を形成する第3の金属材料として機能する亜鉛めっき層2pが施された亜鉛めっき鋼板2と、アルミニウム合金板1を用意し、これら亜鉛めっき鋼板2とアルミニウム合金板1を亜鉛めっき層2pが内側になるように重ねる。なお、その界面にはペースト状のシール材Sが塗布されており、アルミニウム合金板1の表面には酸化皮膜1cが形成している。
FIGS. 3A to 3F are schematic views showing a joining process using eutectic melting in a state where a sealing material is interposed at the interface between different materials.
First, as shown in FIG. 3 (a), a galvanized
次に、上下1対の溶接電極によりこれら被接合材を相対的に押圧すると、図3(b)に示すように、シール材Sは接合部の中央部から外周部に排出され、中央部は亜鉛めっき層2pとアルミニウム合金板1の表面の酸化皮膜1cが直接接触する。
ここで、加圧及び通電により、機械的又は熱的な衝撃が負荷されると、図3(c)に示すように局部的に酸化皮膜が破壊される。
Next, when these materials to be bonded are relatively pressed by a pair of upper and lower welding electrodes, as shown in FIG. 3B, the sealing material S is discharged from the central portion of the bonded portion to the outer peripheral portion. The galvanized
Here, when a mechanical or thermal impact is applied by pressurization and energization, the oxide film is locally broken as shown in FIG.
これによって、亜鉛とアルミニウムの局部的な接触が起こり、亜鉛とアルミニウムの共晶点温度以上に保持されると、図3(d)に示すように亜鉛とアルミニウムの共晶溶融が生じる。
そして、図3(e)に示すように、電極のさらなる押圧によって、共晶溶融金属と共に、酸化皮膜1cや接合界面の不純物(図示せず)が排出物となって、接合部周囲に排出されながら、さらにシール材も排出され、所定の接合面積が確保される。
As a result, local contact between zinc and aluminum occurs, and eutectic melting of zinc and aluminum occurs as shown in FIG. 3 (d) when the temperature is maintained above the eutectic point temperature of zinc and aluminum.
And as shown in FIG.3 (e), the
その後、アルミニウムと鋼の新生面同士が直接接合され、図3(f)に示すように、亜鉛めっき鋼板2とアルミニウム合金板1の間に強固な金属接合を得ることができる。
Thereafter, the new surfaces of aluminum and steel are directly joined to each other, and a strong metal joint can be obtained between the galvanized
本発明の接合方法における異種金属材料の具体的な組合せとしては、まず、上記したような鋼材とアルミニウム合金材の組合せを挙げることができる。
このとき両材料の間に介在させる第3の金属材料としては、アルミニウム合金と低融点共晶を形成する材料でありさえすれば特に限定されることはなく、例えば、上記した亜鉛(Zn)の他には、銅(Cu)、錫(Sn)、銀(Ag)、ニッケル(Ni)などを用いることができる。
As a specific combination of dissimilar metal materials in the joining method of the present invention, first, a combination of a steel material and an aluminum alloy material as described above can be mentioned.
At this time, the third metal material interposed between the two materials is not particularly limited as long as it is a material that forms a low melting point eutectic with an aluminum alloy. For example, the above-described zinc (Zn) In addition, copper (Cu), tin (Sn), silver (Ag), nickel (Ni), or the like can be used.
すなわち、これら金属とAlとのは共晶反応を生じ、母材であるアルミニウム合金材の融点以下の温度で溶融するため、脆弱な金属間化合物が形成し易い鋼材とアルミニウム合金材の接合においても、低温で酸化皮膜を除去することができ、接合過程での接合界面における金属間化合物の形成が抑制でき、強固な接合が可能になる。 That is, these metals and Al cause a eutectic reaction and melt at a temperature lower than the melting point of the aluminum alloy material, which is the base material. Therefore, even in joining steel materials and aluminum alloy materials where fragile intermetallic compounds are easily formed. The oxide film can be removed at a low temperature, the formation of intermetallic compounds at the bonding interface during the bonding process can be suppressed, and strong bonding can be achieved.
また、本発明を自動車ボディの組立てに適用することを考えた場合、被接合材は鋼材とアルミニウム合金材との組合せがほとんどであるが、鋼材とマグネシウム合金材の組合せなども考えられる。
鋼材とマグネシウム合金材との接合に際しては、後述する実施例と同様に鋼材側にめっきした亜鉛とマグネシウムの間に共晶反応を生じさせて接合することが可能である。
Further, when considering application of the present invention to the assembly of an automobile body, the material to be joined is mostly a combination of a steel material and an aluminum alloy material, but a combination of a steel material and a magnesium alloy material is also conceivable.
When joining a steel material and a magnesium alloy material, it is possible to cause a eutectic reaction between zinc and magnesium plated on the steel material side in the same manner as in the examples described later.
なお、本発明においては、第3の金属材料として、上記したような純金属に限定されることはなく、共晶金属は2元合金も3元合金も存在するため、これらの少なくとも1種の金属を含む合金であってもよい。 In the present invention, the third metal material is not limited to the pure metal as described above, and eutectic metal includes both binary alloys and ternary alloys. Therefore, at least one of these eutectic metals exists. An alloy containing a metal may be used.
そして、上記したアルミニウム合金材やマグネシウム合金材と鋼材との異種金属の接合に際しては、上記したように鋼材として、アルミニウムやマグネシウムと低融点共晶を形成する第3の金属材料である亜鉛がその表面にあらかじめめっきされている、いわゆる亜鉛めっき鋼板を用いることができる。この場合には、特別な準備を要することもなく、防錆目的で亜鉛めっきを施した通常の市販鋼材をそのまま使用することができ、極めて簡便かつ安価に、異種金属の強固な接合が可能になる。 And when joining the dissimilar metal of the above-mentioned aluminum alloy material or magnesium alloy material and steel, as described above, zinc, which is a third metal material forming a low melting eutectic with aluminum or magnesium, is used as the steel material. A so-called galvanized steel sheet whose surface is preliminarily plated can be used. In this case, no special preparation is required, and ordinary commercial steel that has been galvanized for the purpose of rust prevention can be used as it is, enabling strong joining of dissimilar metals to be extremely simple and inexpensive. Become.
本発明の異種金属の接合構造は、第1の金属材料から成る2枚以上の板材と、これよりも融点が低い第2の金属材料から成る1枚以上の板材を重ね合わせた時に、異種材界面と同種材界面が形成され、しかも異種材界面における接触抵抗が、同種材界面における接触抵抗よりも小さくなるような3枚以上の異種金属材料の抵抗溶接による接合構造であって、異種材界面には、4.4√t1<Dd<12√t1の範囲、好ましくは5.5√t1<Dd<12√t1の範囲の径Ddを有するナゲット(t1:異種材界面を形成する各材料の単位面積あたりの強度と板厚の積が小さい方の板厚)が形成される一方、同種材界面には、4√t2<Ds<7√t2の範囲の径Dsを有するナゲット(t2:同種材界面を形成する各材料の単位面積あたりの強度と板厚の積が小さい方の板厚)が形成されていることから、継手構造全体として必要な強度を確保することができる。 The dissimilar metal joining structure of the present invention is obtained when two or more plate materials made of a first metal material and one or more plate materials made of a second metal material having a lower melting point are overlapped with each other. A joint structure formed by resistance welding of three or more dissimilar metal materials so that a contact interface at the same material interface is formed and the contact resistance at the dissimilar material interface is smaller than the contact resistance at the same material interface, Includes nuggets having a diameter Dd in the range of 4.4√t1 <Dd <12√t1, preferably in the range of 5.5√t1 <Dd <12√t1 (t1: of each material forming the dissimilar material interface). A nugget having a diameter Ds in the range of 4√t2 <Ds <7√t2 (t2: similar) Per unit area of each material forming the material interface Since the plate thickness towards the product is small in intensity and thickness) is formed, it is possible to ensure the necessary strength as a whole joint structure.
このとき、異種材界面におけるナゲット径Dd及び同種材界面におけるナゲット径Dsがそれぞれ4.4√t1及び4√t2以下であると、それぞれの界面における接合強度が不足するおそれがある。また、上記ナゲット径Dd及びDsがそれぞれ12√t1及び7√t2以上になると、必要以上の過剰品質となると共に、より大きな接合フランジ幅が必要となって重量増加、コストアップという不都合が生じるおそれがある。 At this time, if the nugget diameter Dd at the dissimilar material interface and the nugget diameter Ds at the same material interface are 4.4√t1 and 4√t2, respectively, the bonding strength at each interface may be insufficient. In addition, when the nugget diameters Dd and Ds are 12√t1 and 7√t2 or more, respectively, the quality becomes higher than necessary, and a larger joint flange width is required, which may cause inconveniences such as an increase in weight and an increase in cost. There is.
以下、本発明を実施例に基づいて具体的に説明するが、本発明は、これら実施例によって何ら限定されるものではない。 EXAMPLES Hereinafter, although this invention is demonstrated concretely based on an Example, this invention is not limited at all by these Examples.
(実施例1)
図4(a)に示すように、板厚1.0mmの6000系アルミニウム合金板1と、板厚0.8mmの亜鉛めっき鋼板2と、板厚1.2mmの裸鋼板3をこの順番に重ねた3枚打ちの接合を実施した(t1=1mm、t2=0.8mm)。
Example 1
As shown in FIG. 4A, a 6000 series aluminum alloy plate 1 having a plate thickness of 1.0 mm, a galvanized
このとき、図1(b)に示したような接触抵抗モニタリング装置を備えた交流電源タイプのスポット溶接装置を使用すると共に、電極E1及びE2として、先端曲面の曲率半径が40mmのR型電極をそれぞれ使用した。 At this time, an AC power source type spot welding apparatus provided with a contact resistance monitoring apparatus as shown in FIG. 1B is used, and an R-type electrode having a radius of curvature of a tip curved surface of 40 mm is used as the electrodes E1 and E2. Each was used.
そして、同種材界面、すなわち亜鉛めっき鋼板2と裸鋼板3の間の界面にナゲットNsを優先的に形成させるべく、300kgfの加圧力を加え、モニタリング装置Mによって同種材界面の接触抵抗をモニタリングしながら、4000Aの交流電流を通電した。続いて、同種材界面の接触抵抗が予め計測し記憶させておいた初期接触抵抗値の20%の値に低下したタイミングで、交流電流を22000Aに増加させ、合計0.16秒間通電した。
これによって、図4(b)に示すように、異種材界面、すなわちアルミニウム合金板1と亜鉛めっき鋼板2の間の界面にナゲットNdが形成された。
Then, in order to preferentially form nugget Ns at the same material interface, that is, the interface between the galvanized
As a result, as shown in FIG. 4B, nugget Nd was formed at the dissimilar material interface, that is, the interface between the aluminum alloy plate 1 and the galvanized
このような通電パターンで抵抗溶接を実施することにより、接合初期の接触抵抗差が大きい状態では、異種材界面での発熱が抑制されて、初期の低電流では発熱が不足し、異種材界面ではナゲットが形成されず、同種材界面にナゲットNsが先行して形成され始める。そして、初期の低電流よりも大きな電流に切換わると、同種材界面が一部接合されることによって、界面の電気抵抗が小さくなるため、同種材界面の発熱を抑えた状態で異種材界面にナゲットNdを形成することができる。
したがって、同種材界面の発熱によってアルミニウム合金板1の減肉が生じるといった問題を解消すると共に、両界面におけるナゲット径を適正なサイズのものとし、良好な接合継手を得ることができる。
By carrying out resistance welding with such an energization pattern, heat generation at the dissimilar material interface is suppressed in a state where the contact resistance difference at the initial stage of bonding is large, heat generation is insufficient at the initial low current, and at the dissimilar material interface. Nuggets are not formed, and nugget Ns begins to be formed at the same material interface. When the current is switched to a larger current than the initial low current, the homogeneous material interface is partially joined, and the electrical resistance of the interface is reduced. A nugget Nd can be formed.
Accordingly, it is possible to solve the problem that the thinning of the aluminum alloy plate 1 is caused by heat generation at the interface of the same kind of material, and to make the nugget diameter of both interfaces appropriate, thereby obtaining a good joint joint.
この結果、同種材界面には径Ds=5mmのナゲットNsが形成されると共に、異種材界面には径Dd=7mmのナゲットNdが形成され、その周囲には、溶融共晶金属や酸化皮膜、接合界面の不純物などを含む排出物Dが押し出されている。
また、この実施例においては、亜鉛めっき鋼板2を使用していることから、第3の金属材料としての亜鉛とアルミニウムの共晶溶融が有効に作用し、アルミニウム合金板1の表面の酸化皮膜を低温で除去することができ、異種材界面の新生面同士の接触を低温で実現することができ、薄くて均一なFe−Al拡散反応層(化合物層)が形成され、高強度の接合継手を得ることができた。
As a result, a nugget Ns having a diameter Ds = 5 mm is formed at the interface of the same material, and a nugget Nd having a diameter Dd = 7 mm is formed at the interface of the different material, and a molten eutectic metal, an oxide film, Exhaust D containing impurities at the bonding interface is extruded.
Further, in this embodiment, since the galvanized
(実施例2)
上記実施例1と同様に、板厚1.0mmの6000系アルミニウム合金板1と、板厚0.8mmの亜鉛めっき鋼板2と、板厚1.2mmの裸鋼板3をこの順番に重ねた3枚打ちの接合を実施した。このとき、異種材界面を構成するアルミニウム合金板1と亜鉛めっき鋼板2のうち、アルミニウム合金板1の接合面をエメリー80番で研磨することによって、同種材界面を構成する亜鉛めっき鋼板2及び裸鋼板3の表面よりも粗くなるようにした。つまり、これによって異種材界面の初期の接触抵抗が同種材界面と同等となるようにした。
(Example 2)
Similar to Example 1 above, a 6000 series aluminum alloy plate 1 with a plate thickness of 1.0 mm, a galvanized
そして、図1(b)に示したスポット溶接装置を使用し、初期電流を6000Aとしたこと以外は、上記同様の操作を繰り返すことによって、同種材界面には径Ds=5mmのナゲットNsが形成され、異種材界面には径Dd=7mmのナゲットNdが形成された。
このように、異種材界面の表面粗さを粗くすることによって、当該界面の接触抵抗が増加し、異種材界面での抵抗発熱が増して、異種材界面のナゲット形成が促進される。そして、同種材界面での抵抗発熱の熱伝導によるアルミニウム合金板1の減肉を抑制し、異種材界面、同種材界面で適正な形状、寸法のナゲットを実現して、共晶溶融の効果と相俟って、良好な接合継手を得ることができた。
Then, by using the spot welding apparatus shown in FIG. 1B and repeating the same operation as described above except that the initial current is set to 6000 A, a nugget Ns having a diameter Ds = 5 mm is formed at the same material interface. As a result, a nugget Nd having a diameter Dd = 7 mm was formed at the interface between different materials.
Thus, by increasing the surface roughness of the dissimilar material interface, the contact resistance of the interface increases, the resistance heat generation at the dissimilar material interface increases, and the nugget formation at the dissimilar material interface is promoted. Then, the thinning of the aluminum alloy plate 1 due to the heat conduction of the resistance heat generation at the same kind material interface is suppressed, and the nugget of an appropriate shape and size is realized at the dissimilar material interface and the same kind material interface. Together, it was possible to obtain a good joint joint.
(実施例3)
図5(a)に示すように、板厚1.0mmの6000系アルミニウム合金板1と、板厚1.0mmの溶融亜鉛めっき鋼板2と、板厚1.2mmの裸鋼板3をこの順番に重ねた3枚打ちの接合を行うに際して、アルミニウム合金板1と亜鉛めっき鋼板2の界面に、エポキシ系の熱硬化樹脂から成るシール材Sを配置した。
(Example 3)
As shown in FIG. 5A, a 6000 series aluminum alloy plate 1 having a plate thickness of 1.0 mm, a hot dip galvanized
そして、図1(b)に示したスポット溶接装置を使用し、450kgfの加圧力を加えたこと以外は、上記実施例1と同様の操作を繰り返すことによって、図5(b)に示すように、同種材界面には径Ds=5mmのナゲットNsが形成され、異種材界面には径Dd=8mmのナゲットNdが形成された。
このように、異種材間にシール材Sを挟持したことによって、異種材の直接接触による電食が防止されると共に、シール材の電気抵抗によって異種材界面での抵抗発熱が増すという効果をも得ることができ、異種材界面のナゲット形成が促進される。そして、同様に、接合界面からアルミニウムの酸化皮膜を円滑に排出すると共に、アルミニウム合金板1の減肉を抑制し、異種材界面、同種材界面で適正な形状、寸法のナゲットを形成して、良好な接合継手を得ることができた。
Then, by using the spot welding apparatus shown in FIG. 1B and repeating the same operation as in Example 1 except that a pressing force of 450 kgf was applied, as shown in FIG. 5B. The nugget Ns having a diameter Ds = 5 mm was formed at the same kind material interface, and the nugget Nd having a diameter Dd = 8 mm was formed at the dissimilar material interface.
Thus, by sandwiching the sealing material S between the different materials, the electrolytic corrosion due to the direct contact of the different materials is prevented, and the resistance heat generation at the interface between the different materials is increased due to the electrical resistance of the sealing material. Nugget formation at the interface between different materials can be promoted. Similarly, the aluminum oxide film is smoothly discharged from the joining interface, and the thickness reduction of the aluminum alloy plate 1 is suppressed, and a nugget of an appropriate shape and size is formed at the dissimilar material interface, the same material interface, A good joint was obtained.
(実施例4)
上記実施例1と同様に、板厚1.0mmの6000系アルミニウム合金板1と、板厚0.8mmの亜鉛めっき鋼板2と、板厚1.2mmの裸鋼板3をこの順番に重ねた3枚打ちの接合を実施した。このとき、異種材界面の接触抵抗を増加させるべく、アルミニウム合金板1の接合面にアルミナペーストを薄く塗布した。
Example 4
Similar to Example 1 above, a 6000 series aluminum alloy plate 1 with a plate thickness of 1.0 mm, a galvanized
次に、図1(b)に示したスポット溶接装置を使用し、初期電流を6000Aとしたことを除いて、上記実施例1と同様の操作を繰り返すことによって、同種材界面には径Ds=5mmのナゲットNsが形成され、異種材界面には径Dd=7mmのナゲットNdが形成された。
この実施例では、異種材界面にアルミナが介在することによって、アルミニウム合金板1と亜鉛めっき鋼板2の間の電気抵抗が増加し、異種材界面における抵抗発熱が増して、当該界面のナゲット形成が促進される。また、上記各実施例と同様に、亜鉛めっき層2pの介在に基づく共晶溶融の作用によって酸化被膜の円滑な排出が可能になり、良好な接合継手を得ることができた。
Next, by using the spot welding apparatus shown in FIG. 1B and repeating the same operation as in Example 1 except that the initial current is set to 6000 A, the diameter Ds = A 5 mm nugget Ns was formed, and a nugget Nd having a diameter Dd = 7 mm was formed at the dissimilar material interface.
In this embodiment, the presence of alumina at the dissimilar material interface increases the electrical resistance between the aluminum alloy plate 1 and the galvanized
(比較例1)
上記実施例1と同様に、板厚1.0mmの6000系アルミニウム合金板1と、板厚0.8mmの亜鉛めっき鋼板2と、板厚1.2mmの裸鋼板3をこの順番に重ねた3枚打ちの接合を実施した。
(Comparative Example 1)
Similar to Example 1 above, a 6000 series aluminum alloy plate 1 with a plate thickness of 1.0 mm, a galvanized
このとき、図1(a)に示した交流電源タイプのスポット溶接装置を使用し、上記同様の電極E1及びE2を用いて、同種材界面のナゲットが適正サイズとなるような条件、具体的には、240kgfの加圧力を加えながら、12000Aの交流電流を0.16秒間通電することによって接合した。
この結果、同種材界面には径Ds=6mmのナゲットNsが形成され、異種材界面には径Dd=3mmのナゲットNdが形成された。
At this time, using the AC power source type spot welding apparatus shown in FIG. 1 (a) and using the electrodes E1 and E2 similar to those described above, the condition that the nugget at the interface of the same material becomes an appropriate size, specifically Were joined by applying an alternating current of 12000 A for 0.16 seconds while applying a pressure of 240 kgf.
As a result, a nugget Ns having a diameter Ds = 6 mm was formed at the same material interface, and a nugget Nd having a diameter Dd = 3 mm was formed at the dissimilar material interface.
(比較例2)
上記比較例1と同様な3枚の重ね接合を実施するに際して、異種材界面のナゲットが適正サイズとなるような条件、具体的には、240kgfの加圧力を加えながら、22000Aの交流電流を0.16秒間通電したこと以外は、比較例1と同様の操作を繰り返すことによって、本例の異種金属接合継手を得た。
この結果、同種材界面には径Ds=8mmのナゲットNsが形成された。しかし、異種材界面には、いったんはナゲットが形成されたものの、アルミニウム合金板1に減肉が生じたことで、アルミニウム合金板1が電極E1に溶着し、アルミニウム合金板1に穴が生じたため、異種材界面には適正なナゲットが形成されなかった。
(Comparative Example 2)
When three lap joints similar to Comparative Example 1 are performed, the condition that the nugget at the dissimilar material interface has an appropriate size, specifically, an AC current of 22000 A is applied while applying a pressure of 240 kgf. Except for energization for 16 seconds, the same operation as in Comparative Example 1 was repeated to obtain the dissimilar metal joint of this example.
As a result, nugget Ns having a diameter Ds = 8 mm was formed at the same kind material interface. However, although the nugget was once formed at the interface between the different materials, the aluminum alloy plate 1 was welded to the electrode E1 due to the thinning of the aluminum alloy plate 1, and the aluminum alloy plate 1 had a hole. No proper nugget was formed at the dissimilar material interface.
上記実施例1〜4、比較例1及び比較例2において、各界面に生じるナゲットの形成状態や被接合材の減肉の状態を比較した結果を、表1に示す。
その結果、実施例1〜4においては、異種材及び同種材界面におけるナゲットの大きさが適正であり、減肉も生じなかった。一方、比較例1においては、同種材界面に適正なナゲットが形成されるものの、異種材界面は発熱不足で十分な大きさのナゲットが形成されず、比較例2においては、異種材界面に適正サイズのナゲットを形成するに足る電流を流すと、アルミニウム合金板に減肉が生じ、良好な接合継手を得ることができなくなることが判明した。
Tables 1 to 4 show the results of comparing the nugget formation state occurring at each interface and the thickness reduction state of the materials to be joined in Examples 1 to 4, Comparative Example 1 and Comparative Example 2.
As a result, in Examples 1 to 4, the size of the nugget at the interface between the different material and the same material was appropriate, and no thinning occurred. On the other hand, in Comparative Example 1, an appropriate nugget is formed at the same material interface, but the heterogeneous material interface is not heated enough to form a sufficiently large nugget, and in Comparative Example 2, the appropriate material interface is appropriate. It has been found that if a current sufficient to form a size nugget is applied, the aluminum alloy plate is thinned and a good joint cannot be obtained.
(実施例5)
図6(a)に示すように、板厚1.0mmの6000系アルミニウム合金板1と、板厚1.0mmの裸鋼板4と、板厚1.2mmの裸鋼板3をこの順番に重ねた3枚打ちの接合を行った。
(Example 5)
As shown in FIG. 6A, a 6000 series aluminum alloy plate 1 having a thickness of 1.0 mm, a bare steel plate 4 having a thickness of 1.0 mm, and a bare steel plate 3 having a thickness of 1.2 mm were stacked in this order. Three-piece joining was performed.
そして、上記実施例1と同様の操作を繰り返すことによって、図6(b)に示すように、同種材界面には径Ds=5mmのナゲットNsが形成され、異種材界面には径Dd=7mmのナゲットNdが形成された。
この実施例では、アルミニウム合金板1に接する鋼材として、亜鉛めっき鋼板2に替えて裸鋼板4を用いたことから、共晶溶融が生ぜず、アルミニウム合金板表面の酸化皮膜の円滑な除去が難しくなることから、ナゲット中に酸化アルミニウムの残存が多少生じたことから、接合強度がやや低下する傾向が認められた。
Then, by repeating the same operation as in the first embodiment, as shown in FIG. 6B, a nugget Ns having a diameter Ds = 5 mm is formed at the same material interface, and a diameter Dd = 7 mm at the dissimilar material interface. Nugget Nd was formed.
In this embodiment, since the bare steel plate 4 was used in place of the galvanized
(実施例6)
図7(a)に示すように、板厚1.0mmの6000系アルミニウム合金板1と、板厚0.8mmの溶融亜鉛めっき鋼板2と、板厚0.8mmの裸鋼板5と、板厚1.2mmの裸鋼板3をこの順序に重ねた4枚打ちの接合を実施した(t1=1mm、t2=0.8mm)。
(Example 6)
As shown in FIG. 7A, a 6000 series aluminum alloy plate 1 having a plate thickness of 1.0 mm, a hot-dip galvanized
すなわち、図1(b)に示したスポット溶接装置を使用し、450kgfの加圧力を加え、モニタリング装置Mによって同種材界面の接触抵抗、この場合には溶融亜鉛めっき鋼板2と裸鋼板3の間の抵抗をモニタリングしながら、まず4000Aの交流電流を通電し、上記各実施例と同様に、モニタリングされた抵抗値が初期接触抵抗値の20%の値に低下した時点で交流電流を22000Aに増加させ、都合0.16秒間通電した。
That is, using the spot welding apparatus shown in FIG. 1 (b), a pressure of 450 kgf is applied, and the contact resistance of the same kind material interface by the monitoring apparatus M, in this case, between the hot dip galvanized
これによって、図7(b)に示すように、亜鉛めっき鋼板2と裸鋼板5の同種材界面には径Ds1=5mmのナゲットNs1が、裸鋼板5と裸鋼板3の同種材界面には径Ds2=5mmのナゲットNs2がそれぞれ形成された。一方、アルミニウム合金板1と亜鉛めっき鋼板2から成る異種材界面には径Dd=7mmのナゲットNdが形成された。
このように、4枚打ちの接合の場合にも、亜鉛めっき鋼板を用いることによって、接合界面からアルミニウムの酸化皮膜を円滑に排出することができると共に、アルミニウム合金板1の減肉を抑制し、2つの同種材界面と異種材界面に適正な形状、寸法のナゲットを形成して、良好な接合継手を得ることができた。
As a result, as shown in FIG. 7 (b), the nugget Ns1 having a diameter Ds1 = 5 mm is present at the same material interface between the galvanized
As described above, even in the case of four-sheet joining, by using a galvanized steel sheet, the aluminum oxide film can be smoothly discharged from the joining interface, and the thinning of the aluminum alloy sheet 1 is suppressed. Good joints could be obtained by forming nuggets with appropriate shapes and dimensions at the two homogeneous material interfaces and different material interfaces.
A、B、C 板材
1 アルミニウム合金板(板材)
2 亜鉛めっき鋼板(板材)
2p 亜鉛めっき層(第3の金属材料)
3、4、5 裸鋼板(板材)
4 裸鋼板(板材)
S シール材
A, B, C Plate material 1 Aluminum alloy plate (plate material)
2 Galvanized steel sheet (sheet material)
2p galvanized layer (third metal material)
3, 4, 5 Bare steel plate (plate material)
4 Bare steel plate
S sealing material
Claims (10)
重ね合わせた少なくとも3枚の板材間に、第1の電流を通電して同種材界面におけるナゲットを優先的に形成させた後、第1の電流よりも大きな第2の電流を通電して異種材界面にナゲットを形成して接合することを特徴とする異種金属の接合方法。 At least two plate materials made of the first metal material and at least one plate material made of the second metal material having a melting point lower than that of the first metal material are overlapped, and the dissimilar material interface and the same material interface In forming a lap joint of dissimilar metal material by resistance welding, the contact resistance at the dissimilar material interface is smaller than the contact resistance at the dissimilar material interface,
A preferential formation of a nugget at the interface of the same kind of material is conducted between at least three stacked plates by preferentially forming a nugget at the same kind material interface, and then a different current is produced by energizing a second current larger than the first current. A method for joining dissimilar metals, comprising forming a nugget at an interface and joining.