JP5324360B2 - Fabrics and textile products including core-sheath type composite false twisted yarn - Google Patents

Fabrics and textile products including core-sheath type composite false twisted yarn Download PDF

Info

Publication number
JP5324360B2
JP5324360B2 JP2009196868A JP2009196868A JP5324360B2 JP 5324360 B2 JP5324360 B2 JP 5324360B2 JP 2009196868 A JP2009196868 A JP 2009196868A JP 2009196868 A JP2009196868 A JP 2009196868A JP 5324360 B2 JP5324360 B2 JP 5324360B2
Authority
JP
Japan
Prior art keywords
core
fabric
type composite
sheath type
twisted yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2009196868A
Other languages
Japanese (ja)
Other versions
JP2011047080A (en
Inventor
右文 福永
Original Assignee
帝人フロンティア株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 帝人フロンティア株式会社 filed Critical 帝人フロンティア株式会社
Priority to JP2009196868A priority Critical patent/JP5324360B2/en
Publication of JP2011047080A publication Critical patent/JP2011047080A/en
Application granted granted Critical
Publication of JP5324360B2 publication Critical patent/JP5324360B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、濃染性および吸水性およびドライ感に優れた、芯鞘型複合仮撚加工糸を含む布帛、および該布帛を用いてなる繊維製品に関するものである。   The present invention relates to a fabric including a core-sheath type composite false twisted yarn excellent in deep dyeability, water absorption and dryness, and a fiber product using the fabric.
従来、濃染性を有する布帛として、例えば特許文献1では、ポリメチルメタクリレート系ポリマーおよび/またはポリスチレン系ポリマーを含有する鞘部ポリエステルマルチフィラメントと、芯部ポリエステルマルチフィラメントとからなる芯鞘型複合仮撚加工糸を用いて布帛を構成することが提案されている。しかしながら、かかる布帛において、濃染性には優れるものの、吸水性(吸汗性)およびドライ感の点で十分とはいえなかった。   Conventionally, as a fabric having a deep dyeing property, for example, in Patent Document 1, a core-sheath type composite temporary sheath composed of a sheath polyester multifilament containing a polymethyl methacrylate polymer and / or a polystyrene polymer and a core polyester multifilament is disclosed. Proposing fabrics using twisted yarn has been proposed. However, such a fabric is excellent in deep dyeing property, but it is not sufficient in terms of water absorption (sweat absorption) and dry feeling.
他方、吸水性およびドライ感を有する布帛として、例えば特許文献2では、単繊維横断面形状が十字型である捲縮ポリエステルマルチフィラメントを用いて布帛を構成することが提案されている。しかしながら、かかる布帛において、吸水性およびドライ感には優れるものの濃染性の点で十分とはいえなかった。
以上のように、濃染性および吸水性およびドライ感に優れた布帛はこれまであまり提案されていない。
On the other hand, as a fabric having water absorption and dry feeling, for example, Patent Document 2 proposes that a fabric is formed using a crimped polyester multifilament whose cross-sectional shape of a single fiber is a cross shape. However, such a fabric is excellent in water absorbency and dry feeling, but it is not sufficient in terms of darkness.
As described above, fabrics excellent in deep dyeability, water absorption and dry feeling have not been proposed so far.
特開2006−283245号公報JP 2006-283245 A 特開2002−201541号公報JP 2002-201541 A
本発明は上記の背景に鑑みなされたものであり、その目的は、濃染性および吸水性およびドライ感に優れた布帛、および該布帛を用いてなる繊維製品を提供することにある。   The present invention has been made in view of the above background, and an object of the present invention is to provide a fabric excellent in deep dyeability, water absorption, and dry feeling, and a fiber product using the fabric.
本発明者は上記の課題を達成するため鋭意検討した結果、ポリメチルメタクリレート系ポリマーおよび/またはポリスチレン系ポリマーを含有する鞘部ポリエステルマルチフィラメントと、芯部ポリエステルマルチフィラメントとからなる芯鞘型複合仮撚加工糸を用いて布帛を構成する際に、芯部ポリエステルマルチフィラメントとして異型断面繊維(単繊維横断面形状において凹部を有する繊維)を用いることにより、濃染性および吸水性およびドライ感に優れた布帛が得られることを見出し、さらに鋭意検討を重ねることにより本発明を完成するに至った。   As a result of intensive studies to achieve the above-mentioned problems, the present inventor has found that a core-sheath type composite temporary sheath comprising a sheath polyester multifilament containing a polymethyl methacrylate polymer and / or a polystyrene polymer and a core polyester multifilament. When a fabric is formed using twisted yarns, by using atypical cross-section fibers (fibers having concave portions in a single fiber cross-sectional shape) as the core polyester multifilament, it is excellent in deep dyeing, water absorption and dry feeling. The present invention has been completed by finding that a woven fabric can be obtained and further intensive studies.
かくして、本発明によれば「芯鞘型複合仮撚加工糸を含む布帛であって、前記芯鞘型複合仮撚加工糸が、ポリエステルを主成分とし、かつポリメチルメタクリレート系ポリマーおよび/またはポリスチレン系ポリマーを含有する鞘部ポリエステルマルチフィラメントAと、ポリエステルからなり、かつその単繊維横断面形状が異型である芯部ポリエステルマルチフィラメントBとで構成されることを特徴とする、芯鞘型複合仮撚加工糸を含む布帛。」が提供される。   Thus, according to the present invention, “a fabric including a core-sheath type composite false twisted yarn, wherein the core-sheath type composite false twisted yarn has a polyester as a main component and is a polymethyl methacrylate polymer and / or polystyrene. The core-sheath type composite multi-filament A comprising a sheath-type polyester multi-filament A containing a polymer and a core-portion polyester multi-filament B made of polyester and having a single fiber cross-sectional shape of a different shape. A fabric comprising twisted yarn "is provided.
その際、前記鞘部ポリエステルマルチフィラメントAにおいて、ポリメチルメタクリレート系ポリマーおよび/またはポリスチレン系ポリマーが重量基準で0.5〜3.0重量%添加されていることが好ましい。また、前記鞘部ポリエステルマルチフィラメントAにおいて、単糸繊度が3dtex以上であることが好ましい。また、前記芯部ポリエステルマルチフィラメントBにおいて、単繊維横断面形状が、十字型、星型、卍型、およびT字型からなる群より選択されるいずれかであることが好ましい。また、前記芯部ポリエステルマルチフィラメントBにおいて、単糸繊度が3dtex以下であることが好ましい。また、前記芯鞘型複合仮撚加工糸において、撚り係数10000〜30000の撚りが施されていることが好ましい。
ただし、撚り係数は下記式により定義する。
撚り係数=撚数[T/M]×(繊度[dtex]×9/10)1/2
In that case, in the said sheath part polyester multifilament A, it is preferable that the polymethylmethacrylate type polymer and / or the polystyrene type polymer are added 0.5 to 3.0 weight% on a weight basis. In the sheath polyester multifilament A, the single yarn fineness is preferably 3 dtex or more. Moreover, in the said core part polyester multifilament B, it is preferable that the single fiber cross-sectional shape is either selected from the group which consists of a cross shape, a star shape, a saddle shape, and T shape. In the core polyester multifilament B, the single yarn fineness is preferably 3 dtex or less. The core-sheath type composite false twisted yarn is preferably twisted with a twist coefficient of 10,000 to 30,000.
However, the twist coefficient is defined by the following formula.
Twist factor = twist number [T / M] × (fineness [dtex] × 9/10) 1/2
また、前記芯鞘型複合仮撚加工糸の横断面において、芯部ポリエステルマルチフィラメントBの露出比率が50%以下であることが好ましい。
また、本発明の布帛において、布帛が織物であり、かつ該織物のカバーファクターCFが1200〜3000の範囲内であることが好ましい。
ただし、カバーファクターCFは下記式により定義する。
CF=(DWp/1.1)1/2×MWp+(DWf/1.1)1/2×MWf
ただし、DWpは経糸総繊度(dtex)、MWpは経糸織密度(本/2.54cm)、DWfは緯糸総繊度(dtex)、MWfは緯糸織密度(本/2.54cm)である。
Moreover, it is preferable that the exposure ratio of the core polyester multifilament B is 50% or less in the cross section of the core-sheath type composite false twisted yarn.
In the fabric of the present invention, the fabric is preferably a woven fabric, and the cover factor CF of the woven fabric is preferably in the range of 1200 to 3000.
However, the cover factor CF is defined by the following formula.
CF = (DWp / 1.1) 1/2 × MWp + (DWf / 1.1) 1/2 × MWf
However, DWp is the total warp fineness (dtex), MWp is the warp weave density (main / 2.54 cm), DWf is the total weft fineness (dtex), and MWf is the weft weave density (main / 2.54 cm).
また、本発明の布帛において、布帛の明度指数L値が11以下であることが好ましい。また、布帛の吸水性がJIS L−1907に記載された滴下法(ウイッキング法)により測定して1秒以下であることが好ましい。
また、本発明によれば、前記の布帛を用いてなる、婦人用ブラックフォーマル衣料、パーテイドレス、紳士用スーツ、スラックス、およびスポーツ衣料からなる群より選択されるいずれかの繊維製品が提供される。
In the fabric of the present invention, the lightness index L value of the fabric is preferably 11 or less. Moreover, it is preferable that the water absorption of a fabric is 1 second or less as measured by the dropping method (wicking method) described in JIS L-1907.
In addition, according to the present invention, there is provided a textile product selected from the group consisting of ladies' black formal garments, party dresses, gentleman's suits, slacks, and sports garments, using the fabric. .
本発明によれば、濃染性および吸水性およびドライ感に優れた布帛、および該布帛を用いてなる繊維製品が得られる。   ADVANTAGE OF THE INVENTION According to this invention, the fabric excellent in deep dyeability, water absorption, and dry feeling, and the textiles using this fabric are obtained.
芯鞘型複合仮撚加工糸の横断面において、芯部ポリエステルマルチフィラメントBの露出比率(糸の断面方向)を説明するための図面代用写真である。In the cross section of the core-sheath type composite false twisted yarn, it is a drawing substitute photograph for explaining the exposure ratio (cross-sectional direction of the yarn) of the core polyester multifilament B. 芯鞘型複合仮撚加工糸の横断面において、芯部ポリエステルマルチフィラメントBの露出比率(糸の断面方向)を説明するための図面代用写真である。In the cross section of the core-sheath type composite false twisted yarn, it is a drawing substitute photograph for explaining the exposure ratio (cross-sectional direction of the yarn) of the core polyester multifilament B. 芯鞘型複合仮撚加工糸において、芯部ポリエステルマルチフィラメントBの露出比率(糸の長さ方向)を説明するための図面代用写真である。In the core-sheath type composite false twisted yarn, it is a drawing-substituting photograph for explaining the exposure ratio (length direction of the yarn) of the core polyester multifilament B.
以下、本発明の実施の形態について詳細に説明する。
本発明において、鞘部ポリエステルマルチフィラメントAと芯部ポリエステルマルチフィラメントBに用いられるポリエステルは、主たる繰り返し単位のエチレンテレフタレートが85モル%以上、より好ましくは95モル%以上からなるポリエステルであることが好ましい。テレフタル酸成分および/またはエチレングリコール成分以外の第3成分を少量(通常は、テレフタル酸成分に対して20モル%以下)共重合したものであってもよい。前記ポリエステルの固有粘度(IV)(35℃のオルソ−クロロフェノール溶液を溶媒として使用し算出)は、通常、衣料用布帛素材として使用されるポリエステルと同じ範疇の固有相対粘度0.7dL/g以下のものが好ましい。さらに好ましくは、0.55〜0.65dL/gである。これらのポリエステルには、公知の添加剤、例えば、顔料、染料、艶消し剤、防汚剤、蛍光増白剤、難燃剤、安定剤、紫外線吸収剤、滑剤を含んでもよい。
Hereinafter, embodiments of the present invention will be described in detail.
In the present invention, the polyester used for the sheath polyester multifilament A and the core polyester multifilament B is preferably a polyester comprising 85 mol% or more, more preferably 95 mol% or more of the main repeating unit ethylene terephthalate. . It may be obtained by copolymerizing a small amount of a third component other than the terephthalic acid component and / or the ethylene glycol component (usually 20 mol% or less with respect to the terephthalic acid component). The intrinsic viscosity (IV) of the polyester (calculated using an ortho-chlorophenol solution at 35 ° C. as a solvent) is usually an intrinsic relative viscosity of 0.7 dL / g or less in the same category as the polyester used as a cloth material for clothing. Are preferred. More preferably, it is 0.55-0.65 dL / g. These polyesters may contain known additives such as pigments, dyes, matting agents, antifouling agents, fluorescent whitening agents, flame retardants, stabilizers, ultraviolet absorbers, and lubricants.
前記鞘部ポリエステルマルチフィラメントAでは、かかる基質ポリマーに対して、ポリメチルメタクリレート系ポリマーおよび/またはポリスチレン系ポリマーを含有することにより、紡糸の際に配向結晶が抑制され、濃染効果が得られる。   The sheath polyester multifilament A contains a polymethyl methacrylate polymer and / or a polystyrene polymer with respect to the substrate polymer, whereby oriented crystals are suppressed during spinning and a deep dyeing effect is obtained.
前記ポリメチルメタクリレート系ポリマーおよびポリスチレン系ポリマーは、立体規則性におけるアタックチックあるいはシンジオタクチック構造を示す非晶性のポリメチルメタクリレート系ポリマーまたはポリスチレン系ポリマーであってもよいし、アイソタックチック構造を示す結晶性のポリメチルメタクリレート系ポリマー、ポリスチレン系ポリマーであってもよい。   The polymethyl methacrylate-based polymer and the polystyrene-based polymer may be an amorphous polymethyl methacrylate-based polymer or polystyrene-based polymer exhibiting an stereotactic or syndiotactic structure, and may have an isotactic structure. It may be a crystalline polymethyl methacrylate polymer or polystyrene polymer.
前記基質ポリマーに添加されるポリマー(ポリメチルメタクリレート系ポリマーおよび/またはポリスチレン系ポリマー)の添加量は、基質ポリマーの重量対比で0.5〜3.0重量%の範囲内であることが好ましい。該添加量が0.5重量%よりも小さいと、紡糸の際に配向結晶があまり抑制されず、濃染効果が得られないおそれがある。逆に該添加量が3.0重量%よりも大きいと、糸条の繊度斑、仮撚り加工時の断糸、毛羽発生、さらには染色斑を誘起するおそれがある。このため、適正な添加量は、0.5〜3.0重量の範囲であり、さらに好ましい添加量は、1.0〜2.5重量%である。   The amount of the polymer (polymethyl methacrylate polymer and / or polystyrene polymer) added to the substrate polymer is preferably in the range of 0.5 to 3.0% by weight relative to the weight of the substrate polymer. When the added amount is less than 0.5% by weight, oriented crystals are not suppressed so much during spinning, and there is a possibility that a deep dyeing effect cannot be obtained. On the contrary, when the added amount is larger than 3.0% by weight, there is a risk of causing fineness unevenness of the yarn, yarn breakage during false twisting, generation of fluff, and further dyeing unevenness. For this reason, an appropriate addition amount is in the range of 0.5 to 3.0 weight, and a more preferable addition amount is 1.0 to 2.5 weight percent.
基質ポリマーに添加されるポリマーは、計量機で所望する添加量を基質ポリマー側のポリマー輸送配管内あるいは押出機のポリマー投入口に直接接続する形で添加するのが一般
的である。添加手段としては、計量式のほかに、添加する重合体を単独で溶融押出して、基質ポリマー側に注入するインジェクション方式も可能である。次に、添加されたポリマーと基質ポリマーを溶融、混練、押出する。押出機には1軸あるいは2軸のタイプがある。混練性を向上させるためには2軸押出機が好ましいが、1軸押出機でも十分な混練が可能である。さらに、マドック型押出機などのスクリュー溝形状を変えた押出機を使用すると混錬はより均一となる。
In general, the polymer added to the substrate polymer is added in such a manner that a desired addition amount is directly connected to the polymer transport pipe on the substrate polymer side or to the polymer inlet of the extruder. As the addition means, besides the metering type, an injection method in which the polymer to be added is melt-extruded alone and injected into the substrate polymer side is also possible. Next, the added polymer and the substrate polymer are melted, kneaded, and extruded. Extruders are available in one or two screw types. In order to improve kneadability, a twin screw extruder is preferred, but a single screw extruder can be sufficiently kneaded. Furthermore, kneading becomes more uniform when an extruder having a changed screw groove shape such as a Maddock type extruder is used.
一方、芯部ポリエステルマルチフィラメントBにおいて、単繊維横断面形状が異型(すなわち、丸断面以外の形状)であることが肝要である。該形状が丸断面の場合、ドライ感に優れた布帛が得られず好ましくない。
ここで、前記異型断面において、ドライ感に優れた布帛を得る上で特開2002−201541号公報と同様に、下記に定義する開口深度Sが30%以上であることが好ましい。
On the other hand, in the core polyester multifilament B, it is important that the cross-sectional shape of the single fiber is atypical (that is, a shape other than the round cross-section). When the shape has a round cross section, a fabric excellent in dry feeling cannot be obtained, which is not preferable.
Here, in the modified cross section, the opening depth S defined below is preferably 30% or more in the same manner as in JP-A-2002-201541 in order to obtain a fabric excellent in dry feeling.
(開口深度Sの測定)
芯部ポリエステルマルチフィラメントBを構成する各フィラメントにつき、その任意の断面における凹部の開口部の長さL、凹部の最大深さHより下記式を用いて算出する。
S(%)=H/L×100
なお、芯部ポリエステルマルチフィラメントBにおいて、単繊維横断面形状の具体例としては、例えば、十字型、星型、卍型、T字型などが例示される。なかでも、吸水性およびドライ感に優れた布帛を得る上で十字型が特に好ましい。
(Measurement of opening depth S)
About each filament which comprises the core part polyester multifilament B, it calculates using the following formula from the length L of the opening part of the recessed part in the arbitrary cross sections, and the maximum depth H of the recessed part.
S (%) = H / L × 100
In the core polyester multifilament B, specific examples of the cross-sectional shape of the single fiber include a cross shape, a star shape, a saddle shape, a T shape, and the like. Among these, a cross shape is particularly preferable for obtaining a fabric excellent in water absorption and dry feeling.
本発明において、芯鞘型複合仮撚加工糸は前記鞘部ポリエステルマルチフィラメントAと芯部ポリエステルマルチフィラメントBとで構成される。そして、該芯鞘型複合仮撚加工糸において、前記鞘部ポリエステルマルチフィラメントAは鞘部に位置し、一方、芯部ポリエステルマルチフィラメントBに位置している。   In the present invention, the core-sheath type composite false twisted yarn is composed of the sheath polyester multifilament A and the core polyester multifilament B. In the core-sheath type composite false twisted yarn, the sheath polyester multifilament A is located in the sheath portion, while being located in the core polyester multifilament B.
かかる芯鞘型複合仮撚加工糸は、鞘部ポリエステルマルチフィラメントA用ポリマーと芯部ポリエステルマルチフィラメントB用ポリマーを用い、同一口金または別々の口金を使用して紡糸した後、例えば特開2006−283245号公報に記載された製造方法により製造することができる。ただし、本願では、芯部ポリエステルマルチフィラメントの単糸繊維横断面形状を異型とするため、芯部ポリエステルマルチフィラメントB用として異型吐出孔を穿孔した口金を使用する必要がある。   Such a core-sheath type composite false twisted yarn uses a polymer for the sheath polyester multifilament A and a polymer for the core polyester multifilament B, and after spinning using the same die or separate die, for example, It can be produced by the production method described in Japanese Patent No. 283245. However, in this application, in order to make the cross-sectional shape of the single yarn fiber of the core polyester multifilament atypical, it is necessary to use a die having a perforated discharge hole for the core polyester multifilament B.
その際、紡速(引取速度)は2500〜5000m/分(より好ましくは3000〜4000m/分)の範囲内であることが好ましい。上記引取速度が2500m/分未満では、捲き取られたポリエステル自体の残留伸度があまりにも高く、非相溶ポリマー添加による配向結晶抑制効果が発現しないおそれがある。逆に、引取速度が5000m/分を超えると、細化挙動の異なる2群の糸条を紡糸する場合には、紡糸性が損われるおそれがある。   At that time, the spinning speed (take-off speed) is preferably in the range of 2500 to 5000 m / min (more preferably 3000 to 4000 m / min). When the take-up speed is less than 2500 m / min, the residual elongation of the polyester that has been scraped off is too high, and there is a possibility that the effect of suppressing oriented crystals due to the addition of an incompatible polymer may not be exhibited. Conversely, if the take-up speed exceeds 5000 m / min, spinnability may be impaired when spinning two groups of yarns having different thinning behaviors.
次いで、特開2006−283245号公報の図1に示すように、予め交絡処理された、2種の未延伸ポリエステルマルチフィラメント1は、ガイド2を経てフィードローラー3により延伸同時仮撚域に供給される。この際、仮撚直前に交絡処理することが好ましく、フィードローラー3の後に追加のフィードローラー3’を設け、その間でインターレースノズル4でIL(インターレース)交絡付与することが好ましい。   Next, as shown in FIG. 1 of Japanese Patent Application Laid-Open No. 2006-283245, two types of unstretched polyester multifilaments 1 that have been entangled in advance are supplied to a stretched false false twist region by a feed roller 3 through a guide 2. The At this time, it is preferable to perform the entanglement process immediately before false twisting, and it is preferable to provide an additional feed roller 3 ′ after the feed roller 3 and to provide IL (interlace) entanglement with the interlace nozzle 4 therebetween.
次いで、フィードローラー3と第1デリベリーローラー8との間で延伸されながら冷却プレート6を経てフリクションディスク7により加撚・解撚され、その際、第1仮撚熱セットヒーター5で熱固定される。仮撚加工された糸条は、必要に応じて、(特に必要なければ、省略可)第1デリベリーローラー8と第2デリベリーローラー10との間で再熱処理ヒーター9で再熱処理され、次いで巻取ローラー11でパッケージ12として巻き取られる。   Next, the film is twisted and untwisted by the friction disk 7 through the cooling plate 6 while being stretched between the feed roller 3 and the first delivery roller 8, and at that time, the heat is fixed by the first false twist heat set heater 5. The The false-twisted yarn is reheated by the reheat heater 9 between the first deliberry roller 8 and the second deliberry roller 10 as necessary (can be omitted if not necessary), and then It is wound up as a package 12 by a winding roller 11.
その際に使用される延伸同時仮撚加工機の仮撚具は、仮撚具ディスク直径(D)が58〜62mm、およびディスクの回転軸に対する糸条の走行角が38〜48度であることが好ましい。なお、ここでいう走行角度とは、ディスク回転軸と摩擦円盤の外周上を接触走行する糸条とがなす角を意味する。   The false twisting tool of the drawing simultaneous false twisting machine used at that time has a false twister disk diameter (D) of 58 to 62 mm, and a running angle of the yarn with respect to the rotation axis of the disk is 38 to 48 degrees. Is preferred. Here, the traveling angle means an angle formed by the disk rotating shaft and the yarn traveling in contact on the outer periphery of the friction disk.
仮撚加工糸を製造する際は、加撚張力と解撚張力との関係を、下記範囲を満足させることが工程安定化のために好ましい。すなわち、加工張力KT値=解撚張力KT2/加撚張力KT1とするとき、KT値が0.8〜1.5(より好ましくは0.9〜1.4)であることが好ましい。
ここで、
加撚張力(KT1) 0.2g/dtex≦KT1≦0.5g/dtex
解撚張力(KT2) 0.25g/dtex≦KT2≦0.55g/dtex
であることが好ましい。
When producing false twisted yarn, it is preferable for stabilizing the process that the relationship between twisting tension and untwisting tension satisfies the following range. That is, when the processing tension KT value = untwisting tension KT2 / twisting tension KT1, the KT value is preferably 0.8 to 1.5 (more preferably 0.9 to 1.4).
here,
Twisting tension (KT1) 0.2 g / dtex ≦ KT1 ≦ 0.5 g / dtex
Untwisting tension (KT2) 0.25 g / dtex ≦ KT2 ≦ 0.55 g / dtex
It is preferable that
加工張力KT値を上記範囲内にするには、適正倍率、加工加撚、解撚張力設定、ディス
ク度とヤーン速度の比率を変更すれば良い。KT値が上記領域を外れる場合は、安定した加工、品質(捲縮、毛羽)を維持できないおそれがある。
In order to make the work tension KT value within the above range, the ratio of the appropriate magnification, work twisting, untwisting tension setting, disc degree and yarn speed may be changed. If the KT value is out of the above range, stable processing and quality (crimping and fluff) may not be maintained.
この際、仮撚数TWは、(10000/dtex)1/2≦TW≦(30000/dtex)1/2の範囲にすることが好ましい。仮撚数TW(ケ/m)が(10000/dtex)1/2未満の場合には、得られるポリエステル仮撚加工糸は捲縮性および嵩高性が低下するだけでなく、目的とする高級差別素材としてのウールライク、シルクライクの風合が得がたくなるおそれがある。一方、仮撚数TW(ケ/m)が(30000/dtex)1/2を超える場合には、延伸仮撚加工時に毛羽、風綿が発生し易くなるおそれがある。 At this time, the false twist number TW is preferably in the range of (10000 / dtex) 1/2 ≦ TW ≦ (30000 / dtex) 1/2 . When the number of false twists TW (ke / m) is less than (10,000 / dtex) 1/2 , the polyester false twisted yarn obtained has not only reduced crimpability and bulkiness, but also the desired high-grade discrimination. There is a risk that the texture of wool-like and silk-like will be difficult to obtain. On the other hand, when the number of false twists TW (ke / m) exceeds (30000 / dtex) 1/2 , there is a possibility that fluff and fluff are likely to occur during stretch false twisting.
その他、走行角度を範囲内に設定するには、厚さおよび摩擦円盤の間隔を適宜調節すれ
ばよい。なお、走行角度θは、全ての摩擦円盤について上記範囲内になるように設定することが好ましく、そのためには例えばガイドディスクを利用するのが好ましい。
また、仮撚熱セット温度Hとしては、100〜300℃、仮撚セット時間Tとしては0.05〜0.10秒の範囲が好ましい。
In addition, in order to set the traveling angle within the range, the thickness and the interval between the friction disks may be adjusted as appropriate. The traveling angle θ is preferably set so as to be within the above range for all the friction disks. For this purpose, for example, a guide disk is preferably used.
Moreover, as false twist heat setting temperature H, the range of 100-300 degreeC and false twist setting time T are 0.05-0.10 second.
かくして得られた芯鞘型複合仮撚加工糸において、鞘部ポリエステルマルチフィラメントAの総繊度、単糸繊度、フィラメント数としては、総繊度50〜160dtex、単糸繊度3dtex以上(より好ましくは3〜7dtex)、フィラメント数5〜20本の範囲内であることが好ましい。ここで、鞘部ポリエステルマルチフィラメントAの総繊度が50dtexよりも小さいと、鞘部ポリエステルマルチフィラメントAが芯部ポリエステルマルチフィラメントBを被覆することが困難になるおそれがある。逆に鞘部ポリエステルマルチフィラメントAの総繊度が160dtexよりも大きいと、布帛の風合いが損われるおそれがある。また、鞘部ポリエステルマルチフィラメントAの単糸繊度が3dtexよりも小さいと、鞘部ポリエステルマルチフィラメントAに染料がはいりにくくなり、濃染効果が得られないおそれがある。   In the core-sheath type composite false twisted yarn thus obtained, the total fineness, single yarn fineness, and number of filaments of the sheath polyester multifilament A are 50 to 160 dtex in total fineness, 3 dtex in single yarn fineness or more (more preferably 3 to 3). 7 dtex), preferably in the range of 5 to 20 filaments. Here, if the total fineness of the sheath polyester multifilament A is less than 50 dtex, it may be difficult for the sheath polyester multifilament A to cover the core polyester multifilament B. Conversely, if the total fineness of the sheath polyester multifilament A is larger than 160 dtex, the texture of the fabric may be impaired. Moreover, when the single yarn fineness of the sheath polyester multifilament A is smaller than 3 dtex, it is difficult for the sheath polyester multifilament A to enter the dye, and the deep dyeing effect may not be obtained.
一方、芯部ポリエステルマルチフィラメントBの総繊度、単糸繊度、フィラメント数としては総繊度30〜90dtex、単糸繊度3dtex以下(より好ましくは0.5〜2dtex)、フィラメント数10〜50本の範囲内であることが好ましい。芯部ポリエステルマルチフィラメントBの単糸繊度が3dtexよりも大きいと、十分な吸水性が得られないおそれがある。   On the other hand, the total fineness, single yarn fineness, and the number of filaments of the core polyester multifilament B are in the range of a total fineness of 30 to 90 dtex, a single yarn fineness of 3 dtex or less (more preferably 0.5 to 2 dtex), and a range of 10 to 50 filaments. It is preferable to be within. If the single yarn fineness of the core polyester multifilament B is larger than 3 dtex, sufficient water absorption may not be obtained.
芯鞘型複合仮撚加工糸の全繊度としては、80〜160dtexの範囲内であることが好ましい。該全繊度が80dtex未満では、布帛とした場合の引き裂き強度が低下するおそれがある。逆に該全繊度が160dtexを超えると、風合いが損われるおそれがある。   The total fineness of the core-sheath type composite false twisted yarn is preferably in the range of 80 to 160 dtex. If the total fineness is less than 80 dtex, the tear strength in the case of a fabric may be lowered. Conversely, if the total fineness exceeds 160 dtex, the texture may be impaired.
前記芯鞘型複合仮撚加工糸において、前記鞘部ポリエステルマルチフィラメントAと芯部ポリエステルマルチフィラメントBはそれぞれ1種類であることが好ましいが複数種類でもよい。また、前記芯鞘型複合仮撚加工糸は、前記鞘部ポリエステルマルチフィラメントAと芯部ポリエステルマルチフィラメントBのみで構成されることが好ましいが、芯鞘型複合仮撚加工糸の全重量に対して30重量%以下であれば、他のフィラメントが含まれていてもさしつかえない。   In the core-sheath type composite false twisted yarn, the sheath polyester multifilament A and the core polyester multifilament B are each preferably one type, but may be a plurality of types. Further, the core-sheath type composite false twisted yarn is preferably composed of only the sheath polyester multifilament A and the core polyester multifilament B, but with respect to the total weight of the core-sheath type composite false twisted yarn. If it is 30% by weight or less, other filaments may be contained.
前記芯鞘型複合仮撚加工糸の捲縮率は2%以上(より好ましくは3〜6%)であることが好ましい。2%未満では、非捲縮のフラットヤーン、あるいは融着したガサツイタ風合いとなる。なお、捲縮率は、鞘糸側の添加剤(PS、PMMA)、ヒーター温度、原糸比率変更などにより調整することができる。   The crimp rate of the core-sheath type composite false twisted yarn is preferably 2% or more (more preferably 3 to 6%). If it is less than 2%, a non-crimped flat yarn or a fused texture is obtained. The crimp rate can be adjusted by changing the sheath yarn side additives (PS, PMMA), heater temperature, raw yarn ratio, and the like.
また、前記芯鞘型複合仮撚加工糸においては、鞘部ポリエステルマルチフィラメントAの平均糸長は、鞘部ポリエステルマルチフィラメントAのそれよりも15〜25%、好ましくは17〜23%長いことが好ましい。15%未満では、嵩高性がなく、風合い、ソフト感不足し、一方、25%より長いと、鞘部が余り過ぎて、がさついたタ風合となるおそれがある。   In the core-sheath type composite false twisted yarn, the average yarn length of the sheath polyester multifilament A is 15 to 25%, preferably 17 to 23% longer than that of the sheath polyester multifilament A. preferable. If it is less than 15%, there is no bulkiness, and the texture and soft feeling are insufficient. On the other hand, if it is longer than 25%, the sheath part is too much, and there is a possibility that the texture becomes rough.
前記芯鞘型複合仮撚加工糸において、鞘部ポリエステルマルチフィラメントAが芯部ポリエステルマルチフィラメントBを被覆している。その際、芯鞘型複合仮撚加工糸の横断面において、芯部ポリエステルマルチフィラメントBの露出比率が50%以下であることが好ましい。該露出比率が50%よりも大きいと、濃染性が低下するおそれがある。ただし、横断面における露出比率は下記により測定するものとする。すなわち、芯鞘型複合仮撚加工糸の横断面を、電子顕微鏡を用いて観察し、芯部ポリエステルマルチフィラメントBの露出角度を測定し、その合計値を360で割り、100をかける。例えば、図1の場合、横断面における露出比率(%)=(a+b+c)/360×100であり、図2の場合、横断面における露出比率(%)=(d+f)/360×100である。   In the core-sheath type composite false twisted yarn, the sheath polyester multifilament A covers the core polyester multifilament B. In that case, it is preferable that the exposure ratio of the core polyester multifilament B is 50% or less in the cross section of the core-sheath type composite false twisted yarn. If the exposure ratio is greater than 50%, the deep dyeability may be reduced. However, the exposure ratio in a cross section shall be measured by the following. That is, the cross section of the core-sheath type composite false twisted yarn is observed using an electron microscope, the exposure angle of the core polyester multifilament B is measured, and the total value is divided by 360 and multiplied by 100. For example, in the case of FIG. 1, the exposure ratio (%) in the cross section = (a + b + c) / 360 × 100, and in the case of FIG. 2, the exposure ratio (%) in the cross section = (d + f) / 360 × 100.
また、芯鞘型複合仮撚加工糸の表面において、糸長方向の芯部ポリエステルマルチフィラメントBの露出比率が30%以下であることが好ましい。なお、該露出比率は下記式により求める。
糸長方向の露出比率(%)=AB/(AA+AB)×100
ただし、長さ3mmの芯鞘型複合仮撚加工糸を、電子顕微鏡を用いて観察し、芯部ポリエステルマルチフィラメントBの露出面積をABとし、鞘部ポリエステルマルチフィラメントAの露出面積をAAとする。
Moreover, it is preferable that the exposure ratio of the core polyester multifilament B in the yarn length direction is 30% or less on the surface of the core-sheath type composite false twisted yarn. The exposure ratio is obtained by the following formula.
Yarn length direction exposure ratio (%) = AB / (AA + AB) × 100
However, the core-sheath type composite false twisted yarn having a length of 3 mm is observed using an electron microscope, the exposed area of the core polyester multifilament B is AB, and the exposed area of the sheath polyester multifilament A is AA. .
本発明の布帛は前記芯鞘型複合仮撚加工糸を含む布帛である。その際、かかる布帛には前記芯鞘型複合仮撚加工糸のみが含まれることが最も好ましいが、布帛重量に対して50重量%以下であれば他の繊維が布帛に含まれていてもよい。   The fabric of the present invention is a fabric including the core-sheath type composite false twisted yarn. In this case, it is most preferable that the fabric contains only the core-sheath type composite false twisted yarn, but other fibers may be contained in the fabric as long as it is 50% by weight or less based on the weight of the fabric. .
また、前記芯鞘型複合仮撚加工糸を用いて布帛を構成する際、芯鞘型複合仮撚加工糸に撚りを施すことが好ましい。芯鞘型複合仮撚加工糸に撚りを施すことにより、芯部ポリエステルマルチフィラメントBが周期的に露出することにより、ドライ感が得られ、また、芯部ポリエステルマルチフィラメントBを形成する異型単繊維のくぼみ効果により、光反射を抑えて濃染性がさらに向上し好ましい。
その際、下記式により定義する撚り係数としては10000〜30000の範囲内であることが好ましい。
撚り係数=撚数[T/M]×(繊度[dtex]×9/10)1/2
Moreover, when a fabric is constituted using the core-sheath type composite false twisted yarn, it is preferable to twist the core-sheath type composite false twisted yarn. By twisting the core-sheath type composite false twisted yarn, the core polyester multifilament B is periodically exposed, so that a dry feeling can be obtained, and the atypical single fiber forming the core polyester multifilament B Due to the dent effect, dark reflection is further improved by suppressing light reflection, which is preferable.
At that time, the twisting coefficient defined by the following formula is preferably in the range of 10,000 to 30,000.
Twist factor = twist number [T / M] × (fineness [dtex] × 9/10) 1/2
本発明の布帛において、織編物の組織は限定されず通常の方法で製編織されたものでよく、例えば、織組織としては、平織、斜文織、サテン織物等の三原組織、変化組織、変化斜文織等の変化組織、たて二重織、よこ二重織等の片二重組織、たてビロードなどが例示される。また、編物としては、2枚筬または3枚筬を用いた、ハーフ組織、ハーフベース組織、サテン組織などが好適に例示される。   In the fabric of the present invention, the structure of the woven or knitted fabric is not limited, and may be knitted and woven by a normal method. For example, the woven structure includes three primary structures such as plain weave, oblique weave, satin woven, changed structure, change Examples thereof include a change structure such as a twill weave, a single double structure such as a vertical double weave and a horizontal double weave, and a vertical velvet. As the knitted fabric, a half structure, a half base structure, a satin structure and the like using two or three sheets are preferably exemplified.
なかでも、優れた濃染性および吸水性を得る上で、織編密度としては高密度のほうが好ましい。例えば、布帛が織物の場合、織物のカバーファクターCFが1200〜3000の範囲内であると、優れた濃染性および吸水性が得られ好ましい。   Among these, in order to obtain excellent deep dyeability and water absorption, a high density is preferred as the woven / knitted density. For example, when the fabric is a woven fabric, it is preferable that the cover factor CF of the woven fabric is in the range of 1200 to 3000 because excellent deep dyeability and water absorption are obtained.
ただし、カバーファクターCFは下記式により定義する。
CF=(DWp/1.1)1/2×MWp+(DWf/1.1)1/2×MWf
ただし、DWpは経糸総繊度(dtex)、MWpは経糸織密度(本/2.54cm)、DWfは緯糸総繊度(dtex)、MWfは緯糸織密度(本/2.54cm)である。
かかる布帛は通常、染色加工が施される。その際、染色加工は通常の分散染料を用いた常法の染色加工でよい。
However, the cover factor CF is defined by the following formula.
CF = (DWp / 1.1) 1/2 × MWp + (DWf / 1.1) 1/2 × MWf
However, DWp is the total warp fineness (dtex), MWp is the warp weave density (main / 2.54 cm), DWf is the total weft fineness (dtex), and MWf is the weft weave density (main / 2.54 cm).
Such fabric is usually subjected to a dyeing process. In this case, the dyeing process may be a conventional dyeing process using a normal disperse dye.
本発明の布帛には、エンボス加工、アルカリ減量加工、着色プリント、撥水加工、紫外線遮蔽剤、抗菌剤、消臭剤、防虫剤、蓄光剤、再帰反射剤、マイナスイオン発生剤等の機能を付与する各種加工を付加適用してもよい。特に、濃染性をさらに高めるため、濃染剤(例えば、日本化薬社製カヤディーパー(商品名))を用いて濃染加工することは好ましいことである。   The fabric of the present invention has functions such as embossing, alkali weight loss processing, colored printing, water repellent processing, ultraviolet shielding agent, antibacterial agent, deodorant, insect repellent, phosphorescent agent, retroreflective agent, negative ion generator and the like. Various processes to be applied may be additionally applied. In particular, in order to further enhance the deep dyeing property, it is preferable to carry out the deep dyeing process using a deep dyeing agent (for example, Kayadeper (trade name) manufactured by Nippon Kayaku Co., Ltd.).
かくして得られた布帛には前記の芯鞘型複合仮撚加工糸が含まれるので、該芯鞘型複合仮撚加工糸を構成する鞘部ポリエステルマルチフィラメントAにより濃染性が得られ、芯部ポリエステルマルチフィラメントBにより吸水性(吸汗性)およびドライ感が得られる。さらには、芯部ポリエステルマルチフィラメントBは前記のような異型断面繊維で構成されるので、異型の効果で光反射を抑えて濃染性がより一層向上する。   Since the core-sheath type composite false twisted yarn described above is included in the fabric thus obtained, a deep dyeing property is obtained by the sheath polyester multifilament A constituting the core-sheath type composite false twisted yarn, and the core portion. The polyester multifilament B provides water absorption (sweat absorbency) and dry feeling. Furthermore, since the core polyester multifilament B is composed of the atypical cross-section fibers as described above, the light dyeing is suppressed by the atypical effect, and the deep dyeability is further improved.
ここで、布帛の明度指数L値としては11以下であることが好ましい。また、布帛の吸水性としてはJIS L−1907に記載された滴下法(ウイッキング法)により測定して1秒以下であることが好ましい。   Here, the lightness index L value of the fabric is preferably 11 or less. The water absorption of the fabric is preferably 1 second or less as measured by the dropping method (wicking method) described in JIS L-1907.
次に、本発明の繊維製品は、前記の布帛を用いてなる、婦人用ブラックフォーマル衣料、パーテイドレス、紳士用スーツ、スラックス、スポーツ衣料などの衣料を含む繊維製品である。かかる繊維製品には前記の布帛が含まれるので、濃染性および吸水性およびドライ感に優れる。   Next, the textile product of the present invention is a textile product including clothing such as black formal clothing for women, party dress, suit for men, slacks, sports clothing, etc., using the above-mentioned fabric. Since the above-mentioned fabric is included in such a textile product, it is excellent in deep dyeability, water absorption and dry feeling.
以下、実施例をあげて、本発明をさらに具体的に説明するが、本発明はこれらの実施例
に限定されるものではない。なお、実施例中、特定値の測定は、下記に従った。
(1)固有粘度
35℃のオルソ−クロロフェノール溶液を溶媒として使用し算出した。
(2)撚り係数
下記式により撚り係数を算出した。
撚り係数=撚数[T/M]×(繊度[dtex]×9/10)1/2
(3)織物のカバーファクターCF
下記式により織物のカバーファクターCFを算出した。
CF=(DWp/1.1)1/2×MWp+(DWf/1.1)1/2×MWf
ただし、DWpは経糸総繊度(dtex)、MWpは経糸織密度(本/2.54cm)、DWfは緯糸総繊度(dtex)、MWfは緯糸織密度(本/2.54cm)である。
(4)布帛の明度指数L値
分光側光器(Gretag MacBeth Color−Eye 7000A)で生地表面を測定した。L値は明度を示し、その数値が大きいほど明度が高いことを示し、100に近いほど、淡色で白色に近く、0に近いほど、濃色である事を示す。
(5)吸水性
JIS L−1907に記載された滴下法(ウイッキング法)により吸水性を測定した。
(6)風合い(ドライ感)
試験者3名が官能評価により、「ドライ感がある。」「普通」「ドライ感がない」の3段階評価した。
(7)横断面における芯部ポリエステルマルチフィラメントBの露出比率
芯鞘型複合仮撚加工糸の横断面を、電子顕微鏡を用いて観察し、芯部ポリエステルマルチフィラメントBの露出角度を測定し、その合計値を360で割り100をかけて算出した。
(8)糸長方向における芯部ポリエステルマルチフィラメントBの露出比率
糸長方向の露出比率を記式により求めた。
糸長方向の露出比率(%)=AB/(AA+AB)×100
ただし、長さ3mmの芯鞘型複合仮撚加工糸を、図3のように電子顕微鏡を用いて観察し、芯部ポリエステルマルチフィラメントBの露出面積をABとし、鞘部ポリエステルマルチフィラメントAの露出面積をAAとする。
Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not limited to these examples. In the examples, the specific values were measured as follows.
(1) Intrinsic viscosity The intrinsic viscosity was calculated using an ortho-chlorophenol solution at 35 ° C as a solvent.
(2) Twist coefficient The twist coefficient was calculated by the following formula.
Twist factor = twist number [T / M] × (fineness [dtex] × 9/10) 1/2
(3) Fabric cover factor CF
The cover factor CF of the woven fabric was calculated from the following formula.
CF = (DWp / 1.1) 1/2 × MWp + (DWf / 1.1) 1/2 × MWf
However, DWp is the total warp fineness (dtex), MWp is the warp weave density (main / 2.54 cm), DWf is the total weft fineness (dtex), and MWf is the weft weave density (main / 2.54 cm).
(4) Lightness Index L Value of Fabric The fabric surface was measured with a spectroscopic light device (Gretag MacBeth Color-Eye 7000A). The L value indicates the lightness. The larger the value, the higher the lightness. The closer to 100, the lighter the color is, the closer to white, the closer to 0, the darker the color.
(5) Water absorption Water absorption was measured by the dropping method (wicking method) described in JIS L-1907.
(6) Texture (dry feeling)
Three testers evaluated by a sensory evaluation in three levels: “Dry feeling”, “Normal”, “No dry feeling”.
(7) Exposure ratio of the core polyester multifilament B in the cross section The cross section of the core-sheath type composite false twisted yarn is observed using an electron microscope, and the exposure angle of the core polyester multifilament B is measured. The total value was calculated by dividing by 360 and multiplying by 100.
(8) Exposure ratio of core polyester multifilament B in the yarn length direction The exposure ratio in the yarn length direction was determined by the formula.
Yarn length direction exposure ratio (%) = AB / (AA + AB) × 100
However, the core-sheath type composite false twisted yarn having a length of 3 mm was observed using an electron microscope as shown in FIG. 3, and the exposed area of the core polyester multifilament B was defined as AB, and the sheath polyester multifilament A was exposed. Let the area be AA.
[実施例1]
酸成分がモル比90/10のテレフタル酸及びイソフタル酸からなり、グリコール成分がエチレングリコールからなり、固有粘度が0.64dL/gで、酸化チタンを0.3重量%含有するポリエチテンテレフタレート系共重合ポリエステルを調製し、芯部ポリエステルマルチフィラメントB用ポリマーとした。
一方、固有粘度が0.64dL/gで酸化チタンを0.3重量%含有するポリエチレンテレフタレートを基質ポリマーとして、該基質ポリマーに、分子量50000、メルトインデックス9.0のシンジオタクテイックポリスチレンを前記基質ポリマーの重量対比1.5重量%添加し、鞘部ポリエステルマルチフィラメントA用ポリマーとした。
次いで、芯部ポリエステルマルチフィラメントB用として十字断面の吐出孔を有する口金を使用し、鞘部ポリエステルマルチフィラメントA用として丸断面の吐出孔を有する口金を使用し、常法の複合溶融紡糸混繊(紡糸温度288℃、引取り速度3200m/分)し、総繊度160dtex/36filの混繊原糸を得た。
[Example 1]
A polyethylene terephthalate copolymer comprising an acid component of terephthalic acid and isophthalic acid in a molar ratio of 90/10, a glycol component of ethylene glycol, an intrinsic viscosity of 0.64 dL / g, and containing 0.3% by weight of titanium oxide. Polymerized polyester was prepared and used as the core polyester multifilament B polymer.
On the other hand, polyethylene terephthalate having an intrinsic viscosity of 0.64 dL / g and containing 0.3% by weight of titanium oxide was used as a substrate polymer, and syndiotactic polystyrene having a molecular weight of 50000 and a melt index of 9.0 was added to the substrate polymer. The polymer for sheath polyester multifilament A was added by adding 1.5% by weight with respect to the weight of the polymer.
Next, using a die having a cross-sectional discharge hole for the core polyester multifilament B, and using a die having a round cross-section discharge hole for the sheath polyester multifilament A, a conventional composite melt-spun blend (Spinning temperature 288 ° C., take-up speed 3200 m / min) to obtain a mixed fiber yarn having a total fineness of 160 dtex / 36 fil.
次いで、該原糸を帝人製機HTS−15Vに掛け総繊度110dtex/36filの芯鞘型複合仮撚加工糸を得た。この加工糸を構成する鞘部の糸条(鞘部ポリエステルマルチフィラメントA)は総繊度60dtex/12fil(単糸繊度5.0dtex)、芯部の糸条(芯部ポリエステルマルチフィラメントB、単繊維横断面形状は十字型(異型))は総繊度50dtex/24fil(単糸繊度2.1dtex)となった。
次いで、該混繊糸に1950T/m(撚り係数19500)の撚糸を施し80℃で撚り止めセットを行った後、該混繊糸を経糸と緯糸に配して、経糸密度134本/2.54cm、緯糸密度134本/2.54cmにて平二重組織で製織した後、90℃で予備リラックス、120℃で液流リラックス、190℃でプレセット、アルカリ減量(減量率10%)を行い、黒の分散染料を用いて130℃で染色後、濃染剤(日本化薬社製カヤディーパー(商品名))をパッドし170℃でキュアリングしファイナルセットし仕上げて、カバーファクターCFが2726の織物(布帛)を得た。
Subsequently, the raw yarn was subjected to Teijin Seiki HTS-15V to obtain a core-sheath type composite false twisted yarn having a total fineness of 110 dtex / 36 fil. The sheath yarn (sheath polyester multifilament A) constituting this processed yarn has a total fineness of 60 dtex / 12 fil (single yarn fineness of 5.0 dtex), and the core yarn (core polyester multifilament B, single fiber crossing). As for the surface shape, the cross shape (atypical type) had a total fineness of 50 dtex / 24 fil (single yarn fineness of 2.1 dtex).
Next, the blended yarn was subjected to twisting of 1950 T / m (twisting coefficient 19500) and set to be twisted at 80 ° C., and then the blended yarn was arranged into warps and wefts to obtain a warp density of 134/2. After weaving with a flat double structure at 54cm and weft density of 134 / 2.54cm, pre-relax at 90 ° C, relax at liquid flow at 120 ° C, pre-set at 190 ° C, and reduce the alkali (weight loss rate 10%) After dyeing at 130 ° C. using a black disperse dye, padded with a deep dye (Kayadeper (trade name) manufactured by Nippon Kayaku Co., Ltd.), cured at 170 ° C., final set, and finished with a cover factor CF of 2726 A woven fabric (fabric) was obtained.
得られた織物の黒発色性を計測したところL値10.9となり、濃染性に優れていた。また、諸堅牢度は変退色、汚染とも4級以上で深色性と堅牢度に優れていた。風合いはドライ感があった。また、吸水性を測定したところ0.7秒未満の高吸水性を持っていた。さらに、好ましい張り腰、高反撥性、嵩性を有した織物となった。この織物を構成する芯鞘型複合仮撚加工糸を電子顕微鏡にて観察したところ、横断面における芯部ポリエステルマルチフィラメントBの露出比率が35%であり、糸長方向の芯部ポリエステルマルチフィラメントBの露出比率が25%であった。
次いで、該織物を用いて婦人用ブラックフォーマル衣料を得て着用したところ、濃染性および吸水性およびドライ感に優れるものであった。
When the black color developability of the resulting fabric was measured, the L value was 10.9. Further, the fastnesses were both grade 4 and higher, and the color fastness and fastness were excellent. The texture was dry. Further, when the water absorption was measured, it had a high water absorption of less than 0.7 seconds. Furthermore, it became a woven fabric having preferable tension, high rebound, and bulk. When the core-sheath type composite false twisted yarn constituting this woven fabric was observed with an electron microscope, the exposed ratio of the core polyester multifilament B in the cross section was 35%, and the core polyester multifilament B in the yarn length direction was found. The exposure ratio was 25%.
Next, when a black formal garment for women was obtained and worn using the woven fabric, it was excellent in deep dyeability, water absorption and dry feeling.
[比較例1]
実施例1において、芯部ポリエステルマルチフィラメントB用として丸断面の吐出孔を有する口金を使用し、かつ芯部ポリエステルマルチフィラメントBの繊度を50dtex/72fil(単糸繊度0.7dtex)に変更すること以外は実施例1と同様にした。
得られた織物の黒発色性を計測したところL値11.9となり、実施例1で得られたものより濃染性に劣っていた。また、諸堅牢度は変退色、汚染とも4級以上であった。風合いはドライ感がなかった。また、吸水性を測定したところ1.0秒以下となり吸水性は十分であった。しかし、張り腰は乏しく、嵩性のない織物であり、またドライタッチも発現しない結果となった。この織物を構成する芯鞘型複合仮撚加工糸を電子顕微鏡にて観察したところ、横断面における芯部ポリエステルマルチフィラメントBの露出比率が45%であり、糸長方向の芯部ポリエステルマルチフィラメントBの露出比率が35%であった。
[Comparative Example 1]
In Example 1, a die having a discharge hole having a round cross section is used for the core polyester multifilament B, and the fineness of the core polyester multifilament B is changed to 50 dtex / 72 fil (single yarn fineness 0.7 dtex). Except for this, the procedure was the same as in Example 1.
When the black color developability of the resulting fabric was measured, the L value was 11.9, which was inferior to the one obtained in Example 1 in terms of deep dyeing. Various fastnesses were grade 4 or higher for both discoloration and contamination. The texture did not feel dry. Further, when the water absorption was measured, it was 1.0 second or less and the water absorption was sufficient. However, the tension was low, the fabric was not bulky, and no dry touch was exhibited. When the core-sheath type composite false twisted yarn constituting this fabric was observed with an electron microscope, the exposed ratio of the core polyester multifilament B in the cross section was 45%, and the core polyester multifilament B in the yarn length direction was found. The exposure ratio was 35%.
[比較例2]
実施例1において、芯部ポリエステルマルチフィラメントB用として丸断面の吐出孔を有する口金を使用すること以外は実施例1と同様にした。
得られた織物の黒発色性を計測したところL値13.9となり、実施例1で得られたものより濃染性に劣っていた。また、諸堅牢度は変退色、汚染とも3級以上であった。風合いはドライ感がなかった。また、吸水性を測定したところ1.0秒より大きく、吸水性が不十分であった。さらに、張り腰はあるが、嵩性のない織物となった。この織物を構成する芯鞘型複合仮撚加工糸を電子顕微鏡にて観察したところ、横断面における芯部ポリエステルマルチフィラメントBの露出比率が45%であり、糸長方向の芯部ポリエステルマルチフィラメントBの露出比率が35%であった。
[Comparative Example 2]
In Example 1, it was carried out similarly to Example 1 except using the nozzle | cap | die which has a discharge hole of a round cross section for core part polyester multifilament B. FIG.
When the black color developability of the resulting fabric was measured, the L value was 13.9, which was inferior to the one obtained in Example 1 in the deep dyeing property. Moreover, various fastnesses were grade 3 or more in both discoloration and contamination. The texture did not feel dry. Further, when the water absorption was measured, it was longer than 1.0 seconds and the water absorption was insufficient. Furthermore, there was a woven fabric that had a tight waist but was not bulky. When the core-sheath type composite false twisted yarn constituting this fabric was observed with an electron microscope, the exposed ratio of the core polyester multifilament B in the cross section was 45%, and the core polyester multifilament B in the yarn length direction was found. The exposure ratio was 35%.

Claims (11)

  1. 芯鞘型複合仮撚加工糸を含む布帛であって、前記芯鞘型複合仮撚加工糸が、ポリエステルを主成分とし、かつポリメチルメタクリレート系ポリマーおよび/またはポリスチレン系ポリマーを含有する鞘部ポリエステルマルチフィラメントAと、ポリエステルからなり、かつその単繊維横断面形状が異型である芯部ポリエステルマルチフィラメントBとで構成されることを特徴とする、芯鞘型複合仮撚加工糸を含む布帛。   A sheath polyester containing a core-sheath type composite false twisted yarn, wherein the core-sheath type composite false twisted yarn contains polyester as a main component and contains a polymethyl methacrylate polymer and / or a polystyrene polymer. A fabric comprising a core-sheath type composite false twisted yarn, characterized in that it is composed of a multifilament A and a core polyester multifilament B made of polyester and having a monofilament cross-sectional shape that is atypical.
  2. 前記鞘部ポリエステルマルチフィラメントAにおいて、ポリメチルメタクリレート系ポリマーおよび/またはポリスチレン系ポリマーが重量基準で0.5〜3.0重量%添加されている、請求項1に記載の芯鞘型複合仮撚加工糸を含む布帛。   The core-sheath type compound false twist according to claim 1, wherein 0.5 to 3.0% by weight of polymethyl methacrylate polymer and / or polystyrene polymer is added to the sheath polyester multifilament A on a weight basis. A fabric containing processed yarn.
  3. 前記鞘部ポリエステルマルチフィラメントAにおいて、単糸繊度が3dtex以上である、請求項1または請求項2に記載の芯鞘型複合仮撚加工糸を含む布帛。   The fabric containing the core-sheath type composite false twisted yarn according to claim 1 or 2, wherein the sheath polyester multifilament A has a single yarn fineness of 3 dtex or more.
  4. 前記芯部ポリエステルマルチフィラメントBにおいて、単繊維横断面形状が、十字型、星型、卍型、およびT字型からなる群より選択されるいずれかである、請求項1〜3のいずれかに記載の芯鞘型複合仮撚加工糸を含む布帛。   In the said core part polyester multifilament B, the single fiber cross-sectional shape is any one selected from the group which consists of a cross shape, a star shape, a saddle shape, and a T-shape. A fabric comprising the described core-sheath type composite false twisted yarn.
  5. 前記芯部ポリエステルマルチフィラメントBにおいて、単糸繊度が3dtex以下である、請求項1〜4のいずれかに記載の芯鞘型複合仮撚加工糸を含む布帛。   The fabric containing the core-sheath type composite false twisted yarn according to any one of claims 1 to 4, wherein the core polyester multifilament B has a single yarn fineness of 3 dtex or less.
  6. 前記芯鞘型複合仮撚加工糸において、撚り係数10000〜30000の撚りが施されている、請求項1〜5のいずれかに記載の芯鞘型複合仮撚加工糸を含む布帛。
    ただし、撚り係数は下記式により定義する。
    撚り係数=撚数[T/M]×(繊度[dtex]×9/10)1/2
    The fabric containing the core-sheath type composite false twisted yarn according to any one of claims 1 to 5, wherein the core-sheath type composite false twisted yarn is twisted with a twist coefficient of 10,000 to 30,000.
    However, the twist coefficient is defined by the following formula.
    Twist factor = twist number [T / M] × (fineness [dtex] × 9/10) 1/2
  7. 前記芯鞘型複合仮撚加工糸の横断面において、芯部ポリエステルマルチフィラメントBの露出比率が50%以下である、請求項1〜6のいずれかに記載の芯鞘型複合仮撚加工糸を含む布帛。   The core-sheath type composite false twisted yarn according to any one of claims 1 to 6, wherein an exposure ratio of the core polyester multifilament B is 50% or less in a cross section of the core-sheath type composite false twisted yarn. Containing fabric.
  8. 布帛が織物であり、かつ該織物のカバーファクターCFが1200〜3000の範囲内である、請求項1〜7のいずれかに記載の芯鞘型複合仮撚加工糸を含む布帛。
    ただし、カバーファクターCFは下記式により定義する。
    CF=(DWp/1.1)1/2×MWp+(DWf/1.1)1/2×MWf
    ただし、DWpは経糸総繊度(dtex)、MWpは経糸織密度(本/2.54cm)、DWfは緯糸総繊度(dtex)、MWfは緯糸織密度(本/2.54cm)である。
    The fabric containing a core-sheath type composite false twisted yarn according to any one of claims 1 to 7, wherein the fabric is a woven fabric, and the cover factor CF of the woven fabric is in the range of 1200 to 3000.
    However, the cover factor CF is defined by the following formula.
    CF = (DWp / 1.1) 1/2 × MWp + (DWf / 1.1) 1/2 × MWf
    However, DWp is the total warp fineness (dtex), MWp is the warp weave density (main / 2.54 cm), DWf is the total weft fineness (dtex), and MWf is the weft weave density (main / 2.54 cm).
  9. 布帛の明度指数L値が11以下である、請求項1〜8のいずれかに記載の芯鞘型複合仮撚加工糸を含む布帛。   The fabric containing the core-sheath type composite false twisted yarn according to any one of claims 1 to 8, wherein the lightness index L value of the fabric is 11 or less.
  10. 布帛の吸水性がJIS L−1907に記載された滴下法(ウイッキング法)により測定して1秒以下である、請求項1〜9のいずれかに記載の芯鞘型複合仮撚加工糸を含む布帛。   The core-sheath type composite false twisted yarn according to any one of claims 1 to 9, wherein the water absorption of the fabric is 1 second or less as measured by a dropping method (wicking method) described in JIS L-1907. Fabric.
  11. 請求項1〜10のいずれかに記載された布帛を用いてなる、婦人用ブラックフォーマル衣料、パーテイドレス、紳士用スーツ、スラックス、およびスポーツ衣料からなる群より選択されるいずれかの繊維製品。   A textile product selected from the group consisting of black formal garments for women, party dresses, suits for men, slacks, and sports garments using the fabric according to any one of claims 1 to 10.
JP2009196868A 2009-08-27 2009-08-27 Fabrics and textile products including core-sheath type composite false twisted yarn Expired - Fee Related JP5324360B2 (en)