JP5150363B2 - 放射線照射場における腐食環境評価方法及び放射線照射場における腐食緩和方法 - Google Patents
放射線照射場における腐食環境評価方法及び放射線照射場における腐食緩和方法 Download PDFInfo
- Publication number
- JP5150363B2 JP5150363B2 JP2008133493A JP2008133493A JP5150363B2 JP 5150363 B2 JP5150363 B2 JP 5150363B2 JP 2008133493 A JP2008133493 A JP 2008133493A JP 2008133493 A JP2008133493 A JP 2008133493A JP 5150363 B2 JP5150363 B2 JP 5150363B2
- Authority
- JP
- Japan
- Prior art keywords
- dose rate
- amount
- radiation
- radiation dose
- relationship
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
δ=d/0.023Re0.8Sc0.4
ここで、Reはレイノルズ数、Scはシュミット数でありそれぞれは以下のように表される。
Re:レイノルズ数(Udν-1)
Sc: シュミット数(νD-1)
U:流速 (ms-1)
ν:動性粘度 (m2s-1)
d:代表径
Claims (5)
- 原子炉の放射線場の高温水に晒される構造材の腐食環境を、アノード電流とカソード電流の発生量によって変化する腐食電位を用いて評価する放射線照射場における腐食環境評価方法であって、
前記構造材に付着した触媒物質の作用で発生する電流量と放射線線量率との関係を予め求め、当該電流量と放射線線量率との関係を用いて、評価部位における放射線線量率に応じた前記アノード電流の発生量を推測し、
かつ、
前記構造材表面における前記高温水の拡散層中における放射線線量率と放射線分解生成物の濃度との関係を予め求め、当該放射線線量率と放射線分解生成物の濃度との関係を用いて、評価部位における放射線線量率に応じた前記カソード電流の発生量を推測する
ことを特徴とする放射線照射場における腐食環境評価方法。 - 請求項1記載の放射線照射場における腐食環境評価方法であって、
前記高温水の流速によって変化する前記拡散層の厚さに起因する当該拡散層内の放射線分解生成物の濃度変化と放射線線量率との関係を予め求め、当該放射線分解生成物の濃度変化と放射線線量率との関係を用いて、評価部位における放射線線量率に応じた前記カソード電流の発生量を推測する
ことを特徴とする放射線照射場における腐食環境評価方法。 - 請求項1又は2記載の放射線照射場における腐食環境評価方法であって、
前記構造材に付着した触媒物質の作用で発生する電流量と放射線線量率と触媒物質の量との関係を予め求め、当該電流量と放射線線量率と触媒物質の量との関係を用いて、評価部位に付着した触媒物質の量と評価部位における放射線線量率とに応じた前記アノード電流の発生量を推測する
ことを特徴とする放射線照射場における腐食環境評価方法。 - 原子炉の放射線場の高温水に晒される構造材の腐食環境を、アノード電流とカソード電流の発生量によって変化する腐食電位を用いて評価し、前記構造材の腐食を緩和する方法であって、
前記構造材に付着した触媒物質の作用で発生する電流量と放射線線量率と触媒物質の量との関係を予め求め、当該電流量と放射線線量率と触媒物質の量との関係を用いて、評価部位に付着した触媒物質の量と評価部位における放射線線量率とに応じた前記アノード電流の発生量を推測し、
かつ、
前記構造材表面における前記高温水の拡散層中における放射線線量率と放射線分解生成物の濃度との関係を予め求め、当該放射線線量率と放射線分解生成物の濃度との関係を用いて、評価部位における放射線線量率に応じた前記カソード電流の発生量を推測し、
推測された前記アノード電流と、推測された前記カソード電流とから求められる前記腐食電位に基づいて、前記構造材に付着させる触媒物質の量を決定することを特徴とする放射線照射場における腐食緩和方法。 - 請求項4記載の放射線照射場における腐食緩和方法であって、
前記高温水の流速によって変化する前記拡散層厚さに起因する拡散層内の放射線分解生成物の濃度変化と放射線線量率との関係を予め求め、当該放射線分解生成物の濃度変化と放射線線量率との関係を用いて、評価部位における放射線線量率に応じた前記カソード電流の発生量を推測する
ことを特徴とする放射線照射場における腐食緩和方法。