JP4912339B2 - 加飾性多層成形体 - Google Patents
加飾性多層成形体 Download PDFInfo
- Publication number
- JP4912339B2 JP4912339B2 JP2008059191A JP2008059191A JP4912339B2 JP 4912339 B2 JP4912339 B2 JP 4912339B2 JP 2008059191 A JP2008059191 A JP 2008059191A JP 2008059191 A JP2008059191 A JP 2008059191A JP 4912339 B2 JP4912339 B2 JP 4912339B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- copolymer
- acrylate
- polymer
- surface layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(A)アクリルゴムで変性されたアクリロニトリル−スチレン共重合体;
(B)アルキルアクリレートおよびアルキルメタクリレートからなる群から選択される少なくとも1種類のモノマーを重合してなる(メタ)アクリレート系重合体;および
(C)艶消し剤;
を含有する表面層を基材層上に有してなる加飾性多層成形体に関する。
成分(A)はアクリルゴムで変性されたアクリロニトリル−スチレン共重合体(以下、単に共重合体(A)という)である。
例えば、市販の「ユーエムジーウッド」(ユーエムジー・エービーエス株式会社製)が使用可能である。
成分(B)は、アルキルアクリレートおよびアルキルメタクリレートからなる群から選択される少なくとも1種類のモノマーを重合してなる(メタ)アクリレート系重合体(以下、単に重合体(B)という)であり、単独重合体であってもよいし、または共重合体であってもよい。
アルキルメタクリレートは単官能性のものであり、具体例として、例えば、メチルメタクリレート、エチルメタクリレートおよびイソプロピルメタクリレート等が挙げられる。
重合体(B)のMFR値は2〜40、特に5〜30が好ましい。
例えば、市販の「アクリペット」(三菱レイヨン株式会社製)、「スミペックス」(住友化学株式会社製)が使用可能である。
成分(C)は艶消し剤である。艶消し剤は、表面層に含有されることによって当該層表面を荒らして光沢を低減できる物質であれば特に限定されるものではなく、建築資材用多層成形体の分野で従来から使用されている有機系または無機系のいずれの艶消し剤も使用可能である。
成分(D)はいわゆる種剤であって、着色剤が樹脂中に分散されてなる粒子状のものである。そのような種剤を含有させることにより、実際の木材表面が有する木目柄と同等の適度な明瞭さで木目柄を有効に発現させ得る。
1≦M2−M1≦20、特に、2≦M2−M1≦15。
さらに、基材層の材質として、金属製芯材、無機系芯材又は有機系芯材も使用できる。
金属製芯材としては、ステンレス、アルミニウム、アルミニウム合金、亜鉛メッキ鋼等種々の金属が使用可能である。軽量性、加工性からすれば、好ましくはアルミニウム合金である。無機製芯材としては、セラミック材、発泡セラミック材、セメント系成形体等が使用可能である。有機系芯材としては、熱硬化性樹脂成形体、例えばポリウレタン成形体、エポキシ樹脂成形体等が使用可能であり、さらに、押出成形時の加熱温度の影響をあまり生じないのであれば、熱可塑性樹脂の成形体であっても良い。なお、上記金属製芯材、特にアルミ合金製芯材からなる基材層を用いる場合には、芯材からなる基材層と表面層との間に接着層を介在させるのが好ましい。
基材層を低発泡押出する場合には、上記の基材層の熱可塑性樹脂に発泡剤を配合する必要がある。発泡剤は押出温度で分解して気体を発生する固体状の発泡剤が好ましく、このような発泡剤として重炭酸ナトリウム、炭酸アンモニウム、アゾジカルボン酸アミド、ベンゼンスルホニルヒドラジド等を用いることができる。
中間層の厚さは通常、0.2〜2.0mmである。
表1に記載の成分からなる基材層および表面層のコンパウンド(樹脂組成物)を、図1に示す共押出成形装置において、それぞれ基材層用押出機(図1中、B)および表面層用押出機(図1中、A)から同時に押出し、ダイス内で積層して押出多層成形体を成形した。押出条件は次の通りである:
基材層用押出機:45φ、二軸押出機(押出温度 170〜180℃)
表面層用押出機:40φ、一軸押出機(押出温度 170〜180℃)
成形体形状:平板(8mm×120mm)
表面層厚みは0.3mmである。
ABS樹脂;東レ社製:「トヨラック」
塩ビ樹脂;信越化学社製
充填材;竹原化学工業社製 :タルク
ASA樹脂;ユーエムジー・エービーエス社製:「ユーエムジーウッド」、MFR=18
PMMA樹脂;三菱レイヨン社製:「アクリペット」、MFR=26
艶消し剤;三菱レイヨン社製:「メタブレン」
種剤;ユーエムジー・エービーエス社製:「ユーエムジーウッド」(ブラウン色顔料入り)、ABS樹脂(MFR=10))
得られた多層成形体の表面層を目視および手触りにて評価した。
(艶消し性)
艶を目視により評価した。
◎;光沢が十分に低減され、艶が全くなかった;
○;わずかに艶を有しているものの、実用上問題なかった;
×;明らかに艶を有しており、実用上問題があった。
爪で表面を引っ掻いたときの状態を目視により評価した。
◎;全く跡がつかなかった;
○;わずかに跡がつくが、実用上問題なかった;
×;跡がはっきりとわかり、実用上問題があった。
カーボンブラックを含む懸濁液を試験体表面に塗布し、60℃で1時間乾燥後、室温まで放冷し、流水にて汚れを落とした。室温にて乾燥し、試験前後の汚れの状態を目視により評価した。
◎;汚れが完全に除去できた;
○;汚れがほとんど残らなかった;
△;汚れがわずかに残ったが、実用上問題ないレベルまで除去できた;
×;汚れが水洗いでは除去できず、実用上問題があった。
木材特有の年輪模様(木目模様)を目視により評価した。
◎;木目柄が適度な不明瞭さで発現されていた;
○;木目柄が実用上問題のないレベルで発現されていた;
×;木目柄が明瞭すぎたり、または不明瞭すぎたりして、十分に表現されていなかった。
Claims (5)
- (A)アクリルゴムで変性されたアクリロニトリル−スチレン共重合体;
(B)アルキルアクリレートおよびアルキルメタクリレートからなる群から選択される少なくとも1種類のモノマーを重合してなる(メタ)アクリレート系重合体;
(C)有機系艶消し剤;および
(D)着色剤が樹脂中に分散されてなる種剤;
を含有する表面層を基材層上に有してなり、共重合体(A)と重合体(B)との含有比率が重量比(A/B)で45/55〜80/20である、艶のない木質感を備えた加飾性多層押出成形体。 - 艶消し剤の含有量が共重合体(A)および重合体(B)の合計量に対して1.0〜40重量%である請求項1に記載の加飾性多層押出成形体。
- 艶消し剤(C)がアルキルアクリレート−アルキルメタクリレート−スチレン共重合体、粒状ゴムからなる群から選択される1種類以上の物質である請求項1または2に記載の加飾性多層押出成形体。
- 基材層がアクリロニトリル−ブタジエン−スチレン共重合体を含む請求項1〜3のいずれかに記載の加飾性多層押出成形体。
- 種剤(D)の樹脂が、表面層を構成する共重合体(A)および重合体(B)の混合物よりメルトフローレート値が低い樹脂である請求項1〜4のいずれかに記載の加飾性多層押出成形体。