JP4793954B1 - 色素増感太陽電池 - Google Patents
色素増感太陽電池 Download PDFInfo
- Publication number
- JP4793954B1 JP4793954B1 JP2011031675A JP2011031675A JP4793954B1 JP 4793954 B1 JP4793954 B1 JP 4793954B1 JP 2011031675 A JP2011031675 A JP 2011031675A JP 2011031675 A JP2011031675 A JP 2011031675A JP 4793954 B1 JP4793954 B1 JP 4793954B1
- Authority
- JP
- Japan
- Prior art keywords
- thickness
- dye
- sealing portion
- electrolyte
- solar cell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
【解決手段】互いに対向する一対の電極1,2と、一対の電極1,2を連結する封止部4と、一対の電極1,2と封止部4とによって形成されるセル空間Sに充填される電解質3とを備えており、封止部4が、樹脂を含む樹脂封止部4Aを有し、樹脂封止部4Aが、電解質3から離れるにつれて厚さが減少する厚さ減少部14bを有し、厚さ減少部14bの傾斜面に沿って一対の電極1,2のうち傾斜面に対向する電極2に接触する色素増感太陽電池100。
【選択図】図2
Description
最大変形率(%)=100×(最大変位量/シート状電極の厚さ)
に基づいて算出される値を言う。従って、例えば厚さ0.04mmのシート状電極が上記のようにして荷重をかけることにより撓み、最大変位量が0.01mmとなった場合、最大変形率は25%となり、このシート状電極は「可撓性を有する」こととなる。
まず本発明に係る色素増感太陽電池の第1実施形態について図1〜図4を用いて説明する。図1は、本発明に係る色素増感太陽電池の第1実施形態を示す断面図、図2は、図1の部分拡大断面図、図3は、図2の厚さ増大部を示す部分拡大図、図4は、図2の厚さ減少部を示す部分拡大図である。
まず作用極1及び対極2を準備する。
作用極1は以下のようにして得ることができる(図5)。
一方、対極2は、以下のようにして得ることができる(図6)。
次に、図7及び図8に示すように、作用極1のうち透明導電膜7の表面上の部位であって多孔質酸化物半導体層8を包囲する第1環状部位C1に無機封止部4Bを形成する。具体的には、無機封止部4Bは、透明導電膜7の第1環状部位C1に集電配線11を形成した後、集電配線11を配線保護層12で被覆することによって得ることができる。
一方、図9及び図10に示すように、対極2の表面上の部位である第2環状部位C2に樹脂封止部4Aを形成する。樹脂封止部4Aを構成する樹脂としては、例えばアイオノマー、エチレン−ビニル酢酸無水物共重合体、エチレン−メタクリル酸共重合体、エチレン−ビニルアルコール共重合体などの熱可塑性樹脂、紫外線硬化樹脂、及び、ビニルアルコール重合体などが挙げられる。樹脂封止部4Aが熱可塑性樹脂からなる場合には、例えば熱可塑性樹脂からなる環状のシートを準備し、このシートを第2環状部位C2に配置し加熱溶融させることによって得ることができる。樹脂封止部4Aが紫外線硬化樹脂である場合には、樹脂封止部4Aは、紫外線硬化樹脂の前駆体である紫外線硬化性樹脂を対極2の第2環状部位C2に塗布することによって得ることができる。
次に、作用極1の多孔質酸化物半導体層8に光増感色素を担持させる。このためには、作用極1を、光増感色素を含有する溶液の中に浸漬させ、その色素を多孔質酸化物半導体層8に吸着させた後に上記溶液の溶媒成分で余分な色素を洗い流し、乾燥させることで、光増感色素を多孔質酸化物半導体層8に吸着させればよい。但し、光増感色素を含有する溶液を多孔質酸化物半導体層8に塗布した後、乾燥させることによって光増感色素を酸化物半導体多孔膜に吸着させることによっても、光増感色素を多孔質酸化物半導体層8に担持させることが可能である。
次に、図11に示すように、作用極1上であって無機封止部4Bの内側に電解質3を配置する。電解質3は、作用極1上であって無機封止部4Bの内側に注入したり、印刷したりすることによって得ることができる。
次に、図12に示すように、作用極1と対極2とを対向させて、無機封止部4Bと樹脂封止部4Aとを重ね合わせる。
次に、樹脂封止部4Aを、無機封止部4B及び対極2に接着させる。
次に、本発明に係る色素増感太陽電池の第2実施形態について図14を用いて説明する。図14は、本発明に係る色素増感太陽電池の第2実施形態を示す部分拡大断面図である。なお、図14において、第1実施形態と同一又は同等の構成要素には同一符号を付し、重複する説明を省略する。
はじめに、10cm×10cm×4mmのFTO基板を準備した。続いて、FTO基板の上に、ドクターブレード法によって酸化チタンペースト(Solaronix社製、Ti nanoixide
T/sp)を、その厚さが10μmとなるように塗布した後、熱風循環タイプのオーブンに入れて500℃で3時間焼成し、FTO基板上に多孔質酸化物半導体層を形成し、5cm×5cmの作用極を得た。
厚さ減少部に対して電解質側に、電解質から離れるにつれて厚さが増大する厚さ増大部をさらに設け、厚さ減少部及び厚さ増大部の最小厚さが20μm、最大厚さと最小厚さとの差が5μmとなるように且つ第1及び第2樹脂封止部として、エチレン−メタクリル酸共重合体であるニュクレル(三井・デュポンポリケミカル社製)を用いて封止部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、環状の加圧面を有し、環状の加圧面が深さ5μm、幅50μmの1つのV字状の溝で構成されているものを用いた。
2つの厚さ減少部と1つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が電解質に近づく方向に向かって交互に形成され、厚さ減少部及び厚さ増大部の最小厚さが20μm、最大厚さと最小厚さとの差が5μmとなるように封止部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、環状の加圧面を有し、環状の加圧面が深さ5μmで幅50μmの1つのV字状の環状溝とそれらの内側に環状溝に沿って形成された1つの切欠き面とで構成されているものを用いた。
2つの厚さ減少部と2つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が電解質に近づく方向に向かって交互に形成され且つ厚さ減少部及び厚さ増大部の最小厚さが20μm、最大厚さと最小厚さとの差が5μmとなるように封止部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、環状の加圧面を有し、環状の加圧面が深さ5μmで幅が50μmの2つのV字状の環状溝で構成されているものを用いた。
3つの厚さ減少部と3つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が電解質に近づく方向に向かって交互に形成され、厚さ減少部及び厚さ増大部の最小厚さが20μm、最大厚さと最小厚さとの差が5μmとなるように且つ第1樹脂封止部及び第2樹脂封止部として、エチレン−メタクリル酸共重合体であるニュクレル(三井・デュポンポリケミカル社製)を用いて封止部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、環状の加圧面を有し、環状の加圧面が深さ5μmで幅が50μmの3つのV字状の環状溝で構成されているものを用いた。
5つの厚さ減少部と5つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が電解質に近づく方向に向かって交互に形成され、厚さ減少部及び厚さ増大部の最小厚さが20μm、最大厚さと最小厚さとの差が5μmとなるように且つ第1樹脂封止部及び第2樹脂封止部として、エチレン−ビニル酢酸無水物共重合体であるバイネル(デュポン社製)を用いて封止部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、環状の加圧面を有し、環状の加圧面が深さ5μmで幅が50μmの5つのV字状の環状溝で構成されているものを用いた。
6つの厚さ減少部と5つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が電解質に近づく方向に向かって交互に形成され、厚さ減少部及び厚さ増大部の最小厚さが20μm、最大厚さと最小厚さとの差が5μmとなるように且つ第1樹脂封止部及び第2樹脂封止部として、エチレン−ビニル酢酸無水物共重合体であるバイネル(デュポン社製)を用いて封止部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、環状の加圧面を有し、環状の加圧面が深さ5μmで幅が50μmの5つのV字状の環状溝とそれらの内側に環状溝に沿って形成された1つの切欠き面とを有する加圧面を持ったものを用いた。
まず実施例1と同様にして作用極及び対極を準備した。
封止部を形成した後、UV硬化性樹脂である31x−101中にガラスを混入してなる樹脂組成物を、封止部と作用極との境界、封止部と対極との境界を覆うように塗布し、この樹脂組成物に紫外線を照射することによって被覆部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。
封止部を形成した後、UV硬化性樹脂である31x−101中にガラスを混入してなる樹脂組成物を、封止部と作用極との境界、封止部と対極との境界を覆うように塗布し、この樹脂組成物に紫外線を照射することによって被覆部を形成したこと以外は実施例4と同様にして色素増感太陽電池を作製した。
封止部を形成した後、以下のように被覆部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。
封止部を形成した後、以下のように被覆部を形成したこと以外は実施例3と同様にして色素増感太陽電池を作製した。
厚さ減少部及び厚さ増大部の最小厚さが20μmで、最大厚さと最小厚さとの差が5μmとなるように且つ第1及び第2樹脂封止部としてハイミランを用いて封止部を形成した後、以下のようにして被覆部を形成したこと以外は実施例2と同様にして色素増感太陽電池を作製した。
3つの厚さ減少部と2つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が、電解質に近づく方向に向かって交互に形成され、厚さ減少部及び厚さ増大部の最小厚さが40μmで、最大厚さと最小厚さとの差が5μmとなるように且つ第1樹脂封止部及び第2樹脂封止部として、エチレン−ビニル酢酸無水物共重合体であるバイネルを用いて封止部を形成し、その後、以下のようにして被覆部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。
厚さ減少部及び厚さ増大部の最小厚さが60μmで、最大厚さと最小厚さとの差が5μmとなるように且つ第1及び第2樹脂封止部として、エチレン−ビニル酢酸無水物共重合体であるバイネルを用いて封止部を形成した後、以下のようにして被覆部を形成したこと以外は実施例4と同様にして色素増感太陽電池を作製した。
厚さ減少部及び厚さ増大部の最小厚さが30μmで、最大厚さと最小厚さとの差が90μmとなるように封止部を形成したこと以外は実施例15と同様にして色素増感太陽電池を作製した。
厚さ減少部及び厚さ増大部の最小厚さが30μmで、最大厚さと最小厚さとの差が95μmとなるように封止部を形成したこと以外は実施例15と同様にして色素増感太陽電池を作製した。
厚さ減少部及び厚さ増大部の最小厚さが100μmで、最大厚さと最小厚さとの差が50μmとなるように封止部を形成したこと以外は実施例15と同様にして色素増感太陽電池を作製した。
3つの厚さ減少部と3つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が、電解質に近づく方向に向かって交互に形成され、厚さ減少部及び厚さ増大部は、最小厚さが60μmで、最大厚さと最小厚さとの差が5μmとなるように封止部を形成し、その後、以下のようにして被覆部を形成したこと以外は実施例8と同様にして色素増感太陽電池を作製した。
封止部における最小厚さと最大厚さとの差が1μmとなるように封止部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。
封止部における最小厚さと最大厚さとの差が1μmとなるように封止部を形成したこと以外は実施例3と同様にして色素増感太陽電池を作製した。
封止部における最小厚さと最大厚さとの差が1μmとなるように封止部を形成したこと以外は実施例9と同様にして色素増感太陽電池を作製した。
1つの厚さ減少部と1つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が、電解質に近づく方向に向かって交互に形成され、封止部における最小厚さと最大厚さとの差が1μmとなるように封止部を形成したこと以外は実施例11と同様にして色素増感太陽電池を作製した。
3つの厚さ減少部と3つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が、電解質に近づく方向に向かって交互に形成され、厚さ減少部及び厚さ増大部の最小厚さが40μm、最小厚さと最大厚さとの差が1μmとなるように封止部を形成すると共に、封止部を形成した後、以下のようにして被覆部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。
3つの厚さ減少部と3つの厚さ増大部とを有し、厚さ減少部と厚さ増大部が、電解質に近づく方向に向かって交互に形成され、厚さ減少部及び厚さ増大部の最小厚さが40μm、最小厚さと最大厚さとの差が1μmとなるように封止部を形成すると共に、封止部を形成した後、以下のようにして被覆部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。
PETフィルムの上にスパッタ法でFTO膜を形成した厚さ75μmの対極基板を用いたこと以外は実施例6と同様にして色素増感太陽電池を作製した。
PENフィルムの上にスパッタ法でFTO膜を形成した厚さ75μmの対極基板を用いたこと以外は実施例6と同様にして色素増感太陽電池を作製した。
厚さ減少部に対して電解質と反対側に、電解質から離れるにつれて厚さが増大する厚さ増大部をさらに設け、厚さ減少部及び厚さ増大部の最小厚さが20μm、最大厚さと最小厚さとの差が5μmとなるように且つ第1及び第2樹脂封止部として、エチレン−メタクリル酸共重合体であるニュクレル(三井・デュポンポリケミカル社製)を用いて封止部を形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、環状の加圧面を有し、環状の加圧面が高さ5μm、幅50μmの1つのクサビ状の突起で構成されているものを用いた。
1つの厚さ減少部と2つの厚さ増大部とを有し、電解質から離れるにつれて厚さが増大する厚さ増大部から電解質から離れる方向に向かって厚さ減少部と厚さ増大部が形成され、厚さ増大部及び厚さ減少部の最小厚さが20μm、最大厚さと最小厚さとの差が5μmとなるように封止部を形成したこと以外は実施例28と同様にして色素増感太陽電池を作製した。このとき真鍮製の枠状部材としては、環状の加圧面を有し、環状の加圧面が、深さ5μmで幅50μmの1つのV字状の溝とその外側にV字状の溝に沿って形成された1つの切欠き面とで構成されているものを用いた。
封止部を、最小厚さが5μmで、最小厚さと最大厚さとの差が0μmとなるように形成したこと以外は実施例1と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、枠状部材を平坦面上に、加圧面を平坦面側に向けて置いたときに、環状の加圧面の最内周縁も最外周縁も平坦面に接するように且つ加圧面が平坦面となるように加工された枠状部材を用いた。
封止部を、最小厚さが20μmで、最小厚さと最大厚さとの差が0μmとなるように形成したこと以外は実施例8と同様にして色素増感太陽電池を作製した。このとき、ガラス製の枠状部材としては、枠状部材を平坦面上に、加圧面を平坦面側に向けて置いたときに、環状の加圧面の最内周縁も最外周縁も平坦面に接するように且つ加圧面が平坦面となるように加工された枠状部材を用いた。
封止部を、最小厚さが40μmで、最小厚さと最大厚さとの差が0μmとなるように形成したこと以外は実施例2と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、枠状部材を平坦面上に、加圧面を平坦面側に向けて置いたときに、環状の加圧面の最内周縁も最外周縁も平坦面に接するように且つ加圧面が平坦面となるように加工された枠状部材を用いた。
封止部を、最小厚さが60μmで、最小厚さと最大厚さとの差が0μmとなるように形成したこと以外は実施例6と同様にして色素増感太陽電池を作製した。このとき、真鍮製の枠状部材としては、枠状部材を平坦面上に、加圧面を平坦面側に向けて置いたときに、環状の加圧面の最内周縁も最外周縁も平坦面に接するように且つ加圧面が平坦面となるように加工された枠状部材を用いた。
実施例1〜29及び比較例1〜4で得られた色素増感太陽電池について、光電変換効率(η0)を測定した。続いて、色素増感太陽電池について、大気圧下、40℃で、90%RHの高湿環境下で1000h放置した後の光電変換効率(η)も測定した。そして、下記式:
光電変換効率の保持率(%)=η/η0×100
に基づき、光電変換効率の保持率(光電変換保持率)を算出した。結果を表1に示す。
実施例1〜29及び比較例1〜4で得られた色素増感太陽電池について、1500hPaの低圧下、40℃で、90%RHの高湿環境下で1000h放置した後の光電変換効率(η)を測定し、上記と同様にして光電変換効率の保持率を算出した。結果を表1に示す。
実施例1〜29及び比較例1〜4で得られた色素増感太陽電池について、大気圧下、85℃で、85%RHの高湿環境下で1000h放置した後の光電変換効率(η)を測定し、上記と同様にして光電変換効率の保持率を算出した。結果を表1に示す。
2…対極(電極)
3…電解質
4…封止部
4A…樹脂封止部
4B…無機封止部
5…被覆部
13…作用極と封止部との境界
14…対極と封止部との境界
14a…厚さ増大部
14b…厚さ減少部
14c…傾斜面
14d…傾斜面
15…環状溝
100,200,300,400…色素増感太陽電池
S…セル空間
Claims (9)
- 互いに対向する一対の電極と、
前記一対の電極を連結する封止部と、
前記一対の電極と前記封止部とによって囲まれるセル空間に充填される電解質とを備えており、
前記封止部が、樹脂を含む樹脂封止部を有し、
前記樹脂封止部が、前記電解質から離れるにつれて厚さが減少する厚さ減少部を有し、前記厚さ減少部の傾斜面に沿って、前記一対の電極のうち前記傾斜面に対向する電極に接触すること
を特徴とする色素増感太陽電池。 - 前記樹脂封止部が、前記厚さ減少部に対して前記電解質と反対側に、前記電解質から離れるにつれて厚さが増大する厚さ増大部を更に有し、前記厚さ増大部の傾斜面に沿って、前記一対の電極のうち前記傾斜面に対向する電極に接触する請求項1に記載の色素増感太陽電池。
- 前記樹脂封止部が、前記厚さ増大部に対して前記電解質と反対側に、前記電解質から離れるにつれて厚さが減少する厚さ減少部を更に有し、前記厚さ減少部の傾斜面に沿って、前記一対の電極のうち前記傾斜面に対向する電極に接触する、請求項2に記載の色素増感太陽電池。
- 前記樹脂封止部が、前記厚さ減少部及び前記厚さ増大部をそれぞれ複数有し、
前記厚さ減少部及び前記厚さ増大部が、前記電解質に近づく方向に向かって交互に配列されている、請求項2に記載の色素増感太陽電池。 - 前記樹脂封止部の最大厚さが10μm以上である請求項1〜4のいずれか一項に記載の色素増感太陽電池。
- 前記厚さ減少部と前記電極との接触面と、前記厚さ増大部と前記電極との接触面とにより、前記電解質から離れる方向に交差するように延びる溝が形成されている、請求項2〜4のいずれか一項に記載の色素増感太陽電池。
- 前記一対の電極のうち少なくとも一方の電極が可撓性を有する、請求項1〜6のいずれか一項に記載の色素増感太陽電池。
- 前記一対の電極のうち一方の電極が、導電性基板と、前記導電性基板上に設けられる多孔質酸化物半導体層とを有し、
前記導電性基板の前記多孔質酸化物半導体層側の表面が平坦面であり、
前記厚さ減少部と前記一対の電極のうち他方の電極との接触面が、前記平坦面に対して傾斜している、請求項1〜7のいずれか一項に記載の色素増感太陽電池。 - 前記封止部に対して前記電解質と反対側に、前記封止部と前記一対の電極との境界を少なくとも覆う被覆部を更に備え、前記被覆部が樹脂を含む、請求項1〜8のいずれか一項に記載の色素増感太陽電池。