JP4533806B2 - Water-degradable sanitary paper - Google Patents
Water-degradable sanitary paper Download PDFInfo
- Publication number
- JP4533806B2 JP4533806B2 JP2005166271A JP2005166271A JP4533806B2 JP 4533806 B2 JP4533806 B2 JP 4533806B2 JP 2005166271 A JP2005166271 A JP 2005166271A JP 2005166271 A JP2005166271 A JP 2005166271A JP 4533806 B2 JP4533806 B2 JP 4533806B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- outer layer
- sanitary paper
- paper
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、トイレットペーパーのシートなどの水解性衛生紙に関する。 The present invention relates to a water-decomposable sanitary paper such as a toilet paper sheet.
トイレットペーパーのシートなどの水解性衛生紙は、直接肌に触れるものであることから、消費者から、柔らかさ、ふんわり感、滑らかさ、厚み感等といった官能性に優れるものが要求されている。 Since water-degradable sanitary paper such as toilet paper sheets directly touch the skin, consumers are required to have excellent sensory properties such as softness, softness, smoothness, and thickness.
一方、近年の温水洗浄便座の普及に伴い、トイレットペーパーのシートに要求される性能が変化してきている。すなわち、温水洗浄便座においてトイレットペーパーのシートを用いる主目的は、洗浄後の体表面に残った水をぬぐい取ることであるため、温水洗浄便座において使用されるトイレットペーパーのシートに最も要求されるものは吸水性である。そのため、従来より、このようなトイレットペーパーのシートには、体表面に残った水の全量を吸収し、かつシートに吸収した水分が裏抜けして手の側に付かないことが求められてきた。 On the other hand, the performance required for toilet paper sheets is changing along with the recent widespread use of warm water flush toilet seats. That is, the main purpose of using the toilet paper sheet in the warm water flush toilet seat is to wipe off the water remaining on the body surface after washing, so that the toilet paper sheet used in the warm water flush toilet seat is most required Is water-absorbing. Therefore, conventionally, such a toilet paper sheet has been required to absorb the total amount of water remaining on the body surface and to prevent the moisture absorbed in the sheet from getting through and sticking to the hand side. .
そこで、シートを重ねることによって生ずる空隙を利用することで吸水性を向上させ、１組のシートで必要な機能を果し得る温水洗浄便座に適したトイレットペーパーのシートが提案されている（例えば、特許文献１参照。）。
しかしながら、上記発明では、水解性衛生紙を重ね合わせると共に、衛生紙にエンボス加工を施して、表面積を拡大することにより、シートとシートの間の吸水力を確保して吸水性を向上させているが、エンボスの数が増えると、柔らかさや滑らかさが低下して肌触りが悪くなってしまうといった問題が生じる。また、衛生紙表面の柔らかさや滑らかさについての考慮がないため、排泄部に疾患のある使用者にとっては、使用上使いづらいという問題がある。 However, in the above invention, the water-degradable sanitary paper is overlaid and the sanitary paper is embossed to increase the surface area, thereby ensuring water absorption between the sheets and improving water absorption. When the number of embosses increases, the problem arises that the softness and smoothness are lowered and the touch becomes worse. Moreover, since there is no consideration about the softness and smoothness of the sanitary paper surface, there is a problem that it is difficult to use for a user who has a disease in the excretory part.
そこで、本発明の主たる課題は、吸水性を確保するとともに、裏抜け防止を確実に図り、かつ厚み感と柔軟性を与えることができる水解性衛生紙を提供することである。また、従たる課題は、柔らかくすることにより発生しやすくなる紙粉を低減した水解性衛生紙を提供することでもある。 Then, the main subject of this invention is providing the water-decomposable sanitary paper which can ensure a water absorption, can aim at prevention of a see-through, and can give a feeling of thickness and a softness | flexibility. Another problem is to provide a water-decomposable sanitary paper that reduces paper dust that tends to be generated by softening.
請求項１記載の発明は、３層の多層とされ、各層の米坪が１１〜２２ｇ／ｍ2、かつ各層の紙厚が６０〜２００μｍである水解性衛生紙であって、
該水解性衛生紙における基紙の原料は、合成パルプを除くパルプ繊維を使用し、
少なくとも一方の外層は吸液層とされ、セルロース、ヘミセルロース、親水性アセテートセルロース及び親水性不織布の少なくともいずれか１つを原料とし、
前記一方の外層以外の少なくともいずれかの層は、サイズ剤がパルプ絶乾質量に対する固形分質量比で０．０２〜０．０６％含まれる液透過抑制層とされ、
前記一方の外層の吸水量が１５０〜４００ｇ／ｍ2、かつこの一方の外層以外の少なくともいずれかの層の吸水量が１００〜３００ｇ／ｍ2であり、
少なくとも一方の外層の吸水時間と、この一方の外層以外の少なくともいずれかの層の吸水時間との比率が１：１５〜１：１．５とされた、
ことを特徴とする水解性衛生紙である。
The invention according to claim 1 is a water-decomposable sanitary paper having three layers, a basis weight of 11 to 22 g / m 2 for each layer, and a paper thickness of 60 to 200 μm for each layer,
The raw material of the base paper in the water-degradable sanitary paper uses pulp fibers excluding synthetic pulp,
At least one of the outer layers is a liquid absorbing layer, and at least one of cellulose, hemicellulose, hydrophilic acetate cellulose, and hydrophilic nonwoven fabric is used as a raw material,
At least one of the layers other than the one outer layer is a liquid permeation suppression layer in which a sizing agent is contained in an amount of 0.02 to 0.06% in a solid content ratio relative to the pulp dry weight,
The water absorption of the one outer layer is 150 to 400 g / m 2 , and the water absorption of at least one of the layers other than the one outer layer is 100 to 300 g / m 2 ;
The ratio of the water absorption time of at least one outer layer and the water absorption time of at least any one layer other than this one outer layer was 1:15 to 1: 1.5.
This is a water-decomposable sanitary paper.
請求項２記載の発明は、前記外層の長手方向の湿潤引張強度［ｃＮ／２５ｍｍ］（ＪＩＳ Ｐ ８１１３）が、１０〜５０である、請求項１記載の水解性衛生紙である。 The invention according to claim 2 is the water-decomposable sanitary paper according to claim 1 , wherein the outer layer has a wet tensile strength [cN / 25 mm] (JIS P 8113) in the longitudinal direction of 10-50.
（作用効果）
少なくとも一方の外層の吸水時間と、外層以外の少なくともいずれかの層の吸水時間とで、比率として１：１５〜１：１．５の差を持たせることで、まず外層において吸収した水分を敏速に内部に閉じ込めた後、外層よりも吸水時間の遅い層で水分を拡散させることができ、水解性衛生紙の厚み感及び吸水性を適正に確保した上で、水分の裏抜けを好適に図ることができる。
(Function and effect)
The water absorption time in at least one outer layer and the water absorption time in at least one of the layers other than the outer layer have a ratio of 1:15 to 1: 1.5 as a ratio, so that moisture absorbed in the outer layer is first quickly After being trapped inside, moisture can be diffused in a layer whose water absorption time is slower than that of the outer layer. Can do.
また、水解性衛生紙の構成として、各層の米坪が１１〜２２ｇ／ｍ2、かつ各層の紙厚が６０〜２００μｍとし、さらに、外層の吸水量が１５０〜４００ｇ／ｍ2、かつ外層以外の少なくともいずれかの層の吸水量が１００〜３００ｇ／ｍ2とすることが好ましい。 Moreover, as a constitution of the water-decomposable sanitary paper, the basis weight of each layer is 11 to 22 g / m 2 , the paper thickness of each layer is 60 to 200 μm, the water absorption amount of the outer layer is 150 to 400 g / m 2 , and other than the outer layer It is preferable that the water absorption of at least one of the layers is 100 to 300 g / m 2 .
さらに、外層の長手方向の湿潤引張強度［ｃＮ／２５ｍｍ］（ＪＩＳ Ｐ ８１１３）を、１０〜５０として、外層に水分拭き取りに耐えうるだけの引張強度を持たせることで、使用時の破れ等の不具合を防止することができる。 Furthermore, the wet tensile strength [cN / 25mm] (JIS P 8113) in the longitudinal direction of the outer layer is set to 10 to 50, and the outer layer has a tensile strength sufficient to withstand moisture wiping, so that tearing during use, etc. Problems can be prevented.
請求項３記載の発明は、ＪＩＳ Ｐ ４５０１に規定されるほぐれやすさの試験の結果が９０秒以下である、請求項１又は２記載の水解性衛生紙である。 Invention of Claim 3 is the water-decomposable sanitary paper of Claim 1 or 2 whose result of the test of the ease of loosening prescribed | regulated to JISP4501 is 90 seconds or less.
（作用効果）
ＪＩＳ Ｐ ４５０１に規定されるほぐれやすさの試験の結果が９０秒以下の構成とすることによって、使用後水洗トイレに廃棄しても、敏速に水解し、トイレの詰まりを防止することができる。
(Function and effect)
By adopting a configuration in which the result of the test for ease of loosening specified in JIS P 4501 is 90 seconds or less, even when discarded in a flush toilet after use, it is possible to quickly disintegrate and prevent clogging of the toilet.
請求項４記載の発明は、水平にシートを複数枚積み重ね、積み重ねた該シートの表面に水１ｍｌを滴下した際に、滴下された水分が浸透する枚数が１０枚以下である、請求項１乃至３のいずれか１項記載の水解性衛生紙である。 Fourth aspect of the present invention, stacking a plurality of sheets horizontally, when water was added dropwise 1ml the surface of the sheet stack, is less than ten number dripped moisture to penetrate, to claim 1 3. The water-decomposable sanitary paper according to any one of 3 above.
（作用効果）
水分の裏抜けを好適に防止することができる。
(Function and effect)
It is possible to suitably prevent moisture from getting through.
請求項５記載の発明は、前記外層に柔軟剤が添加された、請求項１乃至４のいずれか１項記載の水解性衛生紙である。 The invention according to claim 5 is the water-decomposable sanitary paper according to any one of claims 1 to 4 , wherein a softening agent is added to the outer layer.
（作用効果）
外層に柔軟剤を添加することにより、排泄部に疾患のある使用者にとって、患部を傷めることなく好適に水分の拭き取りができる。
(Function and effect)
By adding a softening agent to the outer layer, a user who has a disease in the excretory part can wipe off moisture suitably without damaging the affected part.
請求項６記載の発明は、前記外層以外の少なくともいずれかの層に、一過性湿潤紙力剤及び／又はカチオン澱粉が添加された、請求項１乃至５のいずれか１項記載の水解性衛生紙である。 The invention according to claim 6 is the water decomposability according to any one of claims 1 to 5 , wherein a transient wet paper strength agent and / or a cationic starch is added to at least one of the layers other than the outer layer. Sanitary paper.
（作用効果）
一過性湿潤紙力剤及び／又はカチオン澱粉を添加することにより、外層以外の少なくともいずれかの層の表面強度が上がるため、紙粉の発生を抑えることができる。
(Function and effect)
By adding the temporary wet paper strength agent and / or cationic starch, the surface strength of at least one of the layers other than the outer layer is increased, so that the generation of paper dust can be suppressed.
請求項７記載の発明は、ラミネートエンボス加工された、請求項１乃至６のいずれか１項記載の水解性衛生紙である。 The invention according to claim 7 is the water-decomposable sanitary paper according to any one of claims 1 to 6 , which is laminated embossed.
（作用効果）
ラミネートエンボス加工すると、厚み感を向上させると共に、表面積を拡大させることにより吸水性を向上させることができる。
(Function and effect)
Laminate embossing can improve the water absorption by increasing the surface area while improving the feeling of thickness.
本発明の水解性衛生紙によると、吸水性を確保するとともに、裏抜け防止を確実に図り、かつ厚み感と柔軟性を与えることができる。また、柔らかくすることにより発生しやすくなる紙粉を低減することができる。 According to the water-decomposable sanitary paper of the present invention, it is possible to ensure water absorption, reliably prevent back-through, and give a sense of thickness and flexibility. Moreover, the paper dust which becomes easy to generate | occur | produce by making soft can be reduced.
以下、本発明の実施の形態を説明する。
〔構造〕
本発明に係る水解性衛生紙１０は、図１及び図２に示すように、３層以上の多層となっている。ここで、注意を要するのは、本発明の「層」とは、いわゆる「プライ」を意味するものではない。つまり、水解性衛生紙１０は、図示例のように、例えば、多層抄きのように１プライであっても、図示はしないが、２プライ、３プライ、４プライ又はそれ以上の複数プライであってもよい。この際、各プライは、相互に重なり合う複数の層で構成されていても、各層単独で構成されていてもよい。
Embodiments of the present invention will be described below.
〔Construction〕
The water-decomposable
本発明に係る水解性衛生紙１０は、図１に示すように、一方の外層１１以外の少なくともいずれかの層が、図示例では、中層２１が、弱サイズ効果を効かせた浸透速度が遅い液透過抑制層となっている。これにより、外層を吸液層とした場合、一方の外層１１（例えば表層）に吸収（吸水）された水分Ｗの裏抜け（他方の外層１２（例えば裏層）への抜け）が防止され、水分が手についたりして不衛生であるとの問題が解決される。この際、図２に示すように、中層２１，２１を２層以上の複数層とし、これらを全て液透過抑制層とすることもできる。なお、本明細書では、水解性衛生紙１０の両表面を構成する層を、外層１１，１２、この外層１１，１２に挟まれる層を全て中層２１と表現している。
As shown in FIG. 1, the water-decomposable
〔基紙の原料等〕
本発明に係る水解性衛生紙において、基紙の原料は、特に限定されず、適宜の原料を使用することができるが、パルプ繊維（原料パルプ）は、木材パルプ、非木材パルプ、古紙パルプ、などから、より具体的には、砕木パルプ（ＧＰ）、ストーングランドパルプ（ＳＧＰ）、リファイナーグランドパルプ（ＲＧＰ）、加圧式砕木パルプ（ＰＧＷ）、サーモメカニカルパルプ（ＴＭＰ）、ケミサーモメカニカルパルプ（ＣＴＭＰ）、ブリーチケミサーモメカニカルパルプ（ＢＣＴＭＰ）等の機械パルプ（ＭＰ）、化学的機械パルプ（ＣＧＰ）、半化学的パルプ（ＳＣＰ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）、針葉樹晒クラフトパルプ（ＮＢＫＰ）等のクラフトパルプ（ＫＰ）、ソーダパルプ（ＡＰ）、サルファイトパルプ（ＳＰ）、溶解パルプ（ＤＰ）等の化学的パルプ（ＣＰ）、脱墨パルプ（ＤＩＰ）、ウエストパルプ（ＷＰ）等の古紙パルプ、かすパルプ（ＴＰ）、木綿、アマ、麻、黄麻、マニラ麻、ラミー等を原料とするぼろパルプ、わらパルプ、エスパルトパルプ、バガスパルプ、竹パルプ、ケナフパルプ等の茎稈パルプ、靭皮パルプ等の補助パルプなどから、一種又は数種を適宜選択して使用する。
[Raw materials for base paper]
In the hydrolyzable sanitary paper according to the present invention, the raw material of the base paper is not particularly limited, and an appropriate raw material can be used. Pulp fibers (raw pulp) are wood pulp, non-wood pulp , waste paper pulp, etc. More specifically, groundwood pulp (GP), stone ground pulp (SGP), refiner ground pulp (RGP), pressurized groundwood pulp (PGW), thermomechanical pulp (TMP), chemithermomechanical pulp (CTMP) , Bleached chemical thermomechanical pulp (BCTMP) and other mechanical pulp (MP), chemical mechanical pulp (CGP), semi-chemical pulp (SCP), hardwood bleached kraft pulp (LBKP), softwood bleached kraft pulp (NBKP), etc. Kraft pulp (KP), soda pulp (AP), sulfite pulp (SP), dissolved pulp Flop (DP) chemical pulp (CP) such as, deinking pulp (DIP), West pulp (WP), etc. of waste paper pulp, cake pulp (TP), cotton, flax, hemp, jute, Manila hemp, raw materials ramie, etc. One or several kinds of rag pulp, straw pulp, esparto pulp, bagasse pulp, bamboo pulp, kenaf pulp, and other auxiliary pulps such as bast pulp are selected and used.
パルプ繊維等の原料は、例えば、公知の抄紙工程、具体的には、ワイヤパート、プレスパート、ドライヤパート、サイズプレス、カレンダパート等を経るなどして、基紙とする。この抄紙に際しては、例えば、分散剤、苛性ソーダ、アンモニア水等のｐＨ調整剤、消泡剤、防腐剤、蛍光染料、離型剤、耐水化剤、流動変性剤、歩留まり向上剤などの適宜の薬品を添加することができる。 Raw materials such as pulp fibers are used as a base paper through, for example, a known papermaking process, specifically, a wire part, a press part, a dryer part, a size press, a calendar part, and the like. In this papermaking, for example, suitable chemicals such as a dispersant, caustic soda, aqueous ammonia and other pH adjusters, antifoaming agents, preservatives, fluorescent dyes, mold release agents, water resistance agents, flow modifiers, yield improvers, etc. Can be added.
ただし、吸液層は、セルロース、ヘミセルロース、親水性アセテートセルロース及び親水性不織布の少なくともいずれか１つが原料とされているのが好ましい。 However, it is preferable that at least one of cellulose, hemicellulose, hydrophilic acetate cellulose, and hydrophilic nonwoven fabric is used as a raw material for the liquid absorption layer.
一方、液透過抑制層は、フィルム、撥水性不織布及びアセテートセルロースの少なくともいずれか１つが原料とされているのが好ましい。もっとも、液透過抑制層が、パルプ繊維を原料とする場合も、サイズ剤を、パルプ絶乾質量に対する固形分質量比で０．０２〜０．０６％含むと好ましいものとなり、０．０３〜０．０５％含むとより好ましいものとなる。サイズ剤の配合量が、０．０２質量％未満であると、液の裏抜けを十分に低減することができなくなる。他方、サイズ剤の配合量が、０．０６質量％を超えると、撥水性が強くなり過ぎるとの問題が生じる。 On the other hand, the liquid permeation suppression layer is preferably made from at least one of a film, a water-repellent nonwoven fabric, and acetate cellulose. However, even when the liquid permeation suppression layer uses pulp fibers as a raw material, it becomes preferable that the sizing agent is contained in an amount of 0.02 to 0.06% in terms of the solid content to the absolute dry mass of the pulp. .05% is more preferable. If the blending amount of the sizing agent is less than 0.02% by mass, it is impossible to sufficiently reduce the back-through of the liquid. On the other hand, when the compounding quantity of a sizing agent exceeds 0.06 mass%, the problem that water repellency becomes too strong will arise.
サイズ剤としては、例えば、アルキルケテンダイマー、アルケニル無水コハク酸、無水ステアリン酸等の中性サイズ剤、けん化天然ロジン、強化ロジン等の酸性サイズ剤などを、使用することができる。 As the sizing agent, for example, a neutral sizing agent such as alkyl ketene dimer, alkenyl succinic anhydride, and stearic anhydride, an acidic sizing agent such as saponified natural rosin, and reinforced rosin can be used.
〔吸水時間〕
本発明における水解性衛生紙の吸水時間は、ＪＩＳ Ｐ ８１１１の条件下で、次の方法で測定されるものである。すなわち、先ずサンプルシートをコップの口に載せ、サンプルの周縁部を輪ゴムでコップの口に固定する。次に、スポイトを用いて水を１滴（５μｌ）サンプルの上に高さ１ｃｍの位置から落とし、水滴が落下してからサンプル中に完全に吸い込まれるまでの時間をストップウォッチで測定し、吸水時間（秒／１滴）とする。ここで、水滴を真上ではなく斜め（垂直に対して４５度の傾斜）から見たときに光が反射しなくなったと判断されたとき、サンプル中に完全に吸い込まれたと判断するものとする。
[Water absorption time]
The water absorption time of the water-decomposable sanitary paper in the present invention is measured by the following method under the conditions of JIS P8111. That is, first, the sample sheet is placed on the cup mouth, and the peripheral edge of the sample is fixed to the cup mouth with a rubber band. Next, use a dropper to drop 1 drop (5 μl) of water onto the sample from a height of 1 cm, measure the time from when the drop falls until it is completely sucked into the sample with a stopwatch. Time (second / drop). Here, when it is determined that the light is not reflected when the water droplet is viewed not obliquely but obliquely (at an inclination of 45 degrees with respect to the vertical), it is determined that the water has been completely sucked into the sample.
これに基づいて、外層及び中層を、各々単独で測定した際の吸水時間の比率が１：１５〜１：１．５となることが好ましい。一方、外層の吸水時間を１としたとき、中層の吸水時間が１５超である場合は、中層での水分吸収が追いつかず拡散の方が主体となり、中層の表面上に水分が留まり、また、外層に逆戻りするため、吸水性を確保するには不十分となってしまう。他方、外層の吸水時間を１としたとき、中層の吸水時間が１．５未満である場合は、水分の垂直方向の浸透が早くなり、他方の外層まで水分が浸透してしまい、裏抜けする恐れがある。 Based on this, it is preferable that the ratio of the water absorption time when the outer layer and the middle layer are measured independently is from 1:15 to 1: 1.5. On the other hand, when the water absorption time of the outer layer is set to 1, when the water absorption time of the middle layer is more than 15, moisture absorption in the middle layer cannot catch up and the diffusion is mainly, moisture remains on the surface of the middle layer, Since it returns to the outer layer, it is insufficient to ensure water absorption. On the other hand, when the water absorption time of the outer layer is set to 1, if the water absorption time of the middle layer is less than 1.5, the moisture permeates in the vertical direction quickly, and the water penetrates to the other outer layer, so that it penetrates. There is a fear.
〔吸水量〕
吸液層である外層の吸水量が１５０〜４００ｇ／ｍ2となるのが好ましい。なぜなら、１５０ｇ／ｍ2未満では、外層に水分が留まり、吸水性を確保するには不十分であるからである。また、４００ｇ／ｍ2超では、吸水性を確保する上では優れるが、使用時の手の圧力により、水分が逆戻りする恐れがあるためである。
[Water absorption]
It is preferable that the water absorption amount of the outer layer as the liquid absorption layer is 150 to 400 g / m 2 . This is because if it is less than 150 g / m 2 , moisture remains in the outer layer, which is insufficient to ensure water absorption. On the other hand, if it exceeds 400 g / m 2 , it is excellent in securing water absorption, but it is because there is a risk that the moisture may be reversed due to hand pressure during use.
液透過抑制層である中層の吸水量が１００〜３００ｇ／ｍ2となるのが好ましい。なぜなら、１５０ｇ／ｍ2未満では、外層に水分が留まり、吸水性を確保するには不十分であるからである。また、３００ｇ／ｍ2超では、吸水性を確保する上では優れるものの、使用時の手の圧力により、水分が逆戻りする恐れがあるためである。 The water absorption amount of the middle layer which is the liquid permeation suppression layer is preferably 100 to 300 g / m 2 . This is because if it is less than 150 g / m 2 , moisture remains in the outer layer, which is insufficient to ensure water absorption. Further, if it exceeds 300 g / m 2 , it is excellent in securing water absorption, but there is a risk that the moisture may be reversed due to hand pressure during use.
〔坪量〕
本発明に係る水解性衛生紙におけるトイレットペーパーの各層の坪量は、ＪＩＳ Ｐ ８１２４の坪量測定方法において、１１〜２２ｇ／ｍ2となるのが好ましい。なぜなら、１１ｇ／ｍ2未満では、トイレットペーパーの柔らかさの向上の観点からは好ましものの、トイレットペーパーとしての強度を適正に確保することができないためである。また、２２ｇ／ｍ2超では、トイレットペーパーが硬くなりすぎて、トイレットペーパーの肌触りが悪化するためである。
[Basis weight]
The basis weight of each layer of the toilet paper in the water-decomposable sanitary paper according to the present invention is preferably 11 to 22 g / m 2 in the basis weight measurement method of JIS P 8124. This is because if it is less than 11 g / m 2, it is preferable from the viewpoint of improving the softness of the toilet paper, but the strength of the toilet paper cannot be ensured properly. Further, if it exceeds 22 g / m 2 , the toilet paper becomes too hard and the touch of the toilet paper is deteriorated.
〔紙厚〕
各層の紙厚は、６０〜２００μｍとなるのが好ましい。なぜなら、６０μｍ未満では、トイレットペーパーの柔らかさの向上の観点からは好ましいものの、トイレットペーパーとしての強度を適正に確保することができないためである。また、２００μｍ超では、トイレットペーパーが硬くなりすぎて、トイレットペーパーの肌触りが悪化するだけでなく、使用時にゴワツキ感が生じるためである。
[Paper thickness]
The paper thickness of each layer is preferably 60 to 200 μm. This is because the thickness of less than 60 μm is preferable from the viewpoint of improving the softness of the toilet paper, but the strength as the toilet paper cannot be ensured properly. On the other hand, if it exceeds 200 μm, the toilet paper becomes too hard and the touch of the toilet paper is not only deteriorated, but also a feeling of tingling is generated during use.
なお、紙厚の測定方法としては、ＪＩＳ Ｐ ８１１１の条件下で、ダイヤルシックネスゲージ（厚み測定器）「ＰＥＡＣＯＣＫ Ｇ型」（尾崎製作所製）を用いて測定するものとする。具体的には、プランジャーと測定台の間にゴミ、チリ等がないことを確認してプランジャーを測定台の上におろし、前記ダイヤルシックネスゲージのメモリを移動させてゼロ点を合わせ、次いで、プランジャーを上げて試料（トイレットペーパー）を試験台の上におき、プランジャーをゆっくりと下ろしそのときのゲージを読み取る。このとき、プランジャーをのせるだけとする。なお、紙厚は測定を１０回行って得られる平均値とする。
In addition, as a measuring method of paper thickness, it shall measure using the dial thickness gauge (thickness measuring device) "PEACOCK G type" (made by Ozaki Seisakusho) on the conditions of JISP8111. Specifically, confirm that there is no dust, dust, etc. between the plunger and the measuring table, lower the plunger on the measuring table, move the memory of the dial thickness gauge to adjust the zero point, and then Then, raise the plunger and place the sample (toilet paper) on the test table, slowly lower the plunger and read the gauge at that time. At this time, only the plunger is placed. The paper thickness is an average value obtained by performing
〔引張強度〕
本発明に係る水解性衛生紙におけるトイレットペーパーのシートは、当該トイレットペーパーの製造工程において、所定量の湿潤紙力増強剤が添加されているものである。ここで、ＪＩＳ Ｐ ８１１３の引張試験方法において、湿潤状態における当該トイレットペーパーの長手方向の引張強度［ｃＮ／２５ｍｍ］（湿潤紙力）が、１０〜５０となるのが好ましい。なぜなら、１０未満では、加工の際の糊（例えば、水系の糊）の塗布において衛生紙が破れてしまい、糊の塗布を適正に行うことが困難となるからである。また、５０超では、水解性が悪くなって商品価値が低下することとなるからである。よって、トイレットペーパーの長手方向の湿潤引張強度［ｃＮ／２５ｍｍ］を１０〜５０とすることにより、湿潤状態における紙力が適正に確保されたトイレットペーパーを提供することができる。
[Tensile strength]
The sheet of toilet paper in the water-decomposable sanitary paper according to the present invention is one in which a predetermined amount of wet paper strength enhancer is added in the manufacturing process of the toilet paper. Here, in the tensile test method of JIS P 8113, the tensile strength [cN / 25 mm] (wet paper strength) in the longitudinal direction of the toilet paper in a wet state is preferably 10 to 50. This is because if it is less than 10, the sanitary paper is torn during the application of glue (for example, water-based glue) during processing, and it is difficult to properly apply the glue. On the other hand, if it exceeds 50, the water decomposability deteriorates and the commercial value decreases. Therefore, by setting the wet tensile strength [cN / 25 mm] in the longitudinal direction of the toilet paper to 10 to 50, it is possible to provide toilet paper in which paper strength in a wet state is appropriately secured.
なお、引張強度の測定方法としては、ＪＩＳ Ｐ ８１１３において、例えば、筆等の所定の水分付与手段を用いてトイレットペーパーを濡らした状態で行う方法が挙げられる。 In addition, as a measuring method of tensile strength, the method performed in the state where the toilet paper was wetted using predetermined water | moisture-content provision means, such as a brush, in JISP8113 is mentioned, for example.
添加する湿潤紙力増強剤としては、例えば、ポリアミドポリアミンエピクロルヒドリン樹脂、尿素ホルムアルデヒド樹脂、メラミンホルムアルデヒド樹脂等が挙げられる。 Examples of the wet paper strength enhancer to be added include polyamide polyamine epichlorohydrin resin, urea formaldehyde resin, and melamine formaldehyde resin.
また、外層以外の少なくともいずれかの層に、抄紙の段階で一過性湿潤紙力剤及び／又はカチオン澱粉を添加することが好ましく、好適には０．５〜８．０ｋｇ／トン（パルプトン）添加することが望ましい。一方、８．０ｋｇ／トン（パルプトン）を超えると、紙力が強すぎ、使用後水洗トイレに廃棄した際の水解性の阻害要因となる。他方、０．５ｋｇ／トン（パルプトン）未満であると、表面強度が悪いため、表面から突出するセルロース繊維が毛羽立ち、結果セルロース繊維の固まりである紙粉が発生しやすくなる。 Further, it is preferable to add a temporary wet paper strength agent and / or a cationic starch to at least one of the layers other than the outer layer, preferably 0.5 to 8.0 kg / ton (pulp ton). It is desirable to add. On the other hand, if it exceeds 8.0 kg / ton (pulp ton), the paper strength is too strong, which becomes a hindrance to water disintegration when discarded in a flush toilet after use. On the other hand, if it is less than 0.5 kg / ton (pulp ton), the surface strength is poor, so that the cellulose fibers protruding from the surface become fluffy, and as a result, paper powder that is a lump of cellulose fibers tends to be generated.
〔水解性〕
本発明に係る水解性衛生紙におけるトイレットペーパーの水解性は、ＪＩＳ Ｐ ４５０１で規定される、ほぐれやすさの試験方法における結果が９０秒以下が好ましい。９０秒を超えると、使用後水洗トイレに廃棄しても水解が遅く、トイレに詰まる恐れが生じるからである。
[Water disintegration]
As for the water decomposability of the toilet paper in the water-decomposable sanitary paper according to the present invention, the result of the test method for ease of loosening defined by JIS P 4501 is preferably 90 seconds or less. This is because if it exceeds 90 seconds, even if it is discarded in a flush toilet after use, water disintegration is slow and the toilet may be clogged.
〔水分浸透度〕
トイレットペーパーの水分浸透度は、水平に上記構成のトイレットペーパーのシートを複数枚（プライ）積み重ね、積み重ねた該シートの表面に水１ｍｌを滴下した際に、滴下された水分が浸透する枚数が１０枚以下であることが好ましい。
[Moisture penetration]
The water permeability of the toilet paper is such that when a plurality of sheets (ply) of toilet paper having the above-mentioned configuration are stacked horizontally and 1 ml of water is dropped on the surface of the stacked sheets, the number of the permeated water drops is 10 It is preferable that the number is not more than one.
ここで、水分浸透度の具体的な測定方法としては、３プライのトイレットペーパーを１組として、これを順次積み重ねていき、少なくとも１０組の積み重ねの試料を用意する。この試料を水平の台に設置する。次いで１ｍｌの水をスポイドで吸引し、スポイドの先が試料表面に接触しない程度の高さから１ｍｌの水を滴下する。完全に水が試料に吸収されたことを確認後、水により湿潤している層の枚数を上から数えていくものである。 Here, as a specific method for measuring moisture penetration, one set of three-ply toilet paper is sequentially stacked, and at least 10 sets of stacked samples are prepared. Place this sample on a horizontal platform. Next, 1 ml of water is sucked with a spoid, and 1 ml of water is dropped from such a height that the tip of the spoid does not contact the sample surface. After confirming that water has been completely absorbed by the sample, the number of layers wetted by water is counted from above.
水が浸透する枚数が１０枚以下としたのは、先に記載した吸収時間の比率に基づく実使用上の水分の裏抜けの程度を実験値で証明するためであり、１０枚を超えるものは、実質上、吸収時間の比率を逸脱したものとなるからである。 The reason why the number of water permeated was 10 or less was to prove the degree of moisture penetration in actual use based on the ratio of the absorption time described above with experimental values. This is because it substantially deviates from the ratio of absorption time.
〔ソフトネス〕
本発明に係る水解性衛生紙におけるトイレットペーパーのシートのソフトネス（ＪＩＳ Ｌ１０９６ 曲げ合成）は、１．５〜３．５ｇであることが好ましい。なぜなら、１．５ｇ未満では、トイレットペーパーが柔らかくなりすぎて厚み感の確保が困難となるためである。また、３．５ｇ超では、トイレットペーパーが硬くなりすぎて肌触りが悪化するためである。
[Softness]
The softness (JIS L1096 bending synthesis) of the toilet paper sheet in the water-decomposable sanitary paper according to the present invention is preferably 1.5 to 3.5 g. This is because if it is less than 1.5 g, the toilet paper becomes too soft and it is difficult to ensure a sense of thickness. On the other hand, if it exceeds 3.5 g, the toilet paper becomes too hard and the touch becomes worse.
ここで、ソフトネスとは、１０ｃｍ巾の衛生薄葉紙を端子によって巾５．０ｍｍの隙間に押し込んだときの抵抗値（縦横の平均値）であり、値が小さいほど、柔らかいことを意味する。本明細書でソフトネス は、ハンドルオメータ法（ＪＩＳ Ｌ−１０９６ Ｅ法）によって測定した値をいう。ソフトネスは、例えば、坪量、層の数、層を形成する繊維・フィルム等の種類、融着加工条件などを変化させることにより、調節することができる。 Here, softness is a resistance value (average value in length and width) when a sanitary thin paper having a width of 10 cm is pushed into a gap having a width of 5.0 mm by a terminal, and means that the smaller the value is, the softer it is. In this specification, softness refers to a value measured by the handle ohm method (JIS L-1096 E method). The softness can be adjusted, for example, by changing the basis weight, the number of layers, the types of fibers and films forming the layers, the fusing process conditions, and the like.
〔柔軟剤〕
本発明に係る水解性衛生紙においては、外層に柔軟剤を添加することが好ましい。柔軟剤の例としては、界面活性剤系の柔軟剤であり、その柔軟剤としては、アニオン系界面活性剤、非イオン系界面活性剤、カチオン系界面活性剤および両性イオン界面活性剤のなかから適宜選択して用いることができる。
〔Softener〕
In the water-decomposable sanitary paper according to the present invention, it is preferable to add a softening agent to the outer layer. Examples of softeners are surfactant-based softeners, which include anionic surfactants, nonionic surfactants, cationic surfactants and zwitterionic surfactants. It can be appropriately selected and used.
アニオン系界面活性剤としては、カルボン酸塩系、スルホン酸塩系、硫酸エステル塩系、燐酸エステル塩系などを用いることができる。特にアルキル燐酸エステル塩が好ましい。 As the anionic surfactant, carboxylate, sulfonate, sulfate ester, phosphate ester, and the like can be used. An alkyl phosphate ester salt is particularly preferable.
非イオン系界面活性剤としては、ソルビタン脂肪酸エステル、ジエチレングリコールモノステアレート、ジエチレングリコールモノオレエート、グリセリルモノステアレート、グリセリルモノオレート、プロピレングリコールモノステアレートなどの多価アルコールモノ脂肪酸エステル、Ｎ−（３−オレイロシキ−２−ヒドロキシプロピル）ジエタノールアミン、ポリオキシエチレン硬化ヒマシ油、ポリオキシエチレンソルビット密ロウ、ポリオキシエチレンソルビタンセスキステアレート、ポリオキシエチレンモノオレエート、ポリオキシエチレンモノラウレート、ポリオキシエチレンセチルエーテル、ポリオキシエチレンラウリルエーテルなどを用いることができる。 Nonionic surfactants include polysorbic alcohol monofatty acid esters such as sorbitan fatty acid ester, diethylene glycol monostearate, diethylene glycol monooleate, glyceryl monostearate, glyceryl monooleate, propylene glycol monostearate, N- (3 -Oleirosoxy-2-hydroxypropyl) diethanolamine, polyoxyethylene hydrogenated castor oil, polyoxyethylene sorbit dense wax, polyoxyethylene sorbitan sesquistearate, polyoxyethylene monooleate, polyoxyethylene monolaurate, polyoxyethylene cetyl Ether, polyoxyethylene lauryl ether and the like can be used.
カチオン系界面活性剤としては、第４級アンモニウム塩、アミン塩、またはアミンなどをもちいることができる。また、両性イオン界面活性剤としては、カルボキシ、スルホネート、サルフェートを含有する第２級または第３級アミンの脂肪族誘導体、または複素環式第２級または第３級アミンの脂肪族誘導体などを用いることができる。 As the cationic surfactant, a quaternary ammonium salt, an amine salt, an amine, or the like can be used. In addition, as the zwitterionic surfactant, an aliphatic derivative of a secondary or tertiary amine containing carboxy, sulfonate, sulfate, an aliphatic derivative of a heterocyclic secondary or tertiary amine, or the like is used. be able to.
本発明の柔軟剤としては、カチオン系界面活性剤を使用するのが望ましい。このカチオン系界面活性剤としては、第４級アンモニウム塩、アミン塩、またはアミンなどをもちいることができる。また、両性イオン界面活性剤としては、カルボキシ、スルホネート、サルフェートを含有する第２級または第３級アミンの脂肪族誘導体、または複素環式第２級または第３級アミンの脂肪族誘導体などを用いることができる。 As the softener of the present invention, it is desirable to use a cationic surfactant. As the cationic surfactant, a quaternary ammonium salt, an amine salt, an amine, or the like can be used. In addition, as the zwitterionic surfactant, an aliphatic derivative of a secondary or tertiary amine containing carboxy, sulfonate, sulfate, an aliphatic derivative of a heterocyclic secondary or tertiary amine, or the like is used. be able to.
これらの柔軟剤のシートへの添加は、内添でも外添でもよい。また、薬液に対して、陰イオン界面活性剤、香料、着色料、防腐剤、酸化防止剤などの副次的添加剤を、１％以下の割合で添加することができる。 These softeners may be added internally or externally. In addition, secondary additives such as anionic surfactants, fragrances, colorants, preservatives, and antioxidants can be added to the chemical solution at a ratio of 1% or less.
柔軟剤を添加することにより、表面の柔らかさや滑らかさが発現し、肌触りがよくなる。特に、排泄部に疾患のある使用者にとって、患部を傷めることなく好適に水分の拭き取りができる。 By adding a softening agent, surface softness and smoothness are expressed, and the touch is improved. In particular, a user who has a disease in the excretory part can wipe off moisture appropriately without damaging the affected part.
〔エンボス加工〕
本実施の形態の水解性衛生紙において、少なくとも２プライ以上で、かつ各シートにそれぞれエンボスが付与されてから重ねると、厚み感を向上させるとともに表面積を拡大して吸水性を向上させることが可能となり好適である。なお、より好適にはラミネートエンボス加工が望ましい。
[Embossing]
In the water-degradable sanitary paper according to the present embodiment, if it is at least 2 plies and stacked after embossing is applied to each sheet, it becomes possible to improve the thickness feeling and increase the surface area to improve water absorption. Is preferred. More preferably, laminate embossing is desirable.
本発明に係る水解性衛生紙の実施例と、比較例１〜３を比較した。
なお、表１及び表２における吸水量（ｇ／ｍ2）は、予め重量測定済みの１０ｃｍ×１０ｃｍにカットした製品１組を水に浸し、全面に水が浸透しきったら水面から静かに上げて余剰な水分を振り落として秤量した重量増加分のことをいうものとする。
The examples of the water-decomposable sanitary paper according to the present invention were compared with Comparative Examples 1 to 3.
The amount of water absorption (g / m 2 ) in Tables 1 and 2 is determined by immersing one set of products that have been pre-weighed and cut into 10 cm x 10 cm in water. It means the amount of weight increase measured by shaking off excess water.
本発明に係る水解性衛生紙の実施例は、比較例１〜３に比べて、吸水性を確保するとともに、裏抜け防止を確実に図り、かつ厚み感と柔軟性を与えることができることがわかった。また、紙粉を低減させることができた。 It was found that the examples of the water-decomposable sanitary paper according to the present invention can ensure water absorption, reliably prevent back-throwing, and give a feeling of thickness and flexibility as compared with Comparative Examples 1 to 3. . Moreover, paper dust was able to be reduced.
本発明は、トイレットペーパーのシートなどの水解性衛生紙として適用可能である。 The present invention is applicable as water-degradable sanitary paper such as toilet paper sheets.
１０…水解性衛生紙、１１，１２…外層、２１…中層、Ｗ…液。 10 ... water-degradable sanitary paper, 11, 12 ... outer layer, 21 ... middle layer, W ... liquid.
Claims (7)
該水解性衛生紙における基紙の原料は、合成パルプを除くパルプ繊維を使用し、
少なくとも一方の外層は吸液層とされ、セルロース、ヘミセルロース、親水性アセテートセルロース及び親水性不織布の少なくともいずれか１つを原料とし、
前記一方の外層以外の少なくともいずれかの層は、サイズ剤がパルプ絶乾質量に対する固形分質量比で０．０２〜０．０６％含まれる液透過抑制層とされ、
前記一方の外層の吸水量が１５０〜４００ｇ／ｍ2、かつこの一方の外層以外の少なくともいずれかの層の吸水量が１００〜３００ｇ／ｍ2であり、
少なくとも一方の外層の吸水時間と、この一方の外層以外の少なくともいずれかの層の吸水時間との比率が１：１５〜１：１．５とされた、
ことを特徴とする水解性衛生紙。 A water-degradable sanitary paper having three layers, each having a basis weight of 11 to 22 g / m 2 and a paper thickness of each layer of 60 to 200 μm,
The raw material of the base paper in the water-degradable sanitary paper uses pulp fibers excluding synthetic pulp,
At least one of the outer layers is a liquid absorbing layer, and at least one of cellulose, hemicellulose, hydrophilic acetate cellulose, and hydrophilic nonwoven fabric is used as a raw material,
At least one of the layers other than the one outer layer is a liquid permeation suppression layer in which a sizing agent is contained in an amount of 0.02 to 0.06% in a solid content ratio relative to the pulp dry weight,
The water absorption of the one outer layer is 150 to 400 g / m 2 , and the water absorption of at least one of the layers other than the one outer layer is 100 to 300 g / m 2 ;
The ratio of the water absorption time of at least one outer layer and the water absorption time of at least any one layer other than this one outer layer was 1:15 to 1: 1.5.
Water-degradable sanitary paper characterized by that.