JP6816588B2 - Roll toilet paper - Google Patents
Roll toilet paper Download PDFInfo
- Publication number
- JP6816588B2 JP6816588B2 JP2017053586A JP2017053586A JP6816588B2 JP 6816588 B2 JP6816588 B2 JP 6816588B2 JP 2017053586 A JP2017053586 A JP 2017053586A JP 2017053586 A JP2017053586 A JP 2017053586A JP 6816588 B2 JP6816588 B2 JP 6816588B2
- Authority
- JP
- Japan
- Prior art keywords
- toilet paper
- roll
- paper
- shaped
- pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、ロール状トイレットペーパーに関する。 The present invention relates to roll-shaped toilet paper.
長尺のトイレットペーパーを巻回してなるロール状トイレットペーパーには、柔らかく肌触りが良いこと、水解性を有しつつ使用に耐え得る程度の強度を有すること、などといった複数の要求品質がある。 The roll-shaped toilet paper, which is made by winding a long toilet paper, has a plurality of required qualities such as being soft and soft to the touch, having water solubility and having strength enough to withstand use.
近年のシャワートイレの普及などに伴い、多量の水分を裏抜けなく拭き取ることのできる、吸水量の多いロール状トイレットペーパー製品に対する要求がある。 With the spread of shower toilets in recent years, there is a demand for roll-shaped toilet paper products with a large amount of water absorption that can wipe off a large amount of water without strike through.
例えば特許文献１は、水分の吸収能力を確保するためにはバルク（比容積）を高くすることが重要であるとし、兼備が困難であるとする高バルク、高強度および柔らかさの３つの要求品質を満たすために、トイレットペーパー原紙となるウェブに対して凹凸を付与することを提案している。 For example, Patent Document 1 states that it is important to increase the bulk (specific volume) in order to secure the water absorption capacity, and that it is difficult to combine the three requirements of high bulk, high strength and softness. In order to satisfy the quality, it is proposed to add unevenness to the web that is the base paper for toilet paper.
また、特許文献２は、吸水性を確保すると共に裏抜け防止を確実に図ることのできる水解性衛生紙として、表層、中層、裏層の３プライからなり、外層（表層および裏層）と中層の吸水量および吸水時間を異ならせて水分を内部に閉じ込める構成を提案している。 Further, Patent Document 2 is a water-decomposable sanitary paper that can ensure water absorption and prevent strike-through, and is composed of three plies of a surface layer, a middle layer, and a back layer, and has an outer layer (surface layer and back layer) and a middle layer. We are proposing a configuration that traps water inside by making the amount of water absorption and the time of water absorption different.
しかしながら、特許文献２記載の発明では、外層（表層および裏層）と中層の物性をそれぞれ数値規定しており、実施のためには、各層を別個の構成で製造する必要がある。また、特許文献１記載の発明では、水分の吸収能力に関するトイレット製品の実用性の判断基準として、旧ＪＩＳ−Ｓ３１０４法に従う吸水度（所定量の水を吸い込むのに要する時間）を用いているが、この吸水度は、水の吸い込み易さを示すが、吸収可能な水の量の多少、特に実際のトイレにおける短時間における拭き取り量を反映するものではない。そこで、新規な構成の、トイレなどにおける実際の使用状態に対応した短時間における水の吸い取り性の高いロール状トイレットペーパーに対する要求がある。 However, in the invention described in Patent Document 2, the physical properties of the outer layer (surface layer and back layer) and the middle layer are numerically specified, and each layer needs to be manufactured with a separate configuration for implementation. Further, in the invention described in Patent Document 1, the water absorption degree (time required to suck in a predetermined amount of water) according to the old JIS-S3104 method is used as a criterion for determining the practicality of the toilet product regarding the water absorption capacity. Although this water absorption degree indicates the ease of sucking water, it does not reflect the amount of water that can be absorbed, especially the amount of wiping in a short time in an actual toilet. Therefore, there is a demand for a roll-shaped toilet paper having a new configuration and having high water absorption in a short time corresponding to an actual usage state in a toilet or the like.
本発明の目的は、短時間における吸水量の多いロール状トイレットペーパーの提供にある。 An object of the present invention is to provide a roll-shaped toilet paper having a large amount of water absorption in a short period of time.
上記課題を解決するための本発明は、以下の態様を有する。 The present invention for solving the above problems has the following aspects.
長尺のトイレットペーパーがロール状に巻回されてなるロール状トイレットペーパーであって、ロール状トイレットペーパーから巻き出されたトイレットペーパーについて日本工業規格ＪＩＳ Ｐ８１１３に準じて測定された際の縦方向の引張破断伸びが１６．９％よりも高い、ロール状トイレットペーパー。 It is a roll-shaped toilet paper in which a long toilet paper is wound in a roll shape, and the toilet paper unwound from the roll-shaped toilet paper is measured in the vertical direction according to the Japanese Industrial Standards JIS P8113. Roll-shaped toilet paper with a tensile elongation at break of more than 16.9%.
本発明によれば、短時間における吸水量の多いロール状トイレットペーパーを提供することができる。 According to the present invention, it is possible to provide a roll-shaped toilet paper having a large amount of water absorption in a short time.
以下、本発明の実施の形態を説明する。以下の実施の形態は一例であり、本発明は下記実施の形態に限定して解釈されるものではない。 Hereinafter, embodiments of the present invention will be described. The following embodiments are examples, and the present invention is not construed as being limited to the following embodiments.
（ロール状トイレットペーパー）
「ロール状トイレットペーパー」とは、長尺のトイレットペーパーがロール状に巻回されてなるものをいう。ロール状トイレットペーパーには、長尺のトイレットペーパーが芯管に対して巻回されてロール状を示すもの、および芯管を有さず長尺のトイレットペーパーのみが巻回されてロール状を示すもの（いわゆる「ノンコア」タイプ）が含まれる。
(Roll-shaped toilet paper)
"Roll-shaped toilet paper" refers to a long piece of toilet paper that is rolled into a roll. Roll-shaped toilet paper is one in which a long toilet paper is wound around a core tube to show a roll shape, and one in which only a long toilet paper without a core tube is wound to show a roll shape. Things (so-called "non-core" types) are included.
ロール状トイレットペーパーの寸法形状は、日本工業規格ＪＩＳなどの規格や一般的なホルダーのサイズ等を勘案して決定することができ、例えば、幅は１０５〜１１４ｍｍ、および巻径は１２０ｍｍ以下の巻取りとすることができる。この寸法形状であると、ロール状トイレットペーパーを通常のホルダーに収めることができる。ロール状トイレットペーパーにおける長尺のトイレットペーパーの巻回長さは、ロール状トイレットペーパーの所定の巻径が達成されるものであればよく、９０ｍ以下とすることが一般的である。 The dimensions and shape of the roll-shaped toilet paper can be determined in consideration of standards such as Japanese Industrial Standards JIS and the size of general holders. For example, the width is 105 to 114 mm and the winding diameter is 120 mm or less. It can be taken. With this size and shape, the roll-shaped toilet paper can be stored in a normal holder. The winding length of the long toilet paper in the roll-shaped toilet paper may be such that a predetermined winding diameter of the roll-shaped toilet paper can be achieved, and is generally 90 m or less.
巻回長さは、トイレットペーパーの厚さや、トイレットペーパーをロール状に巻回する工程においてトイレットペーパーに掛かる張力などによって、制限を受け得る。一般に、同一の巻径を得るための巻回長さは、トイレットペーパーの厚さが厚いほど短くなり、巻回工程における張力が高いほど長くなる傾向にある。また、巻回工程における張力が高いほど、トイレットペーパーの厚さがつぶされてクレープ（皺）や凹凸が平坦化される傾向が大きい。クレープや凹凸が平坦化されると、その後のトイレットペーパーは、構造上の遊び部分が減り、引っ張っても伸びにくくなる傾向にある。トイレットペーパーのクレープや凹凸の低減の程度の大小は、巻回工程における張力の大小の設定により制御し得る。その結果、トイレットペーパーには、構造上の遊び部分が残り、引っ張った場合に伸びを示す傾向にある。 The winding length may be limited by the thickness of the toilet paper, the tension applied to the toilet paper in the process of winding the toilet paper in a roll shape, and the like. In general, the winding length for obtaining the same winding diameter tends to be shorter as the thickness of the toilet paper is thicker, and longer as the tension in the winding process is higher. Further, the higher the tension in the winding process, the greater the tendency that the thickness of the toilet paper is crushed and the crepes (wrinkles) and irregularities are flattened. When the crepe or unevenness is flattened, the subsequent toilet paper tends to have less structural play and become difficult to stretch even when pulled. The degree of reduction of crepe and unevenness of toilet paper can be controlled by setting the magnitude of tension in the winding process. As a result, the toilet paper has a structural play portion that tends to stretch when pulled.
「巻回」の方法は特に限定されないが、例えば、長尺のトイレットペーパーの原反からトイレットペーパーを巻き出して先端部を芯管に接着固定し、ワインダーにより芯管を回転させてロール状トイレットペーパーの製品長さ分だけトイレットペーパーを巻回してロール状とし、巻回したトイレットペーパーを原反から切離し、巻回したトイレットペーパーの後端部をロールの外周面に接着固定する方法等を挙げることができる。 The method of "winding" is not particularly limited, but for example, the toilet paper is unwound from the original fabric of the long toilet paper, the tip is adhesively fixed to the core tube, and the core tube is rotated by a winder to roll the toilet paper. Toilet paper is wound by the length of the paper product to form a roll, the wound toilet paper is separated from the original fabric, and the rear end of the wound toilet paper is adhered and fixed to the outer peripheral surface of the roll. be able to.
また、ノンコアタイプの場合は、長尺のトイレットペーパーの原反から巻き出したトイレットペーパーの先端部を、芯管を用いずに、ワインダーの軸に直接取り付けて同様に巻回を行い、ロール状トイレットペーパーの外観形状を得た後に、これを軸から取り外す方法等を挙げることができる。 In the case of the non-core type, the tip of the toilet paper unwound from the original fabric of the long toilet paper is directly attached to the shaft of the winder without using a core tube and wound in the same manner to form a roll. After obtaining the appearance shape of the toilet paper, a method of removing the toilet paper from the shaft can be mentioned.
「芯管」とは、ロール状トイレットペーパーの巻き芯となる部材である。芯管は、例えば、ボール紙等の厚紙からなり、外径３５〜５０ｍｍφ、厚さ０．５〜１．５ｍｍの紙管が好適に用いられる。一時に複数個のロール状トイレットペーパー製品を製造できるように、通常は、巻回工程において、製品幅の複数倍（例えば、１０〜６０倍）程度の長尺な管長の芯管を用い、この長尺な芯管に長尺のトイレットペーパーが巻回されたロール（「ログ」ともいう）を得て、このログを切断刃により製品幅にカットして、ロール状トイレットペーパー製品を得る。 The "core tube" is a member that serves as a winding core for roll-shaped toilet paper. The core tube is made of thick paper such as corrugated cardboard, and a paper tube having an outer diameter of 35 to 50 mmφ and a thickness of 0.5 to 1.5 mm is preferably used. In order to be able to manufacture a plurality of roll-shaped toilet paper products at one time, usually, in the winding process, a core tube having a length of about several times the product width (for example, 10 to 60 times) is used. A roll (also called a "log") in which a long toilet paper is wound around a long core tube is obtained, and this log is cut to the product width by a cutting blade to obtain a roll-shaped toilet paper product.
「切断刃」としては、ログソー（丸刃）、バンドソー（平刃）等、従来公知の切断刃を用いることができる。刃の厚さとしては、２〜１０ｍｍのものが好適に用いられる。 As the "cutting blade", a conventionally known cutting blade such as a log saw (round blade) or a band saw (flat blade) can be used. A blade having a thickness of 2 to 10 mm is preferably used.
（トイレットペーパー）
本実施の形態にかかるロール状トイレットペーパーを構成する長尺のトイレットペーパーは、トイレットペーパー原紙１枚からなるもの（１プライ）であってもよく、トイレットペーパー原紙を複数枚重ねたもの（マルチプライ）であってもよい。トイレットペーパー原紙を２枚重ねたものを２プライといい、３枚重ねたものを３プライといい、以下同様に、重ねたトイレットペーパー原紙の枚数をＮとしたとき、その数に応じてＮプライと称される。
(Toilet Paper)
The long toilet paper constituting the roll-shaped toilet paper according to the present embodiment may be composed of one toilet paper base paper (1 ply) or a stack of a plurality of toilet paper base papers (multi-ply). ) May be. Two stacked toilet paper base papers are called 2 plies, three stacked toilet paper base papers are called 3 plies, and similarly, when the number of stacked toilet paper base papers is N, N plies are used according to the number. Is called.
一般に、トイレットペーパー原紙のプライ数が多いほど、裏抜けを防止し厚み感を付与することができるが、一方、プライ数が多いと、トイレットペーパーの柔軟性が低くなり、また、ロール状に巻回したときに所定の巻径とするための巻回長さが短くなってしまう傾向にある。そのため、好ましいプライ数には上限がある。 Generally, the larger the number of plies of the toilet paper base paper, the more it is possible to prevent strike-through and give a sense of thickness. On the other hand, the larger the number of plies, the less flexible the toilet paper is and the more it is rolled into a roll. When it is turned, the winding length for achieving a predetermined winding diameter tends to be shortened. Therefore, there is an upper limit to the preferred number of plies.
マルチプライ（Ｎプライ）のトイレットペーパーは、複数枚（Ｎ枚）のトイレットペーパー原紙をプライマシン（不図示）にて積層することにより得ることができる。プライマシンは、公知のものを特段の制限なく使用することができる。 The multi-ply (N-ply) toilet paper can be obtained by laminating a plurality of (N sheets) of toilet paper base paper with a ply machine (not shown). As the ply machine, a known one can be used without any particular limitation.
トイレットペーパー原紙、および／または複数枚のトイレットペーパー原紙が積層されてなる積層体には、必要に応じて、エンボス加工が施されていてもよい。つまり、マルチプライのトイレットペーパーの場合、マルチプライのトイレットペーパーを構成する全てのトイレットペーパー原紙を積層した状態でエンボス加工を行うことができる。また、各々のトイレットペーパー原紙が積層されていない状態でエンボス加工を施してもよく、この場合には全ての原紙が積層された状態において再度エンボス加工を行うことが好ましい。 The toilet paper base paper and / or the laminated body in which a plurality of toilet paper base papers are laminated may be embossed, if necessary. That is, in the case of multi-ply toilet paper, embossing can be performed in a state where all the toilet paper base papers constituting the multi-ply toilet paper are laminated. Further, the embossing may be performed in a state where the respective toilet paper base papers are not laminated, and in this case, it is preferable to perform the embossing again in a state where all the base papers are laminated.
「エンボス」とは、１対のロール間に対象物（トイレットペーパー原紙および／または複数枚のトイレットペーパー原紙が積層されてなる積層体）を挟み込んで押圧し、ロール表面に形成された凸模様を原紙および／または積層体に型押し（転写）することによって形成される型押し模様である。 "Embossing" is a convex pattern formed on the roll surface by sandwiching and pressing an object (a laminated body of toilet paper base paper and / or a plurality of toilet paper base papers) between a pair of rolls. It is an embossed pattern formed by embossing (transferring) to a base paper and / or a laminate.
このエンボス加工によって、原紙および／または積層体に凹凸が形成され、空気層を含んだ嵩高い状態とすることができる。そのため、トイレットペーパーに柔軟性を付与することができるとともに、この嵩高い部分に水分を取り込むことができ、吸水量が増大し得る。 By this embossing, unevenness is formed on the base paper and / or the laminated body, and a bulky state including an air layer can be obtained. Therefore, flexibility can be imparted to the toilet paper, and water can be taken into this bulky portion, so that the amount of water absorption can be increased.
エンボス加工は、トイレットペーパー原紙および／または複数枚のトイレットペーパー原紙が積層されてなる積層体の両面に多数の凸部と多数の凹部とを有するエンボスパターンを形成するように行う。エンボス加工を施すことによって、トイレットペーパー原紙、および／または複数枚のトイレットペーパー原紙が積層されてなる積層体に、嵩高さ、柔かさ、吸水性を付与し得る。 The embossing is performed so as to form an embossing pattern having a large number of convex portions and a large number of concave portions on both sides of a laminated body formed by laminating a toilet paper base paper and / or a plurality of toilet paper base papers. By embossing, bulkiness, softness, and water absorption can be imparted to the toilet paper base paper and / or the laminate formed by laminating a plurality of toilet paper base papers.
また、紙面に見た目にも楽しい図柄を施すことにより外観上の美しさ（装飾的効果）を高めるというデザイン的な要求から、多数の凸部または凹部の組み合わせによって図柄模様を形成してもよい。このようなエンボスは、デザインエンボスとも称される。 Further, from the design requirement of enhancing the beauty (decorative effect) of the appearance by applying a pattern that is visually pleasing to the paper surface, the pattern may be formed by combining a large number of convex portions or concave portions. Such embossing is also called design embossing.
積層体に筋状エンボスを施すことによって、各層を相互に結合してもよい。筋状エンボスは、重ねられたトイレットペーパー原紙の流れ方向（抄紙方向に相当する縦方向）に沿って直線状に設けられ、両端の少なくとも一方、あるいは中央部に設けることができる。流れ方向に沿って結合することによって、使用時に生じやすい切り離し位置のずれを抑止することができる。特に、両端部に設けた場合にその効果が顕著である。筋状エンボスは、エッジエンボスとも称される。 The layers may be bonded to each other by applying streak embossing to the laminate. The streak embossing is provided linearly along the flow direction (vertical direction corresponding to the papermaking direction) of the stacked toilet paper base papers, and can be provided at at least one of both ends or at the center. By connecting along the flow direction, it is possible to suppress the deviation of the disconnection position that tends to occur during use. In particular, the effect is remarkable when it is provided at both ends. Streaky embossing is also called edge embossing.
エンボス加工の方法は、従来公知の方法の中から目的に応じて適宜選択すればよい。例えば、マッチドスチール法、ラバースチール法、ネステッド法、ポイント・トゥー・ポイント法等の方法を挙げることができる。 The embossing method may be appropriately selected from conventionally known methods according to the purpose. For example, a matched steel method, a rubber steel method, a nested method, a point-to-point method, and the like can be mentioned.
（トイレットペーパー原紙）
トイレットペーパー原紙は、以下に非限定目的で例示する原料を、公知の抄紙機および公知の抄紙工程、具体的には、ワイヤー（フェルト）パート、プレスパート、ドライヤーパートを経て、抄造することにより得ることができる。
(Toilet paper base paper)
Toilet paper base paper is obtained by making a raw material exemplified below for a non-limiting purpose through a known paper machine and a known paper making process, specifically, a wire (felt) part, a press part, and a dryer part. be able to.
公知の抄紙機としては、サクションブレストフォーマー（円網タイプ、長網タイプ）、ツインワイヤーフォーマー、円網フォーマー（Ｃラップ、Ｓラップ）、クレセントフォーマー等の抄紙機にヤンキードライヤーを組合わせたヤンキー抄紙機が使用されるが、クレセントフォーマーが低坪量のウェブを製造することが可能であるため好ましい。 Known paper machines include suction breast formers (circular mesh type, long mesh type), twin wire formers, circular mesh formers (C wrap, S wrap), crescent formers, and other paper machines combined with a Yankee dryer. A Yankee paper machine is used, which is preferred because the crescent former can produce low-basis webs.
トイレットペーパー原紙の製造工程においては、吸水性を向上させるための種々の手法を施すことができる。例えば、プレスパートにおいて、凹凸のあるフェルトを湿紙ウェブに押し付けて凹凸付けを行ってもよい（例えば、特許文献１参照）。また、ドライヤーパートにおいて、公知のクレープ付け手法を行ってもよい。例えば、ヤンキードライヤーの回転速度より巻き取り用のリールの回転速度を遅くする手法がある。ここで、クレープ付けとは、紙を縦方向（抄紙機の走行方向）に機械的に圧縮し、クレープと称される波状の皺を形成する公知の方法である。クレープ付与により、トイレットペーパー原紙に嵩高さ（バルク感）を与えると共に、吸水性を付与することができる。 In the process of manufacturing the base paper for toilet paper, various methods for improving water absorption can be applied. For example, in the press part, the uneven felt may be pressed against the wet paper web to make the unevenness (see, for example, Patent Document 1). Further, in the dryer part, a known crepe attachment method may be performed. For example, there is a method of making the rotation speed of the take-up reel slower than the rotation speed of the Yankee dryer. Here, crepe attachment is a known method of mechanically compressing paper in the vertical direction (running direction of a paper machine) to form wrinkles called crepes. By applying the crepe, it is possible to impart bulkiness (bulk feeling) to the toilet paper base paper and also to impart water absorption.
（原料）
トイレットペーパー原紙を抄造するための原料は、特に限定されず、適宜の原料を使用することができる。原料として、パルプ繊維を使用する場合、このパルプ繊維（原料パルプ）としては、例えば、木材パルプ、非木材パルプ、合成パルプ、古紙パルプなどから、より具体的には、砕木パルプ（ＧＰ）、ストーングランドパルプ（ＳＧＰ）、リファイナーグランドパルプ（ＲＧＰ）、加圧式砕木パルプ（ＰＧＷ）、サーモメカニカルパルプ（ＴＭＰ）、ケミサーモメカニカルパルプ（ＣＴＭＰ）、ブリーチケミサーモメカニカルパルプ（ＢＣＴＭＰ）等の機械パルプ（ＭＰ）、化学的機械パルプ（ＣＧＰ）、半化学的パルプ（ＳＣＰ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）、針葉樹晒クラフトパルプ（ＮＢＫＰ）等のクラフトパルプ（ＫＰ）、ソーダパルプ（ＡＰ）、サルファイトパルプ（ＳＰ）、溶解パルプ（ＤＰ）等の化学的パルプ（ＣＰ）、脱墨パルプ（ＤＩＰ）、ウエストパルプ（ＷＰ）等の古紙パルプ、かすパルプ（ＴＰ）、木綿、アマ、麻、黄麻、マニラ麻、ラミー等を原料とするぼろパルプ、わらパルプ、エスパルトパルプ、バガスパルプ、竹パルプ、ケナフパルプ等の茎稈パルプ、靭皮パルプ等の補助パルプなどから、１種または数種を適宜選択して使用することができる。
(material)
The raw material for making the toilet paper base paper is not particularly limited, and an appropriate raw material can be used. When pulp fiber is used as a raw material, the pulp fiber (raw material pulp) includes, for example, wood pulp, non-wood pulp, synthetic pulp, waste paper pulp, and more specifically, crushed wood pulp (GP) and stone. Mechanical pulp (MP) such as ground pulp (SGP), refiner ground pulp (RGP), pressurized crushed wood pulp (PGW), thermomechanical pulp (TMP), chemithermomechanical pulp (CTMP), bleach chemithermomechanical pulp (BCTMP) ), Chemical mechanical pulp (CGP), semi-chemical pulp (SCP), broadleaf bleached kraft pulp (LBKP), coniferous bleached kraft pulp (NBKP) and other kraft pulp (KP), soda pulp (AP), sulfite pulp Chemical pulp (CP) such as (SP), dissolved pulp (DP), waste paper pulp such as deinked pulp (DIP), waist pulp (WP), waste pulp (TP), cotton, flax, hemp, yellow hemp, Manila hemp. , Straw pulp, straw pulp, esparto pulp, bagas pulp, bamboo pulp, stalk pulp such as kenaf pulp, auxiliary pulp such as bast pulp, etc., which are made from ramie, etc. can do.
トイレットペーパーとして一般に所望される品質、例えば柔らかさや白さ等を得るためには、ＮＢＫＰ：ＬＢＫＰ＝１０：９０〜７０：３０（質量比）の木材パルプを原料とすることが好ましく、より好ましくはＮＢＫＰ：ＬＢＫＰ＝２０：８０ないし７０：３０、さらに好ましくはＮＢＫＰ：ＬＢＫＰ＝２０：８０ないし４０：６０である。上記ＬＢＫＰの材種として、ユーカリ属グランディスおよびユーカリグロビュラスに代表される、フトモモ科ユーカリ属から製造されるパルプが好ましい。このパルプ比率の木材パルプに対し、古紙パルプを５０質量％程度まで含むことができる。古紙パルプは品質的バラツキが大きく、配合割合が増えると製品の品質、特に、柔らかさに大きく影響するので、木材パルプに対して２０質量％以下配合するのが望ましい。 In order to obtain the quality generally desired for toilet paper, for example, softness and whiteness, it is preferable to use wood pulp of NBKP: LBKP = 10: 90 to 70:30 (mass ratio) as a raw material, and more preferably. NBKP: LBKP = 20:80 to 70:30, more preferably NBKP: LBKP = 20:80 to 40:60. As the grade of LBKP, pulp produced from the genus Eucalyptus of the Myrtaceae family, represented by the genus Eucalyptus Grandis and the genus Eucalyptus, is preferable. Waste paper pulp can be contained up to about 50% by mass with respect to wood pulp having this pulp ratio. The quality of used paper pulp varies widely, and increasing the blending ratio greatly affects the quality of the product, especially the softness. Therefore, it is desirable to blend 20% by mass or less with respect to wood pulp.
かかる原料は、例えば、水に分散させたスラリー状の抄紙原料（紙料）の形態で、抄紙に用いることができる。 Such a raw material can be used for papermaking in the form of a slurry-like papermaking raw material (paper material) dispersed in water, for example.
ただし、当該原料としては、上記に限るものではなく、必要に応じて公知の添加剤等を使用してもよい。 However, the raw material is not limited to the above, and known additives and the like may be used as needed.
このトイレットペーパーは、日本工業規格ＪＩＳ Ｐ ８１２４に従って測定したトイレットペーパー原紙１枚当りの坪量が１１〜２３ｇ／ｍ2であり、マルチプライの場合は積層体の坪量が２４〜３５ｇ／ｍ2であることが好ましい。トイレットペーパー原紙の坪量１１ｇ／ｍ2未満では、トイレットペーパー原紙の強度が弱くなり、トイレットロールを製造することができなくなる場合がある。また、坪量が２３ｇ／ｍ2を超えて多くなると、マルチプライの場合、形成される積層体が厚くなり、これを所定の長さに巻き取った場合にロール直径が大きくなり過ぎてしまい、通常のホルダーに収まらなくなってしまう場合がある。 This toilet paper has a basis weight of 11 to 23 g / m 2 per sheet of toilet paper base paper measured according to Japanese Industrial Standards JIS P 8124, and in the case of multiple ply, the basis weight of the laminated body is 24 to 35 g / m 2. Is preferable. If the basis weight of the toilet paper base paper is less than 11 g / m 2 , the strength of the toilet paper base paper becomes weak, and it may not be possible to manufacture the toilet roll. Further, when the basis weight exceeds 23 g / m 2 , the laminated body formed becomes thick in the case of multi-ply, and when this is wound to a predetermined length, the roll diameter becomes too large. It may not fit in a normal holder.
このトイレットペーパーは、トイレットペーパー原紙１枚当りの厚さが８６〜１０９μｍであることが好ましく、マルチプライの場合、重ね合せたトイレットペーパー原紙の積層体は、、ＪＩＳ Ｐ８１１８に準じて測定したロール状トイレットペーパーを構成するトイレットペーパー１組あたりの厚さが１０７〜１９６μｍであることが好ましい。トイレットペーパー原紙の厚さが８６μｍ未満になるとトイレットペーパー原紙の強度が低下し、一方、１０９μｍを超えて厚くなると、これを重ね合せた積層体を所定長さに巻き取った場合にロール直径が大きくなり、通常のホルダーに収まりにくくなる。 The thickness of this toilet paper is preferably 86 to 109 μm per sheet of toilet paper base paper, and in the case of multi-ply, the laminated body of the laminated toilet paper base paper is in the form of a roll measured according to JIS P8118. The thickness of each set of toilet paper constituting the toilet paper is preferably 107 to 196 μm. When the thickness of the toilet paper base paper is less than 86 μm, the strength of the toilet paper base paper decreases, while when the thickness exceeds 109 μm, the roll diameter becomes large when the laminated body in which these are laminated to a predetermined length is wound up. It becomes difficult to fit in a normal holder.
また、積層体の厚さを１０７μｍ未満まで薄くすると、ウェブの密度が高くなり、柔らかさが損なわれてしまい、一方、１９６μｍを超えて厚くすると、積層体を所定長さに巻き取った場合にロール直径が大きくなり、通常のホルダーに収まりにくくなる。 Further, if the thickness of the laminate is reduced to less than 107 μm, the density of the web becomes high and the softness is impaired. On the other hand, if the thickness exceeds 196 μm, the laminate is wound to a predetermined length. The roll diameter becomes large, making it difficult to fit in a normal holder.
（吸水量）
本実施形態においては、ロール状トイレットペーパーの液体吸収能力を、ロール状トイレットペーパーを構成するトイレットペーパー原紙が吸収可能な水の量（吸水量）の観点から判断する。具体的には、吸水量を、以下の手順に従って算出する。
（１）ロール状トイレットペーパーをＪＩＳ Ｐ８１１１に準じて調温調湿する。
（２）前記ロール状トイレットペーパーからトイレットペーパーを巻き出し、縦方向１５ｍｍ、横方向１００ｍｍの短冊形の試験片を切り出して、当該試験片の水浸漬前の重量を量る。なお、本明細書において、「縦方向」とは、トイレットペーパー原紙の抄紙方向に相当する方向をいい、横方向は、縦方向に直交する方向をいう。
（３）前記試験片を、試験片の長辺方向の端から３ｍｍが水中に浸かるように、バットに張った水に漬ける。
（４）前記試験片を水に漬けてから２秒後に引き上げて質量を測定し、ロール状トイレットペーパーを構成するトイレットペーパー原紙のプライ数により割った値（単位：ｍｇ／プライ数）を算出する。
(Water absorption)
In the present embodiment, the liquid absorption capacity of the roll-shaped toilet paper is determined from the viewpoint of the amount of water (water absorption amount) that the toilet paper base paper constituting the roll-shaped toilet paper can absorb. Specifically, the amount of water absorption is calculated according to the following procedure.
(1) The roll-shaped toilet paper is temperature-controlled and humidity-controlled according to JIS P8111.
(2) The toilet paper is unwound from the roll-shaped toilet paper, a strip-shaped test piece having a length of 15 mm and a width of 100 mm is cut out, and the weight of the test piece before being immersed in water is weighed. In the present specification, the "vertical direction" means a direction corresponding to the papermaking direction of the toilet paper base paper, and the horizontal direction means a direction orthogonal to the vertical direction.
(3) The test piece is immersed in water stretched on a vat so that 3 mm from the end in the long side direction of the test piece is immersed in water.
(4) The test piece is soaked in water and then pulled up 2 seconds later to measure the mass, and the value (unit: mg / number of plies) divided by the number of plies of the toilet paper base paper constituting the roll-shaped toilet paper is calculated. ..
上記規定による吸水量は、従来のＪＩＳ等に規定された測定法と異なり、２秒という短時間における吸水性を示す。洗浄便座などによって汚れが落とされた状態のお尻などに対してトイレットペーパーをあてがう場合には、汚れを落とす性能よりも／だけでなく、水分を吸収する性能がより強く求められる。したがって、上記した吸水量は、洗浄便座によってお尻を水洗いした場合などにおける水分の拭き取り性を評価する指標（トイレットペーパーの使用状態に即した速乾性・速吸性を評価するための指標）と言える。 The amount of water absorption according to the above regulation shows water absorption in a short time of 2 seconds, unlike the conventional measurement method specified in JIS and the like. When applying toilet paper to the buttocks that have been cleaned by a washing toilet seat or the like, not only the ability to remove dirt / but also the ability to absorb water is strongly required. Therefore, the above-mentioned water absorption amount is an index for evaluating the wiping property of water when the buttocks are washed with a washing toilet seat (an index for evaluating quick-drying and quick-absorbing property according to the usage state of toilet paper). I can say.
トイレットペーパーの水分拭き取り性能の観点からは、吸水量の値は大きいほど好ましい。 From the viewpoint of the water wiping performance of the toilet paper, the larger the value of the water absorption amount, the more preferable.
（伸び）
トイレットペーパーについての縦方向の伸びは、ロール状トイレットペーパーからトイレットペーパーを巻き出して計測する。具体的には、日本工業規格ＪＩＳ Ｐ８１１３に準じて、ロール状トイレットペーパーからトイレットペーパーを巻き出して、トイレットペーパーの縦方向の長さを１５０ｍｍとし、縦方向と直交する横方向の長さを１５ｍｍとした短冊形の試験片を切り出し、引張試験機（テンシロン万能材料試験機 ＲＴＣ１２５０）にて引張試験を行い、引張破断伸びを計測して、これを伸び（単位：％）とする。
(Growth)
The vertical elongation of the toilet paper is measured by unwinding the toilet paper from the roll-shaped toilet paper. Specifically, according to the Japanese Industrial Standards JIS P8113, the toilet paper is unwound from the roll-shaped toilet paper, the length of the toilet paper in the vertical direction is 150 mm, and the length in the horizontal direction orthogonal to the vertical direction is 15 mm. A strip-shaped test piece is cut out and subjected to a tensile test with a tensile tester (Tencilon universal material tester RTC1250), and the tensile elongation at break is measured and used as the elongation (unit:%).
本実施形態におけるロール状トイレットペーパーの伸びは、１６．９％より高く、好ましくは１９．１％以上、より好ましくは２１．３％以上とされる。伸びを１６．９％より高くすると吸水量が２５ｍｇ/プライ数より高くなりしっかりと水分を拭取ることができるため好ましい。１９．１％以上にすると吸水量が３０ｍｇ/プライ数以上となり裏抜けを防止するも可能となるためより好ましい。２１．３％以上にすると吸水量が３５ｍｇ/プライ数以上となり拭いた後の肌の状態をさらさらな状態にすることができるため極めて好ましい。 The elongation of the roll-shaped toilet paper in the present embodiment is higher than 16.9%, preferably 19.1% or more, and more preferably 21.3% or more. When the elongation is higher than 16.9%, the water absorption amount becomes higher than 25 mg / ply number and the water can be wiped off firmly, which is preferable. When it is 19.1% or more, the water absorption amount becomes 30 mg / ply number or more, and it is possible to prevent strike-through, which is more preferable. When it is 21.3% or more, the water absorption amount becomes 35 mg / ply number or more, and the condition of the skin after wiping can be made smooth, which is extremely preferable.
また、本実施形態に係るロール状トイレットペーパーの伸びは、好ましくは３５％以下とされ、より好ましくは３１．４％以下とされる。伸びを３５％より高くすると製造時に断紙が発生しやすくなるため３５％以下とすることが好ましい。また、伸び率を３１．４％以下とし、下限値を上記したいずれかの値の範囲とすれば、良好な吸水性を有する歩留まりのよいトイレットペーパーとなり好適である。 Further, the elongation of the roll-shaped toilet paper according to the present embodiment is preferably 35% or less, more preferably 31.4% or less. If the elongation is higher than 35%, paper breaks are likely to occur during manufacturing, so it is preferably 35% or less. Further, if the elongation rate is 31.4% or less and the lower limit value is in the range of any of the above values, the toilet paper having good water absorption and good yield is suitable.
すなわち、伸びを１６．９％より高く３５％以下、より好適には１６．９％より高く３１．４％以下とすると、吸水量を２５ｍｇ/プライとすることができ、１プライであってもお尻に付着した水を一度の拭き取りで十分に吸収することができ、かつ、歩留まりよく製造することができ好適である。伸びを１９．１％以上３５％以下、好ましくは１９．１％以上３１．４％以下とすれば、３０ｍｇ/プライ以上の吸水量とすることができる。さらに、伸びを２１．３％以上３５％以下、好ましくは２１．３％以上３１．４％以下とすれば、３５ｍｇ/プライ以上という驚異的な吸水量のトイレットペーパーを提供することが可能となる。このようなトイレットペーパーは、従来の吸水量のトイレットペーパーを３プライにして/３枚重ねにして実現していた吸水量とほぼ同等の性能を２プライで実現することができ、洗浄便座によって洗われた直後の水分の極めて多いお尻について一度の拭き取りでも拭き取り可能とすることも可能となる。従来の同プライのトイレットペーパーと比較すれば、本実施の形態にかかるトイレットペーパーは、極めて優れた吸水性能、すなわちトイレにおける実際の使用時に求められる速乾性能（すばやい吸水性能)を実現でき、洗浄便座用のトイレットペーパーとして特に適していると言い得る。これらの数値の意義については、下記実施例・比較例によっても明らかとなる。 That is, when the elongation is higher than 16.9% and 35% or less, more preferably higher than 16.9% and 31.4% or less, the water absorption amount can be 25 mg / ply, even if it is 1 ply. It is suitable because the water adhering to the buttocks can be sufficiently absorbed by wiping it once and the yield can be improved. If the elongation is 19.1% or more and 35% or less, preferably 19.1% or more and 31.4% or less, the water absorption amount can be 30 mg / ply or more. Further, if the elongation is 21.3% or more and 35% or less, preferably 21.3% or more and 31.4% or less, it becomes possible to provide toilet paper having an astonishing water absorption of 35 mg / ply or more. .. Such toilet paper can achieve almost the same performance as the water absorption amount realized by making 3 plies of conventional toilet paper with a water absorption amount / 3 layers, and can be washed with a washing toilet seat. It is also possible to wipe off the extremely moist butt immediately after it has been damaged, even with a single wipe. Compared with the conventional toilet paper of the same ply, the toilet paper according to this embodiment can realize extremely excellent water absorption performance, that is, quick-drying performance (quick water absorption performance) required at the time of actual use in the toilet, and can be washed. It can be said that it is particularly suitable as toilet paper for toilet seats. The significance of these numerical values will be clarified by the following Examples and Comparative Examples.
以下、実施例により、本発明の実施形態を詳細に説明するが、本発明の実施形態はこれに制限されるものではない。なお、各実施例および比較例で得られたロール状トイレットペーパーについて行った評価と評価方法は、次の通りである。 Hereinafter, embodiments of the present invention will be described in detail with reference to Examples, but the embodiments of the present invention are not limited thereto. The evaluations and evaluation methods performed on the roll-shaped toilet papers obtained in each of the examples and comparative examples are as follows.
（坪量）
日本工業規格ＪＩＳ Ｐ ８１２４に従って、ロール状トイレットペーパーを構成するトイレットペーパー原紙１枚あたりの坪量を測定した。
(Basis weight)
According to the Japanese Industrial Standards JIS P 8124, the basis weight per sheet of toilet paper base paper constituting the roll-shaped toilet paper was measured.
（紙厚）
ＪＩＳ Ｐ ８１１８に準じてロール状トイレットペーパーを構成するトイレットペーパー１組あたりの紙厚を測定した。すなわち、３プライについては３枚、２プライについては２枚の厚さを測定した。
(Paper thickness)
The paper thickness per set of toilet paper constituting the roll-shaped toilet paper was measured according to JIS P 8118. That is, the thickness of 3 sheets for 3 plies and 2 sheets for 2 plies was measured.
（吸水量）
ロール状トイレットペーパーの液体吸収能力を、上記した吸水量によって測定・算出した。
(Water absorption)
The liquid absorption capacity of the roll-shaped toilet paper was measured and calculated based on the above-mentioned water absorption amount.
（伸び）
伸びは上記したようにして算出した。
(Growth)
The elongation was calculated as described above.
（実施例１）
古紙パルプ（ＤＩＰ）７０質量％および広葉樹木材パルプ３０質量％からなる原料パルプを水中に分散させたスラリー（抄紙原料）を、ヤンキードライヤーにて乾燥を行う抄紙機で抄紙してリールに巻き取って、トイレットペーパー原紙の原反とした。このとき、ヤンキードライヤーの周速よりも、トイレットペーパー原紙のリールへの巻き取り速度を遅らせることにより、トイレットペーパー原紙を縦方向（抄紙機の走行方向）に機械的に圧縮し、クレープと称される波状の皺をトイレットペーパー原紙に対して付与した。
(Example 1)
A slurry (papermaking raw material) in which raw material pulp consisting of 70% by mass of used paper pulp (DIP) and 30% by mass of broadleaf wood pulp is dispersed in water is made by a paper machine that dries with a Yankee dryer and wound on a reel. , Toilet paper base paper. At this time, by slowing the winding speed of the toilet paper base paper to the reel faster than the peripheral speed of the Yankee dryer, the toilet paper base paper is mechanically compressed in the vertical direction (running direction of the paper machine), which is called crepe. Wavy wrinkles were added to the base paper of the toilet paper.
このようにして製造したトイレットペーパー原紙の原反を３つ準備してワインダーにかけ、各々からトイレットペーパー原紙を巻き出しつつ積層させ、エンボス装置により、３枚のトイレットペーパー原紙の積層体（３プライ）の両面に多数の凸部と多数の凹部とを有するエンボスパターンが形成されるようなエンボス加工（シングルエンボス）を施し、筋状エンボス装置により、トイレットペーパーの使用時に各層がずれるのを防止するためにトイレットペーパーの幅方向端部付近となる箇所に筋状のエンボス加工を施し、仕上げ原反として巻き取った。仕上げ原反を、通称ロール状トイレットペーパー製造装置にかけ、ミシン目を付与しつつ、所定の巻回長さになるまで芯管に巻回し、スリッターにより幅方向を製品寸法に合わせて切断して表１に示す伸びを有する実施例１のロール状トイレットペーパーを得た。巻長、巻径、坪量は表１に示す通りである。 Three raw sheets of toilet paper base paper produced in this manner are prepared and applied to a winder, and the toilet paper base paper is unwound and laminated from each, and an embossing device is used to stack three sheets of toilet paper base paper (3 plies). Embossing (single embossing) is performed so that an embossed pattern with many convex parts and many concave parts is formed on both sides of the toilet paper, and the streak embossing device prevents each layer from shifting when using toilet paper. The area near the end of the toilet paper in the width direction was embossed in a streak pattern and wound up as a finishing material. The finished raw fabric is placed on a roll-shaped toilet paper manufacturing device, wound around a core tube until it reaches the specified winding length while giving perforations, and cut in the width direction according to the product dimensions with a slitter. A roll-shaped toilet paper of Example 1 having the elongation shown in 1 was obtained. The winding length, winding diameter, and basis weight are as shown in Table 1.
（実施例２〜４）
ヤンキードライヤーの周速およびトイレットペーパー原紙のリールへの巻き取り速度を実施例１と異なるようにしたこと以外は実施例１と同じ材料・条件とし、表１に示す伸びを有する実施例２〜４のロール状トイレットペーパーを製造した。巻長、巻径、プライ数、坪量は表１に示す値とした。
(Examples 2 to 4)
Examples 2 to 4 have the same materials and conditions as in Example 1 except that the peripheral speed of the Yankee dryer and the winding speed of the toilet paper base paper on the reel are different from those in Example 1, and have the elongation shown in Table 1. Manufactured roll-shaped toilet paper. The winding length, winding diameter, number of plies, and basis weight are the values shown in Table 1.
（比較例１〜３）
ヤンキードライヤーの周速およびトイレットペーパー原紙のリールへの巻き取り速度を実施例１と異なるようにしたこと以外は実施例１と同じ材料・条件とし、表１に示す伸びを有する比較例１〜３のロール状トイレットペーパーを製造した。なお、比較例１については３プライ、比較例２〜３については２プライで製造した。巻長、巻径、坪量は表１に示す値とした。
(Comparative Examples 1 to 3)
Comparative Examples 1 to 3 having the same materials and conditions as in Example 1 except that the peripheral speed of the Yankee dryer and the winding speed of the toilet paper base paper on the reel were different from those in Example 1, and having the elongation shown in Table 1. Manufactured roll-shaped toilet paper. In addition, Comparative Example 1 was produced with 3 plies, and Comparative Examples 2 and 3 were produced with 2 plies. The winding length, winding diameter, and basis weight are the values shown in Table 1.
表１から明らかなように、各比較例の１プライあたり、すなわちトイレットペーパー原紙１枚当たりの吸水量は、２８ｍｇ／プライ数以下であったのに対し、各実施例のロール状トイレットペーパーのトイレットペーパー原紙１枚当たりの吸水量は、いずれもそれを上回る値であり、全てが３０ｍｇ／プライ数以上であり、良好であった。すなわち、速乾性（速吸性）に優れたものとなった。また、伸びが３１．４％以下のトイレットペーパーは、断紙などの問題が発生することなく作製することができた。 As is clear from Table 1, the amount of water absorbed per ply of each comparative example, that is, the amount of water absorbed per sheet of toilet paper base paper was 28 mg / ply number or less, whereas the toilet paper of the roll-shaped toilet paper of each example The amount of water absorbed per sheet of paper base paper was higher than that, and all were 30 mg / ply number or more, which was good. That is, it has excellent quick-drying property (quick absorption). Further, the toilet paper having an elongation of 31.4% or less could be produced without causing problems such as paper breakage.
また、ロール状トイレットペーパーを構成するトイレットペーパー１組当たりの伸びは、各比較例が１６．９％以下の値であるが、各実施例はいずれもそれを上回る値となるように製造した。 Further, the growth per set of toilet paper constituting the roll-shaped toilet paper was 16.9% or less in each comparative example, but each example was manufactured so as to exceed that value.
以上の実施例および比較例によると、ロール状トイレットペーパーを構成するトイレットペーパーについての伸びの数値が大きいほど、トイレットペーパーを構成するトイレットペーパー原紙１枚あたりの吸水量が多い傾向にあり、伸びの数値の大きさと吸水量の多さとの間には相関関係が見られた。また、伸びが１６．９％を超えるようにすれば吸水量（上記した速乾性／速吸性を示す本願発明者による新たな指標）が２５ｍｇ/プライを超えた良好なトイレットペーパーとなることが分かった。伸びを１９．１％以上とすると吸水量が３０ｍｇ/プライ以上となり、２１．３％以上とすると吸水量が３５ｍｇ/プライ以上となることが分かった。すなわち、伸びを２１．３％以上にすると、比較例（従来例）において３プライにすることで実現する吸水量７５〜８４ｍｇ/組（一組あたりの吸水量）に対して、実施例１〜３ではそれと同等の吸水量７０〜７２ｍｇ/組を２プライで実現できることが分かった。 According to the above Examples and Comparative Examples, the larger the numerical value of the growth of the toilet paper constituting the roll-shaped toilet paper, the larger the amount of water absorption per toilet paper base paper constituting the toilet paper tends to be. A correlation was found between the magnitude of the numerical value and the amount of water absorption. Further, if the elongation exceeds 16.9%, the water absorption amount (the new index by the inventor of the present application indicating the above-mentioned quick-drying / quick-absorbing property) can be a good toilet paper exceeding 25 mg / ply. Do you get it. It was found that when the elongation was 19.1% or more, the water absorption amount was 30 mg / ply or more, and when the elongation was 21.3% or more, the water absorption amount was 35 mg / ply or more. That is, when the elongation is 21.3% or more, the water absorption amount of 75 to 84 mg / set (water absorption amount per set) realized by using 3 plies in the comparative example (conventional example) is compared with Examples 1 to 1. In No. 3, it was found that an equivalent water absorption amount of 70 to 72 mg / set can be realized with 2 plies.
上記傾向は伸びが高くなればなるほど吸水量が高くなることを示しているが、少なくとも伸びが３１．４％になるまでは製造上の問題も生じることなく上記性能を実現できることがわかった。 The above tendency indicates that the higher the elongation, the higher the water absorption amount, but it was found that the above performance can be realized without causing any manufacturing problem at least until the elongation reaches 31.4%.
以上のことから、本実施形態によれば、吸水量の多いロール状トイレットペーパーが得るためには、ロール状トイレットペーパーを製造するための諸条件を、ロール状トイレットペーパーを構成するトイレットペーパーについての伸びの数値が大きくなるように設定すればよい。つまり、トイレットペーパーがシングルプライである場合はもちろん、マルチプライである場合であってもマルチプライを構成する各トイレットペーパー原紙の物性を別々に規定することなく、トイレットペーパー全体としての総合的な伸びを制御すればよい。 From the above, according to the present embodiment, in order to obtain a roll-shaped toilet paper having a large amount of water absorption, various conditions for producing the roll-shaped toilet paper are set for the toilet paper constituting the roll-shaped toilet paper. The growth value may be set to be large. In other words, not only when the toilet paper is single-ply, but also when it is multi-ply, the overall growth of the toilet paper as a whole does not specify the physical characteristics of each toilet paper base paper that constitutes the multi-ply. Should be controlled.
本発明の実施形態において、伸びの値は、上記した以外の方法によっても制御できる。すなわち、ロール状トイレットペーパーの各製造工程の製造条件を適宜設定することにより、制御することができる。 In the embodiment of the present invention, the elongation value can also be controlled by a method other than the above. That is, it can be controlled by appropriately setting the manufacturing conditions of each manufacturing process of the roll-shaped toilet paper.
例えば、非限定的な１つの例として、トイレットペーパー原紙を抄造する際に、湿紙ウェブに凹凸フェルトを押し付けることにより、トイレットペーパーに凹凸を形成することができ、これによりロール状トイレットペーパーの伸びの値を向上させ得る。また、ヤンキードライヤーと巻取りリールとの速度差を設けることによりトイレットペーパー原紙にあらかじめクレープを付与することができ、これによりロール状トイレットペーパーの伸びの値を向上させ得る。同様に、トイレットペーパー原紙を抄造工程において、その他任意の公知のクレープ付与手法を施すことにより、ロール状トイレットペーパーの伸びの値を向上させ得る。 For example, as a non-limiting example, when making a base paper for toilet paper, unevenness can be formed on the toilet paper by pressing the uneven felt against the wet paper web, whereby the roll-shaped toilet paper is stretched. The value of can be improved. Further, by providing a speed difference between the Yankee dryer and the take-up reel, crepe can be applied to the toilet paper base paper in advance, which can improve the elongation value of the roll-shaped toilet paper. Similarly, the elongation value of the roll-shaped toilet paper can be improved by applying any other known crepe applying method to the toilet paper base paper in the papermaking process.
また、複数のトイレットペーパー原紙をプライマシンにかけて積層させる工程や、エンボス加工を施す工程、ロール状トイレットペーパーを巻き取る工程等において、ワインダーやリワインダーにトイレットペーパー原紙またはトイレットペーパーの原反をかけて巻き取る際に掛かる張力により、伸びの値は低減する方向に向かう。したがって、このような工程において、巻取り速度を遅くするなど、張力が低くなるような設定をすることにより、伸びの値の低減を抑制し得る。 In addition, in the process of laminating a plurality of toilet paper base papers on a ply machine, embossing, winding the roll-shaped toilet paper, etc., the winder or rewinder is wound with the toilet paper base paper or the original fabric of the toilet paper. Due to the tension applied when taking, the elongation value tends to decrease. Therefore, in such a step, reduction of the elongation value can be suppressed by setting the tension to be low, such as slowing down the winding speed.
本発明は上記した実施形態に限定されず、本発明の思想と範囲に含まれる様々な変形および均等物に及ぶことは理解されよう。 It will be appreciated that the invention is not limited to the embodiments described above, but extends to various modifications and equivalents included in the ideas and scope of the invention.
Claims (2)